JP6864012B2 - 道路舗装用アスファルト組成物 - Google Patents
道路舗装用アスファルト組成物 Download PDFInfo
- Publication number
- JP6864012B2 JP6864012B2 JP2018562788A JP2018562788A JP6864012B2 JP 6864012 B2 JP6864012 B2 JP 6864012B2 JP 2018562788 A JP2018562788 A JP 2018562788A JP 2018562788 A JP2018562788 A JP 2018562788A JP 6864012 B2 JP6864012 B2 JP 6864012B2
- Authority
- JP
- Japan
- Prior art keywords
- polyester resin
- less
- asphalt
- mass
- road pavement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
このアスファルト舗装は、骨材をアスファルトで結合したアスファルト組成物によって路面が形成されているので、舗装道路は良好な硬度や耐久性を有している。
しかしながら、アスファルトは、石油精製品であるため、同じ石油精製品であるガソリン、軽油、重油、灯油、エンジン用潤滑油などに溶解する性質を持っている。そのため、車両などから燃料や潤滑油が路面に漏れた場合、アスファルトが溶解し、アスファルト組成物が侵され、ポットホールなどの舗装破壊が生じていた。したがって、舗装の補修を行う必要が生じ、維持費用が増大するとともに、自動車の交通に大きな影響を与える結果となっていた。
[1]アスファルト、ポリエステル樹脂、及び骨材を含有し、
前記ポリエステル樹脂が、溶融混練されたものであり、
前記ポリエステル樹脂の比率が、前記アスファルト100質量部に対し5質量部以上50質量部以下である、道路舗装用アスファルト組成物。
[2]アスファルト、ポリエステル樹脂、及び骨材を130℃以上200℃以下で混合する工程を有し、
前記混合する工程で使用する前記ポリエステル樹脂が、溶融混練されたものであり、
前記ポリエステル樹脂の比率が、前記アスファルト100質量部に対し5質量部以上50質量部以下である、道路舗装用アスファルト組成物の製造方法。
[3]上記[2]に記載の製造方法により得られたアスファルト組成物を塗工し、アスファルト舗装材層を形成する工程を有する道路舗装方法。
そこで、本発明は、乾燥強度、水浸漬強度、及び石油浸漬強度に優れる、道路舗装用アスファルト組成物、その製造方法、及び道路舗装方法に関する。
[1]アスファルト、ポリエステル樹脂、及び骨材を含有し、
前記ポリエステル樹脂が、溶融混練されたものであり、
前記ポリエステル樹脂の比率が、前記アスファルト100質量部に対し5質量部以上50質量部以下である、道路舗装用アスファルト組成物。
[2]アスファルト、ポリエステル樹脂、及び骨材を130℃以上200℃以下で混合する工程を有し、
前記混合する工程で使用する前記ポリエステル樹脂が、溶融混練されたものであり、
前記ポリエステル樹脂の比率が、前記アスファルト100質量部に対し5質量部以上50質量部以下である、道路舗装用アスファルト組成物の製造方法。
[3]上記[2]に記載の製造方法により得られたアスファルト組成物を塗工し、アスファルト舗装材層を形成する工程を有する道路舗装方法。
本発明の道路舗装用アスファルト組成物は、アスファルト、ポリエステル樹脂、及び骨材を含有し、
前記ポリエステル樹脂が、溶融混練されたものであり、
前記ポリエステル樹脂の比率が、前記アスファルト100質量部に対し5質量部以上50質量部以下である。
本発明では、溶融混練を行うことで重量平均分子量が増大し、分子量分布が広くなったポリエステル樹脂を用いることによりポリエステルが様々な骨材と絡みあい、乾燥強度、水浸漬強度、及び石油浸漬強度が向上すると考えられる。これはポリエステルの分子量分布が広がることで、ポリエステル樹脂中に幅広い親疎水性の材料が分散したことによると考えられる。
ポリエステル樹脂は、アルコール成分由来の構成単位とカルボン酸成分由来の構成単位と含むポリエステルである。
ここで、ポリエステル中、アルコール成分由来の構成単位とは、アルコール成分の水酸基から水素原子を除いた構造を意味し、カルボン酸成分由来の構成単位とは、カルボン酸成分のカルボキシル基から水酸基を除いた構造を意味する。
アルコール成分としては、脂肪族ジオール、芳香族ジオール、3価以上の多価アルコール等が挙げられる。これらのアルコール成分は、単独で又は2種以上を組み合わせて使用することができる。
アルコール成分は、優れた乾燥強度を得る観点から、ビスフェノールAのアルキレンオキシド付加物を含み、好ましくは式(I):
〔式中、OR1及びR1Oはアルキレンオキシドであり、R1は炭素数2又は3のアルキレン基、x及びyはアルキレンオキシドの平均付加モル数を示す正の数を示し、xとyの和は1以上、好ましくは1.5以上であり、そして、16以下、好ましくは8以下、より好ましくは4以下である〕で表されるビスフェノールAのアルキレンオキシド付加物を含むことが好ましい。
カルボン酸成分は、優れた乾燥強度を得る観点から、好ましくはテレフタル酸、イソフタル酸、フマル酸及びマレイン酸からなる群から選ばれる1種以上を含み、より好ましくはテレフタル酸及びフマル酸からなる群から選ばれる1種以上を含み、より好ましくはテレフタル酸を含む。
カルボン酸成分中、テレフタル酸、イソフタル酸、フマル酸及びマレイン酸から選ばれる1種以上の量は、アスファルトへの溶融分散性に優れ、乾燥強度を向上させる観点から、50モル%以上、好ましくは60モル%以上、より好ましくは80モル%以上であり、そして好ましくは100モル%以下、そしてより好ましくは100モル%である。
脂肪族ジカルボン酸の主鎖の炭素数は、乾燥強度をより向上させる観点から、好ましくは4以上であり、そして、好ましくは10以下、より好ましくは8以下、より好ましくは6以下である。
具体例としては、シュウ酸、マロン酸、シトラコン酸、イタコン酸、グルタコン酸、コハク酸、アジピン酸、スベリン酸、アゼライン酸、セバシン酸、ドデカン二酸等が挙げられる。また、脂肪族ジカルボン酸の例には、ドデシルコハク酸、ドデセニルコハク酸、オクテニルコハク酸等の炭素数1以上20以下のアルキル基又は炭素数2以上20以下のアルケニル基で置換されたコハク酸も含まれる。これらの中でも、乾燥強度をより向上させる観点から、アジピン酸、ドデセニルコハク酸又はオクテニルコハク酸が好ましく、アジピン酸がより好ましい。
3価以上の多価カルボン酸の例としては、トリメリット酸、2,5,7−ナフタレントリカルボン酸、ピロメリット酸等の3価以上の多価カルボン酸、並びにそれらの酸無水物及びそれらのアルキル(炭素数1以上3以下)エステル等が挙げられ、乾燥強度をより向上させる観点から、トリメリット酸又はその酸無水物が好ましい。
カルボン酸成分中の、3価以上の多価カルボン酸の含有量は、乾燥強度をより向上させる観点から、好ましくは1モル%以上、より好ましくは3モル%以上、より好ましくは5モル%以上であり、そして、好ましくは30モル%以下、より好ましくは20モル%以下、より好ましくは10モル%以下である。
アルコール成分由来の構成単位に対するカルボン酸成分由来の構成単位のモル比〔カルボン酸成分/アルコール成分〕は、骨材に対して高い接着強度を示し、乾燥強度を向上させる観点から、好ましくは0.7以上、より好ましくは0.8以上であり、そして、好ましくは1.5以下、より好ましくは1.3以下、より好ましくは1.1以下、より好ましくは1.0未満である。
なお、物性調整の観点から、アルコール成分には1価のアルコールが適宜含有されていてもよく、カルボン酸成分には1価のカルボン酸化合物が適宜含有されていてもよい。
以下、溶融混練前のポリエステル樹脂の物性について説明する。
ポリエステル樹脂の酸価は、好ましくは2mgKOH/g以上、より好ましくは3mgKOH/g以上、より好ましくは3.5mgKOH/g以上であり、そして、好ましくは30mgKOH/g以下、より好ましくは15mgKOH/g以下、より好ましくは12mgKOH/g以下、より好ましくは10mgKOH/g以下である。
ポリエステル樹脂の水酸基価は、骨材に対して高い接着強度を示し、乾燥強度を向上させる観点から、好ましくは20mgKOH/g以上、より好ましくは30mgKOH/g以上、より好ましくは35mgKOH/g以上であり、そして、乾燥強度及び水浸漬強度を向上させる観点から、好ましくは50mgKOH/g以下、より好ましくは45mgKOH/g以下である。
ポリエステル樹脂のガラス転移点は、乾燥強度を向上させる観点から、好ましくは50℃以上、より好ましくは55℃以上であり、そして、乾燥強度を向上させる観点から、好ましくは80℃以下、より好ましくは70℃以下である。
なお、酸価、水酸基価、軟化点及びガラス転移点は、原料モノマー組成、分子量、触媒量又は反応条件により調整することができる
また、ポリエステル樹脂は、単独で又は2種以上を組み合わせて使用することができる。2種以上を組み合わせて使用する場合、軟化点はその混合物を実施例の方法によって求めた値である。
ポリエステル樹脂の製造方法は、特に限定されるものではないが、例えば、上述したアルコール成分及びカルボン酸成分を重縮合することにより製造することができる。
アルコール成分とカルボン酸の夫々の配合量は、アルコール成分由来の構成単位に対するカルボン酸成分由来の構成単位のモル比〔カルボン酸成分/アルコール成分〕が上述した数値範囲内になるような配合量である。
即ち、ポリエステル樹脂の製造方法は、例えば、上述したアルコール成分及びカルボン酸成分を、アルコール成分由来の構成単位に対するカルボン酸成分由来の構成単位のモル比〔カルボン酸成分/アルコール成分〕が上述した数値範囲内になるような配合量で重縮合することにより製造することができる。
重縮合反応の温度は、反応性の観点から、好ましくは160℃以上、より好ましくは190℃以上、より好ましくは220℃以上であり、そして、好ましくは260℃以下、より好ましくは250℃以下、より好ましくは240℃以下である。
チタン化合物としては、Ti-O結合を有するチタン化合物が好ましく、総炭素数1以上28以下のアルコキシ基、アルケニルオキシ基又はアシルオキシ基を有するチタン化合物がより好ましい。
Sn-C結合を有していない錫(II)化合物としては、Sn-O結合を有する錫(II)化合物、Sn-X(Xはハロゲン原子を示す)結合を有する錫(II)化合物等が好ましく挙げられ、Sn-O結合を有する錫(II)化合物がより好ましく、中でも、反応性、分子量調整及び複合樹脂の物性調整の観点から、ジ(2−エチルヘキサン酸)錫(II)がより好ましい。
上記エステル化触媒の使用量は、反応性の観点から、アルコール成分とカルボン酸成分との総量100質量部に対して、好ましくは0.01質量部以上、より好ましくは0.1質量部以上、より好ましくは0.2質量部以上であり、そして、好ましくは1.5質量部以下、より好ましくは1.0質量部以下、より好ましくは0.6質量部以下である。
エステル化助触媒の使用量は、反応性の観点から、アルコール成分とカルボン酸成分との総量100質量部に対して、好ましくは0.001質量部以上、より好ましくは0.005質量部以上、より好ましくは0.01質量部以上であり、そして、好ましくは0.15質量部以下、より好ましくは0.10質量部以下、より好ましくは0.05質量部以下である。
本発明のポリエステル樹脂は、溶融混練されたものである。ポリエステル樹脂は、溶融混練を経ることで、分子量分布が広くなり、乾燥強度、水浸漬強度、及び石油浸漬強度に優れるアスファルト組成物が得られる。
当該ポリエステル樹脂の製造方法は、好ましくは下記の工程A-1を少なくとも有し、更に好ましくは下記の工程A-1及び工程A-2を有する。
工程A-1:ポリエステル樹脂を含む原料混合物を溶融混練する工程
工程A-2:工程A-1で得られた溶融混練物を粉砕する工程
工程A-1では、ポリエステル樹脂に加えて、更に顔料、ワックス等の添加剤とともに溶融混練することが好ましい。溶融混練時に顔料(中でもカーボンブラック)を分散させることにより、アスファルト組成物中でも顔料が微分散しフィラーとして作用するため、乾燥強度が向上する。
本発明において「溶融混練」とは、樹脂を、該樹脂が流動性を有する温度で、混練機により混練することを意味する。
なお、原料混合物は、あらかじめヘンシェルミキサー、ボールミル等の混合機で混合した後、混練機に供給することが好ましい。
顔料はポリエステル樹脂中に分散していることが好ましい。
顔料としては、特に制限はなく公知の顔料が挙げられ、目的に応じて適宜選択することができる。具体的には、カーボンブラック、無機系複合酸化物、クロムイエロー、ハンザイエロー、ベンジジンイエロー、スレンイエロー、キノリンイエロー、パーマネントオレンジGTR、ピラゾロンオレンジ、バルカンオレンジ、ウオッチヤングレッド、パーマネントレッド、ブリリアンカーミン3B、ブリリアンカーミン6B、デュポンオイルレッド、ピラゾロンレッド、リソールレッド、ローダミンBレーキ、レーキレッドC、ベンガル、アニリンブルー、ウルトラマリンブルー、カルコオイルブルー、メチレンブルークロライド、フタロシアニンブルー、フタロシアニングリーン、及びマラカイトグリーンオクサレート等の種々の顔料が挙げられる。これらは単独で又は2種以上を組み合わせて使用することができる。
これらの中でも、顔料は、好ましくはカーボンブラックを含む。
ワックスとしては、ポリエチレン、ポリプロピレン、ポリブテン等の低分子量ポリオレフィン;シリコーンワックス;オレイン酸アミド、ステアリン酸アミド等の脂肪酸アミド;カルナウバワックス、ライスワックス、キャンデリラワックス等の植物系ワックス;ミツロウ等の動物系ワックス;モンタンワックス、パラフィンワックス、フィッシャートロプシュワックス等の鉱物系又は石油系ワックス;エステルワックス等の合成ワックス等が挙げられる。これらのワックスは、1種を単独で又は2種以上を組み合わせて使用することができる。
なお、上記溶融混練時の原料混合物には、骨材を含まないことが好ましい。
溶融混練には、密閉式ニーダ、一軸又は二軸の押出機などの混練押出機、オープンロール型混練機等の公知の混練機を用いて行うことができる。これらの中でも、混練押出機、オープンロール型混練機が好ましく、混練押出機がより好ましく、二軸押出機がより好ましい。
溶融混練の混練温度は、乾燥強度、水浸漬強度、及び石油浸漬強度を向上させる観点から、好ましくは90℃以上、より好ましくは100℃以上であり、そして、好ましくは140℃以下、より好ましくは120℃以下である。二軸押出機を使用する場合、前記の混練温度は、バレル温度である。
二軸押出機を使用する場合、軸回転の回転速度は、乾燥強度、水浸漬強度、及び石油浸漬強度を向上させる観点から、好ましくは50r/min以上、より好ましくは100r/min以上、より好ましくは150r/min以上であり、そして、好ましくは400r/min以下、より好ましくは300r/min以下、より好ましくは250r/min以下である。
二軸押出機への混合物の供給速度は、使用する混練機の許容能力と、上記のバレル温度及び軸回転の回転速度に応じて適宜調整する。
工程A-1では、ポリエステル樹脂の軟化点は、乾燥強度、水浸漬強度、及び石油浸漬強度を向上させる観点から、前記溶融混練前に比べて、好ましくは5℃以上、より好ましくは8℃以上、より好ましくは10℃以上、そして、好ましくは40℃以下、より好ましくは30℃以下、より好ましくは20℃以下、低下させることが好ましい。
工程A-1で得られるポリエステル樹脂の重量平均分子量Mwは、乾燥強度、水浸漬強度、及び石油浸漬強度を向上させる観点から、前記溶融混練前に比べて、好ましくは2倍以上、より好ましくは3倍以上、より好ましくは4倍以上、そして、好ましくは100倍以下、より好ましくは80倍以下、より好ましくは40倍以下、より好ましくは20倍以下、より好ましくは10倍以下、増加している。
工程A-1で得られるポリエステル樹脂の分子量分布(Mw/Mn)は、乾燥強度、水浸漬強度、及び石油浸漬強度を向上させる観点から、前記溶融混練前に比べて、好ましくは2倍以上、より好ましくは3倍以上、より好ましくは4倍以上、そして、好ましくは80倍以下、より好ましくは40倍以下、より好ましくは20倍以下、より好ましくは10倍以下、増加している。
以下、溶融混練後のポリエステル樹脂の物性について説明する。
ポリエステル樹脂の酸価は、好ましくは2mgKOH/g以上、より好ましくは3mgKOH/g以上、より好ましくは3.5mgKOH/g以上であり、そして、好ましくは30mgKOH/g以下、より好ましくは15mgKOH/g以下、より好ましくは12mgKOH/g以下、より好ましくは10mgKOH/g以下である。
ポリエステル樹脂の水酸基価は、骨材に対して高い接着強度を示し、乾燥強度を向上させる観点から、好ましくは20mgKOH/g以上、より好ましくは30mgKOH/g以上、より好ましくは35mgKOH/g以上であり、そして、乾燥強度及び水浸漬強度を向上させる観点から、好ましくは50mgKOH/g以下、より好ましくは45mgKOH/g以下である。
溶融混練後のポリエステル樹脂の軟化点は、乾燥強度、水浸漬強度、及び石油浸漬強度を向上させる観点から、溶融混練前に比べて、好ましくは5℃以上、より好ましくは8℃以上、より好ましくは10℃以上、そして、好ましくは40℃以下、より好ましくは30℃以下、より好ましくは20℃以下、低下している。
ポリエステル樹脂のガラス転移点は、乾燥強度を向上させる観点から、好ましくは50℃以上、より好ましくは55℃以上であり、そして、乾燥強度を向上させる観点から、好ましくは80℃以下、より好ましくは70℃以下である。
ポリエステル樹脂のTHFに対する可溶分のGPC測定における重量平均分子量Mwは、乾燥強度、水浸漬強度、及び石油浸漬強度を向上させる観点から、溶融混練前に比べて、好ましくは2倍以上、より好ましくは3倍以上、より好ましくは4倍以上、そして、好ましくは100倍以下、より好ましくは80倍以下、より好ましくは40倍以下、より好ましくは20倍以下、より好ましくは10倍以下、増加している。
なお、酸価、水酸基価、軟化点及びガラス転移点は、原料モノマー組成、分子量、触媒量又は反応条件により調整することができる
また、ポリエステル樹脂は、単独で又は2種以上を組み合わせて使用することができる。2種以上を組み合わせて使用する場合、軟化点はその混合物を実施例の方法によって求めた値である。
工程A-2では、工程A-1で得られた溶融混練物を粉砕する。
粉砕工程は、多段階に分けて行ってもよい。例えば、溶融混練物を硬化させて得られた樹脂混練物を、1〜5mm程度に粗粉砕した後、さらに所望の粒径に微粉砕してもよい。
粉砕に使用する粉砕機としては、市販品として、株式会社三力製作所製「SF-1」等が挙げられる。
分級工程に用いられる分級機としては、例えば、ロータ式分級機、気流式分級機、慣性式分級機、篩式分級機等が挙げられる。分級工程の際、粉砕が不十分であれば再度粉砕工程に供してもよく、必要に応じて粉砕工程と分級工程を繰り返してもよい。
外添剤の添加量は、ポリエステル樹脂粒子の流動性を向上させる観点から、処理前の樹脂粒子100質量部に対して、好ましくは0.1質量部以上、より好ましくは0.5質量部以上、より好ましくは1質量部以上であり、そして、好ましくは5質量部以下、より好ましくは4質量部以下、より好ましくは3質量部以下である。
ポリエステル樹脂は、ポリエステル樹脂粒子であることが好ましい。
ポリエステル樹脂粒子の平均粒径は、樹脂の分散性を高めて、乾燥強度を向上させる観点から、好ましくは1μm以上、より好ましくは2μm以上、より好ましくは3μm以上であり、そして、好ましくは10mm以下、より好ましくは2mm以下、樹脂の分散性を高めて、乾燥強度を向上させる観点から、より好ましくは20μm以下、より好ましくは15μm以下、より好ましくは10μm以下である。ポリエステル樹脂粒子の平均粒径が1μm以上20μm以下であることで、アスファルトと混合溶融時に微分散して、骨材への絡み合い(吸着)時間が短くなり、乾燥強度が向上する。
なお、上記平均粒径は、JIS Z 8815の規定に準じて測定した値である。具体的には、開口目開き2830μm、2000μm、1400μm、850μm、600μm、425μm、106μmの7つの篩を用いて、試料の篩分けを行う。各篩の目をその粒径として、各篩に残留した試料の重量により、算出された加重平均粒径を平均粒径とする。
ポリエステル樹脂の比率は、乾燥強度を向上させる観点から、アスファルト100質量部に対して、5質量部以上であり、好ましくは8質量部以上、より好ましくは10質量部以上、より好ましくは15質量部以上であり、そして、50質量部以下であり、好ましくは40質量部以下、より好ましくは30質量部以下である。
本発明に用いるアスファルトとしては、例えば、種々のアスファルトが使用できる。例えば、舗装用石油アスファルトであるストレートアスファルトの他、改質アスファルトが挙げられる。
ストレートアスファルトとは、原油を常圧蒸留装置,減圧蒸留装置などにかけて得られる残留瀝青物質のことである。
改質アスファルトとしては、ブローンアスファルト;熱可塑性エラストマー、熱可塑性樹脂など高分子材料で改質したアスファルト等が挙げられる。
前記熱可塑性エラストマーとしては、例えば、スチレン/ブタジエン/ブロック共重合体(SBS)、スチレン/イソプレン/ブロック共重合体(SIS)、エチレン/酢酸ビニル共重合体(EVA)等が挙げられる。
前記熱可塑性樹脂としては、例えば、エチレン/酢酸ビニル共重合体、エチレン/エチルアクリレート共重合体、ポリエチレン、ポリプロピレン等が挙げられる。
アスファルト、中でもストレートアスファルトの針入度としては、好ましくは40超え、そして、好ましくは120以下、より好ましくは80以下、更に好ましくは60以下である。針入度の測定方法は、JIS K 2207に規定された方法による。なお、JIS K 2207に記載された試験条件の下で、規定の針が試料中に垂直に進入した長さ0.1mmを1として表す。
アスファルト組成物中のアスファルトの含有量は、好ましくは2質量%以上、より好ましくは3質量%以上であり、そして、好ましくは15質量%以下、より好ましくは10質量%以下、より好ましくは8質量%以下である。
本発明のアスファルト組成物は、骨材を含有する。
骨材としては、例えば、砕石、玉石、砂利、砂、再生骨材、セラミックスなどを任意に選択して用いることができる。
骨材としては、粒径2.36mm以上の粗骨材、粒径2.36mm未満の細骨材のいずれも使用することができる。粗骨材としては、例えば、粒径範囲2.36mm以上4.75mm以下の7号砕石、粒径範囲4.75mm以上13.2mm以下の6号砕石、粒径範囲13.2mm以上19mm以下の5号砕石、粒径範囲19mm以上31.5mm以下の4号砕石が挙げられる。
細骨材は、好ましくは粒径0.075mm以上2.36mm未満の細骨材である。
細骨材としては、例えば、川砂、丘砂、山砂、海砂、砕砂、細砂、スクリーニングス、砕石ダスト、シリカサンド、人工砂、ガラスカレット、鋳物砂、再生骨材破砕砂が挙げられる。
上記の粒径はJIS 5001-1995に規定される値である。
これらの中でも、粗骨材と細骨材との組み合わせが好ましい。
フィラーの平均粒径は、乾燥強度向上の観点から、好ましくは0.001mm以上であり、そして、好ましくは0.05mm以下、より好ましくは0.03mm以下、更に好ましくは0.02mm以下である。フィラーの平均粒径は、レーザー回折式粒度分布測定装置で測定することができる。ここで、平均粒径とは、体積累積50%の平均粒径を意味する。
フィラーの平均粒径は、レーザー回折式粒度分布測定装置(堀場製作所株式会社製「LA-950」)を用い、以下に示す条件で測定した値である。
・測定方法:フロー法
・分散媒:エタノール
・試料調製:2mg/100mL
・分散方法:攪拌、内蔵超音波1分
骨材の含有量は、アスファルトとポリエステル樹脂の合計100質量部に対して、好ましくは1,000質量部以上、より好ましくは1,200質量部以上、より好ましくは1,500質量部以上であり、そして、好ましくは3,000質量部以下、より好ましくは2,500質量部以下、更に好ましくは2,000質量部以下である。
(1)一例のアスファルト組成物は、例えば、30容量%以上45容量%未満の粗骨材と、30容量%以上50容量%以下の細骨材と、5容量%以上10容量%以下のアスファルト及びポリエステル樹脂とを含む(細粒度アスファルト)。
(2)一例のアスファルト組成物は、例えば、45容量%以上70容量%未満の粗骨材と、20容量%以上45容量%以下の細骨材と、3容量%以上10容量%以下のアスファルト及びポリエステル樹脂とを含む(密粒度アスファルト)。
(3)一例のアスファルト組成物は、例えば、70容量%以上80容量%以下の粗骨材と、10容量%以上20容量%以下の細骨材と、3容量%以上10容量%以下のアスファルト及びポリエステル樹脂とを含む(ポーラスアスファルト)。
なお、従来の骨材とアスファルトを含むアスファルト組成物におけるアスファルトの配合割合については、通常、社団法人日本道路協会発行の「舗装設計施工指針」に記載されている「アスファルト組成物の配合設計」から求められる最適アスファルト量に準じて決定している。
本発明においては、上記の最適アスファルト量が、アスファルト及びポリエステル樹脂の合計量に相当する。したがって、通常、前記最適アスファルト量を、アスファルト及びポリエステル樹脂の合計配合量とすることが好ましい。
但し、「舗装設計施工指針」に記載の方法に限定する必要はなく、他の方法によって決定してもよい。
本発明のアスファルト組成物は、水を実質的に含まない加熱アスファルト組成物として使用してもよく、また、上記アスファルト組成物に乳化剤や水を配合してアスファルト乳剤とし、常温アスファルト組成物として使用してもよい。
特に、本発明のアスファルト組成物は、ポリエステル樹脂がアスファルト組成物中に均一に分散しやすい性質を有するため、加熱アスファルト組成物として使用すると、その特徴を有効に発揮することができる。
本発明のアスファルト組成物の製造方法は、好ましくは、アスファルト、ポリエステル樹脂、及び骨材を130℃以上200℃以下で混合する工程(以下「工程1」ともいう)を有する。
工程1における混合時間は、好ましくは、30秒以上である。工程1における混合時間の上限は、特に限定されないが例えば約30分程度である。
また、アスファルトとポリエステル樹脂を高温、例えば、130℃以上(好ましくは150℃以上)で事前に攪拌しながら混合して、その混合物を投入してもよい(プレミックス法)。
本発明のアスファルト組成物は、道路舗装のために使用される。
〔工程2〕
本発明の道路舗装方法は、好ましくは、本発明のアスファルト組成物を塗工し、アスファルト舗装材層を形成する工程(以下「工程2」ともいう)を有する。
<1>アスファルト、ポリエステル樹脂、及び骨材を含有し、
前記ポリエステル樹脂が、溶融混練されたものであり、
前記ポリエステル樹脂の比率が、前記アスファルト100質量部に対し5質量部以上50質量部以下である、道路舗装用アスファルト組成物。
<3>ビスフェノールAのアルキレンオキシド付加物が、好ましくはビスフェノールAのプロピレンオキシド付加物、又はビスフェノールAのエチレンオキシド付加物であり、より好ましくはビスフェノールAのプロピレンオキシド付加物及びビスフェノールAのエチレンオキシド付加物の組み合せである、<2>に記載の道路舗装用アスファルト組成物。
<4>ビスフェノールAのアルキレンオキシド付加物の量が、アルコール成分中、好ましくは50モル%以上、より好ましくは65モル%以上であり、より好ましくは80モル%以上、より好ましくは90モル%以上であり、そして100モル%以下であり、そして更に好ましくは100モル%である、<2>又は<3>に記載の道路舗装用アスファルト組成物。
<5>ビスフェノールAのプロピレンオキシド付加物/ビスフェノールAのエチレンオキシド付加物のモル比率が、好ましくは10/90以上、より好ましくは20/80以上、更に好ましくは30/70以上であり、そして、好ましくは70/30以下、より好ましくは60/40以下、より好ましくは55/45以下である、<2>〜<4>のいずれかに記載の道路舗装用アスファルト組成物。
<6>ポリエステル樹脂のカルボン酸成分が、好ましくはテレフタル酸、イソフタル酸、フマル酸及びマレイン酸からなる群から選ばれる1種以上を含み、より好ましくはテレフタル酸及びフマル酸からなる群から選ばれる1種以上を含み、より好ましくはテレフタル酸を含む、<1>〜<5>のいずれかに記載の道路舗装用アスファルト組成物。
<8>溶融混練の混練温度が、好ましくは90℃以上、より好ましくは100℃以上であり、そして、好ましくは140℃以下、より好ましくは120℃以下である、<1>〜<7>のいずれかに記載の道路舗装用アスファルト組成物。
<9>溶融混練において、二軸押出機を使用し、軸回転の回転速度が、好ましくは50r/min以上、より好ましくは100r/min以上、より好ましくは150r/min以上であり、そして、好ましくは400r/min以下、より好ましくは300r/min以下、より好ましくは250r/min以下である、<1>〜<8>のいずれかに記載の道路舗装用アスファルト組成物。
<10>溶融混練は、ポリエステル樹脂の軟化点が、溶融混練前に比べて5℃以上40℃以下、低下するまで、ポリエステル樹脂を溶融混練し、軟化点90℃以上150℃以下のポリエステル樹脂を得る工程である、<1>〜<9>のいずれかに記載の道路舗装用アスファルト組成物。
<11>ポリエステル樹脂の軟化点が、溶融混練前に比べて、好ましくは5℃以上、好ましくは8℃以上、より好ましくは10℃以上、そして、好ましくは40℃以下、より好ましくは30℃以下、より好ましくは20℃以下、低下させるまで溶融混練する、<10>に記載の道路舗装用アスファルト組成物。
<12>溶融混練は、ポリエステル樹脂のTHFに対する可溶分のGPC測定における重量平均分子量Mwが、溶融混練前に比べて2倍以上100倍以下、増加するまで、ポリエステル樹脂を溶融混練する工程である、<1>〜<11>のいずれかに記載の道路舗装用アスファルト組成物。
<13>溶融混練は、ポリエステル樹脂の重量平均分子量Mwが、溶融混練前に比べて、好ましくは2倍以上、より好ましくは3倍以上、より好ましくは4倍以上、そして、好ましくは100倍以下、より好ましくは80倍以下、より好ましくは40倍以下、より好ましくは20倍以下、より好ましくは10倍以下、増加するまで溶融混練する、<12>に記載の道路舗装用アスファルト組成物。
<14>溶融混練は、ポリエステル樹脂のTHFに対する可溶分のGPC測定における分子量分布(Mw/Mn)が、溶融混練前に比べて2倍以上100倍以下、増加するまで、ポリエステル樹脂を溶融混練する工程である、<1>〜<13>のいずれかに記載の道路舗装用アスファルト組成物。
<15>溶融混練は、ポリエステル樹脂の分子量分布(Mw/Mn)が、溶融混練前に比べて、好ましくは2倍以上、より好ましくは3倍以上、より好ましくは4倍以上、そして、好ましくは80倍以下、より好ましくは40倍以下、より好ましくは20倍以下、より好ましくは10倍以下、増加するまで溶融混練する、<14>に記載の道路舗装用アスファルト組成物。
<17>溶融混練後のポリエステル樹脂の水酸基価が、好ましくは20mgKOH/g以上、より好ましくは30mgKOH/g以上、より好ましくは35mgKOH/g以上であり、そして、好ましくは50mgKOH/g以下、より好ましくは45mgKOH/g以下である、<1>〜<16>のいずれかに記載の道路舗装用アスファルト組成物。
<18>溶融混練後のポリエステル樹脂の軟化点が、好ましくは90℃以上、より好ましくは95℃以上、より好ましくは100℃以上であり、そして、好ましくは150℃以下、より好ましくは140℃以下であり、更に好ましくは130℃以下である、<1>〜<17>のいずれかに記載の道路舗装用アスファルト組成物。
<19>溶融混練後のポリエステル樹脂の軟化点が、溶融混練前に比べて、好ましくは5℃以上、より好ましくは8℃以上、より好ましくは10℃以上、そして、好ましくは40℃以下、より好ましくは30℃以下、より好ましくは20℃以下、低下している、<1>〜<18>のいずれかに記載の道路舗装用アスファルト組成物。
<20>溶融混練後のポリエステル樹脂のガラス転移点が、好ましくは50℃以上、より好ましくは55℃以上であり、そして、好ましくは80℃以下、より好ましくは70℃以下である、<1>〜<19>のいずれかに記載の道路舗装用アスファルト組成物。
<21>溶融混練後のポリエステル樹脂の重量平均分子量Mwが、好ましくは10,000以上、より好ましくは20,000以上、より好ましくは30,000以上、より好ましくは50,000以上であり、そして、好ましくは500,000以下、より好ましくは300,000以下、より好ましくは200,000以下である、<1>〜<19>のいずれかに記載の道路舗装用アスファルト組成物。
<22>溶融混練後のポリエステル樹脂のTHFに対する可溶分のGPC測定における重量平均分子量Mwが、溶融混練前に比べて、好ましくは2倍以上、より好ましくは3倍以上、より好ましくは4倍以上、そして、好ましくは100倍以下、より好ましくは80倍以下、より好ましくは40倍以下、より好ましくは20倍以下、より好ましくは10倍以下、増加している、<1>〜<21>のいずれかに記載の道路舗装用アスファルト組成物。
<23>溶融混練後のポリエステル樹脂の数平均分子量Mnが、好ましくは1,000以上、より好ましくは2,000以上、より好ましくは2,500以上であり、そして、好ましくは20,000以下、より好ましくは10,000以下、より好ましくは5,000以下である、<1>〜<22>のいずれかに記載の道路舗装用アスファルト組成物。
<24>溶融混練後のポリエステル樹脂の分子量分布(Mw/Mn)が、好ましくは2以上、より好ましくは4以上、更に好ましくは10以上、更に好ましくは20以上、更に好ましくは30以上であり、そして、好ましくは100以下、より好ましくは80以下、より好ましくは60以下である、<1>〜<23>のいずれかに記載の道路舗装用アスファルト組成物。
<25>溶融混練後のポリエステル樹脂のTHF不溶分が、好ましくは10質量%以下、より好ましくは5質量%以下、更に好ましくは1質量%以下であり、そして、好ましくは0質量%以上であり、そして、更に好ましくは0質量%である、<1>〜<24>のいずれかに記載の道路舗装用アスファルト組成物。
<26>ポリエステル樹脂が、平均粒径1μm以上20μm以下のポリエステル樹脂粒子を配合してなるものである、<1>〜<25>のいずれかに記載の道路舗装用アスファルト組成物。
<27>ポリエステル樹脂粒子の平均粒径が、好ましくは1μm以上、より好ましくは2μm以上、より好ましくは3μm以上であり、そして、好ましくは10mm以下、より好ましくは2mm以下、好ましくは20μm以下、より好ましくは15μm以下、より好ましくは10μm以下である、<1>〜<26>のいずれかに記載の道路舗装用アスファルト組成物。
<29>アスファルトがストレートアスファルトである、<1>〜<28>のいずれかに記載の道路舗装用アスファルト組成物。
<30>アスファルトの含有量は、アスファルト組成物中、好ましくは2質量%以上、より好ましくは3質量%以上であり、そして、好ましくは15質量%以下、より好ましくは10質量%以下、より好ましくは8質量%以下である、<1>〜<29>のいずれかに記載の道路舗装用アスファルト組成物。
<31>骨材の含有量が、アスファルトとポリエステル樹脂の合計100質量部に対して、好ましくは1,000質量部以上、より好ましくは1,200質量部以上、より好ましくは1,500質量部以上であり、そして、好ましくは3,000質量部以下、より好ましくは2,500質量部以下、更に好ましくは2,000質量部以下である、<1>〜<30>のいずれかに記載の道路舗装用アスファルト組成物。
<33>顔料が、好ましくはカーボンブラック含む、<32>に記載の道路舗装用アスファルト組成物。
<34>顔料の含有量が、ポリエステル樹脂100質量部に対し、好ましくは3質量部以上、より好ましくは4質量部以上、より好ましくは5質量部以上であり、そして、好ましくは10質量部以下、より好ましくは8質量部以下、より好ましくは7質量部以下である、<32>又は<33>に記載の道路舗装用アスファルト組成物。
前記混合する工程で使用する前記ポリエステル樹脂が、溶融混練されたものであり、
前記ポリエステル樹脂の比率が、前記アスファルト100質量部に対し5質量部以上50質量部以下である、道路舗装用アスファルト組成物の製造方法。
<38>ポリエステル樹脂が、ビスフェノールAのアルキレンオキシド付加物を50モル%以上含むアルコール成分由来の構成単位と、テレフタル酸及びイソフタル酸からなる群から選ばれる1種以上を50モル%以上含むカルボン酸成分由来の構成単位とを有するポリエステルであって、軟化点が90℃以上140℃以下であり、且つ、水酸基価が20mgKOH/g以上50mgKOH/g以下である、<37>に記載の道路舗装用アスファルト組成物の製造方法。
<39>アスファルトがストレートアスファルトである、<37>又は<38>に記載の道路舗装用アスファルト組成物の製造方法。
<40>混合する工程で使用するポリエステル樹脂が、平均粒径1μm以上20μm以下のポリエステル樹脂粒子である、<37>〜<39>のいずれかに記載の道路舗装用アスファルト組成物の製造方法。
<41>ポリエステル樹脂を含む原料混合物を溶融混練する工程を、混合する工程前に更に有する、<37>〜<40>のいずれかに記載の道路舗装用アスファルト組成物の製造方法。
<42>溶融混練する工程は、ポリエステル樹脂の軟化点が、溶融混練前に比べて5℃以上40℃以下、低下するまでポリエステル樹脂を溶融混練し、軟化点90℃以上140℃以下のポリエステル樹脂を得る工程である、<41>に記載の道路舗装用アスファルト組成物の製造方法。
<43>溶融混練する工程は、ポリエステル樹脂のテトラヒドロフランに対する可溶分のゲルパーミエーションクロマトグラフィー測定における重量平均分子量Mwが、溶融混練前に比べて2倍以上100倍以下、増加するまでポリエステル樹脂を溶融混練する工程である、<37>〜<42>のいずれか一項に記載の道路舗装用アスファルト組成物の製造方法。
<44><37>〜<43>のいずれかに記載の製造方法により得られたアスファルト組成物を塗工し、アスファルト舗装材層を形成する工程を有する道路舗装方法。
<45>アスファルト、及びポリエステル樹脂を含有し、
前記ポリエステル樹脂が、溶融混練されたものであり、
前記ポリエステル樹脂の比率が、前記アスファルト100質量部に対し5質量部以上50質量部以下である、道路舗装用アスファルト組成物。
<46><1>〜<36>,<45>のいずれかに記載のアスファルト組成物の道路舗装への使用。
ポリエステル樹脂の酸価、及び水酸基価は、JIS K 0070の方法に基づき測定した。但し、測定溶媒のみJIS K 0070の規定のエタノールとエーテルの混合溶媒から、アセトンとトルエンの混合溶媒(アセトン:トルエン=1:1(容量比))に変更した。
(1)軟化点
フローテスター「CFT-500D」(株式会社島津製作所製)を用い、1gの試料を昇温速度6℃/分で加熱しながら、プランジャーにより1.96MPaの荷重を与え、直径1mm、長さ1mmのノズルから押し出した。温度に対し、フローテスターのプランジャー降下量をプロットし、試料の半量が流出した温度を軟化点とした。
(2)吸熱の最大ピーク温度
示差走査熱量計「Q-100」(ティー エイ インスツルメント ジャパン株式会社製)を用いて、室温(25℃)から降温速度10℃/分で0℃まで冷却した試料をそのままの温度で1分間維持し、その後、昇温速度10℃/分で180℃まで昇温しながら測定した。観測される吸熱ピークのうち、最も高温側にあるピークの温度を吸熱の最大ピーク温度とした。
(3)ガラス転移点
示差走査熱量計「Q-100」(ティー エイ インスツルメント ジャパン株式会社製)を用いて、試料0.01〜0.02gをアルミパンに計量し、200℃まで昇温し、その温度から降温速度10℃/分で0℃まで冷却した。次に昇温速度10℃/分で150℃まで昇温しながら測定した。吸熱の最大ピーク温度以下のベースラインの延長線とピークの立ち上がり部分からピークの頂点までの最大傾斜を示す接線との交点の温度をガラス転移点とした。
以下の方法により、ゲルパーミエーションクロマトグラフィー測定により分子量分布を測定し、重量平均分子量Mw、数平均分子量Mn、及び分子量分布(Mw/Mn)を算出した。
(1)試料溶液の調製
濃度が0.5g/100mLになるように、ポリエステル樹脂をTHFに溶解させた。次いで、この溶液をポアサイズ2μmのフッ素樹脂フィルター「FP-200」(住友電気工業株式会社製)を用いて濾過して不溶解成分を除き、試料溶液とした。
(2)分子量分布測定
溶解液としてTHFを1mL/minの流速で流し、40℃の恒温槽中でカラムを安定させた。そこに試料溶液200μLを注入して測定を行った。試料の分子量は、あらかじめ作製した検量線に基づき算出した。このときの検量線には、数種類の単分散ポリスチレン(東ソー株式会社製の単分散ポリスチレン;分子量1.11×106, 3.97×105, 1.89×105, 9.89×104, 1.71×104, 9.49×103, 5.87×103, 1.01×103, 5.00×102)を標準試料として作成したものを用いた。
測定装置:「HPLC LC-9130NEXT」(日本分析工業株式会社製)
分析カラム:「JAIGEL-2.5-H-A」+「JAIGEL-MH-A」(以上、日本分析工業株式会社製)
(1) 試料の調製
JIS Z8801の篩を用いて、22メッシュの篩を通過し、30メッシュの篩は通過しない粉末状の試料を採取した。試料が塊等の場合は、市販のハンマー、コーヒーミルを用いて、粉砕し、粉末状として篩いにかけた。
(2) 試料の溶解
試料2.000gを、ガラス瓶「M-140」(柏洋硝子株式会社製)に秤量した後、THF 50gを加え、内蓋及び外蓋を取り付けた。ボールミルにて5時間攪拌した(周速:200mm/sec)。その後、10時間静置した。
(3)濾過
予め計量済み(1000分の1g単位)のナスフラスコ(質量A(g))に取り付けたガラスフィルタ(目開き規格11G-3)を準備した。ガラスフィルタのシールには、減圧が可能なゴム栓を用いた。上記試料の溶解において10時間静置した溶解液の上澄みから20mLをメスピペッドで吸い取り、準備したガラスフィルタを用いて、減圧濾過した。なお、液面から下2cmまでを上澄みとした。溶解液を濾過する前のナスフラスコ内の減圧度を40kPaに調整した。未使用のTHF 20mLをメスピペッドで吸い取り、ガラスフィルタに付着している可溶分を減圧濾過した。
(4) 乾燥
下記条件にて、エバポレータにてナスフラスコ内のTHFを除去した。
ウォーターバス温度:70℃
ナスフラスコ回転数:200r/min
クロロホルム除去中のナスフラスコ内の減圧度:40〜20kPaに調整
時間:10分
その後、50℃ 1torrにて12時間乾燥した後、ナスフラスコの質量B(g)を計量した。
(5)THF不溶分の算出
THF 20mLに溶解したTHF可溶分X(g)を算出した。
X =B − A
THF 50gに溶解するTHF可溶分Y(g)を、THFの比重を0.889として算出した。
Y =X × 50/(20×0.889)
試料1gあたりの可溶分Z(質量%)を算出した。
Z =Y /2×100
THF不溶分(質量%) = 100 - Z
なお、THF不溶分(質量%)は、3回の測定値の平均値とした。
ポリエステル樹脂粒子の平均粒径は、JIS Z 8815篩分け法に準じて測定した。樹脂粒子100gについて、開口目開き2830μm、2000μm、1400μm、850μm、600μm、425μm、106μmの7つの篩をロータップ型振とう機(株式会社シー エム ティ製)を用いて篩分けを行い、平均粒径を求めた。
赤外線水分計「FD-230」(株式会社ケツト科学研究所製)を用いて、試料5gを乾燥温度150℃、測定モード96(監視時間2.5分/変動幅0.05%)の条件にて乾燥させ、試料の水分(質量%)を測定した。固形分濃度は下記式に従って算出した。
固形分濃度(質量%)=100−試料の水分(質量%)
後述の実施例、比較例で得られた成型品を24時間室温(25℃)で保存し、25℃で2時間水に浸漬させ、その後、水浴から回収し、拭取り、直ちに、以下の機器で5.08mm/minで圧力をかけていき、どの荷重まで耐えられるかで算出した。
圧力はKiloNewton/表面積 で算出した。
機器:Resistance assessment press (Mecanica Cientifica, S.A., model Ref. 41.000)
後述の実施例、比較例で得られた成型品を60℃で24時間水に浸漬させ、更に25℃で2時間水に浸漬させた後、水浴から回収し、拭取り、25℃で1時間放置した後で強度を測定した。
後述の実施例、比較例で得られた成型品をガソリン(Varsol 60, petroleum heavy nafta hydrodesulfurized, boiling range 90℃-230℃)に24時間浸漬した後、水で洗い流し、更に25℃で水に2時間浸漬した後、水浴から回収し、拭取り、25℃で1時間放置した後で強度を測定した。
製造例a1及びa2(ポリエステル樹脂a1〜a2、及びその樹脂粒子a1〜a2)
表1に示すポリエステル樹脂のアルコール成分と、無水トリメリット酸以外のカルボン酸成分と、ジ(2-エチルヘキサン酸)錫(II)20g、及びターシャリブチルカテコール2gを添加し、温度計、ステンレス製撹拌棒、脱水管、流下式コンデンサー、及び窒素導入管を装備した10リットル容の四つ口フラスコに入れ、窒素雰囲気にてマントルヒーター中で、120℃から205℃で8時間反応させた。その後8KPaの減圧条件下にて1時間反応させ。さらに無水トリメリット酸を加え205℃で1時間反応させた後、8KPaにて目標Tmまで反応させ目的のポリエステル樹脂a1又はa2を得た。各種物性を測定し、表1に示した。
得られたポリエステル樹脂a1又はa2について、粉砕機「SF-1」(株式会社三力製作所製)を用いて粉砕した。スクリーン目開き、並びに回転数調整により表1の粒径のポリエステル樹脂粒子a1又はa2を得た。
表2に示す樹脂を混合した結着樹脂100質量部、カーボンブラック「Regal 330R」(キャボット社製)5質量部、ポリプロピレンワックス「NP-105」(三菱化学株式会社)1質量部を、ヘンシェルミキサーにてよく攪拌した後、混練部分の全長1560mm、スクリュ径42mm、バレル内径43mmの同方向回転二軸押出機を用いて溶融混練し、ポリエステル樹脂の溶融混練物ak1を得た。スクリュ回転速度は200r/min、トラフ内の加熱温度は120℃であり、混合物の供給速度は10kg/hr、平均滞留時間は約18秒であった。得られた混練物ak1を冷却ローラで圧延冷却した後、ジェットミルで体積中位粒径(D50)6μmに粉砕して混練物の樹脂粒子ak1を得た。
表2に示す樹脂を混練部分の全長1560mm、スクリュ径42mm、バレル内径43mmの同方向回転二軸押出機を用いて溶融混練し、ポリエステル樹脂の溶融混練物ak2〜ak3を得た。スクリュ回転速度は200r/min、トラフ内の加熱温度は120℃であり、混合物の供給速度は10kg/hr、平均滞留時間は約18秒であった。得られた混練物を冷却ローラで圧延冷却した後、粉砕機「SF-1」(株式会社三力製作所製)を用いて粉砕した。スクリーン目開き、並びに回転数調整により表2の粒径の樹脂粒子ak2〜ak3を得た。溶融混練後の各種物性を測定し、表2に示した。
ストレートアスファルト80g、表に示す樹脂粒子20g、2.36〜13.2mmの砕石(粗骨材)600g、2.36mm未満の砂(細骨材)1200gのうち、ストレートアスファルト以外の材料をアスファルト用混合機に入れ160℃にて1分間混合した。次いでストレートアスファルトを加え2分間(アスファルト機械混合器Mecanica Cientifica, S.A., model Ref. 25.0000)混合した。得られた混合物をその温度で、内径101.6mm、外径114.3mm、高さ177.8mmの円筒状成形機に入れ、加圧器(Compaction hydraulic press)(Mecanica Cientifica , S.A., model Ref. 10.2196)を用いて3分かけて21MPaまで上げて成型を行った。2分間21MPaを維持した後、脱圧し、室温まで24時間かけて冷却し、アスファルトブロックが脱型された。各種評価試験を行い、その結果を表3に示した。
実施例1において、ストレートアスファルト80g、表に示す樹脂粒子20gを用いる代わりに、ストレートアスファルト100gにしたこと以外、実施例1と同様にして、アスファルト組成物を調製した。各種評価試験を行い、その結果を表3に示した。
Claims (20)
- アスファルト、ポリエステル樹脂、及び骨材を含有し、
前記ポリエステル樹脂が、溶融混練されたものであり、
前記ポリエステル樹脂のアルコール成分が、ビスフェノールAのアルキレンオキシド付加物を50モル%以上含み、
前記ポリエステル樹脂の比率が、前記アスファルト100質量部に対し5質量部以上50質量部以下である、道路舗装用アスファルト組成物。 - 前記ポリエステル樹脂100質量部に対し3質量部以上10質量部以下の顔料を更に含有する、請求項1に記載の道路舗装用アスファルト組成物。
- 前記顔料が、カーボンブラックを含む、請求項2に記載の道路舗装用アスファルト組成物。
- 前記ポリエステル樹脂が、平均粒径1μm以上20μm以下のポリエステル樹脂粒子を配合してなるものである、請求項1〜3のいずれか一項に記載の道路舗装用アスファルト組成物。
- 前記ポリエステル樹脂のカルボン酸成分が、テレフタル酸及びイソフタル酸からなる群から選ばれる1種以上を50モル%以上含む、請求項1〜4のいずれか一項に記載の道路舗装用アスファルト組成物。
- 前記ポリエステル樹脂の酸価が2mgKOH/g以上30mgKOH/g以下である、請求項1〜5のいずれか一項に記載の道路舗装用アスファルト組成物。
- 前記ポリエステル樹脂の水酸基価が20mgKOH/g以上50mgKOH/g以下である、請求項1〜6のいずれか一項に記載の道路舗装用アスファルト組成物。
- 前記ポリエステル樹脂の軟化点が90℃以上140℃以下である、請求項1〜7のいずれか一項に記載の道路舗装用アスファルト組成物。
- 前記ポリエステル樹脂の軟化点が、前記溶融混練前に比べて5℃以上40℃以下、低下している、請求項1〜8のいずれか一項に記載の道路舗装用アスファルト組成物。
- 前記ポリエステル樹脂のテトラヒドロフランに対する可溶分のゲルパーミエーションクロマトグラフィー測定における重量平均分子量Mwが、前記溶融混練前に比べて2倍以上100倍以下、増加している、請求項1〜9のいずれか一項に記載の道路舗装用アスファルト組成物。
- 前記アスファルト、前記ポリエステル樹脂、及び前記骨材を130℃以上200℃以下で混合して得られたものである、請求項1〜10のいずれか一項に記載の道路舗装用アスファルト組成物。
- アスファルト、ポリエステル樹脂、及び骨材を130℃以上200℃以下で混合する工程を有し、
前記混合する工程で使用する前記ポリエステル樹脂が、溶融混練されたものであり、
前記ポリエステル樹脂のアルコール成分が、ビスフェノールAのアルキレンオキシド付加物を50モル%以上含み、
前記ポリエステル樹脂の比率が、前記アスファルト100質量部に対し5質量部以上50質量部以下である、道路舗装用アスファルト組成物の製造方法。 - 前記ポリエステル樹脂が、ビスフェノールAのアルキレンオキシド付加物を50モル%以上含むアルコール成分由来の構成単位と、テレフタル酸及びイソフタル酸からなる群から選ばれる1種以上を50モル%以上含むカルボン酸成分由来の構成単位とを有するポリエステルであって、軟化点が90℃以上140℃以下であり、且つ、水酸基価が20mgKOH/g以上50mgKOH/g以下である、請求項12に記載の道路舗装用アスファルト組成物の製造方法。
- 前記アスファルトがストレートアスファルトである、請求項12又は13に記載の道路舗装用アスファルト組成物の製造方法。
- 前記混合する工程で使用する前記ポリエステル樹脂が、平均粒径1μm以上20μm以下のポリエステル樹脂粒子である、請求項12〜14のいずれか一項に記載の道路舗装用アスファルト組成物の製造方法。
- 前記ポリエステル樹脂を含む原料混合物を溶融混練する工程を、前記混合する工程前に更に有する、請求項12〜15のいずれか一項に記載の道路舗装用アスファルト組成物の製造方法。
- 前記溶融混錬の温度が、90℃以上140℃以下である、請求項16に記載の道路舗装用アスファルト組成物の製造方法。
- 前記溶融混練する工程は、前記ポリエステル樹脂の軟化点が、前記溶融混練前に比べて5℃以上40℃以下、低下するまで前記ポリエステル樹脂を溶融混練し、軟化点90℃以上140℃以下のポリエステル樹脂を得る工程である、請求項16又は17に記載の道路舗装用アスファルト組成物の製造方法。
- 前記溶融混練する工程は、前記ポリエステル樹脂のテトラヒドロフランに対する可溶分のゲルパーミエーションクロマトグラフィー測定における重量平均分子量Mwが、前記溶融混練前に比べて2倍以上100倍以下、増加するまで前記ポリエステル樹脂を溶融混練する工程である、請求項16〜18のいずれか一項に記載の道路舗装用アスファルト組成物の製造方法。
- 請求項12〜19のいずれか一項に記載の製造方法により得られたアスファルト組成物を塗工し、アスファルト舗装材層を形成する工程を有する道路舗装方法。