KR20030078374A - 감광성 수지 제거용 씬너 조성물 - Google Patents
감광성 수지 제거용 씬너 조성물 Download PDFInfo
- Publication number
- KR20030078374A KR20030078374A KR1020020017385A KR20020017385A KR20030078374A KR 20030078374 A KR20030078374 A KR 20030078374A KR 1020020017385 A KR1020020017385 A KR 1020020017385A KR 20020017385 A KR20020017385 A KR 20020017385A KR 20030078374 A KR20030078374 A KR 20030078374A
- Authority
- KR
- South Korea
- Prior art keywords
- propylene glycol
- ether acetate
- weight
- thinner composition
- parts
- Prior art date
Abstract
본 발명은 반도체 소자 및 액정 디스플레이 소자류 제조공정에 사용되는 감광성 수지 제거용 씬너(thinner) 조성물에 관한 것으로, a) 프로필렌글리콜 모노알킬에테르 아세테이트(propyleneglycol monoalkyl ether acetate); b) 씨클로 케톤(cyclo ketone); c) 폴리에틸렌옥사이드계 축합물(polyethylene based condensate); 및 d) 플루오리네이티드 아크릴릭 코폴리머(fluorinated acrylic copolymer)를 포함하는 씬너 조성물을 제공한다.
Description
본 발명은 반도체 소자 및 액정 디스플레이 소자류 제조공정에 사용되는 감광성 수지 제거용 씬너(thinner) 조성물에 관한 것으로, 특히 포토리소그래피 공정에서 에칭시 마스크로 사용되는 감광성 수지 조성물 중 가장자리 에지 부분의 감광액 및 기판 후면의 감광액을 세정하는데 사용될 수 있는 세정용 씬너 조성물에 관한 것이다.
반도체 소자 및 액정 디스플레이 소자류의 제조공정 중에서 포토리소그래피 공정(photolithography)이라 함은 기판에 감광막을 도포하고, 사전에 설계된 바대로의 패턴을 전사하고, 전사된 패턴에 따라 적절하게 깎아내는 식각 공정을 통하여 전자 회로를 구성해나가는 작업이다.
이러한 포토리소그래피 공정은
a) 기판의 표면에 감광성 수지조성물을 균일하게 도포하는 도포공정;
b) 도포된 감광막으로부터 용제를 증발시켜 감광막이 웨이퍼의 표면에 달라
붙게 하는 소프트베이킹(soft baking) 공정;
c) 자외선 등의 광원을 이용하여 마스크 상의 회로 패턴을 반복적으로
그리고 순차적으로 축소 투영하면서 기판을 노광 시켜 마스크의 패턴을
기판 상으로 전사하는 노광(露光) 공정;
d) 광원에의 노출에 의한 감광에 따라 용해도차와 같은 물리적 성질이 다르
게 된 부분들을 현상액을 사용하여 선택적으로 제거하는 현상(現像)
공정;
e) 현상작업 후 기판상에 잔류하는 감광막을 보다 긴밀하게 고착시키기 위한
하드 베이킹(hard baking) 공정;
f) 현상된 기판의 패턴에 따라 전기적인 특성을 부여하기 위하여 소정 부위
를 에칭하는 식각(蝕刻) 공정; 및
g) 상기 공정 후, 불필요하게 된 감광막을 제거하는 박리(剝離) 공정
등으로 진행된다.
이와 같은 포토리소그래피 공정을 통해 궁극적으로 반도체 집적회로를 제작하기 위해서 기판 상에 다수의 미세회로를 형성한다. 이런 공정 중에 회로 배선 사이의 미세한 간격 때문에 외부입자, 예를 들면 입자(particle)가 도입되는 것을 막아야 한다. 기판 상에 존재하는 입자는 에칭이나 이온주입 등과 같은 후속공정에서 여러 가지 불량이 발생시킬 수 있으며, 이에 따라 전체 공정의 수율 저하를 초래하게 된다. 이러한 입자 유입의 주요 발생처가 감광성 수지 조성물로 도포된 기판 주변에 구형 형태로 존재하는 사용되지 않는 감광성 수지 조성물이다.
상기 포토리소그래피 공정 중에서 기판 위에 감광막을 공급하고 기판을 회전시켜 원심력에 의해 표면에 고르게 퍼지게 하는 회전 도포공정을 이용한 후에 이러한 구형 형태의 감광물질이 발생하게 된다. 이러한 회전 도포공정은 기판 가장자리 부위와 후면에 원심력으로 치우쳐진 감광막을 몰리게 하여 작은 구형 물질을 형성시킨다. 이 구형 물질은 베이크 공정을 거친 후 기판의 이송 도중 박리되어 장치내의 파티클의 원인이 되기도 하고 노광시 디포커스(defocus)의 원인이 된다.
이러한 불필요한 감광물질이 장비 오염의 원인이 되어 반도체 소자류 제조공정의 수율을 저하시키므로 이를 제거하기 위하여 기판 에지 부분과 후면의 상하에 분사노즐을 설치하고 노즐을 통하여 에지 부분과 후면에 유기용제 성분으로 구성된 씬너(thinner) 조성물을 분사하여 이를 제거하고 있다.
상기 씬너 조성물의 성능을 결정짓는 요소는 용해 속도, 휘발성 등을 들 수 있다. 씬너 조성물의 용해 속도는 감광성 수지를 얼마나 효과적으로 빠르게 용해시켜 제거할 수 있느냐 하는 능력으로 매우 중요하다. 상세하게는 에지 부위의 린스에 있어서, 적절한 용해속도를 가져야만 매끄러운 처리단면을 가질 수 있으며, 용해 속도가 너무 높은 경우에는 기판에 도포된 감광막의 린스에서 감광막 어택(attack)이 나타날 수 있다. 반대로 용해 속도가 너무 낮은 경우에는 기판에 도포된 감광막의 린스에서 테일링(tailing)이라 하는 부분 용해된 감광막 테일(tail)의 흐름 현상이 나타날 수 있다. 특히 최근 들어 반도체 집적회로의 고집적화, 고밀도화에 따른 기판의 대구경화로 인해 회전 도포기를 이용한 린스 공정의 경우 회전 속도의 저속화(RPM)는 필연적이라고 할 수 있다. 이러한 린스 공정에서 저회전 속도에 따른 기판의 요동과 분사되는 액의 접촉 속도에서 적절한 용해속도를 지니지 못할 경우 튐(bounding) 현상을 나타내며 불필요한 씬너 약액 사용이 늘게 된다. 이와 같이 대구경화로 인한 저속(RPM) 린스 공정에서는 종래의 고속(RPM) 린스 공정보다 더욱 씬너의 강력한 용해 속도가 요구되고 있다.
또한 휘발성은 감광성 수지를 제거하고 난 후, 쉽게 휘발하여 기판의 표면에 잔류하지 않을 것이 요구되며, 휘발성이 너무 낮아 씬너가 휘발하지 못하고 잔류하는 경우 잔류하는 씬너 자체가 각종의 공정, 특히 후속 에칭공정 등에서 오염원으로 작용하여 반도체 소자의 수율을 저하시키는 문제점으로 작용할 수 있으며, 휘발성이 너무 높으면 기판이 급속히 냉각하여 도포된 감광성 수지의 막두께 편차가 심해지는 현상과 사용 중에 대기중으로 쉽게 휘발되어 청정실 자체를 오염시키는 원인이 될 수 있다. 이로 인한 각종 테일링이나 감광막 어택 등의 불량은 모두 반도체 소자류의 제조 수율을 저하시키는 직접적인 원인이 되고 있다.
종래의 씬너 조성물들을 살펴보면 다음과 같다.
일본공개특허공보 소63-69563호는 씬너를 기판의 주도부(edge upside part), 연도부(edge side part), 배면부(edge backside part)의 불필요한 감광막에 접촉시켜 제거하는 방법을 제안하고 있다. 이 방법에서 세정 제거용 용제로 예를 들면, 셀로솔브, 셀로솔브 아세테이트, 프로필렌글리콜 에테르, 프로필렌글리콜 에테르 아세테이트 등의 에테르 및 에테르 아세테이트류, 아세톤, 메틸에틸케톤, 메틸이소부틸케톤, 씨클로헥사논 등의 케톤류, 메틸 락테이트, 에틸 락테이트, 메틸 아세테이트, 에틸 아세테이트, 부틸 아세테이트 등의 에스테르류를 씬너로 사용한다. 또한 일본특허공개공보 평4-49938호는 프로필렌글리콜 모노메틸에테르아세테이트(PGMEA; propyleneglycol monomethylether acetate)를 씬너로 사용한다. 또한 일본공개 특허공보 평4-42523호는 알킬 알콕시 프로피오네이트를 씬너로 사용하는 방법 등이 개시되어 있다.
그러나 이러한 종래의 씬너 용제는 주로 에틸렌글리콜 모노에틸에테르아세테이트(EGMEA; ethyleneglycol monoethylether acetate), 프로필렌글리콜 모노메틸에테르아세테이트(PGMEA; propyleneglycol monomethylether acetate) 및 에틸 락테이트(EL; ethyl lactate) 등의 단일 용제를 사용하는 것이었으나 다음과 같은 한계를 가지고 있어 사용에 문제가 있다.
즉, 에틸렌글리콜 모노에틸에테르아세테이트의 경우 용해속도는 우수하나 휘발성과 인화성이 높고 특히 백혈구 감소증 및 태아유산 유발 등의 생식 독성을 나타내는 문제점이 있으며 에틸 락테이트는 점도가 높고 용해속도가 낮기 때문에 단독으로는 충분한 세정 효과를 얻을 수 없으며 아세톤, 메틸 에틸 케톤 등과 같은 용제는 인화점이 낮아 작업안전성이 떨어지는 문제점이 있다.
이를 해결하기 위해 종래의 단일 용제들을 혼합하여 사용하는 방법 등이 연구되었다. 구체적으로, 일본공개특허공보 평4-130715호는 피루핀산 알킬계 용제와 메틸 에틸 케톤으로 이루어진 혼합용제를 씬너로 사용한다. 또한 일본공개특허공보 평7-146562호는 프로필렌글리콜 알킬에테르와 3-알콕시프로피온산 알킬류의 혼합물로 이루어진 씬너 조성물을 사용한다. 또한 일본공개특허공보 평7-128867호는 프로필렌글리콜 알킬에테르와 부틸 아세테이트와 에틸 락테이트의 혼합물, 또는 부틸 아세테이트와 에틸 락테이트, 프로필렌글리콜 알킬에테르 아세테이트의 혼합물로 이루어진 씬너조성물을 사용한다. 또한 일본공개특허공보 평7-160008호는 프로필렌글리콜 알킬에테르 프로피오네이트와 메틸 에틸 케톤의 혼합물, 또는 프로필렌글리콜 알킬에테르 프로피오네이트와 초산 부틸의 혼합물로 이루어진 씬너 조성물을 사용한다. 또한 미국특허 제4,983,490호는 프로필렌글리콜 알킬에테르 아세테이트와 프로필렌 글리콜 알킬에테르로 이루어진 혼합 용제를 씬너 조성물로 사용한다. 또한 미국특허 제4,886,728호는 에틸 락테이트와 메틸 에틸 케톤으로 이루어진 혼합물을 씬너 조성물로 사용한다.
그러나 상기에서 서술한 혼합 용제들도 점차 고집적화, 대구경화 되고 있는 반도체 소자와 액정 디스플레이 소자류의 제조에 적용에는 많은 어려움이 있다. 예를 들면, 피루핀산 알킬계 용제와 메틸 에틸 케톤으로 이루어진 혼합 용제는 감광막의 중요 성분중 하나인 감광제중 에스테르화율이 높은 1,2-나프토퀴논디아지드계 감광제에 대한 용해성이 떨어지며, 프로필렌글리콜 알킬에테르 프로피오네이트와 초산 부틸의 혼합 용제 등 휘발성이 높은 용제를 후면 세정에 적용할 경우 기판이 냉각되면서 감광막 두께편차가 심해지는 현상이 발생하며, 에틸 락테이트와 메틸 에틸 케톤의 혼합 용제와 같이 휘발성이 낮은 용제를 사용할 경우 기판 가장자리 부위의 세정 성능이 떨어진다. 특히 메틸 피루베이트, 에틸 피루베이트 등의 용제는 장기간 사용시 감광막 회전도포기에 부착된 감광 폐액 저장조 내의 금속 부위를 부식시키는 것으로 알려져 있다.
사용되는 용제의 특성을 살펴보면 우선 프로필렌글리콜 모노메틸에테르는 종래의 에틸렌글리콜 모노에틸에테르에 비하여 감광성 수지의 감광속도를 증가시키는이점이 있다고 알려져 있으나(즉, 광활성 물질에 대한 용해성이 뛰어남을 의미하나) 이를 접촉하는 사람들은 나쁜 냄새와 생체학적 우려로 불쾌감을 느낀다. 이를 개선하는 방법으로 프로필렌글리콜 모노메틸에테르 아세테이트와 혼합하여 사용하려는 시도(미국특허 제4,983,490호)가 있었지만 이 역시 냄새 등의 의한 불쾌감을 완전히 해소시킬 수는 없었다.
본 발명은 상기 종래기술의 문제점을 고려하여, 반도체 집적회로 소자 및 액정 디스플레이 소자의 제조에 사용되는 기판의 대구경화로 인해 기판의 에지 부위나 후면 부위에서 균일한 감광액 제거 성능을 지닌 씬너 조성물을 제공하는 것을 목적으로 한다.
본 발명의 다른 목적은 반도체 집적회로 소자 제조시 씬너 조성물의 불충분한 용해력으로 인해 웨이퍼 끝단에서 미제거 감광성 수지가 뭉쳐서 생기는 불량에 탁월한 효과가 있는 씬너 조성물을 제공하는 것이다.
본 발명의 또 다른 목적은 감광액 도포 공정에서 불량이 발생하여 리워크(Rework)가 필요한 기판의 경우에 표면에 부착되어 있는 잔류 물질을 완벽하게 제거하여 기판을 경제적으로 사용 가능하게 해주는 씬너 조성물을 제공하는 것이다.
본 발명의 또 다른 목적은 감광성 수지에 대해서 우수한 용해속도와 휘발성을 가지는 감광액 제거용 씬너 조성물을 제공하는 것이다.
본 발명의 또 다른 목적은 안료 감광성 수지에 대한 높은 용해력을 가지는안료 감광성 수지 제거용 씬너 조성물을 제공하는 것이다.
본 발명의 또 다른 목적은 웨이퍼에서 씬너 조성물이 분사에 의하여 감광액과의 계면 접촉시 우수한 퍼짐성을 지녀 감광성 수지 조성물을 효과적으로 제거하여 매끄러운 처리단면을 얻을 수 있는 감광액 제거용 씬너 조성물을 제공하는 것이다.
본 발명의 또 다른 목적은 인체에 대한 독성이 없고, 냄새로 인한 불쾌감이 없어서 작업 안정성이 높으며, 금속에 대한 부식성이 낮은 감광액 제거용 씬너 조성물을 제공하는 것이다.
본 발명은 상기 목적을 달성하기 위하여, 반도체 소자 및 액정 디스플레이 소자 제조 공정의 세정용 씬너 조성물에 있어서,
a) 프로필렌글리콜 모노알킬에테르 아세테이트(propyleneglycol monoalkyl ether acetate);
b) 씨클로 케톤(cyclo ketone);
c) 폴리에틸렌옥사이드계 축합물(polyethylene based condensate) ; 및
d) 플루오리네이티드 아크릴릭 코폴리머(fluorinated acrylic copolymer)
를 포함하는 세정용 씬너 조성물을 제공한다.
상기 씬너 조성물은
a) 프로필렌글리콜 모노알킬에테르 아세테이트 1 내지 80 중량부;
b) 씨클로 케톤 1 내지 99 중량부;
c) 폴리에틸렌옥사이드계 축합물 0.001 내지 1 중량부; 및
d) 플루오리네이티드 아크릴릭 코폴리머 0.001 내지 1 중량부
를 포함하는 것이 바람직하다.
이하에서 본 발명을 상세하게 설명한다.
본 발명은 상기 4 가지 성분을 일정 성분비로 적절히 조합하여 사용할 경우 감광액 제거용 씬너 조성물로서 우수한 성능을 발휘할 수 있다는 발견에 기초한 것이다.
본 발명의 조성물 중 상기 프로필렌글리콜 모노알킬에테르아세테이트와 씨클로 케톤, 알킬 아세테이트 용제들은 모두 반도체 등급의 극히 순수한 것이 선택되어 사용될 수 있으며, VLSI 등급에서는 0.1 ㎛ 수준으로 여과한 것이 사용될 수 있다.
상기 a)의 프로필렌글리콜 모노알킬에테르 아세테이트는 알킬기의 탄소수가 1 내지 5인 것이 사용가능하며, 이들의 예로는 프로필렌글리콜 모노메틸에테르아세테이트, 프로필렌글리콜 모노에틸에테르아세테이트, 프로필렌글리콜 모노프로필에테르아세테이트, 프로필렌글리콜 모노부틸에테르아세테이트 등이 있다.
상기 b)의 씨클로 케톤은 씨클로 펜타논, 씨클로 헥사논, 씨클로 헵타논 등이 있다.
상기 c)의 폴리에틸렌옥사이드계 축합물은 비이온계 계면활성제로 작용하며, 알킬페놀의 폴리에틸렌옥사이드 축합물 등이 해당된다. 구체적인 예는 직쇄 또는 측쇄배열의 탄소수 6 내지 12의 알킬기를 갖고 있는 알킬페놀과 이 알킬페놀 1 몰당 5∼25 몰의 에틸렌 옥사이드를 축합시킨 축합생성물이 포함된다. 여기에서 알킬페놀의 알킬치환체의 예를 들면, 중합시킨 프로필렌, 디이소부틸렌, 옥텐 또는 노넨으로부터 유도된 것일 수 있다. 이런 유형의 화합물 예로는 노닐페놀 1 몰 당 에틸렌 옥사이드 약 9.5 몰을 축합시킨 노닐페놀, 페놀 1 몰 당 약 12 몰의 에틸렌 옥사이드를 축합시킨 도데실페놀, 페놀 1 몰당 약 15 몰의 에틸렌 옥사이드를 축합시킨 디이소옥틸페놀이 있다.
이들은 물과 각종 용제에 우수한 용해성을 지니며 씬너가 감광성 수지와 만날 때 계면에서 그 단차를 줄여주는 역할을 하며, 상용화된 제품으로는 동남합성사의 비이온성 모노폴 시리즈 계면활성제를 들 수 있다. 혼합 첨가량은 0.001 내지 1 중량부가 바람직하다. 즉, 이러한 계면활성제의 함량은 0.001 중량부 미만이면 기판의 끝단에서의 씬너의 휘발성과 세정력이 현저히 저하되고, 1 중량부를 초과하게 되면 거품이 심하게 발생하여 사용이 불편할 수 있다.
상기 d)의 플루오리네이티드 아크릴릭 코폴리머는 물과 각종 용제에 우수한 용해성을 지니며, 상용화된 제품으로는 다이니뽄잉크 앤드 케미칼사의 메가페이스 R-08을 들 수 있다. 혼합 첨가량은 0.001 내지 1 중량부가 바람직하다. 즉, 상기 이 코폴리머의 함량이 0.001 중량부 미만이면 감광액에 대한 용해력이 현저히 저하되고, 1 중량부를 초과하게 되면 계면에서 동적 표면장력을 낮추어 우수한 제거성능을 나타내지만 반면 거품이 심하게 발생하여 사용시 액량을 감지하는 센서의 오동작을 유발시킬 수 있다.
프로필렌글리콜 모노메틸에테르 아세테이트는 공기중에 노출시 인체에 대한안전성이 높다고 보고되어 있으며 물질대사 측면에서도 인체에서 급속히 프로필렌글리콜과 알코올로 분해되어 안전하다. 독성실험에서 마우스에 구강투여로 인한 50 % 치사량을 나타내는 LD50(mouse) = 8.5 g/kg을 나타내며 가수분해에 의하여 빠르게 분해된다. 물리적 성질은 끓는점 146 ℃, 인화점(클로즈드 컵방식으로 측정) 42 ℃, 점도(25 ℃에서) 1.17 cps, 표면장력 26 dyne/㎠ 이다.
씨클로 케톤의 하나인 헥사논은 각종 수지에 대한 용해력이 우수한데 특히 제거하기 힘든 안료 감광수지에도 높은 용해력을 보여 안료 감광수지의 제거에 있어서는 그 성능이 월등하다.
알킬 아세테이트의 하나인 부틸 아세테이트의 경우 표면장력이 낮고, 휘발성이 탁월하여 씬너 조성물에 소정의 함량만 첨가해도 우수한 계면 특성을 발휘할 수 있다.
플루오리네이티드 아크릴릭 코폴리머는 중량평균 분자량이 3000 내지 10000 사이의 것을 사용하며 인화점(오픈컵 방식으로 측정) 200 ℃, 비중 1.10 g/ml(25 ℃), 점도(20 ℃) 2100 cst, 표면장력이 에틸 락테이트상에서 24.0 mN/m(Wilhermy method)을 나타내며 통상적으로 에틸 락테이트에 희석 혼합하여 사용한다.
본 발명의 적용방법은 상기 4 가지 조성을 일정 성분비로 적절히 조합한 후 위에서 언급했던 감광성 수지를 감광액 도포기에 의해 도포하고 기판의 에지와 후면 부위에 발생된 구형태의 불필요한 감광액을 씬너 조성물을 적하 혹은 노즐을 통한 스프레이 방식으로 분사하여 제거한다. 씬너 조성물의 적하 혹은 분사량은 사용하는 감광성 수지의 종류, 막의 두께에 따라 조절이 가능하며 적정량은 통상5∼100 cc/min의 범위에서 선택하여 사용한다. 이렇게 씬너 조성물을 분사한 후 후속 포토리소그래피 공정을 거쳐 미세 회로 패턴을 형성할 수 있다.
이하의 실시예와 비교예를 통하여 본 발명을 더욱 상세하게 설명한다. 단, 실시예는 본 발명을 예시하기 위한 것이지 이들만으로 한정하는 것은 아니다.
[실시예]
본 실시예에서 사용된 기판 시편은 하기와 같이 준비하였다.
직경이 8 inch인 산화 실리콘 기판을 사용한다. 이들 기판을 먼저 각각 과산화수소 / 황산 혼합물을 함유하는 2개의 욕에서 세정(각각의 욕에서 5분 동안 침잠시킴)한 다음 초순수로 헹군다. 이 과정은 주문 제작한 세정 설비에서 진행한다. 이후 이들 기판을 스핀 드라이어(VERTEQ사 제품, 모델 SRD 1800-6)에서 회전 건조시킨다. 이어서 기판의 상부면에 각각의 감광막을 일정 두께로 피복한다. 감광막을 도포하기 위해 회전 피복기 (고려반도체사제품, 모델 EBR TRACK)를 사용한다.
상기 회전 피복조작에 있어서 감광막 조성물 10 cc를 정지된 기판의 중앙에 적하한다. 이후에 회전 피복기를 사용하여 500 rpm에서 3 초간 감광막을 분포시킨다. 이후에 기판을 약 2000∼4000 rpm 정도의 회전속도로 가속시켜 각 감광막을 소정의 두께로 조정한다. 이 속도에서 회전 시간은 약 20∼30 초이다.
실시예 1∼4, 비교예 1∼2
[표 1]
씬너 조성물
구 분 (중량부) | 실시예 1 | 실시예 2 | 실시예 3 | 비교예 1 | 비교예 2 | |
조성 | PGMEA | 40 | 40 | 40 | 100 | 30 |
cyclopentanone | - | 60 | - | - | - | |
cyclohexanone | 60 | - | 60 | - | 50 | |
NP-1019 | 0.01 | - | - | - | - | |
OP-1015 | - | 0.01 | 0.01 | - | 0.01 | |
R-08 | 0.01 | 0.01 | 0.01 | 0.01 | - |
상기 표 1에서,
PGMEA는 프로필렌글리콜 모노메틸 에테르 아세테이트(Propyleneglycol monomethyl ether acetate)이며,
NP-1019는 노닐페놀 1 몰에 에틸렌 옥사이드 9 몰을 축중합시킨 동남합성사의 모노폴 NP-1019이며,
OP-1015는 옥틸페놀 1 몰에 에틸렌 옥사이드 5 몰을 축중합시킨 동남합성사의 모노폴 OP-1015이며,
R-08은 플루오리네이티드 아크릴릭 코폴리머으로서, 다이니뽄잉크 앤드 케미칼사제품 메가페이스 R-08이다.
상기 씬너 조성물들은 포토리소그래피 공정에서 불량품으로 회수되는 기판이나 또는 공정관리를 위하여 임의로 인출한 테스트용 기판들로부터 그 표면에 부착되어 있는 감광막을 제거하여 기판을 재사용 하기 위한 목적으로도 사용 가능한데 이 경우 상기 결과에서 본 발명에 따른 씬너 조성물들이 용해속도가 우수하여 기판 재사용을 위한 공정 시간을 단축시키는 장점이 있다.
감광성 수지 조성물에 대한 씬너 조성물의 불필요 감광막 제거 실험
8 inch 산화 실리콘 기판에 각각의 감광막 조성물을 도포한 후 본 발명에 따른 씬너 조성물과 종래 사용되던 씬너 조성물로 에지 부위의 불필요한 감광막을 제거하는 실험(Edge Bead Removing 실험 : 이하 EBR 실험이라 함)을 진행하였다. EBR 실험 또한 기판에 감광막을 도포할 때 사용한 것과 동일한 회전 피복기를 사용하였다.
표 2에 나타낸 감광성 수지 조성물의 감광막이 피복된 기판에 EBR노즐을 통해 표 1에 나타낸 씬너 조성물을 분사하여 표 3의 조건으로 에지 부분의 구형태의 감광물질을 제거 하였다. 각 씬너 조성물들은 압력계가 장치된 가압통에서 공급되며 이때의 가압 압력은 1.0 kgf이고, EBR노즐에서 나오는 씬너 조성물의 유량은 10 ∼ 20 cc/min으로 하였다.
각 감광성 수지 조성물에 대한 EBR 실험 평가는 표 4에 나타내었다.
[표 2]
감광성 수지 조성물 종류 및 막두께
구 분 | 조성물 종류 | 조성물 제품명 | 막두께(㎛) |
감광성 수지 조성물 | i-line type 포지티브형액정 디스플레이 소자용 | DPR-600D | 2.36 |
[표 3]
EBR 실험 조건
구 분 | 회전속도(rpm) | 시간(sec) |
분배(dispense) 조건 | 500 | 3 |
스핀 코팅 | 감광막 두께에 따라 조절 | |
EBR 조건 1 | 2000 | 7 |
EBR 조건 2 | 2000 | 9 |
건조 조건 | 2500 | 5 |
[표 4]
감광성 수지 조성물에 대한 EBR 실험 평가
구 분 | 실시예 1 | 실시예 2 | 실시예 3 | 비교예 1 | 비교예 2 |
감광성 수지에 대한 EBR 실험 1 조건 | ◎ | ◎ | ◎ | x | △ |
감광성 수지에 대한 EBR 실험 2 조건 | ◎ | ◎ | ◎ | x | O |
감광성 수지에 대한 EBR 끝단 잔사 유무 | 없음 | 없음 | 없음 | 없음 | 있음 |
상기 표 4에서,
평가기호 ◎는 EBR후 에지 부위의 모양이 선명한 것을 나타낸 것이며, O는 EBR후 에지 부위의 모양이 80% 이상 양호한 직선상태인 것을 나타낸 것이며, 평가기호 △는 EBR후 에지 부위의 모양이 씬너의 용해작용을 받아서 일그러진 것을 나타낸 것이며, X는 EBR후 에지 부위에 막의 테일링(tailing) 현상이 발생한 것을 나타낸 것이다.
상기 표 4에 나타난 바와 같이 본 발명에 따른 씬너 조성물들은 모든 감광막에 대하여 우수한 EBR 성능(깨끗한 에지 모양)을 나타내나, 종래의 씬너 조성물들은 감광막에 따라 현저한 차이를 보이며 대체적으로 불량한 에지 형태를 구현한다. 특히 감광막의 두께가 두꺼운 경우 종래의 씬너 조성물들은 테일링(tailing) 현상이 심하게 발생하는 것을 방지하지 못한다. 이는 추후 공정을 진행 하면서 장비 오염 등으로 반도체 소자 및 액정 디스플레이 소자류의 제조 수율을 떨어뜨리는 요인으로 작용한다.
본 발명에 의한 씬너 조성물들은 EBR의 rpm 조건을 변화시킬 경우에도 동등하게 우수한 단면 형태를 유지한다. 이는 본 발명에 의한 씬너 조성물이 특정 조건에서만 효과를 보이는 것이 아니라 다양한 조건에서 동일한 성능을 보이는 것으로, 공정 조건의 변화에 대해 종래의 씬너 조성물 보다 안정하다는 것을 의미한다.
본 발명에 의하면 대구경 기판의 EBR공정에서 기판상의 에지 부위 세정이나 기판 후면의 감광막을 세정 제거하는데 있어서 종래의 씬너 조성물들과는 차별화된 4 성분계 씬너 조성물을 사용하여 여러 종류의 감광막 조성물들을 충분히 빠르고 경제적으로 제거할 수 있도록 하여 반도체 소자 및 액정디스플레이 소자류 제조공정의 간편화 및 생산 수율을 향상시킬 수 있는 효과가 있다. 특히 액정 디스플레이 소자 제조시 씬너 조성물의 불충분한 휘발도로 인해 기판의 끝단에서 완전히 제거되지 못하고 남아 있게 되는 끝단 잔사 불량에 탁월한 효과가 있다. 또한, 본 발명에 의하면 포토리소그래피 공정에서의 불량품으로 회수되는 기판이나 공정관리를 위하여 임의로 인출한 테스트용 기판들로부터 그 표면에 부착되어 있는 감광막을 제거하여 기판을 재사용할 수 있도록 하여 기판의 재활용 및 경제적인 사용을 가능하게 하는 효과가 있다.
Claims (6)
- 반도체 소자 및 액정 디스플레이 소자 제조 공정의 세정용 씬너 조성물에 있어서,a) 프로필렌글리콜 모노알킬에테르 아세테이트;b) 씨클로 케톤;c) 폴리에틸렌옥사이드계 축합물; 및d) 플루오리네이티드 아크릴릭 코폴리머를 포함하는 세정용 씬너 조성물.
- 제 1 항에 있어서,a) 프로필렌글리콜 모노알킬에테르 아세테이트 1 내지 80 중량부;b) 씨클로 케톤 1 내지 99 중량부;c) 폴리에틸렌옥사이드계 축합물 0.001 내지 1 중량부; 및d) 플루오리네이티드 아크릴릭 코폴리머 0.001 내지 1 중량부를 포함하는 세정용 씬너 조성물.
- 제 1 항에 있어서,상기 a)의 프로필렌글리콜 모노알킬에테르 아세테이트가 프로필렌글리콜 모노메틸에테르 아세테이트, 프로필렌글리콜 모노에틸에테르 아세테이트, 프로필렌글리콜 모노프로필에테르 아세테이트, 및 프로필렌글리콜 모노부틸에테르 아세테이트로 이루어진 군으로부터 선택되는 세정용 씬너 조성물.
- 제 1 항에 있어서,상기 b)의 씨클로 케톤이 씨클로 펜타논, 씨클로 헥사논, 및 씨클로 헵타논으로 이루어진 군으로부터 선택되는 세정용 씬너 조성물.
- 제 1 항에 있어서,상기 c)의 폴리에틸렌옥사이드계 축합물은 알킬페놀과 폴리에틸렌옥사이드의 축합물인 세정용 씬너 조성물.
- 안료 감광성 수지 제거용 씬너 조성물에 있어서,a) 프로필렌글리콜 모노알킬에테르 아세테이트 1 내지 80 중량부;b) 씨클로 케톤 1 내지 99 중량부;c) 폴리에틸렌옥사이드계 축합물 0.001 내지 1 중량부; 및d) 플루오리네이티드 아크릴릭 코폴리머 0.001 내지 1 중량부를 포함하는 안료 감광성 수지 제거용 씬너 조성물.