JP7475194B2 - 不飽和ポリエステル樹脂組成物およびパテ組成物 - Google Patents
不飽和ポリエステル樹脂組成物およびパテ組成物 Download PDFInfo
- Publication number
- JP7475194B2 JP7475194B2 JP2020082956A JP2020082956A JP7475194B2 JP 7475194 B2 JP7475194 B2 JP 7475194B2 JP 2020082956 A JP2020082956 A JP 2020082956A JP 2020082956 A JP2020082956 A JP 2020082956A JP 7475194 B2 JP7475194 B2 JP 7475194B2
- Authority
- JP
- Japan
- Prior art keywords
- unsaturated polyester
- mass
- parts
- polyester resin
- resin composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
1.不飽和ポリエステル
不飽和ポリエステルは、多塩基酸と、多価アルコールと、ジシクロペンタジエン(以下、DCPDとする。)との反応生成物である。
重合性単量体は、エチレン性不飽和二重結合を有する重合性モノマー(ビニルモノマー)であって、上記した不飽和ポリエステルを溶解可能なものである。また、重合性単量体は、上記した不飽和ポリエステルと重合可能(架橋可能)な反応性希釈剤である。
パテ組成物には、上記した不飽和ポリエステル樹脂組成物が含まれる。
上記したパテ組成物は、例えば、上記した対象物に塗工した後、必要に応じて加熱により硬化して、パテ組成物の硬化物(硬化パテ組成物)を形成する。
<不飽和ポリエステルの調製>
<<合成例1~合成例6>>
温度計、窒素ガス導入管、還流冷却器および攪拌機を備えたフラスコを反応器とした。この反応器に、無水マレイン酸100モル部を仕込み、窒素気流下で加熱溶解した。次いで、反応器内の温度を125℃に加熱して、水を、ジシクロペンタジエン(DCPD)と同モル部反応器内に滴下して投入した。
合成例1~6と同様の反応器に、表1に示す処方となるように、無水マレイン酸と、ジエチレングリコール全量とを仕込み、さらにエチレングリコールを、ジエチレングリコールとエチレングリコールとの仕込みモル部の総和が無水マレイン酸の半分のモル部となるように仕込む(例えば、合成例7の場合、ジエチレングリコール37モル部、エチレングリコール8モル部)。その後、それらを窒素気流下で加熱溶解した。次いで、DCPDを、表1に示す処方となるように、反応器内に滴下して投入した。その後、90分間125℃で攪拌した。次いで、反応器の内温を100℃以下に冷却した後、表1に示す残りの多価アルコールと、無水フタル酸(合成例7のみ)とを、表1に示す処方となるように反応器に仕込んだ。その後、反応器の内温を180℃~200℃に昇温し、8時間、DCPDおよび多塩基酸の反応生成物と多価アルコールとを反応させた。
<<実施例1~実施例11>><<比較例1~比較例7>>
表2、表3に示す処方となるように、各合成例の不飽和ポリエステル65質量部に、重合性単量体35質量部とハイドロキノン0.01質量部とを添加し、均一に混合して不飽和ポリエステル樹脂組成物を得た。
各実施例および各比較例のパテ組成物に、シクロヘキサノンパーオキサイド溶液(濃度35質量%、硬化剤)2.0質量部を添加して混合し、その後、減圧により、混合物を十分に脱気したものを、亜鉛メッキ鋼板に500μmの厚みとなるように塗工し、各項目を評価した。
各実施例および各比較例のパテ組成物を塗工した亜鉛メッキ鋼板を25℃で60分間放置した。パテ組成物の乾燥性を指触乾燥で評価した。その結果を表2および表3に示す。
○:硬化表面に全くベタツキがない。
△:僅かに指紋が残る。
×:ベタツキが残る。
各実施例および各比較例のパテ組成物を塗工した亜鉛メッキ鋼板を60℃で15分間放置して硬化させた。次いで、鋼板を90°に折り曲げ、パテ組成物の硬化物の密着性を以下の基準で評価した。その結果を表2および表3に示す。
○:パテ組成物の硬化物に裂け目がはいるが、パテ組成物の硬化物は鋼板から剥がれ落ちない。
△:パテ組成物の硬化物に裂け目がはいり、パテ組成物の硬化物の一部は鋼板から剥がれ落ちる。
×:パテ組成物の硬化物に裂け目がはいり、パテ組成物の硬化物の全てが鋼板から剥がれ落ちる。
各実施例および各比較例のパテ組成物を塗工した亜鉛メッキ鋼板を60℃で15分間放置して硬化させた。次いで、#400のサンドペーパーを用いて表面を研磨して、パテ組成物の硬化物の研磨性(硬さ)を以下の基準で評価した。その結果を表2および表3に示す。
○:サンドペーパーは目詰まりをおこさない。
△:サンドペーパーは目詰まりを少しおこす。
×:サンドペーパーの目詰まりが激しい。
Claims (4)
- 不飽和ポリエステルと、
ビニルトルエンを含有する重合性単量体と、を含み、
前記不飽和ポリエステルは、多塩基酸と、多価アルコールと、ジシクロペンタジエンとの反応生成物であり、
前記多塩基酸は、マレイン酸およびその無水物を含み、
前記多価アルコールは、ジエチレングリコールを含み、
ジシクロペンタジエンの含有割合は、前記多塩基酸100モル部に対して、30モル部以上60モル部以下であり、
前記重合性単量体100質量%における前記ビニルトルエンの含有割合は、60質量%以上100質量%以下であることを特徴とする、不飽和ポリエステル樹脂組成物。 - 前記多価アルコール100モル%における前記ジエチレングリコールの含有割合は、30モル%以上60モル%以下であることを特徴とする、請求項1に記載の不飽和ポリエステル樹脂組成物。
- 金属石鹸をさらに含有することを特徴とする、請求項1または2に記載の不飽和ポリエステル樹脂組成物。
- 請求項1~3のいずれか一項に記載の不飽和ポリエステル樹脂組成物を含むことを特徴とする、パテ組成物。