KR880013821A - 바륨 티타네이트(BaTio₃)의 제조방법 - Google Patents
바륨 티타네이트(BaTio₃)의 제조방법 Download PDFInfo
- Publication number
- KR880013821A KR880013821A KR870011432A KR870011432A KR880013821A KR 880013821 A KR880013821 A KR 880013821A KR 870011432 A KR870011432 A KR 870011432A KR 870011432 A KR870011432 A KR 870011432A KR 880013821 A KR880013821 A KR 880013821A
- Authority
- KR
- South Korea
- Prior art keywords
- barium
- titanyl oxalate
- oxalic acid
- water
- solution
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 공지된 방법에 따라 제조한 분말(곡선 B)과 비교되는 본 발명의 방법에 따라 제조한 BaTiO₃분말(곡선 A)의 결정입자 직경(grain size) K에 대한 축정함량 M을 나타내는 그래프이며, 제2도는 온도 T에 대한 친화도(densification) V의 관계를 나타내는 그래프이다.
Claims (9)
- 바륨 티타닐 옥살레이트 BaTiO(C2O42·4H2O를 열분해시켜 바륨 티타네이트 BaTiO₃를 제조하는 방법에 있어서, 바륨 티타닐 옥살레이트 BaTiO(C2O4)2·4H2O를 생성하기 위하여 염화바륨 BaCl2의 수용액을 옥살산 H2C2O4및 옥시염화티탄 TiOCl2의 혼합물을 함유하는 수용액에 20 내지 60℃에서 격렬히 교반하면서 적가한 다음, 침전물을 900 내지 1300℃에서 하소시킴을 특징으로 하는 방법.
- 제1항에 있어서, TiCl4400ml를 30℃ 이하의 온도에서 교반하면서 물 600ml에 적가한 다음, 용액을 2000ml가 되도록 물로 희석시켜 제조한, Ti 0.668몰을 함유하는 옥시염화티탄 TiOCl2용액을 사용함을 특징으로 하는 방법.
- 제1항에 있어서, 옥살산 H2C2O4·2H2O 185.27g을 물 1000ml에 용해시킴을 특징으로 하는 방법.
- 제1항에 있어서, 염화바륨 BaCl2·2H2O 164.81gdmf 물 1600ml에 용해시킴을 특징으로 하는 방법.
- 제2항 또는 제3항에 있어서, 옥시염화티탄 TiOCl2용액을 옥살산 H2C2O4용액에 교반하면서 가함을 특징으로 하는 방법.
- 제4항 또는 제5항에 있어서, 염화바륨 BaCl2용액을 55℃에서 격렬히 교반하면서 옥시염화티탄 TiOCl2및 옥살산 H2C2O4의 혼합물을 함유하는 수용액에 적가하여 1.5 내지 2.5몰% 과량의 TiO2를 함유하는 바륨 티타닐 옥살레이트 침전물을 생성시킴을 특징으로 하는 방법.
- 제6항에 있어서, 잔류 Cl 이온을 세척해낸 후에, 바륨 티타닐 옥살레이트 침전물을 공기중 50℃에서 20시간 동안 건조시켜 분말을 수득함을 특징으로 하는 방법.
- 제7항에 있어서, 바륨 티타닐 옥살레이트 분말을 연소로중 산화성 대기중 1000 내지 1200℃에서, 바람직하게는 1100℃에서 열분해시켜 바륨 티타네이트 BaTiO₃를 생성시킴을 특징으로 하는 방법.
- 수동 전자부품, 특히 양의 저항 온도계수를 가진 저항기를 제조하기 위한 제1항 내지 8항의 방법에 따라 제조한 바륨 티타네이트 BaTiO₃의 용도.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.