KR950032350A - 마이크로셀룰라 폴리우레탄 엘라스토머 및 그 제조방법 - Google Patents
마이크로셀룰라 폴리우레탄 엘라스토머 및 그 제조방법 Download PDFInfo
- Publication number
- KR950032350A KR950032350A KR1019950005435A KR19950005435A KR950032350A KR 950032350 A KR950032350 A KR 950032350A KR 1019950005435 A KR1019950005435 A KR 1019950005435A KR 19950005435 A KR19950005435 A KR 19950005435A KR 950032350 A KR950032350 A KR 950032350A
- Authority
- KR
- South Korea
- Prior art keywords
- terminated prepolymer
- diisocyanate
- isocyanate
- prepolymer
- microcellular polyurethane
- Prior art date
Abstract
본 발명은 NCO-말단 프리폴리머, OH-말단 프리폴리머 및 발포성분을 발포 및 경화되도록 교반하면서 혼합시켜 얻은 마이크로셀룰라 폴리우레탄 엘라스토머에 관한 것으로서, NCO-말단 프리폴리머는 (A)1000-3000의 평균분자량을 갖는 폴리에스테르 폴이올(a) 및 디페닐메탄-4,4′-디이소시아네이트(MDI)를 반응시켜 얻은 프리폴리머 또는 폴리에스테르 폴리올(a)의 반응생성물과 MDI를 저분자량 포리올을 더 반응시켜 얻어진 부분적으로 가교결합된 프리폴리머이고, OH-말단 프리폴리머는 (A)폴리에스트르 폴리올(a)와 폴리이소시아네이트를 반응시켜 얻어진 프리폴리머 또는 (B) 모두 500-3000의 평균분자량을 갖는 폴리에스테르폴리올(b) 및/또는 폴리에스테르 폴리올과 폴리이소시아네이트를 반응시켜 얻어진 프리폴리머이며 발보성분은 주발포제로서 물을 함유하는데 이러한 엘라스토머는 노화시험에서 노화파손 및 영구적인 비틀림에 대한 개선된 저항성을 나타내는 반면에 MDI사용에서의 잇점을 유지한다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 몰딩 해제시에 폴리우레탄 엘라스토머의 크랙 또는 블리스터의 진전을 관찰 및 평가하는데 사용되는 몰드 및 성형된 물품의 단면도이다. 제2도는 몰딩해제형태에서 제1도의 몰드 및 성형된 물품의 단면도이다.
Claims (12)
- 이소시아네이트-말단프리폴리머, 하이드록실-말단 프리폴리머 및 발포성분을 발포 및 경화되도록 교반하면서 혼합하여 얻어진 마이크로셀룰라 폴리우레탄 엘라스토머에 있어서, 상기 이소시아네이트-말단 프리폴리머는 1000-3000의 평균분차량을 갖는 폴리에스테르폴리올과 디페닐메탄-4,4'-디이소시아네이트를 1:0.2-0.6의 중량비로 반응시켜 얻은 프리폴리머이고, 상기 하이드록실-말단 프리폴리머는 1000-3000의 평균 분자량을 갖는 폴리에스테르 폴리올과 폴리이소시아네이트를 1:0.05-0.5의 몰비로 반응시켜 얻은 프리폴리머이며, 상기 발포성분은 주발포제로서 물을 함유하는 것을 특징으로 하는 마이크로셀룰라 폴리우레탄 엘라스토머.
- 제1항에 있어서, 상기 폴리이소시아네이트가 3,3'-디메틸-4,4'-비페닐렌 디이소시아네이트인 마이크로셀룰라 폴리우레탄 엘라스토머.
- 제1항에 있어서, 상기 하이드록실-말단 프리폴리머가 이소시이네이트 말단 프리폴리머를 얻는데 사용되는 폴리에스테르 폴리올 100중량부당 0.1-1.0 중량부의 양으로 사용되는 마이크로셀룰라 폴리우레탄 엘라스토머.
- 제1항에 있어서, 상기 이소시아네이트-말단 프리폴리머가 No.3 로터를 사용하여 30rpm의 로터 회전속도 및 80℃의 측정온도로 브룩필드 회전 점도계로 측정했을 때 2500cp 이하의 점도를 가지며, 마이크로셀룰라 폴리우레탄 엘라스토머 5kN의 하중이 2Hz의 주파수로 시험편에 반복적으로 가해지는 노화시험에서 500,000이하의 노화수명 및 10%이하의 영구적인 비틀림을 나타내는데 노화수명은 파단에 요구되는 반복된 하중 사이클의 수이고 영구적 비틀림은 하기식으로 얻어지는 마이크로셀룰라 폴리우레탄 엘라스토머,:S(%)=(h0-h)/h0X100여기에서, h0는 노화시험전 시험편의 높이이고 h는 시험시 500,000싸이클의 반복된 하중을 가한 후의 시험편의 높이이다.
- 이소시아네이트-말단 프리폴리머, 하이드록실-말단 프리폴리머 및 발포성분을 발포 및 경화시키도록 교반하면서 혼합하여 얻어진 마이크로셀룰라 폴리우레탄 엘라스토머에 있어서, 상기 이소시아네이트-말단 프리폴리머는 1000-3000의 평균분자량을 갖는 폴리에스테르 폴리올과 디페닐메탄-4,4'-디이소시아네이트를 1:0.2-0.6의 중량비로 반응시키고 그 반응생성물 100중량부와 저분자량 폴리올 0.1-2.0 중량부를 반응시켜 얻은 프리폴리머이고, 상기 하이드록실-말단 프리폴리머는 모두 500-3000의 평균분자량을 갖는 폴리에스테르 폴리올 및/또는 폴리에테르 폴리올을 폴리이소시아네이트와 1:0.05-0.5의 몰비로 반응시켜 얻은 프리폴리머이고, 상기 발포성분은 주발포제로서 물을 함유하는 것을 특징으로 하는 마이크로셀룰라 폴리우레탄 엘라스토머.
- 제5항에 있어서, 상기 폴리이소시아네이트가 3,3'-디메틸-4,4'비페닐렌 디이소시아네이트, 나프탈렌-1,5-디이소시아네이트, 2,4-톨릴렌 디이소시아네이트, 2,6-톨릴렌 디이소시아네이트 및 2,4-톨릴렌 디이소시아네이트 및 2,6-톨릴렌 디이소시아네이트의 혼합물로부터 선택되는 최소한 하나의 화합물인 마이크로 셀룰라 폴리우레탄 엘라스토머.
- 제5항에 있어서, 상기 하이드록실-말단 프리폴리머가 이소시아네이트-말단 프리돌리머의 제조에 사용한 폴리에스테르 폴리올 100중량부당 0.1-1.0중량부의 양으로 사용되는 마이크로셀룰라 폴리우레탄 엘라스토머.
- 제5항에 있어서, 상기 마이크로셀룰라 폴리우레탄 엘라스토머가 5kN의 하중물 2Hz의 주파수로 시험편에 반복적으로 가하는 노화시험에서 500,000이하의 노화수명 및 10%이하의 영구적인 비틀림을 나타내는데 노화수명은 파단시에 반복적 하중의 싸이클의 수이고 영구적인 비틀림은 하기식에 의해 얻어지는 마이크로셀룰라 폴리우레탄 엘라스토머:S(%)=(h0-h)/h0X100여기에서, h0는 노화시험전 시험편의 높이이고: h는 시험시 500,000 싸이클의 반복된 하중을 가한 후의 시험편의 높이이다.
- 제5항에 있어서, 상기 이소시아네이트-말단 프리폴리머는 4시간 이상의 폿트라이프를 가지는데 폿트라이프는 몰딩 해제시에 크랙 또는 블리스터와 같은 비정상적인 것 없이 결함이 없는 엘라스토머가 얻어질때까지의 시간의 한계로 정의되는 마이크로셀룰라 폴리우레탄 알라스토머.
- 1000-3000의 분자량을 갖는 폴리에스테르 폴리올과 디페닐 메탄-4,4'-디이소시아네이트를 1:0.2-0.6의 중량비로 반응시키고, 그 반응생성물에 저분자량 폴리올을 둘 사이에 반응이 수행되도록 반응생성물100중량부당 0.1-2.0중량부의 양으로 첨가하여 부분적으로 가교결합된 이소시아네이트-말단 프리폴리머를 얻으며, 얻어진 이소시아네이트-말단 프리폴리머, 모두 500-3000의 평균분자량을 갖는 폴리에스테르 폴리올 및/또는 폴리에테르 폴리올을 폴리이소시아네이트와 1:0.05-0.5의 몰비로 반응시켜 얻은 하이드록실-말단 프리폴리머 및 주발포제로서 물을 함유하는 발포성분을 교반하면서 혼합, 반응시키는 것을 포함하는 마이크로셀룰라 폴리우레탄 엘라스토머.
- 제10항에 있어서, 상기 폴리이소시아네이트가 3,3'-디메틸-4,4'-비페닐렌 디이소시아네이트, 나브탈렌-1,5-디이소시아네이트, 2,4-틀릴렌 디이소시아네이트, 2,6-톨릴렌 디이소시아네이트 및 2,4-톨릴렌 디이소시아네이트와 2,6-톨릴렌 디이소시아네이트의 혼합물로부터 선택된 최소한 하나의 화합물인 방법.
- 제10항에 있어서, 하이드록실-말단 프리폴리머가 이소시아네이트-말단 프리폴리머를 얻는데 사용된 폴리에스테르 폴리올 100중량부의 양으로 사용되는 방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.