RU2020122904A - Композиции активных компонентов кремнеземно-глиноземной матрицы для катализаторов крекинга кубовых остатков - Google Patents
Композиции активных компонентов кремнеземно-глиноземной матрицы для катализаторов крекинга кубовых остатков Download PDFInfo
- Publication number
- RU2020122904A RU2020122904A RU2020122904A RU2020122904A RU2020122904A RU 2020122904 A RU2020122904 A RU 2020122904A RU 2020122904 A RU2020122904 A RU 2020122904A RU 2020122904 A RU2020122904 A RU 2020122904A RU 2020122904 A RU2020122904 A RU 2020122904A
- Authority
- RU
- Russia
- Prior art keywords
- cracking
- alumina
- bottoms
- catalytic composition
- catalyst
- Prior art date
Links
- 238000005336 cracking Methods 0.000 title claims 35
- 239000000203 mixture Substances 0.000 title claims 31
- 239000003054 catalyst Substances 0.000 title claims 22
- 239000011159 matrix material Substances 0.000 title claims 2
- 229910052782 aluminium Inorganic materials 0.000 title 1
- 230000003197 catalytic effect Effects 0.000 claims 20
- 238000000034 method Methods 0.000 claims 19
- PNEYBMLMFCGWSK-UHFFFAOYSA-N aluminium oxide Inorganic materials [O-2].[O-2].[O-2].[Al+3].[Al+3] PNEYBMLMFCGWSK-UHFFFAOYSA-N 0.000 claims 18
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 claims 16
- 229910021536 Zeolite Inorganic materials 0.000 claims 14
- 239000010457 zeolite Substances 0.000 claims 14
- 229910052761 rare earth metal Inorganic materials 0.000 claims 9
- 238000004231 fluid catalytic cracking Methods 0.000 claims 8
- 229910052746 lanthanum Inorganic materials 0.000 claims 8
- FZLIPJUXYLNCLC-UHFFFAOYSA-N lanthanum atom Chemical compound [La] FZLIPJUXYLNCLC-UHFFFAOYSA-N 0.000 claims 8
- HNPSIPDUKPIQMN-UHFFFAOYSA-N dioxosilane;oxo(oxoalumanyloxy)alumane Chemical compound O=[Si]=O.O=[Al]O[Al]=O HNPSIPDUKPIQMN-UHFFFAOYSA-N 0.000 claims 7
- 239000002019 doping agent Substances 0.000 claims 7
- 239000005995 Aluminium silicate Substances 0.000 claims 6
- 235000012211 aluminium silicate Nutrition 0.000 claims 6
- NLYAJNPCOHFWQQ-UHFFFAOYSA-N kaolin Chemical compound O.O.O=[Al]O[Si](=O)O[Si](=O)O[Al]=O NLYAJNPCOHFWQQ-UHFFFAOYSA-N 0.000 claims 6
- 239000000377 silicon dioxide Substances 0.000 claims 6
- -1 aluminum oxychloride Chemical compound 0.000 claims 5
- 229910052684 Cerium Inorganic materials 0.000 claims 4
- 229910052688 Gadolinium Inorganic materials 0.000 claims 4
- 229910052769 Ytterbium Inorganic materials 0.000 claims 4
- 239000007900 aqueous suspension Substances 0.000 claims 4
- GWXLDORMOJMVQZ-UHFFFAOYSA-N cerium Chemical compound [Ce] GWXLDORMOJMVQZ-UHFFFAOYSA-N 0.000 claims 4
- 239000008119 colloidal silica Substances 0.000 claims 4
- UIWYJDYFSGRHKR-UHFFFAOYSA-N gadolinium atom Chemical compound [Gd] UIWYJDYFSGRHKR-UHFFFAOYSA-N 0.000 claims 4
- 239000004005 microsphere Substances 0.000 claims 4
- NAWDYIZEMPQZHO-UHFFFAOYSA-N ytterbium Chemical compound [Yb] NAWDYIZEMPQZHO-UHFFFAOYSA-N 0.000 claims 4
- 229910052727 yttrium Inorganic materials 0.000 claims 4
- VWQVUPCCIRVNHF-UHFFFAOYSA-N yttrium atom Chemical compound [Y] VWQVUPCCIRVNHF-UHFFFAOYSA-N 0.000 claims 4
- FYYHWMGAXLPEAU-UHFFFAOYSA-N Magnesium Chemical compound [Mg] FYYHWMGAXLPEAU-UHFFFAOYSA-N 0.000 claims 3
- 229910052788 barium Inorganic materials 0.000 claims 3
- DSAJWYNOEDNPEQ-UHFFFAOYSA-N barium atom Chemical compound [Ba] DSAJWYNOEDNPEQ-UHFFFAOYSA-N 0.000 claims 3
- 229910052749 magnesium Inorganic materials 0.000 claims 3
- 239000011777 magnesium Substances 0.000 claims 3
- QSHDDOUJBYECFT-UHFFFAOYSA-N mercury Chemical compound [Hg] QSHDDOUJBYECFT-UHFFFAOYSA-N 0.000 claims 3
- 229910052753 mercury Inorganic materials 0.000 claims 3
- 239000002245 particle Substances 0.000 claims 3
- 238000002459 porosimetry Methods 0.000 claims 3
- 239000011148 porous material Substances 0.000 claims 3
- 239000004215 Carbon black (E152) Substances 0.000 claims 2
- PXHVJJICTQNCMI-UHFFFAOYSA-N Nickel Chemical compound [Ni] PXHVJJICTQNCMI-UHFFFAOYSA-N 0.000 claims 2
- 239000000654 additive Substances 0.000 claims 2
- 230000000996 additive effect Effects 0.000 claims 2
- 239000011230 binding agent Substances 0.000 claims 2
- 229930195733 hydrocarbon Natural products 0.000 claims 2
- 150000002430 hydrocarbons Chemical class 0.000 claims 2
- 238000004519 manufacturing process Methods 0.000 claims 2
- 238000001694 spray drying Methods 0.000 claims 2
- BVKZGUZCCUSVTD-UHFFFAOYSA-L Carbonate Chemical compound [O-]C([O-])=O BVKZGUZCCUSVTD-UHFFFAOYSA-L 0.000 claims 1
- 229910017569 La2(CO3)3 Inorganic materials 0.000 claims 1
- 238000005275 alloying Methods 0.000 claims 1
- 238000001354 calcination Methods 0.000 claims 1
- GHLITDDQOMIBFS-UHFFFAOYSA-H cerium(3+);tricarbonate Chemical compound [Ce+3].[Ce+3].[O-]C([O-])=O.[O-]C([O-])=O.[O-]C([O-])=O GHLITDDQOMIBFS-UHFFFAOYSA-H 0.000 claims 1
- 239000004927 clay Substances 0.000 claims 1
- 239000011248 coating agent Substances 0.000 claims 1
- 238000000576 coating method Methods 0.000 claims 1
- 239000000571 coke Substances 0.000 claims 1
- 238000010304 firing Methods 0.000 claims 1
- RQXZRSYWGRRGCD-UHFFFAOYSA-H gadolinium(3+);tricarbonate Chemical compound [Gd+3].[Gd+3].[O-]C([O-])=O.[O-]C([O-])=O.[O-]C([O-])=O RQXZRSYWGRRGCD-UHFFFAOYSA-H 0.000 claims 1
- NZPIUJUFIFZSPW-UHFFFAOYSA-H lanthanum carbonate Chemical compound [La+3].[La+3].[O-]C([O-])=O.[O-]C([O-])=O.[O-]C([O-])=O NZPIUJUFIFZSPW-UHFFFAOYSA-H 0.000 claims 1
- 229960001633 lanthanum carbonate Drugs 0.000 claims 1
- 229910052759 nickel Inorganic materials 0.000 claims 1
- 230000000704 physical effect Effects 0.000 claims 1
- 229910052720 vanadium Inorganic materials 0.000 claims 1
- LEONUFNNVUYDNQ-UHFFFAOYSA-N vanadium atom Chemical compound [V] LEONUFNNVUYDNQ-UHFFFAOYSA-N 0.000 claims 1
- JCDQGOSXWGXOQQ-UHFFFAOYSA-H ytterbium(3+);tricarbonate Chemical compound [Yb+3].[Yb+3].[O-]C([O-])=O.[O-]C([O-])=O.[O-]C([O-])=O JCDQGOSXWGXOQQ-UHFFFAOYSA-H 0.000 claims 1
- QVOIJBIQBYRBCF-UHFFFAOYSA-H yttrium(3+);tricarbonate Chemical compound [Y+3].[Y+3].[O-]C([O-])=O.[O-]C([O-])=O.[O-]C([O-])=O QVOIJBIQBYRBCF-UHFFFAOYSA-H 0.000 claims 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
- C10G11/00—Catalytic cracking, in the absence of hydrogen, of hydrocarbon oils
- C10G11/02—Catalytic cracking, in the absence of hydrogen, of hydrocarbon oils characterised by the catalyst used
- C10G11/04—Oxides
- C10G11/05—Crystalline alumino-silicates, e.g. molecular sieves
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J21/00—Catalysts comprising the elements, oxides, or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium, or hafnium
- B01J21/12—Silica and alumina
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J21/00—Catalysts comprising the elements, oxides, or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium, or hafnium
- B01J21/16—Clays or other mineral silicates
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/10—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of rare earths
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J29/00—Catalysts comprising molecular sieves
- B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
- B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
- B01J29/08—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the faujasite type, e.g. type X or Y
- B01J29/085—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the faujasite type, e.g. type X or Y containing rare earth elements, titanium, zirconium, hafnium, zinc, cadmium, mercury, gallium, indium, thallium, tin or lead
- B01J29/088—Y-type faujasite
-
- B01J35/19—
-
- B01J35/40—
-
- B01J35/51—
-
- B01J35/613—
-
- B01J35/615—
-
- B01J35/633—
-
- B01J35/635—
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/0009—Use of binding agents; Moulding; Pressing; Powdering; Granulating; Addition of materials ameliorating the mechanical properties of the product catalyst
- B01J37/0027—Powdering
- B01J37/0036—Grinding
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/0009—Use of binding agents; Moulding; Pressing; Powdering; Granulating; Addition of materials ameliorating the mechanical properties of the product catalyst
- B01J37/0027—Powdering
- B01J37/0045—Drying a slurry, e.g. spray drying
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/02—Impregnation, coating or precipitation
- B01J37/03—Precipitation; Co-precipitation
- B01J37/038—Precipitation; Co-precipitation to form slurries or suspensions, e.g. a washcoat
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/08—Heat treatment
- B01J37/082—Decomposition and pyrolysis
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/08—Heat treatment
- B01J37/10—Heat treatment in the presence of water, e.g. steam
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
- C10G11/00—Catalytic cracking, in the absence of hydrogen, of hydrocarbon oils
- C10G11/02—Catalytic cracking, in the absence of hydrogen, of hydrocarbon oils characterised by the catalyst used
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
- C10G11/00—Catalytic cracking, in the absence of hydrogen, of hydrocarbon oils
- C10G11/14—Catalytic cracking, in the absence of hydrogen, of hydrocarbon oils with preheated moving solid catalysts
- C10G11/18—Catalytic cracking, in the absence of hydrogen, of hydrocarbon oils with preheated moving solid catalysts according to the "fluidised-bed" technique
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J2229/00—Aspects of molecular sieve catalysts not covered by B01J29/00
- B01J2229/10—After treatment, characterised by the effect to be obtained
- B01J2229/18—After treatment, characterised by the effect to be obtained to introduce other elements into or onto the molecular sieve itself
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J2229/00—Aspects of molecular sieve catalysts not covered by B01J29/00
- B01J2229/30—After treatment, characterised by the means used
- B01J2229/42—Addition of matrix or binder particles
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J2523/00—Constitutive chemical elements of heterogeneous catalysts
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
- C10G2300/00—Aspects relating to hydrocarbon processing covered by groups C10G1/00 - C10G99/00
- C10G2300/70—Catalyst aspects
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Engineering & Computer Science (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Materials Engineering (AREA)
- Oil, Petroleum & Natural Gas (AREA)
- General Chemical & Material Sciences (AREA)
- Crystallography & Structural Chemistry (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Dispersion Chemistry (AREA)
- Catalysts (AREA)
- Production Of Liquid Hydrocarbon Mixture For Refining Petroleum (AREA)
- Silicates, Zeolites, And Molecular Sieves (AREA)
Claims (72)
1. Каталитическая композиция для крекинга кубовых остатков, содержащая:
от около 30 до около 60% мас. глинозема;
от более 0 до около 10% мас. легирующей добавки, включающей иттербий, гадолиний, церий, лантан, иттрий, барий, магний или смесь любых двух или более из них, измеренной в виде оксида;
от около 2 до около 20% мас. реакционноспособного кремнезема;
от около 3 до около 20% мас. компонента, содержащего пептизируемый бомит, коллоидный кремнезем, оксихлорид алюминия или комбинацию любых двух или более из них; и
от около 10 до около 50% мас. каолина.
2. Каталитическая композиция для крекинга кубовых остатков по п. 1, содержащая легирующую добавку, в количестве от около 0,1 до около 5% мас. в расчете на массу композиции, измеренную в виде оксида.
3. Каталитическая композиция для крекинга кубовых остатков по п. 1, отличающаяся тем, что легирующая добавка присутствует в количестве около 4% мас.
4. Каталитическая композиция для крекинга кубовых остатков по п. 1, отличающаяся тем, что легирующая добавка включает лантан.
5. Каталитическая композиция для крекинга кубовых остатков по п. 1, отличающаяся тем, что легирующая добавка импрегнирована в глинозем или нанесена на глинозем покрытием, или осаждена совместно с глиноземом.
6. Каталитическая композиция для крекинга кубовых остатков по п. 1, имеющая средний размер частиц около 70-95 мкм.
7. Каталитическая композиция для крекинга кубовых остатков по п. 1, имеющая объем пор, измеренный ртутной порометрией, 0,3-0,56 см3/г в диапазоне диаметров от 4 до 2000 нм.
8. Каталитическая композиция для крекинга кубовых остатков по п. 1, дополнительно содержащая в составе цеолит.
9. Каталитическая композиция для крекинга кубовых остатков по п. 8, отличающаяся тем, что цеолит представляет собой Y-цеолит.
10. Каталитическая композиция для крекинга кубовых остатков по п. 1, не содержащая цеолита.
11. Каталитическая композиция для крекинга кубовых остатков по любому из пп. 1-10, отличающаяся тем, что глинозем представляет собой кальцинированный глинозем.
12. Способ изготовления катализатора крекинга кубовых остатков, включающий
формирование водной суспензии, содержащей, в расчете на сухую массу,
от около 30 до около 60% мас. глинозема;
от более 0 до около 10% мас. легирующей добавки, включающей иттербий, гадолиний, церий, лантан, иттрий, барий, магний или смесь любых двух или более из них, измеренной в виде оксида, по отношению к глинозему;
от около 2 до около 20% мас. реакционноспособного кремнезема;
от около 3 до около 20% мас. компонента, содержащего пептизируемый бомит, коллоидный кремнезем, оксихлорид алюминия или комбинацию любых двух или более из них; и
от около 10 до около 50% мас. каолина и получение микросфер посредством распылительной сушки водной суспензии.
13. Способ по п. 12, дополнительно включающий прокаливание микросфер.
14. Способ по п. 12, отличающийся тем, что глинозем представляет собой кальцинированный глинозем.
15. Способ крекинга углеводородного сырья, включающий приведение в контакт указанного сырья с катализатором флюид-каталитического крекинга (FCC), содержащим цеолитный компонент и катализатор крекинга кубовых остатков, причем катализатор крекинга кубовых остатков содержит:
от около 30 до около 60% мас. глинозема;
от более 0 до около 10% мас. легирующей добавки, включающей иттербий, гадолиний, церий, лантан, иттрий, барий, магний или смесь любых двух или более из них, измеренной в виде оксида;
от около 2 до около 20% мас. реакционноспособного кремнезема;
от около 3 до около 20% мас. компонента, содержащего пептизируемый бомит, коллоидный кремнезем, оксихлорид алюминия или комбинацию любых двух или более из них; и
от около 10 до около 50% мас. каолина.
16. Способ по п. 15, отличающийся тем, что катализатор содержит легирующую добавку в количестве от около 0,1 до около 5% мае, измеренную в виде оксида.
17. Способ по п. 16, отличающийся тем, что редкоземельный элемент включает лантан.
18. Способ по п. 15, отличающийся тем, что обеспечивает выход кокса, измеренный при 13% мас. кубовых остатков, более чем на 10% ниже, чем в случае, когда сырье приводят в контакт с катализатором, имеющим такие же физические свойства, который не содержит катализатор крекинга кубовых остатков.
19. Способ по п. 15, отличающийся тем, что цеолит включает Y-цеолит.
20. Способ по п. 15, отличающийся тем, что катализатор FCC содержит по меньшей мере 15% мас. катализатора крекинга кубовых остатков.
21. Способ по п. 20, отличающийся тем, что катализатор FCC содержит по меньшей мере 50% мас. цеолитного компонента.
22. Способ по п. 15, отличающийся тем, что катализатор FCC содержит от 15 до 80% мас. катализатора крекинга кубовых остатков.
23. Способ по п. 22, отличающийся тем, что катализатор FCC содержит от 50 до 80% мас. катализатора крекинга кубовых остатков.
24. Способ по п. 15, отличающийся тем, что катализатор FCC содержит от 15 до 50% мас. катализатора крекинга кубовых остатков и от 85 до 50% мас. цеолитного компонента и, необязательно, других компонентов на основе глины.
25. Способ по п. 15, отличающийся тем, что катализатор FCC дополнительно содержит ванадиевую ловушку или никелевую ловушку с кристаллическим бомитом.
26. Способ по любому из пп. 15-25, отличающийся тем, что глинозем представляет собой кальцинированный глинозем.
27. Каталитическая композиция для крекинга кубовых остатков, содержащая:
от около 30 до около 60% мас. глинозема;
от более 0 до около 10% мае карбоната редкоземельного элемента, включающего карбонат иттербия, карбонат гадолиния, карбонат церия, карбонат лантана, карбонат иттрия или смесь любых двух или более из них, измеренного в виде оксида;
от около 2 до около 20% мас. реакционноспособного кремнезема;
от около 3 до около 20% мас. компонента, содержащего пептизируемый бомит, коллоидный кремнезем, оксихлорид алюминия или комбинацию любых двух или более из них; и
от около 10 до около 50% мас. каолина.
28. Каталитическая композиция для крекинга кубовых остатков по п. 27, содержащая карбонат редкоземельного элемента, который присутствует в количестве от около 0,1 до около 5% мас. композиции, измеренный в виде оксида.
29. Каталитическая композиция для крекинга кубовых остатков по п. 27, отличающаяся тем, что редкоземельный элемент включает лантан.
30. Каталитическая композиция для крекинга кубовых остатков по п. 27, имеющая средний размер частиц около 70-95 мкм.
31. Каталитическая композиция для крекинга кубовых остатков по п. 27, имеющая объем пор, измеренный ртутной порометрией, 0,3-0,56 см3/г в диапазоне диаметров от 4 до 2000 нм.
32. Каталитическая композиция для крекинга кубовых остатков по пп. 27-31, отличающаяся тем, что глинозем представляет собой кальцинированный глинозем.
33. Каталитическая композиция для крекинга кубовых остатков, содержащая:
от около 10 до около 20% мас. Y-цеолита, замещенного редкоземельным элементом;
от около 10 до около 30% мас. связующего, содержащего кремнезем и бомит;
от около 30 до около 60% мас. активной матрицы, содержащей глинозем и, необязательно, кристаллический бомит; и
от около 10 до около 50% мас. каолина.
34. Каталитическая композиция для крекинга кубовых остатков по п. 33, отличающаяся тем, что Y-цеолит, замещенный редкоземельным элементом, содержит иттербий, гадолиний, церий, лантан, иттрий или смесь любых двух или более из них.
35. Каталитическая композиция для крекинга кубовых остатков по п. 33, отличающаяся тем, что Y-цеолит, замещенный редкоземельным элементом, содержит лантан.
36. Каталитическая композиция для крекинга кубовых остатков по п. 33, имеющая средний размер частиц около 70-95 мкм.
37. Каталитическая композиция для крекинга кубовых остатков по любому из пп. 33-36, имеющая объем пор, измеренный ртутной порометрией, 0,3-0,56 см3/г в диапазоне диаметров от 4 до 2000 нм.
38. Способ изготовления катализатора крекинга кубовых остатков, включающий:
формирование водной суспензии, содержащей, в расчете на сухую массу,
от около 10 до около 20% мас. Y-цеолита, замещенного редкоземельным элементом;
от около 10 до около 30% мас. связующего, содержащего кремнезем и бомит;
от около 30 до около 60% мас. добавки, содержащей глинозем и, необязательно, кристаллический бомит; а также
от около 10 до около 50% мас. каолина; и
получение микросфер посредством распылительной сушки водной суспензии.
39. Способ по п. 38, дополнительно включающий обжиг микросфер.
40. Способ по п. 38, отличающийся тем, что Y-цеолит замещен редкоземельным элементом в количестве около 1-10% мас.
41. Способ крекинга углеводородного сырья, включающий приведение в контакт указанного сырья с каталитической композицией для крекинга кубовых остатков по любому из пп. 33-37.