MX2020009042A - Recubrimiento de aleacion a base de zinc para acero y metodos. - Google Patents
Recubrimiento de aleacion a base de zinc para acero y metodos.Info
- Publication number
- MX2020009042A MX2020009042A MX2020009042A MX2020009042A MX2020009042A MX 2020009042 A MX2020009042 A MX 2020009042A MX 2020009042 A MX2020009042 A MX 2020009042A MX 2020009042 A MX2020009042 A MX 2020009042A MX 2020009042 A MX2020009042 A MX 2020009042A
- Authority
- MX
- Mexico
- Prior art keywords
- zinc
- based alloy
- steel
- alloy coating
- methods
- Prior art date
Abstract
La presente descripción se refiere a un recubrimiento de aleación a base de zinc para tiras de acero a través de un proceso de galvanizado continuo. Este recubrimiento de aleación a base de zinc proporciona al acero una protección catódica antes y después de que el acero sea procesado por endurecimiento por presión a una temperatura de austenitización alta de hasta 950°C. El recubrimiento de aleación a base de zinc también reduce o elimina la susceptibilidad a la fragilización por metal líquido durante o después de la soldadura para diversos tipos de acero avanzado de resistencia ultra alta endurecidos sin presión. La aleación a base de zinc comprende al menos un elemento seleccionado de manganeso (Mb) y/o antimonio (Sb).
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US201862637102P | 2018-03-01 | 2018-03-01 | |
PCT/US2019/020154 WO2019169199A1 (en) | 2018-03-01 | 2019-02-28 | Zinc-based alloy coating for steel and methods |
Publications (1)
Publication Number | Publication Date |
---|---|
MX2020009042A true MX2020009042A (es) | 2021-01-08 |
Family
ID=67805952
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
MX2020009042A MX2020009042A (es) | 2018-03-01 | 2019-02-28 | Recubrimiento de aleacion a base de zinc para acero y metodos. |
Country Status (5)
Country | Link |
---|---|
US (1) | US20210108301A1 (es) |
EP (1) | EP3758888A4 (es) |
CA (1) | CA3092822A1 (es) |
MX (1) | MX2020009042A (es) |
WO (1) | WO2019169199A1 (es) |
Family Cites Families (17)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS5952947B2 (ja) * | 1980-01-29 | 1984-12-22 | 三菱マテリアル株式会社 | 溶融メツキ用亜鉛合金 |
JPS6055591B2 (ja) * | 1980-10-09 | 1985-12-05 | 新日本製鐵株式会社 | 耐経時めつき剥離性に優れた溶融亜鉛合金めつき鋼板の製造法 |
US5597656A (en) * | 1993-04-05 | 1997-01-28 | The Louis Berkman Company | Coated metal strip |
KR960006049B1 (ko) * | 1993-12-09 | 1996-05-08 | 포항종합제철주식회사 | 합금화 용융아연도금강판의 제조방법 |
JP3382697B2 (ja) * | 1994-02-01 | 2003-03-04 | 川崎製鉄株式会社 | 合金化溶融亜鉛めっき鋼板の製造方法 |
EP1707645B1 (en) * | 2004-01-14 | 2016-04-06 | Nippon Steel & Sumitomo Metal Corporation | Hot dip zinc plated high strength steel sheet excellent in plating adhesiveness and hole expanding characteristics |
MX2010003835A (es) * | 2007-10-10 | 2010-05-13 | Nucor Corp | Acero estructurado metalografico complejo y metodo para manufacturarlo. |
TWI396772B (zh) * | 2009-02-03 | 2013-05-21 | Nippon Steel & Sumitomo Metal Corp | 合金化熔融鍍鋅鋼板及其製造方法 |
TWI447262B (zh) * | 2011-09-30 | 2014-08-01 | Nippon Steel & Sumitomo Metal Corp | 鍍鋅鋼板及其製造方法 |
PL2762585T3 (pl) * | 2011-09-30 | 2020-01-31 | Nippon Steel Corporation | Blacha stalowa cienka o dużej wytrzymałości cynkowana zanurzeniowo na gorąco o doskonałych właściwościach skrawania mechanicznego, stopowa blacha stalowa cienka o dużej wytrzymałości cynkowana zanurzeniowo na gorąco oraz sposób wytwarzania wspomnianych blach cienkich |
JP2013189671A (ja) * | 2012-03-13 | 2013-09-26 | Jfe Steel Corp | 溶融Al−Zn系めっき鋼板 |
MA37745B1 (fr) * | 2013-05-13 | 2016-08-31 | Arcelormittal | Assemblage d'une pièce à base d'aluminium et d'une pièce en acier munie d'un revêtement à base d'un alliage znaimg |
JP6470266B2 (ja) * | 2013-05-17 | 2019-02-13 | エーケー スティール プロパティ−ズ、インク. | プレス焼入れ用亜鉛めっき鋼材およびその製造方法 |
DE102013015032A1 (de) * | 2013-09-02 | 2015-03-05 | Salzgitter Flachstahl Gmbh | Zinkbasierte Korrosionsschutzbeschichtung für Stahlbleche zur Herstellung eines Bauteils bei erhöhter Temperatur durch Presshärten |
CN104099550A (zh) * | 2014-06-27 | 2014-10-15 | 陕西理工学院 | 一种热浸镀Zn-Al-Mn合金的制备方法及热浸镀工艺 |
WO2017033901A1 (ja) * | 2015-08-24 | 2017-03-02 | 新日鐵住金株式会社 | 合金化溶融亜鉛めっき鋼板及びその製造方法 |
KR101819393B1 (ko) * | 2016-12-22 | 2018-01-16 | 주식회사 포스코 | 용접성 및 프레스 가공성이 우수한 용융 아연계 도금강재 및 그 제조방법 |
-
2019
- 2019-02-28 CA CA3092822A patent/CA3092822A1/en active Pending
- 2019-02-28 MX MX2020009042A patent/MX2020009042A/es unknown
- 2019-02-28 US US16/462,885 patent/US20210108301A1/en active Pending
- 2019-02-28 EP EP19759954.1A patent/EP3758888A4/en active Pending
- 2019-02-28 WO PCT/US2019/020154 patent/WO2019169199A1/en active Application Filing
Also Published As
Publication number | Publication date |
---|---|
EP3758888A1 (en) | 2021-01-06 |
WO2019169199A1 (en) | 2019-09-06 |
CA3092822A1 (en) | 2019-09-06 |
US20210108301A1 (en) | 2021-04-15 |
EP3758888A4 (en) | 2021-12-22 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
RU2683397C1 (ru) | Стальной лист для горячей штамповки, способ производства стального листа для горячей штамповки, а также формируемое горячей штамповкой тело | |
JP6718656B2 (ja) | プレス焼入れ用亜鉛めっき鋼材およびその製造方法 | |
US20160122889A1 (en) | Producing a product from a flexible rolled strip material | |
US20160215376A1 (en) | Zinc-based anti-corrosion coating for steel sheets, for producing a component at an elevated temperature by hot forming die quenching | |
JP6668323B2 (ja) | 溶融亜鉛系コーティングを有する高強度高成形性帯鋼 | |
MX2016013771A (es) | Metodo para la produccion de lamina de acero galvanizada de alta resistencia y lamina de acero galvano-recocida de alta resistencia. | |
WO2012085248A3 (de) | Verfahren zum umformen und härten von beschichteten stahlblechen | |
UA100522C2 (ru) | Композиция для предварительной обработки металлической основы и способ обработки металлической основы | |
US9938600B2 (en) | Manufacturing a hardened formed part | |
MX2019004000A (es) | Lamina de acero recubierta de metal, metodo de fabricacion de lamina de acero galvanizada por inmersion en caliente, y metodo de fabricacion de lamina de acero galvanizada-recocida aleada. | |
JP2015520797A (ja) | 犠牲カソード防食を提供するコーティングを備えた鋼板、こうした鋼板を用いる部品の製造方法、および得られた部品 | |
MY171301A (en) | High-strength plated steel plate for welded structural member, and method for producing the same | |
EP3006586A1 (en) | Heat-treated steel material and method for producing same | |
JP2016520162A5 (es) | ||
MX2017010339A (es) | Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma. | |
JP2011117086A (ja) | 耐食性、耐疲労性に優れた高強度焼き入れ成形体 | |
MX2023002114A (es) | Lamina de acero laminada en caliente. | |
CN104136644A (zh) | 含Si高强度冷轧钢板及其制造方法以及汽车构件 | |
HUE060841T2 (hu) | Eljárás vas- és acéltermékek galvanizálására, különösen tûzihorganyzására | |
MX2020009042A (es) | Recubrimiento de aleacion a base de zinc para acero y metodos. | |
WO2016146581A1 (en) | Steel for hot forming | |
UA119946C2 (uk) | Спосіб виробництва надвисокоміцної листової сталі, підданої цинкуванню з відпалюванням, і одержана листова сталь, піддана цинкуванню з відпалюванням | |
MX2017014559A (es) | Componente endurecido por deformacion hecho de acero galvanizado, metodo de produccion para el mismo y metodo para producir una tira de acero adecuada para el endurecimiento por deformacion de los componentes. | |
MX2023001627A (es) | Lamina de acero laminada en caliente. | |
JP2011184797A (ja) | 耐食性、耐疲労性に優れた高強度焼き入れ成形体 |