KR20230052866A - 자외선 차단능력을 상승시키는 무기성 복합안료 및 이를 함유하는 화장료 조성물 - Google Patents
자외선 차단능력을 상승시키는 무기성 복합안료 및 이를 함유하는 화장료 조성물 Download PDFInfo
- Publication number
- KR20230052866A KR20230052866A KR1020230047820A KR20230047820A KR20230052866A KR 20230052866 A KR20230052866 A KR 20230052866A KR 1020230047820 A KR1020230047820 A KR 1020230047820A KR 20230047820 A KR20230047820 A KR 20230047820A KR 20230052866 A KR20230052866 A KR 20230052866A
- Authority
- KR
- South Korea
- Prior art keywords
- pigment
- group
- inorganic composite
- composite pigment
- inorganic
- Prior art date
Abstract
본 발명은 자외선 차단능력을 상승시키는 무기성 복합안료 및 이를 함유하는 화장료 조성물에 관한 것으로서, 백색안료를 포함하는 코어부 및 상기 코어부의 외각표면에 코팅되되, 상기 백색안료가 포함된 무기용액을 포함하는 표면코팅재를 포함하는 것을 특징으로 한다. 또한 상기 백색안료는, 이산화티탄, 징크옥사이드, 세륨옥사이드, 실리카, 탤크, 마이카, 보로실리케이드로 이루어진 군에서 선택된 적어도 1종 이상인 것을 특징으로 한다. 본 발명에 따른 자외선 차단능력을 상승시키는 무기성 복합안료는, 고굴절률의 백색안료에 백색안료를 재코팅처리하는 공정을 통해 안료의 표면이 개질되고 그 결과 자외선 차단능력을 상승시킨다.
Description
본 발명은 자외선 차단능력을 상승시키는 무기성 복합안료 및 이를 함유하는 화장료 조성물에 관한 것으로서, 더욱 상세하게는 고굴절률의 백색안료에 백색안료를 재코팅처리하는 공정을 통해 안료의 표면이 개질되고 그 결과 자외선 차단능력을 상승시키는 무기성 복합안료 및 이를 함유하는 화장료 조성물에 관한 것이다.
화장품에서 사용되는 자외선 차단제는 크게 유기성 자외선 차단제와 무기성 자외선 차단제로 구분한다.
유기성 자외선 차단제는 공명구조나 콘주게이션 구조 등을 갖는 유기 물질의 화학적 구조에 기인하여 자외선과 같은 빛의 파장은 흡수하지만 피부트러블과 같은 피부 자극을 유발할 수 있어 사용에 제한적이며, 시간이 흐름에 따라 피부에서 분비되는 피지 혹은 유분 등에 의해 씻겨 내려가 지속력에 영향을 미친다. 반면 무기성 자외선 차단제는 무기 광물을 이용하여 빛 자체를 차폐하는 차단막을 형성하여 자외선을 산란시키나, 도포 시 발림성이 낮아 뻣뻣하고, 백탁 현상으로 인하여 부자연스러운 피부연출 현상이 나타난다.
이러한 자외선 차단제의 단점을 극복하기 위해 최근에는 새로운 자외선 차단제 개발이 진행됨과 더불어 자외선 차단제의 효과를 극대화 시킬 수 있는 자외선 차단 상승제가 주목받고 있다. 이러한 소재들은 유기성 자외선 차단제의 안정화를 돕거나 무기성 자외선 차단제를 고르게 분산시키는 등의 역할을 한다.
그러나 현재 시장에서 유통되는 대부분의 상승제는 유기성 구조를 갖는 상승제이며 무기성의 상승제는 거의 없는 실정이다.
이에 본 출원인은 이산화티탄과 같은 굴절률이 높은 백색안료에 이산화티탄 등의 백색안료를 재코팅시킨 복합안료인 무기성 소재를 이용한 무기성 자외선 차단 상승제를 개발하였다.
본 발명은 상술한 문제점을 해결하기 위하여 안출된 것으로서, 제1 목적은 기존 이산화티탄과 같은 고굴절률의 백색안료를 코어로 사용하고, 코어에 다시 이산화티탄 등의 백색안료를 재코팅하여 무기 광물 표면에서의 난반사를 통하여 빛의 이동경로를 제어하여 자외선 차단효과를 상승시키는 것이다.
또한, 본 발명의 제2 목적은 일반적인 백색안료의 과도한 은폐력을 보정하여 적정한 은폐력을 부여하면서도 자연스러운 광채와 피부톤 표현이 가능한 자외선 차단능력을 상승시키는 무기성 복합안료를 함유하는 화장료 조성물을 제공하는 것이다.
또한, 본 발명의 제3 목적은 백색안료로 이루어진 코어의 최외각에 안료를 재코팅함으로써, 흡유량 등의 상승효과로 인하여 피부에서 분비되는 피지 등을 흡수하여 자외선 차단효과의 지속력을 제공할 수 있는 자외선 차단능력을 상승시키는 무기성 복합안료를 함유하는 화장료 조성물을 제공하는 것이다.
상기 목적을 달성하기 위하여, 본 발명에 따른 자외선 차단능력을 상승시키는 무기성 복합안료는, 백색안료를 포함하는 코어부 및 상기 코어부의 외각표면에 코팅되되, 상기 백색안료가 포함된 무기용액을 포함하는 표면코팅재를 포함하는 것을 특징으로 한다.
또한 상기 백색안료는, 이산화티탄, 징크옥사이드, 세륨옥사이드, 실리카, 탤크, 마이카, 보로실리케이드로 이루어진 군에서 선택된 적어도 1종 이상인 것을 특징으로 한다.
여기서, 백색안료는 무기성 복합안료 총 중량 대비 20중량% 내지 95중량%, 바람직하게는 20중량% 내지 80중량%이고, 무기용액은 무기성 복합안료 총 중량 대비 10중량% 내지 80중량%, 바람직하게는 20중량% 내지 50중량%인 것을 특징으로 한다.
또한, 본 발명에 따른 자외선 차단능력을 상승시키는 무기성 복합안료는, 표면코팅재가 코어부에 불균일하게 코팅되어 불균일한 표면을 형성하는 것을 특징으로 한다.
또한, 본 발명에 따른 자외선 차단능력을 상승시키는 무기성 복합안료는, 코어부 및 표면코팅재의 불균일한 표면에서의 다중 회절과 난반사의 감소를 통한 공명효과 및 반사광과 투과 반사광의 중첩 및 간섭을 통해 자외선 차단의 상승효과를 갖는 것을 특징으로 한다.
또한, 본 발명에 따른 자외선 차단능력을 상승시키는 무기성 복합안료는, 코어부 및 표면코팅재의 불균일한 표면의 다중 회절과 굴절 및 난반사의 감소를 통한 빛의 제어에 의해 피부자체의 톤이 자연스럽게 구현되는 브라이트닝 효과를 갖는 것을 특징으로 한다.
또한, 본 발명에 따른 자외선 차단능력을 상승시키는 무기성 복합안료는, 표면코팅재의 외각에는 소수성 또는 친수성 또는 피부 친화성을 가지며, 안료의 분산성을 올릴수 있도록, 실리콘 및 실란, 불소계 화합물, 금속 비누계 화합물, 천연 계면활성제, 고분자, 탄화수소류 고분자, 고급지방산, 고급알코올로 이루어진 군에서 선택된 적어도 1종 이상의 소수성 물질로 코팅하거나, 폴리올, 폴리옥시에틸렌, 아미노산계 복합물로 이루어진 군에서 선택된 적어도 1종 이상의 친수성 물질로 코팅되는 것을 특징으로 한다.
여기서, 소수성 물질인 실리콘 및 실란은 다이메티콘, 사이클로메티콘, 다이실록세인, 사이클로실록세인, 트리에톡시카프릴릴실란 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 불소계 화합물은 폴리플루오로알킬포스페이트에터, 퍼플루오로폴리메틸이소프로필에터 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 금속 비누계 화합물은 칼슘스테아레이트, 소듐스테아레이트, 마그네슘스테아레이트 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 천연 계면활성제는 레시틴, 수첨레시틴 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 고분자는 콜라겐, 셀룰로오스, 잔탄검 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 탄화수소류 고분자는 라우로일라이신, 폴리에스터, 폴리에틸렌, 폴리아크릴레이트, 폴리프로필렌 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 고급지방산은 스테아릭애씨드, 미리스틱애씨드, 팔미틱애씨드 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 고급알코올은 세틸알코올, 미리스틸알코올, 스테아릴알코올 등으로 이루어진 군에서 선택된 적어도 1종 이상이다.
또한, 친수성 물질인 폴리올은 글리세린, 부틸렌글라이콜, 다이프로필렌글라이콜, 프로판디올 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 폴리옥시에틸렌은 PEG-10, PEG-40 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 아미노산계 복합물은 라이신, 알지닌, 글라이신 등으로 이루어진 군에서 선택된 적어도 1종 이상이다.
또한, 본 발명에 따른 자외선 차단능력을 상승시키는 무기성 복합안료는, 반사광과 투과 반사광의 중첩 및 간섭으로 은폐력 및 자연스러운 피부톤을 구현할 뿐만 아니라, 흡유량의 증가를 통해 화장이 보다 오랜 시간 지속되는 것을 특징으로 한다.
또한, 본 발명에 따른 화장료 조성물은 자외선 차단능력을 상승시키는 무기성 복합안료를 유효성분으로 포함하는 것을 특징으로 한다.
또한, 본 발명에 따른 자외선 차단능력을 상승시키는 무기성 복합안료의 제조 방법은,
(a) 이산화티탄을 분산하여 백색안료를 제조하는 단계; (b) 분산된 백색안료에 사염화티탄 수용액과 알칼리 수용액을 첨가 및 교반하여 가수분해 반응시키고 수산화티탄 복합안료를 얻는 단계; (c) 상기 (b)단계가 완료된 용액을 냉각 및 세척한 다음 600 ~ 850 ℃에서 소결하여 산화물을 형성하는 단계;를 포함하여 구성된다.
여기서, 상기 (a) 단계는, 증류수에 이산화티탄을 첨가하고 60 ~ 90℃ 온도에서 교반하여 백색안료를 제조하는 것을 특징으로 한다.
또한, 상기 (b) 단계는 사염화티탄을 정제수에 용해시켜 10 ~ 40중량%농도의 사염화티탄 수용액을 제조하고, 제조된 사염화티탄 수용액과 10 ~ 30중량% 농도의 수산화나트륨 수용액을 분산된 백색안료에 첨가 및 교반하여 가수분해 반응시키고 수산화티탄 복합안료를 얻는 것을 특징으로 한다.
또한, 본 발명에 따른 자외선 차단능력을 상승시키는 무기성 복합안료의 제조 방법은,
(a) 증류수에 이산화티탄을 첨가하고 60 ~ 90℃의 온도에서 교반하여 이산화티탄을 분산하여 백색안료를 제조하는 단계; (b) 분산된 백색안료에 사염화티탄 수용액과 알칼리 수용액을 첨가 및 교반하여 가수분해 반응시키고 수산화티탄 복합안료를 얻는 단계; (c) 상기 (b)단계가 완료된 용액을 30분간 교반시켜 준 뒤 30분간 정치 시키고, 정치시켜 발생한 백색 침전물을 증류수를 사용하여 세척하고 여과시킨 다음 60 ~ 100℃에서 건조시켜 수산화티탄 복합분체를 얻고, 상기 수산화티탄 복합 분체를 600 ~ 850℃에서 소결하여 백색안료의 표면에 무기안료의 산화물을 형성하는 단계; (d) 상기 복합안료가 소수성 또는 친수성 또는 피부 친화성을 가지며, 상기 산화물의 수상부 또는 유상부에서의 분산성을 올릴수 있도록, 실리콘 및 실란, 불소계 화합물, 금속 비누계 화합물, 천연 계면활성제, 고분자, 탄화수소류 고분자, 고급지방산, 고급알코올로 이루어진 군에서 선택된 적어도 1종 이상의 소수성 물질로 코팅하거나, 폴리올, 폴리옥시에틸렌, 아미노산계 복합물로 이루어진 군에서 선택된 적어도 1종 이상의 친수성 물질로 코팅하는 단계;를 포함하여 구성되는 것을 특징으로 한다.
여기서, 소수성 물질인 실리콘 및 실란은 다이메티콘, 사이클로메티콘, 다이실록세인, 사이클로실록세인, 트리에톡시카프릴릴실란 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 불소계 화합물은 폴리플루오로알킬포스페이트에터, 퍼플루오로폴리메틸이소프로필에터 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 금속 비누계 화합물은 칼슘스테아레이트, 소듐스테아레이트, 마그네슘스테아레이트 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 천연 계면활성제는 레시틴, 수첨레시틴 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 고분자는 콜라겐, 셀룰로오스, 잔탄검 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 탄화수소류 고분자는 라우로일라이신, 폴리에스터, 폴리에틸렌, 폴리아크릴레이트, 폴리프로필렌 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 고급지방산은 스테아릭애씨드, 미리스틱애씨드, 팔미틱애씨드 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 고급알코올은 세틸알코올, 미리스틸알코올, 스테아릴알코올 등으로 이루어진 군에서 선택된 적어도 1종 이상이다.
또한, 친수성 물질인 폴리올은 글리세린, 부틸렌글라이콜, 다이프로필렌글라이콜, 프로판디올 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 폴리옥시에틸렌은 PEG-10, PEG-40 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 아미노산계 복합물은 라이신, 알지닌, 글라이신 등으로 이루어진 군에서 선택된 적어도 1종 이상이다.
또한, 본 발명에 따른 화장료 조성물은, 상술한 제조방법에 의해 제조된 자외선 차단능력을 상승시키는 무기성 복합안료를 유효성분으로 포함하는 것을 특징으로 한다.
또한, 본 발명에 따른 화장료 조성물은, 무기성 복합안료가 화장료 조성물 총 중량 대비 0.1중량% 내지 20중량%, 바람직하게는 4중량% 내지 7중량% 포함되는 것을 특징으로 한다.
본 발명에 따른 자외선 차단능력을 상승시키는 무기성 복합안료는 이산화티탄과 같은 굴절률이 높은 백색안료에 이산화티탄 등의 백색안료를 재코팅시킨 무기성 소재를 이용하므로, 무기 광물 표면에서의 다중 회절효과 및 공명효과를 통해 난반사를 줄여 피부표면에 도달하는 빛의 이동경로와 반사율을 제어하여 자외선 차단효과를 상승시키는 효과가 있다.
또한, 본 발명에 따른 자외선 차단능력을 상승시키는 무기성 복합안료는 난반사의 감소를 통해 자연스러운 광채와 피부톤 표현효과를 보여주어 자연스러운 외관연출을 가능하게 하는 효과가 있다.
또한, 본 발명에 따른 자외선 차단능력을 상승시키는 무기성 복합안료를 함유하는 화장료 조성물은, 기존 무기성 자외선 차단제의 단점인 발림성과 백탁도를 크게 개선하였으며, 최외각 코팅으로 인하여 일반적인 이산화티탄 대비 우수한 흡유력으로 피부에서 분비되는 피지 등이 흡수되므로 화장품을 피부에서 오랜 시간 지속 시켜 자외선 차단효과가 보다 긴 시간 동안 유지되도록 하는 효과가 있다.
도1은 본 발명의 일실시예에 따른 무기성 복합안료의 제조 공정 모식도.
도 2는 본 발명의 일실시예에 따른, 이산화티탄안료로 된 코어부와 코어부의 외각부에 이산화티탄으로 된 표면코팅재가 코팅된 형태의 복합안료의 모형도 및 외각부에서 빛의 이동경로를 나타낸 도면.
도 3은 본 발명의 일실시예에 따른 무기성 복합안료 표면에서 빛의 다중회절 효과로 인해 난반사가 줄어들며, 피부표면에 달하는 빛의 제어를 통해 자외선 차단 및 피부색이 발현되는 것을 나타낸 도면.
도 4는 본 발명의 일실시예에 따른 무기성 복합안료의 제조예 5의 SEM 및 TEM 이미지를 나타낸 도면.
도 5는 본 발명의 일실시예에 따른 무기성 복합안료를 적용시 자외선 차단지수를 비교예와 비교한 도표.
도 2는 본 발명의 일실시예에 따른, 이산화티탄안료로 된 코어부와 코어부의 외각부에 이산화티탄으로 된 표면코팅재가 코팅된 형태의 복합안료의 모형도 및 외각부에서 빛의 이동경로를 나타낸 도면.
도 3은 본 발명의 일실시예에 따른 무기성 복합안료 표면에서 빛의 다중회절 효과로 인해 난반사가 줄어들며, 피부표면에 달하는 빛의 제어를 통해 자외선 차단 및 피부색이 발현되는 것을 나타낸 도면.
도 4는 본 발명의 일실시예에 따른 무기성 복합안료의 제조예 5의 SEM 및 TEM 이미지를 나타낸 도면.
도 5는 본 발명의 일실시예에 따른 무기성 복합안료를 적용시 자외선 차단지수를 비교예와 비교한 도표.
이하, 첨부된 도면을 참조하여 본 발명의 실시예를 구체적으로 설명하면 다음과 같다. 본 발명의 실시예는 여러 가지 형태로 변형될 수 있으며, 본 발명의 범위가 아래에서 설명하는 실시예에 한정되는 것으로 해석되어서는 안 된다. 본 실시예는 당해 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 본 발명을 더욱 상세하게 설명하기 위해서 제공되는 것이다. 따라서 도면에 나타난 각 요소의 형상은 보다 분명한 설명을 강조하기 위하여 과장될 수 있다.
도1은 본 발명의 일실시예에 따른 무기성 복합안료의 제조 공정 모식도이고, 도 2는 본 발명의 일실시예에 따른 이산화티탄안료로 된 코어부와 코어부의 외각부에 이산화티탄으로 된 표면코팅재가 코팅된 형태의 복합안료의 모형도 및 외각부에서 빛의 이동경로를 나타낸 도면이며, 도 3은 본 발명의 일실시예에 따른 무기성 복합안료 표면에서 빛의 다중회절 효과로 인해 난반사가 줄어들며, 피부표면에 달하는 빛의 제어를 통해 자외선 차단 및 피부색이 발현되는 것을 나타낸 도면이고, 도 4는 본 발명의 일실시예에 따른 무기성 복합안료의 제조예 5의 주사전자현미경(SEM) 및 투과전자현미경(TEM) 이미지를 나타낸 도면이며, 도 5는 본 발명의 일실시예에 따른 무기성 복합안료를 적용시 자외선 차단지수를 비교예와 비교한 도표이다.
<제조예>
증류수에 이산화티탄을 첨가하고 60 ~ 90℃의 온도에서 교반하여 이산화티탄을 분산하여 백색안료를 제조하고, 분산된 백색안료에 사염화티탄용액과 같은 무기용액과 알칼리 수용액을 이용하여 가수분해를 통해 수산화티탄 복합안료를 얻었다. 완료된 용액을 30분간 교반시켜 준 뒤 30분간 정치 시키고, 정치시켜 발생한 백색 침전물을 증류수를 사용하여 세척하고 여과시킨 다음 60 ~ 100℃에서 건조시켜 수산화티탄 복합분체를 얻었다. 이렇게 정제된 수산화티탄 복합 분체를 600 ~ 850℃에서 소결하여 백색안료의 표면에 무기안료의 산화물을 형성하였다.
이후, 복합안료가 소수성 또는 친수성 또는 피부 친화성을 가지며, 상기 산화물의 수상부 또는 유상부에서의 분산성을 올릴수 있도록, 실리콘 및 실란, 불소계 화합물, 금속 비누계 화합물, 천연 계면활성제, 고분자, 탄화수소류 고분자, 고급지방산, 고급알코올로 이루어진 군에서 선택된 적어도 1종 이상의 소수성 물질로 코팅하거나, 폴리올, 폴리옥시에틸렌, 아미노산계 복합물로 이루어진 군에서 선택된 적어도 1종 이상의 친수성 물질로 코팅처리하였다.
여기서, 소수성 물질인 실리콘 및 실란은 다이메티콘, 사이클로메티콘, 다이실록세인, 사이클로실록세인, 트리에톡시카프릴릴실란 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 불소계 화합물은 폴리플루오로알킬포스페이트에터, 퍼플루오로폴리메틸이소프로필에터 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 금속 비누계 화합물은 칼슘스테아레이트, 소듐스테아레이트, 마그네슘스테아레이트 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 천연 계면활성제는 레시틴, 수첨레시틴 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 고분자는 콜라겐, 셀룰로오스, 잔탄검 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 탄화수소류 고분자는 라우로일라이신, 폴리에스터, 폴리에틸렌, 폴리아크릴레이트, 폴리프로필렌 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 고급지방산은 스테아릭애씨드, 미리스틱애씨드, 팔미틱애씨드 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 고급알코올은 세틸알코올, 미리스틸알코올, 스테아릴알코올 등으로 이루어진 군에서 선택된 적어도 1종 이상이다.
또한, 친수성 물질인 폴리올은 글리세린, 부틸렌글라이콜, 다이프로필렌글라이콜, 프로판디올 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 폴리옥시에틸렌은 PEG-10, PEG-40 등으로 이루어진 군에서 선택된 적어도 1종 이상이다. 아미노산계 복합물은 라이신, 알지닌, 글라이신 등으로 이루어진 군에서 선택된 적어도 1종 이상이다.
이와 같은 제조 공정에 따라 제조한 무기성 복합안료의 제조예는 아래 [표1]과 같다.
| 제조예 | 1 | 2 | 3 | 4 | 5 |
| 코어 백색안료 함량 (중량%) |
90 | 80 | 70 | 60 | 50 |
| 외각부 무기용액 함량 (중량%) |
10 | 20 | 30 | 40 | 50 |
상기 제조방법에 따라 만들어진 무기성 복합안료에 대해, 주사전자현미경(SEM) 및 투과전자현미경(TEM)을 통해 복합안료의 표면에 코팅면이 형성되는 것을 확인하였다. 그 중 제조예 5의 표면에 형성된 코팅면의 결과를 도 4에 나타냈다.
도 4에 도시된 바와 같이, 코팅된 복합안료는 일반적인 이산화티탄 안료에 비해 넓고 불균일한 표면을 형성하였다.
이와 같이 코팅된 복합안료의 코어부 및 표면코팅재의 넓고 불균일한 표면에 의하여, 다중 회절과 난반사의 감소를 통한 공명효과 및 반사광과 투과 반사광의 중첩 및 간섭 현상에 따른 자외선 차단의 상승효과를 갖게 된다.
또한, 코팅된 복합안료의 코어부 및 표면코팅재의 표면의 다중 회절과 굴절 및 난반사의 감소를 통한 빛의 제어에 의해 자연스러운 피부자체의 톤이 구현되는 브라이트닝 효과를 갖게 된다.
여기서, 백색안료는 무기성 복합안료 총 중량 대비 20중량% 내지 95중량%, 바람직하게는 30중량% 내지 90중량% 일 수 있다. 상기 백색안료의 함량이 20중량% 미만으로 포함되는 경우 은폐력이 형성되지 않는 단점이 있으며, 95중량%를 초과로 포함하는 경우 사용감 개선 및 백탁현상이 심하게 발생하는 단점이 있다.
그리고, 무기 용액은 무기성 복합안료 총 중량 대비 10중량% 내지 80중량%, 바람직하게 10중량% 내지 70중량% 일 수 있다. 상기 무기 용액의 함량이 10중량% 미만으로 포함되는 경우 사용감이 거칠며 투명도 개선이 되지 않는 단점이 있으며, 80중량%를 초과로 포함하는 경우 과도한 투명도로 인해 은폐력이 형성되지 않는 단점이 있다.
<제형 실시예>
본 발명에 따른 무기성 복합안료를 함유하는 자외선 차단제를 통상의 제조 공정에 따라 제조한 결과는 아래 [표2]와 같다.
| 상 | 성분 | 함량 | ||||
| 비교예1 | 실시예1 | 실시예2 | 실시예3 | 실시예4 | ||
| 유상부 |
폴리글리세릴-4 아이소테아레이트 하이드록시스테아레이트/세바케이트 | 3 | 3 | 3 | 3 | 3 |
| 솔비탄세스퀴올리에이트 | 1 | 1 | 1 | 1 | 1 | |
| 다이카프릴릴카보네이트 | 20 | 20 | 20 | 20 | 20 | |
| 안료부 |
미립자 이산화티탄 | 6 | 6 | 6 | 6 | 6 |
| 미립자 산화아연 | 12 | 12 | 12 | 12 | 12 | |
| 구상 안료 | 5 | |||||
| 제조예2 | 2.5 | 5 | ||||
| 제조예5 | 2.5 | 5 | ||||
| 다이스테아다이모늄헥토라이트 | 1 | 1 | 1 | 1 | 1 | |
| 다이부틸아디페이트 | 10 | 10 | 10 | 10 | 10 | |
| 수상부 | 염화마그네슘 | 1 | 1 | 1 | 1 | 1 |
| 부틸렌글라이콜 | 7 | 7 | 7 | 7 | 7 | |
| 정제수 | to 100 | to 100 | to 100 | to 100 | to 100 | |
| 방부제 | 페녹시에탄올 | q.s | q.s | q.s | q.s | q.s |
상기 제형 실시예로 제조된 무기성 복합안료를 함유하는 자외선 차단제에서 복합안료의 자외선 차단 상승효과를 확인하기 위해 UV 차단 테스트를 진행하였다. 자외선 차단 확인을 위해 HelioScreen Labs의 HELIOPLATE HD6 (크기: 4.7cm X 4.7cm)에 자외선차단제 28.6 mg을 도포한 후 30분 경과 후의 자외선 차단 능력을 Labsphere Inc.의 Sunscreen Analyzer인 UV-2000S 장치를 이용하여 확인하였다. 시험 결과는 도 5와 같이 확인되었다. 자외선 차단지수는 SPF로 표기하였다.
도 5에 나타낸 바와 같이, 자외선 차단제가 제조된 무기성 복합안료를 함유한 경우 자외선 차단 지수가 실시예2에서 57.70, 실시예4에서는 46.19로 비교예에 비해 대략 2배 이상 상승하는 것을 확인할 수 있었다.
여기서, 무기성 복합안료는 자외선 차단제 총 중량 대비 0.1중량% 내지 20중량%, 바람직하게는 4중량% 내지 7중량% 일 수 있다. 상기 무기성 복합안료의 함량이 0.1중량% 미만으로 포함되는 경우 자외선 차단효과가 현저히 떨어지며, 사용감 개선 및 은폐력 형성에 있어서도 효과가 미미하며 자외선 차단 상승 효과 또한 기대할 수 없게 된다. 또한 20중량%를 초과로 포함하는 경우 유분감이 부족해져 매트하게되며, 무겁고 뻑뻑한 사용감을 줄 수 있다.
비록 본 발명이 상기에서 언급한 바람직한 실시예와 관련하여 설명되었지만, 본 발명의 요지와 범위로부터 벗어남이 없이 다른 다양한 수정이나 변형이 가능할 것이다. 그러므로 개시된 실시예들은 한정적인 관점이 아니라 설명적인 관점에서 고려되어야 한다. 본 발명의 범위는 전술한 설명이 아니라 특히 청구범위에 나타나 있으며, 그와 동등한 범위 내에 있는 모든 차이점은 본 발명에 포함된 것으로 해석되어야 할 것이다.
Claims (13)
- 백색안료를 포함하는 코어부 및
상기 코어부의 외각표면에 불균일하게 코팅되며, 상기 백색안료가 포함된 무기용액을 포함하는 표면코팅재를 포함하여 구성되고,
상기 표면코팅재는 상기 코어부에 불균일한 표면을 형성하여, 상기 코어부 및 상기 표면코팅재의 불균일한 표면의 다중 회절과 난반사를 통한 공명효과 및 반사광과 투과 반사광의 중첩 및 간섭을 통해 자외선 차단의 상승효과를 갖는 것을 특징으로 하고,
상기 백색안료는 무기성 복합안료 총 중량 대비 20중량% 내지 80중량%, 상기 무기용액은 무기성 복합안료 총 중량 대비 20중량% 내지 50중량%이며,
상기 백색안료는,
이산화티탄, 징크옥사이드, 세륨옥사이드, 실리카, 탤크, 마이카, 보로실리케이드로 이루어진 군에서 선택된 적어도 1종 이상인 것을 특징으로 하는 자외선 차단능력을 상승시키는 무기성 복합안료.
- 제1 항에 있어서,
상기 코어부 및 상기 표면코팅재의 표면의 다중 회절과 굴절 및 난반사의 감소를 통한 빛의 제어에 의해 피부자체의 톤이 자연스럽게 구현되는 브라이트닝 효과를 갖는 것을 특징으로 하는 자외선 차단능력을 상승시키는 무기성 복합안료.
- 제1 항에 있어서,
상기 표면코팅재의 외각에는 실리콘 및 실란, 불소계 화합물, 금속 비누계 화합물, 천연 계면활성제, 고분자, 탄화수소류 고분자, 고급지방산, 고급알코올로 이루어진 군에서 선택된 적어도 1종 이상의 소수성 물질로 코팅하거나, 또는
폴리올, 폴리옥시에틸렌, 아미노산계 복합물로 이루어진 군에서 선택된 적어도 1종 이상의 친수성 물질이 더 코팅되는 것을 특징으로 하는 자외선 차단능력을 상승시키는 무기성 복합안료.
- 제3 항에 있어서,
상기 실리콘 및 실란은 다이메티콘, 사이클로메티콘, 다이실록세인, 사이클로실록세인, 트리에톡시카프릴릴실란으로 이루어진 군에서 선택된 적어도 1종 이상이고,
상기 불소계 화합물은 폴리플루오로알킬포스페이트에터, 퍼플루오로폴리메틸이소프로필에터로 이루어진 군에서 선택된 적어도 1종 이상이며,
상기 금속 비누계 화합물은 칼슘스테아레이트, 소듐스테아레이트, 마그네슘스테아레이트로 이루어진 군에서 선택된 적어도 1종 이상이고,
상기 천연 계면활성제는 레시틴, 수첨레시틴으로 이루어진 군에서 선택된 적어도 1종 이상이며,
상기 고분자는 콜라겐, 셀룰로오스, 잔탄검으로 이루어진 군에서 선택된 적어도 1종 이상이고,
상기 탄화수소류 고분자는 라우로일라이신, 폴리에스터, 폴리에틸렌, 폴리아크릴레이트, 폴리프로필렌으로 이루어진 군에서 선택된 적어도 1종 이상이며,
상기 고급지방산은 스테아릭애씨드, 미리스틱애씨드, 팔미틱애씨드로 이루어진 군에서 선택된 적어도 1종 이상이고,
상기 고급알코올은 세틸알코올, 미리스틸알코올, 스테아릴알코올로 이루어진 군에서 선택된 적어도 1종 이상인 것을 특징으로 하는 자외선 차단능력을 상승시키는 무기성 복합안료.
- 제3 항에 있어서,
상기 폴리올은 글리세린, 부틸렌글라이콜, 다이프로필렌글라이콜, 프로판디올로 이루어진 군에서 선택된 적어도 1종 이상이고,
상기 폴리옥시에틸렌은 PEG-10, PEG-40로 이루어진 군에서 선택된 적어도 1종 이상이며,
상기 아미노산계 복합물은 라이신, 알지닌, 글라이신으로 이루어진 군에서 선택된 적어도 1종 이상인 것을 특징으로 하는 자외선 차단능력을 상승시키는 무기성 복합안료.
- 제1 항 내지 제5 항 중 어느 한 항의 자외선 차단능력을 상승시키는 무기성 복합안료를 유효성분으로 포함하는 화장료 조성물.
- 제6 항에 있어서,
상기 무기성 복합안료는 화장료 조성물 총 중량 대비 4중량% 내지 7중량% 포함하는 것을 특징으로 하는 자외선 차단능력을 상승시키는 무기성 복합안료를 유효성분으로 함유하는 화장료 조성물.
- (a) 이산화티탄을 분산하여 백색안료를 제조하는 단계;
(b) 분산된 백색안료에 사염화티탄 수용액과 알칼리 수용액을 첨가 및 교반하여 가수분해 반응시키고 수산화티탄 복합안료를 얻는 단계; 및
(c) 상기 (b)단계가 완료된 용액을 냉각 및 세척한 다음, 소결하여 산화물을 형성하는 단계;를 포함하여 구성되며,
상기 (a)단계에서 분산된 백색안료는 코어부를 구성하고,
상기 (b)단계 및 (c)단계를 거치며, 상기 코어부의 외각표면에 무기용액을 포함하는 표면코팅재가 불균일하게 코팅되어 불균일한 표면을 형성하며, 상기 코어부 및 상기 표면코팅재의 불균일한 표면의 다중 회절과 난반사를 통한 공명효과 및 반사광과 투과 반사광의 중첩 및 간섭을 통해 자외선 차단의 상승효과를 가지며,
상기 백색안료는 무기성 복합안료 총 중량 대비 20중량% 내지 80중량%, 상기 무기용액은 무기성 복합안료 총 중량 대비 20중량% 내지 50중량%이고,
상기 백색안료는,
이산화티탄, 징크옥사이드, 세륨옥사이드, 실리카, 탤크, 마이카, 보로실리케이드로 이루어진 군에서 선택된 적어도 1종 이상인 것을 특징으로 하는 자외선 차단능력을 상승시키는 무기성 복합안료의 제조 방법.
- 제8 항에 있어서,
상기 (a) 단계는, 증류수에 이산화티탄을 첨가하고 60 내지 90℃ 온도에서 교반하여 백색안료를 제조하는 것을 특징으로 하는 자외선 차단능력을 상승시키는 무기성 복합안료의 제조 방법.
- 제8 항에 있어서,
상기 (b) 단계는 사염화티탄을 정제수에 용해시켜 10 ~ 40중량%농도의 사염화티탄 수용액을 제조하고, 제조된 사염화티탄 수용액과 10 ~ 30중량% 농도의 수산화나트륨 수용액을 분산된 백색안료에 첨가 및 교반하여 가수분해 반응시키고 수산화티탄 복합안료를 얻는 것을 특징으로 하는 자외선 차단능력을 상승시키는 무기성 복합안료의 제조 방법.
- (a) 증류수에 이산화티탄을 첨가하고 60 ~ 90℃의 온도에서 교반하여 이산화티탄을 분산하여 백색안료를 제조하는 단계;
(b) 분산된 백색안료에 사염화티탄 수용액과 알칼리 수용액을 첨가 및 교반하여 가수분해 반응시키고 수산화티탄 복합안료를 얻는 단계;
(c) 상기 (b)단계가 완료된 용액을 30분간 교반시켜 준 뒤 30분간 정치 시키고, 정치시켜 발생한 백색 침전물을 증류수를 사용하여 세척하고 여과시킨 다음 60 ~ 100℃에서 건조시켜 수산화티탄 복합분체를 얻고, 상기 수산화티탄 복합 분체를 600 ~ 850℃에서 소결하여 백색안료의 표면에 무기안료의 산화물을 형성하는 단계; 및
(d) 상기 산화물에 실리콘 및 실란, 불소계 화합물, 금속 비누계 화합물, 천연 계면활성제, 고분자, 탄화수소류 고분자, 고급지방산, 고급알코올로 이루어진 군에서 선택된 적어도 1종 이상의 소수성 물질을 코팅하거나, 또는 폴리올, 폴리옥시에틸렌, 아미노산계 복합물로 이루어진 군에서 선택된 적어도 1종 이상의 친수성 물질을 코팅하는 단계;를 포함하여 구성되며,
상기 (a)단계에서 분산된 백색안료는 코어부를 구성하고,
상기 (b)단계 및 (c)단계를 거치며, 상기 코어부의 외각표면에 무기용액을 포함하는 표면코팅재가 불균일하게 코팅되어 불균일한 표면을 형성하며, 상기 코어부 및 상기 표면코팅재의 불균일한 표면의 다중 회절과 난반사를 통한 공명효과 및 반사광과 투과 반사광의 중첩 및 간섭을 통해 자외선 차단의 상승효과를 가지며,
상기 백색안료는 무기성 복합안료 총 중량 대비 20중량% 내지 80중량%, 상기 무기용액은 무기성 복합안료 총 중량 대비 20중량% 내지 50중량%이고,
상기 백색안료는,
이산화티탄, 징크옥사이드, 세륨옥사이드, 실리카, 탤크, 마이카, 보로실리케이드로 이루어진 군에서 선택된 적어도 1종 이상인 것을 특징으로 하는 자외선 차단능력을 상승시키는 무기성 복합안료의 제조 방법.
- 제8 항 내지 제11 항 중 어느 한 항의 제조방법으로 제조된 자외선 차단능력을 상승시키는 무기성 복합안료를 유효성분으로 함유하는 화장료 조성물.
- 제12 항에 있어서,
상기 무기성 복합안료는 화장료 조성물 총 중량 대비 4중량% 내지 7중량% 포함하는 것을 특징으로 하는 자외선 차단능력을 상승시키는 무기성 복합안료를 유효성분으로 함유하는 화장료 조성물.