JPS598952B2 - 隔離板材料 - Google Patents

隔離板材料

Info

Publication number
JPS598952B2
JPS598952B2 JP50091838A JP9183875A JPS598952B2 JP S598952 B2 JPS598952 B2 JP S598952B2 JP 50091838 A JP50091838 A JP 50091838A JP 9183875 A JP9183875 A JP 9183875A JP S598952 B2 JPS598952 B2 JP S598952B2
Authority
JP
Japan
Prior art keywords
separator
fibers
separator material
electrolyte
nonwoven fabrics
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
JP50091838A
Other languages
English (en)
Other versions
JPS5138036A (ja
Inventor
グラーベル アドルフ
フアールバツハ エーリツヒ
ホフマン ハーラルト
テクル ボフスラフ
シユヴオーベル ロルフ
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Carl Freudenberg KG
Original Assignee
Carl Freudenberg KG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Carl Freudenberg KG filed Critical Carl Freudenberg KG
Publication of JPS5138036A publication Critical patent/JPS5138036A/ja
Publication of JPS598952B2 publication Critical patent/JPS598952B2/ja
Expired legal-status Critical Current

Description

【発明の詳細な説明】 本発明は、電解液に安定な熱可塑性プラスチックの短繊
維および／または長繊維から製造した不織布を蓄電池用
隔離板として使用することに関する。
公知のとおり蓄電池は、電解液に囲まれている交互に並
んでいる多数の陽極および陰極からなつている。
陽極と陰極との接触を従つてまた望ましくない蓄電池内
部電流を避けるため、電極は隔離板によつて互いに絶縁
してある。隔離板はそれで、電極に相互導電性接触をさ
せない、しかもその際電解液のイオンの通過を本質的に
妨げないことがその任務である。 実用可能な隔離板材
料は多数の要求事項にかなうものでなくてはならない。
それで電解液に対してまた酸化に対して安定性の良いこ
と、単位面積あたり特定の重量であること、厚さが正確
なことおよび引裂強度の大きいことが必要である。さら
に隔離板材料は電解液によく濡れ、これを速やかに吸収
しかつ毛細管現象の顕著なものでなくてはならない。
その上気泡容積が大きいか気泡直径が小さく均等なラビ
リンス構造となつていることが望ましい。この材料はそ
のほか電解液中において電気抵抗が低く、可撓性でしな
やかでなくてはならない。機能上からすると、最も簡単
な場合には気孔のある非導電性のセラミック材料が推奨
されよラが、この種の隔離板としては所要の可撓性に欠
けている。
しかし隔離板材料の可撓性や巻取可能性の良いことは特
に筒状著電池製造の場合に必要である。
この場合には陽極も陰極も薄い巻取可能な板からなつて
いる。次に両者の間に隔離材料を挿入するので、従つて
後者も同様に巻取可能でなくてはならない。陽極、陰極
および隔離板からなる帯状体を巻込んだ後に、この三層
形成物を電解液の満たしてある筒状のハウジングに挿入
し、電解液は急速にまた十分な量が使用隔離板材料に吸
収され、その気孔中に貯えられる。それゆえ隔離板材料
はその都度用いられる電解液に対して安定であり、かつ
陽極、陰極に密に接することのできるものでなくてはな
らない。さらに隔離板材料はラビリンス構造であつて、
電極から分離してくる固形物質に対する戸別作用がそれ
によつて生じることが望ましい。本発明により今回、電
解液に安定な熱可塑性短繊維および／または長繊維から
製造した不織布を用いた隔離板材料を提案する。
本発明の著電池用隔離板材料は、熱可塑性繊維からなる
、重なつている二枚の不織布の間に直線状フイラメント
を並列に配置し、両不織布は該フイラメントと結合しな
いように互に点溶接されており、その点溶接された区域
は材料の全表面の約２ないし４０％を占めることを特徴
とする。
重なつている二枚の不織布の間に挿入されたフイラメン
トは長さ方法に互いに任意の間隔をおいて配列し点溶接
個所内に閉じ込められ、これによつて固定してある。こ
の閉じ込められたフイラメントによつて隔離板の表面に
隆起部が生じ、この隆起部は挿入されたフイラメントの
厚みによつて多少異なる。この隆起部は所謂ガラス板効
果の防止および蓄電池の作動中に往々発生するガスの上
方への排出に役立つ。この隆起部は電解液の外まで延び
て並んでいることが望ましい。加えてこの隆起部は隔離
板の吸収力を増大する。挿入されたフイラメントは例え
ば紡糸糸が使用され得るが好ましくはモノフイラメント
が望ましい。
重ねられた二枚の不織布は別の接合剤を必要とすること
なしに点溶接が通常その構造に充分な個有強度を与える
ことがわかつた。
最適な多孔質が隔離板の戸別作用を妨げることなしに得
られる。好ましくは点溶接区域は全表面の３〜１５％で
あるが、本発明の材料は望ましい高度の可撓性と巻取可
能性を与えることがわかつた。不織布に多種の繊維が使
用される。
これらは一般に隔離板が配置される用途にしたがつて選
択される。酸性電解液たとえば硫酸で作動する電池には
、ポリエステル繊維製不織布が特に適している。アルカ
リ性蓄電池にはポリアミドまたはポリオレフイン繊維特
にポリプロピレン繊維が推称される。ポリプロピレン繊
維は非常にアルカリ液に強くこれで製作した蓄電池は高
温で使用できる。ポリプロピレンおよびポリエチレン基
質のへゼロフィラメントも、場合によつてはポリプロピ
レン繊維と混合して、良い成績を示した。ポリアミドー
ヘテロフイラメントもまた、場合によつてはポリアミド
繊維と混合して、良い成績をもたらした。またポリエス
テノ硼又はポリカーポネート繊維であつてもよい。不織
布の製造は元来公知の方法で行なわれる。
それで繊維は梳綿機その他適宜の装置によつてフリース
の形とし、このフリースを従来公知の方法で点溶接によ
り強化する。点溶接は熱可塑性繊維の使用によつて容易
に実施可能であり、結合剤または助剤たとえば乳化剤、
分散剤、触媒および残留オリゴマ一あるいは繊維溶媒な
どの使用を要しないこれらの成分は後で蓄電池の性能に
悪影響を与え、従つが望ましくないものである。本発明
で提案した隔離板材料の構造から、隔離板の性能に影響
がある場合でも、この故障の原因は速やかに発見でき有
効に対処できる。
特にこの隔離板材料は極めて均質であり異物のない構成
だからである。それゆえ蓄電池内の故章の原因も通常は
隔離板材料に求めるべきではない。杢発明による隔離板
材料は最適の状態にあつては、大部分が自由でばらばら
の左右上下に拡がり重なつていて強化のため上述の方法
で単に点状に相互溶接してある電解液に安定な熱可塑性
繊維のラビリンス様の錯綜からなつている。
これから極めて高度な電解液吸収能が現われる。元来緩
い結合に拘わらず、十分な機械的安定性ないし引裂強度
が存立している。以下の実施例は本発明の特に適した隔
離板材料を記述する。
実施例 繊度３．３デニール、切断長６０Ｔ！Ｒｌｌのポリエス
テル繊維７０部と非延伸ポリエステル繊維３０部とから
製した重量各５０１仙２の繊維フリース２枚の間に太さ
０，４ｎのモノフイラメントポリエステル糸を互いに０
．５ｃｍの間隔をおいてこれらが引続いて行なう溶接の
際それぞれ２列の溶接点の間に来るように挿入する。
これによつて隔離板の表面には挿入した糸の上方に、溶
接条件（圧／温度）に応じて隔離板表面上約０．１ない
し０．２Ｔｍ１高くなつている所望の線状の隆起部が生
じる。本発明の実施の態様を例示すると下記の通りであ
る。
１）電解液に対して安定な熱可塑性短繊維および／また
は長繊維からなる二枚の不織布の間に直線状のフイラメ
ントを並列に配置し、両不織布は該フイラメントと結合
しないように互に点溶接されており、その点溶接された
区域は材料全表面の約２ないし４０％を占めることを特
徴とする隔離板材料。
２）前項の隔離板材料において、点溶接が材料全表面に
対し約３ないし１５％であること３）前２項の何れかの
隔離板材料において、ポリオレフイン繊維からなるもの
４）前３項の何れかの隔離板材料において、ポリプハピ
レン基質の短繊維および／または長繊維からなり、場合
によつてはポリエチレン短繊維を含むもの５）実施の態
様第１ないし第３の何れかの隔離板材料において、ポリ
プロピレンーポリエチレンーヘテロフイラメント、場合
によつてはポリプロピレン長繊維を含むもの６）実施の
態様第４または第２の隔離板材料において、ポリアミド
繊維、場合によつては融点の異なるポリアミド繊維の混
合物からなるもの７）実施の態様第１または第２の隔離
板材料において、ポリカーポネート繊維からなるもの８
）実施の態様第１または第２の隔離板材料において、ポ
リエステル繊維からなるもの。

Claims (1)

    【特許請求の範囲】
  1. １ 電解液に対して安定な熱可塑性短繊維および／また
    は長繊維からなる二枚の不織布の間に直線状のフィラメ
    ントを並列に配置し、両不織布は該フィラメントと結合
    しないように互に点溶接されており、その点溶接された
    区域は材料全表面の約２ないし４０％を占めていること
    を特徴とする蓄電池用隔離板材料。
JP50091838A 1974-08-10 1975-07-28 隔離板材料 Expired JPS598952B2 (ja)