JP6590962B2 - 電子機器の外部接続用コネクタ接続口 - Google Patents
電子機器の外部接続用コネクタ接続口 Download PDFInfo
- Publication number
- JP6590962B2 JP6590962B2 JP2018011112A JP2018011112A JP6590962B2 JP 6590962 B2 JP6590962 B2 JP 6590962B2 JP 2018011112 A JP2018011112 A JP 2018011112A JP 2018011112 A JP2018011112 A JP 2018011112A JP 6590962 B2 JP6590962 B2 JP 6590962B2
- Authority
- JP
- Japan
- Prior art keywords
- polybutylene terephthalate
- terephthalate resin
- connector
- mass
- peripheral surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
また、このようなECUの筐体としてのポリブチレンテレフタレート樹脂材料には、高い難燃性が要求される。ポリブチレンテレフタレート樹脂を難燃化する方法として、臭素系難燃剤を用いる(例えば、特許文献1〜3)ことが行われている。
本発明は、以下の電子機器の外部接続用コネクタ接続口に関する。
前記コネクタ接続口は、ポリブチレンテレフタレート樹脂材料を射出成形した成形体からなり、その外周面又は内周面にはボス部が突設しており、
ボス部、並びに、ボス部を突設する外周面又は内周面の下方には、ポリブチレンテレフタレート樹脂材料中に空隙が存在しており、ボス部における前記外周面又は内周面から高さ0〜0.5mmの範囲に存在する空隙の断面面積の合計をS1とし、ボス部を突設する前記外周面又は内周面から深さ0〜0.5mmの範囲に存在する空隙の断面面積の合計をS2とし、S1とS2の合計面積を100%としたとき、S1の面積率が5〜45%、S2の面積率が55〜95%であることを特徴とする電子機器の外部接続用コネクタ接続口。
[2]前記ポリブチレンテレフタレート樹脂材料が、エポキシ化合物、臭素化エポキシ化合物、エポキシ基を導入したエラストマーからなる群より選択される少なくとも一種を含有するポリブチレンテレフタレート樹脂組成物である上記[1]に記載の外部接続用コネクタ接続口。
[3]前記ポリブチレンテレフタレート樹脂材料が、臭素化エポキシ化合物、臭素化ポリカーボネート化合物、及び、臭素化ポリスチレン化合物からなる群から選択される、異なる少なくとも2つ以上の臭素系難燃剤を含有するポリブチレンテレフタレート樹脂組成物である上記[1]に記載の外部接続用コネクタ接続口。
[4]前記コネクタ接続口が、電子部品と外部接続用コネクタを収納した電子機器の筐体の側面に設けられ、外部コネクタが挿入接続されるための外部接続用コネクタ接続口である上記[1]〜[3]のいずれかに記載の外部接続用コネクタ接続口。
[5]前記電子機器が車両用電子機器である上記[4]に記載の外部接続用コネクタ接続口。
[6]前記車両用電子機器がエンジンコントロールユニットである上記[5]に記載の外部接続用コネクタ接続口。
前記コネクタ接続口は、ポリブチレンテレフタレート樹脂材料を射出成形した成形体からなり、その外周面又は内周面にはボス部が突設しており、
ボス部、並びに、ボス部を突設する外周面又は内周面の下方には、ポリブチレンテレフタレート樹脂材料中に空隙が存在しており、ボス部における前記外周面又は内周面から高さ0〜0.5mmの範囲に存在する空隙の断面面積の合計をS1とし、ボス部を突設する前記外周面又は内周面から深さ0〜0.5mmの範囲に存在する空隙の断面面積の合計をS2とし、S1とS2の合計面積を100%としたとき、S1の面積率が5〜45%、S2の面積率が55〜95%であることを特徴とする。
エンジンコントロールユニット1は、筺体ケース2、外部接続用コネクタ部3を備える。外部接続用コネクタ部3は、ポリブチレンテレフタレート樹脂材料を射出成形により成形した成形体からなる。筺体ケース2は、ポリブチレンテレフタレート樹脂等の樹脂材料の成形物であっても、アルミニウムなどの金属で出来ていてもよい。筺体ケース2下部のベース2’は、通常アルミニウムなどの金属製であるが、ポリブチレンテレフタレート樹脂等の樹脂材料の成形物で出来ている。
エンジンコントロールユニット1内には、各種の多数の電子部品が収納されており、電子部品が実装された回路基板等が筐体ベース2’に固定される。
エンジンコントロールユニット1の側面には、外部接続用コネクタ部3を有しており、外部コネクタプラグ(非図示)を挿入して接続することのできる外部接続用コネクタ接続口4が複数設けられており、その内部には外部コネクタプラグが挿入されたときに外部コネクタプラグ側の端子と接続されるコネクタピン5を有する。
ボス部6の形状は、通常円柱状であり、一部を切り欠いた円柱状でも、また四角柱状等であってもよい。ボス部6の大きさは、その直径又は径が通常2〜4mm程度、高さが2〜4mm程度である。ボス部6の天頂部はフック留め等のために笠が乗ったような形状であることも好ましい。
本発明では、ボス部とボス部下方の外周面又は内周面において、ポリブチレンテレフタレート樹脂材料中に存在する空隙を、ボス部における前記外周面又は内周面から高さ0〜0.5mmの範囲に存在する空隙の断面面積の合計をS1とし、ボス部下方の前記外周面または内周面から深さ0〜0.5mmの範囲に存在する空隙の断面面積の合計をS2とし、S1とS2の合計面積を100%としたとき、S1の面積率が5〜45%、S2の面積率が55〜95%とすることにより、極めて高いボス強度を示すボス部とすることができる。
S1の面積率とS2の面積率は、上記の中でも、S1の面積率が5〜43%、S2の面積率が57〜95%であることが好ましく、より好ましくはS1の面積率が5〜40%、S2の面積率が60〜95%である。
以下、そのようなポリブチレンテレフタレート樹脂材料について説明する。
本発明のポリブチレンテレフタレート樹脂材料に用いるポリブチレンテレフタレート樹脂は、テレフタル酸単位及び1,4−ブタンジオール単位がエステル結合した構造を有するポリエステル樹脂であって、ポリブチレンテレフタレート樹脂(ホモポリマー)の他に、テレフタル酸単位及び1,4−ブタンジオール単位以外の、他の共重合成分を含むポリブチレンテレフタレート共重合体や、ホモポリマーと当該共重合体との混合物を含む。
なお、ポリブチレンテレフタレート樹脂の固有粘度は、テトラクロロエタンとフェノールとの1:1(質量比)の混合溶媒中、30℃で測定する値である。
本発明に使用するポリブチレンテレフタレート樹脂材料は、好ましくは(B)臭素系難燃剤を含有する。そして、本発明では、(B)臭素系難燃剤として、好ましくは、臭素化エポキシ化合物、臭素化ポリカーボネート化合物、及び、臭素化ポリスチレン化合物からなる群から選択される、異なる少なくとも2つ以上の臭素系難燃剤を使用する。ここで、「異なる少なくとも2つ以上の臭素系難燃剤」とは、(i)上記3種の臭素系難燃剤の中で、異なる種類の臭素系難燃剤を2種又は3種以上使用する、(ii)上記した3種の中で1種を選択し、その中で互いに分子量が異なるものを2又は3以上使用する、或いは(iii)上記(i)及び(ii)を組み合わせて使用することを意味する。
また、臭素化エポキシ化合物は、そのエポキシ当量が3000〜40000g/eqであることが好ましく、中でも4,000〜35,000g/eqが好ましく、特に10,000〜30,000g/eqであることが好ましい。
なお、臭素化エポキシ化合物の質量平均分子量(Mw)は、GPC(ゲル浸透クロマトグラフィー)法により測定される値(ポリスチレン換算)である。測定時の溶媒は、臭素化エポキシ化合物、臭素化ポリカーボネート化合物、臭素化ポリスチレン化合物はTHF(テトラヒドロフラン)を、臭素化アクリル化合物はODCB(オルトジクロロベンゼン)を用いる。測定時のカラム温度は、臭素化エポキシ化合物、臭素化ポリカーボネート化合物、臭素化ポリスチレン化合物は40℃、臭素化アクリル化合物は135℃に設定する。
また、臭素化ポリスチレンは、他のビニルモノマーが共重合された共重合体であってもよい。この場合のビニルモノマーとしてはスチレン、α−メチルスチレン、アクリロニトリル、アクリル酸メチル、ブタジエンおよび酢酸ビニル等が挙げられる。
臭素系難燃剤(B1)と臭素系難燃剤(B2)の質量比(B1/B2)は、90/10〜30/70であることが好ましく、より好ましくは90/10〜40/60で、さらに好ましくは90/10〜50/50である。このような質量比とすることで、得られる樹脂組成物の結晶化温度をより低下させ、また耐加水分解性もより向上させることが可能となる。
ポリブチレンテレフタレート樹脂材料は、さらに、難燃助剤であるアンチモン化合物(C)を含有することが好ましい。アンチモン化合物としては、三酸化アンチモン(Sb2O3)、五酸化アンチモン(Sb2O5)、アンチモン酸ナトリウム等が挙げられる。特に、耐衝撃性の点から三酸化アンチモンが好ましい。
本発明のポリブチレンテレフタレート樹脂材料は、エラストマーを含有することが好ましい。エラストマーとしては、ポリブチレンテレフタレート樹脂に配合してその耐衝撃性を改良するのに用いられている熱可塑性エラストマーを用いればよく、例えばゴム性重合体やゴム性重合体にこれと反応する化合物を共重合させたものを用いる。エラストマーのガラス転移温度は0℃以下、特に−20℃以下であるのが好ましい。
本発明のポリブチレンテレフタレート樹脂材料は、さらに離型剤を含有することが好ましい。離型剤としては、脂肪族カルボン酸、脂肪族カルボン酸とアルコールとのエステル、数平均分子量200〜15000の脂肪族炭化水素化合物、ポリシロキサン系シリコーンオイルの群から選ばれる少なくとも1種の化合物等が挙げられる。
本発明のポリブチレンテレフタレート樹脂材料は、エポキシ化合物を含有することが好ましい。エポキシ化合物は、ポリブチレンテレフタレート樹脂が水蒸気等により加水分解を受け、分子量低下を起こすと同時に機械的強度等が低下することを抑制するためのもので、これを含有することにより、エラストマーの配合効果がより促進され、耐加水分解性と耐ヒートショック性を、一層向上させることができるので好ましい。
エポキシ化合物としては、例えば、ビスフェノールA型エポキシ化合物、ビスフェノールF型エポキシ化合物、レゾルシン型エポキシ化合物、ノボラック型エポキシ化合物、脂環式エポキシ化合物、グリシジルエーテル類、グリシジルエステル類、エポキシ化ブタジエン重合体等が挙げられる。
本発明のポリブチレンテレフタレート樹脂材料は、無機充填材を含有することが好ましく、ポリブチレンテレフタレート樹脂100質量部に対し、30〜100質量部の範囲で含有することが好ましい。無機充填材の含有量は、40質量部以上がより好ましく、50質量部以上がさらに好ましく、また90質量部以下がより好ましく、80質量部以下がさらに好ましい。
本発明において、無機充填材とは、樹脂成分に含有させて強度及び剛性を向上させるものをいい、繊維状、板状、粒状、無定形等いずれの形態のものであってもよい。
本発明のポリブチレンテレフタレート樹脂材料は、カーボンブラックを含有することが好ましい。
カーボンブラックは、その種類、原料種、製造方法に制限はなく、ファーネスブラック、チャンネルブラック、アセチレンブラック、ケッチェンブラック等のいずれをも使用することができる。その数平均粒径には特に制限はないが、5〜60nm程度であることが好ましい。
本発明のポリブチレンテレフタレート樹脂材料は、さらに安定剤を含有することが、熱安定性改良や、機械的強度、及び色相の悪化を防止する効果を有するという点で好ましい。安定剤としては、リン系安定剤およびフェノール系安定剤が好ましい。
リン系安定剤としては、亜リン酸、リン酸、亜リン酸エステル、リン酸エステル等が挙げられ、中でもホスファイト、ホスホナイトが好ましい。
本発明のポリブチレンテレフタレート樹脂材料は、本発明の効果を損なわない範囲で、更に種々の添加剤を含有していても良い。このような添加剤としては、滴下防止剤、紫外線吸収剤、染顔料、蛍光増白剤、帯電防止剤、防曇剤、滑剤、アンチブロッキング剤、流動性改良剤、可塑剤、分散剤、抗菌剤等が挙げられる。
その他の熱可塑性樹脂としては、具体的には、例えば、ポリエチレンテレフタレート樹脂、ポリカーボネート樹脂、ポリアセタール樹脂、ポリアミド樹脂、ポリフェニレンオキサイド樹脂、ポリスチレン系樹脂、ポリフェニレンサルファイドエチレン樹脂、ポリサルホン樹脂、ポリエーテルサルホン樹脂、ポリエーテルイミド樹脂、ポリエーテルケトン樹脂、ポリオレフィン樹脂等が挙げられる。
本発明に用いるポリブチレンテレフタレート樹脂材料は、好ましくは(B)臭素化エポキシ化合物、臭素化ポリカーボネート化合物、及び、臭素化ポリスチレン化合物からなる群から選択される、異なる少なくとも2つ以上の臭素系難燃剤を含有することにより、結晶化温度(Tc)が低く、好ましくは193℃以下、より好ましくは192℃以下、さらに好ましくは191℃以下、中でも190℃以下、特に好ましくは189℃以下の結晶化温度を有する。また、Tcの下限は好ましくは170℃、より好ましくは175℃、さらに好ましくは180℃である。
このような結晶化温度にすることで、ボス部内の樹脂が固化する前に十分な樹脂の充填がしやすくなり、ボス部の空隙S1と、ボス部の基底部S2の面積率が前記した範囲にすることができる。
ポリブチレンテレフタレート樹脂材料は、射出成形により、ボス部を有するコネクタ接続口に成形される。本発明のコネクタ接続口は、電子機器(電気機器を含む)における外部コネクタを挿入接続するためのコネクタ接続口であり、電子機器としては、例えば、リレーケース、バリコンケース、コンデンサーケース、パワーモジュールケース、インテリジェントパワーモジュールケース等の電気電子機器、あるいは、エンジンコントロールユニット(ECU)ケース、エンジンコンピューターユニットケース、ABSユニットケース、エアバッグ制御ユニット等の車両用電気電子機器を好ましく挙げることができる。
乾燥温度を高く、また乾燥時間を長くすると、ポリブチレンテレフタレート樹脂材料の水分含有率が低くなり、ボス部のボイド発生が低減する傾向にある。また、S1が低減することで、S1/S2の値は5/95〜45/55の範囲となる傾向にある。ただし、乾燥温度が過度に高すぎたり、乾燥時間が過度に長すぎたりすると、ポリブチレンテレフタレート樹脂又は当該樹脂の酸化劣化が進行するため、上記範囲とすることが好ましい。
以下の実施例および比較例において、射出成形したポリブチレンテレフタレート樹脂材料に使用した成分は、以下の表1の通りである。
上記表1に記載のガラス繊維以外の各成分を、以下の表2以下に示される割合(全て質量部)にて、ブレンドし、これを30mmのベントタイプ二軸押出機(日本製鋼所社製、二軸押出機TEX30α)を使用して、ガラス繊維はサイドフィーダーより供給し、バレル温度270℃にて溶融混練し、ストランドに押し出した後、ストランドカッターによりペレット化し、ポリブチレンテレフタレート樹脂材料のペレットを得た。
得られたペレットを熱風乾燥機を使用して120℃で5時間乾燥させた後、射出成形機(日本製鋼所社製「J85AD」)を用い、シリンダー温度250℃、金型温度80℃の条件で、ISO試験片を射出成形して得られたISO試験片に対して、PerkinElmer社製「PYRIS Diamond DSC」を用いて、窒素雰囲気下、30℃から300℃まで20℃/分の速度で昇温し、300℃で3分保持した後、速度20℃/分の条件で降温し、DSC測定を行った。降温の際に観測される発熱ピークのピークトップの温度を結晶化温度(Tc)とした。
図2は、評価のために成形したボス部付き試験片の形状を示す図である。試験片11の中央にはボス部12が設けられている。図2の(a)図は、(b)図で11と付した側からボス部12側を下にして試験片11を見た図であり、(c)図は(b)図のボス部12を通る中心線A−AでのA−A断面図である。ボス部12は、その高さは2mmであり、図示するようにR=2mmの円を一部切り欠いた切り欠き円柱状に形成されている。また、試験片11の下部には直線状に高さ2mmのリブ13が設けてある。
上記乾燥後のペレットの水分含有率(単位:質量ppm)を、カールフィッシャー法の電量方式の水分測定装置(三菱ケミカルアナリテック社製「CA−200」)を用いて測定した。加熱温度は200℃に設定し、キャリアガスには窒素ガスを用いた。
得られた試験片のボス部及びボス部下方の断面(図2のA−A断面)を、以下のヤマト科学社製X線CT装置を用いて観察した。
装置名:ヤマト科学製 TDM1000H−II(2K)
電圧:80kV 電流:20μA
拡大軸(倍率):40〜110mm
解析ソフト:ラトックシステムエンジニアリング社製、
3次元解析ソフト TRI/3D−BON64
図3中に破線で示す範囲として示したように、ボス部の基体部表面(図3のB−B面)から高さ0〜0.5mmの範囲に存在する空隙の断面面積の合計S1を求め、ボス部下方の基体部表面(図3のB−B面)から深さ0〜0.5mmの範囲に存在する空隙の断面面積の合計S2を求め、S1とS2の合計面積100%に対するS1の面積率(単位:%)及びS2の面積率(単位:%)を算出した。
ボス部強度の測定は、図2に示すように、試験片11を、リブ13とボス部12の間で、台座の固定具(図示せず)にて挟持固定した上で、(b)図中に破線で示した金属製の引張用治具14を用い、その穴部15にボス部12を入れ、引張用治具14を矢印方向に20mm/minの試験速度で引き上げ、ボス部12が破断する際の強度(単位:N)を求め、ボス部強度とした。
上記で得られたポリブチレンテレフタレート樹脂材料のペレットを、熱風乾燥機を使用して120℃で1〜5時間乾燥させ、水分含有率の異なるペレットを得た後、射出成形機(日精樹脂工業社製「NEX80」)にて、シリンダー温度260℃、金型温度80℃、冷却時間20秒、充填時間1.5秒、射出ピーク圧の8割の値を保圧値とする条件で、下側に設けたフィルムゲートから樹脂を注入して、図2に示すボス部付き試験片を成形した。試験片を、プレッシャークッカー(PCT)試験機(平山製作所社製)を用いて、温度121℃、相対湿度100%、圧力2atmの条件で、100時間処理し、同様に強度を測定し、処理前に対する処理後の強度保持率(単位:%)を算出した。
得られたペレットを用い、ファナック製「α100iA型」射出成形機を使用して、シリンダー温度250℃、金型温調機設定温度80℃にて、図4に示すような中央部に仕切りを有する箱形成形品(タテ30mm、ヨコ54mm、奥行き34mm、肉厚1.5mm)を、図4の箱形成形品の矢印で示す左側壁の最前面中央付近に設けたサイドゲート(ゲート厚み1.5mm×ゲート幅3mm)より、樹脂を注入して成形した。
得られた箱形成形品の底板の変形と突き出し時に発生した音により、以下の三段階の基準で判定を行った。
「◎:底板の変形無し、かつ、突き出し時の音発生無し」
「○:底板の変形有り、かつ、突き出し時に異音発生有り」
「×:底板の突き破り有り」
得られたペレットを熱風乾燥機を使用して120℃で表2以下に記載の時間(0〜5時間)乾燥させた後、住友重機械工業社製射出成形機(型締め力50T)を用い、シリンダー温度260℃、金型温度80℃、充填時間1秒、保圧を射出ピーク圧の0割または8割の値、冷却時間10秒の条件にて、厚み1.5mm、外寸30×50×15mm深さの箱型成形品を成形し、エジェクターピンの突き出しで離型させた時の最大抵抗値を離型抵抗値(単位:MPa)として評価した。
評価結果を、以下の表2以下に示す。
2 筐体ケース
3 コネクタ部
4 コネクタ接続口
5 コネクタピン
6 ボス部
Claims (7)
- 電子機器における外部コネクタを挿入接続するためのコネクタ接続口であって、
前記コネクタ接続口は、ポリブチレンテレフタレート樹脂材料を射出成形した成形体からなり、その外周面又は内周面にはボス部が突設しており、
前記ポリブチレンテレフタレート樹脂材料が、ポリブチレンテレフタレート樹脂100質量部に対し、臭素系難燃剤を30〜60質量部、アンチモン化合物を5〜15質量部、無機充填材を30〜100質量部含有し、結晶化温度が180〜193℃であるポリブチレンテレフタレート樹脂組成物であり、
ボス部、並びに、ボス部を突設する外周面又は内周面の下方には、ポリブチレンテレフタレート樹脂材料中に空隙が存在しており、ボス部における前記外周面又は内周面から高さ0〜0.5mmの範囲に存在する空隙の断面面積の合計をS1とし、ボス部を突設する前記外周面又は内周面から深さ0〜0.5mmの範囲に存在する空隙の断面面積の合計をS2とし、S1とS2の合計面積を100%としたとき、S1の面積率が5〜45%、S2の面積率が55〜95%であることを特徴とする電子機器の外部接続用コネクタ接続口。 - 前記無機充填材が、ガラス繊維である請求項1に記載の外部接続用コネクタ接続口。
- 前記ポリブチレンテレフタレート樹脂材料が、エポキシ化合物、臭素化エポキシ化合物、エポキシ基を導入したエラストマーからなる群より選択される少なくとも一種を含有するポリブチレンテレフタレート樹脂組成物である請求項1に記載の外部接続用コネクタ接続口。
- 前記ポリブチレンテレフタレート樹脂材料が、臭素化エポキシ化合物、臭素化ポリカーボネート化合物、及び、臭素化ポリスチレン化合物からなる群から選択される、異なる少なくとも2つ以上の臭素系難燃剤を含有するポリブチレンテレフタレート樹脂組成物である請求項1に記載の外部接続用コネクタ接続口。
- 前記コネクタ接続口が、電子部品と外部接続用コネクタを収納した電子機器の筐体の側面に設けられ、外部コネクタが挿入接続されるための外部接続用コネクタ接続口である請求項1〜4のいずれかに記載の外部接続用コネクタ接続口。
- 前記電子機器が車両用電子機器である請求項5に記載の外部接続用コネクタ接続口。
- 前記車両用電子機器がエンジンコントロールユニットである請求項6に記載の外部接続用コネクタ接続口。