JP6606831B2 - 農業用資材の製造方法 - Google Patents
農業用資材の製造方法 Download PDFInfo
- Publication number
- JP6606831B2 JP6606831B2 JP2015032710A JP2015032710A JP6606831B2 JP 6606831 B2 JP6606831 B2 JP 6606831B2 JP 2015032710 A JP2015032710 A JP 2015032710A JP 2015032710 A JP2015032710 A JP 2015032710A JP 6606831 B2 JP6606831 B2 JP 6606831B2
- Authority
- JP
- Japan
- Prior art keywords
- agricultural
- antibacterial agent
- agricultural material
- sheet
- ion complex
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
農業用資材に、アニオン性高分子およびカチオン性抗菌剤をレイヤー・バイ・レイヤー法により積層してイオンコンプレックスを形成させる、農業用資材の製造方法。
項2.
アニオン性高分子がポリアクリル酸、および、ポリメタクリル酸からなる群より選択される1種以上である、項1に記載の農業用資材の製造方法。
項3.
カチオン性抗菌剤が第4級アンモニウムである、項1に記載の農業用資材の製造方法。
項4.
カチオン性抗菌剤がビグアニドである、項1に記載の農業用資材の製造方法。
項5.
第4級アンモニウムが、セチルピリジニウム、オクタデシルジメチル(3−トリメトキシシリルプロピル)アンモニウム、ベンゼトニウム、ベンザルコニウム、ラウリルピリジニウムからなる群より選択される1種以上の塩である、項3に記載の農業用資材の製造方法。
項6.
ビグアニドが、クロルヘキシジン、ポリヘキサメチレンビグアニドからなる群より選択される1種以上の塩である、項4に記載の農業用資材の製造方法。
項7.
アニオン性高分子とカチオン性抗菌剤から形成されるイオンコンプレックスが水不溶性である、項1〜6のいずれかに記載の農業用資材の製造方法。
項8.
農業用資材が農業用不織布、織物、シート、フィルムである、項1〜7のいずれかに記載の農業用資材の製造方法。
本発明に係わる農業用資材に含有されるイオンコンプレックスを構成する要素の一つであるアニオン性高分子とは、分子内に複数のカルボキシル基を有し、溶液中において負電荷を帯びる高分子電解質のことを示す。具体的には、ポリアクリル酸、ポリメタアクリル酸、アルギン酸、ポリ-γ-グルタミン酸、ポリ-α-グルタミン酸、ヒアルロン酸、カルボキシメチルセルロース、ペクチン、デオキシリボ核酸等が挙げられる。この中でも好ましいのは、ポリアクリル酸、ポリメタクリル酸が挙げられる。ポリアクリル酸、ポリメタクリル酸は、いずれを使用しても、制限はなく、市販されているものがあればそれを用いてもよいし、別途製造してもよく、その共重合体を用いてもよい。使用するポリアクリル酸、ポリメタクリル酸の分子サイズも特に制限されないが、平均分子量で45万〜100万の範囲のものが好適である。一般的に、分子サイズが大きいほど強度などの性能が高くなるが、平均分子量が100万以上になると、カチオン性殺菌剤との塩の形成が不十分となりゲル化する。
本発明に係わる農業用資材に含有されるイオンコンプレックスを構成するもう一つの要素であるするカチオン性抗菌剤は、特に制限されないが、第4級アンモニウム、ポリアミンおよびビグアニドが好ましい。第4級アンモニウムとしては、例えば、ベンゼトニウム、ベンザルコニウム、ジステアリルジメチルアンモニウム、ステアリルジメチルベンジルアンモニウム、ステアリルトリメチルアンモニウム、セチルトリメチルアンモニウム、ラウリルトリメチルアンモニウム、ラウリルピリジニウム、セチルピリジニウム、デカリニウム、オクタデシルジメチル(3−トリメトキシシリルプロピル)アンモニウム等が挙げられる。前記第4級アンモニウムは塩であっても良く、例えばハロゲン化物が挙げられる。前記ハロゲン化物は好ましくは塩化物である。ポリアミンとしては、ポリ-L-リジン、ポリエチレンイミン等が挙げられる。前記ポリアミンは塩であっても良く、例えば塩酸塩が挙げられる。ビグアニドとしては、クロルヘキシジン(またはその塩(例えば塩酸塩、酢酸塩、グルコン酸塩))、アレキシジン(またはその塩(例えば塩酸塩、酢酸塩、グルコン酸塩))、ポリヘキサメチレンビグアニジン(またはその塩)等が挙げられる。この中でも、好ましくはセチルピリジニウム、ベンザルコニウム、オクタデシルジメチル(3−トリメトキシシリルプロピル)アンモニウム、ポリヘキサメチレンビグアニジンが挙げられる。これらのカチオン性抗菌剤は1種のみを使用してもよいし、2種以上を含んでもよい。
本発明の農業用資材に含まれる「アニオン性高分子とカチオン性抗菌剤からなるイオンコンプレックス」の形態は特に限定されない。
例えば、アニオン性高分子としてポリアクリル酸またはポリメタクリル酸(以下、これらをポリ(メタ)クリル酸とも表す。)を使用する場合、イオンコンプレックスは、ポリ(メタ)アクリル酸を構成するアクリル酸単位とカチオン性抗菌剤とを等モルあるいは任意のモル比で含むものを用いることができる。ポリ(メタ)アクリル酸の有する材料としての欠点(例えば、過剰な親水性など)を克服する必要がある場合は、カチオン性抗菌剤により十分に改質されているものが好適である。より具体的には、イオンコンプレックス中に含まれるカチオン性抗菌剤の割合が、アクリル酸単位に対して0.5モル倍以上であることが好ましく、0.6モル倍以上であることがより好ましく、0.7モル倍以上であることがさらに好ましい。特に、アクリル酸単位とカチオン性抗菌剤とを等モルまたは略等モル含むものが好適である。ここで、略等モルとは、両者のモル数がほぼ等しいことを意味するが、具体的にはアクリル酸単位に対するカチオン性抗菌剤が0.8モル倍以上、1.2モル倍以下、特に0.9モル倍以上、1.1モル倍以下であることをいうものとする。
本発明の農業用資材に含有されるポリ(メタ)アクリル酸とカチオン性抗菌剤から形成されるイオンコンプレックスは、アルカリ溶液に対し、ポリ(メタ)アクリル酸を混合して得られる中和液を作製し、続いて、カチオン性抗菌剤を混合して反応液を作製すれば、イオンコンプレックスが形成され、容易に製造できる。
前記イオンコンプレックスの製造法で使用する溶媒としては、水が好適である。原料であるポリ(メタ)アクリル酸を良好に溶解できるからであり、また、目的化合物は水に対して不溶性であることから、反応後における目的物の単離精製に好都合なためである。但し、カチオン性抗菌剤の水溶性などによっては、前記反応液におけるそれらの溶解性を高めるために、メタノールやエタノールなどのアルコール;THFなどのエーテル;ジメチルホルムアミドやジメチルアセトアミドなどのアミドなどの水溶性有機溶媒を反応液に添加してもよい。しかし、反応終了後における生成物の分離を考慮すれば、溶媒としては水のみを用いることが好ましい。
前記イオンコンプレックスの製造法において、原料としてポリ(メタ)アクリル酸を使用する場合は、その塩を用いてもよい。当該塩としては、ナトリウム塩やカリウム塩などのアルカリ金属塩;カルシウム塩やマグネシウム塩などのアルカリ土類金属塩などを挙げることができる。また、塩を用いる場合であっても全てのカルボキシ基が塩となっている必要はなく、その一部のみが塩となっていてもよい。但し、アルカリ土類金属塩などの多価金属塩は、水に対する溶解性が低く、ゲル化する場合があり得るので、好適にはポリ(メタ)アクリル酸のフリー体またはその一価金属塩を用いる。
前記イオンコンプレックスの原料である第4級アンモニウム塩もしくはビグアニド系抗菌剤等のカチオン性抗菌剤は、通常、ハロゲン化物塩として存在する。よって、前記イオンコンプレックスの製造法においては、前記中和液へ第4級アンモニウム塩もしくはビグアニド系抗菌剤を直接添加、或いは当該イオンコンプレックスを水溶媒に溶解した上で添加すればよい。第4級アンモニウム塩もしくはビグアニド系抗菌剤は、ポリ(メタ)アクリル酸を十分に改質するため、ポリ(メタ)アクリル酸に対して十分量用いることが好ましい。
本発明のイオンコンプレックスを製造する別の方法としては、レイヤー・バイ・レイヤー法(交互積層法)が挙げられる。例えば、アニオン性高分子として、ポリ(メタ)アクリル酸を予め水に溶解または分散させて材料表面へコーティングを行い、続いて、カチオン性抗菌剤の溶液をコーティングすることで、材料表面上で塩イオンコンプレックスを形成させて加工することができる。この方法は、例えば農業用資材へコーティング加工する場合に好ましく使用できる。
本発明の農業用資材に含有されるポリ(メタ)アクリル酸とカチオン性抗菌剤からなるイオンコンプレックスは水不溶性であることから、水溶媒から容易に分離できるため、前記イオンコンプレックスの製造法の前記反応液における各成分の濃度は特に制限されない。例えば、反応液におけるポリ(メタ)アクリル酸の濃度を0.5w/v%以上、10w/v%以下程度、カチオン性抗菌剤の濃度を1.0w/v%以上、10w/v%以下程度とすることができる。
前記イオンコンプレックスの製造法で使用するアルカリの具体例としては、水酸化リチウム、水酸化ナトリウム、水酸化カリウム、水酸化セシウム、水酸化アンモニウム等の水酸化物、炭酸リチウム、炭酸ナトリウム、炭酸カリウム、炭酸セシウム等の炭酸塩もしくは炭酸水素塩が挙げられるが、その中でも、炭酸リチウム、炭酸ナトリウム、炭酸カリウム、炭酸セシウム等の炭酸塩が好ましい。
前記イオンコンプレックスの製造法で使用するアルカリは、固形物のまま使用してもよいが、反応を促進するためには、溶液として使用することが好ましい。使用する溶媒は、アルカリが溶解する溶媒が望ましい。具体的には、水、メタノール、エタノールが挙げられるが、水がより好ましい。
前記イオンコンプレックスの製造法において、前記反応液は、ポリ(メタ)アクリル酸とカチオン性抗菌剤のイオンコンプレックスの形成を促進するために適度に加熱することが好ましい。加熱温度は、例えば40℃以上、80℃以下程度とすることができる。反応時間は適宜調整すればよいが、通常、1時間以上、20時間以下程度とすることができる。
本発明の農業用資材に含有されるポリ(メタ)アクリル酸とカチオン性抗菌剤からなるイオンコンプレックスは水不溶性であることから、濾過や遠心分離などにより水溶媒から容易に分離することができる。また、分離した目的物は、水で洗浄することにより、過剰に用いたポリ(メタ)アクリル酸またはカチオン性抗菌剤、その他の塩を除去することも可能である。また、水溶媒は、アセトンなどで洗浄することにより簡便に除去できる。
ポリ(メタ)アクリル酸とカチオン性抗菌剤からなるイオンコンプレックスを含有する本発明の農業用資材は、グラム陽性およびグラム陰性のいずれの細菌類に対しても優れた抗菌効果を発揮するのみならず、同時に真菌類、藻類に対しても優れた抑制効果を示し、食品衛生面で抗細菌性や抗真菌性が要求される分野で広範囲に利用することができる。
本発明の農業用資材は、ポリ(メタ)アクリル酸とカチオン性抗菌剤からなるイオンコンプレックスを含有することを特徴とする。本発明の農業用資材においては、ポリ(メタ)アクリル酸とカチオン性抗菌剤からなるイオンコンプレックスを溶解可能な溶剤に溶かした塗料溶液とし、農業用資材に塗布や噴霧することにより、持続的な微生物抑制を示す塗膜や被膜を形成することが可能になる。
炭酸ナトリウム(3.0g)に対し、蒸留水(196.8 mL)を加え、20分間攪拌し、1.5%(w/v)の炭酸ナトリウム水溶液を調製した。当該炭酸ナトリウム溶液に対して、2.0%(w/v)になるように、アルドリッチ社製の平均分子量45万のポリアクリル酸(4.0 g)を加え、常温で2時間混合し、ポリアクリル酸中和液を作製した。当該中和液に対し、等モル量に相当する塩化ベンザルコニウム(20.4g)と蒸留水(191.2 mL)を加えて得られた溶液を添加し、50 ℃で2時間攪拌した。生成した沈殿を遠心した後、上清液を除去し、蒸留水で3回ろ過した。得られた沈殿物を24時間減圧乾燥した。粉末としてポリアクリル酸ベンザルコニウム(20g)を回収した。
炭酸ナトリウム(0.8g)に対し、蒸留水(49.2 mL)を加え、20分間攪拌し、1.6%(w/v)の炭酸ナトリウム水溶液を調製した。当該炭酸ナトリウム溶液に対して、2.0%(w/v)になるように、アルドリッチ社製の平均分子量45万のポリアクリル酸(1.0 g)を加え、常温で2時間混合し、ポリアクリル酸中和液を作製した。当該中和液に対し、等モル量に相当する塩化セチルピリジニウム(5.0 g)と蒸留水(47.8 mL)を加えて得られた溶液を添加し、50 ℃で2時間攪拌した。生成した沈殿を遠心した後、上清液を除去し、蒸留水で3回ろ過した。得られた沈殿物を24時間減圧乾燥した。粉末としてポリアクリル酸セチルピリジニウム(5g)を回収した。
製造例1および2において製造した農業用シートの抗菌性は、以下の操作により、グラム陽性菌としてStaphylococcus aureus(S. aureus)、グラム陰性菌としてEscherichia coli(E.coli)、真菌としてAspergillus niger(A.niger)をそれぞれ用いて、評価した。S. aureusおよびE.coliをSoybean Casein Digest(SCD)液体培地中で37℃にて16時間液体培養した後、新鮮なSCD液体培地で5×100000個/mlとなるように希釈し、48ウェルマイクロプレートの各ウェルに0.6ml注入した。一方、A.nigerの培養により胞子懸濁液を調製し、新鮮なSabouraud Dextrose液体培地で5×100000個/mlとなるように希釈し、48ウェルマイクロプレートの各ウェルに0.6ml注入した。製造例1および2において製造した6種類の給水シートを5mm角の試験片として切り抜き、上記の各ウェルの培養液に各1枚浸した。尚、比較例として、未処理の3種類の給水シート試験片も同様に各ウェルに浸した。S.aureusおよびE.coliは35℃にて48時間培養し、A.nigerは25℃にて72時間培養した。培養後に、シートを浸した培養液の菌の生育状態を目視で確認し、シートの抗菌性を判定した。表1は、抗菌性試験の結果を示し、抗菌性が認められた場合を−、抗菌性が認められなかった場合を+で表した。抗菌性試験の結果、製造例1で製造したポリアクリル酸ベンザルコニウムを付着させたシートまたは、製造例2で製造したポリアクリル酸セチルピリジニウムを付着させたシートは、上記グラム陽性菌、グラム陰性菌、真菌に対し、抗菌性が確認された。
製造例1で作製した呉羽テック社製防根給水シート(5cm角)を水(200mL)中に浸漬し、室温で350rpmの条件で10分間攪拌洗浄を行った。上記の操作を3回行い、洗濯後のシートの防藻試験を実施した。ポリアクリル酸ベンザルコニウム溶液の浸漬濃度0.05〜0.35wt%で処理した洗濯後の給水シートを5mm角の試験片として切り抜いた。市販の淡水産クロレラをC培地(独立行政法人国立環境研究所微生物系統保存施設の培地リストの組成に従い調製した。)に懸濁し、A660=0.04±0.01に調整したクロレラ懸濁液を48ウェルマイクロプレートの各ウェルに0.6ml注入した。上記の選択後の給水シート試験片を各1枚浸した。シート試験片を浸したクロレラは、人工気象機内で16時間の光照射(6,000lux)、8時間の光非照射のサイクルで25℃にて7日間培養した。
塩化ベンザルコニウム単体の効果と比較するため、0.05〜0.35wt%含有する塩化ベンザルコニウムエタノール溶液をそれぞれ作製し、呉羽テック社製防根給水シート(5cm角)に浸漬処理した後に乾燥させた。続いて、実施例2と同様に、当該塩化ベンザルコニウムシートを水(200mL)中に浸漬し、室温で350rpmの条件で10分間攪拌洗浄を行った。上記の操作を3回行い、洗濯後のシートの防藻試験を実施例2と同様に実施した。
ポリアクリル酸ソーダ10wt%水溶液(和光純薬製)を、ポリアクリル酸を構成するアクリル酸単位が10mmol/Lになるまで精製水で希釈した。当該溶液に、呉羽テック社製防根給水シート(5cm角)を室温で10分間浸漬し、取り出した後、50℃で乾燥させた。続いて、塩化ベンザルコニウム水溶液(10mmol/L)に、当該シートを室温で10分間浸漬し、取り出した後、1Lの水で洗浄し、50℃で乾燥させ、シートを製造した。
塩化ベンザルコニウムの代わりに、塩化セチルピリジニウムを用いた以外は、製造例3と同様に製造した。
塩化ベンザルコニウムの代わりに、ポリヘキサメチレンビグアニジンを用いた以外は、製造例3と同様に製造した。
製造例3〜5で製造したシートを植物栽培用養液中に3週間浸漬し、浸漬後のシートの防藻性試験を行った。植物栽培用養液中に含まれる、無機イオン成分を表3に示す。
Claims (8)
- 農業用資材に、アニオン性高分子およびカチオン性抗菌剤をレイヤー・バイ・レイヤー法により積層してイオンコンプレックスを形成させる、農業用資材の製造方法。
- アニオン性高分子がポリアクリル酸、および、ポリメタクリル酸からなる群より選択される1種以上である、請求項1に記載の農業用資材の製造方法。
- カチオン性抗菌剤が第4級アンモニウムである、請求項1に記載の農業用資材の製造方法。
- カチオン性抗菌剤がビグアニドである、請求項1に記載の農業用資材の製造方法。
- 第4級アンモニウムが、セチルピリジニウム、オクタデシルジメチル(3−トリメトキシシリルプロピル)アンモニウム、ベンゼトニウム、ベンザルコニウム、ラウリルピリジニウムからなる群より選択される1種以上の塩である、請求項3に記載の農業用資材の製造方法。
- ビグアニドが、クロルヘキシジン、ポリヘキサメチレンビグアニドからなる群より選択される1種以上の塩である、請求項4に記載の農業用資材の製造方法。
- アニオン性高分子とカチオン性抗菌剤から形成されるイオンコンプレックスが水不溶性である、請求項1〜6のいずれかに記載の農業用資材の製造方法。
- 農業用資材が農業用不織布、織物、シート、フィルムである、請求項1〜7のいずれかに記載の農業用資材の製造方法。