PT768284E - Conjunto de vidracas montadas sobre um veiculo automovel - Google Patents
Conjunto de vidracas montadas sobre um veiculo automovel Download PDFInfo
- Publication number
- PT768284E PT768284E PT96120971T PT96120971T PT768284E PT 768284 E PT768284 E PT 768284E PT 96120971 T PT96120971 T PT 96120971T PT 96120971 T PT96120971 T PT 96120971T PT 768284 E PT768284 E PT 768284E
- Authority
- PT
- Portugal
- Prior art keywords
- glazing
- total iron
- coo
- colored glass
- glasses
- Prior art date
Description
DESCRIÇÃO EPÍGRAFE : “CONJUNTO DE VIDRAÇAS MONTADAS SOBRE UM VEÍCULO AUTOMÓVEL” A presente invenção reporta-se a uma composição de vidro colorida destinada à fabricação de uma vidraça susceptível, nomeadamente, de ser montada sobre um veículo automóvel. Ela visa mais particularmente uma composição de vidro permitindo realizar uma vidraça susceptível de formar as vidraças laterais traseiras e os óculos traseiros de um veículo automóvel.
Os construtores de automóveis propõem vidraças coloridas aos seus clientes, não sómente por uma preocupação de ordem estética mas também pelo papel funcional que elas podem desempenhar, a saber, nomeadamente a melhoria da visibilidade nas condições críticas de iluminação, e/ou o conforto dos passageiros.
Sob este último aspecto, a proporção de superfície envidraçada progredindo cada ano sobre os novos modelos, o efeito de estufa constitui em consequência um factor importante a tomar em conta na climatização do veículo. Um dos caminhos visando reduzir o dito efeito reside na preparação de vidraças de fraca transmissão para as irradiações próximo do infravermelho, mas cuja transmissão para o espectro do 1
visível, embora inferior àquela dos pára-brisas clássicos, seja ainda aceitável para os passageiros. A patente US-A-4 104 076 propõe vidros à base de óxidos de ferro, de cobalto, de cromo e/ou de urânio e contendo eventualmente selénio. Estes vidros classificam-se em duas categorias : os vidros bronze que apresentam um factor de transmissão luminosa entre 40 e 55 %, os vidros cinzentos para os quais este factor é compreendido entre 35 e 45 %. Estes vidros; mais particularmente destinados à realização de vidraças para edifícios, apresentam um factor de transmissão energético global clássico inferior a 50 % para uma espessura de 6,2 mm. O pedido de patente EP-A-0 349 909 propõe vidros de aparência cinzenta à base de óxidos de ferro e de cobalto aos quais se acrescenta pelo menos 30 ppm de selénio. Estes vidros caracterizam-se, por uma espessura de 5,56 mm, por um factor de transmissão luminosa compreendida entre 5 e 20 % e um factor de transmissão energética global inferior a 40 %. Todos os vidros dados a título de exemplo apresentam um factor de transmissão energética superior ao factor de transmissão luminosa. O pedido de patente EP-A-0 482 535 propõe vidros de aparência escura particularmente adaptada para a realização de tectos de veículos automóveis. Os óxidos de ferro e de cobalto acompanhados de selénio coloram estes vidros que se caracterizam por uma fraca transmissão luminosa (igual ou inferior a 32 %) e uma muito fraca transmissão energética (inferior a 15 %) sob uma espessura de 3,9 mm. 2 O pedido de patente US-A 4 190 452 divulga vidros bronze neutros cuja coloração é provocada por óxidos de ferro e de cobalto, por selénio e, eventualmente, por óxidos de níquel e de cromo. Estes vidros caracterizam-se por uma fraca transmissão luminosa superior a 70 % sob uma espessura de 3 mm, uma pureza de excitação compreendida entre 2 e 6 % e um comprimento de onda dominante variante entre 570 e 580 nm. A patente US-A 4 866 010 descreve vidros utilizáveis tanto na construção como na industria automóvel. Trata-se de vidros azuis cuja coloração é obtida por meio de óxidos de ferro e de cobalto e por selénio. Sob uma espessura de 6,35 mm eles possuem uma transmissão luminosa na ordem de 54 %. A patente FR-A 2 074 983 descreve vidros de cor cinzenta cujos agentes de coloração são igualmente óxidos de ferro e de cobalto acompanhados de selénio. Estes vidros que possuem uma fraca pureza de excitação (inferior a 1,5 %), têm, sob uma espessura de 5 mm, uma transmissão luminosa e uma transmissão energética compreendida entre 57 e 63 %. A patente US-A 3 296 004 descreve vidros bronze neutros mais particularmente destinados à construção. Sob uma espessura de 6,35 mm, eles possuem uma transmissão luminosa compreendida entre 48 e 56 % e uma transmissão energética inferior a 50 %. A coloração destes vidros é devida à presença de selénio e de óxido de ferro e de cobalto. 3 A presente invenção propõe fornecer um conjunto de vidraças montadas sobre um veículo automóvel, compreendendo um pára-brisas, laterais dianteiros e traseiros e um óculo traseiro, no qual as vidraças laterais traseiras e o óculo são realizados a partir de vidros coloridos na massa que apresentam, para uma espessura determinada, uma transmissão luminosa global moderada e uma transmissão energética global correspondente inferior. A invenção propõe igualmente fornecer um conjunto de vidraças no qual as vidraças laterais traseiras e o óculo são realizados a partir de vidros coloridos de composições diferentes.
Conforme a invenção, estes objectivos são atingidos graças a um conjunto de vidraças segundo a reivindicação 1.
As composições formando estas vidraças podem conter outros constituintes em muito pequenas quantidades, proveniente de compostos acrescentados à mistura vitrificável para facilitar a afinação do vidro. É o caso, por exemplo, de S03 proveniente da decomposição de sulfato acrescentado à mistura.
Os vidros formando estas vidraças podem ser elaborados nos fornos clássicos e transformados em tira contínua pela técnica bem conhecida do vidro flotté sobre banho de estanho. 4
Os vidros formando estas vidraças apresentam uma pureza de excitação sob iluminante C pouco elevada. Ela é geralmente inferior a 15 % e geralmente inferior a 12 %.
As características de transmissão de vidros formando estas vidraças assim como o seu comprimento de onda dominante sob iluminante C são regidos pelo seu estado de óxido-reducção. De acordo com a presente invenção 16 a 55 % do ferro total, expresso sob forma de Fe2C>3 pode ser sob forma de óxido ferroso. Mais geralmente, 20 a 40 % do ferro total é sob a forma de óxido ferroso.
Os vidros formando estas vidraças apresentam aparências cinzentas e colorações mais ou menos neutras, susceptíveis de variar do azul/verde ao verde/amarelo passando por todas as tonalidades intermédias, correspondendo aos comprimentos de onda dominantes sob iluminante C compreendidos entre 490 e 560 nm.
Os vidros formando estas vidraças apresentam características de transmissão desejadas utilizando como agentes corantes os óxidos de ferro e de cobalto, em acrescentando, o óxido de cromo e eventualmente selénio, este último tendo por efeito diminuir a pureza de excitação.
Os vidros formando estas vidraças podem compreender uma parte únicamente desses agentes corantes ou a totalidade desses agentes nas proporções devidamente escolhidas em função das características procuradas.
Assim os vidros formando estas vidraças podem compreender como agentes corantes os óxidos de ferro e de cobalto e, eventualmente, selénio. Os teores ponderais dos agentes corantes dos vidros preferidos da invenção pertencendo a esta família podem variar em função das características procuradas.
Os vidros apresentando uma aparência cinzenta e caracterizando-se por um factor de transmissão luminoso elevado (TLA > 40 %) compreendem os agentes corantes seguintes nos limites ponderais assim definidos : (l) Fe2C>3 (ferro total) CoO Se 0,45 a 1 % 0,001 a 0,01 % 0,0002 a 0,002 %
Os vidros apresentando igualmente uma aparência cinzenta mas caracterizando-se por um factor de transmissão luminoso mais fraco (TLa < 40 %) e um factor Te claramente inferior àquele dos vidros (i) compreendem os agentes corantes seguintes nos limites ponderais definidos como segue : (II) Fe203 (ferro total) CoO Se 1 a 1,8% 0,005 a 0,02 % 0,0005 a 0,0025 %
Entre os vidros pertencendo a esta família mas que eventualmente não contêm o 6 selénio, pode-se distinguir os vidros que apresentam um factor TLa elevado (> 40 %) e um factor Te relativamente fraco. Tais vidros compreendem agentes corantes mais abaixo definidos nos limites ponderais seguintes : (III) Fe203 (ferro total) CoO 0,8 a 1,8% 0,001 a 0,01 %
Sempre na categoria dos vidros não contendo eventualmente o selénio, pode-se igualmente definir vidros que apresentam um factor TLA e um factor TE claramente inferiores àqueles dos vidros precedentes (III). Estes vidros compreendem um teor elevado em óxidos de ferro associados ao óxido de cobalto nas proporções ponderais seguintes : (IV) Fe203 (ferro total) CoO 1,3 a 2,5% 0,005 a 0,015%
Os vidros (III) e (IV) podem evidentemente compreender o selénio, nos limites gerais precedentemente definidos.
Para preparar os vidros da invenção, utiliza-se como composição de base uma composição de vidro tradicional na industria do vidro plano, na qual se acrescenta os agentes corantes segundo as proporções que permitam, para uma espessura 7 determinada, obter as características ópticas e a aparência procuradas. O vidro de base escolhido tem a composição ponderai seguinte : SÍ02 72,1 % AI203 0,74 % CaO 8,90 % MgO 3,79 % Na20 14,16 % K20 0,11 % S03 0,20 %
Os agentes corantes são acrescentados no vidro em detrimento da sílica. O quadro em anexo apresenta uma série de exemplos de composições de vidro ilustrando a invenção. Os teores em agentes corantes são expressos em percentagens ponderais. Os valores das diferentes características destes vidros foram medidas sobre vidraças de 3,85 milímetros de espessura. O nível de pureza atingida por certos vidros de acordo com a invenção é notável tendo em conta o muito fraco teor em selénio desses vidros. Para a totalidade dos vidros de acordo com a invenção a relação Fe0203 (total)/Se é superior a 200.
Como indicado precedentemente, os vidros de acordo com a invenção podem ser transformados em tira contínua pela técnica do vidro flotté. As chapas de vidro obtidas por corte dessa tira apresentam espessuras variando entre aproximadamente 2 e 8 mm. Estas chapas de vidro podem ser utilizadas sozinhas ou associadas a uma 8 chapa de vidro não colorida para realizar as vidraças susceptíveis de ser montadas sobre um veículo automóvel como vidraças laterais traseiras e do óculo traseiro.
Estas vidraças podem ser montadas em as associando num conjunto com outras vidraças que formam o pára-brisas e os laterais dianteiros. É assim que um conjunto de vidraças de um veículo automóvel pode ser constituído de vidraças cujo factor de transmissão luminosa global sob iluminante A, para uma espessura determinada, diminuirá passando do pára-brisas ao óculo traseiro.
As vidraças obtidas a partir dos vidros de acordo com a invenção podem ser vantajosamente utilizadas no quadro de um tal conjunto de vidraças para veículo automóvel.
Assim as vidraças laterais traseiras, que se trate de laterais móveis ou fixas chamadas custódias, poderão ser realizadas a partir de vidros que, para uma espessura de 3,85 mm, apresentam um factor de transmissão luminosa global sob iluminante A compreendido entre aproximadamente 30 e 60 %. Elas poderão ser associadas a óculos traseiros realizados a partir de vidros que, para uma espessura idêntica, apresentam um factor de transmissão luminosa global sob iluminante A compreendido entre aproximadamente 20 e 45 %.
Um conjunto de vidraças deste género poderia ser realizado a partir dos vidros referências Ex. 5 e Ex. 2 no quadro em anexo. As vidraças formadas do vidro Ex. 5 9 serviriam de laterais traseiros, a vidraça formada do vidro Ex. 2 constituiria o óculo traseiro.
QUADRO EX. 1 EX. 2 EX. 3 EX. 4 EX. 5 EX. 6 EX. 7 EX. 8 Fe203 (ferro total) 1,15 1,65 1,95 0,62 1,50 1,2 1,25 1,84 CoO 0,0122 0,0110 0,0066 0,0055 0,0058 0,0032 0,0102 0,006 Se 0,0013 - - 0,0009 - - 0,0015 - Cr203 - - - - - - - - Rédox 0,27 0,33 0,25 0,29 0,24 0,29 0,28 0,31 TLa (%) 35 35 35 55,7 45,8 55,0 33,5 34,1 TE (%) 25,3 18,7 17,8 44,9 26,8 32 21,6 16,8 λϋ(0 (nm) 496 488 501 505 490 495 531 494 Pc (%) 3,2 17,4 7,6 1,1 10,8 6,3 2,8 11,7
Lisboa, 31 de Julho de 2001
O AGENTE OFICIAL
10
Claims (1)
- ιτ REIVINDICAÇÕES 1a - Conjunto de vidraças montadas sobre um veículo automóvel compreendendo um pára-brisas, vidraças laterais dianteiras e traseiras e um óculo traseiro, caracterizado pelo facto de as laterais traseiras e o óculo traseiro serem constituídos por vidraças, que, para uma espessura determinada, apresentam factores de transmissão luminosa global sob iluminante A diferentes, as ditas vidraças compreendendo uma chapa de vidro colorida cuja composição compreende os constituintes mais abaixo indicados, expressos em percentagens ponderais : SÍ02 64 a 75 % AI203 0 a 5 % B203 0 a 5 % CaO 5 a 15% MgO 0 a 5 % Na20 10 a 18% K20 0 a 5 % e, a título de agentes corantes : Fe2C>3 (ferro total) 0,45 a 2,5 % CoO 0,001 a 0,02 % Cr203 0 a 0,1 % Se 0 a 0,0025 % 1 esta composição de vidro tendo um factor de transmissão energética global (Te) inferior ao factor de transmissão luminosa sob iluminante A (Tla), o factor TE sendo compreendido entre 10 e 48 % e o factor Tla entre 20 e 60 % para uma espessura de 3,85 milímetros, com excepção dos conjuntos de vidraças cujos laterais traseiros e óculo traseiro são constituídos por vidraças compreendendo uma chapa de vidro colorida cuja composição compreende os constituintes seguintes nos limites mais abaixo expressos em percentagens ponderais : Si02 64 a 75 % AI203 0 a 5 % B203 0 a 5 % CaO 5 a 15 % MgO 0 a 5 % Na20 10 a 18% K20 0 a 5 % Fe2C>3 (ferro total) 0,5 a 1,5% CoO 0,003 a 0,015% Cr203 0,025 a 0,09 % Se 0 a 0,0025 % 2a - Conjunto de vidraças de acordo com a reivindicação 1, caracterizado pelo facto de as vidraças compreenderem uma chapa de vidro colorida cuja composição contém um teor em FeO que representa entre 16 e 55 do teor em ferro total expresso sob forma de Fe203. 3a - Conjunto de vidraças de acordo com a reivindicação 2, caracterizado pelo facto de as vidraças compreenderem uma chapa de vidro colorida cuja composição 2 contém um teor em FeO que representa entre 20 e 40 % do teor em ferro total expresso sob forma de Fe203· 4a - Conjunto de vidraças de acordo com qualquer uma das reivindicações 1 e 2, caracterizado pelo facto de as vidraças compreenderem uma chapa de vidro colorida cuja composição contém a título de agentes corantes : Fe2C>3 (ferro total) CoO Se 0,45 a 1 % 0,001 a 0,01 % 0,0002 a 0,002 % 5a - Conjunto de vidraças de acordo com qualquer uma das reivindicações 1 e 2, caracterizado pelo facto de as vidraças compreenderem uma chapa de vidro colorida cuja composição contém a título de agentes corantes : Fe203 (ferro total) CoO Se 1 a 1,8% 0,005 a 0,02 % 0,0005 a 0,0025 % 6a - Conjunto de vidraças de acordo com qualquer uma das reivindicações 1 e 2, caracterizado pelo facto de as vidraças compreenderem uma chapa de vidro colorida cuja composição contém a título de agentes corantes : Fe203 (ferro total) 0,8 a 1,8 % CoO 0,001 a 0,01 % 7a - Conjunto de vidraças de acordo com qualquer uma das reivindicações 1 e 2, caracterizado pelo facto de as vidraças compreenderem uma chapa de vidro colorida cuja composição contém a título de agentes corantes : Fe203 (ferro total) CoO 1,3 a 2,5% 0,005 a 0,015% 8a - Conjunto de vidraças de acordo com qualquer uma das reivindicações precedentes, caracterizado pelo facto de as vidraças compreenderem uma chapa de vidro colorida cuja espessura é compreendida entre 2 e 8 milímetros. 9a - Conjunto de vidraças de acordo com qualquer uma das reivindicações precedentes, caracterizado pelo facto de as vidraças formando os laterais traseiros apresentarem, para uma espessura de 3,85 mm, um factor de transmissão global sob iluminante A compreendido entre 30 e 60%, a vidraça constituindo o óculo traseiro apresentando, para a mesma espessura, um factor de transmissão global sob iluminante A compreendido entre 20 e 45 %. Lisboa, 31 de Julho de 2001 O AGENTE OFICIAL4