RU2014106733A - Десульфирующий материал, содержащий медь, нанесенную на оксид цинка - Google Patents
Десульфирующий материал, содержащий медь, нанесенную на оксид цинка Download PDFInfo
- Publication number
- RU2014106733A RU2014106733A RU2014106733/04A RU2014106733A RU2014106733A RU 2014106733 A RU2014106733 A RU 2014106733A RU 2014106733/04 A RU2014106733/04 A RU 2014106733/04A RU 2014106733 A RU2014106733 A RU 2014106733A RU 2014106733 A RU2014106733 A RU 2014106733A
- Authority
- RU
- Russia
- Prior art keywords
- copper
- desulfurizing
- zinc oxide
- material according
- binders
- Prior art date
Abstract
1. Зернистый десульфирующий материал, содержащий одно или более соединений меди, нанесенных на зернистый оксид цинка как материал носителя, причем данный десульфирующий материал присутствует в форме гранул, которые составляют одно или более порошкообразных соединений меди, оксид цинка, причем оксид цинка получают прокаливанием одного или более предшественников оксида цинка, и одно или более связующих веществ, и имеет содержание меди, в пересчете на CuO, от 0,1 до 5,0 мас.% и насыпную плотность после уплотнения не менее чем 1,55 кг/л.2. Десульфирующий материал по п. 1, причем у данного десульфирующего материала размер частиц составляет от 1 до 10 мм, предпочтительно от 1,5 до 7,5 мм, предпочтительнее от 2,5 до 5,0 мм.3. Десульфирующий материал по п. 1, причем у данного десульфирующего материала удельный объем пор составляет не более чем 0,22 см/г.4. Десульфирующий материал по п. 1, причем у данного десульфирующего материала удельная площадь поверхности по методу BET составляет не более чем 23 м/г.5. Десульфирующий материал по п. 1, в котором одно или более соединений меди выбирают из группы, состоящей из металлической меди, оксида меди, гидроксида меди и гидрокарбоната меди.6. Десульфирующий материал по п. 1, в котором одно или более связующих веществ выбраны из группы, состоящей из глинистых связующих веществ и цементных связующих веществ, а также их смесей.7. Десульфирующий материал по п. 1, причем данный десульфирующий материал дополнительно содержит второй материал носителя, в качестве которого выбирают один или более тугоплавких оксидов, составляющих вплоть до 20 мас.%.8. Десульфирующий материал по п. 1, причем данный десульфирующий материал
Claims (15)
1. Зернистый десульфирующий материал, содержащий одно или более соединений меди, нанесенных на зернистый оксид цинка как материал носителя, причем данный десульфирующий материал присутствует в форме гранул, которые составляют одно или более порошкообразных соединений меди, оксид цинка, причем оксид цинка получают прокаливанием одного или более предшественников оксида цинка, и одно или более связующих веществ, и имеет содержание меди, в пересчете на CuO, от 0,1 до 5,0 мас.% и насыпную плотность после уплотнения не менее чем 1,55 кг/л.
2. Десульфирующий материал по п. 1, причем у данного десульфирующего материала размер частиц составляет от 1 до 10 мм, предпочтительно от 1,5 до 7,5 мм, предпочтительнее от 2,5 до 5,0 мм.
3. Десульфирующий материал по п. 1, причем у данного десульфирующего материала удельный объем пор составляет не более чем 0,22 см3/г.
4. Десульфирующий материал по п. 1, причем у данного десульфирующего материала удельная площадь поверхности по методу BET составляет не более чем 23 м2/г.
5. Десульфирующий материал по п. 1, в котором одно или более соединений меди выбирают из группы, состоящей из металлической меди, оксида меди, гидроксида меди и гидрокарбоната меди.
6. Десульфирующий материал по п. 1, в котором одно или более связующих веществ выбраны из группы, состоящей из глинистых связующих веществ и цементных связующих веществ, а также их смесей.
7. Десульфирующий материал по п. 1, причем данный десульфирующий материал дополнительно содержит второй материал носителя, в качестве которого выбирают один или более тугоплавких оксидов, составляющих вплоть до 20 мас.%.
8. Десульфирующий материал по п. 1, причем данный десульфирующий материал дополнительно содержит второе соединение металла, в качестве которого выбирают одно или более соединений железа, марганца, кобальта или никеля, предпочтительно никеля.
9. Способ получения десульфирующего материала по любому из п.п. 1-8, включающий следующие стадии:
(i) смешивание порошкообразного соединения меди с зернистым цинковым материалом носителя, содержащим оксид цинка и один или более предшественников, которые образуют оксид цинка в результате прокаливания, для получения содержащей медь композиции,
(ii) формование содержащей медь композиции гранулированием и
(iii) высушивание и прокаливание полученного в результате гранулирования материала.
10. Способ по п. 9, в котором соединение меди выбирают из группы, состоящей из оксида меди, гидроксида меди, нитрата меди, ацетата меди или гидрокарбоната меди.
11. Способ по п. 9, в котором соединение меди и оксид цинка как материал носителя объединяют с одним или несколькими связующими веществами и гранулируют, образуя агломерированные сферы диаметром от 1 до 10 мм, предпочтительно от 1,5 до 7,5 мм и предпочтительнее от 2,5 до 5,0 мм.
12. Способ десульфирования потока технологической текучей среды, включающий контакт потока и необязательно водорода с десульфирующим материалом, описанным в п. 1 или полученным по любому из п.п. 9-11.
13. Способ по п. 12, в котором технологический поток содержит газообразный углеводород и водород.
14. Способ по п. 12, в котором поток технологической текучей среды смешивают с водородом и приводят в контакт с катализатором гидродесульфирования, получая обработанный технологический поток, и затем обработанный технологический поток приводят в контакт с десульфирующим материалом.
15. Способ по п. 12, в котором десульфирующий материал приводят в контакт с технологической текучей средой при температуре от 250 до 450°C, предпочтительно от 300 до 400°C и предпочтительнее от 320 до 400°C.