JP7373135B2 - チューブ容器用包材、チューブ容器およびキャップ付きチューブ容器 - Google Patents
チューブ容器用包材、チューブ容器およびキャップ付きチューブ容器 Download PDFInfo
- Publication number
- JP7373135B2 JP7373135B2 JP2022014455A JP2022014455A JP7373135B2 JP 7373135 B2 JP7373135 B2 JP 7373135B2 JP 2022014455 A JP2022014455 A JP 2022014455A JP 2022014455 A JP2022014455 A JP 2022014455A JP 7373135 B2 JP7373135 B2 JP 7373135B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- paper base
- base layer
- tube container
- paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
第1シーラント層51および第2シーラント層53といったシーラント層は、それぞれ、積層体50同士を接着させるための層であり、シーラント層を構成する材料としては、熱によって溶融し、融着する材料が用いられる。この場合、シーラント層には、例えばポリオレフィンを用いることができる。具体的には、シーラント層としては、例えば、ポリエチレン、ポリプロピレン、ポリエチレン若しくはポリプロピレン等のポリオレフィン系樹脂をアクリル酸、メタクリル酸、マレイン酸、無水マレイン酸、フマール酸、イタコン酸、その他の不飽和カルボン酸で変性した酸変性ポリオレフィン系樹脂、ポリ酢酸ビニル系樹脂、ポリエステル系樹脂、ポリスチレン系樹脂、ポリアクリロニトリル、飽和ポリエステル、ポリビニルアルコール等その他の樹脂の1種ないしそれ以上からなる樹脂を使用することができる。シーラント層がポリエチレンを含む場合、ポリエチレンはバイオマス由来のポリエチレンであってもよい。
第1紙基材層52および第2紙基材層54といった紙基材層は、例えば、第1シーラント層51や第2シーラント層53を支持するとともに積層体50全体のコシを高めるための層である。紙基材層を構成する紙としては、晒紙であってもよく、半晒紙であってもよく、未晒紙であってもよい。また、紙の坪量は、例えば50g/m2以上200g/m2以下であってもよい。
第1接着層56a、第2接着層56bおよび第3接着層56cといった接着層は、第1シーラント層51、第1紙基材層52、第2紙基材層54、補強層58、第2シーラント層53などを互いに接着するための層である。この接着層を構成する材料は、接着する層を構成する樹脂によって適宜選択することができる。
印刷層55は、絵柄等の印刷が施された層であり、積層体50の意匠性を向上させるための層である。印刷層55としては、通常のインキビヒクルの1種ないし2種以上を主成分とし、必要ならば、可塑剤、安定剤、酸化防止剤、光安定剤、紫外線吸収剤、硬化剤、架橋剤、滑剤、帯電防止剤、充填剤、その他の添加剤の1種ないし2種以上を任意に添加し、更に、染料・顔料等の着色剤を添加し、溶媒、希釈剤等で充分に混練してインキ組成物を調整して得たインキ組成物を使用することができる。このようなインキビヒクルとしては、例えば、あまに油、きり油、大豆油、炭化水素油、ロジン、ロジンエステル、ロジン変性樹脂、シェラック、アルキッド樹脂、フェノール系樹脂、マレイン酸樹脂、天然樹脂、炭化水素樹脂、ポリ塩化ビニル系樹脂、ポリ酢酸系樹脂、ポリスチレン系樹脂、ポリビニルブチラール樹脂、アクリルまたはメタクリル系樹脂、ポリアミド系樹脂、ポリエステル系樹脂、ポリウレタン系樹脂、エポキシ系樹脂、尿素樹脂、メラミン樹脂、アミノアルキッド系樹脂、ニトロセルロース、エチルセルロース、塩化ゴム、環化ゴム、その他などの1種または2種以上を併用することができる。印刷方法は、グラビア印刷のほか、凸版印刷、スクリーン印刷、転写印刷、フレキソ印刷、その他の印刷方式であってもよい。
バリア層57は、酸素ガスおよび水蒸気などの透過を抑制するための層である。バリア層57としては、例えば、酸素ガス、水蒸気等に対するガスバリア性素材、太陽光等に対する遮光性素材、あるいは、内容物に対する保香性等を有する材料を使用することができる。具体的には、バリア層57としては、例えば、アルミニウム箔、スズ、鉛、銅、鉄、ニッケル、またはこれらの合金等あるいは、アルミニウム等の金属蒸着薄層を使用することができる。バリア層57としてアルミニウム箔を使用する場合、バリア層57の厚みは、5μm以上20μm以下程度とすることができる。バリア層57としてアルミニウム箔を使用することにより、積層体50の作製を容易にすることができる。
補強層58は、例えば、第1シーラント層51や第2シーラント層53を支持するとともに積層体50全体の強度を高めるための層である。補強層58を構成する材料としては、例えば、ポリエステル系樹脂、ポリアミド系樹脂、ポリアラミド系樹脂、ポリオレフィン系樹脂、ポリカーボネート系樹脂、ポリアセタール系樹脂、フッ素系樹脂、その他の強靱な樹脂のフィルムないしシート、その他を使用することができる。一例として、補強層58は、ポリエチレンテレフタレートを含んでいてもよい。補強層58がポリエチレンテレフタレートを含む場合、ポリエチレンテレフタレートはバイオマス由来成分を含んでいてもよい。
まず、図3Aに示す積層体50を作製した。この際、まず、第1紙基材層52として、未晒紙(王子マテリア社製、厚み120μm)を準備した。また、第1シーラント層51用の樹脂としてポリエチレンを準備した。
PE/未晒紙
上記において、「PE」は、ポリエチレンを意味している(以下同様)。
PE/未晒紙/EMAA/ALM/接着剤/PETフィルム/PE/PEフィルム
上記において、「EMAA」は、エチレン-メタクリル酸共重合体を意味している(以下同様)。また、「ALM」は、バリア層としてのアルミ箔を意味している(以下同様)。「PETフィルム」は、ポリエチレンテレフタレートフィルムを意味している(以下同様)。「PEフィルム」は、ポリエチレンフィルムを意味している(以下同様)。
印/PE/未晒紙/EMAA/ALM/接着剤/PETフィルム/PE/PEフィルム
上記において、「印」は印刷層を意味している(以下同様)。
次に、剥離強度測定試験を行った。この際、浸漬試験を行うことなく、剥離強度測定試験を行った。剥離強度測定試験は、JIS K7127に準拠して行った。試験片Sとしては、胴部チューブ30を、幅(W)15mm、長さ(L)60mmの矩形状に切り出したものを用いた(図5(a)参照)。また、胴部チューブ30を切り出す際、試験片Sの幅方向が胴部チューブ30の周方向となるように、胴部チューブ30を切り出した。このようにして、3つの試験片Sを作製した。次に、これらの試験片Sについて、引張試験機(A&D社製、テンシロン万能材料試験機RTC-1310)を用いて、第1紙基材層52の剥離強度を測定した。
また、浸漬試験を行うとともに、剥離強度測定試験を行った。この際、まず、浸漬試験を行った。浸漬試験では、まず、上述した浸漬試験前の剥離強度測定試験と同様に、胴部チューブ30を、幅(W)15mm、長さ(L)60mmの矩形状に切り出した試験片Sを3つ作製した。また、上述した浸漬試験前の剥離強度測定試験と同様に、第1紙基材層52の一部分を他の部分から剥離した。剥離した部分の長手方向に沿った長さは、約2cmとした。
次に、外観評価試験を行った。この際、図9に示すように、まず、水Wが充填された容器100内に、チューブ容器10を収容した。このとき、口部42を上にして開口部50Bからチューブ容器10内へ水Wが入り込むように、チューブ容器10を倒立させた状態で容器100内に収容した。そして、胴部チューブ30の約半分を水Wに浸漬させた。次に、チューブ容器10が収容された容器100を、保管温度を40℃に設定した恒温槽101で一週間保管した。その後、チューブ容器10の外観に変化がないか目視で確認した。
まず、図3Bに示す積層体50を作製した。この際、まず、第1紙基材層52として、晒紙(天間特殊製紙社製、厚み80μm)を準備した。また、第2紙基材層54として、未晒紙(厚み100μm)を準備した。
印/晒紙/PE/未晒紙
PE/印/晒紙/PE/未晒紙
PE/印/晒紙/PE/未晒紙/EMAA/透明蒸着PETフィルム/PE/乳白PEフィルム
上記において、「透明蒸着PETフィルム」は、透明蒸着層およびガスバリア性塗布膜が設けられたポリエチレンテレフタレートフィルムを意味している。「乳白PEフィルム」は、乳白ポリエチレンフィルムを意味している(以下同様)。
第1紙基材層52として、厚みが75μmの晒紙を使用したこと、第2紙基材層54として、晒紙(天間特殊製紙社製、厚み75μm)を使用したこと、第2シーラント層53として、ポリエチレンフィルム(厚み120μm)を使用したこと、以外は実施例2と同様にして、浸漬試験前の剥離強度測定試験、浸漬試験後の剥離強度測定試験および外観評価試験を行った。実施例2による積層体50の層構成は、以下の通りである。
PE/印/晒紙/PE/晒紙/EMAA/ALM/接着剤/PETフィルム/PE/PEフィルム
第1紙基材層として、厚みが120μmの未晒紙(中越パルプ工業社製)を使用したこと以外は実施例1と同様にして、浸漬試験前の剥離強度測定試験、浸漬試験後の剥離強度測定試験および外観評価試験を行った。比較例による積層体の層構成は、以下の通りである。
印/PE/未晒紙/EMAA/ALM/接着剤/PETフィルム/PE/PEフィルム
第1紙基材層として、厚みが120μmの晒紙(大王製紙社製)を使用したこと、第2紙基材層を設けなかったこと、第2シーラント層として、厚みが120μmの乳白ポリエチレンフィルムを使用したこと、以外は実施例2と同様にして、浸漬試験前の剥離強度測定試験、浸漬試験後の剥離強度測定試験および外観評価試験を行った。比較例による積層体の層構成は、以下の通りである。
PE/印/晒紙/EMAA/透明蒸着PETフィルム/PE/乳白PEフィルム
10A キャップ付きチューブ容器
20 キャップ
30 胴部チューブ
31 一端
32 胴部シール部
35 端部
40 頭部部材
50 積層体
501 外面
502 内面
51 第1シーラント層
52 第1紙基材層
53 第2シーラント層
54 第2紙基材層
Claims (5)
- チューブ容器用包材において、
外面から内面に向かって順に配置された第1シーラント層と、第1紙基材層と、第2紙基材層と、バリア層と、第2シーラント層とを備え、
浸漬試験後の前記第1紙基材層内の剥離強度が、0.40N/15mm以上であり、
前記第1紙基材層を構成する紙は、晒紙、半晒紙または未晒紙であり、
前記第1紙基材層の厚みは、50μm以上160μm以下であり、
前記バリア層は、アルミニウム箔を含む、チューブ容器用包材。 - 前記第1シーラント層の面のうち前記外面側の面上に形成された印刷層を更に備える、請求項1に記載のチューブ容器用包材。
- 前記第1紙基材層の面のうち前記外面側の面上に形成された印刷層を更に備える、請求項1に記載のチューブ容器用包材。
- 浸漬試験後の前記第2紙基材層の剥離強度が、0.40N/15mm以上である、請求項1乃至3のいずれか一項に記載のチューブ容器用包材。
- 前記第2紙基材層の厚みは、50μm以上160μm以下である、請求項1乃至4のいずれか一項に記載のチューブ容器用包材。