JP6216708B2 - レーダカバーの製造方法及びレーダカバー - Google Patents
レーダカバーの製造方法及びレーダカバー Download PDFInfo
- Publication number
- JP6216708B2 JP6216708B2 JP2014264081A JP2014264081A JP6216708B2 JP 6216708 B2 JP6216708 B2 JP 6216708B2 JP 2014264081 A JP2014264081 A JP 2014264081A JP 2014264081 A JP2014264081 A JP 2014264081A JP 6216708 B2 JP6216708 B2 JP 6216708B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- transparent
- colored layer
- black
- radar cover
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、レーダカバーの製造方法及びレーダカバーに関するものである。
近年、ミリ波等の電波を用いて車両の周囲の障害物等を検知するレーダユニットが車両に搭載されている。このようなレーダユニットは、車両の前面に設けられるラジエータグリルやエンブレムの内側に配置されており、ラジエータグリルを透過する電波の送受信を行う。このため、上述のようなレーダユニットを備える車両においては、ラジエータグリルやエンブレムは、電波の減衰を抑制しつつ当該電波を透過可能に形成する必要がある。
一方で、ラジエータグリルやエンブレムは、車両の前面に配置されることから、車両の意匠上、極めて重要な部分であり、高級感や質感を向上させるために金属光輝性を付与することが多い。従来は、このような金属光輝性を付与するため、めっき処理を施すことが一般的であったが、めっき層は電波を透過しない。このため、近年、金属光輝性を付与しかつ電波を透過可能とするため、電波が透過可能な金属製の蒸着層やスパッタリング層を形成する技術が用いられている。
例えば、特許文献1では、金属光輝性を有しかつ電波が透過可能とされたレドーム(レーダカバー)の製造方法が開示されている。このような特許文献1では、レーダユニットを透過する光輝部材を透明層と有色層との間にインサート成型にて埋設することによって、簡易な工程にてレーダカバーを製造している。
しかしながら、特許文献1では、光輝部材をインサート成型によって埋設するものであることから、光輝部材を金型の内部に収容することになる。このため、インサート成型のときの高熱に光輝部材が晒されることになり、光輝部材の表面に形成された光輝性層(蒸着層やスパッタリング層)がインサート成型のときの熱の影響を受けて極僅かな変形や変色等する場合がある。意匠上、特に重要なラジエータグリルやエンブレムは、極僅かな変形や変色等が生じた場合であっても不良と判定することになる。したがって、特許文献1の方法においては少なからず不良品が発生することになる。
本発明は、上述する問題点に鑑みてなされたもので、光輝部材が高温に晒されることによって生じる外観不良を抑制し、レーダカバーの歩留まりの向上を図ることを目的とする。
本発明は、上記課題を解決するための手段として、以下の構成を採用する。
第1の発明は、車両の周囲状況を検知するレーダユニットを覆うレーダカバーの製造方法であって、凹部を備える透明層と当該凹部を避けて前記透明層に積層配置される有色層とを有するベース部を形成するベース部形成工程と、表面に光輝性を有すると共に縁部を有する光輝部材を、前記縁部を前記透明層と反対側から前記有色層に当接させた状態で、前記透明層の凹部に配置する配置工程と、前記光輝部材の縁部と前記有色層とを固着させる固着工程とを有するという構成を採用する。
第2の発明は、上記第1の発明において、上記ベース部形成工程では、樹脂材からなる上記透明層と当該透明層と異なる樹脂材からなる上記有色層とを二色成形によって成型することで上記ベース部を形成するという構成を採用する。
第3の発明は、上記第1または第2の発明において、上記光輝部材の縁部の上記有色層との当接面と上記有色層の当該縁部との当接面との少なくともいずれかに樹脂製の突起部が設けられ、上記固着工程では、当該突起部を溶融させることにより上記光輝部材を上記有色層に溶着させるという構成を採用する。
第4の発明は、車両の周囲を検知するレーダユニットを覆うレーダカバーであって、凹部を備える透明層と、上記凹部を避けて上記透明層に積層配置される有色層と、上記透明層の上記凹部に配置され、上記透明層と反対側から上記有色層に当接する縁部が上記有色層に固着される光輝部材とを備えるという構成を採用する。
本発明によれば、透明層の凹部を避けるように有色層が積層配置されている。このため、透明層に対して有色層を積層配置した後に、光輝部材を凹部に配置することができる。したがって、透明層と有色層との間に光輝部材を埋設する必要がなく、インサート成型を行う必要がなくなる。また、光輝部材を有色層に固着する方法としては、超音波やレーザ光による溶着方法、熱硬化性樹脂等の接着剤を用いた固着方法等が挙げられる。これらの方法によれば、熱を用いた固着であっても、固着箇所のみへの局所的な入熱で済むことから、インサート成型を行う場合と比較して、光輝部材への熱負荷を大幅に低減することが可能となる。よって、本発明によれば、光輝部材への熱負荷を大幅に低減し、光輝部材が高温に晒されることによって生じる外観不良を抑制し、レーダカバーの歩留まりの向上を図ることが可能となる。
以下、図面を参照して、本発明に係るレーダカバーの製造方法及びレーダカバーの一実施形態について説明する。なお、以下の図面において、各部材を認識可能な大きさとするために、各部材の縮尺を適宜変更している。
図1は、本実施形態のレーダカバーからなるエンブレム10を備えるラジエータグリル1の正面図である。また、図2は、本実施形態のエンブレム10の拡大正面図である。また、図3は、本実施形態のエンブレム10の断面図である。
ラジエータグリル1は、車両のエンジンルームに通じる開口を塞ぐように車両の前面に設けられており、エンジンルームへの通気を確保しかつエンジンルームへの異物の進入を防止している。ラジエータグリル1の中央には、エンジンルーム内に配置されるレーダユニットRに対向するようにしてエンブレム10が設けられている。レーダユニットR(図3参照)は、例えばミリ波を発信する発信部、反射波を受信する受信部、及び、演算処理を行う演算部等を有している。このレーダユニットRは、エンブレム10を透過する電波の送受信を行い、受信した電波に基づいて車両の周囲状況を検知する。例えば、レーダユニットRは、障害物までの距離や障害物の相対速度等を算出して出力する。
エンブレム10は、レーダユニットRを車両の正面側から見て覆うように配置されている。このエンブレム10は、図2に示すように、車両の正面側から見て、車両メーカのエンブレムを示す図形や文字等を表す光輝領域10Aと、当該光輝領域10Aの視認性を向上させる黒色領域10Bを有する部品である。このようなエンブレム10は、図3に示すように、ベース部11と、光輝部材12とを備えている。
ベース部11は、透明部11a(透明層)と、黒色部11b(有色層)とを備えている。透明部11aは、最も車両の外側に配置される略矩形状の透明材料により形成される部位である。この透明部11aは、車両の外部からの光輝部材12(光輝領域10A)の視認性を高めるため、表側の面が円滑面とされている。また、透明部11aの裏側には、光輝部材12が配置される凹部11a1が形成されている。また、透明部11aの裏側の面は、凹部11a1が設けられていない領域が、黒色部11bとの接触面とされている。
凹部11a1は、光輝部材12を収容する部位であり、収容された光輝部材12を車両の前方側から立体的に視認可能とする。この凹部11a1は、車両メーカのエンブレム等の図形や文字等の形状に沿って設けられている。このような凹部11a1に光輝部材12が収容されることによって、上述の光輝領域10Aが形成される。
このような透明部11aは、例えば、無色のPC(ポリカーボネート)やPMMA(ポリメタクリル酸メチル樹脂)等の透明合成樹脂によって形成されており、1.5mm〜10mm程度の厚さとされている。また、透明部11aの表側の面には、必要に応じて、傷付き防止のためのハードコート処理、又はウレタン系塗料のクリヤーコート処理が施される。なお、耐傷付き性を備える透明合成樹脂であれば、これらの傷付き防止処理は不要である。
黒色部11bは、透明部11aの裏側の面に対して積層配置される層であり、黒色材料から形成される部位である。この黒色部11bは、図3に示すように、凹部11a1を避けて透明部11aに積層配置されている。つまり、黒色部11bは、凹部11a1が露出されるように開口11b1を有しており、開口11b1が凹部11a1に重なるように透明部11aの裏側に積層配置されている。また、黒色部11bには、開口11b1の縁部に、段部11b3が設けられている。この段部11b3は、黒色部11bの開口11b1に沿った領域が、他の領域に対して薄肉化されることによって形成されており、光輝部材12の後述するフランジ12bが固着される部位である。また、黒色部11bは、エンジンルーム側に突出する係合部11b2を有している。この係合部11b2は、先端部が爪状に成形されており、当該先端部が例えばラジエータグリル本体に係止される。
このように透明部11aの裏側の面に対して積層配置された黒色部11bは、透明部11aの外側から視認可能とされており、上述の黒色領域10Bを形成している。つまり、黒色部11bは、光輝領域10A以外の領域を黒色に視認させ、相対的に光輝領域10Aの視認性を向上させる。
このような黒色部11bは、ABS(アクリロニトリル・ブタジエン・スチレン共重合合成樹脂)、AES(アクリロニトリル・エチレン・スチレン共重合合成樹脂)、ASA(アクリロニトリル・スチレン・アクリレート)、PBT(ポリブチレンテレフタレート)、有色のPC、PET(ポリエチレンテレフタレート)等の合成樹脂、又はこれらの複合樹脂からなり、0.5mm〜10mm程度の厚さとされている。
これらの透明部11a及び黒色部11bを有するベース部11は、二色成形によって形成される。例えば、透明部11aが先に成形され、先に形成された透明部11aの裏側の面に凹部11a1を避けるように黒色部11bが形成される。このような二色成形によって、透明部11aと黒色部11bとが一体化されてなるベース部11を容易に形成することができる。ただし、ベース部11の形成方法については、二色成形に限られるものではなく、例えば別々に透明部11aと黒色部11bとを射出成型し、別体の透明部11aと黒色部11bとを接着剤や溶着により固着することによってベース部11を形成することも可能である。
図3に示すように、光輝部材12は、基部12aと、フランジ12bと、光輝層12cを備えている。基部12aとフランジ12bとは射出成型等によって一体的に成形されており、例えばABS、PC又はPET等の合成樹脂によって形成されている。基部12aは、凹部11a1内に設置されることにより、凹部11a1を埋設する部位である。この基部12aは、表面に形成される光輝層12cを凹部11a1の内壁面に接触させる形状とされている。フランジ12bは、基部12aを囲うように形成されており、光輝部材12の縁部を形成している。このフランジ12bは、黒色部11bに設けられた段部11b3に当接する部位である。なお、図3に示すように、基部12aは、フランジ12bよりも透明部11a側に突出するように設けられている。
光輝層12cは、基部12aの表側の面(透明部11a側の面)に形成されており、金属光輝性を備える層である。この光輝層12cは、例えば金属蒸着処理を用いて形成された金属層と、該金属層を保護するためのベースコート層及びトップコート層(いずれも図示せず)とが積層されてなる。蒸着処理としては真空蒸着法やスパッタリングが用いられ、蒸着される金属としてはインジウム、アルミ又は錫等が使用される。ベースコート層及びトップコート層は、蒸着処理によって形成され薄く脆い金属層を保護するためのものである。ベースコート層及びトップコート層は、透明(着色透明を含む)な合成樹脂を用いたクリヤー塗装によって形成されている。光輝層12cの金属層は非常に薄くかつ目視できない程度の複数の隙間を有しており、十分な電波透過性能を備えている。なお、光輝層12cは上述の方法で形成されることに限定されるものではなく、十分な電波透過性能を持ち、且つ金属光輝性を備えることのできる塗装その他の方法によって形成してもよい。
続いて、本実施形態のエンブレム10の製造方法について説明する。図4は、本実施形態のエンブレム10の製造工程を示す概略図である。
図4(a)は、ベース部形成工程を示す概略図である。この図に示すように、ベース部形成工程では、ベース部11の形成を行う。例えば、まず不図示の第1の型を用いて透明部11aを射出成型によって形成し、続いて不図示の第2の型を用いた射出成型によって透明部11aに黒色部11bを積層配置する。すなわち、樹脂材からなる透明部11aと当該透明部11aと色が異なる樹脂材からなる黒色部11bとが二色成形によって一体的に形成される。このとき、第1の型によって透明部11aを形成するときに、透明部11aに対して凹部11a1が形成される。また、第2の型によって黒色部11bを形成するときに凹部11a1を避けて黒色部11bが形成される。
図4(b)及び図4(c)は、光輝部材形成工程を示す概略図である。この図に示すように、光輝部材形成工程では、まず図4(b)に示すように、基部12aとフランジ12bとを射出成型によって一体的に形成する。このとき、図5(a)の拡大図に示すように、フランジ12bの透明部11aとの当接面には、溶着リブ12d(樹脂製の突起部)が設けられる。この溶着リブ12dは、例えば基部12aを囲うよう環状に設けられており、後の工程において透明部11aとフランジ12bとを溶着するために溶融される部位である。
続いて、光輝部材形成工程では、図4(c)に示すように、基部12aの表側の面に対して光輝層12cを形成する。ここでは、例えばベースコート層、金属層及びトップコート層を基部12a側から順に成膜することによって光輝層12cが形成される。ベースコート層及びトップコート層は例えば透明合成樹脂を用いたクリヤー塗装によって形成され、金属層は金属蒸着処理により形成される。
なお、フランジ12bの表側の面(車両の前方側の面)は、黒色部11bと当接するため、透明部11aを通じて外部から視認することはできない。このため、フランジ12bの表側の面に対しては、光輝層12cを形成する必要はない。したがって、光輝層12cを形成するときには、フランジ12bの表面をマスクしても良い。ただし、光輝層12cは薄く、後の透明部11aとフランジ12bとを溶着する工程で熱により剥離される。したがって、マスクを行うことなく、光輝層12cをフランジ12bの表側の面にも形成してしまうことが簡便で良い。
また、図4(a)に示すベース部形成工程と、図4(b)及び図4(c)に示す光輝部材形成工程とは、独立して進行できる作業工程である。このため、製造時間の短縮のため、ベース部形成工程と光輝部材形成工程とは並行して行うことが望ましい。
図4(d)は、光輝部材配置工程を示す概略図である。この図に示すように、光輝部材配置工程では、まず上述の光輝部材形成工程で形成された光輝部材12を、上述のベース部形成工程で形成されたベース部11の凹部11a1に収容するように配置する。このとき、図5(b)に示すように、光輝部材12の溶着リブ12dが、ベース部11の黒色部11bが有する段部11b3に当接するように、凹部11a1に対して光輝部材12を配置する(配置工程)。
次に、溶着リブ12dを溶融させて光輝部材12を黒色部11bに対して溶着させる(固着工程)。溶着リブ12dを溶融させると溶着リブ12dが溶融して広がることによって光輝部材12が透明部11a側に近づき、これによって光輝層12cが凹部11a1の内壁面に当接する。
ここでは、例えば、超音波溶着法やレーザ透過溶着法等によって光輝部材12を黒色部11bに対して溶着させる。超音波溶着法を用いる場合には、例えば光輝部材12に対して超音波振動を付与し、この振動によって溶着リブ12dと黒色部11bとの界面に摩擦熱を発生させ、この摩擦熱によって溶着リブ12dを溶融させ、その後冷却することで光輝部材12を黒色部11bに対して溶着させる。また、レーザ透過溶着法では、例えば光輝部材12をレーザ光が透過する材料によって形成し、裏側からレーザ光を溶着リブ12dに照射することにより溶着リブ12dを溶融させ、その後冷却することで光輝部材12を黒色部11bに対して溶着させる。
以上のような工程によって本実施形態のエンブレム10が製造される。このような本実施形態のエンブレム10及び当該エンブレム10の製造方法によれば、透明部11aの凹部11a1を避けるように黒色部11bが積層配置されている。このため、透明部11aに対して黒色部11bを積層配置した後に、光輝部材12を凹部11a1に配置することができる。したがって、透明部11aと黒色部11bとの間に光輝部材12を挟み込むように埋設する必要がなく、インサート成型を行う必要がなくなる。また、光輝部材12の黒色部11bへの固着は、超音波やレーザ光による溶着方法によって行うことができる。これらの方法によれば、固着箇所のみへの局所的な入熱で済むことから、インサート成型を行う場合と比較して、光輝部材12(すなわち光輝層12c)への熱負荷を大幅に低減することが可能となる。よって、本実施形態のエンブレム10及び当該エンブレム10の製造方法によれば、光輝部材12への熱負荷を大幅に低減し、光輝部材12が高温に晒されることによって生じる外観不良を抑制し、エンブレム10の歩留まりの向上を図ることが可能となる。
また、本実施形態のエンブレム10の製造方法においては、ベース部形成工程で、樹脂材からなる透明部11aと当該透明部11aと色が異なる樹脂材からなる黒色部11bとを二色成形によって成型することでベース部11を形成している。このため、透明部11aと黒色部11bとを容易に一体化させることができ、ベース部11を短時間で形成することが可能となる。
また、本実施形態のエンブレム10の製造方法においては、光輝部材12のフランジ12bを透明部11aと反対側から黒色部11bに当接させた状態で光輝部材12を凹部11a1に配置し、光輝部材12のフランジ12bと黒色部11bとを固着させている。このため、光輝部材12の一部(すなわちフランジ12b)のみを黒色部11bに固着すれば良く、固着の時における光輝層12cへの影響をより抑止することが可能となる。
また、本実施形態のエンブレム10の製造方法においては、光輝部材12のフランジ12bの黒色部11bとの当接面に溶着リブ12dが設けられ、この溶着リブ12dを溶融させることにより光輝部材12を黒色部11bに溶着させている。このため、フランジ12bのそのものを直接的に加熱する必要がなくなり、フランジ12b等にヒケが生じることを防止することが可能となる。
以上、添付図面を参照しながら本発明の好適な実施形態について説明したが、本発明は上記実施形態に限定されないことは言うまでもない。上述した実施形態において示した各構成部材の諸形状や組み合わせ等は一例であって、本発明の趣旨から逸脱しない範囲において設計要求等に基づき種々変更可能である。
例えば、上記実施形態においては、フランジ12bが当接される黒色部11bの当接面が平面である構成について説明した。しかしながら、本発明はこれに限定されるものではなく、例えば図6(a)に示すように、溶着リブ12dが嵌合される溝部11cを設けるようにしても良い。このような溝部11cを設けることによって、溶着前の光輝部材12の位置決めを容易に行うことが可能となる。なお、黒色部11b側に溶着リブを設けても良い。
また、図6(b)に示すように、溶着リブ12d及び溝部11cを複数設けるようにしても良い。このとき、溝部11cは必須ではなく、上記実施形態と同様に黒色部11bの当接面を平面としても良い。このように、溶着リブ12dを複数設けることによって、光輝部材12をより強固に黒色部11bに対して固定することができる。上記実施形態のエンブレム10においては、光輝部材12の裏側の面を抑える部材が存在しないことから、このように光輝部材12をより強固に黒色部11bに対して固定することによって、光輝部材12の剥離等を確実に防止することができる。また、このように、光輝部材12をより強固に黒色部11bに対して固定するために、どのような溶着方法を用いる場合であっても、光輝部材12を黒色部11b側に押圧しながら溶着を行うことが望ましい。
また、上記実施形態においては、光輝部材12の基部12aを囲うように環状とされた溶着リブ12dを有する構成を採用した。しかしながら、本発明はこれに限定されるものではない。例えば、図7(a)に示すように、C型の溶着リブ12d1を切欠きの方向を変化させながら、フランジ12bに沿って複数配列する構成を採用することも可能である。また、図7(b)に示すように、略S型の溶着リブ12d2を、姿勢を変化させて、フランジ12bに沿って複数配列する構成を採用することも可能である。また、図7(c)に示すように、半円弧状の溶着リブ12d3を、姿勢を変化させて、フランジ12bに沿って複数配列する構成を採用することも可能である。また、図7(d)に示すように、並行に並ぶ3本の棒状部からなる溶着リブ12d4を、姿勢を変化させて、フランジ12bに沿って複数配列する構成を採用することも可能である。このような溶着リブ12d1〜12d4によれば、様々な姿勢とされているため、溶融したときの濡れ広がりを均一化することができ、フランジ12b等におけるヒケの発生を抑止することが可能となる。
また、上記実施形態においては、黒色部11bと光輝部材12とを溶着させる構成について説明した。しかしながら、本発明はこれに限定されるものではなく、接着剤を用いて黒色部11bと光輝部材12とを固着させる構成を採用することも可能である。
また、上記実施形態においては、透明部11aと黒色部11bとを二色成形によって一体的に形成する構成を採用した。しかしながら、本発明はこれに限定されるものではなく、例えば、透明部11aと黒色部11bとを接着剤等によって固着するようにしても良い。
また、黒色部11bではなく、他の色の有色部(有色層)を用いる構成を採用することも可能である。
また、上記実施形態においては、本発明のレーダカバーがエンブレム10である構成について説明した。しかしながら、本発明はこれに限定されるものではない。例えば、ラジエータグリルの他の一部あるいは全部を本発明のレーダカバーとする構成を採用することも可能である。
1……ラジエータグリル、10……エンブレム(レーダカバー)、11……ベース部、11a……透明部(透明層)、11a1……凹部、11b……黒色部(有色層)、12……光輝部材、12a……基部、12b……フランジ(縁部)、12c……光輝層、12d……溶着リブ、12d1〜12d4……溶着リブ
Claims (4)
- 車両の周囲状況を検知するレーダユニットを覆うレーダカバーの製造方法であって、
凹部を備える透明層と当該凹部を避けて前記透明層に積層配置される有色層とを有するベース部を形成するベース部形成工程と、
表面に光輝性を有すると共に縁部を有する光輝部材を、前記縁部を前記透明層と反対側から前記有色層に当接させた状態で、前記透明層の凹部に配置する配置工程と、
前記光輝部材の縁部と前記有色層とを固着させる固着工程と
を有することを特徴とするレーダカバーの製造方法。 - 前記ベース部形成工程では、樹脂材からなる前記透明層と当該透明層と異なる樹脂材からなる前記有色層とを二色成形によって成型することで前記ベース部を形成することを特徴とする請求項1記載のレーダカバーの製造方法。
- 前記光輝部材の縁部の前記有色層との当接面と前記有色層の当該縁部との当接面との少なくともいずれかに樹脂製の突起部が設けられ、
前記固着工程では、当該突起部を溶融させることにより前記光輝部材を前記有色層に溶着させる
ことを特徴とする請求項1または2記載のレーダカバーの製造方法。 - 車両の周囲状況を検知するレーダユニットを覆うレーダカバーであって、
凹部を備える透明層と、
前記凹部を避けて前記透明層に積層配置される有色層と、
前記透明層の前記凹部に配置され、前記透明層と反対側から前記有色層に当接する縁部が前記有色層に固着される光輝部材と
を備えることを特徴とするレーダカバー。