MX2021013782A - Acero recubierto con zinc para aplicaciones de conformado en caliente y metodo de produccion. - Google Patents
Acero recubierto con zinc para aplicaciones de conformado en caliente y metodo de produccion.Info
- Publication number
- MX2021013782A MX2021013782A MX2021013782A MX2021013782A MX2021013782A MX 2021013782 A MX2021013782 A MX 2021013782A MX 2021013782 A MX2021013782 A MX 2021013782A MX 2021013782 A MX2021013782 A MX 2021013782A MX 2021013782 A MX2021013782 A MX 2021013782A
- Authority
- MX
- Mexico
- Prior art keywords
- zinc
- coated steel
- production
- heat treatment
- steel
- Prior art date
Abstract
Un acero recubierto con zinc se puede producir al llevar a cabo un tratamiento térmico de aleación térmica después de satinar el acero y antes de estampar en caliente el acero; el tratamiento térmico de aleación previa se lleva a cabo a una temperatura entre aproximadamente 454.4°C (850°F) y aproximadamente 510°C (950°F) en un proceso de recocido de bobina abierta; el tratamiento térmico de aleación previa permite un tiempo más corto a temperatura de austenización para formar una fase deseada de a-Fe en el recubrimiento al incrementar la concentración de hierro; esto también disminuye la pérdida de zinc y existe un óxido más adherente después del estampado en caliente.
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US201361824791P | 2013-05-17 | 2013-05-17 |
Publications (1)
Publication Number | Publication Date |
---|---|
MX2021013782A true MX2021013782A (es) | 2021-12-10 |
Family
ID=50942354
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
MX2015015776A MX2015015776A (es) | 2013-05-17 | 2014-05-16 | Acero recubierto con zing para aplicaciones de conformado en caliente y metodo de produccion. |
MX2021013782A MX2021013782A (es) | 2013-05-17 | 2015-11-13 | Acero recubierto con zinc para aplicaciones de conformado en caliente y metodo de produccion. |
Family Applications Before (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
MX2015015776A MX2015015776A (es) | 2013-05-17 | 2014-05-16 | Acero recubierto con zing para aplicaciones de conformado en caliente y metodo de produccion. |
Country Status (14)
Country | Link |
---|---|
US (1) | US10718045B2 (es) |
EP (1) | EP2997173B1 (es) |
JP (2) | JP6470266B2 (es) |
KR (1) | KR20160007648A (es) |
CN (2) | CN107267905A (es) |
AU (1) | AU2014265241B2 (es) |
BR (1) | BR112015027811A2 (es) |
CA (1) | CA2910703C (es) |
MX (2) | MX2015015776A (es) |
PL (1) | PL2997173T3 (es) |
RU (2) | RU2018134251A (es) |
TR (1) | TR201818914T4 (es) |
TW (2) | TWI567235B (es) |
WO (1) | WO2014186749A1 (es) |
Families Citing this family (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP6211908B2 (ja) * | 2013-12-02 | 2017-10-11 | トヨタ自動車株式会社 | ホットスタンプ成形品の製造方法 |
DE102016218957A1 (de) | 2016-09-30 | 2018-04-05 | Thyssenkrupp Ag | Temporäre Korrosionsschutzschicht |
CN106825177B (zh) * | 2017-01-16 | 2018-07-17 | 佛山市高明伟昌兴钢管有限公司 | 镀锌钢板热冲压成型方法 |
MX2020009042A (es) * | 2018-03-01 | 2021-01-08 | Nucor Corp | Recubrimiento de aleacion a base de zinc para acero y metodos. |
CA3092904A1 (en) * | 2018-03-01 | 2019-09-06 | Nucor Corporation | Zinc alloy coated high-strength steels and method of manufacturing the same |
US10481052B2 (en) | 2018-03-28 | 2019-11-19 | Ford Global Technologies, Llc | Quality control process to assess the aluminized coating characteristics of hot stamped parts |
CN111434404B (zh) * | 2019-05-27 | 2022-03-25 | 苏州普热斯勒先进成型技术有限公司 | 一种耐腐蚀热冲压件的制造方法及装置 |
WO2021182465A1 (ja) * | 2020-03-12 | 2021-09-16 | 日本製鉄株式会社 | ホットスタンプ用めっき鋼板 |
CN111618146A (zh) * | 2020-05-12 | 2020-09-04 | 首钢集团有限公司 | 一种锌基镀层涂覆钢材热冲压方法及热冲压成型构件 |
Family Cites Families (51)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
BE708005A (es) | 1967-12-14 | 1968-04-16 | ||
US3873377A (en) * | 1973-11-21 | 1975-03-25 | Bethlehem Steel Corp | Process for improving batch annealed strip surface quality |
JPS5914541B2 (ja) * | 1976-12-14 | 1984-04-05 | 日新製鋼株式会社 | 亜鉛めつき鋼板の合金化処理方法 |
US4264684A (en) | 1979-12-17 | 1981-04-28 | Bethlehem Steel Corporation | Zinc-alloy coated ferrous product resistant to embrittlement |
JPS5834168A (ja) * | 1981-08-25 | 1983-02-28 | Nippon Kokan Kk <Nkk> | 溶融亜鉛メツキ鋼板のFe−Zn合金化処理方法 |
JPS60230970A (ja) * | 1984-05-02 | 1985-11-16 | Kawasaki Steel Corp | 合金化亜鉛めつき鋼板の製造方法 |
US5015341A (en) | 1988-08-05 | 1991-05-14 | Armco Steel Company, L.P. | Induction galvannealed electroplated steel strip |
US5897967A (en) * | 1996-08-01 | 1999-04-27 | Sumitomo Metal Industries, Ltd. | Galvannealed steel sheet and manufacturing method thereof |
EP0964078A1 (en) | 1998-06-12 | 1999-12-15 | Enamels and Ceramic Coatings International C.V. | Enamelling of zinc or zinc-alloy precoated steel surfaces |
FR2807447B1 (fr) | 2000-04-07 | 2002-10-11 | Usinor | Procede de realisation d'une piece a tres hautes caracteristiques mecaniques, mise en forme par emboutissage, a partir d'une bande de tole d'acier laminee et notamment laminee a chaud et revetue |
CN101125473B (zh) * | 2001-06-06 | 2012-07-18 | 新日本制铁株式会社 | 热浸镀锌薄钢板和热浸镀锌层扩散处理薄钢板及制造方法 |
FR2828888B1 (fr) | 2001-08-21 | 2003-12-12 | Stein Heurtey | Procede de galvanisation a chaud de bandes metalliques d'aciers a haute resistance |
JP3582504B2 (ja) * | 2001-08-31 | 2004-10-27 | 住友金属工業株式会社 | 熱間プレス用めっき鋼板 |
JP3758549B2 (ja) * | 2001-10-23 | 2006-03-22 | 住友金属工業株式会社 | 熱間プレス加工方法 |
KR100678406B1 (ko) | 2001-10-23 | 2007-02-02 | 수미도모 메탈 인더스트리즈, 리미티드 | 강철재의 열간 프레스 성형방법 |
US6902829B2 (en) * | 2001-11-15 | 2005-06-07 | Isg Technologies Inc. | Coated steel alloy product |
JP4085876B2 (ja) * | 2003-04-23 | 2008-05-14 | 住友金属工業株式会社 | 熱間プレス成形品およびその製造方法 |
DE602004021802D1 (de) | 2003-04-23 | 2009-08-13 | Sumitomo Metal Ind | Heisspressgeformtes produkt und herstellungsverfahren dafür |
DE10333166A1 (de) | 2003-07-22 | 2005-02-10 | Daimlerchrysler Ag | Pressgehärtetes Bauteil und Verfahren zur Herstellung eines pressgehärteten Bauteils |
ES2421182T3 (es) | 2003-07-29 | 2013-08-29 | Voestalpine Stahl Gmbh | Componente de chapa de acero con una capa de protección anticorrosiva catódica |
JP3931859B2 (ja) * | 2003-07-30 | 2007-06-20 | 住友金属工業株式会社 | 熱間成形用亜鉛系めっき鋼材と熱間成形方法 |
JP4192051B2 (ja) * | 2003-08-19 | 2008-12-03 | 新日本製鐵株式会社 | 高強度合金化溶融亜鉛めっき鋼板の製造方法と製造設備 |
JP4325442B2 (ja) * | 2004-03-12 | 2009-09-02 | 住友金属工業株式会社 | 溶融亜鉛系めっき鋼材の製造方法 |
WO2007048883A1 (fr) | 2005-10-27 | 2007-05-03 | Usinor | Procede de fabrication d'une piece a tres hautes caracteristiques mecaniques a partir d'une tole laminee et revetue |
JP4020409B2 (ja) * | 2006-02-02 | 2007-12-12 | シーケー金属株式会社 | 溶融亜鉛メッキ浴及び亜鉛メッキ処理鉄物製品 |
KR20100019500A (ko) * | 2007-06-15 | 2010-02-18 | 수미도모 메탈 인더스트리즈, 리미티드 | 성형품의 제조 방법 |
EP2009128A1 (en) * | 2007-06-29 | 2008-12-31 | ArcelorMittal France | Galvanized or galvannealed silicon steel |
EP2009129A1 (en) * | 2007-06-29 | 2008-12-31 | ArcelorMittal France | Process for manufacturing a galvannealed steel sheet by DFF regulation |
CN101353755B (zh) * | 2007-07-24 | 2011-08-24 | 宝山钢铁股份有限公司 | 一种高抗拉强度基板、热镀锌汽车外板及其制造方法 |
DE102007061489A1 (de) | 2007-12-20 | 2009-06-25 | Voestalpine Stahl Gmbh | Verfahren zum Herstellen von gehärteten Bauteilen aus härtbarem Stahl und härtbares Stahlband hierfür |
DE102008006771B3 (de) * | 2008-01-30 | 2009-09-10 | Thyssenkrupp Steel Ag | Verfahren zur Herstellung eines Bauteils aus einem mit einem Al-Si-Überzug versehenen Stahlprodukt und Zwischenprodukt eines solchen Verfahrens |
JP4590025B2 (ja) | 2008-04-22 | 2010-12-01 | 新日本製鐵株式会社 | めっき鋼板及びめっき鋼板の熱間プレス方法 |
CN102089451B (zh) * | 2008-07-11 | 2013-03-06 | 新日铁住金株式会社 | 快速加热热压用镀铝钢板及其制造方法、以及使用该镀铝钢板的快速加热热压方法 |
KR101008042B1 (ko) | 2009-01-09 | 2011-01-13 | 주식회사 포스코 | 내식성이 우수한 알루미늄 도금강판, 이를 이용한 열간 프레스 성형 제품 및 그 제조방법 |
JP4825882B2 (ja) | 2009-02-03 | 2011-11-30 | トヨタ自動車株式会社 | 高強度焼き入れ成形体及びその製造方法 |
DE102009007909A1 (de) | 2009-02-06 | 2010-08-12 | Thyssenkrupp Steel Europe Ag | Verfahren zum Herstellen eines Stahlbauteils durch Warmformen und durch Warmformen hergestelltes Stahlbauteil |
JP5436009B2 (ja) | 2009-04-07 | 2014-03-05 | 株式会社神戸製鋼所 | めっき密着性に優れた高強度合金化溶融亜鉛めっき鋼板及びその製造方法 |
ATE554190T1 (de) | 2009-08-25 | 2012-05-15 | Thyssenkrupp Steel Europe Ag | Verfahren zum herstellen eines mit einem metallischen, vor korrosion schützenden überzug versehenen stahlbauteils und stahlbauteil |
CN102021482B (zh) * | 2009-09-18 | 2013-06-19 | 宝山钢铁股份有限公司 | 一种冷轧热镀锌双相钢及其制造方法 |
JP4849186B2 (ja) | 2009-10-28 | 2012-01-11 | Jfeスチール株式会社 | 熱間プレス部材およびその製造方法 |
JP5578038B2 (ja) * | 2009-11-13 | 2014-08-27 | 新日鐵住金株式会社 | 曲げ加工部材の製造方法 |
EP2520693B1 (en) | 2009-12-28 | 2017-01-25 | Nippon Steel & Sumitomo Metal Corporation | Method for manufacturing a hot press-molded member |
KR101171450B1 (ko) | 2009-12-29 | 2012-08-06 | 주식회사 포스코 | 도금 강재의 열간 프레스 성형방법 및 이를 이용한 열간 프레스 성형품 |
CN104388870B (zh) | 2009-12-29 | 2017-04-12 | Posco公司 | 一种热压模塑部件 |
EP2536857B1 (en) | 2010-02-19 | 2019-08-21 | Tata Steel Nederland Technology B.V. | Strip, sheet or blank suitable for hot forming and process for the production thereof |
JP4883240B1 (ja) | 2010-08-04 | 2012-02-22 | Jfeスチール株式会社 | 熱間プレス用鋼板およびそれを用いた熱間プレス部材の製造方法 |
JP5547287B2 (ja) * | 2010-10-22 | 2014-07-09 | 新日鐵住金株式会社 | ホットスタンプ成形体の製造方法及びホットスタンプ成形体 |
US20120118437A1 (en) * | 2010-11-17 | 2012-05-17 | Jian Wang | Zinc coated steel with inorganic overlay for hot forming |
CN102021472B (zh) * | 2011-01-12 | 2013-02-06 | 钢铁研究总院 | 一种适用于连续退火工艺高强塑积汽车钢板的生产方法 |
DE102012021031A1 (de) * | 2012-10-26 | 2013-05-02 | Daimler Ag | Verfahren und Vorrichtung zur Herstellung pressgehärteter Blechbauteile |
CN103100825A (zh) * | 2013-01-07 | 2013-05-15 | 广州先艺电子科技有限公司 | 一种预合金化金锡预成型焊片的制备方法 |
-
2014
- 2014-05-16 CA CA2910703A patent/CA2910703C/en active Active
- 2014-05-16 BR BR112015027811A patent/BR112015027811A2/pt not_active Application Discontinuation
- 2014-05-16 TR TR2018/18914T patent/TR201818914T4/tr unknown
- 2014-05-16 EP EP14730045.3A patent/EP2997173B1/en active Active
- 2014-05-16 MX MX2015015776A patent/MX2015015776A/es unknown
- 2014-05-16 JP JP2016514142A patent/JP6470266B2/ja active Active
- 2014-05-16 TW TW103117385A patent/TWI567235B/zh not_active IP Right Cessation
- 2014-05-16 US US14/279,818 patent/US10718045B2/en active Active
- 2014-05-16 AU AU2014265241A patent/AU2014265241B2/en not_active Ceased
- 2014-05-16 TW TW105132804A patent/TWI613325B/zh not_active IP Right Cessation
- 2014-05-16 CN CN201710513551.1A patent/CN107267905A/zh active Pending
- 2014-05-16 KR KR1020157035339A patent/KR20160007648A/ko active Search and Examination
- 2014-05-16 WO PCT/US2014/038467 patent/WO2014186749A1/en active Application Filing
- 2014-05-16 RU RU2018134251A patent/RU2018134251A/ru not_active Application Discontinuation
- 2014-05-16 PL PL14730045T patent/PL2997173T3/pl unknown
- 2014-05-16 RU RU2015146678A patent/RU2669663C2/ru not_active IP Right Cessation
- 2014-05-16 CN CN201480028556.XA patent/CN105247095B/zh not_active Expired - Fee Related
-
2015
- 2015-11-13 MX MX2021013782A patent/MX2021013782A/es unknown
-
2019
- 2019-01-17 JP JP2019005603A patent/JP6718656B2/ja active Active
Also Published As
Publication number | Publication date |
---|---|
MX2015015776A (es) | 2016-03-09 |
RU2018134251A (ru) | 2019-03-20 |
AU2014265241B2 (en) | 2017-01-19 |
RU2669663C2 (ru) | 2018-10-12 |
KR20160007648A (ko) | 2016-01-20 |
US20140342181A1 (en) | 2014-11-20 |
TW201706426A (zh) | 2017-02-16 |
US10718045B2 (en) | 2020-07-21 |
TW201510275A (zh) | 2015-03-16 |
CA2910703A1 (en) | 2014-11-20 |
JP6718656B2 (ja) | 2020-07-08 |
CA2910703C (en) | 2018-07-03 |
JP2016520162A (ja) | 2016-07-11 |
TWI613325B (zh) | 2018-02-01 |
CN105247095B (zh) | 2017-07-18 |
BR112015027811A2 (pt) | 2017-07-25 |
JP2019116685A (ja) | 2019-07-18 |
RU2018134251A3 (es) | 2019-06-14 |
PL2997173T3 (pl) | 2019-04-30 |
CN105247095A (zh) | 2016-01-13 |
TWI567235B (zh) | 2017-01-21 |
CN107267905A (zh) | 2017-10-20 |
EP2997173B1 (en) | 2018-10-03 |
WO2014186749A1 (en) | 2014-11-20 |
RU2015146678A (ru) | 2017-06-23 |
JP6470266B2 (ja) | 2019-02-13 |
EP2997173A1 (en) | 2016-03-23 |
RU2015146678A3 (es) | 2018-04-02 |
AU2014265241A1 (en) | 2015-11-12 |
TR201818914T4 (tr) | 2019-01-21 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
MX2021013782A (es) | Acero recubierto con zinc para aplicaciones de conformado en caliente y metodo de produccion. | |
MX2017001106A (es) | Metodo para la fabricacion de lamina de acero galvanizada de alta resistencia. | |
MX2018006883A (es) | Metodo para la produccion de lamina de acero electrico de grano no orientado. | |
PL2240622T3 (pl) | Sposób wytwarzania elementu konstrukcyjnego z produktu stalowego wyposażonego w powłokę al-si oraz produkt pośredni tego sposobu | |
WO2012085248A3 (de) | Verfahren zum umformen und härten von beschichteten stahlblechen | |
MX348196B (es) | Metodo para fabricar cuerpo estampado en caliente que tiene pared vertical y cuerpo estampado en caliente que tiene pared vertical. | |
MX2018003455A (es) | Lamina de acero galvanizado para prensado en caliente y metodo para la produccion de articulo moldeado prensado en caliente. | |
MX2018006127A (es) | Metodo para producir lamina de acero electrico no orientado. | |
MX2015012015A (es) | Metodo para preparar y tratar un substrato de acero. | |
MX2017002974A (es) | Metodo e instalacion para la produccion de laminas de acero galvanizadas de alta resistencia. | |
MX2016001902A (es) | Metodo para la produccion de lamina de acero galvanizada por inmersion en caliente de alta resistencia y metodo para la produccion de lamina de acero recocida despues de galvanizada de alta resistencia. | |
MX2016016705A (es) | Metodo para la fabricacion de una lamina de acero galvanizada de alta resistencia. | |
MX2016003258A (es) | Metodo para fabricar articulo moldeado a presion, y articulo moldeado a presion. | |
EP3598121A4 (en) | METHOD FOR MEASURING MAGNETIC TRANSFORMATION RATE OF STEEL PLATE IN AN ANNUIT OVEN, ASSOCIATED DEVICE FOR MEASURING MAGNETIC TRANSFORMATION RATE, CONTINUOUS ANNUIT PROCESS AND CONTINUOUS HOT GALVANIZATION PROCESS | |
MX2015011117A (es) | Metodo para producir un material con ultra elevada resistencia y con alta elongacion. | |
MX2016010667A (es) | Lamina de acero galvanizada por inmersion en caliente de alta resistencia y metodo para la produccion de la misma. | |
MX2015011581A (es) | Lamina de acero galvanizada de alta resistencia y metodo para la produccion de la misma. | |
MY171863A (en) | Methods for treating a ferrous metal substrate | |
FI20135775L (fi) | Menetelmä valmistaa galvannealed-käsitelty teräsnauhatuote kuumapuristusmuovaukseen, menetelmä valmistaa kuumapuristettu teräskomponentti, ja galvannealed-käsitelty teräsnauhatuote | |
IN2015KN00599A (es) | ||
MX2016010665A (es) | Lamina de acero de alta resistencia y metodo para la fabricacion de la misma. | |
MX2019007699A (es) | Metodo de fabricacion de un miembro revenido y miembro revenido. | |
WO2015028871A3 (en) | Induction heat-treating apparatus and process | |
PH12018500105A1 (en) | High formability dual phase steel | |
PH12017501293A1 (en) | Dual phase steel with improved properties |