JP6311776B2 - 積層ガラスの製造方法、積層ガラスおよび窓ガラス - Google Patents
積層ガラスの製造方法、積層ガラスおよび窓ガラス Download PDFInfo
- Publication number
- JP6311776B2 JP6311776B2 JP2016225626A JP2016225626A JP6311776B2 JP 6311776 B2 JP6311776 B2 JP 6311776B2 JP 2016225626 A JP2016225626 A JP 2016225626A JP 2016225626 A JP2016225626 A JP 2016225626A JP 6311776 B2 JP6311776 B2 JP 6311776B2
- Authority
- JP
- Japan
- Prior art keywords
- glass
- glass substrate
- laminated glass
- substrate
- laminated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(a)第1の表面および第2の表面を有し、厚さが1.5mm以下であり、アルカリ金属酸化物を含有する第1のガラス基板を準備し、該第1のガラス基板の少なくとも第1の表面を、化学強化処理するステップと、
(b)第3の表面および第4の表面を有し、厚さが1.5mm以下の第2のガラス基板を準備し、該第2のガラス基板の前記第3の表面および/または第4の表面に、熱処理工程を経て、機能部を形成するステップであって、前記第2のガラス基板の前記機能部が形成されていない領域は、化学強化処理されている、ステップと、
(c)接着層を介して、前記第1および第2のガラス基板を、前記第2の表面および前記第3の表面が内側となるようにして接合するステップと、
を有することを特徴とする積層ガラスの製造方法が提供される。
(d)前記第1のガラス基板を曲面状に加工するステップを有し、
前記(c)のステップの前に、
(e)前記第2のガラス基板を曲面状に加工するステップを有し、
前記(c)のステップ後に、曲面状の積層ガラスが得られても良い。
第1のガラス基板は、厚さが1.5mm以下であり、第1の表面および第2の表面を有し、前記第1の表面は、当該積層ガラスの第1の露出面側となり、
第2のガラス基板は、厚さが1.5mm以下であり、第3の表面および第4の表面を有し、前記第4の表面は、当該積層ガラスの第2の露出面側となり、
前記第1のガラス基板の少なくとも前記第1の表面は、化学強化処理されており、
前記第2のガラス基板の前記第3の表面および/または第4の表面には、機能部が形成されており、前記第2のガラス基板の前記機能部が形成されていない領域は、化学強化処理されていることを特徴とする積層ガラスが提供される。
以下、図面を参照して、本発明による積層ガラスの製造方法(積層ガラスの第1の製造方法)について、詳しく説明する。
(a)第1の表面および第2の表面を有し、厚さが1.5mm以下であり、アルカリ金属酸化物を含有する第1のガラス基板を準備し、該第1のガラス基板の少なくとも第1の表面を、化学強化処理するステップ(ステップS110)と、
(b)第3の表面および第4の表面を有し、厚さが1.5mm以下の第2のガラス基板を準備し、該第2のガラス基板の前記第3の表面および/または第4の表面に、熱処理工程を経て、機能部を形成するステップ(ステップS120)と、
(c)接着層を介して、前記第1および第2のガラス基板を、前記第2の表面および前記第3の表面が内側となるようにして接合するステップ(ステップS130)と、
を有する。以下、各ステップについて説明する。
まず、第1のガラス基板が準備される。第1のガラス基板は、アルカリ金属酸化物(例えば、Na2OやLi2O)を含有する限り、その組成は、特に限られない。第1のガラス基板としては、例えば、ソーダライムガラスが代表的な例として挙げられる。
ステップS120は、前述のステップS110とは別途、その前、または後に、あるいは前述のステップS110と併行して同時に、実施される。すなわち、ステップS110とステップS120との順はどちらが先でも、同時でも構わない。
まず、後に黒色セラミック層を構成することになる、セラミック粒子を含む組成物が調製される。この組成物の形態は、特に限られないが、例えばインク状(またはペースト状。以下同じ)であっても良い。
次に、ステップS110で調製された第1のガラス基板と、ステップS120で調製された第2のガラス基板が、接着層を介して接合される。
このステップS112では、まず、第1の表面および第2の表面を有し、厚さが1.5mm以下であり、アルカリ金属酸化物を含有する第1のガラス基板が準備される。
ステップS122は、ステップS112とは別途、その前、または後に、またはステップS112と併行して同時に、実施される。すなわち、ステップS112とステップS122との順はどちらが先でも、同時でも構わない。
次に、図3を参照して、本発明による積層ガラスの第2の製造方法について説明する。
(a)第1の表面および第2の表面を有し、厚さが1.5mm以下であり、アルカリ金属酸化物を含有する第1のガラス基板を準備し、該第1のガラス基板の少なくとも第1の表面を、化学強化処理するステップ(ステップS210)と、
(b)第3の表面および第4の表面を有し、厚さが1.5mm以下の第2のガラス基板を準備し、該第2のガラス基板の前記第3の表面および/または第4の表面に、熱処理工程を経て、機能部を形成するステップ(ステップS220)と、
(c)前記第1および第2のガラス基板を、前記第2の表面および前記第3の表面が内側となるようにして接合するステップであって、前記第1および第2のガラス基板の間には、熱可塑性樹脂基板が配置されるステップ(ステップS230)と、
を有する。
第2の製造方法において、このステップS230では、前記第1および第2のガラス基板が、前記第2の表面および前記第3の表面が内側となるようにして接合される。
ここで、実際に、化学強化処理されたガラス基板に対して熱処理層を形成した場合に、圧縮応力残留層に対して、どのような影響が生じるかを把握するため、以下の実験を行った。
102 第1の露出表面
104 第2の露出表面
110 第1のガラス基板
112 第1のガラス基板の第1の表面
130 第2のガラス基板
134 第2のガラス基板の第4の表面
170 熱処理層
180 接着層
200 本発明による第2の積層ガラス
202 第1の露出表面
204 第2の露出表面
210 第1のガラス基板
212 第1のガラス基板の第1の表面
230 第2のガラス基板
234 第2のガラス基板の第4の表面
270 熱処理層
280 第1の接着層
282 第2の接着層
290 熱可塑性樹脂基板。
Claims (14)
- 第1および第2のガラス基板が積層されて構成される積層ガラスの製造方法であって、
(a)第1の表面および第2の表面を有し、厚さが1.5mm以下(ただし1.5mmを除く)であり、アルカリ金属酸化物を含有する第1のガラス基板を準備し、該第1のガラス基板の少なくとも第1の表面を、化学強化処理するステップと、
(b)第3の表面および第4の表面を有し、厚さが1.5mm以下(ただし1.5mmを除く)の第2のガラス基板を準備し、該第2のガラス基板の前記第3の表面および/または第4の表面に、熱処理工程を経て、機能部を形成するステップであって、前記第2のガラス基板の前記機能部が形成されていない領域は、化学強化処理されており、前記機能部が形成された領域は、化学強化処理されない、ステップと、
(c)接着層を介して、前記第1および第2のガラス基板を、前記第2の表面および前記第3の表面が内側となるようにして接合するステップと、
を有することを特徴とする積層ガラスの製造方法。 - 前記熱処理工程は、前記第2のガラス基板を、600℃〜750℃の温度範囲に保持するステップを有することを特徴とする請求項1に記載の製造方法。
- 前記機能部は、黒色セラミック層、アンテナ線、および曇り止め熱線からなる群から選定された少なくとも一種であることを特徴とする請求項1または2に記載の製造方法。
- 前記(a)のステップの前に、
(d)前記第1のガラス基板を曲面状に加工するステップを有し、
前記(c)のステップの前に、
(e)前記第2のガラス基板を曲面状に加工するステップを有し、
前記(c)のステップ後に、曲面状の積層ガラスが得られることを特徴とする請求項1乃至3のいずれか一項に記載の製造方法。 - 前記(e)のステップは、前記第2のガラス基板の前記熱処理工程と同時に行われることを特徴とする請求項4に記載の製造方法。
- 前記(c)のステップは、前記第1のガラス基板と前記第2のガラス基板の間に、熱可塑性樹脂からなる少なくとも一つの基板を介在させた状態で、実施されることを特徴とする請求項1乃至5のいずれか一項に記載の製造方法。
- 前記熱可塑性樹脂からなる少なくとも一つの基板の厚さは、1mm〜8mmの間であることを特徴とする請求項6に記載の製造方法。
- 第1および第2のガラス基板が積層されて構成される積層ガラスであって、
第1のガラス基板は、厚さが1.5mm以下(ただし1.5mmを除く)であり、第1の表面および第2の表面を有し、前記第1の表面は、当該積層ガラスの第1の露出面側となり、
第2のガラス基板は、厚さが1.5mm以下(ただし1.5mmを除く)であり、第3の表面および第4の表面を有し、前記第4の表面は、当該積層ガラスの第2の露出面側となり、
前記第1のガラス基板の少なくとも前記第1の表面は、化学強化処理されており、
前記第2のガラス基板の前記第3の表面および/または第4の表面には、機能部が形成されており、前記第2のガラス基板の前記機能部が形成されていない領域は、化学強化処理されており、前記機能部が形成された領域は、化学強化処理されていないことを特徴とする積層ガラス。 - 前記第1および第2のガラス基板の間には、接着層が存在することを特徴とする請求項8に記載の積層ガラス。
- 前記第1および第2のガラス基板の間には、熱可塑性樹脂からなる少なくとも一つの基板が配されていることを特徴とする請求項8または9に記載の積層ガラス。
- 前記熱可塑性樹脂からなる少なくとも一つの基板の厚さは、1mm〜8mmの間であることを特徴とする請求項10に記載の積層ガラス。
- 前記機能部は、黒色セラミック層、アンテナ線、および曇り止め熱線からなる群から選定された少なくとも一種であることを特徴とする請求項8乃至11のいずれか一項に記載の積層ガラス。
- 前記積層ガラスは、曲面状であることを特徴とする請求項8乃至12のいずれか一項に記載の積層ガラス。
- 車両用の窓ガラスであって、
当該窓ガラスは、請求項8乃至13のいずれか一項に記載の積層ガラスを有することを特徴とする窓ガラス。