MX2015011581A - Lamina de acero galvanizada de alta resistencia y metodo para la produccion de la misma. - Google Patents

Lamina de acero galvanizada de alta resistencia y metodo para la produccion de la misma.

Info

Publication number
MX2015011581A
MX2015011581A MX2015011581A MX2015011581A MX2015011581A MX 2015011581 A MX2015011581 A MX 2015011581A MX 2015011581 A MX2015011581 A MX 2015011581A MX 2015011581 A MX2015011581 A MX 2015011581A MX 2015011581 A MX2015011581 A MX 2015011581A
Authority
MX
Mexico
Prior art keywords
steel sheet
dip galvanized
galvanized steel
strength hot
steel
Prior art date
Application number
MX2015011581A
Other languages
English (en)
Inventor
Yasunobu Nagataki
Yoichi Makimizu
Yoshitsugu Suzuki
Original Assignee
Jfe Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jfe Steel Corp filed Critical Jfe Steel Corp
Publication of MX2015011581A publication Critical patent/MX2015011581A/es

Abstract

Se proporcionan una lámina de acero galvanizada de alta resistencia cuyo acero base es una lámina de acero de alta resistencia que contiene Si, Mn, y B y la cual tiene buena adherencia del recubrimiento y un método de producción para la misma. Una lámina de acero base que contiene Si, Mn, y B se oxida a una temperatura de calentamiento de lámina de acero T que satisface la fórmula a continuación, y posteriormente se somete a recocido por reducción y galvanización. T = 58.65 x [Si] + 29440 x [B] - 13.59 x [O2] + 548.1 [Si]: contenido de Si en el acero sobre una base de por ciento en masa [B]: contenido de B en el acero base sobre una base de por ciento en masa [O2]: concentración de O2 sobre una base de por ciento en volumen en una atmósfera en tratamiento de oxidación.
MX2015011581A 2013-03-05 2014-02-28 Lamina de acero galvanizada de alta resistencia y metodo para la produccion de la misma. MX2015011581A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2013042854A JP5920249B2 (ja) 2013-03-05 2013-03-05 めっき密着性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
PCT/JP2014/001108 WO2014136417A1 (ja) 2013-03-05 2014-02-28 高強度溶融亜鉛めっき鋼板およびその製造方法

Publications (1)

Publication Number Publication Date
MX2015011581A true MX2015011581A (es) 2015-12-09

Family

ID=51490953

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2015011581A MX2015011581A (es) 2013-03-05 2014-02-28 Lamina de acero galvanizada de alta resistencia y metodo para la produccion de la misma.

Country Status (7)

Country Link
US (1) US20160017471A1 (es)
EP (1) EP2942419A4 (es)
JP (1) JP5920249B2 (es)
KR (1) KR101752077B1 (es)
CN (1) CN105026599B (es)
MX (1) MX2015011581A (es)
WO (1) WO2014136417A1 (es)

Families Citing this family (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6237937B2 (ja) * 2016-03-11 2017-11-29 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法
CN106222541B (zh) * 2016-08-26 2018-06-08 武汉钢铁有限公司 一种屈服强度为250MPa级的铁-锌镀层钢板及生产方法
CN106119714B (zh) * 2016-08-26 2018-08-07 武汉钢铁有限公司 一种屈服强度为310MPa级的铁-锌镀层钢板及生产方法
CN106191663B (zh) * 2016-08-26 2018-05-01 武汉钢铁有限公司 一种屈服强度为280MPa级的铁-锌镀层钢板及生产方法
CN106086633B (zh) * 2016-08-26 2018-05-01 武汉钢铁有限公司 一种屈服强度为210MPa级的铁-锌镀层钢板及生产方法
CN106367690A (zh) * 2016-08-31 2017-02-01 宁波耐可邦制冷配件有限公司 一种制冷压缩机用滚动活塞及其制造方法
JP6822506B2 (ja) * 2019-03-22 2021-01-27 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法

Family Cites Families (19)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS55122865A (en) 1979-03-12 1980-09-20 Nippon Steel Corp Molten zinc plating method for difficult plating steel sheet
JP2587724B2 (ja) 1990-11-30 1997-03-05 新日本製鐵株式会社 めっき密着性の良好な高Ｓｉ含有高張力溶融亜鉛めっき鋼板の製造方法
JP2530939B2 (ja) 1990-11-30 1996-09-04 新日本製鐵株式会社 高Ｓｉ含有高張力溶融亜鉛めっき鋼板の製造方法
JP2513532B2 (ja) 1990-11-30 1996-07-03 新日本製鐵株式会社 高Ｓｉ含有鋼の高張力溶融亜鉛めっき鋼板の製造方法
JP2587725B2 (ja) 1990-11-30 1997-03-05 新日本製鐵株式会社 Ｐ含有高張力合金化溶融亜鉛めっき鋼板の製造方法
JPH04254531A (ja) 1991-02-01 1992-09-09 Nippon Steel Corp 高Ｓｉ含有高張力鋼の溶融亜鉛めっき前の焼鈍方法
JPH04254532A (ja) 1991-02-01 1992-09-09 Nippon Steel Corp 加工性の優れた合金化溶融亜鉛めっき鋼板の製造方法
JP3255765B2 (ja) 1993-07-14 2002-02-12 川崎製鉄株式会社 高張力溶融または合金化溶融亜鉛めっき鋼板の製造方法
JP4741376B2 (ja) 2005-01-31 2011-08-03 新日本製鐵株式会社 外観が良好な高強度合金化溶融亜鉛めっき鋼板及びその製造方法と製造設備
JP4589880B2 (ja) 2006-02-08 2010-12-01 新日本製鐵株式会社 成形性と穴拡げ性に優れた高強度溶融亜鉛めっき鋼板と高強度合金化溶融亜鉛めっき鋼板及び高強度溶融亜鉛めっき鋼板の製造方法並びに高強度合金化溶融亜鉛めっき鋼板の製造方法
CA2647687C (en) * 2006-04-26 2012-10-02 Thyssenkrupp Steel Ag Hot dip coating process for a steel plate product made of high strengthheavy-duty steel
JP4411326B2 (ja) 2007-01-29 2010-02-10 株式会社神戸製鋼所 リン酸塩処理性に優れた高強度合金化溶融亜鉛めっき鋼板
EP2009129A1 (en) * 2007-06-29 2008-12-31 ArcelorMittal France Process for manufacturing a galvannealed steel sheet by DFF regulation
EP2009127A1 (en) * 2007-06-29 2008-12-31 ArcelorMittal France Process for manufacturing a galvanized or a galvannealed steel sheet by DFF regulation
JP2011026674A (ja) * 2009-07-28 2011-02-10 Jfe Steel Corp 耐めっき剥離性に優れる高強度溶融亜鉛めっき鋼板
JP5667363B2 (ja) * 2009-11-02 2015-02-12 株式会社神戸製鋼所 溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板の製造方法
JP5513148B2 (ja) * 2009-11-19 2014-06-04 株式会社神戸製鋼所 めっき鋼板、およびその製造方法
JP5513216B2 (ja) * 2010-03-31 2014-06-04 株式会社神戸製鋼所 合金化溶融亜鉛めっき鋼板の製造方法
JP5966528B2 (ja) * 2011-06-07 2016-08-10 Ｊｆｅスチール株式会社 めっき密着性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法

Also Published As

Publication number Publication date
KR101752077B1 (ko) 2017-06-28
EP2942419A4 (en) 2016-02-24
JP2014169489A (ja) 2014-09-18
WO2014136417A1 (ja) 2014-09-12
US20160017471A1 (en) 2016-01-21
JP5920249B2 (ja) 2016-05-18
EP2942419A1 (en) 2015-11-11
CN105026599A (zh) 2015-11-04
KR20150123919A (ko) 2015-11-04
CN105026599B (zh) 2017-10-10

Similar Documents

Publication Publication Date Title
MX2015011581A (es) Lamina de acero galvanizada de alta resistencia y metodo para la produccion de la misma.
MX2014012798A (es) Metodo de fabricacion de hoja de acero galvanizado para estampacion en caliente, hoja de acero galvanizado y recocido por inmersion en caliente para estampacion en caliente y metodo de fabricacion de las mismas, y componente estampado en caliente.
MX2016016129A (es) Hoja de acero galvanizada multifasica de alta resistencia, metodo de produccion y uso.
MX2016007518A (es) Metodo para la produccion de laminas de acero recocidas despues de galvanizadas de alta resistencia.
MX2015005838A (es) Plancha de acero galvanizado en caliente super-resistente y de elevada aptitud de conformacion y su metodo de fabricacion.
UA118036C2 (uk) Високоміцна сталь та спосіб виготовлення
MX2019004000A (es) Lamina de acero recubierta de metal, metodo de fabricacion de lamina de acero galvanizada por inmersion en caliente, y metodo de fabricacion de lamina de acero galvanizada-recocida aleada.
MX2013012422A (es) Lamina de acero para miembro de estampado en caliente y metodo para producir la misma.
MX2018003455A (es) Lamina de acero galvanizado para prensado en caliente y metodo para la produccion de articulo moldeado prensado en caliente.
MX2017011825A (es) Lamina de acero laminada en frio de alta resistencia y metodo para producir la misma.
MX2013009235A (es) Acero inoxidable duplex y metodo para la produccion del mismo.
MX2015015890A (es) Metodo para la fabricacion de una lamina de acero recocida despues de galvanizada de alta resistencia.
MX2016003144A (es) Laminas de acero galvanizadas por inmersion en caliente y laminas de acero recocidas despues de galvanizadas que tienen buen aspecto y buena adherencia al recubrimiento y metodos para la produccion de las mismas.
MX2016000008A (es) Lamina de acero laminada en caliente de alto contenido en carbono y metodo para la produccion de la misma.
JP2014208902A5 (ja) めっき密着性に優れた溶融亜鉛系めっき鋼板の製造方法
MX2021013782A (es) Acero recubierto con zinc para aplicaciones de conformado en caliente y metodo de produccion.
MX2017005505A (es) Lamina de acero galvanizado por inmersion en caliente.
MX2015016367A (es) Placa de acero laminada en frio, placa de acero laminada en frio galvanizada, y metodo para manufacturar las placas.
MX366776B (es) Lamina de acero, laminada en caliente, recocida y galvanizada por inmersion en caliente, y proceso para producir la misma.
MX2016003143A (es) Laminas de acero galvanizadas por inmersion en caliente y laminas de acero recocidas despues de galvanizadas que tienen buen aspecto y buena adherencia al recubrimiento y metodos para la produccion de las mismas.
MX354352B (es) Lámina de acero galvanizado de alta resistencia excelente en términos de adherencia de recubrimiento y método para la fabricación de la misma.
MX2017006374A (es) Acero multifase ultra resistente de endurecimiento al aire teniendo propiedades excelentes de procesamiento y metodo para produccion de cinta del acero referido.
MX2015011463A (es) Lamina de acero de alta resistencia y metodo para la produccion de la misma y lamina de acero galvanizada de alta resistencia y metodo para la produccion de la misma.
MX2020006052A (es) Lamina de acero laminada en caliente de alto contenido en carbono y metodo para la produccion de la misma.
EP3598121A4 (en) METHOD FOR MEASURING MAGNETIC TRANSFORMATION RATE OF STEEL PLATE IN AN ANNUIT OVEN, ASSOCIATED DEVICE FOR MEASURING MAGNETIC TRANSFORMATION RATE, CONTINUOUS ANNUIT PROCESS AND CONTINUOUS HOT GALVANIZATION PROCESS