KR20010080751A - Haz 인성의 입열 의존성이 없는 용접 구조물 용강과 그제조방법 - Google Patents
Haz 인성의 입열 의존성이 없는 용접 구조물 용강과 그제조방법 Download PDFInfo
- Publication number
- KR20010080751A KR20010080751A KR1020017007269A KR20017007269A KR20010080751A KR 20010080751 A KR20010080751 A KR 20010080751A KR 1020017007269 A KR1020017007269 A KR 1020017007269A KR 20017007269 A KR20017007269 A KR 20017007269A KR 20010080751 A KR20010080751 A KR 20010080751A
- Authority
- KR
- South Korea
- Prior art keywords
- steel
- added
- heat input
- less
- amount
- Prior art date
Abstract
Description
Claims (6)
- 질량%로,C:0.0l∼0.2%Si:0.02∼0.5%,Mn:0.3∼2%,P:0.03% 이하,S:0.0001∼0.03%,Al:0.0005∼0.05%,Ti:0.003∼0.05%,Mg:0.0001∼0.01%O:0.0001∼0.008%를 함유하고, 나머지가 철 및 불가피한 불순물로 이루어지며,입자 지름이 0·2∼5μm인 Mg 함유 산화물을 핵으로, 황화물 및 질화물의 일방이 단독으로, 또는, 양방이 복합적으로 석출된 입자가, 평균 입자 간격 30∼100μm로 강 중에 분산되고, 또는입자 지름이 0·005∼0·2μm 미만인 Mg 함유 산화물을 핵으로, 황화물 및 질화물의 일방이 단독으로, 또는, 양방이 복합적으로 석출된 입자가, 평균 입자 간격 30μm이하로 강 중에 분산되는,것을 특징으로 하는 HAZ 인성의 입열 의존성이 없는 용접 구조물용 강.
- 제 1항에 있어서,질량%로,Cu:0.05∼1.5%,Ni:0.05∼5%,Cr:0.02∼1.5%,Mo:0.02∼1.5%,V:0.01∼0.1%Nb:0.0001∼0.2%Zr:0.0001∼0.05%,Ta:0.0001∼0.05%,B:0.0003∼0.005% 중 1종류 또는 2 종류 이상을 함유하는 것을 특징으로 하는 HAZ 인성의 입열 의존성이 없는 용접 구조물용 강.
- 제 1항 또는 제 2항에 있어서질량%로,Ca:0.0005∼0.005%REM:0.0005∼0.005% 중에 1종류 또는 2종류 이상을 함유하는 것을 특징으로 하는 HAZ 인성의 입열 의존성이 없는 용접 구조물용 강.
- 제 1, 2 또는 3항 중 어느 한 항에 있어서,HAZ 조직 구오스테나이트 입경이, 용접 입열에 의하지 않고 l0∼200μm인 것을 특징으로 하는 HAZ 인성의 입열 의존성이 없는 용접 구조물용 강.
- 제 1, 2, 3항 또는 4항 중 어느 한 항에 있어서제강단계에 있어서,Si, Mn을 첨가하여 약탈산 처리를 한 후,Ti:0.003∼0.05질량%와, 소요량의 Mg를, 순차적으로 혹은 동시에 첨가하여 용존 산소량을 50ppm이하로 하고, 그 상태에서 주조, 또는, 추가적으로 Mg를, 최종 함유량으로 0.0l 질량% 이하가 되도록 첨가하여, 주조하는 것을 특징으로 하는 HAZ 인성의 입열 의존성이 없는 용접 구조물용 강의 제조 방법.
- 제 1, 2, 3항 또는 4항 중 어느 한 항에 있어서,제강단계에 있어서, Si, Mn을 첨가하여 약탈산 처리를 한 후, Ti:0.003∼0.05질량%와, 소요량의 Al, Ca, Mg를, 순차적으로 혹은 동시에 첨가하여 용존 산소량을 50ppn이하로 하고, 그 상태에서 주조, 혹은, 추가적으로 Mg를, 최종 함유량으로 0.01질량% 이하가 되도록 첨가하여, 주조하는 것을 특징으로 하는 HAZ 인성의 입열 의존성이 없는 용접 구조물용 강의 제조 방법.