KR100937123B1 - 방향성 전기 강판 및 그 제조 방법 - Google Patents
방향성 전기 강판 및 그 제조 방법 Download PDFInfo
- Publication number
- KR100937123B1 KR100937123B1 KR1020077009327A KR20077009327A KR100937123B1 KR 100937123 B1 KR100937123 B1 KR 100937123B1 KR 1020077009327 A KR1020077009327 A KR 1020077009327A KR 20077009327 A KR20077009327 A KR 20077009327A KR 100937123 B1 KR100937123 B1 KR 100937123B1
- Authority
- KR
- South Korea
- Prior art keywords
- less
- steel sheet
- grain
- ppm
- oriented electrical
- Prior art date
Abstract
Description
Claims (9)
- 인히비터리스법으로 제조한 방향성 전기 강판으로서, 질량% 로,Si : 2.0% 이상, 4.5% 이하, Mn : 0.01% 이상, 0.5% 이하를 함유하고,Ca, Mg, 또는 Ca 및 Mg 를 함유하는 산화물 중, 직경이 1 ∼ 3㎛ 인 것이, 압연 직각 방향 단면에 있어서의 단위 면적 : 1㎠ 당 400 개 이하인 방향성 전기 강판.
- 제 1 항에 있어서,상기 Ca, Mg, 또는 Ca 및 Mg 를 함유하는 산화물 중, 직경이 1 ∼ 3㎛ 인 것이, 압연 직각 방향 단면에 있어서의 단위 면적 : 1㎠ 당 150 개 이하인 방향성 전기 강판.
- 제 1 항 또는 제 2 항에 있어서,강판이, 추가로 질량% 로,Ni : 0.005 ∼ 1.50%, Sn : 0.01 ∼ 0.50%,Sb : 0.005 ∼ 0.50%, Cu : 0.01 ∼ 0.50%,Mo : 0.01 ∼ 0.50%, P : 0.0050 ∼ 0.50% 및Cr : 0.01 ∼ 1.50%중에서 선택된 1 종 또는 2 종 이상을 함유하는 조성이 되는 것을 특징으로 하는 방향성 전기 강판.
- 포스테라이트질 피막 (forsterite film) 을 갖는 방향성 전기 강판으로서,질량% 로, Si : 2.0% 이상, 4.5% 이하, Mn : 0.01% 이상, 0.5% 이하를 함유하고,그 포스테라이트질 피막을 포함하는 강판 중의 불순물이 Al : 50ppm 이하, Se : 30ppm 이하, N : 50ppm 이하, 및 B : 2ppm 이하로 저감되고, 또한 지철 중의 O 가 20ppm 이하로 저감되고,Ca, Mg, 또는 Ca 및 Mg 를 함유하는 산화물 중, 직경이 1 ∼ 3㎛ 인 것이, 압연 직각 방향 단면에 있어서의 단위 면적 : 1㎠ 당 400 개 이하인 것을 특징으로 하는 방향성 전기 강판.
- 제 4 항에 있어서,상기 Ca, Mg, 또는 Ca 및 Mg 를 함유하는 산화물 중, 직경이 1 ∼ 3㎛ 인 것이, 압연 직각 방향 단면에 있어서의 단위 면적 : 1㎠ 당 150 개 이하인 방향성 전기 강판.
- 제 4 항 또는 제 5 항에 있어서,강판이, 추가로 질량% 로,Ni : 0.005 ∼ 1.50%, Sn : 0.01 ∼ 0.50%,Sb : 0.005 ∼ 0.50%, Cu : 0.01 ∼ 0.50%,Mo : 0.01 ∼ 0.50%, P : 0.0050 ∼ 0.50% 및Cr : 0.01 ∼ 1.50%중에서 선택된 1 종 또는 2 종 이상을 함유하는 조성이 되는 것을 특징으로 하는 방향성 전기 강판.
- 질량% 로, Si : 2.0% 이상, 4.5% 이하, Mn : 0.01% 이상, 0.5% 이하를 함유하고, 또한, Al : 100ppm 미만, S, Se, O 및 N : 각 50ppm 이하로 억제한 조성인 강 슬래브를 열간 압연하여 열연 강판으로 하고,그 열연 강판을 냉간 압연하여 냉연 강판으로 하고,그 냉연 강판에 1 차 재결정 소둔 및 2 차 재결정 소둔을 실시함과 함께,상기 열연 강판에 있어서의 Ca, Mg, 또는 Ca 및 Mg 를 함유하는 산화물 중, 직경이 1 ∼ 3㎛ 인 것을, 압연 직각 방향 단면에 있어서의 단위 면적 : 1㎠ 당 400 개 이하로 제어하는 방향성 전기 강판의 제조 방법.
- 제 7 항에 있어서,강 슬래브의 조성에 있어서, 추가로 B 를 5ppm 미만으로 억제한 방향성 전기 강판의 제조 방법.
- 제 7 항 또는 제 8 항에 있어서,상기 열연 강판에 있어서, 상기 Ca, Mg, 또는 Ca 및 Mg 를 함유하는 산화물 중, 직경이 1 ∼ 3㎛ 인 것을, 압연 직각 방향 단면에 있어서의 단위 면적 : 1㎠ 당 150 개 이하로 하는 방향성 전기 강판.