KR880012660A - 무표피 다공성의 가교된 pvc수지입자 및 이의 제조방법 - Google Patents
무표피 다공성의 가교된 pvc수지입자 및 이의 제조방법 Download PDFInfo
- Publication number
- KR880012660A KR880012660A KR1019880003219A KR880003219A KR880012660A KR 880012660 A KR880012660 A KR 880012660A KR 1019880003219 A KR1019880003219 A KR 1019880003219A KR 880003219 A KR880003219 A KR 880003219A KR 880012660 A KR880012660 A KR 880012660A
- Authority
- KR
- South Korea
- Prior art keywords
- parts
- weight
- vinyl monomer
- dispersant
- monomer
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
본 도는 본 발명의 구체형에서 제조한 무표피 가교수지 및 표피형의 가교수지를 나타내는 log와 유사한 그래프로서, X축은 tanδ, Y축은 log눈금으로 복소점성계수, 숫자는 구체형에서 시행번호, 문자는 구체형에서 사용한 수지를 나타낸다.
Claims (20)
- 90중량 %이상의 수지입자가 (a)본질적으로 연소적인 주변기포막이 없다는 사실에 의해 증명되듯이 입자는 표피가 없고 : (b)210℃에서 측정할때 약 0.9 ×105포이즈 내지 약 1000.0 ×105포이즈의 복소점성계수 : (c)210℃에서 측정할때 1.0이하의 tanδ를 가지는 것을 특징으로 하는 미립자형태의 가교된 폴리비닐클로라이드 수지.
- 제1항에 있어서, 수지입자가 (a)약 0.85이하의 형상계수 : (b)약 0.1cc/g 내지 약 0.8cc/g의 수온다공성 : (c)약 70미크론 내지 약 1000미크론의 입도 : (d)약 2이하의 무롬성 : (e)약 400초이하의 분말혼합시간 : (f)입장의 약 20%이상의 표면 부위가 PVC이고 : (g)약 0.3내지 약 0.7의 tanδ: 및 (h)약 1.0 ×105내지 60.0 ×105포이즈의 복소점성계수를 가짐을 특징으로 하는 폴리비닐 클로라이드 단독 중합체수지.
- 제2항에 있어서, 수지입자가 (a)약 0.80이하의 형상계수 : (b)약 0.3cc/g 내지 약 0.5cc/g의 수온다공성 : (c)약 100미크론 내지 약 250미크론의 입도 : (d)약 0이하의 무롬성 : (e)약 250초이하의 분말혼합시간 : (f)입자의 약 60%이상의 표면 부위가 PVC이고 (g)약 4.0 ×105내지 60.0 ×105포이즈의 복소점성계수를 가짐을 특징으로 하는 폴리비닐 클로라이드 단독 중합체수지.
- 100중량부의 중합단량체당 약 0.01중량부 내지 약 0.1중량부의 물을 점성화 할수 있는 적어도 하나의 이온민감성 일차분산제, 및 적어도 하나의 이차분산제의 존재하에서 적어도 하나의 가교제와 함께 비닐단량체를 중합함에 있어서, 약 1%내지 약 5%의 단량체에서 중합체로의 전환시에 단량체 소적으로부터 상기의 실질적인 양의 일차분산제를 탈착하기에 충분한 양의 한 이온성물질을 중합매질에 장입시켜서 무표피의, 덩어리지고, 가교되고, 다공성인 미립자형태의 PVC수지를 제조하는, 다공성의, 무표피, 덩어리지고, 가교된 폴리비닐클로라이드 수지입자를 제조하기 위한 교반수성현탁방법.
- 제4항에 있어서, 이온민감성 일차분산제가 가볍게 가교된 아크릴산의 공중합체이고, 이차분산제가 60%이하 가수분해된 폴리비닐아세테이트이고, 이온성재료가 수산화나트륨인 방법.
- 제5항에 있어서, 일차분산제의 양이 비닐단량체 100중량부당 약 0.02내지 약 0.06중량부이고, 이차 계면활성제의 양이 비닐단량체 100중량부당 약 0.1내지 0.4중량부이고, 이온성재료가 비닐단량체 100중량부당 약 0.001중량부 내지 약 0.0100중량부인 방법.
- 제4항에 있어서, 비닐단량체가 비닐클로라이드이고, 가교제의 양이 비닐단량체 100중량부당 약 0.05중량부 내지 약 5.0중량부이고, 가교제가 디알릴크탈레이트이고, 중합매질에 가하기 이전에 가교제를 비닐단량체와 미리 혼합시키는 방법.
- (a)물과 적어도 하나의 물을 점성화할 수 있는 이온민감성 일차분산제를 교반 및 냉각수단이 장치된 중합용기에 장입하고, (b)물과 분산제를 교반하고 : (c)비-난류가 얻어지도록 교반을 감소하거나 중지하고 (d)하부는 점성화된 수성층이고 상부는 비닐단량체층인 두 액체층이 중합용기에 형성되도록 적어도 하나의 비닐단량체를 적어도 하나의 가교제 함께 중합용기에 장입하고 : (e)상부의 비닐단량체층에다 1.0gg/cc이하의 비중을 가지는 하나의 촉매, 중합될 비닐단량체보다 같거나 낮은 비중을 가지는 적어도 하나의 용매, 및 적어도 하나의 이차분산제로 이루어지는 용액을 장입하고 : (f)촉매가 비닐단량체 상부층을 통해 확산되도록 하고 : (g)전체 중합매질이 에멀션화되어 단량체소적이 수성 중합매질에 현탁되도록 교반을 증가하고 : (h)약 1%내지 약 5%의 전환이 되도록 비닐단량체를 중합하고 : (i)중합매질에 단량체 소적으로부터 실질적으로 일차분산제를 탈착하기에 충분한 양의 이온성물질을 장입하고 : (j)비닐단량체의 중합을 계속하여 다공성의 가교되고, 덩어리진, 무표피의 수지입자를 형성하고 : (k)반응용기로부터 중합된 수지를 옮김으로써 이루어지는, 수성매질에서 다공성의 가교된, 덩어리진, 무표피의 비닐수지입자를 제조하기 위한 방법.
- 제8항에 있어서, 비닐단량체가 비닐클로라이드이고, 이온민감성 일차분산제가 가볍게 가교된 아클릴산의 공중합체이고, 이차분산제가 솔비탄에스테르 및 약 60%이하의 가수분해도를 가지는 가수분해된 폴리비닐아세테이트로 이루어지는 군으로부터 선택되어지는 적어도 하나의 분산제인 방법.
- 제9항에 있어서, 일차분산제의 양이 비닐단량체 100중량부당 약 0.02내지 약 0.06중량부이고, 이온성재료가 비닐단량체에서 중합체로의 1%내지 2%전환시점에서 중합매질에 가해지고, 이차분산제의 양이 비닐단량체 100중량부당 약 0.1중량부 내지 약 0.4중량부인 방법.
- 제8항에 있어서, (e)의 용매를 적어도 2탄소원자 및 탄화수소를 가지는 알코올로 이루어지는 군으로부터 선택하고, 적어도 하나의 이차분산제를 중합용기에 장입되기 이전에 비닐단량체 및 가교제와 미리 혼합하고, (a)에서 물과 물을 점성화 할 수 있는 분산제(들)을 중합용기에 가해지기 이전에 미리 혼합하고, (d)에서 촉매, 용매 및 적어도 하나의 이차분산제를 함유하는 촉매용액을 중합용기에 가하기 이전에 비닐단량체와 미리 혼합시키는 방법.
- 제8항에 있어서, 가교제의 양이 비닐단량체 100중량부당 약 0.05중량부 내지약 5.0중량부이고, 가교제가 디알릴프탈레이트이고, 가교제를 중합용기에 비닐단량체와 분리해서 장입하는 방법.
- 본질적으로 (a)단량체 100중량부당 약 0.01내지 약 0.03 중량부의 물을 점성화할 수 있는 비중화된 이온민감성 일차분산제, 및 (b)단량체 100중량부당 약 0.1내지 약 0.4중량부의 이차분산제로 이루어지는 분산제계의 존재하에서 비닐단량체를 적어도 하나의 가교제와 함께 중합시키는 것으로 이루어지는, 다공성의, 무표피의, 덩어리진 폴리비닐클로라이드 수지입자를 생산하기 위한 교반 수성현탁방법.
- 제13항에 있어서, 일차분산제가 가볍게 가교된 아크릴산의 공중합체이고, 이차분산제가 60%이하 가수분해된 폴리비닐아세테이트이고, 비닐단량체가 비닐클로라이드이고, 가교제의 양이 비닐단량체 100중량부당 약 0.05중량부 내지 약 5.0중량부인 방법.
- (a)단량체 100중량부당 약 0.02 내지 약 약 0.06중량부의 물을 점성화할 수 있는 이온민감성 일차분산제 : (b)약 0.2 내지 약 0.4중량부의 비-폴리에틸렌 산화물을 함유하는 이차분산제 : 및 (c)비닐단량체 100중량부당 약 0.1 내지 약 0.3중량부의 70%이하의 가수분해도를 가지는 폴리비닐아세테이트 이차분산제를 포함하는 분산제계의 존재하에서 비닐단량체를 적어도 하나의 가교제와 중합하는 것으로 이루어지는 다공성, 무표피의, 덩어리지고, 가교된 폴리비닐클로라이드 수지입자를 생산하기 위한 교반 수성현탁방법.
- 제15항에 있어서, 비-폴리에틸렌 산화물을 함유하는 분산제가 솔비탄 트리올레에이트, 솔비탄 트리스테레이트, 솔비탄 모노올레이트, 솔비탄 모노팔미테이트, 글리세롤 모노올레에이트, 글리세롤 모노스테레이트, 및 트리글리세롤 모노올레에이트로 이루어지는 군으로부터 선택되고, 일차분산제가 가볍게 가교된 아크릴산의 공중합체이고, 가교제의 양이 비닐단량체 100중량부당 약 0.05중량부 내지 약 5.0중량부인 방법.
- 비닐단량체를 적어도 하나의 가교제와 괴상중합함으로써 이루어지는 무표피, 다공성의 가교된 PVC수지를 제조하기 위한 방법.
- 제17항에 있어서, 단량체에서 중합체로의 최종 전환이 약 35% 내지 약 65%이고, 비닐단량체가 비닐클로라이드이고, 가교제의 양이 비닐클로라이드 단량체 100중량부당 약 0.05중량부 내지 약 5.0중량부인 방법.
- 비닐단량체를 적어도 하나의 가교제와 중합시킴에 있어서 처음에 연속상으로서 단량체상을 사용하고 단량체에서 중합체로의 전환이 약 1퍼센트 내지 약 10%가 된후에 물을 가해서 수성상이 연속상이 되고 단량체가 비연속상이 되도록 하는 무표피, 다공성의, 가교된 PVC수지를 생산하기 위한 수성상 전화방법.
- 제19항에 있어서, 가교제의 양이 비닐단량체 100중량부당 약 0.05중량부 내지 약 5.0중량부이고, 가교제가 디알릴 프탈레이트인 방법.참고사항 : 최초출원 내용에 의하여 공개하는 것임.