JPWO2015152090A1 - 非水電解質二次電池負極用炭素質材料、非水電解質二次電池用負極電極、非水電解質二次電池及び車両 - Google Patents
非水電解質二次電池負極用炭素質材料、非水電解質二次電池用負極電極、非水電解質二次電池及び車両 Download PDFInfo
- Publication number
- JPWO2015152090A1 JPWO2015152090A1 JP2016511846A JP2016511846A JPWO2015152090A1 JP WO2015152090 A1 JPWO2015152090 A1 JP WO2015152090A1 JP 2016511846 A JP2016511846 A JP 2016511846A JP 2016511846 A JP2016511846 A JP 2016511846A JP WO2015152090 A1 JPWO2015152090 A1 JP WO2015152090A1
- Authority
- JP
- Japan
- Prior art keywords
- secondary battery
- negative electrode
- electrolyte secondary
- carbonaceous material
- average particle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
また、二次電池の使用形態についても、例えば、小型携帯機器で1〜2時間であった充電時間がハイブリッド自動車用電源では、ブレーキ時のエネルギー回生を行うことを考慮すると数十秒であり、放電もアクセルを踏み込む時間を考えれば数十秒と、小型携帯向けのリチウムイオン二次電池と比較し、圧倒的に優れた急速な充放電(入出力)特性が求められている。
リチウムイオン二次電池の負極として、従来、有機材料や植物原料を炭素化して得られる炭素質材料が有用に使用されているが、上記のように車載リチウムイオン二次電池に用いられる負極用炭素質材料には、優れた充放電特性が求められており、その実現には入出力特性の向上が不可欠である。
本発明の非水電解質二次電池負極用炭素質材料は、個数平均粒子径が0.1〜2.0μmであり、個数平均粒子径を体積平均粒子径で除した値が0.3以下であり、X線回折法により定めた(002)面の平均層面間隔d002が0.340〜0.390nmであり、水素および炭素の原子比(H/C)が0.10以下であることを特徴とする。
本発明の炭素質材料は、炭素前駆体から製造されるものである。炭素前駆体として、石油ピッチ若しくはタール、石炭ピッチ若しくはタール、熱可塑性樹脂、又は熱硬化性樹脂を挙げることができる。また、熱可塑性樹脂としては、ポリアセタール、ポリアクリロニトリル、スチレン/ジビニルベンゼン共重合体、ポリイミド、ポリカーボネート、変性ポリフェニレンエーテル、ポリブチレンテレフタレート、ポリアリレート、ポリスルホン、ポリフェニレンスルフィド、フッ素樹脂、ポリアミドイミド、又はポリエーテルエーテルケトンを挙げることができる。更に、熱硬化性樹脂としては、フェノール樹脂、アミノ樹脂、不飽和ポリエステル樹脂、ジアリルフタレート樹脂、アルキド樹脂、エポキシ樹脂、ウレタン樹脂を挙げることができる。
なお、本明細書において、「炭素前駆体」は、未処理の炭素質の段階から、最終的に得られる非水電解質二次電池用炭素質材料の前段階までの炭素質を意味する。すなわち、最終工程の終了していないすべての炭素質を意味する。
炭素前駆体として、石油ピッチ若しくはタール、石炭ピッチ若しくはタール、又は熱可塑性樹脂を用いる場合、架橋処理を行う。架橋処理の方法は、特に限定されるものではないが、例えば、酸化剤を用いて行うことができる。酸化剤も特に限定されるものではないが、気体としては、O2、O3、SO3、NO2、これらを空気、窒素などで希釈した混合ガス、又は空気などの酸化性気体を用いることができる。また、液体としては、硫酸、硝酸、若しくは過酸化水素等の酸化性液体、又はそれらの混合物を用いることができる。酸化温度も、特に限定されるものではないが、好ましくは、120〜400℃であり、より好ましくは、150〜350℃である。温度が120℃未満であると、十分に架橋反応が進行せず、反応に長時間を要してしまう。また温度が400℃を超えると、架橋反応よりも分解反応のほうが多くなり、得られる炭素材料の収率が低くなる。
本発明における予備焼成工程は、炭素源を300℃以上900℃未満で焼成することによって行う。予備焼成は、揮発分、例えばCO2、CO、CH4、及びH2などと、タール分とを除去し、本焼成において、それらの発生を軽減し、焼成器の負担を軽減することができる。予備焼成温度が300℃未満であると脱タールが不十分となり、粉砕後の本焼成工程で発生するタール分やガスが多く、粒子表面に付着する可能性があり、粉砕したときの表面性を保てず電池性能の低下を引き起こすので好ましくない。予備焼成温度は300℃以上が好ましく、更に好ましくは500℃以上、特に好ましくは600℃以上である。一方、予備焼成温度が900℃以上であるとタール発生温度領域を超えることになり、使用するエネルギー効率が低下するため好ましくない。更に、発生したタールが二次分解反応を引き起こしそれらが炭素前駆体に付着し、性能の低下を引き起こすことがあるので好ましくない。また、予備焼成温度が高すぎると炭素化が進んで炭素前駆体の粒子が硬くなりすぎて、予備焼成後に粉砕を行う場合、粉砕機の内部を削り取ってしまうなど粉砕が困難になる場合があるため、好ましくない。
予備焼成は、不活性ガス雰囲気中で行い、不活性ガスとしては、窒素、又はアルゴンなどを挙げることができる。また、予備焼成は、減圧下で行うこともでき、例えば、10kPa以下で行うことができる。予備焼成の時間も特に限定されるものではないが、例えば0.5〜10時間で行うことができ、1〜5時間がより好ましい。
粉砕工程は、炭素前駆体の粒径を、均一にするために行うものである。本焼成による炭素化後に粉砕することもできる。炭素化反応が進行すると炭素前駆体が硬くなり、粉砕による粒子径分布の制御が困難になるため、粉砕工程は、予備焼成の後で本焼成の前が好ましい。
粉砕に用いる粉砕機は、特に限定されるものではなく、例えばジェットミル、ボールミル、ハンマーミル、又はロッドミルなどを使用することができる。
分級として、篩による分級、湿式分級、又は乾式分級を挙げることができる。湿式分級機としては、例えば重力分級、慣性分級、水力分級、又は遠心分級などの原理を利用した分級機を挙げることができる。また、乾式分級機としては、沈降分級、機械的分級、又は遠心分級の原理を利用した分級機を挙げることができる。
更に、粉砕機と分級機とが独立した装置を用いることもできる。この場合、粉砕と分級とを連続して行うこともできるが、粉砕と分級とを不連続に行うこともできる。
本発明における本焼成工程は、通常の本焼成の手順に従って行うことができ、本焼成を行うことにより、非水電解質二次電池負極用炭素質材料を得ることができる。本焼成の温度は、900〜1600℃である。本焼成温度が900℃未満では、炭素質材料に官能基が多く残存してH/Cの値が高くなり、リチウムとの反応により不可逆容量が増加するため好ましくない。本発明の本焼成温度の下限は900℃以上であり、より好ましくは1000℃以上であり、特に好ましくは1100℃以上である。一方、本焼成温度が1600℃を超えると炭素六角平面の選択的配向性が高まり放電容量が低下するため好ましくない。本発明の本焼成温度の上限は1600℃以下であり、より好ましくは1500℃以下であり、特に好ましくは1450℃以下である。
本焼成は、非酸化性ガス雰囲気中で行うことが好ましい。非酸化性ガスとしては、ヘリウム、窒素又はアルゴンなどを挙げることができこれらを単独或いは混合して用いることができる。更には塩素などのハロゲンガスを上記非酸化性ガスと混合したガス雰囲気中で本焼成を行うことも可能である。また、本焼成は、減圧下で行うこともでき、例えば、10kPa以下で行うことも可能である。本焼成の時間も特に限定されるものではないが、例えば0.1〜10時間で行うことができ、0.2〜8時間が好ましく、0.4〜6時間がより好ましい。
タール又はピッチからの本発明の炭素質材料の製造方法について、以下に例を挙げて説明する。
まず、タール又はピッチに対して架橋処理(不融化)を施した。この架橋処理を施したタール又はピッチは、その後の焼成で炭素化されて構造制御された炭素質材料になる。
タール又はピッチとしては、エチレン製造時に複製する石油タール又はピッチ、石炭乾留時に生成するコールタール、及びコールタールの低沸点成分を蒸留除去した重質成分又はピッチ、石炭の液化により得られるタール又はピッチなどの石油又は石炭のタール又はピッチが使用できる。また、これらのタール及びピッチの2種類以上を混合してもよい。
上述のようにして架橋処理を施した炭素前駆体を、予備焼成を行った後、非酸化性ガス雰囲気中で900℃〜1600℃で炭素化することにより、本発明の炭素質材料を得ることができる。
樹脂からの炭素質材料の製造方法について、以下に例を挙げて説明する。
本発明の炭素質材料は、樹脂を前駆体として用い、900℃〜1600℃で炭素化することによっても得ることができる。樹脂としては、フェノール樹脂又はフラン樹脂など、或いはそれらの樹脂の官能基を一部変性した熱硬化性樹脂を使用することができる。熱硬化性樹脂を必要に応じて900℃未満の温度で予備焼成したのち、粉砕し、900℃〜1600℃で炭素化することによっても得ることができる。熱硬化性樹脂の硬化促進、架橋度の促進、或いは炭素化収率の向上を目的に必要に応じて120〜400℃の温度で酸化処理を行ってもよい。酸化剤としては、O2、O3、NO2、これらを空気、窒素等で希釈した混合ガス、又は空気等の酸化性気体、あるいは硫酸、硝酸、過酸化水素水等の酸化性液体を用いることができる。
更に、ポリアクリロニトリル又はスチレン/ジビニルベンゼン共重合体などの熱可塑性樹脂に架橋処理を施した炭素前駆体を使用することもできる。これらの樹脂は、例えばラジカル重合性のビニルモノマー及び重合開始剤を混合したモノマー混合物を、分散安定剤を含有する水性分散媒体中に添加し、撹拌混合により懸濁してモノマー混合物を微細な
液滴とした後、ついで昇温することによりラジカル重合を進めて得ることができる。得られた樹脂を架橋処理により、架橋構造を発達させることにより球状の炭素前駆体とすることができる。架橋処理は、120〜400℃の温度範囲で行うことができ、特に好ましくは170℃〜350℃、更に好ましくは220〜350℃の温度範囲で行うことが好ましい。酸化剤としては、O2、O3、SO3、NO2、これらを空気、窒素等で希釈した混合ガス、又は空気等の酸化性気体、又は硫酸、硝酸、過酸化水素水等の酸化性液体を用いることができる。その後、前記のように熱に不融である炭素前駆体を、必要に応じて予備焼成を行った後、粉砕し、非酸化性ガス雰囲気中で900℃〜1600℃で炭素化することにより、本発明の炭素質材料を得ることができる。
粉砕工程は、炭素化後に行うことも出来るが、炭素化反応が進行すると炭素前駆体が硬くなるため、粉砕による粒子径分布の制御が困難になるため、粉砕工程は900℃未満の予備焼成の後で本焼成の前が好ましい。
本発明の非水電解質二次電池負極は、本発明の非水電解質二次電池負極用炭素質材料を含む。
本発明の炭素質材料を用いる負極電極は、炭素質材料に結合剤(バインダー)を添加し適当な溶媒を適量添加、混練し、電極合剤とした後に、金属板などからなる集電板に塗布・乾燥後、加圧成形することにより製造することができる。本発明の炭素質材料を用いることにより特に導電助剤を添加しなくとも高い導電性を有する電極を製造することができるが、更に高い導電性を賦与することを目的に必要に応じて電極合剤を調製時に、導電助剤を添加することができる。導電助剤としては、導電性のカーボンブラック、気相成長炭素繊維(VGCF)、ナノチューブなどを用いることができ、添加量は使用する導電助剤の種類によっても異なるが、添加する量が少なすぎると期待する導電性が得られないので好ましくなく、多すぎると電極合剤中の分散が悪くなるので好ましくない。このような観点から、添加する導電助剤の好ましい割合は0.5〜10質量%(ここで、活物質(炭素質材料)量+バインダー量+導電助剤量=100質量%とする)であり、更に好ましくは0.5〜7質量%、とくに好ましくは0.5〜5質量%である。結合剤としては、PVDF(ポリフッ化ビニリデン)、ポリテトラフルオロエチレン、及びSBR(スチレン・ブタジエン・ラバー)とCMC(カルボキシメチルセルロース)との混合物などの電解液と反応しないものであれば特に限定されない。中でもPVDFは、活物質表面に付着したPVDFがリチウムイオン移動を阻害することが少なく、良好な入出力特性を得るために好ましい。PVDFを溶解しスラリーを形成するためにN−メチルピロリドン(NMP)などの極性溶媒が好ましく用いられるが、SBRなどの水性エマルジョンやCMCを水に溶解して用いることもできる。結合剤の添加量が多すぎると、得られる電極の抵抗が大きくなるため、電池の内部抵抗が大きくなり電池特性を低下させるので好ましくない。また、結合剤の添加量が少なすぎると、負極材料粒子相互及び集電材との結合が不十分となり好ましくない。結合剤の好ましい添加量は、使用するバインダーの種類によっても異なるが、PVDF系のバインダーでは好ましくは3〜13質量%であり、更に好ましくは3〜10質量%である。一方、溶媒に水を使用するバインダーでは、SBRとCMCとの混合物など、複数のバインダーを混合して使用することが多く、使用する全バインダーの総量として0.5〜5質量%が好ましく、更に好ましくは1〜4質量%である。電極活物質層は集電板の両面に形成するのが基本であるが、必要に応じて片面でもよい。電極活物質層が厚いほど、集電板やセパレータなどが少なくて済むため高容量化には好ましいが、対極と対向する電極面積が広いほど入出力特性の向上に有利なため活物質層が厚すぎると入出力特性が低下するため好ましくない。
本発明の非水電解質二次電池は、本発明の非水電解質二次電池負極を含む。
本発明の負極材料を用いて、非水電解質二次電池の負極電極を形成した場合、正極材料、セパレータ、及び電解液など電池を構成する他の材料は特に限定されることなく、非水溶媒二次電池として従来使用され、あるいは提案されている種々の材料を使用することが可能である。
真密度は、JIS R 7212に定められた方法に従い、ブタノール法により測定した。内容積約40mLの側管付比重びんの質量(m1)を正確に量る。次に、その底部に試料を約10mmの厚さになるように平らにいれた後、その質量(m2)を正確に量る。これに1−ブタノールを静かに加えて、底から20mm程度の深さにする。次に比重びんに軽い振動を加えて、大きな気泡の発生がなくなったのを確かめた後、真空デシケーター中にいれ、徐々に排気して2.0〜2.7kPaとする。その圧力に20分間以上保ち、気泡の発生が止まった後に、取り出し、更に1−ブタノールを満たし、栓をして恒温水槽(30±0.03℃に調節してあるもの)に15分間以上浸し、1−ブタノールの液面を標線に合わせる。次に、これを取り出して外部をよくぬぐって室温まで冷却した後質量(m4)を正確に量る。
以下にBETの式から誘導された近似式を記す。
JIS M8819に定められた方法に準拠し測定した。CHNアナライザーによる元素分析により得られる試料中の水素及び炭素の質量割合から、水素/炭素の原子数の比として求めた。
炭素質材料粉末を試料ホルダーに充填し、PANalytical社製X’Pert PROを用いて、対称反射法にて測定した。走査範囲は8<2θ<50°で印加電流/印加電圧は45kV/40mAの条件で、Niフィルターにより単色化したCuKα線(λ=1.5418Å)を線源とし、X線回折図形を得た。標準物質用高純度シリコン粉末の(111)面の回折ピークを用いて補正した。CuKα線の波長を0.15418nmとし、Braggの公式によりd002を算出する。
試料約0.01gに対し、分散剤(カチオン系界面活性剤「SNウェット366」(サンノプコ社製))を3滴加え、試料に分散剤を馴染ませる。次に純水を加えて、超音波により分散させた後、粒径分布測定器(日機装株式会社製「Microtrac MT3300EX」)で、粒径0.02〜2000μmの範囲の粒径分布を求めた。測定条件において、透過性は吸収、粒子屈折率は1.81、形状は非球形を選択した。得られた粒径分布から、体積基準とした累積容積が50%となる粒径をもって、体積平均粒子径Dv50とした。また、累積容積が90%となる粒径をDv90とし、累積容積が10%となる粒径をDv10とした。
また、体積粒子径30μm以上の粒子の量は、測定された体積粒子径30μmまでの累積値を100から減じることにより算出した。
上記と同様の方法で個数基準とした累積容積が50%となる粒径をもって、個数平均粒子径とした。
実施例1〜10及び比較例1〜5で得られた炭素質材料1〜10及び比較炭素質材料1〜3を用いて、以下の(a)〜(d)の操作を行い、負極電極及び非水電解質二次電池を作製し、そして電極性能の評価を行った。
上記炭素質材料94質量部、ポリフッ化ビニリデン(株式会社クレハ製「KF#9100」)6質量部にNMPを加えてペースト状にし、銅箔上に均一に塗布した。乾燥した後、銅箔より直径15mmの円板状に打ち抜き、これを2.5tf/cm2(13MPa)プレスして電極とした。なお、電極中の炭素質材料の量は約9mgになるように調整した。
負極は、厚さがt1[cm]、単位面積あたりの質量がW1[g/cm2]である集電体上に、炭素質材料の質量割合がPである結合剤との混合物を塗布し、加圧して製造した厚さt2[cm]の負極電極を、所定の面積S[cm2]で打抜き、この打抜き後の負極電極の質量をW2[g]としたものである。このとき、電極密度は、以下のように計算した。
電極密度[g/cm3]=(W2/S−W1)/(t2−t1)
負極活物質層の厚みは、負極電極の集電体の両面に負極活物質層が存在する場合は、負極電極から集電体の厚みを差し引いた厚みの半分に相当する。また、集電体の片側にのみ負極活物質層が存在する場合は、負極電極から集電体の厚みを差し引いた厚みに相当する。具体的には、厚さ測定機により、負極活物質および集電体の厚みを測定した。5箇所で測定し、その平均値を平均厚みとした。
本発明の炭素質材料は非水電解質二次電池の負極電極を構成するのに適しているが、電池活物質の放電容量(脱ドープ量)及び不可逆容量(非脱ドープ量)を、対極の性能のバラツキに影響されることなく精度良く評価するために、特性の安定したリチウム金属を対極として、上記で得られた電極を用いてリチウム二次電池を構成し、その特性を評価した。
上記構成のリチウム二次電池について、充放電試験装置(東洋システム製「TOSCAT」)を用いて25℃にて充放電試験を行った。炭素極へのリチウムのドープ反応を定電流定電圧法により行い、脱ドープ反応を定電流法で行った。ここで、正極にリチウムカルコゲン化合物を使用した電池では、炭素極へのリチウムのドープ反応が「充電」であり、本発明の試験電池のように対極にリチウム金属を使用した電池では、炭素極へのドープ反応が「放電」と呼ぶことになり、用いる対極により同じ炭素極へのリチウムのドープ反応の呼び方が異なる。そこでここでは、便宜上炭素極へのリチウムのドープ反応を「充電」と記述することにする。逆に「放電」とは試験電池では充電反応であるが、炭素質材料からのリチウムの脱ドープ反応であるため便宜上「放電」と記述することにする。ここで採用した充電方法は定電流定電圧法であり、具体的には端子電圧が0.050Vになるまで0.5mA/cm2で定電流充電を行い、端子電圧が0.050Vに達した後、端子電圧0.050Vで定電圧充電を行い電流値が20μAに達するまで充電を継続した。このとき、供給した電気量を電極の炭素質材料の質量で除した値を炭素質材料の単位質量当たりの充電容量(mAh/g)と定義した。充電終了後、30分間電池回路を開放し、その後放電を行った。放電は0.5mA/cm2で定電流放電を行い、終止電圧を1.5Vとした。このとき放電した電気量を電極の炭素質材料の質量で除した値を炭素質材料の単位質量当たりの放電容量(mAh/g)と定義する。これらの質量当たり容量に上記の電極密度をかけあわせることで、体積当たり容量を算出する。不可逆容量は、充電容量−放電容量として計算される。同一試料を用いて作製した試験電池について3回(n=3)測定し、その測定値を平均して充放電容量及び不可逆容量を決定した。さらに、放電容量を充電容量で除した値に100を乗じて、初期効率(%)を求めた。これは活物質がどれだけ有効に使用されたかを示す値である。
負極は、上記(a)と同様の手順で負極電極を作製した。なお、電極中の炭素質材料の量は、プレス後に規定の電極厚みとなるよう調整した。正極は、コバルト酸リチウム(LiCoO2)94質量部、カーボンブラック3質量部、ポリフッ化ビニリデン(クレハ製KF#1300)3質量部にNMPを加えてペースト状にし、アルミニウム箔上に均一に塗布した。乾燥した後、塗工電極を直径14mmの円板上に打ち抜き、これをプレスし電極とした。なお、負極活物質の充電容量の95%となるよう正極電極中のコバルト酸リチウムの量を調整した。コバルト酸リチウムの容量を150mAh/gとして計算した。
このようにして調製した電極の対を用い、電解液としてはエチレンカーボネートとジメチルカーボネートとメチルエチルカーボネートを容量比で1:2:2で混合した混合溶媒に1.4モル/リットルの割合でLiPF6を加えたものを使用し、直径19mmの硼珪酸塩ガラス繊維製微細細孔膜をセパレータとして使用し、ポリエチレン製のガスケットを用いて、Arグローブボックス中で、2032サイズのコイン型非水電解質系リチウム二次電池を組み立てた。
軟化点205℃、H/C原子比0.65の石油ピッチ70kgと、ナフタレン30kgとを、撹拌翼および出口ノズルのついた内容積300リットルの耐圧容器に仕込み、190℃で加熱溶融混合を行った後、80〜90℃に冷却し、耐圧容器内を窒素ガスにより加圧して、内容物を出口ノズルから押出し、直径約500μmの紐状成型体を得た。次いで、この紐状成型体を直径(D)と長さ(L)の比(L/D)が約1.5になるように粉砕し、得られた破砕物を93℃に加熱した0.53質量%のポリビニルアルコール(ケン化度88%)を溶解した水溶液中に投入し、撹拌分散し、冷却して球状ピッチ成型体スラリーを得た。大部分の水をろ過により取り除いた後、球状ピッチ成形体の約6倍量の質量のn−ヘキサンでピッチ成形体中のナフタレンを抽出除去した。このようにして得た多孔性球状ピッチを、流動床を用いて、加熱空気を通じながら、240℃まで昇温し、240℃に1時間保持して酸化し、熱に対して不融性の多孔性球状酸化ピッチを得た。
次に多孔性球状酸化ピッチ7kgを直径130mmの縦型管状炉に入れ、窒素ガス流通下、600℃まで100℃/hで昇温し、600℃で1時間保持して予備焼成を実施し、炭素前駆体を得た。得られた炭素前駆体をスチームジェットミル(東洋ハイテック株式会社)で粉砕し、個数平均粒子径0.73μm、体積平均粒子径6.9μmの粉末状炭素前駆体とした。続いて、この粉末状炭素前駆体10gを直径100mmの横型管状炉に入れ、250℃/hの昇温速度で1200℃まで昇温し、1200℃で1時間保持して、本焼成を行い、炭素質材料1を調製した。なお、本焼成は、流量10L/minの窒素雰囲気下で行った。
個数平均粒子径0.68μm、体積平均粒子径4.9μmの粉末状炭素前駆体とした以外は実施例1と同様にして炭素質材料2を得た。
個数平均粒子径0.59μm、体積平均粒子径2.8μmの粉末状炭素前駆体とした以外は実施例1と同様にして炭素質材料3を得た。
多孔性球状ピッチの酸化温度を270℃に変更して、カウンタージェットミル(ホソカワミクロン株式会社/100−AFG)で回転数20000rpmで粉砕し、バグフィルターで回収された微粉を混合して、個数平均粒子径0.62μm、体積平均粒子径3.8μmの粉末状炭素前駆体とした以外は実施例1と同様にして炭素質材料4を得た。
多孔性球状ピッチの酸化温度を240℃にし、個数平均粒子径0.67μm、体積平均粒子径3.8μmの粉末状炭素前駆体とした以外は実施例4と同様にして炭素質材料5を得た。
多孔性球状ピッチの酸化温度を205℃に変更し、個数平均粒子径0.62μm、体積平均粒子径3.7μmの粉末状炭素前駆体とした以外は実施例4と同様にして炭素質材料6を得た。
実施例1と同様の方法で得た多孔性球状ピッチを、流動床を用いて、加熱空気を通じながら、190℃まで昇温し、190℃に1時間保持して酸化し、架橋処理を施した多孔性球状酸化ピッチを得た。得られた多孔性球状酸化ピッチ200gを150mmの横型管状炉に入れ、600℃まで150℃/hで昇温し、600℃で1時間保持して予備焼成を実施し、炭素前駆体を得た。得られた炭素前駆体を直径2mm以下まで粗粉砕した後、カウンタージェットミル(ホソカワミクロン株式会社/100−AFG)で粉砕し、バグフィルターで回収された微粉を混合して、個数平均粒子径0.55μm、体積平均粒子径3.2μmの粉末状炭素前駆体とした。続いて、この粉末状炭素前駆体10gを直径100mmの横型管状炉に入れ、250℃/hの昇温速度で1200℃まで昇温し、1200℃で1時間保持して、本焼成を行い、炭素質材料7を調製した。なお、本焼成は、流量10L/minの窒素雰囲気下で行った。
多孔性球状ピッチの酸化処理時間を7minに変更し、個数平均粒子径0.53μm、体積平均粒子径3.1μmの粉末状炭素前駆体とした以外は実施例7と同様にして炭素質材料8を得た。
個数平均粒子径0.53μm、体積平均粒子径4.6μmの粉末状炭素前駆体とした以外は実施例6と同様にして炭素質材料9を得た。
軟化点188℃、H/C原子比0.51の石炭ピッチをカウンタージェットミル(ホソカワミクロン株式会社/100−AFG)で回転数13000rpmで粉砕し、平均粒径5.2μmの粉末状ピッチを得た。続いて、この粉末状ピッチをマッフル炉(株式会社デンケン)に入れ、空気を20L/minで流通させながら、280℃で1時間保持して不融化処理を行い、不融化ピッチを得た。得られた不融化ピッチ100gを坩堝に入れ、縦型管状炉で、600℃まで50℃/hの速度で昇温し、600℃で1時間保持して予備焼成を実施し、炭素前駆体を得た。予備焼成は流量5L/minの窒素雰囲気下で行い、坩堝は開放した状態で実施した。得られた炭素前駆体をサンプルミルにて粉砕し、平均粒径4.6μmの粉末状炭素前駆体を得た。粉末状炭素前駆体10gを直径100mmの横型管状炉に入れ、250℃/hの昇温速度で1200℃まで昇温し、1200℃で1時間保持して、本焼成を行い、炭素質材料10を調製した。なお、本焼成は、流量10L/minの窒素雰囲気下で行った。
予備焼成後の前駆体をボールミルによって粉砕し、微粉分級することで、個数平均粒子径2.9μm、体積平均粒子径10.5μmの粉末状炭素前駆体とした以外は実施例4と同様にして比較炭素質材料1を得た。
予備焼成後の前駆体をカウンタージェットミル(ホソカワミクロン株式会社/100−AFG)で粉砕し、微粉分級することによって、個数平均粒子径2.7μm、体積平均粒子径6.5μmの粉末状炭素前駆体とした以外は実施例4と同様にして、比較炭素質材料2を得た。
実施例2のバグフィルターで回収した個数平均粒子径0.44μm、体積平均粒子径0.80μmの粉末状炭素前駆体を用いた以外は、実施例2と同様にして比較炭素質材料3を得た。
焼成温度を800℃に変更した以外は実施例2と同様にして比較炭素質材料4を得た。
これに対し、比較例1〜3の炭素質材料は、個数平均粒子径および個数平均粒子径/体積平均粒子径が本発明の範囲を満たすものではなく、比較例4の炭素材料は、H/Cが本発明の範囲を満たすものではない。そのため、電極密度が実施例よりも低かった。また、体積当たり放電容量が実施例よりも低く、初期効率または低温環境下での入力密度が実施例よりも劣る傾向にあった。このように、本発明の範囲を満たす実施例は、良好な入出力特性を備えていた。
Claims (9)
- 個数平均粒子径が0.1〜2.0μmであり、個数平均粒子径を体積平均粒子径で除した値が0.3以下であり、X線回折法により定めた(002)面の平均層面間隔d002が0.340〜0.390nmであり、水素および炭素の原子比(H/C)が0.10以下であることを特徴とする非水電解質二次電池負極用炭素質材料。
- 体積平均粒子径Dv50が1〜7μmである請求項1に記載の非水電解質二次電池負極用炭素質材料。
- 累積体積粒子径Dv10が2.5μm以下である請求項1または2に記載の非水電解質二次電池負極用炭素質材料。
- 体積粒子径30μm以上の粒子の量が1.0体積%以下である請求項1から3のいずれかに記載の非水電解質二次電池負極用炭素質材料。
- 請求項1から4のいずれかに記載の非水電解質二次電池負極用炭素質材料を含む非水電解質二次電池用負極電極。
- 13MPa(2.5tf/cm2)のプレス圧力を加えた場合に電極密度が1.02g/cm3以上である請求項5に記載の非水電解質二次電池用負極電極。
- 平均厚みが60μm以下である請求項5または6に記載の非水電解質二次電池用負極電極。
- 請求項5から7のいずれかに記載の非水電解質二次電池用負極電極を備える非水電解質二次電池。
- 請求項8に記載の非水電解質二次電池を搭載した車両。