MX368208B - Placa de acero laminada en frío de alta maleabilidad y superresistente, y método de fabricación de la misma. - Google Patents

Placa de acero laminada en frío de alta maleabilidad y superresistente, y método de fabricación de la misma.

Info

Publication number
MX368208B
MX368208B MX2015005836A MX2015005836A MX368208B MX 368208 B MX368208 B MX 368208B MX 2015005836 A MX2015005836 A MX 2015005836A MX 2015005836 A MX2015005836 A MX 2015005836A MX 368208 B MX368208 B MX 368208B
Authority
MX
Mexico
Prior art keywords
cold
super
manufacturing
rolled steel
strength
Prior art date
Application number
MX2015005836A
Other languages
English (en)
Other versions
MX2015005836A (es
Inventor
Wang Li
Zhong Yong
Feng Weijun
Xiong Wei
Zhi Jianjun
Hu Guangkui
Original Assignee
Baoshan Iron & Steel
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Baoshan Iron & Steel filed Critical Baoshan Iron & Steel
Publication of MX2015005836A publication Critical patent/MX2015005836A/es
Publication of MX368208B publication Critical patent/MX368208B/es

Abstract

Una placa de acero laminada en frío de alta maleabilidad y superresistente y un método de fabricación de la misma. El porcentaje en peso de sus componentes es: C 0,15-0,25 %, Si 1,00-2,00 %, Mn 1,50-3,00 %, P = 0,015%, S = 0,012 %, Al 0,03-0,06 %, N = 0,008 %, y el resto son Fe e impurezas inevitables. El método de fabricación comprende las siguientes etapas: 1) fundir y verter; 2) calentar hasta 1.170~1.230 °C y realizar el aislamiento térmico; 3) realizar el laminado en caliente, siendo la temperatura de laminado final de 880 ± 30 °C, y el enrollamiento a 550~650 °C; y 4) realizar el lavado con ácido, laminado en frío y recocido, siendo la reducción del laminado en frío del 40-60 %, el recocido a 860-920 °C y realizar el enfriamiento lento hasta 690-750 °C con la velocidad de enfriamiento de 3~10 °C/s; realizar el enfriamiento rápido a 240~320 °C con la velocidad de enfriamiento = 50 °C/s, a continuación, calentar hasta 360~460 °C y realizar el aislamiento térmico durante 100~500 s hasta enfriar, por fin, hasta la temperatura ambiente. Finalmente, se obtiene una placa de acero laminada en frío de alta maleabilidad, baja propiedad de rebote y superresistente con el límite elástico de 600~900 MPa, la resistencia a la tracción de 980~1.150 MPa y el alargamiento del 17~25 %.
MX2015005836A 2012-11-15 2013-02-21 Placa de acero laminada en frío de alta maleabilidad y superresistente, y método de fabricación de la misma. MX368208B (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN201210461631.4A CN103805838B (zh) 2012-11-15 2012-11-15 一种高成形性超高强度冷轧钢板及其制造方法
PCT/CN2013/071711 WO2014075404A1 (zh) 2012-11-15 2013-02-21 一种高成形性超高强度冷轧钢板及其制造方法

Publications (2)

Publication Number Publication Date
MX2015005836A MX2015005836A (es) 2015-09-24
MX368208B true MX368208B (es) 2019-09-24

Family

ID=50703215

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2015005836A MX368208B (es) 2012-11-15 2013-02-21 Placa de acero laminada en frío de alta maleabilidad y superresistente, y método de fabricación de la misma.

Country Status (9)

Country Link
US (1) US10287659B2 (es)
EP (1) EP2921568B1 (es)
JP (1) JP6207621B2 (es)
KR (1) KR20150086312A (es)
CN (1) CN103805838B (es)
CA (1) CA2890126C (es)
ES (1) ES2668653T3 (es)
MX (1) MX368208B (es)
WO (1) WO2014075404A1 (es)

Families Citing this family (54)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN105039846B (zh) * 2015-08-17 2016-09-14 攀钢集团攀枝花钢铁研究院有限公司 钒微合金化tam钢及其制造方法
WO2017109542A1 (en) * 2015-12-21 2017-06-29 Arcelormittal Method for producing a high strength steel sheet having improved ductility and formability, and obtained steel sheet
CN106350731B (zh) * 2016-08-30 2018-08-10 宝山钢铁股份有限公司 一种具有优良磷化性能和成形性的冷轧高强度钢板及其制造方法
CN106244923B (zh) * 2016-08-30 2018-07-06 宝山钢铁股份有限公司 一种磷化性能和成形性能优良的冷轧高强度钢板及其制造方法
CN108018484B (zh) * 2016-10-31 2020-01-31 宝山钢铁股份有限公司 抗拉强度1500MPa以上成形性优良的冷轧高强钢及其制造方法
JP6414246B2 (ja) 2017-02-15 2018-10-31 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
CN108660369A (zh) * 2017-03-29 2018-10-16 鞍钢股份有限公司 抗拉强度大于1180MPa的淬火配分冷轧钢板及生产方法
CN107236891A (zh) * 2017-06-12 2017-10-10 苏州双金实业有限公司 一种环保型高强度钢材
CN109694992A (zh) * 2017-10-20 2019-04-30 鞍钢股份有限公司 一种抗拉强度大于1500MPa的淬火配分钢及其生产方法
CN109957715A (zh) * 2017-12-14 2019-07-02 鞍钢股份有限公司 热成形用钢板、制造方法、热成形方法、及制得的部件
CN108396242A (zh) * 2018-01-10 2018-08-14 唐山钢铁集团有限责任公司 一种低成本焊管用超高强度冷轧连退带钢及其生产方法
CN109355578B (zh) * 2018-12-14 2022-02-18 辽宁衡业高科新材股份有限公司 一种1000MPa级别热处理车轮的制备方法
CN109652625B (zh) * 2019-01-15 2021-02-23 象山华鹰塑料工程有限公司 一种汽车车窗用超高强度冷轧钢板制造工艺
CN109930079A (zh) * 2019-03-29 2019-06-25 本钢板材股份有限公司 一种980MPa级低成本冷轧淬火配分钢及其制备方法
CN114040988B (zh) * 2019-07-29 2022-12-09 Posco公司 高强度钢板及其制造方法
CN110499461B (zh) * 2019-08-22 2021-10-08 唐山钢铁集团有限责任公司 一种汽车座椅焊管用超高强钢板及其生产方法
CN110747391A (zh) * 2019-08-30 2020-02-04 武汉钢铁有限公司 一种具有优良延伸率的冷轧超高强钢及其制备方法
CN112760554A (zh) * 2019-10-21 2021-05-07 宝山钢铁股份有限公司 一种延展性优异的高强度钢及其制造方法
CN111334701B (zh) * 2020-03-25 2021-04-06 武汉钢铁有限公司 一种抗拉强度≥800MPa的高延伸率热轧组织调控钢及生产方法
CN111349771B (zh) * 2020-04-22 2022-04-01 马鞍山钢铁股份有限公司 一种具有优异塑性的980MPa级冷轧Q＆P钢及其制造方法
WO2021230079A1 (ja) * 2020-05-11 2021-11-18 Ｊｆｅスチール株式会社 鋼板、部材及びそれらの製造方法
CN111440987B (zh) * 2020-05-11 2021-03-02 武汉钢铁有限公司 采用短流程生产的抗拉强度≥980MPa淬火配分钢及方法
CN113718168B (zh) * 2020-05-25 2022-07-19 宝山钢铁股份有限公司 一种高强度冷轧钢板及其制造方法
CN113802051A (zh) * 2020-06-11 2021-12-17 宝山钢铁股份有限公司 一种塑性优异的超高强度钢及其制造方法
CN113926892B (zh) * 2020-06-29 2024-07-12 宝山钢铁股份有限公司 抗拉强度≥980MPa级热轧超高强度双相钢零件冲压成形工艺及应用
CN111979470A (zh) * 2020-08-05 2020-11-24 鞍钢股份有限公司 具有良好弯折性能超高强度冷轧马氏体钢板的生产方法
CN112159931B (zh) * 2020-09-28 2022-08-12 首钢集团有限公司 一种具有连续屈服的1000MPa级中锰TRIP钢及其制备方法
CN114381655A (zh) * 2020-10-21 2022-04-22 宝山钢铁股份有限公司 一种高强塑积冷轧qp钢及其退火工艺和制造方法
CN112680660B (zh) * 2020-12-03 2022-04-15 山东钢铁集团日照有限公司 一种1.2GPa级TRIP钢及其微观组织的调控方法
IN202131002770A (es) * 2021-01-20 2022-11-04 Tata Steel Ltd
CN115181892B (zh) * 2021-04-02 2023-07-11 宝山钢铁股份有限公司 1180MPa级别低碳低合金TRIP钢及快速热处理制造方法
CN115181884B (zh) * 2021-04-02 2023-08-11 宝山钢铁股份有限公司 1280MPa级别低碳低合金热镀锌Q&P钢及快速热处理热镀锌制造方法
CN115181893B (zh) * 2021-04-02 2023-07-11 宝山钢铁股份有限公司 1180MPa级低碳低合金热镀锌TRIP钢及快速热处理热镀锌制造方法
CN115181899B (zh) * 2021-04-02 2023-07-07 宝山钢铁股份有限公司 980MPa级别低碳低合金TRIP钢及其快速热处理制造方法
CN115181897B (zh) * 2021-04-02 2023-07-11 宝山钢铁股份有限公司 1280MPa级别低碳低合金超高强度双相钢及快速热处理制造方法
CN115181895B (zh) * 2021-04-02 2023-09-12 宝山钢铁股份有限公司 1180MPa级别低碳低合金热镀锌Q&P钢及快速热处理热镀锌制造方法
CN115181898B (zh) * 2021-04-02 2023-10-13 宝山钢铁股份有限公司 一种1280MPa级别低碳低合金Q&P钢及其快速热处理制造方法
CN115181887B (zh) * 2021-04-02 2023-08-11 宝山钢铁股份有限公司 一种1180MPa级别低碳低合金Q＆P钢及其快速热处理制造方法
CN113416890B (zh) * 2021-05-21 2022-07-22 鞍钢股份有限公司 高扩孔高塑性980MPa级冷轧连退钢板及其制备方法
CN113416893B (zh) * 2021-05-24 2022-10-18 鞍钢股份有限公司 汽车用高强高塑性铁素体奥氏体双相冷轧钢板及生产方法
CN115505835B (zh) * 2021-06-07 2024-04-05 宝山钢铁股份有限公司 一种冷轧钢板及其制造方法
CN115505834A (zh) * 2021-06-07 2022-12-23 宝山钢铁股份有限公司 一种热镀锌钢板及其制造方法
KR102372546B1 (ko) * 2021-07-27 2022-03-10 현대제철 주식회사 연신율이 우수한 초고강도 강판 및 그 제조방법
CN113930665A (zh) * 2021-09-01 2022-01-14 武汉钢铁有限公司 一种以贝氏体为基体的冷轧高强钢及其制备方法
CN114000053B (zh) * 2021-10-19 2022-05-20 湖南华菱涟钢特种新材料有限公司 热轧钢板及其制造方法
KR20240044568A (ko) * 2022-09-28 2024-04-05 주식회사 포스코 우수한 강도 및 성형성을 갖는 냉연강판 및 그 제조방법
CN115612816B (zh) * 2022-09-30 2024-02-02 攀钢集团攀枝花钢铁研究院有限公司 含硼钢制备复相钢、热成形用钢镀层板的方法
CN116288037A (zh) * 2022-12-13 2023-06-23 安钢集团冷轧有限责任公司 一种超深冲冷轧汽车钢及其生产方法
CN116288021B (zh) * 2023-02-06 2025-03-04 武汉科技大学 一种高强韧性双相低密度钢及其制备方法和应用
CN117867372B (zh) * 2023-04-28 2024-12-03 鞍钢股份有限公司 新能源汽车用1500MPa电池包用钢及其制备方法
CN116926422B (zh) * 2023-07-12 2025-11-25 河北河钢材料技术研究院有限公司 一种吉帕级冷轧高强钢及其生产方法
CN119715049A (zh) * 2023-09-28 2025-03-28 宝山钢铁股份有限公司 一种1200MPa冷轧超高强度钢拉伸标样的制作方法
CN118814054A (zh) * 2024-06-25 2024-10-22 包头钢铁（集团）有限责任公司 一种供中石油润滑油桶用冷轧低碳钢的制备方法
CN120719210B (zh) * 2025-08-28 2026-01-09 鞍钢股份有限公司 一种低成本420MPa级热轧车轮钢及其制备方法

Family Cites Families (24)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0635619B2 (ja) * 1986-02-05 1994-05-11 新日本製鐵株式会社 延性の良い高強度鋼板の製造方法
JP2652539B2 (ja) 1987-09-21 1997-09-10 株式会社神戸製鋼所 張出し成形性及び疲労特性にすぐれる複合組織高強度冷延鋼板の製造方法
JPH0735536B2 (ja) * 1988-01-14 1995-04-19 株式会社神戸製鋼所 高延性高強度複合組織鋼板の製造法
JP3257009B2 (ja) * 1991-12-27 2002-02-18 日本鋼管株式会社 高加工性高強度複合組織鋼板の製造方法
JP2776203B2 (ja) 1993-06-17 1998-07-16 住友金属工業株式会社 常温非時効性に優れた冷延鋼板の製造方法
JP3320014B2 (ja) 1997-06-16 2002-09-03 川崎製鉄株式会社 耐衝撃特性に優れた高強度高加工性冷延鋼板
TW504519B (en) * 1999-11-08 2002-10-01 Kawasaki Steel Co Hot dip galvanized steel plate excellent in balance of strength and ductility and in adhesiveness between steel and plating layer, and method for producing the same
CN1151301C (zh) * 2002-11-29 2004-05-26 武汉钢铁(集团)公司 超细化完整铁素体晶粒及残余奥氏体钢的生产方法
JP4268535B2 (ja) 2004-02-17 2009-05-27 株式会社神戸製鋼所 強度成形性バランスに優れた高強度冷延鋼板
CN100410410C (zh) * 2005-01-28 2008-08-13 株式会社神户制钢所 耐氢脆化性优异的高强度弹簧钢
JP3889768B2 (ja) 2005-03-31 2007-03-07 株式会社神戸製鋼所 塗膜密着性と延性に優れた高強度冷延鋼板および自動車用鋼部品
EP1749895A1 (fr) * 2005-08-04 2007-02-07 ARCELOR France Procédé de fabrication de tôles d'acier présentant une haute résistance et une excellente ductilité, et tôles ainsi produites
JP5402007B2 (ja) 2008-02-08 2014-01-29 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5438302B2 (ja) * 2008-10-30 2014-03-12 株式会社神戸製鋼所 加工性に優れた高降伏比高強度の溶融亜鉛めっき鋼板または合金化溶融亜鉛めっき鋼板とその製造方法
JP5185874B2 (ja) 2009-03-30 2013-04-17 株式会社神戸製鋼所 高強度鋼板の製造方法
JP5493986B2 (ja) * 2009-04-27 2014-05-14 Ｊｆｅスチール株式会社 加工性に優れた高強度鋼板および高強度溶融亜鉛めっき鋼板並びにそれらの製造方法
JP5703608B2 (ja) 2009-07-30 2015-04-22 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5333298B2 (ja) 2010-03-09 2013-11-06 Ｊｆｅスチール株式会社 高強度鋼板の製造方法
JP5327106B2 (ja) 2010-03-09 2013-10-30 Ｊｆｅスチール株式会社 プレス部材およびその製造方法
JP5668337B2 (ja) 2010-06-30 2015-02-12 Ｊｆｅスチール株式会社 延性及び耐遅れ破壊特性に優れる超高強度冷延鋼板およびその製造方法
EP2604715B1 (en) * 2010-08-12 2019-12-11 JFE Steel Corporation Method for manufacturing a high-strength cold-rolled steel sheet having excellent formability and crashworthiness
JP5462742B2 (ja) 2010-08-20 2014-04-02 株式会社神戸製鋼所 機械的特性の安定性に優れた高強度鋼板の製造方法
CN102409235A (zh) 2010-09-21 2012-04-11 鞍钢股份有限公司 高强度冷轧相变诱导塑性钢板及其制备方法
JP5857909B2 (ja) * 2012-08-09 2016-02-10 新日鐵住金株式会社 鋼板およびその製造方法

Also Published As

Publication number Publication date
JP6207621B2 (ja) 2017-10-04
ES2668653T3 (es) 2018-05-21
CN103805838A (zh) 2014-05-21
JP2016503458A (ja) 2016-02-04
US10287659B2 (en) 2019-05-14
WO2014075404A1 (zh) 2014-05-22
EP2921568A1 (en) 2015-09-23
KR20150086312A (ko) 2015-07-27
EP2921568B1 (en) 2018-04-11
MX2015005836A (es) 2015-09-24
EP2921568A4 (en) 2016-08-03
US20150337416A1 (en) 2015-11-26
CA2890126A1 (en) 2014-05-22
CA2890126C (en) 2021-05-04
CN103805838B (zh) 2017-02-08

Similar Documents

Publication Publication Date Title
MX368208B (es) Placa de acero laminada en frío de alta maleabilidad y superresistente, y método de fabricación de la misma.
JP2016513179A5 (es)
CN104694817B (zh) 超低碳冷轧钢板生产方法
BR112013011013A2 (pt) chapa de aço de alta resistência laminada a frio, possuindo excelente capacidade de estiramento profundo e excelente temperabilidade, e método para fabricação dessa chapa de aço
RU2017123716A (ru) Автомобильный алюминиевый лист высокой формуемости с уменьшенной или отсутствующей бороздчатостью поверхности и способ его получения
RU2012124187A (ru) Способ производства нетекстурированной электротехнической стали с высокой магнитной индукцией
IN2014MN01980A (es)
IN2015DN00610A (es)
IN2015DN00612A (es)
RU2013139431A (ru) Высокопрочная многофазная сталь для холодно- или горячекатаной стальной полосы и способ изготовления холодно- и горячекатаной стальной полосы
MX2014002935A (es) Metodo para producir una cinta electrica superiormente resistente de grano no orientado y su uso.
RU2013127584A (ru) Способ производства текстурированной электротехнической стали с высокими магнитными свойствами
CN105239001B (zh) 油汀用冷轧钢板及其制备方法
MY180218A (en) Method for manufacturing high strenght coll rolled steel sheet having excellent workability
MY161948A (en) Cold rolled steel sheet having excellent formability,shape fixability after aging,and method for manufacturing the same
IN2015KN00599A (es)
JP2010255069A5 (es)
CN100485074C (zh) 一种薄板坯连铸连轧生产if钢的生产工艺
JP2012177175A5 (es)
CN102816914B (zh) 一种冷轧钢板生产方法
CN105369133B (zh) 冰箱侧板用冷轧钢板及其制备方法
TH161402A (th) แผ่นเหล็กกล้ารีดเย็นแรงยึดสูงยิ่งยวดและมีอัตราขึ้นรูปงานสูงและวิธีการผลิตตัวมัน
TH134396A (th) แผ่นเหล็กกล้ารีดเย็นความแข็งแรงสูงอัตราส่วนการครากต่ำที่มีการยืดตัวและคุณสมบัติการขึ้นรูปปีกโค้งเว้าดีเลิศ รวมทั้งกรรมวิธีการผลิตนั้น
TH48765B (th) แผ่นเหล็กกล้ารีดเย็นความแข็งแรงสูงอัตราส่วนการครากต่ำที่มีการยืดตัวและคุณสมบัติการขึ้นรูปปีกโค้งเว้าดีเลิศ รวมทั้งกรรมวิธีการผลิตนั้น
TH135643A (th) แผ่นเหล็กกล้ารีดเย็นกำลังสูงที่มีสภาพดึงยืดได้ที่ดีและวิธีการสำหรับการผลิตสิ่งที่เหมือนกันนี้

Legal Events

Date Code Title Description
FG Grant or registration