JP5926569B2 - 二重袋包装体用インフレーションフィルムおよび二重袋包装体 - Google Patents
二重袋包装体用インフレーションフィルムおよび二重袋包装体 Download PDFInfo
- Publication number
- JP5926569B2 JP5926569B2 JP2012022573A JP2012022573A JP5926569B2 JP 5926569 B2 JP5926569 B2 JP 5926569B2 JP 2012022573 A JP2012022573 A JP 2012022573A JP 2012022573 A JP2012022573 A JP 2012022573A JP 5926569 B2 JP5926569 B2 JP 5926569B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- film
- mass
- double bag
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
物性強度が強いという特徴がある。
(1)A/E/B/E/D
(2)A/E/C/B/E/D
(3)A/E/B/C/E/D
本発明においては、本発明の効果を阻害しない範囲で、最外層、中間層および最内層のいずれか、またはすべての層に添加剤を含有させることができる。例えば、顔料を添加した場合、遮光効果による被収容物の鮮度保持やフィルム切り片が被収容物に混入したとしても発見しやすいというメリットがある。また、色の異なる顔料を使用することで被充填物の種類を包装体の色で判別できる効果もある。なお、顔料は内容物と接触しない最外層側もしくは中間層に添加することが好ましい。
各インフレーションフィルムのイージーピール面同士をシール温度170℃、シール時間1.5秒、シール圧力3.1kg/cm2でフィルム幅方向にヒートシールした。上記シール部分を15mm幅の短冊状に切り取り、95℃条件下で引張試験にて200mm/分の引張速度で引っ張った時の応力を測定した。測定されたイージーピール強度から、5.88N/15mm幅以上:「○」、5.88gf/15mm幅以下:「×」とした。
各インフレーションフィルムを用いて、縦ピロー包装機ONP−2550(オリヒロ社製)にかけ、二重袋包装体を作製した。シール温度は、140℃〜170℃までの10℃刻みとした。上記縦シール部分を15mm幅の短冊状に切り取り、常温下で引張試験機にて200mm/分の引張速度で引っ張った時の応力を測定した。測定されたイージーピール強度から、7.85〜15.69N/15mm幅:「○」、7.85N/15mm幅以下または15.69N/15mm幅以上:「×」とした。
各インフレーションフィルムを用いて、縦ピロー包装機ONP−2550(オリヒロ社製)にかけ、二重袋包装体を作製し、シール温度170℃で熱水(95℃)を5kg充填した。熱水の荷重がかかる底シール部分が、シール抜けしなかった場合:「○」、シール侵食やシール抜けがあった場合:「×」とした。
各インフレーションフィルムを用いて、縦ピロー包装機ONP−2550(オリヒロ社製)にかけ、二重袋包装体を作製し、シール温度170℃で熱水(95℃)を5kg充填した2重袋包装体を高さ80cmから水平に10回、落下させた。破袋やシール漏れが発生したものを「×」、破袋やシール漏れが起きなかったものを「○」とした。
実施例1〜5および比較例1〜9として、5層からなる共押出しインフレーションフィルムを製造した。フィルムの総厚みは60μmである。
インフレーションフィルムの層構成を以下に示す。なお、内層とは円筒形フィルムの軸芯側の層であり、外層とはその反対側の層である。
第1層(外層(イージーピール層)):直鎖状低密度ポリエチレン樹脂(LLDPE)+ポリブチレン−1樹脂(PB−1)(6μm)
第2層(接着樹脂層):カルボン酸変性エチレン−酢酸ビニル共重合体(7.5μm)
第3層(中間層):6ナイロン(11μm)
第4層(接着樹脂層):カルボン酸変性エチレン−酢酸ビニル共重合体(7.5μm)
第5層(内層):直鎖状低密度ポリエチレン樹脂(LLDPE)(28μm)
総厚み60μm
外層として、密度=0.952g/cm3、MFR(温度:190℃、21.18N、キャピラリーダイの内径:9.550mm±0.025mm)=9g/10分のLLDPE(プライムポリマー社製、ハイゼックス)85質量%と、MFR(温度:190℃、21.18N、キャピラリーダイの内径:9.550mm±0.025mm)=1.8g/10分のポリブチレン−1樹脂(三井化学社製、タフマー)25質量%のブレンド樹脂に、実施例1と同様のスリップ剤を添加した組成物を用いた以外は、実施例1と同様にしてインフレーションフィルムを作製した。
外層として、密度=0.931g/cm3、MFR(温度:190℃、21.18N、キャピラリーダイの内径:9.550mm±0.025mm)=20g/10分のLLDPE(宇部丸善ポリエチレン社製、ユメリット)70質量%と、MFR(温度:230℃、21.18N、キャピラリーダイの内径:9.550mm±0.025mm)=1.3g/10分のポリプロピレン樹脂(日本ポリプロ社製、ノバテックPP)20質量%のブレンド樹脂に、実施例1と同様のスリップ剤およびアンチブロッキング剤を添加した組成物を用いた以外は、実施例1と同様にしてインフレーションフィルムを作製した。
外層として、密度=0.910g/cm3、MFR(温度:190℃、21.18N、キャピラリーダイの内径:9.550mm±0.025mm)=8g/10分のLLDPE(プライムポリマー社製、モアテック)80質量%と、MFR(温度:190℃、21.18N、キャピラリーダイの内径:9.550mm±0.025mm)=1.8g/10分のポリブチレン−1樹脂(三井化学社製、タフマー)20質量%のブレンド樹脂に、該ブレンド樹脂全体を100質量部として、実施例1と同様のスリップ剤およびアンチブロッキング剤を添加した組成物を用いた以外は、実施例1と同様にしてインフレーションフィルムを作製した。
外層として、密度=0.921g/cm3、MFR(温度:190℃、21.18N、キャピラリーダイの内径:9.550mm±0.025mm)=16g/10分のLLDPE(日本ポリエチレン社製、ノバテックLL)80質量%と、MFR(温度:190℃、21.18N、キャピラリーダイの内径:9.550mm±0.025mm)=1.8g/10分のポリブチレン−1樹脂(三井化学社製、タフマー)20質量%のブレンド樹脂に、該ブレンド樹脂全体を100質量部として、実施例1と同様のスリップ剤およびアンチブロッキング剤を添加した組成物を用いた以外は、実施例1と同様にしてインフレーションフィルムを作製した。
外層として、密度=0.947g/cm3、MFR(温度:190℃、21.18N、キャピラリーダイの内径:9.550mm±0.025mm)=6g/10分のLLDPE(プライムポリマー社製、モアテック)80質量%と、MFR(温度:190℃、21.18N、キャピラリーダイの内径:9.550mm±0.025mm)=1.8g/10分のポリブチレン−1樹脂(三井化学社製、タフマー)20質量%のブレンド樹脂に、該ブレンド樹脂全体を100質量部として、実施例1と同様のスリップ剤およびアンチブロッキング剤を添加した組成物を用いた以外は、実施例1と同様にしてインフレーションフィルムを作製した。
10’ 平板状フィルム
11 円筒形金型
12、13 ロール
14 巻き取り機
15 原反
21 内層
22 中間層
23 外層
24 空間(空気層)
30a、30b、30c 単葉
40a 単葉(折目つき)
40b 中間品
40c 二重袋包装体
41、42、43、44 折り目
45、46、48 重複部分
47 開口
50 被収容物
Claims (2)
- イージーピール性を有する、厚み3〜15μmの外層、
ポリアミド樹脂からなる中間層、および、
低密度ポリエチレン樹脂からなる内層
を備えて構成される二重袋包装体用インフレーションフィルムであって、
前記外層が、外層全体の質量を100質量%として、以下に示される50〜90質量%の樹脂組成物Aと10〜50質量%の樹脂組成物Bとから構成されており、
前記外層が95℃で5.88N/15mm幅以上の剥離強度を有し、かつ常温で7.85〜15.69N/15mm幅の剥離強度を有することを特徴とする二重袋包装体用インフレーションフィルム。
・樹脂組成物A:主成分が密度0.930g/cm3以上であり、かつメルトフローレート(温度:190℃、荷重:21.18N、キャピラリーダイの内径:9.550mm±0.025mm)9g/10分以上の直鎖状低密度ポリエチレンである樹脂組成物、
・樹脂組成物B:主成分がメルトフローレート(温度:190℃、21.18N、キャピラリーダイの内径:9.550mm±0.025mm)2g/10分以下のポリブチレンまたはメルトフローレート(温度:230℃、21.18N、キャピラリーダイの内径:9.550mm±0.025mm)2g/10分以下のポリプロピレンである樹脂組成物。 - 請求項1に記載のインフレーションフィルムにより製袋したイージーピール性を有する二重袋包装体。