JP6785679B2 - スタッドレスタイヤ用ゴム組成物 - Google Patents
スタッドレスタイヤ用ゴム組成物 Download PDFInfo
- Publication number
- JP6785679B2 JP6785679B2 JP2017032878A JP2017032878A JP6785679B2 JP 6785679 B2 JP6785679 B2 JP 6785679B2 JP 2017032878 A JP2017032878 A JP 2017032878A JP 2017032878 A JP2017032878 A JP 2017032878A JP 6785679 B2 JP6785679 B2 JP 6785679B2
- Authority
- JP
- Japan
- Prior art keywords
- meth
- mass
- resin particles
- rubber
- acrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
[測定方法]
樹脂粒子を空気などの酸化性雰囲気中、950℃で焼成したときの灰分質量(これをSiO2量とする)からケイ素原子に相当する質量を算出し、該ケイ素原子量を焼成処理に供した樹脂粒子の質量で除すことにより求めることができる。灰分質量からSi分に相当する質量を算出するには、灰分質量に0.4672(ケイ素原子量/SiO2式量)を乗じることによって求めることができる。
樹脂粒子-Aの調製
冷却管、温度計、滴下口を備えた四つ口フラスコに、イオン交換水100質量部と、25質量%アンモニア水0.3質量部を入れ、攪拌下、滴下口から、3−メタクリロキシプロピルトリメトキシシラン24質量部、メタノール67質量部の混合溶液を添加し、3−メタクリロキシプロピルトリメトキシシランの加水分解、縮合反応を行って、ポリシロキサン粒子の分散液を調製した。このポリシロキサン粒子の平均粒子径は15μmであった。
得られた樹脂粒子‐Aは、真球状の粒子であり、平均粒径30μm、10%圧縮強度4.1GPa、ガラス転移温度125℃、ケイ素含有量1.8質量%であった。
イオン交換水、メタノール、アンモニア水の量を適宜変更し、平均粒子径が25μmのポリシロキサン粒子を作製したしたこと以外は、製造例1と同様にして、樹脂粒子‐Bを得た。
得られた樹脂粒子‐Bは、真球状の粒子であり、平均粒径50μm、10%圧縮強度3.6GPa、ガラス転移温度125℃、ケイ素含有量2.0質量%であった。
イオン交換水、メタノール、アンモニア水の量を適宜変更し、平均粒子径が12μmのポリシロキサン粒子を作製した後、単量体成分の種類と使用量を、n−ブチルメタクリレート228質量部と、トリエチレングリコールジメタクリレート12質量部に変更し、粒子の乾燥を窒素雰囲気下40℃で12時間としたこと以外は、製造例1と同様にして、樹脂粒子‐Cを得た。
得られた樹脂粒子‐Cは、真球状の粒子であり、平均粒径30μm、10%圧縮強度1.5GPa、ガラス転移温度53℃、ケイ素含有量0.9質量%であった。
イオン交換水、メタノール、アンモニア水の量を適宜変更し、平均粒子径が1μmのポリシロキサン粒子を作製したしたこと以外は、製造例1と同様にして、樹脂粒子‐Dを得た。
得られた樹脂粒子‐Dは、真球状の粒子であり、平均粒径2μm、10%圧縮強度5.5GPa、ガラス転移温度125℃、ケイ素含有量1.8質量%であった。
得られた樹脂粒子‐Eは、真球状の粒子であり、平均粒径80μm、10%圧縮強度2.8GPa、ガラス転移温度125℃、ケイ素含有量2.0質量%であった。
イオン交換水、メタノール、アンモニア水の量を適宜変更し、平均粒子径が26μmのポリシロキサン粒子を作製した後、単量体成分の種類と使用量を、2−エチルヘキシルアクリレート228質量部と、トリエチレングリコールジメタクリレート12質量部に変更し、粒子の乾燥を窒素雰囲気下40℃で12時間としたこと以外は、製造例1と同様にして、樹脂粒子‐Fを得た。得られた樹脂粒子‐Fは、真球状の粒子であり、平均粒径70μm、10%圧縮強度0.4GPa、ガラス転移温度−40℃、ケイ素含有量0.9質量%であった。
表2に記載の共通組成を有し、表1に記載の樹脂粒子を配合した11種類のスタッドレスタイヤ用ゴム組成物(実施例1〜5、標準例、比較例1〜5)を調製するにあたり、硫黄、加硫促進剤および樹脂粒子を除く成分を1.7Lのバンバリーミキサーで5分間混練し、145℃に達したとき放出しマスターバッチとした。得られたマスターバッチに、硫黄、加硫促進剤および樹脂粒子を加えて70℃のオープンロールで混練することにより、11種類のスタッドレスタイヤ用ゴム組成物を得た。なお、表1に記載の樹脂粒子の配合量は、表2に記載のジエン系ゴム100質量部に対する質量部として表されている。
得られた加硫ゴム試験片を偏平円柱状の台ゴムに貼り付け、インサイドドラム型氷上摩擦試験機を用いて、測定温度−1.5℃、荷重5.5kg/cm2、ドラム回転速度25km/hの条件で氷上摩擦係数を測定した。得られた氷上摩擦係数を、標準例の値を100とする指数にして、「氷上性能」の欄に示した。この指数値が大きいほど氷上摩擦係数が大きく氷上性能が優れることを意味する。
得られた加硫ゴム試験片をJIS K6264に準拠して、ランボーン摩耗試験機(岩本製作所社製)を使用して、温度20℃、荷重39N、スリップ率30%、時間4分の条件で摩耗量を測定した。得られた結果は標準例の逆数を100にする指数とし、「耐摩耗性」の欄に示した。この指数が大きいほど耐摩耗性が優れることを意味し、指数が95以上であれば実用することができる。
・樹脂粒子−A〜−F:上述した調製方法により得た樹脂粒子
・天然ゴム:RSS#3
・ブタジエンゴム:日本ゼオン(株)製ポリブタジエンゴムNipol BR1220
・カーボンブラック:東海カーボン(株)製カーボンブラックシースト6、窒素吸着比表面積が115m2/g
・シリカ:日本シリカ工業(株)製Nipsil AQ
・カップリング剤:硫黄含有シランカップリング剤、デクサ社製Si69
・酸化亜鉛:正同化学工業社製酸化亜鉛3種
・ステアリン酸:NOF社製ビーズステアリン酸
・老化防止剤:フレキシス社製6PPD
・アロマオイル:富士興産(株)製アロマオイル
・硫黄:鶴見化学工業(株)製金華印油入微粉硫黄
・加硫促進剤:大内新興化学工業(株)製ノクセラー CZ−G
Claims (3)
- ジエン系ゴム100質量部、カーボンブラックおよび/または白色充填剤30〜100質量部、および前記ジエン系ゴムに相溶しない樹脂粒子0.5〜30質量部を含み、前記樹脂粒子が(メタ)アクリル系化合物に由来する構造単位およびシリコン系化合物に由来する構造単位を有する共重合体を含む樹脂粒子であって、前記樹脂粒子の平均粒子径が3〜70μm、10%圧縮強度が0.5〜5.0GPaであることを特徴とするスタッドレスタイヤ用ゴム組成物。
- 前記樹脂粒子に含まれるケイ素原子の含有量が、0.5〜10質量%であることを特徴とする請求項1に記載のスタッドレスタイヤ用ゴム組成物。
- 請求項1または2に記載のスタッドレスタイヤ用ゴム組成物からなるトレッド部を有するスタッドレスタイヤ。