RU2005136360A - Лист поливинилбутираля с антиадгезионными характеристиками - Google Patents

Лист поливинилбутираля с антиадгезионными характеристиками Download PDF

Info

Publication number
RU2005136360A
RU2005136360A RU2005136360/04A RU2005136360A RU2005136360A RU 2005136360 A RU2005136360 A RU 2005136360A RU 2005136360/04 A RU2005136360/04 A RU 2005136360/04A RU 2005136360 A RU2005136360 A RU 2005136360A RU 2005136360 A RU2005136360 A RU 2005136360A
Authority
RU
Russia
Prior art keywords
polymer sheet
polymer
amide
fatty acid
sheet according
Prior art date
Application number
RU2005136360/04A
Other languages
English (en)
Other versions
RU2351619C2 (ru
Inventor
Пин ЮАНЬ (US)
Пин ЮАНЬ
Джон Д`ЭРРИКО (US)
Джон Д`ЭРРИКО
Original Assignee
Солютиа Инкорпорейтед (Us)
Солютиа Инкорпорейтед
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Солютиа Инкорпорейтед (Us), Солютиа Инкорпорейтед filed Critical Солютиа Инкорпорейтед (Us)
Publication of RU2005136360A publication Critical patent/RU2005136360A/ru
Application granted granted Critical
Publication of RU2351619C2 publication Critical patent/RU2351619C2/ru

Links

Classifications

    • CCHEMISTRY; METALLURGY
    • C08ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08JWORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J5/00Manufacture of articles or shaped materials containing macromolecular substances
    • C08J5/18Manufacture of films or sheets
    • CCHEMISTRY; METALLURGY
    • C08ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08KUse of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00Use of organic ingredients
    • C08K5/16Nitrogen-containing compounds
    • C08K5/20Carboxylic acid amides
    • BPERFORMING OPERATIONS; TRANSPORTING
    • B32LAYERED PRODUCTS
    • B32BLAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/10009Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the number, the constitution or treatment of glass sheets
    • B32B17/10036Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the number, the constitution or treatment of glass sheets comprising two outer glass sheets
    • BPERFORMING OPERATIONS; TRANSPORTING
    • B32LAYERED PRODUCTS
    • B32BLAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B17/00Layered products essentially comprising sheet glass, or glass, slag, or like fibres
    • B32B17/06Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
    • B32B17/10Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
    • B32B17/10005Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
    • B32B17/1055Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
    • B32B17/10761Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer containing vinyl acetal
    • CCHEMISTRY; METALLURGY
    • C08ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08FMACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
    • C08F8/00Chemical modification by after-treatment
    • C08F8/28Condensation with aldehydes or ketones
    • YGENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10TTECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00Stock material or miscellaneous articles
    • Y10T428/31504Composite [nonstructural laminate]
    • Y10T428/31551Of polyamidoester [polyurethane, polyisocyanate, polycarbamate, etc.]
    • YGENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10TTECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00Stock material or miscellaneous articles
    • Y10T428/31504Composite [nonstructural laminate]
    • Y10T428/31551Of polyamidoester [polyurethane, polyisocyanate, polycarbamate, etc.]
    • Y10T428/31627Next to aldehyde or ketone condensation product

Landscapes

  • Chemical & Material Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Manufacturing & Machinery (AREA)
  • Engineering & Computer Science (AREA)
  • General Chemical & Material Sciences (AREA)
  • Materials Engineering (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
  • Laminated Bodies (AREA)
  • Adhesives Or Adhesive Processes (AREA)
  • Joining Of Glass To Other Materials (AREA)
  • Manufacture Of Macromolecular Shaped Articles (AREA)
  • Application Of Or Painting With Fluid Materials (AREA)
  • Treatments Of Macromolecular Shaped Articles (AREA)
  • Protection Of Plants (AREA)
  • Extrusion Moulding Of Plastics Or The Like (AREA)

Claims (30)

1. Лист полимера, содержащий амид жирной кислоты в качестве антиадгезионной добавки, при этом данный лист полимера имеет силу слипания по меньшей мере на 50% меньше, чем сила слипания листа полимера того же состава, но без амида жирной кислоты и имеет меньше 3% мутности и величину адгезии в пределах 20% отклонения от величины адгезии листа полимера того же состава, но без амидной добавки.
2. Лист полимера по п.1, в котором указанный амид является моноамидом жирной кислоты.
3. Лист полимера по п.1, в котором указанный амид является амидом жирной кислоты, содержащим углеводородную цепь, имеющую от примерно 12 до примерно 40 атомов углерода.
4. Лист полимера по п.3, в котором указанный амид жирной кислоты выбирают из группы, состоящей из эрукамида, бегенамида, олеилпальмитамида, стеарилэрукамида, эруцилстеарамида, гидроксистеарамида, диэтаноламида олеиновой кислоты, диэтаноламида стеариновой кислоты, полиэтиленгликоль олеамида, стеарамида, и комбинации состоящей из по меньшей мере одного из вышеупомянутых амидов и им подобных амидов.
5. Лист полимера по п.2, в котором указанный полимер является поливинилбутиралем.
6. Лист полимера по п.2, в котором моноамид жирной кислоты является вторичным амидом.
7. Лист полимера по п.4, в котором моноамид жирной кислоты является олеилпальмитамидом.
8. Лист полимера по п.7, в котором общее количество олеилпальмитамида, используемое как добавка, составляет 0,001-1 мас.%.
9. Лист полимера по п.8, в котором общее количество олеилпальмитамида, используемое как добавка, составляет 0,01-0,6 мас.%.
10. Лист полимера по п.9, в котором общее количество олеилпальмитамида, используемое как добавка, составляет 0,1-0,3 мас.%.
11. Лист полимера по п.1, в котором полимер выбирают из группы, состоящей из поливинилбутираля, полиуретана, поливинилхлорида, поли(этиленвинилацетата), их комбинации и им подобных полимеров.
12. Лист полимера по п.10, в котором полимер является поливинилбутиралем.
13. Лист полимера по п.12, в котором полимер является пластифицированным поливинилбутиралем, в котором пластификатор содержит примерно 20-80 частей пластификатора на сто частей смолы.
14. Лист полимера по п.13, в котором полимер является пластифицированным поливинилбутиралем, в котором пластификатор содержит примерно 25-60 частей пластификатора на сто частей смолы.
15. Лист полимера по п.14, в котором полимер является пластифицированным поливинилбутиралем, в котором пластификатор выбирают из группы, состоящей из ди-(2-этилбутирата) триэтиленгликоля, ди-(2-этилгексаноата) триэтиленгликоля, дигептаноата триэтиленгликоля, дигептаноата тетраэтиленгликоля, дигексиладипата, диоктиладипата, гексил(циклогексил)адипата, смеси гептил- и нониладипатов, диизонониладипата, гептил(нонил)адипата, дибутилсебацината и их смеси.
16. Способ изготовления листа полимера, предусматривающий смешивание амида жирной кислоты, содержащего углеводородную цепь, имеющую от примерно 12 до примерно 40 атомов углерода, с полимером для придания поверхности указанного листа полимера свойств противодействия слипанию.
17. Способ изготовления листа полимера по п.16, в котором амид жирной кислоты смешивают с полимером путем выработки листа полимера экструзией расплава и нанесения амида на поверхность листа.
18. Способ изготовления листа полимера по п.16, в котором амид жирной кислоты смешивают с полимером путем введения амида в экструдируемую загрузку расплавленного полимера.
19. Способ изготовления листа полимера по п.18, в котором амид жирной кислоты смешивают с полимером путем введения амида в форме шариков в экструдируемую загрузку расплавленного полимера.
20. Способ изготовления листа полимера по п.18, в котором амид жирной кислоты смешивают с полимером путем введения амида в экструдируемую загрузку расплавленного полимера диспергированием указанного амида в пластификаторе.
21. Способ по п.17, в котором указанное нанесение указанного амида на поверхность указанного листа полимера выполняют методом, выбранным из группы, состоящей из методов покрытия распылением, методов погружения, методов экструзии, методов рифления покрытия и комбинации предыдущих методов.
22. Способ по п.17, в котором указанный метод покрытия распылением включает распределение указанного амида в жидком носителе, тонкое измельчение смеси указанного амида и указанного жидкого носителя, выбрасывание указанной измельченной смеси на указанный лист полимера и улетучивание указанного жидкого носителя с поверхности указанного листа полимера.
23. Способ по п.17, в котором указанный метод погружения включает погружение указанного листа полимера в жидкость, несущую указанный амид, вынимание указанного листа полимера и улетучивание указанного жидкого носителя с поверхности указанного листа полимера.
24. Способ по п.17, в котором указанный метод экструзии рифленого покрытия включает распределение указанного амида в жидком носителе, перенос жидкого носителя, содержащего указанный амид, на указанный лист полимера, когда полимер плавят, используя аппарат для нанесения рифленого покрытия, и удаление указанного носителя с поверхности указанного листа полимера при экструдировании указанного расплавленного полимера и указанного амида через листовую головку.
25. Способ по п.16, в котором указанный полимер является поливинилбутиралем.
26. Способ по п.25, в котором указанный амид является амидом жирной кислоты, содержащим углеводородную цепь, имеющую от примерно 12 до примерно 40 атомов углерода.
27. Способ по п.26, в котором указанный моноамид жирной кислоты выбирают из группы, состоящей из эрукамида, бегенамида, олеилпальмитамида, стеарилэрукамида, эруцилстеарамида, гидроксистеарамида, N,N'-этиленбисолеамида, N,N'-этиленбисстеарамида, диэтаноламида олеиновой кислоты, диэтаноламида стеариновой кислоты, полиэтиленгликоль олеамида, стеарамида, и комбинации,содержащей по меньшей мере один из вышеупомянутых амидов и им подобных амидов.
28. Способ по п.26, в котором амид жирной кислоты является вторичным амидом.
29. Способ по п.28, в котором моноамид жирной кислоты является олеилпальмитамидом.
30. Ламинированное небьющееся стекло, содержащее два листа стекла и промежуточный лист полимера, расположенный между ними, в котором лист полимера включает моноамид жирной кислоты в качестве антиадгезионного средства, включенного в лист.
RU2005136360A 2003-05-01 2004-04-29 Лист поливинилбутираля с противослипающими свойствами RU2351619C2 (ru)