KR960031366A - 펀칭성 향상 결정 이방성 전기강 제조에서의 산화 마그네슘 코팅 및 처리 - Google Patents

펀칭성 향상 결정 이방성 전기강 제조에서의 산화 마그네슘 코팅 및 처리 Download PDF

Info

Publication number
KR960031366A
KR960031366A KR1019960004769A KR19960004769A KR960031366A KR 960031366 A KR960031366 A KR 960031366A KR 1019960004769 A KR1019960004769 A KR 1019960004769A KR 19960004769 A KR19960004769 A KR 19960004769A KR 960031366 A KR960031366 A KR 960031366A
Authority
KR
South Korea
Prior art keywords
magnesium oxide
coating
silicon oxide
weight
oxide
Prior art date
Application number
KR1019960004769A
Other languages
English (en)
Inventor
에이. 머피 로빈
Original Assignee
로버트 에이취. 존슨
암코 인크.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 로버트 에이취. 존슨, 암코 인크. filed Critical 로버트 에이취. 존슨
Publication of KR960031366A publication Critical patent/KR960031366A/ko

Abstract

본 발명은 2차 결정 성장을 위한 최종 고온 소둔에 앞서 결정 이방성 전기강의 코팅을 위한 소둔 분리제 조성을 제공하는 것이다. 산화 마그네슘 기초 코팅은 물이 없는 기지에 적어도 20%의 산화 규소를 포함한다. 산화규소를 많이 첨가하는 것은 코팅과 기지 금속 사이의 접촉면을 제한하고 쉽게 제거될 수 있는 두터운 유리막을 형성한다. 산화 마그네슘 코팅은 뛰어난 자기적 특성을 나타내고 정상적 강산 소재 또는 형성된 유리막을 제거하기 위한 특수 연마 수단을 필요로 하지 않는다. 편칭성 개선을 위해 코팅될 수 있는 순 전기강은 경한 유리막이 실질적으로 제거되기 때문에 공구 수명을 증가시킨다.

Description

편칭성 향상 결정 이방성 전기강 제조에서의 산화 마그네슘 코팅 및 처리
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (10)

  1. 결정 이방성 전기강에 대한 소둔 분리제 코팅 조성에 있어서, 상기 코팅 조성이, 중량당 백분율로서, 및 물이 없는 상태에서, a) 35내지 85중량%의 산화 마그네슘과, b) 15내지 65중량%의 산화 규소 및 c) 최대 5중량%의 황으로 조성되는 것을 특징으로 하는 코팅 조성.
  2. 제1항에 있어서, 상기 산화 마그네슘이 200초보다 큰 구연산 활성도를 갖는 것을 특징으로 하는 코팅 조성.
  3. 제1항에 있어서, 상기 코팅이 적어도 0.5중량%의 황 첨가물을 포함하는 것을 특징으로 하는 코팅 조성.
  4. 제1항에 있어서, 상기 산화 규소가 콜로이드성인 것을 특징으로 하는 코팅 조성.
  5. 제1항에 있어서, 상기 산화 규소가 20중량% 내지 55중량%인 것을 특징으로 하는 코팅 조성.
  6. 제1항에 있어서, 상기 산화 규소가 25중량% 내지 45중량%인 것을 특징으로 하는 코팅 조성.
  7. 제1항에 있어서, 상기 산화 마그네슘이 1000초보다 큰 구연산 활성도를 갖는 것을 특징으로 하는 코팅 조성.
  8. 제1항에 있어서, 상기 산화 마그네슘이 100초보다 작은 구연산 활성도를 갖는 산화 마그네슘으로 적어도 20%의 산화 마그네슘과 1000초보다 큰 구연산 활성도를 갖는 산화 마그네슘으로 적어도 40%의 산화 마그네슘으로 혼합된 것을 특징으로 하는 코팅 조성.
  9. 796A/m에서 측정된 적어도 1780의 투자율을 갖는 규칙적 결정 이방성 전기강 스트립 제조 방법에 있어서, a) 0.005%의 최대 탄소 수준 및 상기 스트립 상의 산화 규소층을 제공하기 위하여 상기 스트립을 탈탄하는 단계와, b) 상기 마그네슘 및 적어도 15중량% 만큼의 산화 규소를 포함하는 소둔 분리제 코팅을 상기 스트립에 사용하는 단계와, c) 상기 산화 규소가 상기 강 스트립과 매끄러운 접촉면을 형성하고 상기 산화 마그네슘 코팅이 된 상기 시트립에 상기 산화 마그네슘이 쉽게 제거될 수 있는 유리막을 형성하는 고온 소둔을 행하는 단계를 포함하는 것을 특징으로 하는 방법.
  10. 제9항에 있어서, 상기 산화 마그네슘이 콜로이드성 산화 규소인 것을 특징으로 하는 방법.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019960004769A 1995-02-28 1996-02-27 펀칭성 향상 결정 이방성 전기강 제조에서의 산화 마그네슘 코팅 및 처리 KR960031366A (ko)