KR20190025726A - 수지 조성물, 프리프레그, 적층판, 금속박 피복 적층판, 프린트 배선판, 및 다층 프린트 배선판 - Google Patents
수지 조성물, 프리프레그, 적층판, 금속박 피복 적층판, 프린트 배선판, 및 다층 프린트 배선판 Download PDFInfo
- Publication number
- KR20190025726A KR20190025726A KR1020197004770A KR20197004770A KR20190025726A KR 20190025726 A KR20190025726 A KR 20190025726A KR 1020197004770 A KR1020197004770 A KR 1020197004770A KR 20197004770 A KR20197004770 A KR 20197004770A KR 20190025726 A KR20190025726 A KR 20190025726A
- Authority
- KR
- South Korea
- Prior art keywords
- group
- resin composition
- parts
- mass
- structural unit
- Prior art date
Abstract
높은 유리 전이 온도를 갖거나 (고 Tg), 명확한 유리 전이 온도를 갖지 않고 (Tg 레스), 또한, 프린트 배선판, 특히, 다층 코어리스 기판의 휨을 충분히 저감 (저휨을 달성) 할 수 있는 수지 조성물, 프리프레그, 적층판, 금속박 피복 적층판, 프린트 배선판, 및 다층 프린트 배선판을 제공하기 위해서, 본 발명에 의한 수지 조성물은, 말레이미드 화합물 (A) 와, 알릴기 함유 화합물 (B) 와, 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 및/또는 빗형 그래프트 폴리머 (D) 를 함유한다. 또, 상기 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 또는 상기 빗형 그래프트 폴리머 (D) 의 수지 조성물에 있어서의 함유량이, 수지 고형분 100 질량부에 대하여 3 ∼ 25 질량부이다.
Description
본 발명은 수지 조성물, 프리프레그, 적층판, 금속박 피복 적층판, 프린트 배선판, 및 다층 프린트 배선판에 관한 것이다.
최근, 전자 기기나 통신기, 퍼스널 컴퓨터 등에 널리 사용되고 있는 반도체 패키지의 고기능화, 소형화가 진행됨에 따라서, 반도체 패키지용의 각 부품의 고집적화나 고밀도 실장화가 최근 더욱더 가속되고 있다. 이에 수반하여, 반도체 패키지용의 프린트 배선판에 요구되는 여러 특성은 더욱더 어려운 것이 되고 있다. 이러한 프린트 배선판에 요구되는 특성으로는, 예를 들어, 저흡수성, 흡습 내열성, 난연성, 저유전율, 저유전 정접, 저열팽창률, 내열성, 내약품성, 고 (高) 도금 필 강도 등을 들 수 있다. 또, 그것들에 더하여, 프린트 배선판, 특히, 다층 코어리스 기판의 휨을 억제하는 (저 (低) 휨을 달성하는) 것이, 최근, 중요한 과제로 되고 있어, 다양한 대책이 강구되어 오고 있다.
그 대책의 하나로서, 프린트 배선판에 사용되는 절연층의 저열팽창화를 들 수 있다. 이것은, 프린트 배선판의 열팽창률을 반도체 소자의 열팽창률에 가까이 함으로써 휨을 억제하는 수법이며, 현재 활발히 받아들여지고 있다 (예를 들어, 특허문헌 1 ∼ 3 참조).
반도체 플라스틱 패키지의 휨을 억제하는 수법으로는, 프린트 배선판의 저열팽창화 이외에도, 적층판의 강성을 높게 하는 것 (고강성화) 이나 적층판의 유리 전이 온도를 높게 하는 것 (고 Tg 화) 이 검토되고 있다 (예를 들어, 특허문헌 4 및 5 참조).
그러나, 본 발명자들의 상세한 검토에 의하면, 상기 종래의 기술로써도, 프린트 배선판, 특히, 다층 코어리스 기판의 휨을 아직 충분히 저감할 수는 없어, 추가적인 개량이 요망되고 있다.
즉, 본 발명은, 높은 유리 전이 온도를 갖거나 (고 Tg), 명확한 유리 전이 온도를 갖지 않고 (이른바 Tg 레스), 또한, 프린트 배선판, 특히, 다층 코어리스 기판의 휨을 충분히 저감 (저휨을 달성) 할 수 있는 수지 조성물, 그리고, 그 수지 조성물을 사용한, 프리프레그, 적층판, 금속박 피복 적층판, 프린트 배선판, 및 다층 프린트 배선판을 제공하는 것을 목적으로 한다.
본 발명자들은, 상기 과제를 해결하기 위해서 예의 검토를 실시한 결과, 종래, 반도체 플라스틱 패키지용의 프린트 배선판의 휨 거동에 관해서는, 프리프레그의 경화물에 있어서, 보다 큰 열시 (熱時) 저장 탄성률, 및 보다 높은 탄성률 유지율을 실현할 수 있는 수지 조성물이 유효한 것으로 생각되어 왔기는 했지만, 반드시 그렇다고는 할 수 없는 것이 판명되어 왔다. 또한, 본 발명자들은, 예의 연구를 진행시킨 결과, 말레이미드 화합물 및 알릴기 함유 화합물에 더하여, 특정한 에폭시 수지 및/또는 빗형 그래프트 폴리머를 소정의 함유량으로 사용함으로써, 상기 문제점을 해결할 수 있는 것을 알아내어, 본 발명을 완성하기에 이르렀다.
즉, 본 발명은 이하와 같다.
[1]
말레이미드 화합물 (A) 와,
알릴기 함유 화합물 (B) 와,
비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 및/또는 빗형 그래프트 폴리머 (D)
를 함유하고,
상기 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 또는 상기 빗형 그래프트 폴리머 (D) 의 수지 조성물에 있어서의 함유량이, 수지 고형분 100 질량부에 대하여 3 ∼ 25 질량부인, 수지 조성물.
[2] 상기 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 와 상기 빗형 그래프트 폴리머 (D) 의 수지 조성물에 있어서의 함유량의 합계량이, 수지 고형분 100 질량부에 대하여 3 ∼ 25 질량부인,
[1] 에 기재된 수지 조성물.
[3]
상기 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 의 에폭시 당량이 400 g/eq. 이상인,
[1] 또는 [2] 에 기재된 수지 조성물.
[4]
상기 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 는, 하기 식 (1) 로 나타내는 것인,
[1] ∼ [3] 중 어느 하나에 기재된 수지 조성물.
[화학식 1]
식 (1) 중, R1 및 R2 는, 각각 독립적으로, 수소 원자, 또는 메틸기를 나타내고, R3 ∼ R6 은, 각각 독립적으로, 수소 원자, 메틸기, 염소 원자, 또는 브롬 원자를 나타내고, X 는, 에틸렌옥시에틸기, 디(에틸렌옥시)에틸기, 트리(에틸렌옥시)에틸기, 프로필렌옥시프로필기, 디(프로필렌옥시)프로필기, 트리(프로필렌옥시)프로필기, 또는 탄소수 2 ∼ 15 의 알킬렌기를 나타내고, n 은, 자연수를 나타낸다.
[5]
상기 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 는, 상기 식 (1) 에 있어서의 X 가 에틸렌기의 것인,
[4] 에 기재된 수지 조성물.
[6]
상기 알릴기 함유 화합물 (B) 가, 알릴페놀 유도체 (E) 및/또는 알케닐 치환 나디이미드 화합물 (F) 인,
[1] ∼ [5] 중 어느 하나에 기재된 수지 조성물.
[7]
상기 알케닐 치환 나디이미드 화합물 (F) 가, 하기 식 (6) 으로 나타내는 화합물을 포함하는,
[6] 에 기재된 수지 조성물.
[화학식 2]
식 (6) 중, R1 은, 각각 독립적으로, 수소 원자, 또는 탄소수 1 ∼ 6 의 알킬기를 나타내고, R2 는, 탄소수 1 ∼ 6 의 알킬렌기, 페닐렌기, 비페닐렌기, 나프틸렌기, 또는 하기 식 (7) 혹은 (8) 로 나타내는 기를 나타낸다.
[화학식 3]
식 (7) 중, R3 은, 메틸렌기, 이소프로필리덴기, 또는, CO, O, S, 혹은 SO2 로 나타내는 치환기를 나타낸다.
[화학식 4]
식 (8) 중, R4 는, 각각 독립적으로, 탄소수 1 ∼ 4 의 알킬렌기, 또는 탄소수 5 ∼ 8 의 시클로알킬렌기를 나타낸다.
[8]
상기 말레이미드 화합물 (A) 로서, 비스(4-말레이미드페닐)메탄, 2,2-비스-{4-(4-말레이미드페녹시)-페닐}프로판, 비스(3-에틸-5-메틸-4-말레이미드페닐)메탄, 및 하기 식 (3) 으로 나타내는 말레이미드 화합물로 이루어지는 군에서 선택되는 적어도 1 종을 포함하는,
[1] ∼ [7] 중 어느 한 항에 기재된 수지 조성물.
[화학식 5]
식 (3) 중, R5 는, 각각 독립적으로, 수소 원자 또는 메틸기를 나타내고, n1 은, 1 이상의 정수를 나타낸다.
[9]
상기 빗형 그래프트 폴리머 (D) 의 중량 평균 분자량 Mw 가, 1.0 × 105 ∼ 3.5 × 105 인,
[1] ∼ [8] 중 어느 한 항에 기재된 수지 조성물.
[10]
시안산에스테르 화합물 (G) 를 추가로 함유하는,
[1] ∼ [9] 중 어느 하나에 기재된 수지 조성물.
[11]
상기 시안산에스테르 화합물 (G) 가, 하기 식 (4) 및/또는 (5) 로 나타내는 화합물을 포함하는,
[10] 에 기재된 수지 조성물.
[화학식 6]
식 (4) 중, R6 은, 각각 독립적으로, 수소 원자 또는 메틸기를 나타내고, n2 는, 1 이상의 정수를 나타낸다.
[화학식 7]
식 (5) 중, R7 은, 각각 독립적으로, 수소 원자 또는 메틸기를 나타내고, n3 은, 1 이상의 정수를 나타낸다.
[12]
상기 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 이외의 에폭시 화합물 (H) 를 추가로 함유하는,
[1] ∼ [11] 중 어느 하나에 기재된 수지 조성물.
[13]
충전재 (I) 를 추가로 함유하는,
[1] ∼ [12] 중 어느 하나에 기재된 수지 조성물.
[14]
상기 충전재 (I) 의 수지 조성물에 있어서의 함유량이, 수지 고형분 100 질량부에 대하여 100 ∼ 700 질량부인,
[13] 에 기재된 수지 조성물.
[15]
기재와,
그 기재에 함침 또는 도포된, [1] ∼ [14] 중 어느 하나에 기재된 수지 조성물,
을 갖는 프리프레그.
[16]
상기 기재가, E 유리 섬유, D 유리 섬유, S 유리 섬유, T 유리 섬유, Q 유리 섬유, L 유리 섬유, NE 유리 섬유, HME 유리 섬유, 및 유기 섬유로 이루어지는 군에서 선택되는 1 종 이상의 섬유로 구성된 것인,
[15] 에 기재된 프리프레그.
[17]
적어도 1 매 이상 적층된 [15] 또는 [16] 에 기재된 프리프레그를 갖는,
적층판.
[18]
적어도 1 매 이상 적층된 [15] 또는 [16] 에 기재된 프리프레그와,
그 프리프레그의 편면 또는 양면에 배치된 금속박,
을 갖는 금속박 피복 적층판.
[19]
절연층과,
그 절연층의 표면에 형성된 도체층,
을 갖고,
상기 절연층이, [1] ∼ [14] 중 어느 하나에 기재된 수지 조성물을 포함하는,
프린트 배선판.
[20]
적어도 1 매 이상 적층된 [15] 또는 [16] 에 기재된 프리프레그로 형성된 제 1 절연층, 및, 상기 제 1 절연층의 편면 방향으로 적어도 1 매 이상 적층된 [15] 또는 [16] 에 기재된 프리프레그로 형성된 제 2 절연층으로 이루어지는 복수의 절연층과,
상기 복수의 절연층의 각각의 사이에 배치된 제 1 도체층, 및, 상기 복수의 절연층의 최외층의 표면에 배치된 제 2 도체층으로 이루어지는 복수의 도체층,
을 갖는 다층 프린트 배선판.
본 발명에 의하면, 높은 유리 전이 온도를 갖거나 (고 Tg), 명확한 유리 전이 온도를 갖지 않고 (Tg 레스), 또한, 프린트 배선판, 특히, 다층 코어리스 기판의 휨을 충분히 저감 (저휨을 달성) 할 수 있는 수지 조성물, 그리고, 그 수지 조성물을 사용한, 프리프레그, 적층판, 금속박 피복 적층판, 프린트 배선판, 및 다층 프린트 배선판을 제공할 수 있다.
도 1 은, 다층 코어리스 기판의 패널을 제조하는 순서의 일례를 나타내는 프로세스 플로우도이다 (단, 다층 코어리스 기판의 제조 방법은 이것에 한정되지 않는다. 이하의 각 도에 있어서 동일하다.).
도 2 는, 다층 코어리스 기판의 패널을 제조하는 순서의 일례를 나타내는 프로세스 플로우도이다.
도 3 은, 다층 코어리스 기판의 패널을 제조하는 순서의 일례를 나타내는 프로세스 플로우도이다.
도 4 는, 다층 코어리스 기판의 패널을 제조하는 순서의 일례를 나타내는 프로세스 플로우도이다.
도 5 는, 다층 코어리스 기판의 패널을 제조하는 순서의 일례를 나타내는 프로세스 플로우도이다.
도 6 은, 다층 코어리스 기판의 패널을 제조하는 순서의 일례를 나타내는 프로세스 플로우도이다.
도 7 은, 다층 코어리스 기판의 패널을 제조하는 순서의 일례를 나타내는 프로세스 플로우도이다.
도 8 은, 다층 코어리스 기판의 패널을 제조하는 순서의 일례를 나타내는 프로세스 플로우도이다.
도 9 는, 다층 코어리스 기판의 패널의 일례의 구성을 나타내는 부분 단면도이다.
도 2 는, 다층 코어리스 기판의 패널을 제조하는 순서의 일례를 나타내는 프로세스 플로우도이다.
도 3 은, 다층 코어리스 기판의 패널을 제조하는 순서의 일례를 나타내는 프로세스 플로우도이다.
도 4 는, 다층 코어리스 기판의 패널을 제조하는 순서의 일례를 나타내는 프로세스 플로우도이다.
도 5 는, 다층 코어리스 기판의 패널을 제조하는 순서의 일례를 나타내는 프로세스 플로우도이다.
도 6 은, 다층 코어리스 기판의 패널을 제조하는 순서의 일례를 나타내는 프로세스 플로우도이다.
도 7 은, 다층 코어리스 기판의 패널을 제조하는 순서의 일례를 나타내는 프로세스 플로우도이다.
도 8 은, 다층 코어리스 기판의 패널을 제조하는 순서의 일례를 나타내는 프로세스 플로우도이다.
도 9 는, 다층 코어리스 기판의 패널의 일례의 구성을 나타내는 부분 단면도이다.
이하, 본 발명을 실시하기 위한 형태 (이하 「본 실시형태」 라고 한다.) 에 대해서 상세하게 설명하는데, 본 발명은 이것에 한정되는 것이 아니라, 그 요지를 일탈하지 않는 범위에서 다양한 변형이 가능하다. 또한, 본 실시형태에 있어서, 「수지 고형분」 이란, 특별히 언급이 없는 한, 수지 조성물에 있어서의, 용제, 및 충전재를 제외한 성분을 말하고, 「수지 고형분 100 질량부」 란, 수지 조성물에 있어서의 용제, 및 충전재를 제외한 성분의 합계가 100 질량부인 것을 말하는 것으로 한다.
[수지 조성물]
본 실시형태의 수지 조성물은, 말레이미드 화합물 (A) 와, 알릴기 함유 화합물 (B) 와, 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 및/또는 빗형 그래프트 폴리머 (D) 를 함유하고, 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 또는 빗형 그래프트 폴리머 (D) 의 수지 조성물에 있어서의 함유량이, 수지 고형분 100 질량부에 대하여 5 ∼ 25 질량부의 것이다. 수지 조성물이, 이와 같은 조성을 함유함으로써, 예를 들어, 프리프레그를 경화시킨 경화물에 있어서, 높은 유리 전이 온도를 갖거나 (고 Tg), 명확한 유리 전이 온도를 갖지 않고 (Tg 레스), 또한, 프린트 배선판, 특히, 다층 코어리스 기판의 휨을 충분히 저감 (저휨을 달성) 할 수 있는 경향이 있다.
[말레이미드 화합물 (A)]
말레이미드 화합물 (A) 로는, 분자 중에 1 개 이상의 말레이미드기를 갖는 화합물이면 특별히 한정되지 않지만, 예를 들어, N-페닐말레이미드, N-하이드록시페닐말레이미드, 비스(4-말레이미드페닐)메탄, 2,2-비스{4-(4-말레이미드페녹시)-페닐}프로판, 비스(3,5-디메틸-4-말레이미드페닐)메탄, 비스(3-에틸-5-메틸-4-말레이미드페닐)메탄, 비스(3,5-디에틸-4-말레이미드페닐)메탄, 하기 식 (3) 으로 나타내는 말레이미드 화합물, 이들 말레이미드 화합물의 프리폴리머, 혹은 말레이미드 화합물과 아민 화합물의 프리폴리머를 들 수 있다. 이 중에서도, 비스(4-말레이미드페닐)메탄, 2,2-비스{4-(4-말레이미드페녹시)-페닐}프로판, 비스(3-에틸-5-메틸-4-말레이미드페닐)메탄, 및 하기 식 (3) 으로 나타내는 말레이미드 화합물로 이루어지는 군에서 선택되는 적어도 1 종이 바람직하고, 특히 하기 식 (3) 으로 나타내는 말레이미드 화합물이 바람직하다. 이와 같은 말레이미드 화합물 (A) 를 포함함으로써, 얻어지는 경화물의 열팽창률이 보다 저하되고, 내열성, 유리 전이 온도 (Tg) 가 보다 향상되는 경향이 있다. 말레이미드 화합물 (A) 는, 1 종류를 단독으로 사용해도 되고, 2 종류 이상을 병용해도 된다.
[화학식 8]
여기서, 식 (3) 중, R5 는, 각각 독립적으로, 수소 원자 또는 메틸기를 나타내고, 바람직하게는 수소 원자를 나타낸다. 또, 식 (3) 중, n1 은, 1 이상의 정수를 나타내고, 바람직하게는 10 이하의 정수이고, 보다 바람직하게는 7 이하의 정수이다.
말레이미드 화합물 (A) 의 함유량은, 수지 고형분 100 질량부에 대하여, 바람직하게는 10 ∼ 70 질량부이고, 한층 바람직하게는 20 ∼ 60 질량부이고, 보다 바람직하게는 25 ∼ 55 질량부이고, 더욱 바람직하게는 35 ∼ 55 질량부이고, 특히 바람직하게는 35 ∼ 45 질량부이다. 말레이미드 화합물 (A) 의 함유량이 상기 범위 내임으로써, 얻어지는 경화물의 열팽창률이 보다 저하되고, 내열성이 보다 향상되는 경향이 있다.
[알릴기 함유 화합물 (B)]
알릴기 함유 화합물 (B) 는, 분자 중에 1 개 이상의 알릴기를 갖는 화합물이면 특별히 한정되지 않지만, 알릴기 이외의 반응성 관능기를 추가로 가지고 있어도 된다. 알릴기 이외의 반응성 관능기로는, 특별히 한정되지 않지만, 예를 들어, 시아네이트기 (시안산에스테르), 하이드록실기, 에폭시기, 아민기, 이소시아네이트기, 글리시딜기, 및 인산기를 들 수 있다. 이 중에서도, 시아네이트기 (시안산에스테르), 하이드록실기, 및 에폭시기로 이루어지는 군에서 선택되는 적어도 1 개가 바람직하고, 시아네이트기 (시안산에스테르) 가 보다 바람직하다. 하이드록실기, 시아네이트기 (시안산에스테르), 에폭시기를 가짐으로써, 높은 굽힘 강도 및 굽힘 탄성률, 낮은 유전율, 높은 유리 전이 온도 (Tg) 를 갖고, 열팽창 계수가 낮고, 열전도율이 보다 향상되는 경향이 있다.
알릴기 함유 화합물 (B) 는, 1 종류를 단독으로 사용해도 되고, 2 종류 이상을 병용해도 된다. 2 종류 이상의 알릴기 이외의 반응성 관능기를 갖는 알릴기 함유 화합물 (B) 를 병용하는 경우에는, 알릴기 이외의 반응성 관능기는 동일해도 되고, 상이해도 된다. 이 중에서도, 알릴기 함유 화합물 (B) 가, 반응성 관능기가 시아네이트기 (시안산에스테르) 인 알릴기 함유 화합물과, 반응성 관능기가 에폭시기인 알릴기 함유 화합물을 포함하는 것이 바람직하다. 이와 같은 알릴기 함유 화합물 (B) 를 병용함으로써, 굽힘 강도, 굽힘 탄성률, 유리 전이 온도 (Tg), 열전도율이 보다 향상되는 경향이 있다.
상기 서술한 중에서, 알릴기 함유 화합물 (B) 로서, 알릴기 이외의 반응성 관능기를 갖는 알릴기 함유 화합물 및/또는 후술하는 알케닐 치환 나디이미드 화합물 (F) 를 사용하는 것이 바람직하다. 이와 같은 알릴기 함유 화합물 (B) 를 사용함으로써, 유리 전이 온도 (Tg), 열팽창률, 열전도율이 향상되는 경향이 있다.
또, 알릴기 함유 화합물 (B) 로서, 후술하는 알릴페놀 유도체 (E) 및/또는 알케닐 치환 나디이미드 화합물 (F) 를 사용하는 것이 특히 바람직하다. 이와 같은 알릴기 함유 화합물 (B) 를 사용함으로써, 유리 전이 온도 (Tg), 열팽창률, 열전도율이 보다 향상되는 경향이 있다
알릴기 함유 화합물 (B) 의 함유량은, 수지 고형분 100 질량부에 대하여, 바람직하게는 1 ∼ 90 질량부이고, 한층 바람직하게는 10 ∼ 80 질량부이고, 보다 바람직하게는 20 ∼ 75 질량부이고, 더욱 바람직하게는 25 ∼ 40 질량부이고, 특히 바람직하게는 25 ∼ 35 질량부이다. 알릴기 함유 화합물 (B) 의 함유량이 상기 범위 내임으로써, 얻어지는 경화물의 유연성, 굽힘 강도, 굽힘 탄성률, 유리 전이 온도 (Tg), 열팽창률, 열전도율, 및 동박 필 강도가 보다 향상되는 경향이 있다.
(알릴페놀 유도체 (E))
알릴페놀 유도체 (E) 로는, 방향 고리에 알릴기와 페놀성 수산기가 직접 결합한 화합물 및 그 유도체이면, 특별히 한정되지 않지만, 예를 들어, 방향 고리의 수소 원자가 알릴기로 치환된 비스페놀, 방향 고리의 수소 원자가 알릴기로 치환되고, 페놀성 수산기가, 상기 서술한 알릴기 이외의 반응성 관능기 중, 하이드록실기 이외의 반응성 관능기로 변성된 변성 비스페놀 화합물을 들 수 있고, 보다 구체적으로는, 하기 식 (2) 로 나타내는 화합물을 들 수 있고, 더욱 구체적으로는 디알릴 비스페놀 A, 디알릴 비스페놀 A 의 시안산에스테르 화합물, 디알릴 비스페놀 A 형 에폭시를 들 수 있다.
[화학식 9]
식 (2) 중, Ra는, 각각 독립적으로, 알릴기 이외의 반응성 치환기를 나타낸다.
식 (2) 로 나타내는 화합물로는, 특별히 한정되지 않지만, 예를 들어, 하기 식 (2a) 로 나타내는 화합물 및/또는 하기 식 (2b) 로 나타내는 화합물을 들 수 있다. 이와 같은 알릴페놀 유도체 (E) 를 사용함으로써, 굽힘 강도, 굽힘 탄성률, 유리 전이 온도 (Tg), 열팽창률, 열전도율, 동박 필 강도가 보다 향상되는 경향이 있다.
[화학식 10]
[화학식 11]
상기 비스페놀로는, 특별히 한정되지 않지만, 예를 들어, 비스페놀 A, 비스페놀 AP, 비스페놀 AF, 비스페놀 B, 비스페놀 BP, 비스페놀 C, 비스페놀 C, 비스페놀 E, 비스페놀 F, 비스페놀 G, 비스페놀 M, 비스페놀 S, 비스페놀 P, 비스페놀 PH, 비스페놀 TMC, 비스페놀 Z 를 들 수 있다. 이 중에서도, 비스페놀 A 가 바람직하다.
알릴페놀 유도체 (E) 1 분자 중의 알릴기의 기 수는, 바람직하게는 1 ∼ 5 이고, 보다 바람직하게는 2 ∼ 4 이고, 더욱 바람직하게는 2 이다. 알릴페놀 유도체 (E) 1 분자 중의 알릴기의 기 수가 상기 범위 내임으로써, 굽힘 강도, 굽힘 탄성률, 동박 필 강도, 유리 전이 온도 (Tg) 가 보다 향상되고, 열팽창 계수가 낮고, 열전도율이 우수한 경향이 있다.
알릴페놀 유도체 (E) 1 분자 중의 알릴기 이외의 반응성 관능기 수는, 바람직하게는 1 ∼ 5 이고, 보다 바람직하게는 2 ∼ 4 이고, 더욱 바람직하게는 2 이다. 알릴페놀 유도체 (E) 1 분자 중의 반응성 관능기 수가 상기 범위 내임으로써, 굽힘 강도, 굽힘 탄성률, 동박 필 강도, 유리 전이 온도 (Tg) 가 보다 향상되고, 열팽창 계수가 낮고, 열전도율이 우수한 경향이 있다.
알릴페놀 유도체 (E) 의 함유량의 적합한 범위는, 상기 서술한 알릴기 함유 화합물 (B) 의 함유량에 준한다.
(알케닐 치환 나디이미드 화합물 (F))
알케닐 치환 나디이미드 화합물 (F) 는, 분자 중에 1 개 이상의 알케닐 치환 나디이미드기를 갖는 화합물이면 특별히 한정되지 않는다. 이 중에서도, 하기 식 (6) 으로 나타내는 화합물이 바람직하다. 이와 같은 알케닐 치환 나디이미드 화합물 (F) 를 사용함으로써, 얻어지는 경화물의 열팽창률이 보다 저하되고, 내열성이 보다 향상되는 경향이 있다.
[화학식 12]
식 (6) 중, R1 은, 각각 독립적으로, 수소 원자, 또는 탄소수 1 ∼ 6 의 알킬기를 나타내고, R2 는, 탄소수 1 ∼ 6 의 알킬렌기, 페닐렌기, 비페닐렌기, 나프틸렌기, 또는 하기 식 (7) 혹은 (8) 로 나타내는 기를 나타낸다.
[화학식 13]
식 (7) 중, R3 은, 메틸렌기, 이소프로필리덴기, 또는, CO, O, S, 혹은 SO2 로 나타내는 치환기를 나타낸다.
[화학식 14]
식 (8) 중, R4 는, 각각 독립적으로, 탄소수 1 ∼ 4 의 알킬렌기, 또는 탄소수 5 ∼ 8 의 시클로알킬렌기를 나타낸다.
또, 알케닐 치환 나디이미드 화합물 (F) 가, 하기 식 (9) 및/또는 (10) 으로 나타내는 화합물이면 더욱 바람직하다. 이와 같은 알케닐 치환 나디이미드 화합물 (F) 를 사용함으로써, 얻어지는 경화물의 열팽창률이 보다 저하되고, 내열성이 보다 향상되는 경향이 있다.
[화학식 15]
[화학식 16]
그 외, 알케닐 치환 나디이미드 화합물 (F) 는, 시판되는 것을 사용할 수도 있다. 시판되고 있는 것으로는, 특별히 한정되지 않지만, 예를 들어, BANI-M (마루젠 석유 화학 (주) 제조, 식 (9) 로 나타내는 화합물), BANI-X (마루젠 석유 화학 (주) 제조, 식 (10) 으로 나타내는 화합물) 등을 들 수 있다. 이들은 1 종 또는 2 종 이상을 조합하여 사용해도 된다.
알케닐 치환 나디이미드 화합물 (F) 의 함유량은, 수지 고형분 100 질량부에 대하여, 바람직하게는 20 ∼ 50 질량부이고, 더욱 바람직하게는 20 ∼ 40 질량부이고, 특히 바람직하게는 25 ∼ 35 질량부이다. 또, 보다 한층 바람직하게는, 알릴페놀 유도체 (E) 와 알케닐 치환 나디이미드 화합물 (F) 의 합계 함유량이, 수지 고형분 100 질량부에 대하여, 바람직하게는 25 ∼ 45 질량부이고, 한층 바람직하게는 30 ∼ 45 질량부이다. 알케닐 치환 나디이미드 화합물 (F) 의 함유량이 상기 범위 내임으로써, 얻어지는 경화물의 열팽창률이 보다 저하되고, 내열성이 보다 향상되는 경향이 있다.
[비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C)]
비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 는, 분자 중에, 1 개 이상의 비스페놀 A 형 구조 단위와, 1 개 이상의 탄화수소계 구조 단위를 갖는 화합물이면 특별히 한정되지 않는다. 이 중에서도, 하기 식 (1) 로 나타내는 화합물이 바람직하다. 이와 같은 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 를 사용함으로써, 얻어지는 경화물의 가열시의 저장 탄성률 E' 가 휨 억제에 적합한 값이 되는 경향이 있다.
[화학식 17]
여기서, 식 (1) 중, R1 및 R2 는, 각각 독립적으로, 수소 원자, 또는 메틸기를 나타내고, R3 ∼ R6 은, 각각 독립적으로, 수소 원자, 메틸기, 염소 원자, 또는 브롬 원자를 나타내고, X 는, 에틸렌옥시에틸기, 디(에틸렌옥시)에틸기, 트리(에틸렌옥시)에틸기, 프로필렌옥시프로필기, 디(프로필렌옥시)프로필기, 트리(프로필렌옥시)프로필기, 또는 탄소수 2 ∼ 15 의 알킬렌기를 나타내고, n 은, 자연수를 나타낸다.
상기 서술한 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 는, 시판되는 것을 사용할 수도 있다. 시판되고 있는 것으로는, 특별히 한정되지 않지만, 예를 들어, EPICLON EXA-4850-150 (DIC (주) 제조, 식 (1) 로 나타내는 구조를 갖는 화합물), EPICLON EXA-4816 (DIC (주) 제조, 식 (1) 에 있어서의 X 가 에틸렌기인 화합물) 등을 들 수 있다. 이들은 1 종 또는 2 종 이상을 조합하여 사용해도 된다.
비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 의 함유량은, 상기 서술한 바와 같이, 수지 고형분 100 질량부에 대하여, 3 ∼ 25 질량부이고, 바람직하게는 5 ∼ 25 질량부이고, 한층 바람직하게는 5 ∼ 20 질량부이고, 보다 바람직하게는 10 ∼ 20 질량부이다. 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 의 함유량이 상기 범위 내임으로써, 얻어지는 경화물의 가열시의 저장 탄성률 E' 가 휨 억제에 적합한 값이 되는 경향이 있다.
또, 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 의 에폭시 당량은, 바람직하게는 400 g/eq. 이상이고, 보다 바람직하게는 400 ∼ 800 g/eq. 이고, 더욱 바람직하게는 400 ∼ 500 g/eq. 이다. 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 의 에폭시 당량이 상기 범위 내임으로써, 얻어지는 경화물의 가열시의 저장 탄성률 E' 가 휨 억제에 적합한 값이 되는 경향이 있다.
[빗형 그래프트 폴리머 (D)]
빗형 그래프트 폴리머 (D) 로는, (메트)아크릴계 모노머 유래의 구성 단위를 갖는 고분자 주사슬 (줄기 부분;즉 (메트)아크릴 주사슬) 에, 측사슬 (가지 부분) 로서 1 개 이상의 실리콘 모노머 유래의 구성 단위가 그래프트 중합된 것 (실리콘 변성 (메트)아크릴 수지 화합물) 이면 특별히 한정되지 않고, 또, (메트)아크릴 주사슬에 관능기를 가지고 있어도 된다. 이 관능기로는, 특별히 제한되지 않고, 예를 들어, OH 기, 카르복실기 등을 들 수 있고, 이들 중에서도, 카르복실기가 바람직하다.
또, 상기 (메트)아크릴계 모노머로는, 특별히 한정되지 않지만, 예를 들어, 아크릴산, 메타크릴산, 및 그 유도체 등을 들 수 있다. 또한, 상기 실리콘 모노머로는, 특별히 한정되지 않지만, 예를 들어, 폴리디메틸실록산의 실록산 골격의 편말단에 반응성 관능기를 갖는 모노머 등을 들 수 있다.
이와 같은 빗형 그래프트 폴리머 (D) 를 사용함으로써, 얻어지는 경화물의 가열시의 저장 탄성률 E' 가 휨 억제에 적합한 값이 되는 경향이 있다.
빗형 그래프트 폴리머 (D) 의 중량 평균 분자량 Mw 는, 바람직하게는 1.0 × 105 ∼ 3.5 × 105 이고, 보다 바람직하게는 1.0 × 105 ∼ 2.0 × 105 이고, 더욱 바람직하게는 1.0 × 105 ∼ 1.5 × 105 이다. 빗형 그래프트 폴리머 (D) 의 중량 평균 분자량 Mw 가 상기 범위 내임으로써, 얻어지는 경화물이 블리드 아웃하는 경우가 없고, 본 발명에 의한 작용 효과를 확실하게 발현시키기 쉬워진다. 중량 평균 분자량 Mw 의 측정 방법으로는, 특별히 한정되지 않지만, 예를 들어, 본 명세서의 실시예에 서술한 방법으로 측정할 수 있다.
또, 빗형 그래프트 폴리머 (D) 의 제조 방법으로는, 특별히 한정되지 않고, 예를 들어, 아크릴계 수지와 편말단 실리콘 오일을, 유기 용매 중에서, 중합 개시제 존재하 라디칼 중합시켜 그래프트화하는 방법을 들 수 있다. 또한, 빗형 그래프트 폴리머 (D) 로는, 시판품을 사용할 수 있으며, 시판품으로는, 예를 들어, 토아 합성 (주) 의 사이맥 (등록상표) 시리즈의 US-350, 및 US-380 등 (모두 상품명) 을 들 수 있다. 이들은 1 종 또는 2 종 이상을 조합하여 사용해도 된다.
빗형 그래프트 폴리머 (D) 의 함유량은, 상기 서술한 바와 같이, 수지 고형분 100 질량부에 대하여, 3 ∼ 25 질량부이고, 바람직하게는 5 ∼ 25 질량부이고, 보다 바람직하게는 5 ∼ 20 질량부이고, 특히 바람직하게는 10 ∼ 20 질량부이다. 빗형 그래프트 폴리머 (D) 의 함유량이 상기 범위 내임으로써, 얻어지는 경화물의 가열시의 저장 탄성률 E' 가 휨 억제에 적합한 값이 되는 경향이 있다.
또, 보다 적합하게는, 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 와 빗형 그래프트 폴리머 (D) 의 수지 조성물에 있어서의 함유량의 합계량이, 수지 고형분 100 질량부에 대하여, 바람직하게는 3 ∼ 25 질량부이고, 한층 바람직하게는 5 ∼ 25 질량부이고, 보다 바람직하게는 5 ∼ 20 질량부이고, 더욱 바람직하게는 10 ∼ 20 질량부이다. 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 와 빗형 그래프트 폴리머 (D) 의 수지 조성물에 있어서의 함유량의 합계량이 상기 범위 내임으로써, 얻어지는 경화물의 가열시의 저장 탄성률 E' 가 휨 억제에 의해 적합한 값이 되는 경향이 있다.
[시안산에스테르 화합물 (G)]
본 실시형태의 수지 조성물은, 시안산에스테르 화합물 (G) 를 추가로 함유해도 된다. 시안산에스테르 화합물 (G) 로는, 상기 서술한 알릴페놀 유도체 (E) 이외의 시안산에스테르 화합물이면 특별히 한정되지 않지만, 예를 들어, 하기 식 (4) 로 나타내는 나프톨아르알킬형 시안산에스테르, 하기 식 (5) 로 나타내는 노볼락형 시안산에스테르, 비페닐아르알킬형 시안산에스테르, 비스(3,5-디메틸4-시아나토페닐)메탄, 비스(4-시아나토페닐)메탄, 1,3-디시아나토벤젠, 1,4-디시아나토벤젠, 1,3,5-트리시아나토벤젠, 1,3-디시아나토나프탈렌, 1,4-디시아나토나프탈렌, 1,6-디시아나토나프탈렌, 1,8-디시아나토나프탈렌, 2,6-디시아나토나프탈렌, 2,7-디시아나토나프탈렌, 1,3,6-트리시아나토나프탈렌, 4,4'-디시아나토비페닐, 비스(4-시아나토페닐)에테르, 비스(4-시아나토페닐)티오에테르, 비스(4-시아나토페닐)술폰, 및 2,2'-비스(4-시아나토페닐)프로판;이들 시안산에스테르의 프리폴리머 등을 들 수 있다. 이들 시안산에스테르 화합물 (G) 는, 1 종 단독으로, 또는 2 종 이상을 조합하여 사용해도 된다.
[화학식 18]
식 (4) 중, R6 은, 각각 독립적으로, 수소 원자 또는 메틸기를 나타내고, 이 중에서도 수소 원자가 바람직하다. 또, 식 (4) 중, n2 는, 1 이상의 정수를 나타낸다. n2 의 상한값은, 통상적으로는 10 이며, 바람직하게는 6 이다.
[화학식 19]
식 (5) 중, R7 은, 각각 독립적으로, 수소 원자 또는 메틸기를 나타내고, 이 중에서도 수소 원자가 바람직하다. 또, 식 (5) 중, n3 은, 1 이상의 정수를 나타낸다. n3 의 상한값은, 통상적으로는 10 이며, 바람직하게는 7 이다.
이들 중에서도, 시안산에스테르 화합물 (G) 가, 식 (4) 로 나타내는 나프톨아르알킬형 시안산에스테르, 식 (5) 로 나타내는 노볼락형 시안산에스테르, 및 비페닐아르알킬형 시안산에스테르로 이루어지는 군에서 선택되는 1 종 이상을 포함하는 것이 바람직하고, 식 (4) 로 나타내는 나프톨아르알킬형 시안산에스테르 및 식 (5) 로 나타내는 노볼락형 시안산에스테르로 이루어지는 군에서 선택되는 1 종 이상을 포함하는 것이 보다 바람직하다. 이와 같은 시안산에스테르 화합물 (G) 를 사용함으로써, 난연성이 보다 우수하고, 경화성이 보다 높고, 또한 열팽창 계수가 보다 낮은 경화물이 얻어지는 경향이 있다.
이들 시안산에스테르 화합물 (G) 의 제조 방법으로는, 특별히 한정되지 않고, 시안산에스테르 화합물의 합성 방법으로서 공지된 방법을 이용할 수 있다. 공지된 방법으로는, 특별히 한정되지 않지만, 예를 들어, 페놀 수지와 할로겐화 시안을 불활성 유기 용매 중에서, 염기성 화합물 존재하 반응시키는 방법, 페놀 수지와 염기성 화합물의 염을, 물을 함유하는 용액 중에서 형성시키고, 그 후, 얻어진 염과 할로겐화 시안을 2 상계 계면 반응시키는 방법을 들 수 있다.
이들 시안산에스테르 화합물 (G) 의 원료가 되는 페놀 수지로는, 특별히 한정되지 않지만, 예를 들어, 하기 식 (11) 로 나타내는 나프톨아르알킬형 페놀 수지, 노볼락형 페놀 수지, 비페닐아르알킬형 페놀 수지를 들 수 있다.
[화학식 20]
식 (11) 중, R8 은, 각각 독립적으로, 수소 원자 또는 메틸기를 나타내고, 이 중에서도 수소 원자가 바람직하다. 또, 식 (11) 중, n4 는, 1 이상의 정수를 나타낸다. n4 의 상한값은, 통상적으로는 10 이며, 바람직하게는 6 이다.
식 (11) 로 나타내는 나프톨아르알킬형 페놀 수지는, 나프톨아르알킬 수지와 시안산을 축합시켜 얻을 수 있다. 나프톨아르알킬형 페놀 수지로는, 특별히 한정되지 않지만, 예를 들어, α-나프톨 및 β-나프톨 등의 나프톨류와, p-자일릴렌글리콜, α,α'-디메톡시-p-자일렌, 및 1,4-디(2-하이드록시-2-프로필)벤젠 등의 벤젠류의 반응에 의해 얻어지는 것을 들 수 있다. 나프톨아르알킬형 시안산에스테르는, 상기와 같이 하여 얻어지는 나프톨아르알킬 수지와 시안산을 축합시켜 얻어지는 것에서 선택할 수 있다.
시안산에스테르 화합물 (G) 의 함유량은, 수지 고형분 100 질량부에 대하여, 바람직하게는 0 ∼ 10 질량부이고, 보다 바람직하게는 0 ∼ 5 질량부이다. 시안산에스테르 화합물의 함유량이 상기 범위 내임으로써, 얻어지는 경화물의 내열성과 내약품성이 보다 향상되는 경향이 있다.
[에폭시 화합물 (H)]
본 실시형태의 수지 조성물은, 상기 서술한 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 이외의 에폭시 화합물 (H) 를 추가로 함유해도 된다. 이러한 에폭시 화합물 (H) 로는, 1 분자 중에 2 개 이상의 에폭시기를 갖는 화합물이면 특별히 한정되지 않지만, 예를 들어, 비스페놀 A 형 에폭시 수지, 비스페놀 E 형 에폭시 수지, 비스페놀 F 형 에폭시 수지, 비스페놀 S 형 에폭시 수지, 페놀 노볼락형 에폭시 수지, 비스페놀 A 노볼락형 에폭시 수지, 크레졸 노볼락형 에폭시 수지, 비페닐형 에폭시 수지, 나프탈렌형 에폭시 수지, 안트라센형 에폭시 수지, 3 관능 페놀형 에폭시 수지, 4 관능 페놀형 에폭시 수지, 글리시딜에스테르형 에폭시 수지, 페놀아르알킬형 에폭시 수지, 비페닐아르알킬형 에폭시 수지, 아르알킬 노볼락형 에폭시 수지, 나프톨아르알킬형 에폭시 수지, 디시클로펜타디엔형 에폭시 수지, 폴리올형 에폭시 수지, 이소시아누레이트 고리 함유 에폭시 수지, 혹은 이들의 할로겐화물을 들 수 있다. 또한, 알릴기 함유 화합물 (B) 가 에폭시기를 갖는 경우, 에폭시 화합물 (H) 는, 에폭시기를 갖는 알릴기 함유 화합물 (B) 이외의 것이다.
에폭시 화합물 (H) 의 함유량은, 수지 고형분 100 질량부에 대하여, 바람직하게는 0 ∼ 30 질량부이고, 보다 바람직하게는 0 ∼ 10 질량부이다. 에폭시 화합물 (H) 의 함유량이 상기 범위 내임으로써, 얻어지는 경화물의 유연성, 동박 필 강도, 내약품성, 및 내디스미어성이 보다 향상되는 경향이 있다.
[충전재 (I)]
본 실시형태의 수지 조성물은, 충전재 (I) 를 추가로 함유해도 된다. 충전재 (I) 로는, 특별히 한정되지 않지만, 예를 들어, 무기 충전재 및 유기 충전재를 들 수 있고, 양자 중 무기 충전재를 함유하고 있는 것이 바람직하고, 유기 충전재는 무기 충전재와 함께 사용하는 것 적합하다. 무기 충전재로는, 특별히 한정되지 않지만, 예를 들어, 천연 실리카, 용융 실리카, 합성 실리카, 아모르퍼스 실리카, 아에로질, 중공 실리카 등의 실리카류;화이트 카본 등의 규소 화합물;티탄 화이트, 산화아연, 산화마그네슘, 산화지르코늄 등의 금속 산화물;질화붕소, 응집 질화붕소, 질화규소, 질화알루미늄 등의 금속 질화물;황산바륨 등의 금속 황산화물;수산화알루미늄, 수산화알루미늄 가열 처리품 (수산화알루미늄을 가열 처리하여, 결정수의 일부를 줄인 것), 베마이트, 수산화마그네슘 등의 금속 수화물;산화몰리브덴, 몰리브덴산아연 등의 몰리브덴 화합물;붕산아연, 주석산아연 등의 아연 화합물;알루미나, 클레이, 카올린, 탤크, 소성 클레이, 소성 카올린, 소성 탤크, 마이카, E-유리, A-유리, NE-유리, C-유리, L-유리, D-유리, S-유리, M-유리 G20, 유리 단섬유 (E 유리, T 유리, D 유리, S 유리, Q 유리 등의 유리 미세 분말류를 포함한다.), 중공 유리, 구상 (球狀) 유리 등을 들 수 있다. 또, 유기 충전재로는, 특별히 한정되지 않지만, 예를 들어, 스티렌형 파우더, 부타디엔형 파우더, 아크릴형 파우더 등의 고무 파우더;코어 쉘형 고무 파우더;실리콘 레진 파우더;실리콘 고무 파우더;실리콘 복합 파우더 등을 들 수 있다. 충전재 (I) 는, 1 종을 단독으로 사용해도 되고, 2 종 이상을 병용해도 된다.
이 중에서도, 무기 충전재인, 실리카, 알루미나, 산화마그네슘, 수산화알루미늄, 베마이트, 질화붕소, 응집 질화붕소, 질화규소, 및 질화알루미늄으로 이루어지는 군에서 선택되는 적어도 1 종을 포함하는 것이 바람직하고, 실리카, 알루미나, 및 베마이트로 이루어지는 군에서 선택되는 적어도 1 종을 포함하는 것이 보다 바람직하다. 이와 같은 충전재 (I) 를 사용함으로써, 얻어지는 경화물의 고강성화, 저휨화가 보다 향상되는 경향이 있다.
충전재 (I) (특히 무기 충전재) 의 함유량은, 수지 고형분 100 질량부에 대하여, 바람직하게는 100 ∼ 700 질량부이고, 보다 바람직하게는 100 ∼ 450 질량부이고, 더욱 바람직하게는 120 ∼ 250 질량부이다. 충전재 (I) 의 함유량이 상기 범위 내임으로써, 얻어지는 경화물의 고강성화, 저휨화가 보다 한층 향상되는 경향이 있다.
[실란 커플링제 및 습윤 분산제]
본 실시형태의 수지 조성물은, 실란 커플링제나 습윤 분산제를 추가로 함유해도 된다. 실란 커플링제나 습윤 분산제를 포함함으로써, 상기 충전재 (I) 의 분산성, 수지 성분, 충전재 (I), 및 후술하는 기재의 접착 강도가 보다 향상되는 경향이 있다.
실란 커플링제로는, 일반적으로 무기물의 표면 처리에 사용되고 있는 실란 커플링제이면, 특별히 한정되지 않지만, 예를 들어, γ-아미노프로필트리에톡시실란, N-β-(아미노에틸)-γ-아미노프로필트리메톡시실란 등의 아미노실란계 화합물;γ-글리시독시프로필트리메톡시실란 등의 에폭시실란계 화합물;γ-아크릴옥시프로필트리메톡시실란 등의 아크릴실란계 화합물;N-β-(N-비닐벤질아미노에틸)-γ-아미노프로필트리메톡시실란염산염 등의 카티오닉 실란계 화합물;페닐실란계 화합물 등을 들 수 있다. 실란 커플링제는, 1 종을 단독으로 사용해도 되고, 2 종 이상을 병용해도 된다.
습윤 분산제로는, 도료용으로 사용되고 있는 분산 안정제이면, 특별히 한정되지 않지만, 예를 들어, 빅케미·재팬 (주) 제조의 DISPER BYK-110, 111, 118, 180, 161, BYK-W996, W9010, W903 등을 들 수 있다.
[그 밖의 수지 등]
본 실시형태의 수지 조성물은, 필요에 따라, 상기 서술한 알릴기 함유 화합물 (B) 이외의, 알릴기 함유 화합물 (이하 「그 밖의 알릴기 함유 화합물」 이라고도 한다), 페놀 수지, 옥세탄 수지, 벤조옥사진 화합물, 및 중합 가능한 불포화기를 갖는 화합물로 이루어지는 군에서 선택되는 1 종 또는 2 종 이상을 추가로 함유해도 된다. 이와 같은 그 밖의 수지 등을 포함함으로써, 얻어지는 경화물의 동박 필 강도, 굽힘 강도, 및 굽힘 탄성률 등이 보다 향상되는 경향이 있다.
[그 밖의 알릴기 함유 화합물]
그 밖의 알릴기 함유 화합물로는, 특별히 한정되지 않지만, 예를 들어, 알릴 클로라이드, 아세트산알릴, 알릴에테르, 프로필렌, 트리알릴시아누레이트, 트리알릴이소시아누레이트, 프탈산디알릴, 이소프탈산디알릴, 말레산디알릴 등을 들 수 있다.
그 밖의 알릴기 함유 화합물의 함유량은, 수지 고형분 100 질량부에 대하여, 바람직하게는 0 ∼ 50 질량부이고, 한층 바람직하게는 10 ∼ 45 질량부이고, 보다 바람직하게는 15 ∼ 45 질량부이고, 더욱 바람직하게는 20 ∼ 35 질량부이다. 그 밖의 알릴기 함유 화합물의 함유량이 상기 범위 내임으로써, 얻어지는 경화물의 굽힘 강도, 굽힘 탄성률, 내열성, 내약품성이 보다 향상되는 경향이 있다.
[페놀 수지]
페놀 수지로는, 1 분자 중에 2 개 이상의 하이드록시기를 갖는 페놀 수지이면, 일반적으로 공지된 것을 사용할 수 있으며, 그 종류는 특별히 한정되지 않다. 그 구체예로는, 비스페놀 A 형 페놀 수지, 비스페놀 E 형 페놀 수지, 비스페놀 F 형 페놀 수지, 비스페놀 S 형 페놀 수지, 페놀 노볼락 수지, 비스페놀 A 노볼락형 페놀 수지, 글리시딜에스테르형 페놀 수지, 아르알킬 노볼락형 페놀 수지, 비페닐아르알킬형 페놀 수지, 크레졸 노볼락형 페놀 수지, 다관능 페놀 수지, 나프톨 수지, 나프톨 노볼락 수지, 다관능 나프톨 수지, 안트라센형 페놀 수지, 나프탈렌 골격 변성 노볼락형 페놀 수지, 페놀아르알킬형 페놀 수지, 나프톨아르알킬형 페놀 수지, 디시클로펜타디엔형 페놀 수지, 비페닐형 페놀 수지, 지환식 페놀 수지, 폴리올형 페놀 수지, 인 함유 페놀 수지, 수산기 함유 실리콘 수지류 등을 들 수 있지만, 특별히 제한되는 것은 아니다. 이들 페놀 수지는, 1 종을 단독으로 또는 2 종 이상을 조합하여 사용할 수 있다. 이와 같은 페놀 수지를 포함함으로써, 얻어지는 경화물의 접착성이나 가요성 등이 보다 우수한 경향이 있다.
페놀 수지의 함유량은, 수지 고형분 100 질량부에 대하여, 바람직하게는 0 ∼ 99 질량부이고, 보다 바람직하게는 1 ∼ 90 질량부이고, 더욱 바람직하게는 3 ∼ 80 질량부이다. 페놀 수지의 함유량이 상기 범위 내임으로써, 얻어지는 경화물의 접착성이나 가요성 등이 보다 한층 우수한 경향이 있다.
[옥세탄 수지]
옥세탄 수지로는, 일반적으로 공지된 것을 사용할 수 있으며, 그 종류는 특별히 한정되지 않는다. 그 구체예로는, 옥세탄, 2-메틸옥세탄, 2,2-디메틸옥세탄, 3-메틸옥세탄, 3,3-디메틸옥세탄 등의 알킬옥세탄, 3-메틸-3-메톡시메틸옥세탄, 3,3'-디(트리플루오로메틸)퍼플루옥세탄, 2-클로로메틸옥세탄, 3,3-비스(클로로메틸)옥세탄, 비페닐형 옥세탄, OXT-101 (토아 합성 제조 상품명), OXT-121 (토아 합성 제조 상품명) 등을 들 수 있다. 이들 옥세탄 수지는, 1 종 또는 2 종 이상을 조합하여 사용할 수 있다. 이와 같은 옥세탄 수지를 포함함으로써, 얻어지는 경화물의 접착성이나 가요성 등이 보다 우수한 경향이 있다.
옥세탄 수지의 함유량은, 수지 고형분 100 질량부에 대하여, 바람직하게는 0 ∼ 99 질량부이고, 보다 바람직하게는 1 ∼ 90 질량부이고, 더욱 바람직하게는 3 ∼ 80 질량부이다. 옥세탄 수지의 함유량이 상기 범위 내임으로써, 얻어지는 경화물의 밀착성이나 가요성 등이 보다 한층 우수한 경향이 있다.
[벤조옥사진 화합물]
벤조옥사진 화합물로는, 1 분자 중에 2 개 이상의 디하이드로벤조옥사진 고리를 갖는 화합물이면, 일반적으로 공지된 것을 사용할 수 있으며, 그 종류는 특별히 한정되지 않는다. 그 구체예로는, 비스페놀 A 형 벤조옥사진 BA-BXZ (코니시 화학 제조 상품명) 비스페놀 F 형 벤조옥사진 BF-BXZ (코니시 화학 제조 상품명), 비스페놀 S 형 벤조옥사진 BS-BXZ (코니시 화학 제조 상품명) 등을 들 수 있다. 이들 벤조옥사진 화합물은, 1 종 또는 2 종 이상 혼합하여 사용할 수 있다. 이와 같은 벤조옥사진 화합물을 포함함으로써, 얻어지는 경화물의 난연성, 내열성, 저흡수성, 저유전 등이 보다 우수한 경향이 있다.
벤조옥사진 화합물의 함유량은, 수지 고형분 100 질량부에 대하여, 바람직하게는 0 ∼ 99 질량부이고, 보다 바람직하게는 1 ∼ 90 질량부이고, 더욱 바람직하게는 3 ∼ 80 질량부이다. 벤조옥사진 화합물의 함유량이 상기 범위 내임으로써, 얻어지는 경화물의 내열성 등이 보다 한층 우수한 경향이 있다.
[중합 가능한 불포화기를 갖는 화합물]
중합 가능한 불포화기를 갖는 화합물로는, 일반적으로 공지된 것을 사용할 수 있으며, 그 종류는 특별히 한정되지 않는다. 그 구체예로는, 에틸렌, 프로필렌, 스티렌, 디비닐벤젠, 디비닐비페닐 등의 비닐 화합물;메틸(메트)아크릴레이트, 2-하이드록시에틸(메트)아크릴레이트, 2-하이드록시프로필(메트)아크릴레이트, 폴리프로필렌글리콜디(메트)아크릴레이트, 트리메틸올프로판디(메트)아크릴레이트, 트리메틸올프로판트리(메트)아크릴레이트, 펜타에리트리톨테트라(메트)아크릴레이트, 디펜타에리트리톨헥사(메트)아크릴레이트 등의 1 가 또는 다가 알코올의 (메트)아크릴레이트류;비스페놀 A 형 에폭시 (메트)아크릴레이트, 비스페놀 F 형 에폭시 (메트)아크릴레이트 등의 에폭시 (메트)아크릴레이트류;벤조시클로부텐 수지;(비스)말레이미드 수지 등을 들 수 있다. 이들 불포화기를 갖는 화합물은, 1 종 또는 2 종 이상 혼합하여 사용할 수 있다. 이와 같은 중합 가능한 불포화기를 갖는 화합물을 포함함으로써, 얻어지는 경화물의 내열성이나 인성 (靭性) 등이 보다 우수한 경향이 있다.
중합 가능한 불포화기를 갖는 화합물의 함유량은, 수지 고형분 100 질량부에 대하여, 바람직하게는 0 ∼ 99 질량부이고, 보다 바람직하게는 1 ∼ 90 질량부이고, 더욱 바람직하게는 3 ∼ 80 질량부이다. 중합 가능한 불포화기를 갖는 화합물의 함유량이 상기 범위 내임으로써, 얻어지는 경화물의 내열성이나 인성 등이 보다 한층 우수한 경향이 있다.
[경화 촉진제]
본 실시형태의 수지 조성물은, 경화 촉진제를 추가로 함유해도 된다. 경화 촉진제로는, 특별히 한정되지 않지만, 예를 들어, 트리페닐이미다졸 등의 이미다졸류;과산화벤조일, 라우로일퍼옥사이드, 아세틸퍼옥사이드, 파라클로로벤조일퍼옥사이드, 디-tert-부틸-디-퍼프탈레이트 등의 유기 과산화물;아조비스니트릴 등의 아조 화합물;N,N-디메틸벤질아민, N,N-디메틸아닐린, N,N-디메틸톨루이딘, N,N-디메틸피리딘, 2-N-에틸아닐리노에탄올, 트리-n-부틸아민, 피리딘, 퀴놀린, N-메틸모르폴린, 트리에탄올아민, 트리에틸렌디아민, 테트라메틸부탄디아민, N-메틸피페리딘 등의 제 3 급 아민류;페놀, 자일레놀, 크레졸, 레조르신, 카테콜 등의 페놀류;나프텐산 납, 스테아르산 납, 나프텐산 아연, 옥틸산 아연, 올레산 주석, 디부틸주석 말레이트, 나프텐산 망간, 나프텐산 코발트, 아세틸아세톤 철 등의 유기 금속염;이들 유기 금속염을 페놀, 비스페놀 등의 수산기 함유 화합물에 용해하여 이루어지는 것;염화주석, 염화아연, 염화알루미늄 등의 무기 금속염;디옥틸주석옥사이드, 그 밖의 알킬주석, 알킬주석옥사이드 등의 유기 주석 화합물 등을 들 수 있다. 이들 중에서도, 트리페닐이미다졸이 경화 반응을 촉진하고, 유리 전이 온도 (Tg), 열팽창률이 우수한 경향이 있기 때문에, 특히 바람직하다.
[용제]
본 실시형태의 수지 조성물은, 용제를 추가로 함유해도 된다. 용제를 포함함으로써, 수지 조성물의 조제시에 있어서의 점도가 내려가고, 핸들링성이 보다 향상됨과 함께 후술하는 기재에 대한 함침성이 보다 향상되는 경향이 있다.
용제로는, 수지 조성물 중의 수지 성분의 일부 또는 전부를 용해 가능한 것이면, 특별히 한정되지 않지만, 예를 들어, 아세톤, 메틸에틸케톤, 메틸셀로솔브 등의 케톤류;톨루엔, 자일렌 등의 방향족 탄화수소류;디메틸포름아미드 등의 아미드류;프로필렌글리콜모노메틸에테르 및 그 아세테이트 등을 들 수 있다. 용제는, 1 종을 단독으로 사용해도 되고, 2 종 이상을 병용해도 된다.
[수지 조성물의 제조 방법]
본 실시형태의 수지 조성물의 제조 방법은, 특별히 한정되지 않지만, 예를 들어, 각 성분을 순차 용제에 배합하고, 충분히 교반하는 방법을 들 수 있다. 이 때, 각 성분을 균일하게 용해 혹은 분산시키기 위해서, 교반, 혼합, 혼련 처리 등의 공지된 처리를 실시할 수 있다. 구체적으로는, 적절한 교반 능력을 갖는 교반기를 부설한 교반조를 사용하여 교반 분산 처리를 실시함으로써, 수지 조성물에 대한 충전재 (I) 의 분산성을 향상시킬 수 있다. 상기의 교반, 혼합, 혼련 처리는, 예를 들어, 볼 밀, 비즈 밀 등의 혼합을 목적으로 한 장치, 또는, 공전 또는 자전형의 혼합 장치 등의 공지된 장치를 사용하여 적절히 실시할 수 있다.
또, 본 실시형태의 수지 조성물의 조제시에 있어서는, 필요에 따라 유기 용제를 사용할 수 있다. 유기 용제의 종류는, 수지 조성물 중의 수지를 용해 가능한 것이면, 특별히 한정되지 않는다. 그 구체예는, 상기 서술한 바와 같다.
[수지 조성물의 특성]
본 실시형태의 수지 조성물은, 그것과 기재를 함유하는 프리프레그를 230 ℃ 및 100 분의 조건으로 열 경화시켜 얻어지는 경화물이, 하기 식 (12) ∼ (16) 으로 나타내는 기계 특성에 관한 물성 파라미터의 수치 범위를 만족하는 것이면 바람직하고, 하기 식 (12A) ∼ (16A) 로 나타내는 기계 특성에 관한 물성 파라미터의 수치 범위를 만족하면 보다 바람직하다.
여기서, 각 식 중, E' 는, 괄호 내에 나타내는 온도에 있어서의 경화물의 저장 탄성률을 나타내고, E''max 는, 30 ℃ 내지 330 ℃ 의 온도 범위에 있어서의 경화물의 손실 탄성률의 최대값을 나타내고, E''min 은, 30 ℃ 내지 330 ℃ 의 온도 범위에 있어서의 경화물의 손실 탄성률의 최소값을 나타낸다 (E'' 는, 경화물의 손실 탄성률을 나타낸다.).
종래, 프린트 배선판의 휨 거동에 관해서는, 프리프레그의 경화물에 있어서, 보다 큰 열시 저장 탄성률, 및보다 높은 탄성률 유지율을 실현할 수 있는 수지 조성물이 유효한 것으로 생각되어 왔지만, 반드시 그렇다고는 할 수 없고, 프리프레그를 230 ℃ 및 100 분의 조건으로 열 경화시켜 얻어지는 경화물의 기계 특성에 관한 물성 파라미터의 수치가 상기 식 (12) ∼ (16) 바람직하게는 식 (12A) ∼ (16A) 의 범위 내임으로써, 유리 전이 온도 (Tg) 를 충분히 높일 수 있고, 또한, 적층판, 금속박 피복 적층판, 프린트 배선판, 특히 다층 코어리스 기판 자체의 휨량을 충분히 저감하는 것이 가능해진다.
바꾸어 말하면, 프리프레그를 230 ℃ 및 100 분의 조건으로 열 경화시켜 얻어지는 경화물의 기계 특성에 관한 물성 파라미터의 수치가 상기 식 (12) ∼ (16) 바람직하게는 식 (12A) ∼ (16A) 의 범위 내임으로써, 적합하게, 높은 유리 전이 온도를 갖거나 (고 Tg), 명확한 유리 전이 온도를 갖지 않고 (Tg 레스), 또한, 프린트 배선판 (특히, 다층 코어리스 기판) 의 휨을 충분히 저감 (저휨을 달성) 하는 것이 가능해진다. 즉, 손실 탄성률에 관련된 식 (15) 및 (16) 바람직하게는 식 (15A) 및 (16A) 를 만족하는 것은, 높은 유리 전이 온도를 갖거나 (고 Tg), 명확한 유리 전이 온도를 갖지 않는 (Tg 레스) 것과 동일한 의미라고 할 수 있는 바, 경화물이 식 (15) 및 (16) 바람직하게는 식 (15A) 및 (16A) 만을 만족하고, 식 (12) ∼ (14) 바람직하게는 식 (12A) ∼ (14A) 를 만족하지 않는 것은, 손실 탄성률 자체는 작아서 잘 신장되지 않기는 하지만, 프린트 배선판으로 했을 때에, 그 잘 신장되지 않는 것이 화가 되어, 저휨을 달성하는 것이 곤란해진다. 이에 반해, 경화물이 식 (15) 및 (16) 바람직하게는 식 (15A) 및 (16A) 뿐만 아니라, 식 (12) ∼ (14) 바람직하게는 식 (12A) ∼ (16A) 도 만족하는 것은, 높은 유리 전이 온도를 갖거나 (고 Tg), 명확한 유리 전이 온도를 갖지 않음 (Tg 레스) 으로써 잘 신장되지 않고, 또한, 프린트 배선판의 저휨을 달성하기 쉬워지는 경향이 있다.
프리프레그의 경화물의 기계 특성 (저장 탄성률 E' 및 손실 탄성률 E'') 의 측정 방법은, 특별히 한정되지 않고, 예를 들어, 이하의 방법에 의해 측정할 수 있다. 즉, 프리프레그 1 매의 상하 양면에, 동박 (3EC-VLP, 미츠이 금속 광업 (주) 제조, 두께 12 ㎛) 을 배치하고, 압력 30 kgf/㎠, 온도 230 ℃ 에서 100 분간의 적층 성형 (열 경화) 을 실시하고, 소정의 절연층 두께의 동박 피복 적층판을 얻는다. 이어서, 얻어진 동박 피복 적층판을 다이싱 소로 사이즈 5.0 ㎜ × 20 ㎜ 로 절단 후, 표면의 동박을 에칭에 의해 제거하고, 측정용 샘플을 얻는다. 이 측정용 샘플을 사용하여, JIS C6481 에 준거하여 동적 점탄성 분석 장치 (TA 인스트루먼트 제조) 로 DMA 법에 의해, 기계 특성 (저장 탄성률 E' 및 손실 탄성률 E'') 을 측정할 수 있다. 이 때, n = 3 의 평균값을 구해도 된다.
[용도]
본 실시형태의 수지 조성물은, 프리프레그, 절연층, 적층판, 금속박 피복 적층판, 프린트 배선판, 또는 다층 프린트 배선판으로서 적합하게 사용할 수 있다. 이하, 프리프레그, 적층판, 금속박 피복 적층판, 및 프린트 배선판 (다층 프린트 배선판을 포함한다.) 에 대해서 설명한다.
[프리프레그]
본 실시형태의 프리프레그는, 기재와, 그 기재에 함침 또는 도포된, 상기 수지 조성물을 갖는다. 프리프레그의 제조 방법은, 통상적인 방법에 따라서 실시할 수 있으며, 특별히 한정되지 않는다. 예를 들어, 본 실시형태에 있어서의 수지 조성물을 기재에 함침 또는 도포시킨 후, 100 ∼ 200 ℃ 의 건조기 중에서 1 ∼ 30 분 가열하는 등 하여 반경화 (B 스테이지화) 시킴으로써, 본 실시형태의 프리프레그를 제조할 수 있다.
본 실시형태의 프리프레그에 있어서의 수지 조성물 (충전재 (I) 를 포함한다.) 의 함유량은, 프리프레그의 총량에 대하여, 바람직하게는 30 ∼ 90 체적% 이고, 보다 바람직하게는 35 ∼ 85 체적% 이며, 더욱 바람직하게는 40 ∼ 80 체적% 이다. 수지 조성물의 함유량이 상기 범위 내임으로써, 성형성이 보다 향상되는 경향이 있다.
기재로는, 특별히 한정되지 않고, 각종 프린트 배선판 재료에 사용되고 있는 공지된 것을, 목적으로 하는 용도나 성능에 따라 적절히 선택하여 사용할 수 있다. 기재로는, 예를 들어, 유리 기재, 유리 이외의 무기 기재, 유기 기재 등을 들 수 있으며, 이들 중에서는, 고강성, 및 가열 치수 안정성의 관점에서, 유리 기재가 특히 바람직하다. 이들 기재를 구성하는 섬유의 구체예로는, 특별히 한정되지 않고, 유리 기재에서는, 예를 들어, E 유리, D 유리, S 유리, T 유리, Q 유리, L 유리, NE 유리, HME 유리로 이루어지는 군에서 선택되는 1 종 이상의 유리의 섬유를 들 수 있다. 또, 유리 이외의 무기 기재에서는, 쿼츠 등의 유리 이외의 무기 섬유를 들 수 있다. 또한, 유기 기재에서는, 폴리파라페닐렌테레프탈라미드 (케블라 (등록상표), 듀퐁 주식회사 제조), 코폴리파라페닐렌·3,4'옥시디페닐렌·테레프탈라미드 (테크노라 (등록상표), 테이진 테크노 프로덕츠 주식회사 제조) 등의 전체 방향족 폴리아미드;2,6-하이드록시나프토산·파라하이드록시벤조산 (벡트란 (등록상표), 주식회사 쿠라레 제조), 젝시온 (등록상표, KB 세이렌 제조) 등의 폴리에스테르;폴리파라페닐렌벤즈옥사졸 (자일론 (등록상표), 토요 방적 주식회사 제조), 폴리이미드 등의 유기 섬유를 들 수 있다. 이들 기재는, 1 종을 단독으로 사용해도 되고, 2 종 이상을 병용해도 된다.
기재의 형상으로는, 특별히 한정되지 않지만, 예를 들어, 직포, 부직포, 로빙, 촙드 스트랜드 매트, 서페이싱 매트 등을 들 수 있다. 직포 짜는 방법으로는, 특별히 한정되지 않지만, 예를 들어, 평직, 사자직 (斜子織), 능직 등이 알려져 있으며, 이들 공지된 것에서 목적으로 하는 용도나 성능에 따라 적절히 선택하여 사용할 수 있다. 또, 이들을 개섬 처리한 것이나 실란 커플링제 등으로 표면 처리한 유리 직포가 적합하게 사용된다. 기재의 두께나 질량은, 특별히 한정되지 않지만, 통상적으로는 0.01 ∼ 0.3 ㎜ 정도의 것이 적합하게 사용된다. 특히, 강도와 흡수성의 관점에서, 기재는, 두께 200 ㎛ 이하, 질량 250 g/㎡ 이하의 유리 직포가 바람직하고, E 유리, S 유리, 및 T 유리의 유리 섬유로 이루어지는 유리 직포가 보다 바람직하다.
[적층판 및 금속박 피복 적층판]
본 실시형태의 적층판은, 적어도 1 매 이상 적층된 본 실시형태의 상기 프리프레그를 갖는 것이다. 또, 본 실시형태의 금속박 피복 적층판은, 본 실시형태의 적층판 (즉 적어도 1 매 이상 적층된 본 실시형태의 상기 프리프레그) 과, 그 적층판의 편면 또는 양면에 배치된 금속박 (도체층) 을 갖는 것이다.
도체층은, 구리나 알루미늄 등의 금속박으로 할 수 있다. 여기서 사용하는 금속박은, 프린트 배선판 재료에 사용되는 것이면, 특별히 한정되지 않지만, 압연 동박이나 전해 동박 등의 공지된 동박이 바람직하다. 또, 도체층의 두께는, 특별히 한정되지 않지만, 1 ∼ 70 ㎛ 가 바람직하고, 보다 바람직하게는 1.5 ∼ 35 ㎛ 이다.
적층판 또는 금속박 피복 적층판의 성형 방법 및 그 성형 조건은, 특별히 한정되지 않고, 일반적인 프린트 배선판용 적층판 및 다층판의 수법 및 조건을 적용할 수 있다. 예를 들어, 적층판 또는 금속박 피복 적층판의 성형시에는 다단 프레스기, 다단 진공 프레스기, 연속 성형기, 오토클레이브 성형기 등을 사용할 수 있다. 또, 적층판 또는 금속박 피복 적층판의 성형 (적층 성형) 에 있어서, 온도는 100 ∼ 300 ℃, 압력은 면압 2 ∼ 100 kgf/㎠, 가열 시간은 0.05 ∼ 5 시간의 범위가 일반적이다. 또한, 필요에 따라, 150 ∼ 300 ℃ 의 온도에서 후 경화를 실시할 수도 있다. 특히 다단 프레스기를 사용한 경우에는, 프리프레그의 경화를 충분히 촉진시키는 관점에서, 온도 200 ℃ ∼ 250 ℃, 압력 10 ∼ 40 kgf/㎠, 가열 시간 80 분 ∼ 130 분이 바람직하고, 온도 215 ℃ ∼ 235 ℃, 압력 25 ∼ 35 kgf/㎠, 가열 시간 90 분 ∼ 120 분이 보다 바람직하다. 또, 상기 서술한 프리프레그와, 별도 제조한 내층용의 배선판을 조합하여 적층 성형함으로써, 다층판으로 하는 것도 가능하다.
[프린트 배선판]
본 실시형태의 프린트 배선판은, 절연층과, 그 절연층의 표면에 형성된 도체층을 갖는 프린트 배선판으로서, 절연층이, 상기 수지 조성물을 포함한다. 예를 들어, 상기 서술한 금속박 피복 적층판에, 소정의 배선 패턴을 형성함으로써, 프린트 배선판으로서 적합하게 사용할 수 있다. 그리고, 본 실시형태의 수지 조성물을 사용한 금속박 피복 적층판은, 높은 유리 전이 온도를 갖거나 (고 Tg), 명확한 유리 전이 온도를 갖지 않고 (Tg 레스), 또한, 휨을 충분히 저감 (저휨을 달성) 할 수 있는 경향이 있으므로, 그러한 성능이 요구되는 프린트 배선판으로서, 특히 유효하게 사용할 수 있다.
본 실시형태의 프린트 배선판은, 구체적으로는, 예를 들어, 이하의 방법에 의해 제조할 수 있다. 먼저, 상기 서술한 금속박 피복 적층판 (구리 피복 적층판 등) 을 준비한다. 금속박 피복 적층판의 표면에 에칭 처리를 실시하여 내층 회로의 형성을 실시하고, 내층 기판을 제조한다. 이 내층 기판의 내층 회로 표면에, 필요에 따라 접착 강도를 높이기 위한 표면 처리를 실시하고, 이어서, 그 내층 회로 표면에 상기 서술한 프리프레그를 소요 매수 겹치고, 또한 그 외측에 외층 회로용의 금속박을 적층하고, 가열 가압하여 일체 성형 (적층 성형) 한다. 이와 같이 하여, 내층 회로와 외층 회로용의 금속박의 사이에, 기재 및 열경화성 수지 조성물의 경화물로 이루어지는 절연층이 형성된 다층의 적층판이 제조된다. 적층 성형의 방법 및 그 성형 조건은, 상기 서술한 적층판 또는 금속박 피복 적층판과 동일하다. 이어서, 이 다층의 적층판에 스루홀이나 비어홀용의 구멍뚫기 가공을 실시한 후, 경화물 층에 포함되어 있는 수지 성분에서 유래하는 수지의 잔류물인 스미어를 제거하기 위해서 디스미어 처리가 실시된다. 그 후 이 구멍의 벽면에 내층 회로와 외층 회로용의 금속박을 도통시키는 도금 금속 피막을 형성하고, 또한 외층 회로용의 금속박에 에칭 처리를 실시하여 외층 회로를 형성하고, 프린트 배선판이 제조된다.
예를 들어, 상기 서술한 프리프레그 (기재 및 이것에 첨착된 상기 서술한 수지 조성물), 금속박 피복 적층판의 수지 조성물층 (상기 서술한 수지 조성물로 이루어지는 층) 이, 상기 서술한 수지 조성물을 포함하는 절연층을 구성하는 것이 된다.
또, 금속박 피복 적층판을 사용하지 않는 경우에는, 상기 프리프레그 또는 상기 수지 조성물로 이루어지는 것에, 회로가 되는 도체층을 형성하여 프린트 배선판을 제조해도 된다. 이 때, 도체층의 형성에 무전해 도금의 수법을 이용할 수도 있다.
또한, 본 실시형태의 프린트 배선판은, 도 9 에 나타내는 바와 같이, 적어도 1 매 이상 적층된 상기 서술한 프리프레그로 형성된 제 1 절연층 (1), 및, 그 제 1 절연층 (1) 의 편면 방향 (도시 하면 방향) 으로 적어도 1 매 이상 적층된 상기 서술한 프리프레그로 형성된 제 2 절연층 (2) 으로 이루어지는 복수의 절연층과, 그들의 복수의 절연층 (1, 2) 의 각각의 사이에 배치된 제 1 도체층 (3), 및, 그들의 복수의 절연층 (1, 2) 의 최외층에 배치된 제 2 도체층 (3) 으로 이루어지는 복수의 도체층을 가지면 적합하다. 본 발명자들의 지견에 의하면, 통상적인 적층판에서는, 예를 들어 하나의 코어 기판인 프리프레그의 양면 방향으로 다른 프리프레그를 적층함으로써 다층 프린트 배선판을 형성하는 것이 실시되지만, 본 실시형태의 프리프레그는, 제 1 절연층 (1) 을 형성하는 하나의 프리프레그의 편면 방향으로만, 제 2 절연층 (2) 을 형성하는 다른 프리프레그를 적층함으로써 제조되는 코어리스 타입의 다층 프린트 배선판 (다층 코어리스 기판) 에 특히 유효한 것이 확인되었다.
바꾸어 말하면, 본 실시형태의 프리프레그 및 수지 조성물은, 프린트 배선판에 사용한 경우에 그 휨량을 유효하게 저감할 수 있고, 특별히 한정되는 것은 아니지만, 프린트 배선판 중에서도 다층 코어리스 기판에 있어서 특히 유효하다. 즉, 통상적인 프린트 배선판은, 일반적으로 양면 대칭의 구성이 되기 때문에 잘 휘지 않는 경향이 있는 데 반해, 다층 코어리스 기판은, 양면 비대칭의 구성이 되기 쉽기 때문에, 통상적인 프린트 배선판에 비하여 휘기 쉬운 경향이 있다. 따라서, 본 실시형태의 프리프레그 및 수지 조성물을 사용함으로써, 종래 휘기 쉬운 경향이 있던 다층 코어리스 기판의 휨량을 특히 유효하게 저감할 수 있다.
또한, 도 9 에 있어서는, 1 매의 제 1 절연층 (1) 에 제 2 절연층 (2) 이 2매 적층되어 있는 구성 (요컨대, 복수의 절연층이 3 층인 구성) 을 나타냈지만, 제 2 절연층 (2) 은 1 매여도 되고 2 매 이상이어도 된다. 따라서, 제 1 도체층 (3) 도 1 층이어도 되고 2 층 이상이어도 된다.
이와 같이, 상기 서술한 구성을 갖는 본 실시형태의 프린트 배선판은, 상기 서술한 본 실시형태의 수지 조성물이, 예를 들어, 프리프레그를 경화시킨 경화물에 있어서, 열시 저장 탄성률이나 손실 탄성률 등의 기계 특성을 저휨에 적합한 특정한 범위로 제어할 수 있고, 이에 따라, 높은 유리 전이 온도를 갖거나 (고 Tg), 명확한 유리 전이 온도를 갖지 않고 (Tg 레스), 또한, 프린트 배선판, 특히, 다층 코어리스 기판의 휨을 충분히 저감 (저휨을 달성) 하기 때문에, 반도체 패키지용 프린트 배선판 및 다층 코어리스 기판으로서, 특히 유효하게 사용할 수 있다.
실시예
이하, 본 발명을 실시예 및 비교예를 사용하여 보다 구체적으로 설명한다. 단, 본 발명은, 이하의 실시예에 의해 조금도 한정되는 것은 아니다.
[합성예 1] α-나프톨아르알킬형 시안산에스테르 화합물 (SN495VCN) 의 합성
반응기 내에서, α-나프톨아르알킬 수지 (SN495V, OH 기 당량:236 g/eq., 신닛테츠 화학 (주) 제조:나프톨아르알킬의 반복 단위수 n 은 1 ∼ 5 인 것이 포함된다.) 0.47 몰 (OH 기 환산) 을, 클로로포름 500 ㎖ 에 용해시키고, 이 용액에 트리에틸아민 0.7 몰을 첨가하였다. 온도를 ―10 ℃ 로 유지하면서 반응기 내에 0.93 몰의 염화시안의 클로로포름 용액 300 g 을 1.5 시간 걸쳐 적하하고, 적하 종료 후, 30 분 교반하였다. 그 후 또한, 0.1 몰의 트리에틸아민과 클로로포름 30 g 의 혼합 용액을 반응기 내에 적하하고, 30 분 교반하여 반응을 완결시켰다. 부생한 트리에틸아민의 염산염을 반응액으로부터 여과 분리한 후, 얻어진 여과액을 0.1 N 염산 500 ㎖ 로 세정한 후, 물 500 ㎖ 에서의 세정을 4 회 반복하였다. 이것을 황산나트륨에 의해 건조시킨 후, 75 ℃ 에서 이배퍼레이트하고, 또한 90 ℃ 에서 감압 탈기함으로써, 갈색 고형의 상기 식 (4) 로 나타내는 α-나프톨아르알킬형 시안산에스테르 화합물 (식 중의 R6 은 모두 수소 원자이다.) 을 얻었다. 얻어진 α-나프톨아르알킬형 시안산에스테르 화합물을 적외 흡수 스펙트럼에 의해 분석한 바, 2264 ㎝-1 부근에 시안산에스테르의 흡수가 확인되었다.
[실시예 1]
말레이미드 화합물 (A) (BMI-2300, 다이와 화성 공업 (주) 제조, 말레이미드 당량 186 g/eq.) 46 질량부, 알릴기 함유 화합물 (B) 또한 알케닐 치환 나디이미드 화합물 (F) (BANI-M, 마루젠 석유 화학 (주) 제조, 알릴 당량:286 g/eq.) 33 질량부, 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) (EPICLON EXA-4850-150, DIC (주) 제조, 에폭시 당량:450 g/eq.) 10 질량부, 시안산에스테르 화합물 (G) 인 합성예 1 의 α-나프톨아르알킬형 시안산에스테르 화합물 (SN495VCN, 시아네이트 당량:261 g/eq.) 1 질량부, 에폭시 화합물 (H) (NC-3000FH, 닛폰 화약 (주) 제조, 에폭시 당량:320 g/eq.) 10 질량부, 충전재 (I) 인 슬러리 실리카 (SC-2050MB, 아드마텍스 (주) 제조) 120 질량부 및 동 (同) 실리콘 복합 파우더 (KMP-600, 신에츠 화학 공업 (주) 제조) 20 질량부, 실란 커플링제 (Z-6040, 토오레·다우코닝 (주) 제조) 5 질량부, 습윤 분산제 (DISPERBYK-161, 빅케미·재팬 (주) 제조) 1 질량부, 그리고, 경화 촉진제인 트리페닐이미다졸 (토쿄 화성 (주) 제조) 0.5 질량부 및 동 옥틸산아연 (닛폰 화학 산업 (주) 제조) 0.1 질량부를 혼합하고, 메틸에틸케톤으로 희석함으로써 바니시를 얻었다. 이 바니시를 E 유리 직포에 함침 도공하고, 160 ℃ 에서 3 분간 가열 건조시켜, 수지 조성물 함유량 57 체적% 의 프리프레그를 얻었다.
[실시예 2]
말레이미드 화합물 (A) (BMI-2300) 52 질량부, 알릴기 함유 화합물 (B) 또한 알케닐 치환 나디이미드 화합물 (F) (BANI-M) 38 질량부, 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) (EPICLON EXA-4816, DIC (주) 제조, 에폭시 당량:403 g/eq.) 5 질량부, 시안산에스테르 화합물 (G) 인 합성예 1 의 α-나프톨아르알킬형 시안산에스테르 화합물 (SN495VCN) 5 질량부, 충전재 (I) 인 슬러리 실리카 (SC-2050MB) 100 질량부, 동 슬러리 실리카 (SC-5050MOB, 아드마텍스 (주) 제조) 100 질량부, 및 동 실리콘 복합 파우더 (KMP-600) 20 질량부, 실란 커플링제 (Z-6040) 5 질량부, 습윤 분산제 (DISPERBYK-111, 빅케미·재팬 (주) 제조) 2 질량부 및 동 (DISPERBYK-161) 1 질량부, 그리고, 경화 촉진제인 트리페닐이미다졸 0.5 질량부 및 동 옥틸산아연 0.1 질량부를 혼합하고, 메틸에틸케톤으로 희석함으로써 바니시를 얻었다. 이 바니시를 E 유리 직포에 함침 도공하고, 160 ℃ 에서 3 분간 가열 건조시켜, 수지 조성물 함유량 57 체적% 의 프리프레그를 얻었다.
[실시예 3]
말레이미드 화합물 (A) (BMI-2300) 43 질량부, 알릴기 함유 화합물 (B) 또한 알케닐 치환 나디이미드 화합물 (F) (BANI-M) 32 질량부, 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) (EPICLON EXA-4816) 10 질량부, 시안산에스테르 화합물 (G) 인 합성예 1 의 α-나프톨아르알킬형 시안산에스테르 화합물 (SN495VCN) 5 질량부, 에폭시 화합물 (H) (NC-3000FH) 10 질량부, 충전재 (I) 인 슬러리 실리카 (SC-2050MB) 100 질량부, 동 슬러리 실리카 (SC-5050MOB) 100 질량부, 및 동 실리콘 복합 파우더 (KMP-600) 20 질량부, 실란 커플링제 (Z-6040) 5 질량부, 습윤 분산제 (DISPERBYK-111) 2 질량부 및 동 (DISPERBYK-161) 1 질량부, 그리고, 경화 촉진제인 트리페닐이미다졸 0.5 질량부 및 동 옥틸산아연 0.1 질량부를 혼합하고, 메틸에틸케톤으로 희석함으로써 바니시를 얻었다. 이 바니시를 E 유리 직포에 함침 도공하고, 160 ℃ 에서 3 분간 가열 건조시켜, 수지 조성물 함유량 57 체적% 의 프리프레그를 얻었다.
[실시예 4]
비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) (EPICLON EXA-4816) 10 질량부 대신에, 동 에폭시 수지 (C) (EPICLON EXA-4850-150) 10 질량부를 사용한 것, 및, 습윤 분산제 (DISPERBYK-111) 를 1 질량부로 한 것 이외에는, 실시예 3 과 동일한 방법에 의해, 수지 조성물 함유량 57 체적% 의 프리프레그를 얻었다.
[실시예 5]
비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) (EPICLON EXA-4850-150) 10 질량부 대신에, 동 에폭시 수지 (C) (EPICLON EXA-4816) 20 질량부를 사용한 것, 및, 에폭시 화합물 (H) (NC-3000FH) 를 사용하지 않은 것 이외에는, 실시예 4 와 동일한 방법에 의해, 수지 조성물 함유량 57 체적% 의 프리프레그를 얻었다.
[비교예 1]
말레이미드 화합물 (A) (BMI-2300) 51 질량부, 알릴기 함유 화합물 (B) 또한 알케닐 치환 나디이미드 화합물 (F) (BANI-M) 38 질량부, 시안산에스테르 화합물 (G) 인 합성예 1 의 α-나프톨아르알킬형 시안산에스테르 화합물 (SN495VCN) 1 질량부, 에폭시 화합물 (H) (NC-3000FH) 10 질량부, 충전재 (I) 인 슬러리 실리카 (SC-2050MB) 120 질량부 및 동 실리콘 복합 파우더 (KMP-600) 20 질량부, 실란 커플링제 (Z-6040) 5 질량부, 습윤 분산제 (DISPERBYK-161) 1 질량부, 그리고, 경화 촉진제인 트리페닐이미다졸 0.5 질량부 및 동 옥틸산아연 0.1 질량부를 혼합하고, 메틸에틸케톤으로 희석함으로써 바니시를 얻었다. 이 바니시를 E 유리 직포에 함침 도공하고, 160 ℃ 에서 3 분간 가열 건조시켜, 수지 조성물 함유량 57 체적% 의 프리프레그를 얻었다.
[비교예 2]
말레이미드 화합물 (A) (BMI-2300) 49 질량부, 알릴기 함유 화합물 (B) 또한 알케닐 치환 나디이미드 화합물 (F) (BANI-M) 36 질량부, 시안산에스테르 화합물 (G) 인 합성예 1 의 α-나프톨아르알킬형 시안산에스테르 화합물 (SN495VCN) 5 질량부, 에폭시 화합물 (H) (NC-3000FH) 10 질량부, 충전재 (I) 인 슬러리 실리카 (SC-2050MB) 100 질량부, 동 슬러리 실리카 (SC-5050MOB) 100 질량부, 및 동 실리콘 복합 파우더 (KMP-600) 20 질량부, 실란 커플링제 (Z-6040) 5 질량부, 습윤 분산제 (DISPERBYK-111) 2 질량부 및 동 (DISPERBYK-161) 1 질량부, 그리고, 경화 촉진제인 트리페닐이미다졸 0.5 질량부 및 동 옥틸산아연 0.1 질량부를 혼합하고, 메틸에틸케톤으로 희석함으로써 바니시를 얻었다. 이 바니시를 E 유리 직포에 함침 도공하고, 160 ℃ 에서 3 분간 가열 건조시켜, 수지 조성물 함유량 57 체적% 의 프리프레그를 얻었다.
[비교예 3]
말레이미드 화합물 (BMI-70, 케이·아이 화성 (주) 제조, 말레이미드 당량:221 g/eq.) 15 질량부, 시안산에스테르 화합물 (G) 인 합성예 1 의 α-나프톨아르알킬형 시안산에스테르 화합물 (SN495VCN) 35 질량부, 에폭시 화합물 (H) (NC-3000FH) 50 질량부, 충전재 (I) 인 슬러리 실리카 (SC-2050MB) 100 질량부, 동 슬러리 실리카 (SC-5050MOB) 100 질량부 및 동 실리콘 복합 파우더 (KMP-600) 20 질량부, 실란 커플링제 (Z-6040) 5 질량부, 습윤 분산제 (DISPERBYK-111) 2 질량부 및 동 (DISPERBYK-161) 1 질량부, 그리고, 경화 촉진제인 트리페닐이미다졸 0.5 질량부 및 동 옥틸산아연 0.1 질량부를 혼합하고, 메틸에틸케톤으로 희석함으로써 바니시를 얻었다. 이 바니시를 E 유리 직포에 함침 도공하고, 160 ℃ 에서 3 분간 가열 건조시켜, 수지 조성물 함유량 57 체적% 의 프리프레그를 얻었다.
[비교예 4]
말레이미드 화합물 (A) (BMI-2300) 35 질량부, 알릴기 함유 화합물 (B) 또한 알케닐 치환 나디이미드 화합물 (F) (BANI-M) 30 질량부, 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) (EPICLON EXA-4816) 30 질량부, 시안산에스테르 화합물 (G) 인 합성예 1 의 α-나프톨아르알킬형 시안산에스테르 화합물 (SN495VCN) 5 질량부, 충전재 (I) 인 슬러리 실리카 (SC-2050MB) 100 질량부, 동 슬러리 실리카 (SC-5050MOB, 아드마텍스 (주) 제조) 100 질량부, 및 동 실리콘 복합 파우더 (KMP-600) 20 질량부, 실란 커플링제 (Z-6040) 5 질량부, 습윤 분산제 (DISPERBYK-111) 0.1 질량부 및 동 (DISPERBYK-161) 1 질량부, 그리고, 경화 촉진제인 트리페닐이미다졸 0.5 질량부 및 동 옥틸산아연 0.1 질량부를 혼합하고, 메틸에틸케톤으로 희석함으로써 바니시를 얻었다. 이 바니시를 E 유리 직포에 함침 도공하고, 160 ℃ 에서 3 분간 가열 건조시켜, 수지 조성물 함유량 57 체적% 의 프리프레그를 얻었다.
[실시예 6]
말레이미드 화합물 (A) (BMI-2300, 다이와 화성 공업 (주) 제조, 말레이미드 당량 186 g/eq.) 46 질량부, 알릴기 함유 화합물 (B) 또한 알케닐 치환 나디이미드 화합물 (F) (BANI-M, 마루젠 석유 화학 (주) 제조, 알릴 당량:286 g/eq.) 34 질량부, 빗형 그래프트 폴리머 (D) (사이맥 (등록상표) US-350, 토아 합성 (주) 제조) 5 질량부, 시안산에스테르 화합물 (G) 인 합성예 1 의 α-나프톨아르알킬형 시안산에스테르 화합물 (SN495VCN, 시아네이트 당량:261 g/eq.) 5 질량부, 에폭시 화합물 (H) (NC-3000FH, 닛폰 화약 (주) 제조, 에폭시 당량:320 g/eq.) 10 질량부, 충전재 (I) 인 슬러리 실리카 (SC-2050MB, 아드마텍스 (주) 제조) 100 질량부, 동 슬러리 실리카 (SC-5050MOB, 아드마텍스 (주) 제조) 100 질량부, 실란 커플링제 (Z-6040, 토오레·다우코닝 (주) 제조) 5 질량부, 습윤 분산제 (DISPERBYK-161, 빅케미·재팬 (주) 제조) 1 질량부, 그리고, 경화 촉진제인 트리페닐이미다졸 (토쿄 화성 (주) 제조) 0.5 질량부 및 동 옥틸산아연 (닛폰 화학 산업 (주) 제조) 0.1 질량부를 혼합하고, 메틸에틸케톤으로 희석함으로써 바니시를 얻었다. 이 바니시를 E 유리 직포에 함침 도공하고, 160 ℃ 에서 3 분간 가열 건조시켜, 수지 조성물 함유량 73 체적% 의 프리프레그를 얻었다.
또한, 후술하는 「중량 평균 분자량 Mw 의 측정 방법」 에 의해 빗형 그래프트 폴리머 (D) (사이맥 (등록상표) US-350, 토아 합성 (주) 제조) 의 중량 평균 분자량 Mw 를 측정한 결과, 145,000 이었다.
[실시예 7]
말레이미드 화합물 (A) (BMI-2300, 다이와 화성 공업 (주) 제조, 말레이미드 당량 186 g/eq.) 를 43 질량부로 한 것, 알릴기 함유 화합물 (B) 또한 알케닐 치환 나디이미드 화합물 (F) (BANI-M, 마루젠 석유 화학 (주) 제조, 알릴 당량:286 g/eq.) 를 32 질량부로 한 것, 및, 빗형 그래프트 폴리머 (D) (사이맥 (등록상표) US-350, 토아 합성 (주) 제조) 를 10 질량부로 한 것 이외에는, 실시예 6 과 동일한 방법에 의해, 수지 조성물 함유량 73 체적% 의 프리프레그를 얻었다.
[실시예 8]
빗형 그래프트 폴리머 (D) (사이맥 (등록상표) US-350, 토아 합성 (주) 제조) 5 질량부 대신에, 빗형 그래프트 폴리머 (D) (사이맥 (등록상표) US-380, 토아 합성 (주) 제조) 5 질량부를 사용한 것 이외에는, 실시예 6 과 동일한 방법에 의해, 수지 조성물 함유량 73 체적% 의 프리프레그를 얻었다.
또한, 후술하는 「중량 평균 분자량 Mw 의 측정 방법」 에 의해 빗형 그래프트 폴리머 (D) (사이맥 (등록상표) US-380, 토아 합성 (주) 제조) 의 중량 평균 분자량 Mw 를 측정한 결과, 120,000 이었다.
[실시예 9]
빗형 그래프트 폴리머 (D) (사이맥 (등록상표) US-350, 토아 합성 (주) 제조) 10 질량부 대신에, 빗형 그래프트 폴리머 (D) (사이맥 (등록상표) US-380, 토아 합성 (주) 제조) 10 질량부를 사용한 것 이외에는, 실시예 7 과 동일한 방법에 의해, 수지 조성물 함유량 73 체적% 의 프리프레그를 얻었다.
[실시예 10]
말레이미드 화합물 (A) (BMI-2300, 다이와 화성 공업 (주) 제조, 말레이미드 당량 186 g/eq.) 를 38 질량부로 한 것, 알릴기 함유 화합물 (B) 또한 알케닐 치환 나디이미드 화합물 (F) (BANI-M, 마루젠 석유 화학 (주) 제조, 알릴 당량:286 g/eq.) 를 30 질량부로 한 것, 빗형 그래프트 폴리머 (D) (사이맥 (등록상표) US-350, 토아 합성 (주) 제조) 5 질량부 대신에, 빗형 그래프트 폴리머 (D) (사이맥 (등록상표) US-380, 토아 합성 (주) 제조) 20 질량부를 사용한 것, 시안산에스테르 화합물 (G) 인 합성예 1 의 α-나프톨아르알킬형 시안산에스테르 화합물 (SN495VCN, 시아네이트 당량:261 g/eq.) 을 4 질량부로 한 것, 및, 에폭시 화합물 (H) (NC-3000FH, 닛폰 화약 (주) 제조, 에폭시 당량:320 g/eq.) 를 8 질량부로 한 것 이외에는, 실시예 6 과 동일한 방법에 의해, 수지 조성물 함유량 73 체적% 의 프리프레그를 얻었다.
[비교예 5]
말레이미드 화합물 (A) (BMI-2300, 다이와 화성 공업 (주) 제조, 말레이미드 당량 186 g/eq.) 를 49 질량부로 한 것, 알릴기 함유 화합물 (B) 또한 알케닐 치환 나디이미드 화합물 (F) (BANI-M, 마루젠 석유 화학 (주) 제조, 알릴 당량:286 g/eq.) 를 36 질량부로 한 것, 및, 빗형 그래프트 폴리머 (D) (사이맥 (등록상표) US-350, 토아 합성 (주) 제조) 를 사용하지 않은 것 이외에는, 실시예 6 과 동일한 방법에 의해, 수지 조성물 함유량 73 체적% 의 프리프레그를 얻었다.
[비교예 6]
말레이미드 화합물 (A) (BMI-2300, 다이와 화성 공업 (주) 제조, 말레이미드 당량 186 g/eq.) 를 35 질량부로 한 것, 알릴기 함유 화합물 (B) 또한 알케닐 치환 나디이미드 화합물 (F) (BANI-M, 마루젠 석유 화학 (주) 제조, 알릴 당량:286 g/eq.) 를 25 질량부로 한 것, 빗형 그래프트 폴리머 (D) (사이맥 (등록상표) US-350, 토아 합성 (주) 제조) 를 30 질량부로 한 것, 시안산에스테르 화합물 (G) 인 합성예 1 의 α-나프톨아르알킬형 시안산에스테르 화합물 (SN495VCN, 시아네이트 당량:261 g/eq.) 을 3 질량부로 한 것, 및, 에폭시 화합물 (H) (NC-3000FH, 닛폰 화약 (주) 제조, 에폭시 당량:320 g/eq.) 를 7 질량부로 한 것 이외에는, 실시예 6 과 동일한 방법에 의해, 수지 조성물 함유량 73 체적% 의 프리프레그를 얻었다.
[중량 평균 분자량 Mw 의 측정 방법]
실시예 6 및 7 그리고 비교예 6 에서 사용한 빗형 그래프트 폴리머 (D) (사이맥 (등록상표) US-350, 토아 합성 (주) 제조) 와 실시예 8 내지 10 에서 사용한 빗형 그래프트 폴리머 (D) (사이맥 (등록상표) US-380, 토아 합성 (주) 제조) 의 중량 평균 분자량 Mw 를, 이하와 같이 측정하였다.
빗형 그래프트 폴리머 (D) 30 wt% MEK 용액 1 g 을 4 g 의 THF (용매) 에 용해시킨 용액 20 ㎕ 를, 고속 액체 크로마토그래피 ((주) 시마즈 제작소 제조, 펌프:LC-20AD) 에 주입하고 분석을 실시하였다. 칼럼은, 쇼와 전공 (주) 제조의 Shodex GPC KF-804 (길이 30 ㎝ × 내경 8 ㎜), Shodex GPC KF-803 (길이 30 ㎝ × 내경 8 ㎜), Shodex GPC KF-802 (길이 30 ㎝ × 내경 8 ㎜), Shodex GPC KF-801 (길이 30 ㎝ × 내경 8 ㎜) 의 합계 4 개를 사용하고, 이동상으로서 THF (용매) 를 사용하고, 유속을 1 ㎖/min. 으로 하고, 검출기는 RID-10A 를 사용하였다. 중량 평균 분자량 Mw 는, GPC 법에 의해 표준 폴리스티렌을 표준 물질로서 구하였다.
[물성 측정 평가]
실시예 1 ∼ 10 및 비교예 1 ∼ 6 에서 얻어진 프리프레그를 사용하여, 이하의 각 항목에 나타내는 순서에 의해 물성 측정 평가용의 샘플을 제조하고, 기계 특성 (저장 탄성률 및 손실 탄성률), 식 (12) ∼ (16) 및 식 (12A) ∼ (16A) 에 있어서의 기계 특성에 관한 물성 파라미터, 유리 전이 온도 (Tg), 휨량 (2 종류), 그리고 리플로우 공정 전후 기판 수축률을 측정 평가하였다. 실시예의 결과를 정리하여 표 1 및 표 2 에 나타내고, 비교예의 결과를 정리하여 표 3 에 나타낸다.
[기계 특성]
실시예 1 ∼ 10 및 비교예 1 ∼ 6 에서 얻어진 프리프레그 1 매의 상하 양면에, 동박 (3EC-VLP, 미츠이 금속 광업 (주) 제조, 두께 12 ㎛) 을 배치하고, 압력 30 kgf/㎠, 온도 230 ℃ 에서 100 분간의 적층 성형 (열 경화) 을 실시하고, 소정의 절연층 두께의 동박 피복 적층판을 얻었다. 얻어진 동박 피복 적층판을 다이싱 소로 사이즈 5.0 ㎜ × 20 ㎜ 로 절단 후, 표면의 동박을 에칭에 의해 제거하고, 측정용 샘플을 얻었다. 이 측정용 샘플을 사용하여, JIS C6481 에 준거하여 동적 점탄성 분석 장치 (TA 인스트루먼트 제조) 로 DMA 법에 의해, 기계 특성 (저장 탄성률 E' 및 손실 탄성률 E'') 을 측정하였다 (n = 3 의 평균값).
[유리 전이 온도 (Tg)]
실시예 1 ∼ 10 및 비교예 1 ∼ 6 에서 얻어진 프리프레그 1 매의 상하 양면에, 동박 (3EC-VLP, 미츠이 금속 광업 (주) 제조, 두께 12 ㎛) 을 배치하고, 압력 30 kgf/㎠, 온도 230 ℃ 에서 100 분간의 적층 성형 (열 경화) 을 실시하고, 소정의 절연층 두께의 동박 피복 적층판을 얻었다. 얻어진 동박 피복 적층판을 다이싱 소로 사이즈 12.7 ㎜ × 2.5 ㎜ 로 절단 후, 표면의 동박을 에칭에 의해 제거하고, 측정용 샘플을 얻었다. 이 측정용 샘플을 사용하여, JIS C6481 에 준거하여 동적 점탄성 분석 장치 (TA 인스트루먼트 제조) 로 DMA 법에 의해, 유리 전이 온도 (Tg) 를 측정하였다 (n = 3 의 평균값).
[휨량:바이메탈법]
먼저, 실시예 1 ∼ 10 및 비교예 1 ∼ 6 에서 얻어진 프리프레그 1 매의 상하 양면에, 동박 (3EC-VLP, 미츠이 금속 광업 (주) 제조, 두께 12 ㎛) 을 배치하고, 압력 30 kgf/㎠, 온도 220 ℃ 에서 120 분간의 적층 성형 (열 경화) 을 실시하고, 동박 피복 적층판을 얻었다. 다음으로, 얻어진 동박 피복 적층판으로부터 상기 동박을 제거하였다. 이어서, 동박을 제거한 적층판의 편면에, 실시예 1 ∼ 10 및 비교예 1 ∼ 6 에서 얻어진 프리프레그 1 매를 추가로 배치하고, 그 상하 양면에, 상기 동박 (3EC-VLP, 미츠이 금속 광업 (주) 제조, 두께 12 ㎛) 을 배치하고, 압력 30 kgf/㎠, 온도 220 ℃ 에서 120 분간의 적층 성형 (열 경화) 을 실시하고, 다시 동박 피복 적층판을 얻었다. 또한, 얻어진 동박 피복 적층판으로부터 상기 동박을 제거하고, 적층판을 얻었다. 그리고, 얻어진 적층판으로부터 20 ㎜ × 200 ㎜ 의 단책상 (短冊狀) 판을 잘라내고, 장척 (長尺) 방향 양단의 휨량을 금척으로 측정하고, 그 평균값을 바이메탈법에 의한 「휨량」 으로 하였다.
[휨량:다층 코어리스 기판]
먼저, 도 1 에 나타내는 바와 같이, 지지체 (a) 가 되는 프리프레그의 양면에, 캐리어가 부착된 극박 (極薄) 동박 (b1) (MT18Ex, 미츠이 금속 광업 (주) 제조, 두께 5 ㎛) 의 캐리어 동박면을 프리프레그측으로 향하게 하여 배치하고, 그 위에 실시예 1 ∼ 10 및 비교예 1 ∼ 6 에서 얻어진 프리프레그 (c1) 을 추가로 배치하고, 그 위에 동박 (d) (3EC-VLP, 미츠이 금속 광업 (주) 제조, 두께 12 ㎛) 을 추가로 배치하고, 압력 30 kgf/㎠, 온도 220 ℃ 에서 120 분간의 적층 성형을 실시하여 도 2 에 나타내는 동박 피복 적층판을 얻었다.
이어서, 얻어진 도 2 에 나타내는 동박 피복 적층판의 상기 동박 (d) 을, 예를 들어 도 3 에 나타내는 바와 같이 소정의 배선 패턴으로 에칭하여 도체층 (d') 을 형성하였다. 다음으로, 도체층 (d') 이 형성된 도 3 에 나타내는 적층판 상에, 도 4 에 나타내는 바와 같이, 실시예 1 ∼ 10 및 비교예 1 ∼ 6 에서 얻어진 프리프레그 (c2) 를 배치하고, 그 위에 또한, 캐리어가 부착된 극박 동박 (b2) (MT18Ex, 미츠이 금속 광업 (주) 제조, 두께 5 ㎛) 을 배치하고, 압력 30 kgf/㎠, 온도 230 ℃ 에서 120 분간의 적층 성형을 실시하여 도 5 에 나타내는 동박 피복 적층판을 얻었다.
이어서, 도 5 에 나타내는 동박 피복 적층판에 있어서, 지지체 (a) (경화한 지지체용 프리프레그) 에 배치한 캐리어가 부착된 극박 동박 (b1) 의 캐리어 동박과 극박 동박을 박리함으로써, 도 6 에 나타내는 바와 같이, 지지체 (a) 로부터 2 매의 적층판을 박리하고, 또한, 그들의 각 적층판에 있어서의 상부의 캐리어가 부착된 극박 동박 (b2) 으로부터 캐리어 동박을 박리하였다. 다음으로, 얻어진 각 적층판의 상하의 극박 동박 상에 레이저 가공기에 의한 가공을 실시하고, 도 7 에 나타내는 바와 같이, 화학 구리 도금으로 소정의 비아 (v) 를 형성하였다. 그리고, 예를 들어 도 8 에 나타내는 바와 같이, 소정의 배선 패턴으로 에칭하여 도체층을 형성하고, 다층 코어리스 기판의 패널을 얻었다. 그리고, 얻어진 패널의 4 개 모서리 및 4 변 중앙 부분의 합계 8 개 지점에 있어서의 휨량을 금척으로 측정하고, 그 평균값을 다층 코어리스 기판의 패널의 「휨량」 으로 하였다.
[리플로우 공정 전후 기판 수축률]
실시예 1 ∼ 10 및 비교예 1 ∼ 6 에서 얻어진 프리프레그 1 매의 상하 양면에, 동박 (3EC-VLP, 미츠이 금속 광업 (주) 제조, 두께 12 ㎛) 을 배치하고, 압력 30 kgf/㎠, 온도 220 ℃ 에서 120 분간의 적층 성형을 실시하여, 동박 피복 적층판을 얻었다. 다음으로, 얻어진 동박 피복 적층판에 드릴로 격자상 균등하게 9 점의 구멍뚫기 가공을 실시한 후, 상기 동박을 제거하였다.
그리고, 먼저, 동박이 제거된 적층판에 있어서의 구멍간의 거리를 측정하였다 (거리 가). 다음으로, 그 적층판에 대하여, 살라만더 리플로우 장치로 260 ℃ 를 최고 온도로 하여 리플로우 처리를 실시하였다. 그 후, 적층판에 있어서의 구멍간의 거리를 재차 측정하였다 (거리 나). 그리고, 측정된 거리 가와 거리 나를 하기 식 (I) 에 대입하고, 리플로우 처리에 있어서의 기판의 치수 변화율을 구하고, 그 값을 리플로우 공정 전후 기판 수축률로 하였다.
((거리 가) ― (거리 나)) / 거리 가 × 100 … 식 (I)
산업상 이용가능성
본 실시형태의 수지 조성물은, 프리프레그, 적층판, 금속박 피복 적층판, 프린트 배선판, 또는 다층 프린트 배선판의 재료로서 산업상 이용가능성을 갖는다. 또한, 본 출원은, 2016년 12월 28일에 출원된 일본 특허출원번호 2016-255207, 및, 2017년 2월 27일에 출원된 일본 특허출원번호 2017-035200 에 기초하는 것이며, 여기에 그들의 기재 내용을 원용한다.
Claims (20)
- 말레이미드 화합물 (A) 와,
알릴기 함유 화합물 (B) 와,
비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 및/또는 빗형 그래프트 폴리머 (D),
를 함유하고,
상기 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 또는 상기 빗형 그래프트 폴리머 (D) 의 수지 조성물에 있어서의 함유량이, 수지 고형분 100 질량부에 대하여 3 ∼ 25 질량부인, 수지 조성물. - 제 1 항에 있어서,
상기 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 와 상기 빗형 그래프트 폴리머 (D) 의 수지 조성물에 있어서의 함유량의 합계량이, 수지 고형분 100 질량부에 대하여 3 ∼ 25 질량부인,
수지 조성물. - 제 1 항 또는 제 2 항에 있어서,
상기 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 의 에폭시 당량이 400 g/eq. 이상인,
수지 조성물. - 제 1 항 내지 제 3 항 중 어느 한 항에 있어서,
상기 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 는, 하기 식 (1) 로 나타내는 것인,
수지 조성물.
[화학식 1]
(식 (1) 중, R1 및 R2 는, 각각 독립적으로, 수소 원자, 또는 메틸기를 나타내고, R3 ∼ R6 은, 각각 독립적으로, 수소 원자, 메틸기, 염소 원자, 또는 브롬 원자를 나타내고, X 는, 에틸렌옥시에틸기, 디(에틸렌옥시)에틸기, 트리(에틸렌옥시)에틸기, 프로필렌옥시프로필기, 디(프로필렌옥시)프로필기, 트리(프로필렌옥시)프로필기, 또는 탄소수 2 ∼ 15 의 알킬렌기를 나타내고, n 은, 자연수를 나타낸다.) - 제 4 항에 있어서,
상기 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 는, 상기 식 (1) 에 있어서의 X 가 에틸렌기의 것인,
수지 조성물. - 제 1 항 내지 제 5 항 중 어느 한 항에 있어서,
상기 알릴기 함유 화합물 (B) 가, 알릴페놀 유도체 (E) 및/또는 알케닐 치환 나디이미드 화합물 (F) 인,
수지 조성물. - 제 6 항에 있어서,
상기 알케닐 치환 나디이미드 화합물 (F) 가, 하기 식 (6) 으로 나타내는 화합물을 포함하는,
수지 조성물.
[화학식 2]
(식 (6) 중, R1 은, 각각 독립적으로, 수소 원자, 또는 탄소수 1 ∼ 6 의 알킬기를 나타내고, R2 는, 탄소수 1 ∼ 6 의 알킬렌기, 페닐렌기, 비페닐렌기, 나프틸렌기, 또는 하기 식 (7) 혹은 (8) 로 나타내는 기를 나타낸다.)
[화학식 3]
(식 (7) 중, R3 은, 메틸렌기, 이소프로필리덴기, 또는, CO, O, S, 혹은 SO2 로 나타내는 치환기를 나타낸다.)
[화학식 4]
(식 (8) 중, R4 는, 각각 독립적으로, 탄소수 1 ∼ 4 의 알킬렌기, 또는 탄소수 5 ∼ 8 의 시클로알킬렌기를 나타낸다.) - 제 1 항 내지 제 8 항 중 어느 한 항에 있어서,
상기 빗형 그래프트 폴리머 (D) 의 중량 평균 분자량 Mw 가, 1.0 × 105 ∼ 3.5 × 105 인,
수지 조성물. - 제 1 항 내지 제 9 항 중 어느 한 항에 있어서,
시안산에스테르 화합물 (G) 를 추가로 함유하는,
수지 조성물. - 제 1 항 내지 제 11 항 중 어느 한 항에 있어서,
상기 비스페놀 A 형 구조 단위와 탄화수소계 구조 단위로 이루어지는 에폭시 수지 (C) 이외의 에폭시 화합물 (H) 를 추가로 함유하는,
수지 조성물. - 제 1 항 내지 제 12 항 중 어느 한 항에 있어서,
충전재 (I) 를 추가로 함유하는,
수지 조성물. - 제 13 항에 있어서,
상기 충전재 (I) 의 수지 조성물에 있어서의 함유량이, 수지 고형분 100 질량부에 대하여 100 ∼ 700 질량부인,
수지 조성물. - 기재와,
그 기재에 함침 또는 도포된, 제 1 항 내지 제 14 항 중 어느 한 항에 기재된 수지 조성물,
을 갖는 프리프레그. - 제 15 항에 있어서,
상기 기재가, E 유리 섬유, D 유리 섬유, S 유리 섬유, T 유리 섬유, Q 유리 섬유, L 유리 섬유, NE 유리 섬유, HME 유리 섬유, 및 유기 섬유로 이루어지는 군에서 선택되는 1 종 이상의 섬유로 구성된 것인,
프리프레그. - 적어도 1 매 이상 적층된 제 15 항 또는 제 16 항에 기재된 프리프레그를 갖는, 적층판.
- 적어도 1 매 이상 적층된 제 15 항 또는 제 16 항에 기재된 프리프레그와,
그 프리프레그의 편면 또는 양면에 배치된 금속박,
을 갖는 금속박 피복 적층판. - 절연층과,
그 절연층의 표면에 형성된 도체층,
을 갖고,
상기 절연층이, 제 1 항 내지 제 14 항 중 어느 한 항에 기재된 수지 조성물을 포함하는,
프린트 배선판. - 적어도 1 매 이상 적층된 제 15 항 또는 제 16 항에 기재된 프리프레그로 형성된 제 1 절연층, 및, 상기 제 1 절연층의 편면 방향으로 적어도 1 매 이상 적층된 제 15 항 또는 제 16 항에 기재된 프리프레그로 형성된 제 2 절연층으로 이루어지는 복수의 절연층과,
상기 복수의 절연층의 각각의 사이에 배치된 제 1 도체층, 및, 상기 복수의 절연층의 최외층의 표면에 배치된 제 2 도체층으로 이루어지는 복수의 도체층,
을 갖는 다층 프린트 배선판.