KR970021171A - 타이어 트레드의 제조시 사용할 수 있는 유기 실란 유도체를 포함하는 디엔 중합체를 기재로 하는 고무 조성물 - Google Patents

타이어 트레드의 제조시 사용할 수 있는 유기 실란 유도체를 포함하는 디엔 중합체를 기재로 하는 고무 조성물 Download PDF

Info

Publication number
KR970021171A
KR970021171A KR1019960024829A KR19960024829A KR970021171A KR 970021171 A KR970021171 A KR 970021171A KR 1019960024829 A KR1019960024829 A KR 1019960024829A KR 19960024829 A KR19960024829 A KR 19960024829A KR 970021171 A KR970021171 A KR 970021171A
Authority
KR
South Korea
Prior art keywords
functionalized
functional group
modified
carbon black
composition
Prior art date
Application number
KR1019960024829A
Other languages
English (en)
Other versions
KR100413300B1 (ko
Inventor
라보즈 제라르
Original Assignee
쟝-이브 모노
꽁빠니 제네랄르 데 제따블리스망 미쉐린-미쉐린 에 꽁빠니
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 쟝-이브 모노, 꽁빠니 제네랄르 데 제따블리스망 미쉐린-미쉐린 에 꽁빠니 filed Critical 쟝-이브 모노
Publication of KR970021171A publication Critical patent/KR970021171A/ko
Application granted granted Critical
Publication of KR100413300B1 publication Critical patent/KR100413300B1/ko

Abstract

본 발명은 알콕시실란 유도체에 의해 작용화되거나 개질된 하나 이상의 디엔 중합체와 1차 또는 2차 아민 작용기 또는 이민 작용기를 포함하는 하나 이상의 유기 실란 화합물을 포함하는, 카본 블랙 및 가능한 경우 카본 블랙과 실리카로 보강된, 타이어의 제조시 사용될 수 있는, 특히 이력 특성이 향상된 고무 조성물에 관한 것이다.

Description

타이어 트레드의 제조시 사용할 수 있는 유기 실란 유도체를 포함하는 디엔 중합체를 기재로 하는 고무 조성물
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (17)

  1. 작용화거나 개질된 하나 이상의 디엔 중합체와 보강 충전제로서의 카본 블랙 또는 카본 블랙과 실리카와의 혼합물을 포함하는 가황성 고무 조성물로서, 작용화되거나 개질된 디엔 중합체가 알콕시실란 유도체에 의해 작용화되거나 개질된 중합체이고, 아민 또는 이민 작용기를 포함하는 하나 이상의 일반식(Ⅰ)의 유기 실란 화합물을 추가로 포함함을 특징으로 하는 가황성 고무 조성물.
    Z-R1-Si(OR2)3-n(R3)n(Ⅰ)
    상기 식에서, Z는 1차 아민 작용기, 사이클릭 또는 비사이클릭 2차 아민 작용기, 이민 작용기 또는 폴리아민 라디칼이고, R1, R2및 R3은 동일하거나 상이하고 탄소수 1 내지 12, 바람직하게는 1 내지 4의 알킬, 아릴, 알크아릴 또는 아르알킬 라디칼이며, n은 0, 1 및 2의 값으로부터 선택된 정수이다.
  2. 제1항에 있어서, 일반식(Ⅰ)의 화합물의 라디칼 R2가 탄소수 1 내지 4의 저급 알킬 라디칼임을 특징으로 하는 조성물.
  3. 제1항에 있어서, 알콕시실란 작용화 디엔 중합체가 일반식(Ⅱ)로 표시됨을 특징으로 하는 조성물.
    (Y)-R5-Si(OR4)2-P (Ⅱ)
    상기 식에서, Y는 할로겐 또는 알킬 에폭시, 글리시딜옥시, 비닐 또는 알릴 라디칼이고, R5및 R4'는 동일하거나 상이하며 탄소수 1 내지 12의 알킬, 아릴, 알크아릴 또는 아르알킬 라디칼이며, P는 탄소수 4 내지 12의 공액 디엔 단량체를 중합시켜 수득한 임의의 단독중합체 및 서로 공액되거나 탄소수 8 내지 20의 하나 이상의 방향족 비닐 화합물과 함께 공액된 하나 이상의 디엔을 공중합시켜 수득한 공중합체의 그룹으로부터 선택된 디엔 중합체 쇄이다.
  4. 제3항에 있어서, 알콕시실란 작용화 디엔 중합체가 3-글리시딜옥시프로필트리메톡시실란 또는 2-(3,4-에폭시 사이클로헥실)-에틸트리메톡시실란에 의해 작용화됨을 특징으로 하는 조성물.
  5. 제1항에 있어서, 디엔 중합체가 부타디엔-스티렌 공중합체 또는 부타디엔-스티렌-이소프렌 공중합체임을 특징으로 하는 조성물.
  6. 제1항에 있어서, 카본 블랙이 보강 충전제의 전부임을 특징으로 하는 조성물.
  7. 제1항에 있어서, 보강 충전제가, 카본 블랙과, 전체 충전제의 70중량% 이하의 실리카와의 혼합물로 이루어짐을 특징으로 하는 조성물.
  8. 제7항에 있어서, 실리카가, CTAB 비표면적이 450㎡/g 이하인 고분산성 침강 실리카임을 특징으로 하는 조성물.
  9. 제8항에 있어서, 실리카의 BET 비표면적이 100 내지 300㎡/g이 CTAB 비표면적에 대한 BET 비표면적의 비가 1 내지 1.2임을 특징으로 하는 조성물.
  10. 하나 이상의 일반식(Ⅰ)의 유기 실란 시약을 알콕시실란 유도체에 의해 작용화되거나 개질된 디엔 탄성 중합체에 열역학적 공정에 의해 혼입시킨 다음, 타이어 제조용 고무 조성물에 통상적으로 사용되는, 보강 충전제를 포함하는 모든 다른 성분들을 부가 및 혼입시킴을 특징으로 하는, 이력 특성이 향상된 디엔 탄성중합체를 기재로 하는 가황성 고무 조성물의 제조방법.
    Z-R1-Si(OR2)3-n(R3)n(Ⅰ)
    상기 식에서, Z는 1차 아민 작용기, 사이클릭 또는 비사이클릭 2차 아민 작용기, 이민 작용기 또는 폴리아민 라디칼이고, R1, R2및 R3은 동일하거나 상이하고 탄소수 1 내지 12, 바람직하게는 1 내지 4의 알킬, 아릴, 알크아릴 또는 아르알킬 라디칼이며, n은 0, 1 및 2의 값으로부터 선택된 정수이다.
  11. 제10항에 있어서, 유기 실란 시약이 모든 열역학적 공정 전에 작용화 디옌 탄성중합체에 부가되고, 이어서 이러한 유기 실란 시약이 열역학적 공정에 의해 탄성중합체 안으로 혼입됨을 특징으로 하는 방법.
  12. 제10항에 있어서, 유기 실란 시약이, 작용화되거나 개질된 디엔 탄성중합체의 열역학적 공정의 초기 단계 후에 알콕시실란 작용화 또는 개질화 디엔 탄성중합체에 부가되고, 유기 실란 시약이 열역학적 공정에 의해 디엔 탄성중합체로 혼입됨을 특징으로 하는 방법.
  13. 제10항에 있어서, 알콕시실란 유도체에 의해 작용화되거나 개질된 하나 이상의 디엔 중합체, 일반식(Ⅰ)의 유기 실란 및 카본 블랙을 포함하는 탄성중합체가 열역학적 공정의 초기 단계에 도입되고, 이 때 가황 시스템을 제외하고, 타이어 제조용 고무 조성물에 통상적으로 사용되는 다른 성분들이 부가되며 열역학적 공정이 적당한 시간 동안 계속 수행됨을 특징으로 하는 방법.
  14. 제12항에 있어서, 보강 충전제가 카본 블랙과 실리카로 이루어지는 경우, 열역학적 공정의 초기 단계를 수행하는 탄성중합체에, 일반식(Ⅰ)의 유기 실란 시약, 실리카 및 결합제, 이어서 오일, 그리고 최종적으로 카본 블랙이 스테아르산 및 산화방지제와 함께 순서대로 연속 부가되고, 제조된 탄성중합체 블록이 회수 냉각되며, 제2열역학적 단계에서, 가황 시스템을 제외하고 이러한 가황성 고무 조성물에 통상적으로 사용되는 다른 성분들이 부가되고, 열역학적 공정에 혼입된 다음, 혼합물이 회수된 후, 후처리 단계에서 가황 시스템이 혼입되고 가황성 조성물이 회수됨을 특징으로 하는 방법.
  15. 하나 이상의 작용화되거나 개질된 디엔 중합체와 보강 충전제로서의 카본 블랙 또는 카본 블랙과 실리카와의 혼합물을 포함하는 가황성 고무 조성물을 함유하는, 회전 저항성이 향상된 타이어로서, 작용화되거나 개질된 디엔 중합체가 알콕시실란 유도체에 의해 작용화되거나 개질된 중합체이고 아민 또는 이민 작용기를 포함하는 하나 이상의 일반식(Ⅰ)의 유기 실란 화합물을 추가로 포함함을 특징으로 하는 타이어.
    Z-R1-Si(OR2)3-n(R3)n(Ⅰ)
    상기 식에서, Z는 1차 아민 작용기, 사이클릭 또는 비사이클릭 2차 아민 작용기, 이민 작용기 또는 폴리아민 라디칼이고, R1, R2및 R3은 동일하거나 상이하고 탄소수 1 내지 12, 바람직하게는 1 내지 4의 알킬, 아릴, 알크아릴 또는 아르알킬 라디칼이며, n은 0, 1 및 2의 값으로부터 선택된 정수이다.
  16. 제15항에 있어서, 고무 조성물이 트레드의 제조공정에 혼입됨을 특징으로 하는 타이어.
  17. 하나 이상의 작용화되거나 개질된 디엔 중합체와 보강 충전제로서의 카본 블랙 또는 카본 블랙과 실리카와의 혼합물을 포함하는 가황성 고무 조성물을 포함하는 타이어 트레드로서, 작용화되거나 개질된 디엔 중합체가 알콕시실란 유도체에 의해 작용화되거나 개질된 중합체이고, 아민 또는 이민 작용기를 포함하는 하나 이상의 일반식(Ⅰ)의 유기 실란 화합물을 추가로 포함함을 특징으로 하는 타이어 트레드.
    Z-R1-Si(OR2)3-n(R3)n(Ⅰ)
    상기 식에서, Z는 1차 아민 작용기, 사이클릭 또는 비사이클릭 2차 아민 작용기, 이민 작용기 또는 폴리아민 라디칼이고, R1, R2및 R3은 동일하거나 상이하고 탄소수 1 내지 12, 바람직하게는 1 내지 4의 알킬, 아릴, 알크아릴 또는 아르알킬 라디칼이며, n은 0, 1 및 2의 값으로부터 선택된 정수이다.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019960024829A 1995-10-04 1996-06-28 유기실란화합물을포함하는가황성고무조성물,이의제조방법,및당해조성물을포함하는타이어및타이어트레드 KR100413300B1 (ko)