JPWO2012043599A1 - ポリブチレンテレフタレート樹脂製フィルム - Google Patents
ポリブチレンテレフタレート樹脂製フィルム Download PDFInfo
- Publication number
- JPWO2012043599A1 JPWO2012043599A1 JP2012536496A JP2012536496A JPWO2012043599A1 JP WO2012043599 A1 JPWO2012043599 A1 JP WO2012043599A1 JP 2012536496 A JP2012536496 A JP 2012536496A JP 2012536496 A JP2012536496 A JP 2012536496A JP WO2012043599 A1 JPWO2012043599 A1 JP WO2012043599A1
- Authority
- JP
- Japan
- Prior art keywords
- film
- polybutylene terephthalate
- brominated
- bisphenol
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
背景技術
発明の概要
発明を実施するための形態
臭素系難燃剤としては、本発明に用いるビスフェノールA骨格を持つ臭素系難燃剤以外にも、臭素化ベンジルアクリレート、臭素化フタルイミド等が知られており、また臭素系以外の難燃剤も種々知られているが、耐加水分解性と難燃性を両立させるためには、ビスフェノールA以外の骨格をもった臭素系難燃剤とアンチモン化合物との組合せ以外では効果が極めて小さいものとなる。
実施例
実施例1〜5、比較例1〜10
表1に示す成分を秤量後ドライブレンドし、二軸押出機にて溶融混練(シリンダー温度260℃、スクリュー回転数130rpm、押出量15kg/hr)してペレットを作成し、140℃で3時間乾燥させた後、Tダイ(リップ幅150mm)を取り付けた(株)東洋精機製作所製の20φプラストミルを用い、シリンダー温度250℃、50rpm、ロール温度40℃で厚さ150μmになるようにフィルムを製膜した。次いで、このフィルムから各試験片を切り出し、各種物性を測定した。結果をあわせて表1に示す。
(A)ポリブチレンテレフタレート樹脂
・A-1 固有粘度1.1dL/g、末端カルボキシル基量7meq/kg
製造法は以下の通りである。
(B)難燃剤
・B-1 臭素化ポリカーボネート樹脂 帝人化成(株) ファイヤーガード7500 臭素含有量 52 %
・B-2 臭素化エポキシ樹脂 阪本薬品工業(株)製 SRT5000S 臭素含有量52%
・B-3 臭素化ポリベンジルアクリレート樹脂 ブロモケム・ファーイースト(株)製 FR-1025 臭素含有量70%
・B-4 臭素化フタルイミド樹脂 アルベマール日本(株)製 SAYTEX BT93W 臭素含有量67%
・B-5 リン系難燃剤 クラリアントジャパン(株)製 EXOLIT OP1240
(C)アンチモン化合物
・C-1 日本精鉱(株)製 三酸化アンチモン アンチモン含有量83%
(D)カルボジイミド化合物
・D-1 芳香族カルボジイミド化合物;ラインケミージャパン(株)製、スタバックゾールP400(メジアン径283μm) カルボジイミド含有量12.5%
[PCT試験]
プラストミルで作成したフィルムについて、PCT試験(121℃、2atm)を実施した。PCT処理前と100時間処理後の引張り強さを測定し、PCT処理後の引張強度保持率により耐加水分解性として評価した。比較例4、5、6についてはPCT処理品の劣化が激しく、測定できなかった。
[UL94 VTM難燃性評価]
UL94 VTM評価法に従い、上記で得られたフィルムを用い、難燃性評価を行った。VTM-0に達したものを○、到達しないものを×とした。
Claims (7)
- (A)ポリブチレンテレフタレート樹脂と(B)主鎖にビスフェノールA骨格を持つ臭素系難燃剤と(C)アンチモン化合物を含有する組成物からなるフィルムであり、(B)主鎖にビスフェノールA骨格を持つ臭素系難燃剤の臭素量が(A)ポリブチレンテレフタレート樹脂100重量部に対し8〜30重量部となる量であり、UL94 VTM難燃性がVTM−0となるフィルム。
- (A)ポリブチレンテレフタレート樹脂が、末端カルボキシル基量が30meq/kg以下であり、且つ固有粘度が0.8dL/g以上のものである請求項1記載のフィルム。
- (B)主鎖にビスフェノールA骨格を持つ臭素系難燃剤と(C)アンチモン化合物との配合比率が、臭素原子とアンチモン原子のモル比が1〜3となる比率である請求項1又は2記載のフィルム。
- (B)主鎖にビスフェノールA骨格を持つ臭素系難燃剤が、臭素化ポリカーボネート樹脂または臭素化エポキシ樹脂である請求項1〜3のいずれか1項記載のフィルム。
- さらに(D)カルボジイミド化合物を添加してなる組成物からなる請求項1〜4のいずれか1項記載のフィルム
- 150μm厚みのフィルムで、120℃、203kPa、100%RH環境下で100hr後の強度保持率が50%以上である請求項1〜5の何れか1項記載のフィルム。
- 太陽電池モジュール用バックシートフィルムである請求項1〜6の何れか1項記載のフィルム。