MX366776B - Lamina de acero, laminada en caliente, recocida y galvanizada por inmersion en caliente, y proceso para producir la misma. - Google Patents

Lamina de acero, laminada en caliente, recocida y galvanizada por inmersion en caliente, y proceso para producir la misma.

Info

Publication number
MX366776B
MX366776B MX2014011901A MX2014011901A MX366776B MX 366776 B MX366776 B MX 366776B MX 2014011901 A MX2014011901 A MX 2014011901A MX 2014011901 A MX2014011901 A MX 2014011901A MX 366776 B MX366776 B MX 366776B
Authority
MX
Mexico
Prior art keywords
less
steel sheet
rolled steel
inclusive
hot
Prior art date
Application number
MX2014011901A
Other languages
English (en)
Other versions
MX2014011901A (es
Inventor
Yokoyama Takafumi
Nomura Shigeki
Original Assignee
Nippon Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel Corp filed Critical Nippon Steel Corp
Publication of MX2014011901A publication Critical patent/MX2014011901A/es
Publication of MX366776B publication Critical patent/MX366776B/es

Abstract

En una lámina de acero laminada en caliente recocida y galvanizada por inmersión en caliente de alta resistencia que tiene una excelente capacidad de expansión, adecuada para rebordeado, y tiene de manera preferente una alta relación elástica y una resistencia a la tracción de al menos 650 MPa, una lámina de acero laminada en caliente usada como un material base para recubrimiento electrolítico tiene una composición química que comprende: en % en masa, C: desde al menos 0.01% y a lo mucho 0.20%; Si: a lo mucho 0.50%; Mn: desde al menos 0.01% a lo mucho 1.30%; P: a lo mucho 0.05%; S: a lo mucho 0.01%; N: a lo mucho 0.01%; Al: a lo mucho 0.50%; y Ti: desde al menos 0.05% a lo mucho 0.50%; y una estructura de acero que consiste de una ferrita poligonal que tiene al menos 80% de área y el resto que consiste de una clase o dos o más clases seleccionadas de ferrita bainítica, bainita, perlita, y cementita.
MX2014011901A 2012-04-06 2012-09-11 Lamina de acero, laminada en caliente, recocida y galvanizada por inmersion en caliente, y proceso para producir la misma. MX366776B (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2012087539 2012-04-06
PCT/JP2012/073163 WO2013150669A1 (ja) 2012-04-06 2012-09-11 合金化溶融亜鉛めっき熱延鋼板およびその製造方法

Publications (2)

Publication Number Publication Date
MX2014011901A MX2014011901A (es) 2015-05-08
MX366776B true MX366776B (es) 2019-07-23

Family

ID=49300186

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2014011901A MX366776B (es) 2012-04-06 2012-09-11 Lamina de acero, laminada en caliente, recocida y galvanizada por inmersion en caliente, y proceso para producir la misma.

Country Status (11)

Country Link
US (1) US10351942B2 (es)
EP (1) EP2835440B1 (es)
JP (1) JP5339005B1 (es)
KR (2) KR20160121599A (es)
CN (1) CN104364408B (es)
BR (1) BR112014024879B1 (es)
ES (1) ES2699996T3 (es)
IN (1) IN2014DN08590A (es)
MX (1) MX366776B (es)
PL (1) PL2835440T3 (es)
WO (1) WO2013150669A1 (es)

Families Citing this family (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE102014017274A1 (de) * 2014-11-18 2016-05-19 Salzgitter Flachstahl Gmbh Höchstfester lufthärtender Mehrphasenstahl mit hervorragenden Verarbeitungseigenschaften und Verfahren zur Herstellung eines Bandes aus diesem Stahl
BR112018000633A2 (pt) * 2015-07-31 2018-09-18 Nippon Steel & Sumitomo Metal Corporation chapa de aço laminada a quente de alta resistência
JP6398967B2 (ja) * 2015-12-25 2018-10-03 Ｊｆｅスチール株式会社 表面外観及びめっき密着性に優れた高強度溶融めっき熱延鋼板およびその製造方法
KR101839227B1 (ko) * 2016-09-12 2018-03-16 주식회사 포스코 피로저항성이 우수한 파이프용 강재, 이의 제조방법 및 이를 이용한 용접강관
JP6801717B2 (ja) * 2016-09-30 2020-12-16 日本製鉄株式会社 冷間鍛造用鋼及びその製造方法
KR101889174B1 (ko) * 2016-12-13 2018-08-16 주식회사 포스코 저온역 버링성이 우수한 고항복비형 고강도강 및 그 제조방법
CN107858497B (zh) * 2017-12-19 2019-04-26 温州市研制阀门厂 一种能够提高锻件质量的热处理工艺
KR102098478B1 (ko) * 2018-07-12 2020-04-07 주식회사 포스코 고강도, 고성형성, 우수한 소부경화성을 갖는 열연도금강판 및 그 제조방법
CN111690869A (zh) * 2019-03-11 2020-09-22 上海梅山钢铁股份有限公司 一种冷弯钢板桩用热轧钢板及其制造方法
CN110983196A (zh) * 2019-12-17 2020-04-10 首钢集团有限公司 一种600MPa级热轧镀锌高扩孔钢及其生产方法
EP3925771A1 (en) * 2020-06-16 2021-12-22 SSAB Technology AB High strength steel product and method of manufacturing the same
KR102403648B1 (ko) * 2020-11-17 2022-05-30 주식회사 포스코 고강도 열연강판, 열연 도금강판 및 이들의 제조방법
CN113215485B (zh) * 2021-04-15 2022-05-17 首钢集团有限公司 一种780MPa级热基镀层双相钢及其制备方法
CN113957337A (zh) * 2021-09-24 2022-01-21 河钢股份有限公司承德分公司 一种含钒热基镀锌板及其制备方法
EP4180544A1 (en) * 2021-11-11 2023-05-17 SSAB Technology AB A hot-rolled steel strip product and method for its production

Family Cites Families (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2783809B2 (ja) * 1988-06-28 1998-08-06 川崎製鉄株式会社 冷間加工性および溶接性に優れた引張り強さが５５▲ｋｇ▼ｆ／▲ｍｍ▼▲上２▼以上の高張力熱延鋼帯
JP2563021B2 (ja) 1991-10-25 1996-12-11 株式会社神戸製鋼所 伸びフランジ性の優れた高強度熱延原板合金化溶融亜鉛めっき鋼板の製造方法
JP3048278B2 (ja) 1992-05-27 2000-06-05 株式会社神戸製鋼所 溶接部の疲労特性が優れた高強度熱延原板合金化溶融亜鉛めっき鋼板及びその製造方法
JPH0826433B2 (ja) 1992-12-28 1996-03-13 株式会社神戸製鋼所 伸びフランジ性に優れた高強度熱延鋼板
JP3577987B2 (ja) * 1999-04-08 2004-10-20 Ｊｆｅスチール株式会社 プレス成形用熱延鋼板およびその製造方法
JP2001234282A (ja) * 2000-02-21 2001-08-28 Kawasaki Steel Corp 温間プレス成形性に優れた高張力熱延鋼板およびその製造方法
US20030015263A1 (en) * 2000-05-26 2003-01-23 Chikara Kami Cold rolled steel sheet and galvanized steel sheet having strain aging hardening property and method for producing the same
JP3680262B2 (ja) 2000-06-28 2005-08-10 Ｊｆｅスチール株式会社 伸びフランジ性に優れた溶融亜鉛めっき鋼板およびその製造方法
EP1176217B1 (en) 2000-07-24 2011-12-21 KABUSHIKI KAISHA KOBE SEIKO SHO also known as Kobe Steel Ltd. High-strength hot-rolled steel sheet superior in strech flange formability and method for production thereof
JP2002322539A (ja) * 2001-01-31 2002-11-08 Nkk Corp プレス成形性に優れた薄鋼板およびその加工方法
JP2004043978A (ja) * 2001-02-20 2004-02-12 Jfe Steel Kk 加工性に優れた高張力鋼板ならびにその製造方法および加工方法
US6669789B1 (en) 2001-08-31 2003-12-30 Nucor Corporation Method for producing titanium-bearing microalloyed high-strength low-alloy steel
JP3821043B2 (ja) 2002-04-30 2006-09-13 Ｊｆｅスチール株式会社 溶接性に優れた溶融亜鉛系めっき高張力熱延鋼板ならびにその製造方法および加工方法
JP3760888B2 (ja) * 2002-04-30 2006-03-29 Ｊｆｅスチール株式会社 加工性に優れた高張力冷延鋼板ならびにその製造方法および加工方法
JP4649868B2 (ja) * 2003-04-21 2011-03-16 Ｊｆｅスチール株式会社 高強度熱延鋼板およびその製造方法
EP1681362B1 (en) * 2003-10-17 2012-08-22 Nippon Steel Corporation High strength thin steel sheet excellent in hole expansibility and ductility
US7955444B2 (en) * 2005-08-05 2011-06-07 Jfe Steel Corporation High strength steel sheet and method for manufacturing the same
JP4853075B2 (ja) * 2006-03-28 2012-01-11 住友金属工業株式会社 ハイドロフォーム加工用熱延鋼板及びその製造法と、ハイドロフォーム加工用電縫鋼管
JP5142141B2 (ja) * 2008-01-24 2013-02-13 新日鐵住金株式会社 ハイドロフォーム加工用鋼管素材熱延鋼板およびハイドロフォーム加工用鋼管ならびにそれらの製造方法
WO2009118945A1 (ja) * 2008-03-26 2009-10-01 新日本製鐵株式会社 疲労特性と伸びフランジ性に優れた熱延鋼板およびその製造方法
WO2009119751A1 (ja) * 2008-03-27 2009-10-01 新日本製鐵株式会社 成形性と溶接性に優れた高強度冷延鋼板、高強度亜鉛めっき鋼板、高強度合金化溶融亜鉛めっき鋼板、及びそれらの製造方法
WO2010131303A1 (ja) * 2009-05-11 2010-11-18 新日本製鐵株式会社 打抜き加工性と疲労特性に優れた熱延鋼板、溶融亜鉛めっき鋼板、およびそれらの製造方法
JP5041083B2 (ja) 2010-03-31 2012-10-03 Ｊｆｅスチール株式会社 加工性に優れた高張力溶融亜鉛めっき鋼板およびその製造方法
JP5765080B2 (ja) 2010-06-25 2015-08-19 Ｊｆｅスチール株式会社 伸びフランジ性に優れた高強度熱延鋼板およびその製造方法
JP5609786B2 (ja) * 2010-06-25 2014-10-22 Ｊｆｅスチール株式会社 加工性に優れた高張力熱延鋼板およびその製造方法

Also Published As

Publication number Publication date
KR20160121599A (ko) 2016-10-19
US10351942B2 (en) 2019-07-16
BR112014024879B1 (pt) 2019-01-22
EP2835440A4 (en) 2016-01-13
CN104364408A (zh) 2015-02-18
IN2014DN08590A (es) 2015-05-22
JPWO2013150669A1 (ja) 2015-12-17
EP2835440B1 (en) 2018-08-29
WO2013150669A1 (ja) 2013-10-10
US20150140358A1 (en) 2015-05-21
EP2835440A1 (en) 2015-02-11
CN104364408B (zh) 2016-10-26
MX2014011901A (es) 2015-05-08
KR20150000897A (ko) 2015-01-05
JP5339005B1 (ja) 2013-11-13
PL2835440T3 (pl) 2019-02-28
ES2699996T3 (es) 2019-02-13

Similar Documents

Publication Publication Date Title
MX366776B (es) Lamina de acero, laminada en caliente, recocida y galvanizada por inmersion en caliente, y proceso para producir la misma.
UA118036C2 (uk) Високоміцна сталь та спосіб виготовлення
MX2020003923A (es) Lamina de acero laminada en caliente de alta resistencia y metodo para la fabricacion de la misma.
MX2017009200A (es) Lamina de acero galvanizada de alta resistencia y metodo para producir la misma.
MX2017001529A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma, y metodo de produccion para lamina de acero galvanizada de alta resistencia.
MX2018001082A (es) Lamina de acero laminada en caliente de alta resistencia y metodo para la fabricacion de la misma.
MX2016007954A (es) Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma.
MX2010008558A (es) Lamina de acero recubierta con zinc por inmersion en caliente, de alta tenacidad, excelente en trabajabilidad y procedimiento para la produccion de la misma.
MX2017001689A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma, y metodo de produccion para lamina de acero galvanizada de alta resistencia.
MX2018009643A (es) Lamina de acero de alta resistencia y metodo para la produccion de la misma.
MX2016009745A (es) Lamina de acero laminada en frio de alta resistencia y metodo para la fabricacion de la misma.
MX357839B (es) Hoja de acero platinada con zinc de alta resistencia y lámina de acero de alta resistencia que tiene maleabilidad superior y método para producir cada una de ellas.
MX2018009735A (es) Lamina de acero de alta resistencia y metodo para fabricar la misma.
WO2016098964A8 (ko) 재질 불균일이 작고 성형성이 우수한 고강도 냉연강판, 용융아연도금강판, 및 그 제조 방법
MX335961B (es) Lamina de acero laminada en frio de alta resistencia y metodo para la fabricacion de la misma.
MX2013002893A (es) Chapa delgada de acero laminada en caliente de alta resistencia que tiene excelente resistencia a la fatiga y metodo para fabricar la misma.
MX2014009471A (es) Plancha de acero laminada en frio de alta resistencia y proceso para fabricar la misma.
MX2018007641A (es) Metodo para producir una lamina de acero de alta resistencia que tiene resistencia y formabilidad mejoradas, y la lamina de acero de alta resistencia obtenida.
MX335950B (es) Lamina de acero galvanizado de alta resistencia que tiene excelente formabilidad y metodo para manufacturar la misma.
MX2017001720A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma, y metodo de produccion para lamina de acero galvanizada de alta resistencia.
MX2015013579A (es) Lamina de acero recocida despues de galvanizada de alta resistencia y metodo para la fabricacion de la misma.
MX356054B (es) Lámina de acero laminada en frío, de alta resistencia y método para la fabricación de la misma.
MX2017011825A (es) Lamina de acero laminada en frio de alta resistencia y metodo para producir la misma.
MX2015007724A (es) Lamina de acero laminada en frio de alta resistencia con bajo limite de elasticidad y metodo para la fabricacion de la misma.
UA113404C2 (xx) Гарячекатаний сталевий лист та спосіб його виготовлення

Legal Events

Date Code Title Description
FG Grant or registration