KR100815051B1 - 탄산세륨 나노 분말의 제조방법 - Google Patents
탄산세륨 나노 분말의 제조방법 Download PDFInfo
- Publication number
- KR100815051B1 KR100815051B1 KR1020050054020A KR20050054020A KR100815051B1 KR 100815051 B1 KR100815051 B1 KR 100815051B1 KR 1020050054020 A KR1020050054020 A KR 1020050054020A KR 20050054020 A KR20050054020 A KR 20050054020A KR 100815051 B1 KR100815051 B1 KR 100815051B1
- Authority
- KR
- South Korea
- Prior art keywords
- cerium
- carbonate
- cerium carbonate
- water
- organic solvent
- Prior art date
Abstract
Description
구분 | 평균입경 | 입자형태 | 입자구조 |
실시예 1 | 100 ㎚∼10 ㎛ | rod 형태 | Ce2O(CO3)2H2O |
실시예 2 | 10 ㎚∼1 ㎛ | rod 형태 | Ce2O(CO3)2H2O |
실시예 3 | 200 ㎚∼2 ㎛ | rod 형태 | Ce2O(CO3)2H2O |
실시예 4 | 50 ㎚∼300 ㎚ | 구형 | Ce(CO3)OH |
실시예 5 | 200 ㎚∼2 ㎛ | 각진 구형 | Ce2O(CO3)2H2O |
실시예 6 | 500 ㎚∼10 ㎛ | rod 형태 + 구형 | Ce2O(CO3)2H2O |
실시예 7 | 500 ㎚∼5 ㎛ | rod 형태 | Ce2O(CO3)2H2O |
비교예 1 | 100 ㎚∼1 ㎛ | 각진 구형 | Ce(CO3)OH |
Claims (10)
- 탄산세륨 나노 분말의 제조방법에 있어서, 물과 유기용매의 혼합용매 하에서 세륨염을 카보네이트 반응체와 침전반응시키는 단계를 포함하며,상기 세륨염이 세륨 나이트레이트 또는 세륨 아세테이트이고, 상기 카보네이트 반응체는 요소이고, 상기 유기용매가 알코올계 유기용매이며, 얻어지는 상기 탄산세륨 분말은 Ce2O(CO3)2의 수화물 형태이고, 상기 침전반응이 20 내지 100 ℃의 온도에서 실시되는 것임을 특징으로 하는 탄산세륨 나노 분말의 제조방법.
- 삭제
- 삭제
- 제1항에 있어서,상기 세륨염과 카보네이트 반응체가 1 : 1 내지 20 : 1의 몰비로 혼합하여 반응하는 것을 특징으로 하는 탄산세륨 나노 분말의 제조방법.
- 삭제
- 제1항에 있어서,상기 알코올계 유기용매가 에탄올, 프로판올, 또는 부탄올인 것을 특징으로 하는 탄산세륨 나노 분말의 제조방법.
- 제1항에 있어서,상기 혼합용매가 물 : 알코올계 유기용매 = 1 : 0.1 내지 1 : 10의 중량비로 혼합하여 사용되는 것을 특징으로 하는 탄산세륨 나노 분말의 제조방법.
- 제1항에 있어서,물과 알코올계 유기용매의 상기 혼합용매가 세륨염에 대하여 중량을 기준으로 1 : 1 내지 20 : 1의 비율로 혼합되는 것을 특징으로 하는 탄산세륨 나노 분말의 제조방법.
- 삭제
- 제1항에 있어서,상기 탄산세륨 나노 분말의 평균입경이 200 ㎚ 내지 10 ㎛인 것을 특징으로 하는 탄산세륨 나노 분말의 제조방법.