JPH03254173A - 電気用積層板 - Google Patents
電気用積層板Info
- Publication number
- JPH03254173A JPH03254173A JP5216290A JP5216290A JPH03254173A JP H03254173 A JPH03254173 A JP H03254173A JP 5216290 A JP5216290 A JP 5216290A JP 5216290 A JP5216290 A JP 5216290A JP H03254173 A JPH03254173 A JP H03254173A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- base material
- impregnated base
- laminate
- irradiation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は電気機器・電子機器、コンピュータ、通信機器
等に用いられる電気用積層板に関するものである。
等に用いられる電気用積層板に関するものである。
電気用積層板から印刷印線板に加工する際には、積層板
表面にインク、エツチングレジスト等を印刷する必要が
ある。しかし積層板を長期間保管後に使用すると積層板
構成材の樹脂から発生するガスが隣接する金属箔面や樹
脂面に接触、付着し印刷性を低下させている。この為積
層板表面を研削ブラシ等で研磨し異物、有機物を除去し
ているが有機物の除去は困難で、且つ表面粗度が大とな
りレジストインクをはしいて回路欠落を招来する等の欠
点があった。
表面にインク、エツチングレジスト等を印刷する必要が
ある。しかし積層板を長期間保管後に使用すると積層板
構成材の樹脂から発生するガスが隣接する金属箔面や樹
脂面に接触、付着し印刷性を低下させている。この為積
層板表面を研削ブラシ等で研磨し異物、有機物を除去し
ているが有機物の除去は困難で、且つ表面粗度が大とな
りレジストインクをはしいて回路欠落を招来する等の欠
点があった。
従来の技術で述べたように、従来の積層板はインク、エ
ツチングレジスト等の印刷性がよくない本発明は従来の
技術における上述の問題点に鑑みてなされたもので、そ
の目的とするところはインク、エツチングレジスト等の
印刷性のよい電気用積層板を提供することにある。
ツチングレジスト等の印刷性がよくない本発明は従来の
技術における上述の問題点に鑑みてなされたもので、そ
の目的とするところはインク、エツチングレジスト等の
印刷性のよい電気用積層板を提供することにある。
本発明は所要枚数の樹脂含浸基材の上面及び又は下面に
金属箔を配設した積層体を積層一体化後、該表面をＵＶ
照射したことを特徴とする電気用積層板のため、金属箔
面や樹脂面に付着する有機物成分を分解除去するため上
記目的を達成することができたもので、以下本発明の詳
細な説明する。
金属箔を配設した積層体を積層一体化後、該表面をＵＶ
照射したことを特徴とする電気用積層板のため、金属箔
面や樹脂面に付着する有機物成分を分解除去するため上
記目的を達成することができたもので、以下本発明の詳
細な説明する。
本発明に用いる樹脂含浸基材の樹脂としては、フェノー
ル樹脂、クレゾール樹脂、エポキシ樹脂、不飽和ポリエ
ステル樹脂、メラミン樹脂、ポリイミド、ポリブタジェ
ン、ポリアミド、ボリア柔トイミド、ポリスルフォン、
ポリフェニレンサルファイド、ポリフェニレンオキサイ
ド、ポリブチレンテレフタレート、ポリエーテルエーテ
ルケトン、弗化樹脂等の単独、変性物、混合物等が用い
られ必要に応して粘度調整に水、メチルアルコール、ア
セトン・シクロヘキサノン、スチレン等の溶媒を添加し
たもので、基材としては、ガラス、アスベスト等の無機
繊維やポリエステル、ポリアミド、ポリビニルアルコー
ル、アクリル等の有機合成繊維や木綿等の天然繊維から
なる織布、不織布、マット或は祇又はこれらの組合せ基
材等である。金属箔としては銅、アルミニウム、鉄、ニ
ッケル、亜鉛等の単独、合金、複合箔が用いられ必要に
応して金属箔の片面に接着剤層を設けておき、より接着
性を向上させることもできる。積層−体化手段としては
プレス、多段プレス、マルチロール、ダブルベルト等に
よる加圧下積層成型や無圧積層成型の各れでもよく特に
限定するものではない。ＵＶ照射としては１５０〜２６
０ ｎｍのＵＶ線を１０〜１８０秒間照射することがよ
り効果的で好ましいことである。
ル樹脂、クレゾール樹脂、エポキシ樹脂、不飽和ポリエ
ステル樹脂、メラミン樹脂、ポリイミド、ポリブタジェ
ン、ポリアミド、ボリア柔トイミド、ポリスルフォン、
ポリフェニレンサルファイド、ポリフェニレンオキサイ
ド、ポリブチレンテレフタレート、ポリエーテルエーテ
ルケトン、弗化樹脂等の単独、変性物、混合物等が用い
られ必要に応して粘度調整に水、メチルアルコール、ア
セトン・シクロヘキサノン、スチレン等の溶媒を添加し
たもので、基材としては、ガラス、アスベスト等の無機
繊維やポリエステル、ポリアミド、ポリビニルアルコー
ル、アクリル等の有機合成繊維や木綿等の天然繊維から
なる織布、不織布、マット或は祇又はこれらの組合せ基
材等である。金属箔としては銅、アルミニウム、鉄、ニ
ッケル、亜鉛等の単独、合金、複合箔が用いられ必要に
応して金属箔の片面に接着剤層を設けておき、より接着
性を向上させることもできる。積層−体化手段としては
プレス、多段プレス、マルチロール、ダブルベルト等に
よる加圧下積層成型や無圧積層成型の各れでもよく特に
限定するものではない。ＵＶ照射としては１５０〜２６
０ ｎｍのＵＶ線を１０〜１８０秒間照射することがよ
り効果的で好ましいことである。
以下本発明を実施例にもとづいて説明する。
実施例
厚み０．２ｍｍのクラフト紙にフェノール樹脂ワニスを
乾燥後樹脂量が５０重量％（以下単に％と記す）になる
ように含浸・乾燥した樹脂含浸基材７枚の上下面に厚み
３５ミクロンの接着剤付銅箔を夫々接着剤側が樹脂含浸
基材と対向するように配設した積層体を成型圧力１００
ｋｇ／ｃ＋ｆｌ、 １６０°Ｃで６０分間積層成型
して得た積層板の表裏面を１８４、９ ｎｍのＵＶ線で
６０秒間照射して厚み１．６ｍｍの電気用積層板を得た
。
乾燥後樹脂量が５０重量％（以下単に％と記す）になる
ように含浸・乾燥した樹脂含浸基材７枚の上下面に厚み
３５ミクロンの接着剤付銅箔を夫々接着剤側が樹脂含浸
基材と対向するように配設した積層体を成型圧力１００
ｋｇ／ｃ＋ｆｌ、 １６０°Ｃで６０分間積層成型
して得た積層板の表裏面を１８４、９ ｎｍのＵＶ線で
６０秒間照射して厚み１．６ｍｍの電気用積層板を得た
。
比較例１
積層成形後の積層板表裏面を研削ブラシ（商品名、タイ
ネックス）で研磨して電気用積層板を得た。
ネックス）で研磨して電気用積層板を得た。
比較例２
積層成形後の積層板を研磨やＵＶ照射せずそのまま電気
用積層板とした。
用積層板とした。
実施例１及び比較例１とこの電気用積層板の性能は第１
表のようである。
表のようである。
本発明は上述した如く構成されている。特許請求の範囲
に記載した構成を有する電気用積層板においては印刷性
がよく且つ回路欠落不良率を低減させる効果がある。
に記載した構成を有する電気用積層板においては印刷性
がよく且つ回路欠落不良率を低減させる効果がある。
４２
Claims (1)
- （１） 所要枚数の樹脂含浸基材の上面及び又は下面に
金属箔を配設した積層体を積層一体化後、該表面をＵＶ
照射したことを特徴とする電気用積層板。