KR890001616A - 향상된 가스분리를 위한 투과성 막 - Google Patents
향상된 가스분리를 위한 투과성 막 Download PDFInfo
- Publication number
- KR890001616A KR890001616A KR1019880009779A KR880009779A KR890001616A KR 890001616 A KR890001616 A KR 890001616A KR 1019880009779 A KR1019880009779 A KR 1019880009779A KR 880009779 A KR880009779 A KR 880009779A KR 890001616 A KR890001616 A KR 890001616A
- Authority
- KR
- South Korea
- Prior art keywords
- membrane
- support layer
- separation
- composite membrane
- swellable
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (53)
- 향상된 가스분리 특성을 갖는 복합막에 있어서, (a) 압력하에 표피영역이 붕괴되는 것을 막기 위한 역할을 하는 덜 조밀하고 다공성인 비선택성 지지영역과 비교적 얇고 조밀하고 반투과성인 표피영역(이 표피영역은 분리될 공급가스 혼합물 중의 더 쉽게 투과될 수 있는 성분을 원하는 만큼의 높은 투과율로 선택적으로 투과할 수 있는 영역이다)을 갖는 비대칭 형태의 다공성 중합체 지지층과, 그리고 (b) 상기 지지층 구조의 변경없이 상기의 표피영역 상에 적층된 분리층(이 분리층은 상기의 비대칭형 지지층 재료의 더 쉽게 투과될 수 있는 성분에 대한 선택력에 비해 같거나 또는 더 큰 선택력을 갖는 것이다)으로 구성되는 것을 특징으로 하여, 상기 비대칭형 지지층 재료의 고유한 분리특성에 비해 같거나 또는 더 놓은 분리특성을 나타내고 그래서 향상된 가스투과 특성과 분리특성을 나타내는 복합막.
- 제 1 항에 있어서, 막이 유공섬유 형태인 것을 특징으로 하는 복합막.
- 제 1 항에 있어서, 분리층이 중합체 재료로 이루어지는 것을 특징으로 하는 복합막.
- 제 1 항에 있어서, 지지층이 폴리술폰으로 이루어지는 것을 특징으로 하는 복합막.
- 제 2 항에 있어서, 지지층은 폴리술폰으로 이루어지고 분리층은 중합체 재료로 이루어지는 것을 특징으로 하는 북합막.
- 제 5 항에 있어서, 지지층이 셀룰로이스 아세테이트로 이루어지는 것을 특징으로 하는 복합막.
- 제 5 항에 있어서, 지지층이 폴리아크릴레이트로 이루어지는 것을 특징으로 하는 복합막.
- 제 7항에 있어서, 분리층은 술폰화된 폴리술폰으로 이루어지는 것을 특징으로 하는 복합막.
- 제 7 항에 있어서, 분리층은 브롬화된 폴리페닐렌옥사이드로 이루어지는 것을 특징으로 하는 복합막.
- 원하는 다공성 형태로 막을 제조하고, 씻고 건조시키는 방법이고, 공급가스 혼합물 중의 더 쉽게 투과될 수 있는 성분을 선택적으로 투과할 수 있는 중합체 막을 제조하는 방법에 있어서, 막구조를 변성시키기에 충분한 시간동안 비팽윤 조건하에서, 막재료의 유리전이 온도에 가까운 높혀진 온도에 상기의 막(본질상 건조한 형태)을 노출시키는 것을 포함시켜서, 막내에 비대칭성을 형성하고, 막의 치밀화저항성과 붕괴 압력을 증가시켜서, 가스 분리조작에 사용하기 위한 처리된 막의 균일성과 신뢰성을 향상시키는 것을 특징으로 하는 중합체 막을 제조하는 방법.
- 제 10 항에 있어서, 비팽윤성 조건을 가열된 가스분위기를 포함하는 것을 특징으로 하는 방법.
- 제 11 항에 있어서, 불활성가스 분위기는 막재료의 유리전이 온도에 비해 약 20@ 이하만큼 낮은 온도인 것을 특징으로 하는 방법.
- 제 12 항에 있어서, 온도는 유리전이 온도에 비해 약 15℃ 내지 약 1℃만큼 낮은 온도임을 특징으로 하는 방법.
- 제 10 항에 있어서, 중합체 막은 폴리술폰으로 이루어지는 것을 특징으로 하는 방법.
- 제 12 항에 있어서, 가열된 가스분위기는 뜨겁고 본질상 건조한 공기인 것을 특징으로 하는 방법.
- 제 11 항에 있어서, 막은 약 5초 내지 약 5분동안 높혀진 온도에 노축되는 것을 특징으로 하는 방법.
- 제 16항에 있어서, 노출시간은 약 30초 내지 약 4분인 것을 특징으로 하는 방법.
- 제 10항에 있어서, 막의 붕괴를 일으키기에는 불충분한 시간동안 비팽윤성 비팽윤성 액체의 배쓰에 막을 통과시킴으로써, 비팽윤성 조건하의 높혀진 온도에 막이 노출되는 것을 특징으로 하는 방법.
- 제 18항에 있어서, 비팽윤성 액체는 실리콘 오일로 구성되며, 그리고 철된 막을 씻고 건조시키는 것이 추가되는 것을 특징으로 하는 방법.
- 제 19항에 있어서, 처리된 막이 유공섬유 형태인 것을 특징으로 하는 방법.
- 처리된 막의 외부 표피영역 상에 분리층을 적층시키는 것이 포함되는데, 분리될 가스 혼합중의 더 쉽게 투과될 수 있는 성분에 대한 이 분리층의 선택력은 비대칭형 지지층재료의 고유한 분리특성에 비해 같거나 또는 더 큰 것임을 특징으로 하는 방법.
- 막에 비대칭성을 형성하기 위해서 막을 처리하기에 앞서 다공성 막 상에 분리층을 적층시키는 것이 더욱 더 포함되는데, 분리될 가스혼합물 중의 더 쉽게 투과될 수 있는 성분에 대한 이 분리층의 선택력은 상기의 다공성 재료막의 고유한 분리특성에 비해 같거나 또는 더 큰 것임을 특징으로 하는 제 18항에 따른 방법.
- 제 21 항에 있어서, 비대칭성의 처리된 막은 유공섬유의 형태로서 폴리술폰으로 이루어지는 것을 특징으로 하는 방법.
- 제 23 항에 있어서, 비팽윤성 조건은 열기분위기로 이루어지는 것을 특징으로 하는 방법.
- 제 23 항에 있어서, 비팽윤성 조건은 불활성 가스분리기로 이루어지는 것을 특징으로 하는 방법.
- 향상된 가스분리 특성을 갖는 복합막에 있어서, (a) 압력하에서 표피영역이 붕괴되는 것을 막기 위한 역할을 하는 덜 조밀하고 다공성인 비선택력 지지영역과 비교적 얇고 조밀하고 반투과성인 표피영역을 갖는 비대칭성 형태의 다공성 지지??(여기서, 상기의 표피영역은 분리될 공급가스 혼합물 중의 더 쉽게 투과 할수 있는 성분을 원하는 만큼의 높은 투과율로 선택적으로 투과할 수 있는 영역이며, 이 층은 원하는 다공성 형태로 형성되 후에는 씻겨지고, 건조되고, 막 구조를 변성시켜서 비대칭성을 일으키기에 그리고 막의 치밀화 저항성 및 붕괴 압력을 증가시키기에 충분한 단시간 동안 비팽윤성 조건하에 지지층 재료의 유리전이온도에 가까운 높혀진 온도에 본질상 건조한 형태로 막의 붕괴를 일으킴이 없이 노출된 것이다)과, 그리고 (b) 상기 표피영역의 외부표면 상에 적층된 분리층(여기서, 이 분리층은 상기의 비대칭형 지지층의 표피영역의 더 쉽게 투과될 수 있는 성분에 대한 선택력에 비해 같거나 또는 더 큰 선택력을 가지며, 그래서 상기의 분리층은 복합막의 분리성을 결정한다)으로 구성되는 것을 특징으로 하여, 원하는 치밀화 저항성 및 붕괴 압력과 함께, 향상된 선택력 및 투과력 그리고 선택력과 투과력의 유리한 조합을 나타내어, 향상된 가스 분리 조작에 사용하기 위한 복합막의 균일성 및 신뢰성을 향상시키는 복합막.
- 제 26항에 있어서, 막이 유공섬유의 형태에 있는 것을 특징으로 하는 복합막.
- 제 26항에 있어서, 분리층이 중합체 재료로 이루어지는 것을 특징으로 하는 복합막.
- 제 26항에 있어서, 지지층이 폴리술폰으로 이루어지는 것을 특징으로 하는 복합막.
- 제 27항에 있어서, 지지층이 폴리술폰으로 이루어지는 것을 특징으로 하는 복합막.
- 제 26항에 있어서, 비팽윤성 조건은 지지층 재료의 유리전이온도에 비해 약 20℃ 이하 만큼 낮은 온도에서 가열된 가스분위기로 이루어지는 것을 특징으로 하는 복합막.
- 제 32항에 있어서, 지지층은 폴리술폰으로 이루어지며 가열된 가스분위기는 뜨거운 본질상 건조공기로 이루어지는데, 이 지지층은 약 5초 내지 약 5분 동안 높혀진 온도에 노출되는 것을 특징으로 하는 복합막.
- 제 26항에 있어서, 지지층의 붕괴를 일으키기에는 불충분한 시간 동안 비팽윤성 액체 배쓰에 막을 통과시킴으로써, 지지층이 비팽윤성 조건하의 높혀진 온도에 노출되는 것을 특징으로 하는 복합막.
- 제 33항에 있어서, 지지층은 유공섬유의 형태로서 술리술폰으로 이루어지는 것을 특징으로 하는 복합막.
- 제 28항에 있어서, 분리층은 셀룰로오스 아세테이트로 이루어지는 것을 특징으로 하는 복합막.
- 제 28항에 있어서, 분리층은 폴리아크릴레이트로 이루어지는 것을 특징으로 하는 복합막.
- 제 36 항에 있어서, 분리층은 술폰화된 폴리술폰으로 이루어지는 것을 특징으로 하는 복합막.
- 제 36 항에 있어서, 분리층은 브롬화된 폴리페닐렌 옥사이드로 이루어지는 것을 특징으로 하는 복합막.
- 가스분리 특성을 갖는 복합막의 공급단부와 공급가스 흐름을 접촉시키고, 그리고 더 쉽게 투과할 수 있는 성분을 복합막으로부터의 투과 흐름으로 그리고 덜 쉽게 투과될 수 있는 성분을 비쿠과 흐름으로 따로따로 회수함으로써, 공급가스 흐름중의 덜 쉽게 투과될 수 있는 성분으로부터 더 쉽게 투과될 수 있는 성분을 분리하는 방법에 있어서, (a) 압력하에서 표피영역이 붕괴되는 것을 박기 위한 역할을 하는 덜 조밀하고 다공성인 비선택성 지지영역과 비교적 얇고 조밀하고 반투과성인 표피영역(이 표피영역은 분리될 공급가스 혼합물 중의 더 쉽게 투과 될 수 있는 성분을 원하는 만큼의 높은 투과율로 선택적으로 투과할 수 있는 영역이다)을 갖는 비대칭 형태의 다공성 중합체 지지층과, 그리고 (b) 상기 지지층 구조의 변경없이 상기의 표피영역 상에 적층된 분리층 (이 분리층은 상기의 비대칭형 지지층 재료의 더 쉽게 투과될 수 있는 성분에 대한 선택력에 비해 같거나 또는 더 큰 선택력을 갖는 것이다)으로 구성되어, 상기 비대칭형 지지층 재료의 고유한 분리특성에 비해 같거나 또는 더 높은 분리특성을 나타내고 그래서 향상된 가스투과 특성과 분리특성을 나타내는 복합막이 이용되는 것을 특징으로 하는 방법.
- 제 39 항에 있어서, 복합막이 우공섬유의 형태인 것을 특징으로 하는 방법.
- 제 40 항에 있어서, 지지층이 폴리술폰으로 이루어지는 것을 특징으로 하는 방법.
- 제 30항에 있어서, 원하는 다공성 형태로 처음에 형성되고 씻겨지고 건조된 후의 다공성 중합체 지지층은 막 구조를 변성시키기에 그리고 막의 치밀화 저항성 및 붕괴 압력을 증가시키기에 충분한 시간동안 비팽윤성 조건하에서, 지지층 재료의 유리전이온도에 가까운 높혀진 온도에 본질상 건조한 형태로 지지층의 붕괴를 일으킴이 없이 노출되는 것을 특징으로 하는 방법.
- 제 42항에 있어서, 비팽윤성 조건은 가열된 가스 분위기로 이루어지는 것을 특징으로 하는 방법.
- 제 42항에 있어서, 지지층은 폴리술폰으로 이루어지며 복합막은 유공섬유의 형태를 갖는 것을 특징으로 하는 방법.
- 제 39항에 있어서, 공급가스 혼합물은 공기로 이루어지고, 투과가스는 산소로 이루어지고, 비투과가스는 질소로 이루어지는 것을 특징으로 하는 방법.
- 제 29항에 있어서, 공급가스 혼합물은 수소와 질소의 혼합물로 이루어지고, 투과가스는 수소로 이루어지고 비투과 가스는 질소로 이루어지는 것을 특징으로 하는 방법.
- 제 46항에 있어서, 공급가스 혼합물은 이산화탄소와 메탄의 혼합물로 이루어지고, 투과가스는 이산화탄소로 이루어지고 비투과가스는 메탄으로 이루어지는 것을 특지응로 하는 방법.
- 압력하에서 표피영역이 붕괴되는 것을 막기 위한 역할을 하는 덜 조밀하고 다공성인 비선택적 지지영역과 비교적 얇고 조밀한 반투과성 표피영역으로 이루어지는 비대칭성막인데, 상기의 표피영역은 분리될 공급가스 혼합물중의 더 쉽게 투과될 수 있는 성분을 원하는 만틈의 높은 투과율로 선택적으로 투과할 수 있는 영역이며, 상기의 막은 처음에는 원하는 형태로 형성되고, 씻겨지고 건조되고, 그리고 나중에, 막 구조를 변성시켜서 비대칭성을 일으키기에 그리고 막의 치밀화 저항성 및 붕괴압력을 증가시키기에 충분한 시간동안 비팽윤성 조건하에 지지층 재료의 유리전이온도에 가까운 높혀진 온도에 본질상 건조한 형탤 막의 붕괴를 일으킴이 없이 노출되어진 것임을 특징으로 하여, 원하는 치밀화 저항성 및 붕괴 압력과 함께 향상된 선택력 및 투과력 그리고 선택력과 투과력의 우리한 조합을 나타내어, 향상된 가스분리 조작에 사용하기 위한 복합막의 균일성 및 신뢰성을 향상시키는 비대칭형 막.
- 제 48항에 있어서, 막재료는 폴리술폰으로 이루어지는 것임을 특징으로 하는 비대칭형 막.
- 제 48항에 있어서, 원하는 형태는 유공섬유의 형태인 것을 특징으로 하는 비대칭형 막.
- 제 48항에 있어서, 비팽윤성 조건은 막재료의 유리전이온도에 비해 약 20℃ 이하 만큼 낮은 온도에서 가열된 가스분위기로 이루어지는 것을 특징으로 하는 비대칭형 막.
- 제 48 항에 있어서, 가열된 가스분위기는 뜨겁고 본질상 건조한 공기로 이루어지는 것을 특징으로 하는 비대칭형 막.
- 제 48 항에 있어서, 상기의 비팽윤성 조건은 비팽윤성 액체로 이루어지는데, 이것에 대한 막의 노출은 막의 붕괴를 일으키기에는 불충분한 시간동안 노출되는 것을 특징으로 하는 비대칭형 막.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.