RU2012121580A - Устойчивые к тепловому старению полиамиды с огнезащитой - Google Patents
Устойчивые к тепловому старению полиамиды с огнезащитой Download PDFInfo
- Publication number
- RU2012121580A RU2012121580A RU2012121580/04A RU2012121580A RU2012121580A RU 2012121580 A RU2012121580 A RU 2012121580A RU 2012121580/04 A RU2012121580/04 A RU 2012121580/04A RU 2012121580 A RU2012121580 A RU 2012121580A RU 2012121580 A RU2012121580 A RU 2012121580A
- Authority
- RU
- Russia
- Prior art keywords
- thermoplastic molding
- molding materials
- component
- materials according
- butyl
- Prior art date
Abstract
1. Термопластические формовочные массы, содержащиеA) от 10 до 98 мас.%, полиамида;B) 0,001-20 мас.%, железного порошка с размером частиц максимум 10 мкм (величина d) и удельной площадью ВЕТ-поверхности 0,1-5 м/г согласно DIN ISO 9277;C) от 1 до 40 мас.%, не содержащего галогенов огнезащитного средства из группы фосфорсодержащих или азотсодержащих соединений, или P-N-конденсатов, или их смесей;D) от 0 до 70 мас.%, других добавок,причем сумма массовых процентных долей компонентов А)-D) составляет 100%.2. Термопластические формовочные массы по п.1, содержащие в качестве компонента D3) от 0,05 до 3 мас.%. Cu-стабилизатора или стерически затрудненного фенола или их смеси.3. Термопластические формовочные массы по п.1, у которых компонент В) имеет значение dот 1 до 5 мкм.4. Термопластические формовочные массы по п.1, у которых компонент В) имеет значение dот 3 до 35 мкм.5. Термопластические формовочные массы по п.1, у которых содержание углерода в компоненте В) составляет от 0,05 до 1,2 г/100 г (согласно ASTM Е 1019).6. Термопластические формовочные массы по п.1, у которых компонент В) получают термическим разложением пентакарбонила железа.7. Термопластические формовочные массы по п.1, у которых компонент В) имеет плотность после утряски от 2,5 до 5 г/см.8. Термопластические формовочные массы по пп.1-7, у которых компонент С) сформирован из солей фосфиновой кислоты формулы (I), и/или солей дифосфиновой кислоты формулы (II), и/или их полимеровпричем заместители имеют следующие значения:R, Rводород, алкил с 1-8 атомами углерода, предпочтительно алкил с 1-4 атомами углерода, линейный или разветвленный, например, метил, этил, н-пропил, изопропил, н-бутил, трет-бутил, н-пентил; фенил; причем предпочтительно,
Claims (10)
1. Термопластические формовочные массы, содержащие
A) от 10 до 98 мас.%, полиамида;
B) 0,001-20 мас.%, железного порошка с размером частиц максимум 10 мкм (величина d50) и удельной площадью ВЕТ-поверхности 0,1-5 м2/г согласно DIN ISO 9277;
C) от 1 до 40 мас.%, не содержащего галогенов огнезащитного средства из группы фосфорсодержащих или азотсодержащих соединений, или P-N-конденсатов, или их смесей;
D) от 0 до 70 мас.%, других добавок,
причем сумма массовых процентных долей компонентов А)-D) составляет 100%.
2. Термопластические формовочные массы по п.1, содержащие в качестве компонента D3) от 0,05 до 3 мас.%. Cu-стабилизатора или стерически затрудненного фенола или их смеси.
3. Термопластические формовочные массы по п.1, у которых компонент В) имеет значение d10 от 1 до 5 мкм.
4. Термопластические формовочные массы по п.1, у которых компонент В) имеет значение d90 от 3 до 35 мкм.
5. Термопластические формовочные массы по п.1, у которых содержание углерода в компоненте В) составляет от 0,05 до 1,2 г/100 г (согласно ASTM Е 1019).
6. Термопластические формовочные массы по п.1, у которых компонент В) получают термическим разложением пентакарбонила железа.
7. Термопластические формовочные массы по п.1, у которых компонент В) имеет плотность после утряски от 2,5 до 5 г/см3.
8. Термопластические формовочные массы по пп.1-7, у которых компонент С) сформирован из солей фосфиновой кислоты формулы (I), и/или солей дифосфиновой кислоты формулы (II), и/или их полимеров
причем заместители имеют следующие значения:
R1, R2 водород, алкил с 1-8 атомами углерода, предпочтительно алкил с 1-4 атомами углерода, линейный или разветвленный, например, метил, этил, н-пропил, изопропил, н-бутил, трет-бутил, н-пентил; фенил; причем предпочтительно, чтобы по меньшей мере один остаток R1 или R2, в частности R1 и R2, представлял собой водород;
R3 алкилен, с 1-10 атомами углерода, линейный или разветвленный, например, метилен, этилен, н-пропилен, изопропилен, н-бутилен, трет-бутилен, н-пентилен, н-октилен, н-додецилен;
арилен, например, фенилен, нафтилен;
алкиларилен, например, метил-фенилен, этил-фенилен, трет-бутил-фенилен, метил-нафтилен, этил-нафтилен, трет-бутил-нафтилен;
арилалкилен, например, фенил-метилен, фенил-этилен, фенил-пропилен, фенил-бутилен;
М щелочноземельный или щелочной металл, Al, Zn, Fe, бор;
m целое число от 1 до 3;
n целое число от 1 до 3 и
x 1 или 2.
9. Применение термопластических формовочных масс по пп.1-8 для изготовления волокон, пленок и формованных изделий.
10. Волокна, пленки и формованные изделия, получаемые из термопластических формовочных масс по пп.1-8.