JPWO2018194831A5 - - Google Patents
Download PDFInfo
- Publication number
- JPWO2018194831A5 JPWO2018194831A5 JP2019555917A JP2019555917A JPWO2018194831A5 JP WO2018194831 A5 JPWO2018194831 A5 JP WO2018194831A5 JP 2019555917 A JP2019555917 A JP 2019555917A JP 2019555917 A JP2019555917 A JP 2019555917A JP WO2018194831 A5 JPWO2018194831 A5 JP WO2018194831A5
- Authority
- JP
- Japan
- Prior art keywords
- material according
- particle size
- refractory material
- porous refractory
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
本発明の実施に有用な粗骨材は、ブロック状、長方形状、繊維状、棒状、角状、球状、又は、球晶状であってもよい。セラミック球晶状物は、アルミナ、ＭｇＯ、シリカ、又は、ムライトやスピネルといった複合材料のような耐火性鉱物から形成されてもよい。球晶状物は、例えば、１ｍｍから２５ｍｍの範囲の径を有するものが市販されている。球晶状物は、均一な大きさであってもよいし、大きさに幅があってもよい。球晶状物は密であっても軽量であってもよい。転動造粒により形成された球晶状物は多孔質であり、キャベツの内部に似た葉状の内部構造を有する。これら葉状球晶状物は、不純物やスラグを保持可能であり、一定の断熱効果を付与する構造を有する。
Claims (17)
- キャベツの内部状に似た内部構造を有する多孔質球晶状物であって、最小粒子サイズ及び最大粒子サイズを有する耐火骨材部であって、前記最大粒子サイズと最小粒子サイズとの比が１０／１以下である耐火骨材部と、
カルシウムアルミネートセメント、アルミニウムホスフェート、水和性アルミナ形態のアルミナ、コロイダルシリカ形態のシリカ及びこれらの組み合わせからなる群より選ばれる第一鉄対応型耐火バインダーを含むバインダー相と、を備え、
前記耐火骨材部が、０．１ｍｍ超の粒子径を有する材料を１００重量％含み、
前記耐火骨材部及び前記バインダー相の合計重量に占める前記耐火骨材部の重量割合が８５重量％以上９８重量％以下であり、
気孔が開いている、
多孔質耐火材。 - 前記最大粒子サイズと最小粒子サイズとの比が５／１以下である、
請求項１に記載の多孔質耐火材。 - 前記最大粒子サイズと最小粒子サイズとの比が２／１以下である、
請求項１に記載の多孔質耐火材。 - 前記耐火骨材部及び前記バインダー相の合計重量に占める前記耐火骨材部の重量割合が９０重量％以上９８重量％以下である、
請求項１に記載の多孔質耐火材。 - 前記耐火バインダーがカルシウムアルミネートセメントを含むとともに、前記バインダー相がさらに（ａ）反応性アルミナ及び（ｂ）シリカを含む、
請求項４に記載の多孔質耐火材。 - 前記耐火骨材部の１００重量％が、少なくとも５．０ｍｍ径の粒子サイズを有する、
請求項１に記載の多孔質耐火材。 - 前記耐火骨材部が、アルミナ、マグネシア、ジルコニア、酸化カルシウム、シリカ、スピネル、カルシウムアルミネート類、ムライト、オリビン、フォルステライト、ジルコン、カルシウムシリケート、ＡＺＳ及びこれらの組み合わせからなる群より選ばれる材料を含む、
請求項１に記載の多孔質耐火材。 - 前記バインダー相が、反応性アルミナ、か焼アルミナ、板状アルミナ、溶融アルミナ、カーボン、ジルコニア、マグネシア、フュームドシリカ、ボーキサイト、酸化クロム及びこれらの組み合わせからなる群より選ばれる材料を含む、
請求項１に記載の多孔質耐火材。 - 耐火骨材の最小粒子のサイズと前記バインダー相における最大粒子のサイズとの比が、少なくとも１０：１である、
請求項１に記載の多孔質耐火材。 - 耐火骨材の最小粒子のサイズと前記バインダー相における最大粒子のサイズとの比が、少なくとも２：１である、
請求項１に記載の多孔質耐火材。 - 前記バインダー相の１００重量％が１００ミクロン以下のサイズを有する粒子からなる、
請求項１に記載の多孔質耐火材。 - 開気孔率が２０体積％以上６０体積％以下である、
請求項１に記載の多孔質耐火材。 - 気孔が屈曲している、
請求項１に記載の多孔質耐火材。 - 請求項１に係る第１の多孔質耐火材を含むとともに、最小骨材粒子サイズを有する、第１の層と、
請求項１に係る第２の多孔質耐火材を含むとともに、最大骨材粒子サイズを有する、第２の層と、を備え、
前記第１の層の前記最小骨材粒子サイズが、前記第２の層の前記最大骨材粒子サイズよりも大きい、
多孔質耐火材構造。 - 内側及び外側を有する冶金容器であって、前記冶金容器の前記内側に、請求項１に係る多孔質耐火材を有するライニング構造が設けられている、
冶金容器。 - 溶融金属の酸化を最小化するためのプロセスであって、
ａ）請求項１に係る多孔質耐火材を含むライニング構造を備える容器へと、溶融金属を移送すること、
ｂ）前記容器外に前記溶融金属を移送すること、
を含むプロセス。 - 前記耐火骨材部が、３．０ｍｍ以上６．０ｍｍ以下の粒子径を有する材料を１００重量％含む、
請求項１に記載の多孔質耐火材。