JPH0133181B2 - - Google Patents
Info
- Publication number
- JPH0133181B2 JPH0133181B2 JP59114267A JP11426784A JPH0133181B2 JP H0133181 B2 JPH0133181 B2 JP H0133181B2 JP 59114267 A JP59114267 A JP 59114267A JP 11426784 A JP11426784 A JP 11426784A JP H0133181 B2 JPH0133181 B2 JP H0133181B2
- Authority
- JP
- Japan
- Prior art keywords
- maleic anhydride
- medical device
- reactive functional
- functional group
- based polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
第５図に示すように、本発明実施例および比較
例の被覆を有するよう処理したポリ塩化ビニルま
たはポリウレタンシート４１を、被覆を水で膨潤
させてから傾斜板上に固定し、その上に底面にポ
リアミド樹脂製シート４３を貼り付けた重さ約
100ｇの鉄製円柱形状のおもり４４をのせ、板４
１の傾斜角θを徐々に増大させていつた時、おも
りが摺動し始める角度θを求め、μ＝tanθとして
摩擦係数を求めた。その結果を表１に示す。 グリセリンコート(8)およびオリーブ油コート(9)
については、コート液にポリ塩化ビニルシートを
浸漬し、液が滴下しない程度に振り切つて試料表
面を得た。 〔持続性試験−（摩擦係数の経時変化）〕 本発明の実施例に記す被覆表面、オリーブ油、
グリセリン塗布表面を有する試料を１の水中に
浸漬し、500〜600rpmにて撹拌し、第５図に示し
たような試験方法により摩擦係数を求め、その経
時変化を調べた。その結果を表−１および第６図
に示す。 〔持続性試験−（摩擦による潤滑性変化）〕 本発明の実施例および比較例に記すような試料
表面を、水でぬらした指で強くこすり、その潤滑
性の持続性の有無を確認した。その結果を表−１
に示す。 〔持続性試験−（過酷摩擦による潤滑性変化）〕 持続性試験−よりも激しく何回も強く水でぬ
らした指でこすり、潤滑性の持続性を評価した。
結果を表−１に示す。
例の被覆を有するよう処理したポリ塩化ビニルま
たはポリウレタンシート４１を、被覆を水で膨潤
させてから傾斜板上に固定し、その上に底面にポ
リアミド樹脂製シート４３を貼り付けた重さ約
100ｇの鉄製円柱形状のおもり４４をのせ、板４
１の傾斜角θを徐々に増大させていつた時、おも
りが摺動し始める角度θを求め、μ＝tanθとして
摩擦係数を求めた。その結果を表１に示す。 グリセリンコート(8)およびオリーブ油コート(9)
については、コート液にポリ塩化ビニルシートを
浸漬し、液が滴下しない程度に振り切つて試料表
面を得た。 〔持続性試験−（摩擦係数の経時変化）〕 本発明の実施例に記す被覆表面、オリーブ油、
グリセリン塗布表面を有する試料を１の水中に
浸漬し、500〜600rpmにて撹拌し、第５図に示し
たような試験方法により摩擦係数を求め、その経
時変化を調べた。その結果を表−１および第６図
に示す。 〔持続性試験−（摩擦による潤滑性変化）〕 本発明の実施例および比較例に記すような試料
表面を、水でぬらした指で強くこすり、その潤滑
性の持続性の有無を確認した。その結果を表−１
に示す。 〔持続性試験−（過酷摩擦による潤滑性変化）〕 持続性試験−よりも激しく何回も強く水でぬ
らした指でこすり、潤滑性の持続性を評価した。
結果を表−１に示す。
実施例７の無水マレイン酸系高分子物質を共有
結合したもの、比較例２のポリビニルピロリドン
をイオン結合ないし錯形成結合させたもの、およ
び比較例３の無水マレイン酸系高分子物質をイオ
ン結合させたものの３種の２cm巾の軟質ポリ塩化
ビニルシートを用意した。このものを用い、被覆
を膨潤させてから、第５図に示すような装置に
て、おもり４４のくりかえし上下動試験を行つ
た。この際、傾斜角θは30゜とし、おもり４４は、
振巾10mm、線速500mm／Ｓで上下動した。 各シートにおける上下動１回目、50回目、150
回目、500回目での引上時の荷重を表−２に示す。
また、表−２には、カツコ内にて摩擦係数μが併
記される。
結合したもの、比較例２のポリビニルピロリドン
をイオン結合ないし錯形成結合させたもの、およ
び比較例３の無水マレイン酸系高分子物質をイオ
ン結合させたものの３種の２cm巾の軟質ポリ塩化
ビニルシートを用意した。このものを用い、被覆
を膨潤させてから、第５図に示すような装置に
て、おもり４４のくりかえし上下動試験を行つ
た。この際、傾斜角θは30゜とし、おもり４４は、
振巾10mm、線速500mm／Ｓで上下動した。 各シートにおける上下動１回目、50回目、150
回目、500回目での引上時の荷重を表−２に示す。
また、表−２には、カツコ内にて摩擦係数μが併
記される。
メチルビニルエーテル無水マレイン酸共重合体
（GANTREZ AN169）のハーフエチルエステル
（エステル化度40〜50％）およびポリビニルピロ
リドン（Ｋ−90）を、それぞれ、THFおよびク
ロロホルムに溶解し、これをキヤステイングして
厚さ0.1mmのシートを得た。 このものを水にて膨潤後、引張試験を行つたと
ころ、無水マレイン酸系高分子物質GANTREZ
AN169は、ポリビニルピロリドンＫ−90に比較
して大きな破断強度をもつていることが確認され
た。 以上の両試験および表−１の結果から以下のこ
とが明らかである。 表−２に示される結果から、上下動50回まで
は、いずれのコートもほぼ一定の引上荷重であ
り、良好な潤滑性を示すことがわかる。そして、
このような条件が、前記持続性試験−に対応す
るものであると考えられる。 一方、上下動150回では、ポリビニルピロリド
ンは摩擦抵抗が増大するのに対し、無水マレイン
酸系高分子物質では、それが共有結合で担持され
ていようと、イオン結合で担持されていようとに
かかわらず、安定した潤滑性を示している。 そして、このような条件は、前記持続性試験−
に対応している。 このような現象は、膜強度試験の結果から明ら
かなように、無水マレイン酸系高分子物質が、ポ
リビニルピロリドンに比較して高いポリマー強度
をもつており、この結果、持続性（持続性−）
が向上しているものであると考えられる。 しかし、同じく膜強度の高い無水マレイン酸系
高分子物質を用いても、イオン結合で担持した場
合は、基材との接着強度が不足している。 この結果、500回の上下動後には本発明の共有
結合で担持した場合には安定した潤滑性を示すの
に対し、イオン結合で担持した場合には、摩擦抵
抗が増大してしまう。 表−１に示されるように被覆層なしの摩擦抵抗
は１程度であるので、イオン結合による比較例３
の潤滑性はきわめて悪いものである。 これらより、イオン結合の場合には、苛酷な持
続試験−で不十分な結果しか得られない。
（GANTREZ AN169）のハーフエチルエステル
（エステル化度40〜50％）およびポリビニルピロ
リドン（Ｋ−90）を、それぞれ、THFおよびク
ロロホルムに溶解し、これをキヤステイングして
厚さ0.1mmのシートを得た。 このものを水にて膨潤後、引張試験を行つたと
ころ、無水マレイン酸系高分子物質GANTREZ
AN169は、ポリビニルピロリドンＫ−90に比較
して大きな破断強度をもつていることが確認され
た。 以上の両試験および表−１の結果から以下のこ
とが明らかである。 表−２に示される結果から、上下動50回まで
は、いずれのコートもほぼ一定の引上荷重であ
り、良好な潤滑性を示すことがわかる。そして、
このような条件が、前記持続性試験−に対応す
るものであると考えられる。 一方、上下動150回では、ポリビニルピロリド
ンは摩擦抵抗が増大するのに対し、無水マレイン
酸系高分子物質では、それが共有結合で担持され
ていようと、イオン結合で担持されていようとに
かかわらず、安定した潤滑性を示している。 そして、このような条件は、前記持続性試験−
に対応している。 このような現象は、膜強度試験の結果から明ら
かなように、無水マレイン酸系高分子物質が、ポ
リビニルピロリドンに比較して高いポリマー強度
をもつており、この結果、持続性（持続性−）
が向上しているものであると考えられる。 しかし、同じく膜強度の高い無水マレイン酸系
高分子物質を用いても、イオン結合で担持した場
合は、基材との接着強度が不足している。 この結果、500回の上下動後には本発明の共有
結合で担持した場合には安定した潤滑性を示すの
に対し、イオン結合で担持した場合には、摩擦抵
抗が増大してしまう。 表−１に示されるように被覆層なしの摩擦抵抗
は１程度であるので、イオン結合による比較例３
の潤滑性はきわめて悪いものである。 これらより、イオン結合の場合には、苛酷な持
続試験−で不十分な結果しか得られない。
第１図、第２図、第３図および第４図は本発明
の医療用具の構成例を示すもので、それぞれED
チユーブ、バルーンカテーテル、冠動脈造影用カ
テーテルおよびガイドワイヤーの側面図、第５図
は摩擦係数を測定する方法を示す図、第６図は摩
擦係数の経時変化を示すグラフである。 符号の説明、１……本発明の被覆層、２……
EDチユーブ、２１……オリーブ、２２……本体
チユーブ、２４……コネクタ、３１……側孔、３
２……バルーン、３３……本体チユーブ、３４…
…バルーン用分岐管、３５……本体コネクタ、４
１……試料板、４２……傾斜板、４３……底板、
４４……おもり、５……冠動脈造影用カテーテ
ル、６……ガイドワイヤー。
の医療用具の構成例を示すもので、それぞれED
チユーブ、バルーンカテーテル、冠動脈造影用カ
テーテルおよびガイドワイヤーの側面図、第５図
は摩擦係数を測定する方法を示す図、第６図は摩
擦係数の経時変化を示すグラフである。 符号の説明、１……本発明の被覆層、２……
EDチユーブ、２１……オリーブ、２２……本体
チユーブ、２４……コネクタ、３１……側孔、３
２……バルーン、３３……本体チユーブ、３４…
…バルーン用分岐管、３５……本体コネクタ、４
１……試料板、４２……傾斜板、４３……底板、
４４……おもり、５……冠動脈造影用カテーテ
ル、６……ガイドワイヤー。
Claims (1)
- 【特許請求の範囲】 １ 医療用具を構成する基材の少なくとも表面に
存在する反応性官能基と、無水マレイン酸系高分
子物質とを共有結合させ、湿潤時に該表面が潤滑
性を有するように構成したことを特徴とする医療
用具。 ２ 反応性官能基がアルデヒド基、エポキシ基、
イソシアネート基またはアミノ基である特許請求
の範囲第１項に記載の医療用具。 ３ 医療用具は医療用チユーブ内に挿通可能な棒
状体からなり、医療用チユーブを体内へ導入また
は体内から抜去可能とする案内具である特許請求
の範囲第１項に記載の医療用具。 ４ 反応性官能基を有する化合物の溶液で医療用
具を構成する基材を処理し、該基材の少なくとも
表面に反応性官能基が存在するよう下地層を形成
し、次いで無水マレイン酸系高分子物質で処理し
て、該反応性官能基と該無水マレイン酸系高分子
物質とを共有結合させ、該下地層上に無水マレイ
ン酸系高分子物質の被覆層を形成し、湿潤時に該
表面が潤滑性を有するようにしたことを特徴とす
る医療用具の製造方法。 ５ 反応性官能基を有する化合物の溶液で医療用
具を構成する基材を処理し、該基材の少なくとも
表面に反応性官能基が存在するよう下地層を形成
し、次いで無水マレイン酸系高分子物質で処理し
て、該反応性官能基と該無水マレイン酸系高分子
物質とを共有結合させ、該下地層上に無水マレイ
ン酸系高分子物質の被覆層を形成し、この後、水
処理を行い湿潤時に該表面が潤滑性を有するよう
にしたことを特徴とする医療用具の製造方法。