KR950032536A - 수성 폴리에스테르-폴리우레탄 분산액 및 그의 도료 조성물 용도 - Google Patents

수성 폴리에스테르-폴리우레탄 분산액 및 그의 도료 조성물 용도 Download PDF

Info

Publication number
KR950032536A
KR950032536A KR1019950003625A KR19950003625A KR950032536A KR 950032536 A KR950032536 A KR 950032536A KR 1019950003625 A KR1019950003625 A KR 1019950003625A KR 19950003625 A KR19950003625 A KR 19950003625A KR 950032536 A KR950032536 A KR 950032536A
Authority
KR
South Korea
Prior art keywords
weight
component
molecular weight
acid
contg
Prior art date
Application number
KR1019950003625A
Other languages
English (en)
Other versions
KR100363805B1 (ko
Inventor
블룸 하랄트
페쫄트 요아힘
Original Assignee
게르하르트 뮬러, 로타르 스타일링
바이엘 악티엔게젤샤프트
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=6511209&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=KR950032536(A) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by 게르하르트 뮬러, 로타르 스타일링, 바이엘 악티엔게젤샤프트 filed Critical 게르하르트 뮬러, 로타르 스타일링
Publication of KR950032536A publication Critical patent/KR950032536A/ko
Application granted granted Critical
Publication of KR100363805B1 publication Critical patent/KR100363805B1/ko

Abstract

본 발명은 a)본질적으로 선형인 1종 이상의 폴리에스테르 폴리올 15내지 90 중량%, b)i)폴리카르보네이트, ii)폴리에테르 폴리올 및 iii)카르복실기의 히드록실기로의 수소화, 카르복실기의 알콕실화 또는 아량체 지방상의 저분자량의 디올을 사용한 카르복실기의 에스테르화에 의해 얻어지는 폴리에스테르 폴리올로부터 선택되는 필수적으로 1종이상의 이관능성 폴리올 4 내지 75중량%, c)i)히드록시카복실산, ii)아미노산, iii)아미노술폰산 및 i).ii)및 iii)의 산의 알칼리염 1내지 10중량%,d)2이상의 히드록실 및(또는) 아미노기를 함유하는 저분자량 성분 0내지 20 중량%, e)1종 이상의 친수성 1가 또는 2가 알코올 0내지 20 중량%, 및 f)분자량이 168내지 300인 선형 지방족 디이소시아네이트 50 중량% 이상을 함유하는 폴리이소시아네이트 성분 5내지 50 중량%로 부터 제조(성분a)내지 f)의 퍼센트의 합은 100이다,) 되는 히드록실기 함유 폴리에스테르 -폴리우레탄의 수성 분산액에 관한 것이다.

Description

수성 폴리에스테르-폴리우레탄 분산액 및 그의 도료 조성물 용도
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (12)

  1. a)성분 b)의 요건을 만족시키는 것 외에 분자량이 500 내지 4,000이고 본질적으로 선형인 1종 이상의 폴리에스테르 폴리올 15 내지 90 중량%, b) i)분자량이 400 내지 6,000인 폴리카르보네이트, ii)알킬렌옥사이드 총량을 기준으로 에틸렌옥사이드 단위를 30 중량% 미만으로 함유하고 폴리에테르 사슬 형태로 존재하는 분자량이 350 내지 3,500인 폴리에테르 폴리올, iii)및 에스테르기를 함유하며 카르복실기의 히드록실기로의 수소화, 카르복실기의 알콕실화 또는 이량체 지방산의 저분자량 디올을 사용한 카르복실기의 에스테르화에 의해 얻어지는 폴리에스테르, 폴리올로부터 선택되는 본질적으로 이관능성인 1종 이상의 폴리올 4내지 75중량%, c) i)히드록시카르복실산, ii)아미노산, iii)아미노술폰산 및i), ii) 및 iii)의 산의 알칼리염으로부터 선택된 1종 이상의 산 성분1 내지 10 중량%, d)분자량이 60 내지 300이고 2이상의 히드록실 및/또는 아미노기를 함유하는 화합물로부터 선택된 저분자량 성분 0내지 20 중량%, e)분자량이 350내지 3,000이고 측면 및/또는 말단 에틸렌옥사이드 단위를 함유하는 1종 이상의 친수성1가 또는 2가 알코올 0내지 20중량%, 및 f)분자량이 168내지 1,000인 유기폴리이소시아네이트로부터 선택되며 그 성분 중 적어도 50 중량%는 분자량이 168내지 300인 성형 지방족 디이소시아네이트로부터 선택되는 폴리이소시아네이트 성분 5내지 50중량%의 반응생성물 (성분a) 내지 f)의 백분률 합은 100이다) 로서, 필요시 적어도 부분적으로 염기에 의해서 중화처리되며, 폴리에스테르-폴리우레탄 고체를 기준으로 할때 산 값이 5 내지 60㎎ KOH/g,히드록실기 함량이 0.25내지 6.5 중량% 및 우레탄기 함량(-NH-CO-O-로서 계산)이 2 내지 25중량%인 폴리에스테르-폴리우레탄의 수성 분산액.
  2. 제1항에 있어서, 폴리에스테르 폴리올a)는 a1) 아디프산, 세박산, 아젤라산, 수소화된 이량체 지방산 및 그들의 혼합물로 이루어진 군으로부터 선택된 산 성분 30내지 65중량%, a2) 에틸렌글리콜, 1,2-및 1,3-프로판디올, 1,3-및 1,4-부탄디올, 1,6-헥산디올, 디에틸렌 글리콜, 디프로필렌 글리콜, 네오펜틸 글리콜 및 그들의 혼합물로 이루어진 군으로부터 선택된 디올 성분 20 내지 65 중량%, a3)프탈산 무수물, 이소프탈산, 헥사히드로프탈산 무수물, 1,4-시클로헥산 디카르복실산, 삼량체 지방산을 다량 함유하는 이량체 지방산, 수소화된 공업용 지방산, 이소노난산, 2-에틸헥산산 및 그들의 혼합물로 이루어진 군으로부터 선택되는 산 성분 0 내지 15 중량% 및 a4)트리메틸올프로판, 글리세로 및 그들의 혼합물로 이루어진 군으로부터 선택된트리올 성분 0 내지 7 중량%및 반응 생성물이고, 성분 b)는 분자량이 750내지 4,000인 선형 폴리카르보네이트디올로 구성되어 있고, 성분 c)는 2,2-디메틸올프로피온산 및/또는 2,2-디메틸올부티르산 85 중량%이상으로 구성되어 있고, 성분 d)는 분자량이 90 내지 150인 저분자량의 디올 또는 트리올 1종 이상으로 구성되어 있고, 성분 e)는분자량이 168내지 300이고 선형 지방족 디이소시아네이트를 75 중량% 이상 함유하며, 성분 a1)내지 a4)의 백분률의 합이 100인 것이 특징인 수성 분산액.
  3. 제1항에 있어서, 분산된 폴리에스테르-폴리우레탄은 27 내지 70 중량%의 성분 a) 10 내지 60 중량%의 성분 b) 2 내지 70 중량%의 성분 c), 0.5 내지 10 중량%의 성분 d), 0 내지 10 중량%의 성분 e) 및 7 내지 30 중량%의 성분 f)의 반응 생성물 (성분a) 내지 f)의 백분률 합은 100이다) 로서, 산 값이 8 내지 40mg KOH/g 이고 히드록실기 함량이 0.5 내지 3.5 중량%이고, 우레탄기 함량이 4 내지 19 중량%인 것이 특징인 수성 분산액.
  4. 제1항에 있어서, 분산된 폴리에스테르-폴리우레탄은 27 내지 70 중량%의 성분 a) 10 내지 60 중량%의 성분 b) 2 내지 70 중량%의 성분 c), 0.5 내지 10 중량%의 성분 d), 0 내지 10 중량%의 성분 e) 및 7 내지 30 중량%의 성분 f)의 반응 생성물 (성분a) 내지 f)의 백분률 합은 100이다) 로서, 산 값이 8 내지 40mg KOH/g 이고 히드록실기 함량이 0.5 내지 3.5 중량%이고, 우레탄기 함량이 4 내지 19 중량%인 것이 특징인 수성 분산액.
  5. 제1항에 있어서,i) 성분 b)는 분자량이 750 내지 4,000인 선형 폴리카르보네이트 디올을 함유하고,ii) 성분 c)는 성분 c)의 중량을 기준으로 85 중량% 이상의 2,2-디메틸올프로피온산 및 (또는) 2,2-디메틸올부티르산을 함유하고, iii)성분 d)는 분자량이 90 내지 150인 저분자량의 디올 또는 트리올 1종 이상을 함유하고, iv)성분 e)는 성분 e)의 중량을 기준으로 75 중량% 이상의 선형 지방족 디이소시아네이트를 함유하는 것이 특징인 수성 분산액.
  6. 제2항에 있어서,i) 성분 b)는 분자량이 750 내지 4,000인 선형 폴리카르보네이트 디올을 함유하고,ii) 성분 c)는 성분 c)의 중량을 기준으로 85 중량% 이상의 2,2-디메틸올프로피온산 및 (또는) 2,2-디메틸올부티르산을 함유하고, iii)성분 d)는 분자량이 90 내지 150인 저분자량의 디올 또는 트리올 1종 이상을 함유하고, iv)성분 e)는 성분 e)의 중량을 기준으로 75 중량% 이상의 선형 지방족 디이소시아네이트를 함유하는 것이 특징인 수성 분산액.
  7. 제3항에 있어서,i) 성분 b)는 분자량이 750 내지 4,000인 선형 폴리카르보네이트 디올을 함유하고,ii) 성분 c)는 성분 c)의 중량을 기준으로 85 중량% 이상의 2,2-디메틸올프로피온산 및 (또는) 2,2-디메틸올부티르산을 함유하고, iii)성분 d)는 분자량이 90 내지 150인 저분자량의 디올 또는 트리올 1종 이상을 함유하고, iv)성분 e)는 성분 e)의 중량을 기준으로 75 중량% 이상의 선형 지방족 디이소시아네이트를 함유하는 것이 특징인 수성 분산액.
  8. 제4항에 있어서,i) 성분 b)는 분자량이 750 내지 4,000인 선형 폴리카르보네이트 디올을 함유하고,ii) 성분 c)는 성분 c)의 중량을 기준으로 85 중량% 이상의 2,2-디메틸올프로피온산 및 (또는) 2,2-디메틸올부티르산을 함유하고, iii)성분 d)는 분자량이 90 내지 150인 저분자량의 디올 또는 트리올 1종 이상을 함유하고, iv)성분 e)는 성분 e)의 중량을 기준으로 75 중량% 이상의 선형 지방족 디이소시아네이트를 함유하는 것이 특징인 수성 분산액.
  9. A) 제1항의 폴리에스테르-폴리우레탄 25 내지 100 중량%를 함유하고 다른 결합제 0 내지 75 중량%를 함유하는 폴리올 성분과, B) 아미노 수지 , 친수성으로 개질될 수 있는 블록화 폴리이소시아네이트 및 친수성으로 개질될 수 있는 유리 이소시아네이트기를 함유하는 폴리이소시아네이트로부터 선택되는 가교 수지를 결합제로서 함유하는 수성 도료 조성물.
  10. A) 제1항의 폴리에스테르-폴리우레탄 25 내지 80 중량%를 함유하고 히디록실기를 함유하지 않고 중량 평균 분자량이 15,000 이상인 음이온적으로 및(또는) 비이온적으로 친수성으로 개질된 폴리우레탄 수지를 20 내지 75 중량%함유하는 폴리올 성분과, B) 멜라민 수지, 친수성으로 개질될 수 있는 블록화 폴리이소시아네이트 및 친수성으로 개질될 수 있는 유리 이소시아네이트기를 함유하는 폴리이소시아네이트로부터 선택되는 가교 수지를 결합제로서 함유하는 수성 도료 조성물.
  11. 제9항의 도료 조성물로부터 제조된 도장 기판.
  12. 제10항의 도료 조성물로부터 제조된 도장 기판.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019950003625A 1994-02-25 1995-02-24 폴리에스테르-폴리우레탄의 수성분산액 및 그의 수성도료 조성물 KR100363805B1 (ko)