JPWO2019065878A1 - ハードコートフィルム - Google Patents
ハードコートフィルム Download PDFInfo
- Publication number
- JPWO2019065878A1 JPWO2019065878A1 JP2019545624A JP2019545624A JPWO2019065878A1 JP WO2019065878 A1 JPWO2019065878 A1 JP WO2019065878A1 JP 2019545624 A JP2019545624 A JP 2019545624A JP 2019545624 A JP2019545624 A JP 2019545624A JP WO2019065878 A1 JPWO2019065878 A1 JP WO2019065878A1
- Authority
- JP
- Japan
- Prior art keywords
- hard coat
- film
- coat layer
- peak area
- curable resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
(1)基材フィルムの少なくとも片面に、電離放射線硬化型樹脂を含有するハードコート層を設けたハードコートフィルムであって、該電離放射線硬化型樹脂が下記条件(I)を満たすことを特徴とするハードコートフィルム。
条件(I):ピーク面積比1(A/C×100)が5%以上
(但し、未硬化の電離放射線硬化型樹脂の赤外分光スペクトル測定で3250〜3500cm−1に現れるピーク面積をAとし、1650〜1800cm−1に現れるピーク面積をCとする。)
(2)前記電離放射線硬化型樹脂が、さらに下記条件(II)を満たすことを特徴とする(1)に記載のハードコートフィルム。
条件(II):ピーク面積比2(B/C×100)が5%以上
(但し、未硬化の電離放射線硬化型樹脂の赤外分光スペクトル測定で1500〜1580cm−1に現れるピーク面積をBとし、1650〜1800cm−1に現れるピーク面積をCとする。)
(3)前記ハードコート層が、下記条件(III)を、さらに満たすことを特徴とする(1)〜(2)いずれかに記載のハードコートフィルム。
条件(III):ピーク面積比3(D/E×100)が400%未満
(但し、硬化後のハードコート層の赤外分光スペクトル測定で、855〜1325cm−1に現れるピーク面積をDとし、1650〜1800cm−1に現れるピーク面積をEとする。)
(4)前記電離放射線硬化型樹脂は、(メタ)アクリロイル基を含むアクリル系樹脂を含むことを特徴とする(1)〜(3)のいずれかに記載のハードコートフィルム。
(5)前記基材フィルムは、シクロオレフィンフィルム、ポリエチレンテレフタレート、ポリエチレンナフタレートから選ばれるいずれかであることを特徴とする(1)〜(4)のいずれかに記載のハードコートフィルム。
本発明は、基材フィルムの少なくとも片面に、電離放射線硬化型樹脂を含有するハードコート層を設けたハードコートフィルムであって、該電離放射線硬化型樹脂が下記条件(I)を満たすことを特徴とするハードコートフィルムである。
条件(I):ピーク面積比1(A/C×100)が5%以上
(但し、未硬化の電離放射線硬化型樹脂の赤外分光スペクトル測定で3250〜3500cm−1に現れるピーク面積をAとし、1650〜1800cm−1に現れるピーク面積をCとする。)
まず、ハードコートフィルムの基材フィルムについて説明する。
次に、上記ハードコート層について説明する。
硬化後のハードコート層で1650〜1800cm−1に現れる赤外分光スペクトルのピークは、上述される電離放射線硬化型樹脂で現れるピークと同等であると想定される。
また、本発明においては、硬化後のハードコート層で、855〜1325cm−1に現れる赤外分光スペクトルのピークは、エーテル基やエステル基の炭素−酸素伸縮振動や、カルボニル基の炭素−水素変角振動、及び無機微粒子であるシリカ骨格、酸化アルミニウム骨格など、様々な構造に由来している。アクリロイル基の存在割合に対し、一定割合以下の855〜1325cm−1に現れるピークとすることで、基材フィルムに対する密着性とのバランスをとることができると推察される。
ウレタンアクリレート系紫外線硬化型樹脂「TOMAX FA-3312−2」(固形分40%、日本化工塗料株式会社製)を主剤とし、酢酸ブチルで紫外線硬化型樹脂の塗料中の固形分濃度が30%となるまで希釈し十分攪拌してハードコート層塗料1を調製した。
上記ウレタンアクリレート系紫外線硬化型樹脂「TOMAX FA−3312−2」(固形分40%、日本化工塗料株式会社製)とウレタンアクリレート系紫外線硬化型樹脂「A−9550」(固形分100%、新中村化学株式会社製)を主剤として、TOMAX FA−3312−2とA−9550の固形分配合比が80/20となるように配合し、酢酸ブチルで紫外線硬化型樹脂の塗料中の固形分濃度が30%となるまで希釈し十分攪拌してハードコート層塗料2を調製した。
製造例2のTOMAX FA−3312−2とA−9550の固形分配合比を75/25とした以外は製造例2と同様にしてハードコート層塗料3を得た。
製造例2のTOMAX FA−3312−2とA−9550の固形分配合比を50/50とした以外は製造例2と同様にしてハードコート層塗料4を得た。
製造例1のTOMAX FA−3312−2をTOMAX FA−3312−4とした以外は製造例1と同様にしてハードコート層塗料5を得た。
製造例2のTOMAX FA−3312−2とA−9550の固形分配合比を30/70とした以外は製造例2と同様にしてハードコート層塗料6を得た。
製造例2のTOMAX FA−3312−2とA−9550の固形分配合比を10/90とした以外は製造例2と同様にしてハードコート層塗料7を得た。
製造例1のハードコート層に用いた「TOMAX FA−3312−2」の代わりにウレタンアクリレート系紫外線硬化型樹脂「A−9550」(固形分100%、新中村化学株式会社製)を用いたこと以外は、製造例1と同様にしてハードコート層塗料8を得た。
製造例1のハードコート層に用いた「TOMAX FA−3312−2」の代わりにウレタンアクリレート系紫外線硬化型樹脂「BS-575CSB」(固形分100%、荒川化学工業株式会社製)を用いたこと以外は、製造例1と同様にしてハードコート層塗料9を得た。
参考例として、希釈溶剤として用いた酢酸ブチル100%を示す。
表2記載の組合せとなるように基材フィルム及びハードコート層塗料を選択し、各基材フィルムの片面に、上記の各ハードコート層塗料を、バーコーターを用いて塗工し、80℃の乾燥炉で1分間熱風乾燥させ、塗膜厚み2.5μmの塗工層を形成した。これを、塗工面より60mmの高さにセットされたUV照射装置を用い、UV照射量250mJ/cm2にて硬化させてハードコート層を形成し、実施例1〜13及び比較例1〜4のハードコートフィルムを得た。
得られた上記各実施例および各比較例のハードコートフィルムを下記の基準で評価した。その結果を纏めて表1に示した。
赤外分光光度計を用いて未硬化の状態の電離放射線硬化型樹脂に対するATR法により、赤外分光スペクトル(赤外吸収スペクトル)を測定した。赤外分光光度計はFT−IR Spectrometer Spectrum 100 (パーキンエルマージャパン社製)を使用した。
赤外分光光度計を用いてハードコートフィルムのハードコート層表面に対するATR法により、赤外分光スペクトル(赤外吸収スペクトル)を測定した。赤外分光光度計はFT−IR Spectrometer Spectrum 100(パーキンエルマージャパン社製)を使用した。得られた横軸を波数(cm-1)とし、縦軸を吸光度としたスペクトルチャート上において、855〜1325cm-1、1650〜1800cm-1にそれぞれベースラインを引き、このベースラインとスペクトル曲線とで囲まれる面積をそれぞれD、及びEとし、その比(D/E×100)をピーク面積比3とした。
密着性は、JIS−K5600−5−6に準じて碁盤目剥離試験を行った。ハードコートフィルムのハードコート層形成面に、カッターナイフを用いて、碁盤目状に1mm間隔で縦11本、横11本の切り込みを入れて合計100マスの正方形の升目を刻み、積水化学工業株式会社製の粘着テープNo.252をその上に貼り付け、ヘラを用いて均一に押し付け後、60度方向に剥離し、ハードコート層の残存個数を4段階評価した。同じ箇所で5回、圧着・剥離を行った後に判定を行った。評価基準は下記の通りであり、◎と○評価品を密着性は合格と判定したが、△評価品も実用上可である。
◎:100個 ○:99〜90個 △:89〜50個 ×:49〜0個
実施例、比較例で作製した各ハードコートフィルムについて、JIS−K5600−5−10に準じた試験方法にて、ハードコート層面を、スチールウール#0000を用い、荷重250g/cm2をかけ10往復摩擦し、傷のつき具合を次の基準で評価した。○評価品を耐擦傷性は良好としたが、△評価品も製品として使用可能である。
◎:傷の発生なし。○:傷が1〜5本発生する。△:傷が6〜10本発生する。×:傷が10本以上発生する。
ZF16:シクロオレフィンフィルム(厚み100μm、日本ゼオン株式会社製)
A4300:ポリエチレンテレフタレートフィルム(厚み100μm、東洋紡株式会社製)
Q65HW:ポリエチレンナフタレートフィルム(厚み100μm、帝人フィルムソリューションズ株式会社製)
Claims (5)
- 基材フィルムの少なくとも片面に、電離放射線硬化型樹脂を含有するハードコート層を設けたハードコートフィルムであって、該電離放射線硬化型樹脂が下記条件(I)を満たすことを特徴とするハードコートフィルム。
条件(I):ピーク面積比1(A/C×100)が5%以上
(但し、未硬化の電離放射線硬化型樹脂の赤外分光スペクトル測定で3250〜3500cm−1に現れるピーク面積をAとし、1650〜1800cm−1に現れるピーク面積をCとする。) - 前記電離放射線硬化型樹脂が、さらに下記条件(II)を満たすことを特徴とする請求項1に記載のハードコートフィルム。
条件(II):ピーク面積比2(B/C×100)が5%以上
(但し、未硬化の電離放射線硬化型樹脂の赤外分光スペクトル測定で1500〜1580cm−1に現れるピーク面積をBとし、1650〜1800cm−1に現れるピーク面積をCとする。) - 前記ハードコート層が、下記条件(III)を、さらに満たすことを特徴とする請求項1又は2に記載のハードコートフィルム。
条件(III):ピーク面積比3(D/E×100)が400%未満
(但し、硬化後のハードコート層の赤外分光スペクトル測定で、855〜1325cm−1に現れるピーク面積をDとし、1650〜1800cm−1に現れるピーク面積をEとする。) - 前記電離放射線硬化型樹脂は、(メタ)アクリロイル基を含むアクリル系樹脂を含むことを特徴とする請求項1乃至3のいずれかに記載のハードコートフィルム。
- 前記基材フィルムは、シクロオレフィンフィルム、ポリエチレンテレフタレート、ポリエチレンナフタレートから選ばれるいずれかであることを特徴とする請求項1乃至4のいずれかに記載のハードコートフィルム。