MX2017002974A - Metodo e instalacion para la produccion de laminas de acero galvanizadas de alta resistencia. - Google Patents
Metodo e instalacion para la produccion de laminas de acero galvanizadas de alta resistencia.Info
- Publication number
- MX2017002974A MX2017002974A MX2017002974A MX2017002974A MX2017002974A MX 2017002974 A MX2017002974 A MX 2017002974A MX 2017002974 A MX2017002974 A MX 2017002974A MX 2017002974 A MX2017002974 A MX 2017002974A MX 2017002974 A MX2017002974 A MX 2017002974A
- Authority
- MX
- Mexico
- Prior art keywords
- hot
- steel sheet
- galvanized steel
- dipped galvanized
- subjected
- Prior art date
Abstract
La invención proporciona un método para la producción de láminas de acero galvanizadas de alta resistencia que tienen excelentes adherencia del recubrimiento, trabajabilidad y aspecto. El método para la producción de láminas de acero galvanizadas de alta resistencia incluye una etapa de laminación en caliente para laminar en caliente un desbaste plano que incluye, en % en masa, C: 0.05 a 0.30%, Si: 0.1 a 2.0% y Mn: 1.0 a 4.0%, después de eso enrollar la lámina de acero en una bobina a una temperatura TC específica, y decapar la lámina de acero, una etapa de laminación en frío para laminar en frío la lámina de acero laminada en caliente que resulta de la etapa de laminación en caliente, una etapa de recocido para recocer la lámina de acero laminada en frío que resulta de la etapa de laminación en frío bajo condiciones específicas, y una etapa de galvanización para galvanizar la lámina recocida que resulta de la etapa de recocido en un baño de galvanización que contiene de 0.12 a 0.22% en masa de Al.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2014182153 | 2014-09-08 | ||
PCT/JP2015/004151 WO2016038801A1 (ja) | 2014-09-08 | 2015-08-20 | 高強度溶融亜鉛めっき鋼板の製造方法及び製造設備 |
Publications (1)
Publication Number | Publication Date |
---|---|
MX2017002974A true MX2017002974A (es) | 2017-06-19 |
Family
ID=55458576
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
MX2017002974A MX2017002974A (es) | 2014-09-08 | 2015-08-20 | Metodo e instalacion para la produccion de laminas de acero galvanizadas de alta resistencia. |
Country Status (7)
Country | Link |
---|---|
US (1) | US10648054B2 (es) |
EP (1) | EP3159420B1 (es) |
JP (1) | JP6172297B2 (es) |
KR (1) | KR101889795B1 (es) |
CN (1) | CN106715726B (es) |
MX (1) | MX2017002974A (es) |
WO (1) | WO2016038801A1 (es) |
Families Citing this family (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN106065429B (zh) * | 2016-07-21 | 2018-10-02 | 洛阳Lyc轴承有限公司 | 一种保证轴承零件热后件表面颜色一致的方法 |
JP6323628B1 (ja) * | 2016-10-25 | 2018-05-16 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板の製造方法 |
JP6822934B2 (ja) * | 2017-10-26 | 2021-01-27 | 株式会社神戸製鋼所 | 溶融亜鉛めっき鋼板の製造方法 |
MX2020007610A (es) * | 2018-01-17 | 2020-09-03 | Jfe Steel Corp | Lamina de acero electrogalvano-recocida de alta resistencia y metodo para la fabricacion de la misma. |
JP7086666B2 (ja) * | 2018-03-23 | 2022-06-20 | 株式会社神戸製鋼所 | 合金化溶融亜鉛めっき鋼板の製造方法 |
CN112041475B (zh) * | 2018-05-01 | 2021-09-17 | 日本制铁株式会社 | 镀锌钢板及其制造方法 |
JP2021014605A (ja) * | 2019-07-10 | 2021-02-12 | 株式会社神戸製鋼所 | 溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板の製造方法 |
CN110964981A (zh) * | 2019-11-13 | 2020-04-07 | 浙江金洲管道科技股份有限公司 | 一种镀锌管材及制造方法 |
TR202016190A2 (tr) * | 2020-10-12 | 2021-01-21 | Borcelik Celik San Tic A S | Galvani̇zli̇ yüzeylere kaplama i̇çi̇n i̇şlem |
KR20230145590A (ko) | 2021-03-08 | 2023-10-17 | 가부시키가이샤 고베 세이코쇼 | 강판의 제조 방법 |
KR20230145442A (ko) | 2021-03-08 | 2023-10-17 | 가부시키가이샤 고베 세이코쇼 | 용융 아연 도금용 강판, 용융 아연 도금 강판 및 합금화 용융 아연 도금 강판 |
KR20230145441A (ko) | 2021-03-08 | 2023-10-17 | 가부시키가이샤 고베 세이코쇼 | 용융 아연 도금 강판의 제조 방법 및 합금화 용융 아연 도금 강판의 제조 방법 |
CN113897545A (zh) * | 2021-09-02 | 2022-01-07 | 河钢股份有限公司承德分公司 | 一种超厚锌层高强无花热镀锌钢板、超厚锌层高强无花热镀锌钢卷及其制备方法 |
JP7468819B2 (ja) | 2022-03-25 | 2024-04-16 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板の製造方法 |
Family Cites Families (22)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS55122865A (en) | 1979-03-12 | 1980-09-20 | Nippon Steel Corp | Molten zinc plating method for difficult plating steel sheet |
JP2741617B2 (ja) | 1989-03-31 | 1998-04-22 | 日本鋼管株式会社 | 直火式加熱炉の空気比制御方法 |
JP2530939B2 (ja) | 1990-11-30 | 1996-09-04 | 新日本製鐵株式会社 | 高Si含有高張力溶融亜鉛めっき鋼板の製造方法 |
JP2587724B2 (ja) | 1990-11-30 | 1997-03-05 | 新日本製鐵株式会社 | めっき密着性の良好な高Si含有高張力溶融亜鉛めっき鋼板の製造方法 |
JP2513532B2 (ja) | 1990-11-30 | 1996-07-03 | 新日本製鐵株式会社 | 高Si含有鋼の高張力溶融亜鉛めっき鋼板の製造方法 |
JP2587725B2 (ja) | 1990-11-30 | 1997-03-05 | 新日本製鐵株式会社 | P含有高張力合金化溶融亜鉛めっき鋼板の製造方法 |
JPH04254531A (ja) | 1991-02-01 | 1992-09-09 | Nippon Steel Corp | 高Si含有高張力鋼の溶融亜鉛めっき前の焼鈍方法 |
JPH04254532A (ja) | 1991-02-01 | 1992-09-09 | Nippon Steel Corp | 加工性の優れた合金化溶融亜鉛めっき鋼板の製造方法 |
JP3255765B2 (ja) | 1993-07-14 | 2002-02-12 | 川崎製鉄株式会社 | 高張力溶融または合金化溶融亜鉛めっき鋼板の製造方法 |
JP3184445B2 (ja) | 1995-12-27 | 2001-07-09 | 川崎製鉄株式会社 | 合金化溶融亜鉛めっき鋼板の製造方法 |
JPH11279659A (ja) * | 1998-03-30 | 1999-10-12 | Nkk Corp | 鋼帯の直火還元加熱方法及び直火還元加熱装置 |
JP4202632B2 (ja) | 2001-09-28 | 2008-12-24 | 株式会社東芝 | 一括封止型半導体パッケージの樹脂封止構造およびその製造装置 |
JP4254531B2 (ja) | 2003-12-25 | 2009-04-15 | 豊田合成株式会社 | 等速ジョイント用ブーツ |
JP4254532B2 (ja) | 2003-12-26 | 2009-04-15 | ダイキン工業株式会社 | ヒートポンプ式給湯装置 |
JP4972775B2 (ja) * | 2006-02-28 | 2012-07-11 | Jfeスチール株式会社 | 外観性とめっき密着性に優れる高強度溶融亜鉛めっき鋼板の製造方法 |
ES2758553T3 (es) * | 2009-11-30 | 2020-05-05 | Nippon Steel Corp | Lámina de acero de alta resistencia con excelente resistencia a la fragilidad por hidrógeno y una resistencia a tensión máxima de 900 MPa o más, y método para su producción |
JP5434960B2 (ja) * | 2010-05-31 | 2014-03-05 | Jfeスチール株式会社 | 曲げ性および溶接性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法 |
JP5966528B2 (ja) * | 2011-06-07 | 2016-08-10 | Jfeスチール株式会社 | めっき密着性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
DE102011051731B4 (de) | 2011-07-11 | 2013-01-24 | Thyssenkrupp Steel Europe Ag | Verfahren zur Herstellung eines durch Schmelztauchbeschichten mit einer metallischen Schutzschicht versehenen Stahlflachprodukts |
JP5978826B2 (ja) * | 2012-07-23 | 2016-08-24 | Jfeスチール株式会社 | 表面安定性に優れた高強度溶融亜鉛めっき鋼板の製造方法 |
JP5915569B2 (ja) | 2013-03-01 | 2016-05-11 | Jfeスチール株式会社 | 溶融亜鉛めっき鋼板の製造方法および連続溶融亜鉛めっき装置 |
JP5962582B2 (ja) * | 2013-05-21 | 2016-08-03 | Jfeスチール株式会社 | 高強度合金化溶融亜鉛めっき鋼板の製造方法 |
-
2015
- 2015-08-20 JP JP2015559387A patent/JP6172297B2/ja active Active
- 2015-08-20 KR KR1020177006318A patent/KR101889795B1/ko active IP Right Grant
- 2015-08-20 MX MX2017002974A patent/MX2017002974A/es unknown
- 2015-08-20 US US15/509,353 patent/US10648054B2/en active Active
- 2015-08-20 WO PCT/JP2015/004151 patent/WO2016038801A1/ja active Application Filing
- 2015-08-20 EP EP15839932.9A patent/EP3159420B1/en active Active
- 2015-08-20 CN CN201580048205.XA patent/CN106715726B/zh active Active
Also Published As
Publication number | Publication date |
---|---|
JPWO2016038801A1 (ja) | 2017-04-27 |
EP3159420A4 (en) | 2017-07-26 |
WO2016038801A1 (ja) | 2016-03-17 |
US10648054B2 (en) | 2020-05-12 |
JP6172297B2 (ja) | 2017-08-02 |
EP3159420B1 (en) | 2020-09-16 |
KR20170039733A (ko) | 2017-04-11 |
EP3159420A1 (en) | 2017-04-26 |
KR101889795B1 (ko) | 2018-08-20 |
US20170253943A1 (en) | 2017-09-07 |
CN106715726A (zh) | 2017-05-24 |
CN106715726B (zh) | 2018-11-06 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
MX2017002974A (es) | Metodo e instalacion para la produccion de laminas de acero galvanizadas de alta resistencia. | |
MX2015014436A (es) | Lamina de acero laminada en caliente de alta resistencia y metodo para la produccion de la misma. | |
MX363038B (es) | Metodo para producir hoja de acero laminada en frio. | |
MX2017001106A (es) | Metodo para la fabricacion de lamina de acero galvanizada de alta resistencia. | |
MX357847B (es) | Método para la producción de una lámina de acero eléctrico de grano no orientado.. | |
MX368208B (es) | Placa de acero laminada en frío de alta maleabilidad y superresistente, y método de fabricación de la misma. | |
WO2012085248A3 (de) | Verfahren zum umformen und härten von beschichteten stahlblechen | |
MX2014002935A (es) | Metodo para producir una cinta electrica superiormente resistente de grano no orientado y su uso. | |
IN2015DN00610A (es) | ||
MX2016016705A (es) | Metodo para la fabricacion de una lamina de acero galvanizada de alta resistencia. | |
MX2017002726A (es) | Lamina de acero laminado en frio, metodo de fabricacion de lamina de acero laminado en frio, miembro de automovil e instalaciones para la fabricacion de lamina de acero laminado en frio. | |
RU2018122307A (ru) | Способ производства высокопрочной листовой стали, характеризующейся улучшенными прочностью и формуемостью, и полученная высокопрочная листовая сталь | |
WO2015099402A8 (ko) | 스트립의 연속소둔 장치 및 그 연속소둔 방법 | |
FI3741874T3 (fi) | Menetelmä tinaa sisältävän ei-raeorientoidun piiteräslevyn valmistamiseksi | |
RU2011139832A (ru) | Универсальная линия для обработки стальной полосы для производства различных видов высокопрочной стали | |
IN2015DN00612A (es) | ||
RU2016151402A (ru) | Способ изготовления высокопрочного стального листа с покрытием или без покрытия и полученный стальной лист | |
MX354352B (es) | Lámina de acero galvanizado de alta resistencia excelente en términos de adherencia de recubrimiento y método para la fabricación de la misma. | |
MX2018006419A (es) | Metodo para la fabricacion de lamina de acero galvanizada de alta resistencia, metodo para la fabricacion de lamina de acero laminada en caliente para laminas de acero galvanizadas de alta resistencia, metodo para la fabricacion de lamina de acero laminada en frio para laminas de acero galvanizadas de alta resistencia, y lamina de acero galvanizada de alta resistencia. | |
MX2016001902A (es) | Metodo para la produccion de lamina de acero galvanizada por inmersion en caliente de alta resistencia y metodo para la produccion de lamina de acero recocida despues de galvanizada de alta resistencia. | |
RU2018107257A (ru) | Высокопрочная марганцевая сталь, содержащая алюминий, способ производства листового стального продукта из указанной стали и листовой стальной продукт, полученный в соответствии с этим способом | |
RU2012143205A (ru) | Высокопрочный с низким отношением предела текучести к пределу прочности оцинкованный погружением стальной лист, высокопрочный с низким отношением предела текучести к пределу прочности отожженный оцинкованный погружением стальной лист, способ изготовления высокопрочного с низким отношением предела текучести к пределу прочности оцинкованного погружением стального листа и способ изготовления высокопрочного с низким отношением предела текучести к пределу прочности отожженного оцинкованного погружением стального листа | |
MX2016010667A (es) | Lamina de acero galvanizada por inmersion en caliente de alta resistencia y metodo para la produccion de la misma. | |
MX2009011698A (es) | Metodo para galvanizacion en caliente de material de ahss o uhss en tira, y este material. | |
RU2012143206A (ru) | Высокопрочный с высоким отношением предела текучести к пределу прочности стальной лист, высокопрочный с высоким отношением предела текучести к пределу прочности холоднокатаный стальной лист, высокопрочный с высоким отношением предела текучести к пределу прочности оцинкованный стальной лист, высокопрочный с высоким отношением предела текучести к пределу прочности оцинкованный погружением стальной лист, высокопрочный с высоким отношением предела текучести к пределу прочности отожженный оцинкованный погружением стальной лист, способ изготовления высокопрочного с высоким отношением предела текучести к пределу прочности холоднокатаного стального листа, способ изготовления высокопрочного с высоким отношением предела текучести к пределу прочности оцинкованного погружением стального листа и способ изготовления высокопрочного с высоким отношением предела текучести к пределу прочности отожженного оцинкованного погружением стального листа |