KR102584089B1 - 2-차원적인 코드를 갖는 차량 윈드실드 및 그 제조 방법 - Google Patents

2-차원적인 코드를 갖는 차량 윈드실드 및 그 제조 방법 Download PDF

Info

Publication number
KR102584089B1
KR102584089B1 KR1020207002913A KR20207002913A KR102584089B1 KR 102584089 B1 KR102584089 B1 KR 102584089B1 KR 1020207002913 A KR1020207002913 A KR 1020207002913A KR 20207002913 A KR20207002913 A KR 20207002913A KR 102584089 B1 KR102584089 B1 KR 102584089B1
Authority
KR
South Korea
Prior art keywords
glass
vehicle
dimensional code
enamel paint
printed
Prior art date
Application number
KR1020207002913A
Other languages
English (en)
Other versions
KR20200100584A (ko
Inventor
체 쉬
후안후안 우
Original Assignee
쌩-고벵 글래스 프랑스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 쌩-고벵 글래스 프랑스 filed Critical 쌩-고벵 글래스 프랑스
Publication of KR20200100584A publication Critical patent/KR20200100584A/ko
Application granted granted Critical
Publication of KR102584089B1 publication Critical patent/KR102584089B1/ko

Abstract

본 개시 내용은 2-차원적인 코드를 갖는 차량 윈드실드 및 그 제조 프로세스에 관한 것이다. 차량 윈드실드는 제1 유리(10), 제2 유리(20) 및 제1 유리(10)와 제2 유리(20) 사이에 제공되는 중간 필름(5)을 포함한다. 제1 유리(10)는 차량의 외부로 대면되는 제1 표면(1) 및 중간 필름(5)에 부착되는 제2 표면(2)을 포함하는 한편, 제2 유리(20)는 중간 필름(5)에 부착되는 제3 표면(3) 및 차량의 내부로 대면되는 제4 표면(4)을 포함한다. 검은색 에나멜 페인트가 제2 표면(2) 및/또는 제4 표면(4) 상에 인쇄된다. 제2 표면(2) 또는 제4 표면(4)은, 검은색 에나멜 페인트에 상응하는 위치에서 에나멜 페인트로 인쇄된 2-차원적인 코드(6)를 구비한다. 2-차원적인 코드(6)는 유리 및/또는 차량에 관한 특유의 정보를 포함한다. 본 개시 내용의 2-차원적인 코드를 갖는 차량 윈드실드는 실제 요건에 따라 다양한 효과를 달성할 수 있다. 예를 들어, 2-차원적인 코드(6)가 육안으로 보이거나 보이지 않게 만들어질 수 있고; 2-차원적인 코드(6)는 차량의 내부 또는 외부에서 스캐닝될 수 있고; 상이한 유리들이 상이한 2-차원적인 코드들을 가질 수 있다.

Description

2-차원적인 코드를 갖는 차량 윈드실드 및 그 제조 방법
본 개시 내용은 일반적으로 유리 프로세싱 분야에 관한 것이다. 더 구체적으로, 본 개시 내용은 2-차원적인 코드를 갖는 차량 윈드실드 및 그 제조 방법에 관한 것이다.
다양한 유리 제품이 다양한 산업에서 널리 적용되어 왔다. 자동차 산업에서, 사고의 경우에 유리가 파괴되는 것을 방지하고 승객이 상처 입는 것을 방지하도록 승객 안전을 개선하기 위해서, 적층형 유리가 특히 전방 윈드실드로서 이용된다. 또한, 그러한 적층형 유리는 에너지 흡수 성능 및 충격 흡수 성능을 갖는다. 합판 유리로도 알려진 적층형 유리는 2개의 유리 단편 및 그 사이에 개재된 유기질 중합체 중간 필름의 하나 이상의 층으로 구성된 일체형의 복합 유리 제품이고, 이는, 특히 높은 온도 그리고 고온 및 고압 프로세스가 조합된 예비-프레싱(pre-pressing)(또는 진공화) 프로세스에 의해서 처리된 후에, 영구적으로 부착될 수 있다. 적층형 유리를 위한 일반적인 중간 필름은 PVB(폴리비닐 부티랄)이다.
위조방지 및 정품 식별의 목적을 실현하기 위해서, 차량 윈드실드의 모서리에는 일반적으로 제조자의 라벨, 제조자의 마크, 품질 인증 마크 및 기타와 같은 정보가 인쇄되거나 샌드브래스팅 처리된다. 그러나, 이러한 방식으로 넓은 면적에 보다 많은 정보를 마킹하는 것은 어렵다. 특히 현재의 프로세스에서, 배치식(batch)으로 유리에 인쇄된 콘텐츠는 정확하게 동일할 수 밖에 없고, 그에 따라 유리의 각각의 단편은 특유의 마크에 상응할 수 없다. 무선 주파수 식별(RFID) 칩 적층 기술을 채택함으로써, 위조-방지 기능 및 보다 많은 정보의 저장이 효과적으로 달성될 수 있다. 그러나, 이는 부가적인 구성요소를 필요로 하고, 그에 따라 고가이다. 모바일 통신 기술의 개발 및 대중화로, 차량 윈드실드에 관한 정보의 등록 및 증명을 위한 보다 많은 디지털 정보를 포함하는 2-차원적인 코드를 적용하는 것이 개발 경향이 되었다.
본 개시 내용의 목적은 종래 기술에서의 전술한 문제를 해결하는 것이고, 2-차원적인 코드를 갖는 차량 윈드실드가 제공된다. 유리 및/또는 차량에 관한 특유의 정보를 기록하는 2-차원적인 코드는 실제 요건에 따라 육안으로 보이게 또는 보이지 않게 만들어질 수 있고, 그에 따라 차량 윈드실드의 외관에 미적인 영향을 미치지 않고 위조-방지 기능을 효과적으로 달성할 수 있다.
이를 위해서, 본 개시 내용의 일 양태에 따라, 2-차원적인 코드를 갖는 차량 윈드실드가 제공된다. 차량 윈드실드는 제1 유리, 제2 유리 및 제1 유리와 제2 유리 사이에 제공되는 중간 필름을 포함한다. 제1 유리는 차량의 외부로 대면되는 제1 표면 및 중간 필름에 부착되는 제2 표면을 포함하는 한편, 제2 유리는 중간 필름에 부착되는 제3 표면 및 차량의 내부로 대면되는 제4 표면을 포함한다. 검은색 에나멜 페인트가 제2 표면 및/또는 제4 표면 상에 인쇄된다. 또한, 제2 표면 또는 제4 표면은, 검은색 에나멜 페인트에 상응하는 위치에서 에나멜 페인트로 인쇄된 2-차원적인 코드를 구비한다. 2-차원적인 코드는 유리 및/또는 차량에 관한 특유의 정보를 포함한다.
전술한 기술적 개념에 따라, 본 개시 내용은 이하의 바람직한 실시예 중 임의의 하나 이상을 더 포함할 수 있다.
일부 바람직한 실시예에서, 에나멜 페인트는 검은색 에나멜 페인트 또는 은 페이스트를 포함한다.
일부 바람직한 실시예에서, 제2 표면 및/또는 제4 표면 상의 검은색 에나멜은 2-차원적인 코드를 인쇄하기 위한 에나멜 페인트와는 상이한 광택을 갖는다.
일부 바람직한 실시예에서, 상이한 차량 윈드실드들 내에 인쇄된 2-차원적인 코드들이 상이하다.
본 개시 내용의 다른 양태에 따라, 2-차원적인 코드를 갖는 차량 윈드실드를 제조하기 위한 프로세스가 제공된다. 차량 윈드실드는 제1 유리, 제2 유리 및 제1 유리와 제2 유리 사이에 제공되는 중간 필름을 포함한다. 제1 유리는 차량의 외부로 대면되는 제1 표면 및 중간 필름에 부착되는 제2 표면을 포함하는 한편, 제2 유리는 중간 필름에 부착되는 제3 표면 및 차량의 내부로 대면되는 제4 표면을 포함한다. 그러한 프로세스는 이하의 단계를 포함한다:
a. 절단되고 성형된 제1 유리 및 제2 유리를 제공하는 단계;
b. 검은색 에나멜 페인트를 제2 표면 및/또는 제4 표면 상에 인쇄하는 단계;
c. 검은색 에나멜 페인트에 상응하는 위치에서 에나멜 페인트로 2-차원적인 코드를 제2 표면 또는 제4 표면에 인쇄하는 단계로서, 2-차원적인 코드가 유리 및/또는 차량에 관한 특유의 정보를 포함하는, 단계;
d. 제1 유리 및 제2 유리를 열적-굽힘 퍼니스 내에서 몰딩하는 단계; 및
e. 마감된 제품을 얻기 위해서, 열적으로-굽혀지고 몰딩된 제1 유리와 제2 유리 사이에 중간 필름을 개재하는 단계.
일부 바람직한 실시예에서, 에나멜 페인트는 검은색 에나멜 페인트 또는 은 페이스트를 포함한다.
일부 바람직한 실시예에서, 제2 표면 및/또는 제4 표면 상의 검은색 에나멜 페인트는 2-차원적인 코드를 인쇄하기 위한 에나멜 페인트와는 상이한 광택을 갖는다.
일부 바람직한 실시예에서, 단계 d에 앞서서, 제1 유리 및/또는 제2 유리를 예비-소결하는 단계를 더 포함한다.
일부 바람직한 실시예에서, 단계 c에서, 상이한 2-차원적인 코드들이 상이한 차량 윈드실드들에 인쇄된다.
본 개시 내용의 2-차원적인 코드를 갖는 차량 윈드실드를 채택함으로써, 실제 요건에 따라 육안에 보이거나 보이지 않는 것으로서, 2-차원적인 코드의 외관 효과가 실현될 수 있다. 또한, 상이한 2-차원적인 코드들이 상이한 차량 윈드실드들에 인쇄될 수 있다. 지능형 식별 장치(예를 들어, 모바일 전화기)와의 상호작용에 의해서, 2-차원적인 코드는 유리 및/또는 차량에 관한 특유 정보의 위조-방지 및 인증뿐만 아니라, 비제한적으로: 제품 추적, 품질 제어, 네트워크 문의, 및 전자 지불 등을 포함하는, 다른 적용예를 실현할 수 있다. 또한, 그러한 해결책은, 유리 재료 자체의 광 반사 특성으로 인한 2-차원적인 코드 식별 스캐너의 식별 오류를 방지할 수 있다.
첨부 도면을 참조하여 구체적으로 설명된 이하의 바람직한 실시예로부터, 본 개시 내용의 다른 특징 및 장점이 보다 잘 이해될 것이다.
도 1은 본 개시 내용의 바람직한 실시예에 따른 차량 윈드실드의 개략도로서, 여기에서 2-차원적인 코드는 제2 유리의 제4 표면 상에 형성된다.
도 2는 본 개시 내용의 다른 바람직한 실시예에 따른 차량 윈드실드의 개략도로서, 여기에서 2-차원적인 코드는 제1 유리의 제2 표면 상에 형성된다.
구현예 및 실시예의 용도를 이하에서 구체적으로 설명할 것이다. 그러나, 본원에서 설명된 구체적인 실시예는, 본 개시 내용의 범위를 제한하지 않고 본 개시 내용의 구현 및 용도를 단순히 구체적인 방식으로 예시하는 것이라는 것을 이해하여야 한다. 본원에서 사용된 "외부" 및 "내부"는 차량 본체에 대한 방향이다. "외부"는 차량 본체로부터 멀어지는 방향을 지칭하고, "내부"는 차량 본체에 대면되는 방향을 지칭한다.
본원에서, 에나멜로도 알려진 "에나멜 페인트"는 안료 및 보조 작용제 등이 첨가된 기본 재료로서 작용하는 바니시를 연마하는 것에 의해서 제조된다. 에나멜 페인트를 도포한 후에 형성된 페인트 필름은 경질이고, 편평하며 매끄럽고, 에나멜 채색 페인트와 유사한 외관을 갖는다. 페놀 알데히드 에나멜 및 알키드 에나멜의, 주로 2가지 유형의 에나멜이 있고, 이는 양호한 광택, 내기후성, 방수성, 강한 접착력을 가지고, 큰 기후 변화를 견딜 수 있다. 차량 윈드실드(특히, 전방 윈드실드)에 적용될 때, 에나멜 페인트는 또한 창 잉크로서 지칭된다. 이는 주로 유리 분말 및 안료(대부분 검은색)를 포함하고, 분산제로서 적은 양의 유기 용매를 포함한다. 에나멜 페인트는 전형적으로, 인쇄된 패턴 및 상표와 같은, 검은색 인쇄 경계를 형성하기 위해서 윈드실드 상으로 인쇄되도록 사용되고, 태양광 또는 자외선광에 대한 보호를 제공한다. "차량 윈드실드"는 제1 유리, 제2 유리 및 제1 유리와 제2 유리 사이에 제공되는 중간 필름을 포함하는 적층형 유리를 지칭한다. 도 1 및 도 2에 도시된 바와 같이, 제1 유리(10)는, 차량의 외부로 대면되는 제1 표면(1) 및 중간 필름(5)에 부착되는 제2 표면(2)을 가지는 외부 유리로서 지칭될 수 있다. 제2 유리(20)는, 중간 필름(5)에 부착된 제3 표면(3) 및 차량의 내부로 대면되는 제4 표면(4)을 갖는 내부 유리로서 지칭될 수 있다.
본 개시 내용의 개념에 따라, 검은색 에나멜 페인트가 제2 표면(2) 및/또는 제4 표면(4) 상에 인쇄되어 검은색 인쇄 경계를 형성하고, 2-차원적인 코드(6)가 에나멜 페인트로 검은색 에나멜 페인트에 상응하는 위치에서 제2 표면(2) 상에 또는 제4 표면(4) 상에 인쇄된다. 2-차원적인 코드는 유리 및/또는 차량에 관한 특유의 정보를 포함한다. 예를 들어, 유리에 관한 정보는 제조자, 제조자의 마크, 제조 일자, 유리의 종류, 및 품질 인증 마크 등과 같은 정보를 포함할 수 있다. 차량에 관한 정보는 차량 브랜드 마크 등과 같은 차량 식별 정보를 포함할 수 있다.
이하에서, 실시예를 참조하여, 본 개시 내용에 따른 2-차원적인 코드를 갖는 차량 윈드실드 및 그 제조 프로세스를 구체적으로 설명할 것이다.
도 1에 도시된 실시예를 참조하면, 이러한 실시예에서, 2-차원적인 코드(6)는 제2 유리(20)의 제4 표면(4) 상에 인쇄되고, 검은색 에나멜 페인트는 통상적인 스크린 인쇄에 의해서 제1 유리(10)의 제2 표면(2) 상에 인쇄된다. 동일한 배치(batch)로부터의 유리는 스크린 인쇄에 의해서 인쇄된 동일한 검은색 에나멜 페인트를 갖는다.
일부 실시예에서, 상이한 유리에 대해서, 상이한 2-차원적인 코드(6)가 잉크-젯 인쇄에 의해서 또한 검은색 에나멜 페인트로 제4 표면(4) 상에 인쇄된다. 잉크-젯 인쇄기가 비교적 느린 인쇄 속력을 가지는 반면 비교적 높은 해상도 비율을 가지고, 그에 따라 이는 작은 면적 상에서의 고-정밀 2-차원적인 코드 인쇄를 잘 실현할 수 있다. 또한, 에나멜 페인트로 2-차원적인 코드를 인쇄함으로써, 2-차원적인 코드는 차량의 총 수명 전체를 통해서 영구적으로 부착될 수 있고 마모 또는 변화가 방지될 수 있다. 특히, 이러한 방식으로, 2-차원적인 코드가 차량의 내측에서 스캐닝될 수 있고 차량의 외부로부터 보이지 않으며, 그에 따라 2-차원적인 코드의 위치는 전문가만이 알 수 있다. 따라서, 윈드실드의 위조-방지 증명 기능이 신뢰 가능하게 실현되고, 윈드실드의 미적 외관이 또한 보장된다.
일부 실시예에서, 검은색 에나멜 페인트는 또한 통상적인 스크린 인쇄에 의해서 제2 유리(20)의 제4 표면(4) 상에 선택적으로 인쇄될 수 있다. 이러한 실시예에서, 제4 표면(4) 상의 2-차원적인 코드(6)는 차량의 외부에서 보일 수 있거나 보이지 않을 수 있다.
보이지 않는 2-차원적인 코드의 경우에, 예를 들어, 검은색 에나멜 페인트가 제2 표면(2) 및 제4 표면(4) 모두에 인쇄되거나 검은색 에나멜 페인트가 제2 표면(2) 상에 인쇄되고, 2-차원적인 코드는, 제2 표면(2) 상의 검은색 에나멜 페인트와는 상이한 광택을 가지는 검은색 에나멜 페인트로, 제4 표면(4) 상에 인쇄될 수 있다. 예를 들어, 더 밝은 Ferro 14501 및 더 어두운 JM1T505가 각각 사용된다.
보일 수 있는 2-차원적인 코드의 경우에, 예를 들어 검은색 에나멜 페인트가 제4 표면(4) 상에만 인쇄되고, 제4 표면(4) 상의 2-차원적인 코드(6)는 은 페이스트로 인쇄되어 큰 콘트라스트 및 가시적 코드를 획득한다. 그에 의해서, 제4 표면(4) 상의 2-차원적인 코드는 차량 내측 또는 차량 외측에서 육안으로 분명하게 볼 수 있고, 그에 따라 2-차원적인 코드에 포함된 정보가 2-차원적인 코드 식별 스캐너에 의해서 스캐닝 및 식별될 수 있다.
2-차원적인 코드(6)가 제4 표면(4) 상에 인쇄되는 실시예에서, 윈드실드를 제조하기 위한 프로세스가 이하의 단계에 의해서 실시될 수 있다:
첫 번째로, 절단되고 성형된 제1 유리(10) 및 제2 유리(20)가 제공될 것이고, 제1 유리 및 제2 유리는 이러한 순간에 편평한 유리이다.
다음에, 검은색 에나멜 페인트가 제1 유리(10)의 제2 표면(2) 및/또는 제2 유리(20)의 제4 표면(4) 상에 스크린 인쇄에 의해서 인쇄된다. 여기에서, 검은색 에나멜 페인트의 응고 그리고 유리의 성능 및 안정성 개선을 촉진하기 위해서, 검은색 에나멜 페인트가 인쇄된 제2 표면(2) 및/또는 제4 표면(4)을 예비-소결하는 단계가 바람직하게 포함된다.
이어서, 검은색 에나멜 페인트 또는 은 페이스트가 잉크-젯 인쇄에 의해서 제2 유리(20)의 제4 표면(4) 상에 인쇄되어 2-차원적인 코드(6)를 형성한다.
다음에, 제1 유리(10) 및 제2 유리(20)가 열적-굽힘 퍼니스 내로 공급되고, 고온 및 고압 몰딩에 의해서, 요구되는 윈드실드 곡률을 갖도록 몰딩되고, 그에 따라 2-차원적인 코드가 소결 및 응고된다.
마지막으로, 개재 단계가 실시된다. 유리의 2개의 층이 함께 단단히 부착되어 마감된 윈드실드가 얻어지도록, PVB와 같은, 투명 접착성 중간 필름이, 열-굽힘 및 몰딩된 제1 유리(10)와 제2 유리(20) 사이에 개재된다. 여기에서, 소위 "마감된 윈드실드"는 직접적으로 사용될 수 있는 윈드실드를 지칭하지 않는다는 것을 이해하여야 한다. 통상적인 제조 프로세스는 후속 단계, 예를 들어 유리 중간층을 진공처리하는 단계 및 고온 퍼니스에 의해서 가열하는 단계 등을 더 포함할 수 있고, 그에 따라, 양호한 단열 성능, 큰 투과도 및 방폭 등과 같은, 우수한 성능을 갖는 차량 윈드실드를 형성할 수 있다.
차량 외부로부터 스캐닝하는 것 및 식별하는 것이 필요할 때, 2-차원적인 코드(6)가 또한, 도 2에 도시된 실시예에서와 같이, 제1 유리(10)의 제2 표면(2) 상에 인쇄될 수 있다. 한편, 또한 통상적인 스크린 인쇄에 의해서 검은색 인쇄 경계를 형성하기 위해서, 검은색 에나멜 페인트가 제2 표면(2) 및/또는 제4 표면(4) 상에 인쇄된다.
일부 실시예에서, 2-차원적인 코드(6)는 잉크-젯 인쇄에 의해서 검은색 에나멜 페인트 또는 은 페이스트로 제2 표면(2) 상으로 인쇄된다. 검은색 에나멜 페인트가 채택된 실시예에서, 2-차원적인 코드는 또한, 검은색 인쇄 경계 내로 형성되는 검은색 에나멜 페인트와는 상이한 광택을 가지는 에나멜 페인트로 인쇄될 수 있다. 따라서, 전문가는, 차량 외측에서 식별 스캐너를 이용함으로써, 2-차원적인 코드를 식별할 수 있다. 그 이외에도, 2-차원적인 코드가 윈드실드의 중간층 내측에 형성되기 때문에, 2-차원적인 코드는 윈드실드가 손상되지 않고 유지되는 한 제거 또는 변경될 수 없고, 그에 따라 위조-방지 기능을 더 개선한다.
2-차원적인 코드(6)가 제2 표면(2) 상에 인쇄되는 실시예에서, 윈드실드를 제조하기 위한 프로세스는 전술한 바와 같이 제4 표면(4) 상에 2-차원적인 코드를 형성하기 위한 프로세스와 실질적으로 유사하고, 차이점은 이하와 같다:
검은색 에나멜 페인트가 제1 유리(10)의 제2 표면(2) 및/또는 제2 유리(20)의 제4 표면(4) 상에 스크린 인쇄에 의해서 인쇄된 후에, 제2 표면(2) 및/또는 제4 표면(4)이 예비-소결될 수 있다. 그 후에, 검은색 에나멜 페인트 또는 은 페이스트가, 잉크-젯 인쇄에 의해서, 소결 및 응고된 제2 표면(2) 상에 인쇄되어 2-차원적인 코드(6)를 형성한다. 이어서, 열-굽힘 몰딩 프로세스 및 개재 프로세스가 제1 유리(10) 및 제2 유리(20) 상에서 실시되어 마감된 윈드실드를 형성한다.
본 개시 내용에 따른 2-차원적인 코드를 갖는 차량 윈드실드를 채택함으로써, 유리 및/또는 차량에 관한 정보를 포함하는 2-차원적인 코드가, 일상적인 사용 중의 긁힘으로 인해서 마모되는 것 또는 악의적으로 손상되는 것으로부터 보호될 수 있고, 그에 의해서 위조-방지 기능을 보장할 수 있다. 그 이외에, 다양한 외관 효과 및 기능이 실제의 요건에 따라 실현될 수 있다. 예를 들어, 2-차원적인 코드가 육안으로 보이거나 보이지 않게 만들어질 수 있고; 2-차원적인 코드는 차량의 내부 또는 외부에서 스캐닝될 수 있고; 상이한 유리들이 상이한 2-차원적인 코드들을 가질 수 있다. 전술한 실시예에서 예시된 에나멜 페인트의 색채 또는 유형이 비제한적인 예로서 제공된다. 본 개시 내용의 사상 및 범위로부터 벗어나지 않고도, 임의의 다른 색채 또는 유형이 구현될 수 있다. 또한, 비록 2-차원적인 코드가 윈드실드의 검은색 인쇄 경계 상의 임의의 곳에 형성될 수 있지만, 전문가에 의한 관찰 및 스캐닝 식별을 돕기 위해서, 2-차원적인 코드가 유리의 모서리에 형성되는 것이 바람직하다는 것을 또한 이해하여야 한다.
본 개시 내용의 기술적 내용 및 기술적 특징을 전술하였다. 그러나, 당업자가 본 개시 내용의 발명적 아이디어 하의 전술한 개념에 대한 다양한 변경 및 개선을 할 수 있다는 것, 그리고 그러한 모든 변경 및 개선이 본 개시 내용의 보호 범위에 포함된다는 것을 이해하여야 한다. 전술한 실시예에 관한 설명은 예시적인 것이고 제한적인 것이 아니며, 본 개시 내용의 보호 범위는 청구범위에 의해서 결정된다.

Claims (9)

  1. 2-차원적인 코드를 갖는 차량 윈드실드로서,
    차량 윈드실드는 제1 유리, 제2 유리, 및 제1 유리와 제2 유리 사이에 제공되는 중간 필름을 포함하며,
    제1 유리는 차량의 외부에 대면하는 제1 표면과, 중간 필름에 부착되는 제2 표면을 포함하고, 제2 유리는 중간 필름에 부착되는 제3 표면과, 차량의 내부에 대면하는 제4 표면을 포함하며,
    검은색 에나멜 페인트가 제2 표면 상에, 또는 제4 표면 상에, 또는 제2 표면 및 제4 표면 상에 인쇄되고, 제2 표면 또는 제4 표면은 검은색 에나멜 페인트에 상응하는 위치에서 에나멜 페인트로 인쇄된 2-차원적인 코드를 구비하며, 2-차원적인 코드는 유리에 관한, 또는 차량에 관한, 또는 유리 및 차량에 관한 특유의 정보를 포함하고,
    에나멜 페인트는 은 페이스트를 포함하는, 차량 윈드실드.
  2. 제1항에 있어서, 제2 표면 상의, 또는 제4 표면 상의, 또는 제2 표면 및 제4 표면 상의 검은색 에나멜 페인트는 2-차원적인 코드를 인쇄하기 위한 에나멜 페인트와는 상이한 광택을 가지는, 차량 윈드실드.
  3. 제1항 또는 제2항에 있어서, 상이한 차량 윈드실드들 내에 인쇄된 2-차원적인 코드들이 상이한, 차량 윈드실드.
  4. 2-차원적인 코드를 갖는 차량 윈드실드를 제조하기 위한 방법으로서,
    차량 윈드실드는 제1 유리, 제2 유리, 및 제1 유리와 제2 유리 사이에 제공되는 중간 필름을 포함하며,
    제1 유리는 차량의 외부에 대면하는 제1 표면과, 중간 필름에 부착되는 제2 표면을 포함하고, 제2 유리는 중간 필름에 부착되는 제3 표면과, 차량의 내부에 대면하는 제4 표면을 포함하며, 상기 방법은,
    a. 절단되고 성형된 제1 유리 및 제2 유리를 제공하는 단계;
    b. 검은색 에나멜 페인트를 제2 표면 상에, 또는 제4 표면 상에, 또는 제2 표면 및 제4 표면 상에 인쇄하는 단계;
    c. 검은색 에나멜 페인트에 상응하는 위치에서 에나멜 페인트로 2-차원적인 코드를 제2 표면 또는 제4 표면에 인쇄하는 단계로서, 2-차원적인 코드는 유리에 관한, 또는 차량에 관한, 또는 유리 및 차량에 관한 특유의 정보를 포함하고, 에나멜 페인트는 은 페이스트를 포함하는, 단계;
    d. 제1 유리 및 제2 유리를 열적-굽힘 퍼니스 내에서 몰딩하는 단계; 및
    e. 마감된 제품을 얻기 위해서, 열적으로-굽혀지고 몰딩된 제1 유리와 제2 유리 사이에 중간 필름을 개재하는 단계를 포함하는, 방법.
  5. 제4항에 있어서, 제2 표면 상의, 또는 제4 표면 상의, 또는 제2 표면 및 제4 표면 상의 검은색 에나멜 페인트는 2-차원적인 코드를 인쇄하기 위한 에나멜 페인트와는 상이한 광택을 가지는, 방법.
  6. 제4항 또는 제5항에 있어서, 단계 d에 앞서서, 제1 유리, 또는 제2 유리, 또는 제1 유리 및 제2 유리를 예비-소결하는 단계를 더 포함하는, 방법.
  7. 제6항에 있어서, 단계 c에서, 상이한 2-차원적인 코드들이 상이한 차량 윈드실드들에 인쇄되는, 방법.
  8. 삭제
  9. 삭제
KR1020207002913A 2017-12-29 2018-12-25 2-차원적인 코드를 갖는 차량 윈드실드 및 그 제조 방법 KR102584089B1 (ko)