SG43908A1 - Coating composition having good corrosion and oxidation resistance - Google Patents

Coating composition having good corrosion and oxidation resistance

Info

Publication number
SG43908A1
SG43908A1 SG1996004902A SG1996004902A SG43908A1 SG 43908 A1 SG43908 A1 SG 43908A1 SG 1996004902 A SG1996004902 A SG 1996004902A SG 1996004902 A SG1996004902 A SG 1996004902A SG 43908 A1 SG43908 A1 SG 43908A1
Authority
SG
Singapore
Prior art keywords
coating composition
oxidation resistance
good corrosion
rcralr
rhenium
Prior art date
Application number
SG1996004902A
Other languages
English (en)
Inventor
David Frederick Bettridge
Robert Clarke Tucker Jr
Thomas Alan Taylor
Original Assignee
Praxair Technology Inc
Rolls Royce Plc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Praxair Technology Inc, Rolls Royce Plc filed Critical Praxair Technology Inc
Publication of SG43908A1 publication Critical patent/SG43908A1/en

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C4/00—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge
    • C23C4/04—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge characterised by the coating material
    • C23C4/06—Metallic material
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C16/00—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes
    • C23C16/22—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the deposition of inorganic material, other than metallic material
    • C23C16/30—Deposition of compounds, mixtures or solid solutions, e.g. borides, carbides, nitrides
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C30/00—Coating with metallic material characterised only by the composition of the metallic material, i.e. not characterised by the coating process
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C4/00—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge
    • C23C4/18—After-treatment
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02T—CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO TRANSPORTATION
    • Y02T50/00—Aeronautics or air transport
    • Y02T50/60—Efficient propulsion technologies, e.g. for aircraft
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12535—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.] with additional, spatially distinct nonmetal component
    • Y10T428/12611—Oxide-containing component
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/1266—O, S, or organic compound in metal component
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/1266—O, S, or organic compound in metal component
    • Y10T428/12667—Oxide of transition metal or Al

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Plasma & Fusion (AREA)
  • General Chemical & Material Sciences (AREA)
  • Inorganic Chemistry (AREA)
  • Other Surface Treatments For Metallic Materials (AREA)
  • Turbine Rotor Nozzle Sealing (AREA)
  • Paints Or Removers (AREA)
  • Coating By Spraying Or Casting (AREA)
SG1996004902A 1993-11-08 1994-11-01 Coating composition having good corrosion and oxidation resistance SG43908A1 (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US08/148,460 US5455119A (en) 1993-11-08 1993-11-08 Coating composition having good corrosion and oxidation resistance

Publications (1)

Publication Number Publication Date
SG43908A1 true SG43908A1 (en) 1997-11-14

Family

ID=22525880

Family Applications (1)

Application Number Title Priority Date Filing Date
SG1996004902A SG43908A1 (en) 1993-11-08 1994-11-01 Coating composition having good corrosion and oxidation resistance

Country Status (10)

Country Link
US (1) US5455119A (ko)
EP (1) EP0652299B1 (ko)
JP (1) JP2920076B2 (ko)
KR (1) KR100227237B1 (ko)
CN (1) CN1055512C (ko)
AT (1) ATE146825T1 (ko)
BR (1) BR9404361A (ko)
CA (1) CA2135233C (ko)
DE (1) DE69401260T2 (ko)
SG (1) SG43908A1 (ko)

Families Citing this family (83)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5824423A (en) * 1996-02-07 1998-10-20 N.V. Interturbine Thermal barrier coating system and methods
US6071627A (en) * 1996-03-29 2000-06-06 Kabushiki Kaisha Toshiba Heat-resistant member and a method for evaluating quality of a heat-resistant member
US5989733A (en) * 1996-07-23 1999-11-23 Howmet Research Corporation Active element modified platinum aluminide diffusion coating and CVD coating method
GB2319783B (en) * 1996-11-30 2001-08-29 Chromalloy Uk Ltd A thermal barrier coating for a superalloy article and a method of application thereof
JP2991991B2 (ja) 1997-03-24 1999-12-20 トーカロ株式会社 耐高温環境用溶射被覆部材およびその製造方法
JP2991990B2 (ja) * 1997-03-24 1999-12-20 トーカロ株式会社 耐高温環境用溶射被覆部材およびその製造方法
US5916518A (en) 1997-04-08 1999-06-29 Allison Engine Company Cobalt-base composition
US5958204A (en) * 1997-09-26 1999-09-28 Allison Enaine Company, Inc. Enhancement of coating uniformity by alumina doping
US20040180233A1 (en) * 1998-04-29 2004-09-16 Siemens Aktiengesellschaft Product having a layer which protects against corrosion. and process for producing a layer which protects against corrosion
US6306524B1 (en) * 1999-03-24 2001-10-23 General Electric Company Diffusion barrier layer
US6210812B1 (en) 1999-05-03 2001-04-03 General Electric Company Thermal barrier coating system
US6207297B1 (en) * 1999-09-29 2001-03-27 Siemens Westinghouse Power Corporation Barrier layer for a MCrAlY basecoat superalloy combination
US6346134B1 (en) * 2000-03-27 2002-02-12 Sulzer Metco (Us) Inc. Superalloy HVOF powders with improved high temperature oxidation, corrosion and creep resistance
US6475642B1 (en) * 2000-08-31 2002-11-05 General Electric Company Oxidation-resistant coatings, and related articles and processes
US6924046B2 (en) * 2001-10-24 2005-08-02 Siemens Aktiengesellschaft Rhenium-containing protective layer for protecting a component against corrosion and oxidation at high temperatures
US6942929B2 (en) * 2002-01-08 2005-09-13 Nianci Han Process chamber having component with yttrium-aluminum coating
US7371467B2 (en) 2002-01-08 2008-05-13 Applied Materials, Inc. Process chamber component having electroplated yttrium containing coating
WO2004016819A1 (de) * 2002-08-16 2004-02-26 Alstom Technology Ltd Intermetallisches material und verwendung dieses materials
EP1411210A1 (en) * 2002-10-15 2004-04-21 ALSTOM Technology Ltd Method of depositing an oxidation and fatigue resistant MCrAIY-coating
DE60225569T2 (de) * 2002-12-06 2009-09-03 Alstom Technology Ltd. Verfahren zur örtlichen Abscheidung einer MCrAlY - Beschichtung
EP1428982B1 (en) * 2002-12-06 2009-02-04 ALSTOM Technology Ltd A method of depositing a local MCrAIY-coating
US6893750B2 (en) 2002-12-12 2005-05-17 General Electric Company Thermal barrier coating protected by alumina and method for preparing same
US6887589B2 (en) * 2003-04-18 2005-05-03 General Electric Company Nickel aluminide coating and coating systems formed therewith
US7273662B2 (en) 2003-05-16 2007-09-25 Iowa State University Research Foundation, Inc. High-temperature coatings with Pt metal modified γ-Ni+γ′-Ni3Al alloy compositions
US7153338B2 (en) * 2003-05-20 2006-12-26 Exxonmobil Research And Engineering Company Advanced erosion resistant oxide cermets
DE10332420A1 (de) 2003-07-16 2005-02-10 Alstom Technology Ltd Aluminiumbasierte multinäre Legierungen und deren Verwendung als wärme- und korrosionsschützende Beschichtungen
EP1524334A1 (de) 2003-10-17 2005-04-20 Siemens Aktiengesellschaft Schutzschicht zum Schutz eines Bauteils gegen Korrosion und Oxidation bei hohen Temperaturen und Bauteil
US7316850B2 (en) * 2004-03-02 2008-01-08 Honeywell International Inc. Modified MCrAlY coatings on turbine blade tips with improved durability
US7175888B2 (en) * 2004-03-03 2007-02-13 General Electric Company Mischmetal oxide TBC
US7230696B2 (en) * 2004-03-08 2007-06-12 Philip Morris Usa Inc. Calibration of instruments for measuring the permeability of a material
EP1693473B1 (de) * 2005-02-18 2008-05-07 Siemens Aktiengesellschaft MCrAIX-Legierung, Schutzschicht aus MCrAIX-Legierung und Verfahren zur Herstellung
US7833472B2 (en) 2005-06-01 2010-11-16 General Electric Company Article prepared by depositing an alloying element on powder particles, and making the article from the particles
US20060280955A1 (en) * 2005-06-13 2006-12-14 Irene Spitsberg Corrosion resistant sealant for EBC of silicon-containing substrate and processes for preparing same
US20060280954A1 (en) * 2005-06-13 2006-12-14 Irene Spitsberg Corrosion resistant sealant for outer EBL of silicon-containing substrate and processes for preparing same
US8603930B2 (en) 2005-10-07 2013-12-10 Sulzer Metco (Us), Inc. High-purity fused and crushed zirconia alloy powder and method of producing same
EP1780294A1 (de) 2005-10-25 2007-05-02 Siemens Aktiengesellschaft Legierung, Schutzschicht zum Schutz eines Bauteils gegen Korrosion und Oxidation bei hohen Temperaturen und Bauteil
US20070099013A1 (en) * 2005-10-27 2007-05-03 General Electric Company Methods and apparatus for manufacturing a component
EP1790746B1 (de) * 2005-11-24 2010-11-10 Siemens Aktiengesellschaft Legierung, Schutzschicht und Bauteil
EP1790743A1 (de) * 2005-11-24 2007-05-30 Siemens Aktiengesellschaft Legierung, Schutzschicht und Bauteil
US20100068556A1 (en) * 2005-12-09 2010-03-18 General Electric Company Diffusion barrier layer and methods of forming
US8920883B2 (en) * 2005-12-28 2014-12-30 Ansaldo Energia S.P.A. Alloy composition for the manufacture of protective coatings, its use, process for its application and super-alloy articles coated with the same composition
EP1818419A1 (de) * 2006-01-16 2007-08-15 Siemens Aktiengesellschaft Legierung, Schutzschicht und Bauteil
US20070187005A1 (en) * 2006-02-13 2007-08-16 Taylor Thomas A Alloy powders and coating compositions containing same
US7910225B2 (en) * 2006-02-13 2011-03-22 Praxair S.T. Technology, Inc. Low thermal expansion bondcoats for thermal barrier coatings
US20070190354A1 (en) * 2006-02-13 2007-08-16 Taylor Thomas A Low thermal expansion bondcoats for thermal barrier coatings
US20070207328A1 (en) * 2006-03-01 2007-09-06 United Technologies Corporation High density thermal barrier coating
US8021762B2 (en) * 2006-05-26 2011-09-20 Praxair Technology, Inc. Coated articles
US20070274837A1 (en) * 2006-05-26 2007-11-29 Thomas Alan Taylor Blade tip coatings
US20080026160A1 (en) * 2006-05-26 2008-01-31 Thomas Alan Taylor Blade tip coating processes
EP1925687A1 (de) * 2006-11-24 2008-05-28 Siemens Aktiengesellschaft NiCoCrAI-Schicht und metallisches Schichtsystem
US7727318B2 (en) * 2007-01-09 2010-06-01 General Electric Company Metal alloy compositions and articles comprising the same
US7931759B2 (en) 2007-01-09 2011-04-26 General Electric Company Metal alloy compositions and articles comprising the same
US7846243B2 (en) 2007-01-09 2010-12-07 General Electric Company Metal alloy compositions and articles comprising the same
US7883784B2 (en) * 2007-02-16 2011-02-08 Praxair S. T. Technology, Inc. Thermal spray coatings and applications therefor
US8043718B2 (en) * 2007-09-14 2011-10-25 Siemens Energy, Inc. Combustion turbine component having rare earth NiCrAl coating and associated methods
US8039117B2 (en) * 2007-09-14 2011-10-18 Siemens Energy, Inc. Combustion turbine component having rare earth NiCoCrAl coating and associated methods
US7867626B2 (en) * 2007-09-14 2011-01-11 Siemens Energy, Inc. Combustion turbine component having rare earth FeCrAI coating and associated methods
US8043717B2 (en) * 2007-09-14 2011-10-25 Siemens Energy, Inc. Combustion turbine component having rare earth CoNiCrAl coating and associated methods
US8821654B2 (en) 2008-07-15 2014-09-02 Iowa State University Research Foundation, Inc. Pt metal modified γ-Ni+γ′-Ni3Al alloy compositions for high temperature degradation resistant structural alloys
JP5660428B2 (ja) 2010-04-20 2015-01-28 独立行政法人物質・材料研究機構 耐熱コーティング材
CN103102716B (zh) * 2011-11-11 2015-11-04 神华集团有限责任公司 一种涂层组合物、涂层系统、和具有所述涂层系统的构件
US20130337215A1 (en) * 2012-06-19 2013-12-19 Caterpillar, Inc. Remanufactured Component And FeA1SiC Thermal Spray Wire For Same
WO2014133538A1 (en) * 2013-03-01 2014-09-04 Siemens Aktiengesellschaft High temperature bond coating with increased oxidation resistance
CA2904185C (en) * 2013-03-13 2021-02-23 General Electric Company Coatings for metallic substrates
CN104451655B (zh) * 2013-09-13 2018-02-16 中国科学院金属研究所 抗高温材料用表面合金涂层复合材料、涂层及其制备方法
GB201407151D0 (en) 2014-04-23 2014-06-04 Rolls Royce Plc A method of testing the oxidation resistance of an alloy
CN104046979B (zh) * 2014-06-21 2016-06-29 上海君山表面技术工程股份有限公司 抗结瘤复合涂层的喷涂方法
CN104761943B (zh) * 2015-04-15 2017-02-22 西安科技大学 一种镁合金耐蚀涂料及其应用
CN105803376B (zh) * 2016-03-17 2018-03-02 广东省新材料研究所 一种抗高温氧化耐磨涂层制备方法
US10202855B2 (en) * 2016-06-02 2019-02-12 General Electric Company Airfoil with improved coating system
CN106756838B (zh) * 2016-09-22 2019-01-18 常熟理工学院 一种γ-TiAl合金表面纳米梯度结构高温防护涂层及其制备方法
CN107034429B (zh) * 2017-03-10 2019-06-28 广东省新材料研究所 一种低散热摩托车发动机的制备方法
CN106987755A (zh) * 2017-06-05 2017-07-28 北京普瑞新材科技有限公司 一种MCrAlY合金及其制备方法
KR20190016863A (ko) * 2017-08-09 2019-02-19 엘지전자 주식회사 의류처리장치
CN107620061B (zh) * 2017-10-30 2019-11-05 江苏大学 一种高温抗氧化钴基涂层材料及其制备方法
CN110835719A (zh) * 2018-08-17 2020-02-25 北京航化节能环保技术有限公司 一种气化炉燃烧器用热喷涂抗高温氧化涂层及其制备方法
EP3663706B1 (en) * 2018-12-06 2022-08-24 General Electric Company Quantitative multilayer assessment method
CN110343988A (zh) * 2019-08-30 2019-10-18 北方工业大学 抑制活性元素过度掺杂的MCrAlRe/RexOy涂层材料、涂层及制备方法
US11686208B2 (en) 2020-02-06 2023-06-27 Rolls-Royce Corporation Abrasive coating for high-temperature mechanical systems
CN112030098A (zh) * 2020-09-03 2020-12-04 昆明理工大学 一种艾萨炉冶炼长寿命喷枪之高温合金涂层及其制备方法
EP4053222A1 (en) * 2021-03-03 2022-09-07 General Electric Company Anti-fretting coating composition and coated components
CN115747795B (zh) * 2022-12-05 2024-03-26 江苏大学 一种高服役寿命的热障涂层粘结层及其制备方法
CN116445846B (zh) * 2023-05-08 2024-02-02 中国科学院兰州化学物理研究所 一种爆炸喷涂镍基宽温域自润滑涂层

Family Cites Families (34)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3754903A (en) * 1970-09-15 1973-08-28 United Aircraft Corp High temperature oxidation resistant coating alloy
US3676085A (en) * 1971-02-18 1972-07-11 United Aircraft Corp Cobalt base coating for the superalloys
US3864093A (en) * 1972-11-17 1975-02-04 Union Carbide Corp High-temperature, wear-resistant coating
US3928026A (en) * 1974-05-13 1975-12-23 United Technologies Corp High temperature nicocraly coatings
US3918139A (en) * 1974-07-10 1975-11-11 United Technologies Corp MCrAlY type coating alloy
US3993454A (en) * 1975-06-23 1976-11-23 United Technologies Corporation Alumina forming coatings containing hafnium for high temperature applications
USRE33876E (en) * 1975-09-11 1992-04-07 United Technologies Corporation Thermal barrier coating for nickel and cobalt base super alloys
US4124737A (en) * 1976-12-30 1978-11-07 Union Carbide Corporation High temperature wear resistant coating composition
US4101713A (en) * 1977-01-14 1978-07-18 General Electric Company Flame spray oxidation and corrosion resistant superalloys
US4101715A (en) * 1977-06-09 1978-07-18 General Electric Company High integrity CoCrAl(Y) coated nickel-base superalloys
US4313760A (en) * 1979-05-29 1982-02-02 Howmet Turbine Components Corporation Superalloy coating composition
SE8000750L (sv) * 1980-01-30 1981-07-31 Bulten Kanthal Ab Varmhallfast maskinkomponent och sett att framstella densamma
US4447503A (en) * 1980-05-01 1984-05-08 Howmet Turbine Components Corporation Superalloy coating composition with high temperature oxidation resistance
US4615864A (en) * 1980-05-01 1986-10-07 Howmet Turbine Components Corporation Superalloy coating composition with oxidation and/or sulfidation resistance
US4585481A (en) * 1981-08-05 1986-04-29 United Technologies Corporation Overlays coating for superalloys
US4677034A (en) * 1982-06-11 1987-06-30 General Electric Company Coated superalloy gas turbine components
US4451496A (en) * 1982-07-30 1984-05-29 The United States Of America As Represented By The Administrator Of The National Aeronautics And Space Administration Coating with overlay metallic-cermet alloy systems
US4451431A (en) * 1982-10-25 1984-05-29 Avco Corporation Molybdenum-containing high temperature coatings for nickel- and cobalt-based superalloys
US4743514A (en) * 1983-06-29 1988-05-10 Allied-Signal Inc. Oxidation resistant protective coating system for gas turbine components, and process for preparation of coated components
JPS60194056A (ja) * 1984-03-14 1985-10-02 Hitachi Ltd セラミツク被覆層を有する耐熱部材
CA1233998A (en) * 1984-04-05 1988-03-15 Subramaniam Rangaswamy Aluminum and yttrium oxide coated thermal spray powder
EP0194391B1 (en) * 1985-03-13 1989-06-21 General Electric Company Yttrium and yttrium-silicon bearing nickel-base superalloys especially useful as compatible coatings for advanced superalloys
US4719080A (en) * 1985-06-10 1988-01-12 United Technologies Corporation Advanced high strength single crystal superalloy compositions
EP0244458B1 (en) * 1985-10-18 1990-06-27 Union Carbide Corporation High volume fraction refractory oxide, thermal shock resistant coatings
JPS6396257A (ja) * 1986-10-11 1988-04-27 Sanwa Tokushu Seiko Kk セラミツク・コ−テイングにおけるアンダ−・コ−ト形成用金属材料
CH674019A5 (ko) * 1988-01-18 1990-04-30 Asea Brown Boveri
US4943487A (en) * 1988-07-18 1990-07-24 Inco Alloys International, Inc. Corrosion resistant coating for oxide dispersion strengthened alloys
DE3918380A1 (de) * 1989-06-06 1990-12-20 Starck Hermann C Fa Hochtemperatur-verbund-werkstoff, verfahren zu seiner herstellung sowie dessen verwendung
DE3926479A1 (de) * 1989-08-10 1991-02-14 Siemens Ag Rheniumhaltige schutzbeschichtung, mit grosser korrosions- und/oder oxidationsbestaendigkeit
US5064727A (en) * 1990-01-19 1991-11-12 Avco Corporation Abradable hybrid ceramic wall structures
JPH04285114A (ja) * 1991-03-15 1992-10-09 Nippon Steel Corp 耐熱ロール
JPH04323357A (ja) * 1991-04-23 1992-11-12 Toshiba Corp 耐熱構造体
US5316866A (en) * 1991-09-09 1994-05-31 General Electric Company Strengthened protective coatings for superalloys
CA2076091A1 (en) * 1991-09-09 1993-03-10 Edward H. Goldman Superalloy component with dispersion-containing protective coatings, and method of preparation

Also Published As

Publication number Publication date
ATE146825T1 (de) 1997-01-15
BR9404361A (pt) 1995-07-04
KR100227237B1 (ko) 1999-11-01
EP0652299B1 (en) 1996-12-27
CN1055512C (zh) 2000-08-16
US5455119A (en) 1995-10-03
DE69401260T2 (de) 1997-04-30
KR950014358A (ko) 1995-06-16
JPH07252674A (ja) 1995-10-03
CN1105396A (zh) 1995-07-19
CA2135233A1 (en) 1995-05-09
DE69401260D1 (de) 1997-02-06
CA2135233C (en) 1998-07-14
EP0652299A1 (en) 1995-05-10
JP2920076B2 (ja) 1999-07-19

Similar Documents

Publication Publication Date Title
SG43908A1 (en) Coating composition having good corrosion and oxidation resistance
BRPI0414602A (pt) pigmento preto brilhante e preparação cosmética, composição de revestimento, composição de resina e composição de tinta de escrever contendo o mesmo
HK1001592A1 (en) Polymer blend
CA2152524A1 (en) Process for producing an oxide dispersed mcraly-based coating
MY111923A (en) Semiconducting ceramic composition having positive temperature coefficient of resistance and production process thereof
AU4628496A (en) Catalyst
AU585991B2 (en) Corrosion inhibitive pigment compositions and aqueous coating composition containing same
CA2012948A1 (en) Aqueous coating compositions
AU5769298A (en) Use of mixtures with base of pt and of transition metal compounds other than pt for improving the resistance to arc tracking and to arc erosion of silicon elastomers
IT1261480B (it) Composti disazoici basici contenenti gruppi solfo, loro preparazione e loro impiego come coloranti.
Bettridge et al. Coating composition having good corrosion and oxidation resistance
TW372994B (en) Low pigment content polyester film
KR960010790A (ko) 전도성 안료 배합물
GB2288411B (en) Metal pigments
WO1987002389A3 (en) High volume fraction refractory oxide, thermal shock resistant coatings
FR2682951B1 (ko)
BR9405363A (pt) Processo para produzir um pó de magnetita monofásico
AU2143895A (en) Method of manufacturing an electrical resistance heating means
KR880004049A (ko) 산화철 자기안료 및 이의 제조방법
CA2375354A1 (en) Cr-based alloy having an excellent strength-ductility balance at high temperature
CA2099224A1 (en) A single-phase superconductive metal oxide and method of manufacturing the same
Biegun et al. The Reactive Element Effect on the Oxidation Resistance of Fe--23 Cr--5 Al Commercial Alloys
Ceratelli Platinum
Panarin et al. Gaseous Thermal Coatings From Eutectic Melts Based on Iron With an Ultradispersed Structure
Pierantoni et al. Surface Coating Made From an Aluminum-Based Alloy