JP5587312B2 - 機能膜付粘着テープおよび機能膜の転写方法 - Google Patents
機能膜付粘着テープおよび機能膜の転写方法 Download PDFInfo
- Publication number
- JP5587312B2 JP5587312B2 JP2011520728A JP2011520728A JP5587312B2 JP 5587312 B2 JP5587312 B2 JP 5587312B2 JP 2011520728 A JP2011520728 A JP 2011520728A JP 2011520728 A JP2011520728 A JP 2011520728A JP 5587312 B2 JP5587312 B2 JP 5587312B2
- Authority
- JP
- Japan
- Prior art keywords
- functional film
- adhesive layer
- pressure
- sensitive adhesive
- adhesive tape
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(i)前記機能膜の表面に、接着層を介して転写部材を接着する工程。
(ii)ついで前記粘着剤層の温度を、前記側鎖結晶性ポリマーの融点以上の温度にして粘着力を低下させ、前記粘着剤層から機能膜を取り外し、機能膜を粘着剤層から転写部材に転写する工程。
以下、本発明の機能膜付粘着テープ(以下、「粘着テープ」と言うことがある。)にかかる一実施形態について、機能膜に無機封止膜を用いた場合を例に挙げ、図1を参照して詳細に説明する。同図に示すように、本実施形態にかかる機能膜付粘着テープ10は、基材フィルム1の片面に、粘着剤層2と、無機封止膜3と、離型層4とが、この順に積層されてなる。
次に、前記した機能膜付粘着テープ10における無機封止膜3の転写方法について、図2を参照して詳細に説明する。なお、図2においては、前述した図1と同一の構成部分には同一の符号を付して説明は省略する。
エチルヘキシルアクリレートを52部、メチルアクリレートを40部、ヒドロキシエチルアクリレートを8部、および開始剤としてパーブチルND(日油社製)を0.2部の割合で、それぞれトルエン200部に加え、60℃で5時間攪拌して、これらのモノマーを重合させた。得られた共重合体の重量平均分子量は46万であった。
エチルヘキシルアクリレートを92部、ヒドロキシエチルアクリレートを8部、および開始剤としてパーブチルND(日油社製)を0.2部の割合で、それぞれトルエン200部に加え、60℃で5時間攪拌して、これらのモノマーを重合させた。得られた共重合体の重量平均分子量は47万であった。
ベヘニルアクリレートを40部、ステアリルアクリレートを35部、メチルアクリレートを20部、アクリル酸を5部、連鎖移動剤としてドデシルメルカプタンを6部、および開始剤としてパーヘキシルPV(日油社製)を1.0部の割合で、それぞれトルエン100部に加え、80℃で5時間攪拌して、これらのモノマーを重合させた。得られた共重合体の重量平均分子量は8,000、融点は52℃であった。
ステアリルアクリレートを95部、アクリル酸を5部、連鎖移動剤としてドデシルメルカプタンを5部、および開始剤としてパーヘキシルPV(日油社製)を1.0部の割合で、それぞれトルエン100部に加え、80℃で5時間攪拌して、これらのモノマーを重合させた。得られた共重合体の重量平均分子量は8,500、融点は51℃であった。
(非粘着層)
組成:フッ素樹脂(PTFE)
形状:ドット状
厚さ:500nm
形成方法:蒸着
(蒸着)
雰囲気温度:200℃
真空度:10-2torr
アクリル系粘着剤(綜研化学社製の「SK−1340」)100部に対し、固形分換算で架橋剤(綜研化学社製の「M−5A」)を2.4部添加して得た粘着剤溶液を、厚さ100μmのポリエチレンテレフタレートフィルムの片面に塗布して乾燥させ、厚さ30μmの粘着剤層が形成された粘着テープを作製した。
上記で得た各粘着テープについて、無機封止膜の取り外し性を評価した。評価方法を以下に示すとともに、その結果を表2に示す。
無機封止膜として、いずれも厚さ50μmのアルミニウム膜および石英ガラス膜を用いた。これら各無機封止膜を、23℃の雰囲気温度において、前記粘着剤層の表面に積層した。ついで、各無機封止膜表面に、アクリル系粘着テープ(日東電工社製の「No−535A」)を貼着した。ついで、雰囲気温度を23℃から60℃に昇温した後、前記アクリル系粘着テープを指で軽く持ち上げることによって、無機封止膜の取り外し性を評価した。評価基準は以下のように設定した。
△:若干の負荷がかかるものの、実使用上は問題のない範囲であり、無機封止膜を破損することなく粘着剤層から取り外すことができた。
×:大きな負荷がかかり、無機封止膜が変形するか破損した。
Claims (11)
- 基材フィルムと、
この基材フィルムの片面に積層される粘着剤層と、
この粘着剤層の表面に積層される機能膜と、を備え、
前記粘着剤層は、
感圧性接着剤および側鎖結晶性ポリマーを含有するとともに、
該側鎖結晶性ポリマーの融点以上の温度で粘着力が低下し、
前記機能膜が無機封止膜であることを特徴とする機能膜付粘着テープ。 - 前記側鎖結晶性ポリマーは、前記融点未満の温度で結晶化し、かつ前記融点以上の温度で流動性を示す請求項1記載の機能膜付粘着テープ。
- 前記側鎖結晶性ポリマーが、炭素数16以上の直鎖状アルキル基を有する(メタ)アクリレート20〜100重量部と、炭素数1〜6のアルキル基を有する(メタ)アクリレート0〜70重量部と、極性モノマー0〜10重量部と、を重合させて得られる重合体である請求項1または2記載の機能膜付粘着テープ。
- 前記粘着剤層と機能膜との間に介在され、前記粘着剤層の表面を部分的に露出させる非粘着層と、を更に備えた請求項1〜3のいずれかに記載の機能膜付粘着テープ。
- 前記非粘着層は、蒸着により形成されている請求項4記載の機能膜付粘着テープ。
- 前記非粘着層がフッ素樹脂からなる請求項4または5記載の機能膜付粘着テープ。
- 前記非粘着層の厚さが1μm以下である請求項4〜6のいずれかに記載の機能膜付粘着テープ。
- 前記機能膜の厚さが0.01〜100μmである請求項1〜7のいずれかに記載の機能膜付粘着テープ。
- 前記機能膜の表面に離型層を設けた請求項1〜8のいずれかに記載の機能膜付粘着テープ。
- 前記無機封止膜がアルミニウム膜または石英ガラス膜である請求項1〜9のいずれかに記載の機能膜付粘着テープ。
- 請求項1〜10のいずれかに記載の機能膜付粘着テープにおける機能膜を転写部材に転写する方法であって、
前記機能膜の表面に、接着層を介して転写部材を接着する工程と、
ついで前記粘着剤層の温度を、前記側鎖結晶性ポリマーの融点以上の温度にして粘着力を低下させ、前記粘着剤層から機能膜を取り外し、機能膜を粘着剤層から転写部材に転写する工程と、
を含むことを特徴とする機能膜の転写方法。