RU2002105507A - Изделие из стекла с солнцезащитным покрытием - Google Patents
Изделие из стекла с солнцезащитным покрытиемInfo
- Publication number
- RU2002105507A RU2002105507A RU2002105507/03A RU2002105507A RU2002105507A RU 2002105507 A RU2002105507 A RU 2002105507A RU 2002105507/03 A RU2002105507/03 A RU 2002105507/03A RU 2002105507 A RU2002105507 A RU 2002105507A RU 2002105507 A RU2002105507 A RU 2002105507A
- Authority
- RU
- Russia
- Prior art keywords
- tin oxide
- coated glass
- thickness
- glass substrate
- coating
- Prior art date
Links
- 239000011521 glass Substances 0.000 title claims 45
- 239000011248 coating agent Substances 0.000 claims 19
- 238000000576 coating method Methods 0.000 claims 19
- XOLBLPGZBRYERU-UHFFFAOYSA-N Tin dioxide Chemical compound O=[Sn]=O XOLBLPGZBRYERU-UHFFFAOYSA-N 0.000 claims 18
- 239000000758 substrate Substances 0.000 claims 18
- 229910001887 tin oxide Inorganic materials 0.000 claims 18
- 238000002834 transmittance Methods 0.000 claims 12
- WATWJIUSRGPENY-UHFFFAOYSA-N antimony Chemical compound [Sb] WATWJIUSRGPENY-UHFFFAOYSA-N 0.000 claims 10
- 229910052787 antimony Inorganic materials 0.000 claims 10
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 claims 6
- 238000001228 spectrum Methods 0.000 claims 4
- 235000012239 silicon dioxide Nutrition 0.000 claims 3
- 239000000377 silicon dioxide Substances 0.000 claims 3
- NPNMHHNXCILFEF-UHFFFAOYSA-N [F].[Sn]=O Chemical compound [F].[Sn]=O NPNMHHNXCILFEF-UHFFFAOYSA-N 0.000 claims 2
- 239000002131 composite material Substances 0.000 claims 2
- 229910052731 fluorine Inorganic materials 0.000 claims 2
- 239000011737 fluorine Substances 0.000 claims 2
- YCKRFDGAMUMZLT-UHFFFAOYSA-N fluorine atom Chemical compound [F] YCKRFDGAMUMZLT-UHFFFAOYSA-N 0.000 claims 2
- 230000001264 neutralization Effects 0.000 claims 2
- 230000037250 Clearance Effects 0.000 claims 1
- 210000000554 Iris Anatomy 0.000 claims 1
- 230000035512 clearance Effects 0.000 claims 1
- 230000003287 optical Effects 0.000 claims 1
- 230000001629 suppression Effects 0.000 claims 1
- ATJFFYVFTNAWJD-UHFFFAOYSA-N tin hydride Chemical compound [Sn] ATJFFYVFTNAWJD-UHFFFAOYSA-N 0.000 claims 1
Claims (23)
1. Стеклянное изделие с покрытием, включающее а) стеклянную подложку, б) покрытие из легированного сурьмой оксида олова, нанесенное и связанное со стеклянной подложкой, и в) покрытие из легированного фтором оксида олова, нанесенное и связанное с покрытием из легированного сурьмой оксида олова, причем толщину этих покрытий выбирают таким образом, чтобы стеклянное изделие с покрытием проявляло разницу между коэффициентом пропускания видимого света (источник света С) и общим коэффициентом пропускания солнечной энергии, интегрированным с воздушной массой 1,5 на прозрачной стеклянной подложке при номинальной толщине 3 мм, обеспечивающую селективность 13 или больше.
8. Стеклянное изделие с покрытием по п.1, у которого коэффициент излучения этого стеклянного изделия с покрытием меньше или равен примерно 0,2.
9. Стеклянное изделие с покрытием по п.8, у которого коэффициент излучения этого стеклянного изделия с покрытием меньше или равен примерно 0,15.
10. Стеклянное изделие с покрытием по п.1, у которого стеклянная подложка представляет собой прозрачную стеклянную флоат-ленту.
11. Стеклянное изделие с покрытием по п.1, у которого это изделие в отраженном свете со стороны стеклянной подложки проявляет нейтральный цветовой оттенок, значение а* которого равно от примерно 0 до примерно -6 и значение b* составляет от примерно 0 до примерно -6, как это устанавливают по шкале оценки цвета в системе CIELAB.
12. Стеклянное изделие с покрытием по п.1, у которого значение молярного соотношения между сурьмой и оловом в покрытии из легированного сурьмой оксида олова находится в пределах от примерно 0,05 до 0,12.
13. Стеклянное изделие с покрытием по п.1, у которого коэффициент пропускания излучения в видимой области спектра (источник света С) этого стеклянного изделия с покрытием составляет 63% или больше, а общий коэффициент пропускания солнечной энергии, интегрированный с воздушной массой 1,5, на прозрачной стеклянной подложке при номинальной толщине 3 мм равен 53% или меньше.
14. Стеклянное изделие с покрытием по п.1, у которого коэффициент пропускания излучения в видимой области спектра (источник света С) этого стеклянного изделия с покрытием составляет 59% или больше, а общий коэффициент пропускания солнечной энергии, интегрированный с воздушной массой 1,5, на прозрачной стеклянной подложке при номинальной толщине 3 мм равен 49% или меньше.
15. Стеклянное изделие с покрытием по п.1, далее включающее подавляющий иризирование промежуточный слой между стеклянной подложкой и покрытием из легированного сурьмой оксида олова.
16. Стеклянное изделие с покрытием по п.15, где коэффициент пропускания излучения в видимой области спектра (источник света С) этого стеклянного изделия с покрытием составляет 63% или больше, а общий коэффициент пропускания солнечной энергии, интегрированный с воздушной массой 1,5, на прозрачной стеклянной подложке при номинальной толщине 3 мм равен 53% или меньше, и где оно в отраженном свете со стороны стеклянной подложки проявляет нейтральный цветовой оттенок, значение а* которого равно от примерно 0 до примерно -6 и значение b* составляет от примерно 0 до примерно -6, как это устанавливают по шкале оценки цвета в системе CIELAB.
17. Стеклянное изделие с покрытием по п.15, у которого подавляющий иризирование промежуточный слой включает слой из нелегированного оксида олова и слой диоксида кремния, нанесенный и связанный с этим слоем из нелегированного оксида олова.
18. Стеклянное изделие с покрытием по п.17, у которого общая оптическая толщина слоя нелегированного оксида олова и слоя диоксида кремния составляет от 1/6 до 1/12 расчетной длины волны 500 нм.
20. Стеклопакет, включающий а) первую стеклянную подложку, б) вторую стеклянную подложку, у которой имеются внутренняя поверхность и внешняя поверхность, причем эта вторая стеклянная подложка прочно связана с первой стеклянной подложкой с некоторым зазором между ними, а ее внутренняя поверхность обращена к первой стеклянной подложке, и в) многослойное композитное покрытие, нанесенное и связанное с внутренней поверхностью второй стеклянной подложки, причем это многослойное композитное покрытие включает (I) покрытие из легированного сурьмой оксида олова, нанесенное и связанное с внутренней поверхностью, причем толщина этого покрытия из легированного сурьмой оксида олова находится в пределах от примерно 1400 до 1900, и (II) покрытие из легированного фтором оксида олова, нанесенное и связанное с покрытием из легированного сурьмой оксида олова, причем толщина этого покрытия из легированного фтором оксида олова находится в пределах от примерно 2200 до 3500; это многослойное покрытие таково, что вторая стеклянная подложка проявляет такую разницу между коэффициентом пропускания излучения в видимой области спектра (источник света С) и общим коэффициентом пропускания солнечной энергии, интегрированным с воздушной массой 1,5, на прозрачной стеклянной подложке при номинальной толщине 3 мм, которая обеспечивает селективность 13 или больше.
21. Стеклопакет по п.20, где показатель U этого стеклопакета составляет меньше 0,4.
22. Стеклопакет по п.20, где показатель U этого стеклопакета по крайней мере на 15% меньше показателя U у стеклопакета такой же конструкции, в котором использовано два оконных стекла без покрытия.
23. Стеклопакет по п.20, в котором общий коэффициент пропускания солнечной энергии по крайней мере на 25% меньше общего коэффициента пропускания солнечной энергии у стеклопакета такой же конструкции, в котором использовано два оконных стекла без покрытия.