JP5586008B2 - 強度が非常に高い最終製品の熱機械的成形方法およびその方法により製造された製品 - Google Patents

強度が非常に高い最終製品の熱機械的成形方法およびその方法により製造された製品 Download PDF

Info

Publication number
JP5586008B2
JP5586008B2 JP2009550726A JP2009550726A JP5586008B2 JP 5586008 B2 JP5586008 B2 JP 5586008B2 JP 2009550726 A JP2009550726 A JP 2009550726A JP 2009550726 A JP2009550726 A JP 2009550726A JP 5586008 B2 JP5586008 B2 JP 5586008B2
Authority
JP
Japan
Prior art keywords
steel
product
forming
aluminum
blank
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP2009550726A
Other languages
English (en)
Japanese (ja)
Other versions
JP2010527407A5 (https=
JP2010527407A (ja
Inventor
マルゴット、ユリア、フロット
ロナルド、セオドア、ファン、トル
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tata Steel Ijmuiden BV
Original Assignee
Tata Steel Ijmuiden BV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tata Steel Ijmuiden BV filed Critical Tata Steel Ijmuiden BV
Publication of JP2010527407A publication Critical patent/JP2010527407A/ja
Publication of JP2010527407A5 publication Critical patent/JP2010527407A5/ja
Application granted granted Critical
Publication of JP5586008B2 publication Critical patent/JP5586008B2/ja
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C21D1/185—Hardening; Quenching with or without subsequent tempering from an intercritical temperature
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D7/00—Modifying the physical properties of iron or steel by deformation
    • C21D7/13—Modifying the physical properties of iron or steel by deformation by hot working
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C21D9/48—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals deep-drawing sheets
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C18/00—Alloys based on zinc
    • C22C18/04—Alloys based on zinc with aluminium as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12785—Group IIB metal-base component
    • Y10T428/12792—Zn-base component
    • Y10T428/12799—Next to Fe-base component [e.g., galvanized]

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • Metallurgy (AREA)
  • Mechanical Engineering (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Coating With Molten Metal (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Heat Treatment Of Articles (AREA)
  • Body Structure For Vehicles (AREA)
  • Heat Treatment Of Steel (AREA)
JP2009550726A 2007-02-23 2008-02-22 強度が非常に高い最終製品の熱機械的成形方法およびその方法により製造された製品 Expired - Fee Related JP5586008B2 (ja)

Applications Claiming Priority (5)

Application Number Priority Date Filing Date Title
EP07003812.0 2007-02-23
EP07003812 2007-02-23
EP07004332 2007-03-02
EP07004332.8 2007-03-02
PCT/EP2008/052213 WO2008102012A1 (en) 2007-02-23 2008-02-22 Method of thermomechanical shaping a final product with very high strength and a product produced thereby

Publications (3)

Publication Number Publication Date
JP2010527407A JP2010527407A (ja) 2010-08-12
JP2010527407A5 JP2010527407A5 (https=) 2011-04-07
JP5586008B2 true JP5586008B2 (ja) 2014-09-10

Family

ID=39462004

Family Applications (1)

Application Number Title Priority Date Filing Date
JP2009550726A Expired - Fee Related JP5586008B2 (ja) 2007-02-23 2008-02-22 強度が非常に高い最終製品の熱機械的成形方法およびその方法により製造された製品

Country Status (9)

Country Link
US (2) US8721809B2 (https=)
EP (1) EP2126144B1 (https=)
JP (1) JP5586008B2 (https=)
KR (1) KR101504370B1 (https=)
BR (1) BRPI0807565B1 (https=)
ES (1) ES2656070T3 (https=)
MX (1) MX2009008557A (https=)
RU (1) RU2469102C2 (https=)
WO (1) WO2008102012A1 (https=)

Families Citing this family (53)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5425770B2 (ja) * 2007-07-19 2014-02-26 タタ、スティール、アイモイデン、ベスローテン、フェンノートシャップ 長さ方向において厚さが変化する鋼ストリップ
CN101755063A (zh) * 2007-07-19 2010-06-23 科鲁斯斯塔尔有限公司 用于对在长度方向具有不同厚度的钢带进行退火的方法
EP2025771A1 (en) * 2007-08-15 2009-02-18 Corus Staal BV Method for producing a coated steel strip for producing taylored blanks suitable for thermomechanical shaping, strip thus produced, and use of such a coated strip
DE102007048504B4 (de) * 2007-10-10 2013-11-07 Voestalpine Stahl Gmbh Korrosionsschutzbeschichtung für Stahlbleche und Verfahren zum Konditionieren einer Korrosionsschutzbeschichtung
KR100902857B1 (ko) * 2008-10-16 2009-06-16 현대하이스코 주식회사 형상이 복잡한 성형품 제조를 위한 초고강도 강철성형체 제조방법
KR100987901B1 (ko) * 2010-02-22 2010-10-13 현대하이스코 주식회사 초고강도 강관을 이용한 향상된 성능의 범퍼 하부 보강재 및 그 제조방법
EP2374910A1 (de) 2010-04-01 2011-10-12 ThyssenKrupp Steel Europe AG Stahl, Stahlflachprodukt, Stahlbauteil und Verfahren zur Herstellung eines Stahlbauteils
MX2013002063A (es) * 2010-08-31 2013-04-05 Tata Steel Ijmuiden Bv Metodo para conformar en caliente una parte de metal revestida y parte conformada.
CN103620075B (zh) * 2011-06-10 2016-02-17 株式会社神户制钢所 热压成形品、其制造方法和热压成形用薄钢板
JP5704721B2 (ja) * 2011-08-10 2015-04-22 株式会社神戸製鋼所 シーム溶接性に優れた高強度鋼板
ES2586555T3 (es) * 2011-09-01 2016-10-17 Kabushiki Kaisha Kobe Seiko Sho Pieza moldeada estampada en caliente y método de fabricación de la misma
UA109963C2 (uk) * 2011-09-06 2015-10-26 Катана сталь, яка затвердіває внаслідок виділення часток після гарячого формування і/або загартовування в інструменті, яка має високу міцність і пластичність, та спосіб її виробництва
JP5890710B2 (ja) * 2012-03-15 2016-03-22 株式会社神戸製鋼所 熱間プレス成形品およびその製造方法
JP5942560B2 (ja) * 2012-04-18 2016-06-29 マツダ株式会社 鋼板のプレス成形方法
WO2014037627A1 (fr) * 2012-09-06 2014-03-13 Arcelormittal Investigación Y Desarrollo Sl Procede de fabrication de pieces d'acier revêtues et durcies a la presse, et tôles prerevêtues permettant la fabrication de ces pieces
DE102012024626A1 (de) * 2012-12-17 2014-06-18 GM Global Technology Operations LLC (n. d. Gesetzen des Staates Delaware) Fahrzeugkarosserie und Verfahren zur Fertigung eines Formteils dafür
MX374823B (es) * 2013-03-14 2025-03-06 Nippon Steel Corp Star Placa de acero de alta firmeza con excelentes caracteristicas de resistencia a la destruccion retardada y tenacidad a temperaturas bajas y elemento de alta firmeza manufacturado que usa la misma.
DE102013009232A1 (de) * 2013-05-28 2014-12-04 Salzgitter Flachstahl Gmbh Verfahren zur Herstellung eines Bauteils durch Warmumformen eines Vorproduktes aus Stahl
ES2749209T3 (es) * 2013-06-11 2020-03-19 Nippon Steel Corp Producto estampado en caliente y proceso para la producción de un producto estampado en caliente
DE102013015032A1 (de) * 2013-09-02 2015-03-05 Salzgitter Flachstahl Gmbh Zinkbasierte Korrosionsschutzbeschichtung für Stahlbleche zur Herstellung eines Bauteils bei erhöhter Temperatur durch Presshärten
US20160289809A1 (en) * 2013-09-19 2016-10-06 Tata Steel Ijmuiden B.V. Steel for hot forming
CN105200441A (zh) * 2014-05-30 2015-12-30 宝山钢铁股份有限公司 带氧化物层的热镀产品、其制造方法及其应用
CN110439185A (zh) * 2014-10-23 2019-11-12 贝卡尔特公司 用于路面加固的结构
US20160145731A1 (en) * 2014-11-26 2016-05-26 GM Global Technology Operations LLC Controlling Liquid Metal Embrittlement In Galvanized Press-Hardened Components
US11000890B2 (en) 2014-12-25 2021-05-11 Nippon Steel Corporation Panel-shaped formed product and method for producing panel-shaped formed product
DK3250719T3 (da) * 2015-01-30 2019-11-25 Bekaert Sa Nv Ståltråd med høj trækstyrke
JP2018512503A (ja) * 2015-03-16 2018-05-17 タタ、スティール、アイモイデン、ベスローテン、フェンノートシャップＴａｔａ Ｓｔｅｅｌ Ｉｊｍｕｉｄｅｎ Ｂｖ 熱間成形鋼材
WO2016156896A1 (en) * 2015-03-31 2016-10-06 Arcelormittal Panel for vehicle comprising a coated steel sheet locally reinforced
CN105586530A (zh) * 2015-04-04 2016-05-18 王文姣 一种汽车保险杠及其制备方法
WO2016163469A1 (ja) 2015-04-08 2016-10-13 新日鐵住金株式会社 熱処理鋼板部材およびその製造方法
RU2686713C1 (ru) * 2015-04-08 2019-04-30 Ниппон Стил Энд Сумитомо Метал Корпорейшн Элемент из термообработанного стального листа и способ его производства
EP3282029B1 (en) 2015-04-08 2020-02-12 Nippon Steel Corporation Steel sheet for heat treatment
TWI607916B (zh) * 2015-09-18 2017-12-11 Nippon Steel & Sumitomo Metal Corp Panel shaped product and its manufacturing method
KR20170075046A (ko) 2015-12-22 2017-07-03 주식회사 포스코 내식성이 우수한 열간 프레스 성형품 및 그 제조방법
DE102016100648B4 (de) * 2015-12-23 2018-04-12 Benteler Automobiltechnik Gmbh Wärmebehandlungsofen sowie Verfahren zur Wärmebehandlung einer vorbeschichteten Stahlblechplatine und Verfahren zur Herstellung eines Kraftfahrzeugbauteils
DE102016102504A1 (de) * 2016-02-08 2017-08-10 Salzgitter Flachstahl Gmbh Aluminiumbasierte Beschichtung für Stahlbleche oder Stahlbänder und Verfahren zur Herstellung hierzu
KR101644798B1 (ko) 2016-02-18 2016-08-02 주식회사 아이레즈 디밍 시 발생하는 플리커의 과도한 변화를 조절하기 위한 장치
US10385415B2 (en) 2016-04-28 2019-08-20 GM Global Technology Operations LLC Zinc-coated hot formed high strength steel part with through-thickness gradient microstructure
US10619223B2 (en) 2016-04-28 2020-04-14 GM Global Technology Operations LLC Zinc-coated hot formed steel component with tailored property
WO2018096387A1 (en) 2016-11-24 2018-05-31 Arcelormittal Hot-rolled and coated steel sheet for hot-stamping, hot-stamped coated steel part and methods for manufacturing the same
KR20190115024A (ko) 2017-03-01 2019-10-10 에이케이 스틸 프로퍼티즈 인코포레이티드 극도로 높은 강도를 갖는 프레스 경화 강
SE540978C2 (en) * 2017-06-08 2019-02-12 Gestamp Hardtech Ab Process of applying a cfrp patch on a steel plate to be formed
JP7326247B2 (ja) 2017-07-25 2023-08-15 タタ、スティール、アイモイデン、ベスローテン、フェンノートシャップ 熱間成形された部品を製造するための鋼ストリップ、シート又はブランク、部品、及びブランクを部品に熱間成形する方法
CN110945148B (zh) * 2017-07-25 2023-01-24 塔塔钢铁艾默伊登有限责任公司 用于制备热成形零件的钢带材、片材或坯料，零件，和用于将坯料热成形为零件的方法
CN112513310A (zh) * 2018-05-24 2021-03-16 通用汽车环球科技运作有限责任公司 改善压制硬化钢的强度和延性的方法
KR20190138010A (ko) 2018-06-04 2019-12-12 주식회사 아이레즈 플리커 조절 컨버터
CN112534078A (zh) 2018-06-19 2021-03-19 通用汽车环球科技运作有限责任公司 具有增强的机械性质的低密度压制硬化钢
WO2020259842A1 (de) * 2019-06-27 2020-12-30 Thyssenkrupp Steel Europe Ag Verfahren zur herstellung eines beschichteten stahlflachprodukts, verfahren zur herstellung eines stahlbauteils und beschichtetes stahlflachprodukt
US11530469B2 (en) 2019-07-02 2022-12-20 GM Global Technology Operations LLC Press hardened steel with surface layered homogenous oxide after hot forming
MY210557A (en) 2020-09-01 2025-09-30 Hyundai Steel Co Material for hot stamping and method of manufacturing the same
DE102020130543A1 (de) 2020-11-19 2022-05-19 Voestalpine Stahl Gmbh Stahlmaterial und Verfahren zu seiner Herstellung
CN113388796B (zh) * 2021-08-16 2021-11-02 天津市新宇彩板有限公司 钢材表面热镀锌铝镁镀液及使用该镀液的镀覆方法
CN116288095A (zh) * 2022-09-08 2023-06-23 首钢集团有限公司 一种合金镀液、合金镀层和镀层钢板及其制备方法和应用

Family Cites Families (45)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB706681A (en) 1948-04-23 1954-04-07 Sylvania Electric Prod Improvements in or relating to the production of aluminium-iron alloy coated ferroussheet stock
JPS5924166B2 (ja) * 1977-10-20 1984-06-07 新日本製鐵株式会社 ストリツプの連続加熱に於ける板温制御方法
SU863681A1 (ru) 1979-04-09 1981-09-15 Предприятие П/Я В-2996 Способ управлени отжигом полосы в многозонной печи
JPS5891162A (ja) 1981-11-18 1983-05-31 Nisshin Steel Co Ltd 溶融亜鉛めつき鋼板の製造方法
JPS58120742A (ja) * 1982-01-11 1983-07-18 Nippon Steel Corp 鋼帯の冷却制御方法
JPS602634A (ja) 1983-06-21 1985-01-08 Sumitomo Metal Ind Ltd 鋼帯の連続加熱方法
JPS60169525A (ja) 1984-02-15 1985-09-03 Mitsubishi Heavy Ind Ltd 連続焼鈍炉冷却帯の鋼帯冷却方法
NL8800391A (nl) 1988-02-17 1989-09-18 Hoogovens Groep Bv Verouderingsbestendig laaggelegeerd warmgewalst bandvormig vervormingsstaal.
JPH02258933A (ja) 1989-03-29 1990-10-19 Sumitomo Metal Ind Ltd 連続焼鈍炉における板温制御方法
JPH06932B2 (ja) 1989-04-20 1994-01-05 川崎製鉄株式会社 冷間圧延ステンレス鋼帯の連続焼鈍方法
JP2825535B2 (ja) 1989-07-17 1998-11-18 川崎製鉄株式会社 連続焼鈍炉の炉内圧制御方法
FR2688802B1 (fr) * 1992-03-19 1994-09-30 Stein Heurtey Procede de traitement thermique de bandes metalliques.
KR960010811B1 (ko) * 1992-04-16 1996-08-09 신니뽄세이데스 가부시끼가이샤 자성이 우수한 입자배향 전기 강 시트의 제조방법
RU2073070C1 (ru) * 1992-07-22 1997-02-10 Производственное объединение "Чепецкий механический завод" Расплав для горячего цинкования
RU2037550C1 (ru) * 1993-07-29 1995-06-19 Общество с ограниченной ответственностью (акционерное общество закрытого типа) Научно-производственный центр "Гальва", Лтд. Состав сплава для нанесения защитного покрытия на основе цинка
FR2780984B1 (fr) * 1998-07-09 2001-06-22 Lorraine Laminage Tole d'acier laminee a chaud et a froid revetue et comportant une tres haute resistance apres traitement thermique
FR2787735B1 (fr) * 1998-12-24 2001-02-02 Lorraine Laminage Procede de realisation d'une piece a partir d'une bande de tole d'acier laminee et notamment laminee a chaud
CN1145709C (zh) 2000-02-29 2004-04-14 川崎制铁株式会社 应变时效硬化特性优良的高强度冷轧钢板及其制造方法
FR2807447B1 (fr) * 2000-04-07 2002-10-11 Usinor Procede de realisation d'une piece a tres hautes caracteristiques mecaniques, mise en forme par emboutissage, a partir d'une bande de tole d'acier laminee et notamment laminee a chaud et revetue
DE10055338C1 (de) * 2000-11-08 2002-03-07 Thyssenkrupp Stahl Ag Verfahren zum Herstellen eines bei niedrigen Verformungsgraden kaltverformten Kaltbandes
JP3580261B2 (ja) * 2001-03-23 2004-10-20 住友金属工業株式会社 溶融Ｚｎ−Ａｌ−Ｍｇめっき鋼板およびその製造方法
JP3600804B2 (ja) * 2001-06-27 2004-12-15 新日本製鐵株式会社 成形性に優れた溶融亜鉛めっき鋼板
JP2003105500A (ja) * 2001-09-26 2003-04-09 Nippon Metal Ind Co Ltd ステンレス鋼／銅クラッドおよびその製造方法
DE10307184B3 (de) * 2003-02-20 2004-04-08 Benteler Automobiltechnik Gmbh Verfahren zur Herstellung eines gehärteten Strukturbauteils für den Fahrzeugbau
DE10315357B4 (de) * 2003-04-03 2005-05-25 Muhr Und Bender Kg Verfahren zum Walzen und Walzanlage zum Walzen von Metallband
JP2004315883A (ja) * 2003-04-15 2004-11-11 Nisshin Steel Co Ltd ブラウン管バンド用高強度高透磁率鋼板およびその製造法
JP3885763B2 (ja) 2003-04-25 2007-02-28 住友金属工業株式会社 焼入用溶融亜鉛系めっき鋼板とその製造方法及び用途
DE502004011583D1 (de) * 2003-07-29 2010-10-07 Voestalpine Automotive Gmbh Verfahren zum herstellen von geharteten bauteilen aus stahlblech
JP2005113233A (ja) * 2003-10-09 2005-04-28 Nippon Steel Corp 熱間プレス用Ｚｎ系めっき鋼材
WO2005068676A1 (ja) 2004-01-14 2005-07-28 Nippon Steel Corporation めっき密着性および穴拡げ性に優れた溶融亜鉛めっき高強度鋼板とその製造方法
EP1621645A1 (en) * 2004-07-28 2006-02-01 Corus Staal BV Steel sheet with hot dip galvanized zinc alloy coating
JP4329639B2 (ja) * 2004-07-23 2009-09-09 住友金属工業株式会社 耐液体金属脆性に優れた熱処理用鋼板
US20060130940A1 (en) * 2004-12-20 2006-06-22 Benteler Automotive Corporation Method for making structural automotive components and the like
JP4449795B2 (ja) * 2005-03-22 2010-04-14 住友金属工業株式会社 熱間プレス用熱延鋼板およびその製造方法ならびに熱間プレス成形部材の製造方法
JP4630099B2 (ja) * 2005-03-25 2011-02-09 株式会社神戸製鋼所 リン酸塩処理性および塗装後耐食性に優れた熱処理加工用溶融Ｚｎめっき鋼板並びにその製造方法
DE102005025026B3 (de) * 2005-05-30 2006-10-19 Thyssenkrupp Steel Ag Verfahren zum Herstellen eines Metallbauteils mit aneinander angrenzenden Abschnitten unterschiedlicher Materialeigenschaften
US7543384B2 (en) * 2005-08-11 2009-06-09 Gm Global Technology Operations, Inc. Method of making a variable thickness member for a vehicle
EP1767659A1 (fr) * 2005-09-21 2007-03-28 ARCELOR France Procédé de fabrication d'une pièce en acier de microstructure multi-phasée
WO2007048883A1 (fr) * 2005-10-27 2007-05-03 Usinor Procede de fabrication d'une piece a tres hautes caracteristiques mecaniques a partir d'une tole laminee et revetue
TWI354706B (en) 2006-01-30 2011-12-21 Nippon Steel Corp Hot-dip galvanealed high-strength steel sheet and
US8904456B2 (en) 2006-02-13 2014-12-02 Tvu Networks Corporation Methods, apparatus, and systems for providing media content over a communications network
DE102007013739B3 (de) 2007-03-22 2008-09-04 Voestalpine Stahl Gmbh Verfahren zum flexiblen Walzen von beschichteten Stahlbändern
CN101755063A (zh) * 2007-07-19 2010-06-23 科鲁斯斯塔尔有限公司 用于对在长度方向具有不同厚度的钢带进行退火的方法
JP5425770B2 (ja) 2007-07-19 2014-02-26 タタ、スティール、アイモイデン、ベスローテン、フェンノートシャップ 長さ方向において厚さが変化する鋼ストリップ
EP2025771A1 (en) 2007-08-15 2009-02-18 Corus Staal BV Method for producing a coated steel strip for producing taylored blanks suitable for thermomechanical shaping, strip thus produced, and use of such a coated strip

Also Published As

Publication number Publication date
KR20090123877A (ko) 2009-12-02
US9481916B2 (en) 2016-11-01
EP2126144A1 (en) 2009-12-02
US8721809B2 (en) 2014-05-13
BRPI0807565B1 (pt) 2017-06-13
KR101504370B1 (ko) 2015-03-19
BRPI0807565A2 (pt) 2014-07-01
MX2009008557A (es) 2009-08-21
US20100026048A1 (en) 2010-02-04
ES2656070T3 (es) 2018-02-23
EP2126144B1 (en) 2017-12-27
WO2008102012A1 (en) 2008-08-28
RU2009135392A (ru) 2011-03-27
JP2010527407A (ja) 2010-08-12
RU2469102C2 (ru) 2012-12-10
US20140212687A1 (en) 2014-07-31

Similar Documents

Publication Publication Date Title
JP5586008B2 (ja) 強度が非常に高い最終製品の熱機械的成形方法およびその方法により製造された製品
JP5726419B2 (ja) 延性が改善された装置レス熱間成形または焼入れ用鋼
CA2742671C (en) High-strength cold-rolled steel sheet having excellent formability, high-strength galvanized steel sheet, and methods for manufacturing the same
RU2403291C2 (ru) Способ получения стальной детали с многофазной микроструктурой
RU2684655C1 (ru) Сверхпрочная многофазная сталь и способ производства холоднокатаной стальной полосы из нее
KR101485306B1 (ko) 공구로 열간 성형 이후 석출 및/또는 담금질을 통해 경화된 초고강도 및 연성을 갖는 압연 강 및 이를 제조하는 방법
CN101617059A (zh) 热机械形成具有很高强度的最终产品的方法及由此制备的产品
RU2732711C1 (ru) Способ изготовления деталей из стали с высокой механической прочностью и повышенной вязкостью и полученные этим способом детали
US20080286603A1 (en) Steel Sheet for Hot Press Forming Having Excellent Heat Treatment and Impact Property, Hot Press Parts Made of It and the Method for Manufacturing Thereof
JP4589880B2 (ja) 成形性と穴拡げ性に優れた高強度溶融亜鉛めっき鋼板と高強度合金化溶融亜鉛めっき鋼板及び高強度溶融亜鉛めっき鋼板の製造方法並びに高強度合金化溶融亜鉛めっき鋼板の製造方法
KR20160039304A (ko) 열간-압연 ｔｗｉｐ-강의 제조 방법 및 이에 의해 제조된 ｔｗｉｐ-강 제품
KR20200063167A (ko) 초고강도 다중 상 강 및 상기 다중 상 강으로부터 강 스트립을 제조하는 방법
RU2725939C1 (ru) Способ изготовления подвергнутой повторному формованию детали из плоского стального продукта с содержанием марганца и деталь такого типа
CN110944765B (zh) 通过热成型扁钢产品生产的金属板构件及其生产方法
CN115087751A (zh) 高可卷边的超高强度延展热轧钢，制造所述热轧钢的方法及其用途
KR20190130681A (ko) 오스테나이트계 매트릭스를 가지는 twip 강 시트를 제조하는 방법
JP4855442B2 (ja) 低降伏比型合金化溶融亜鉛メッキ高強度鋼板の製造方法
RU2734216C9 (ru) Способ изготовления плоского стального продукта из стали с содержанием марганца и такой плоский стальной продукт
JP4140962B2 (ja) 低降伏比型高強度合金化溶融亜鉛めっき鋼板の製造方法
HK1140235A (en) Method of thermomechanical shaping a final product with very high strength and a product produced thereby

Legal Events

Date Code Title Description
A521 Request for written amendment filed

Free format text: JAPANESE INTERMEDIATE CODE: A523

Effective date: 20110215

A621 Written request for application examination

Free format text: JAPANESE INTERMEDIATE CODE: A621

Effective date: 20110215

A977 Report on retrieval

Free format text: JAPANESE INTERMEDIATE CODE: A971007

Effective date: 20121207

A131 Notification of reasons for refusal

Free format text: JAPANESE INTERMEDIATE CODE: A131

Effective date: 20121211

A601 Written request for extension of time

Free format text: JAPANESE INTERMEDIATE CODE: A601

Effective date: 20130311

A602 Written permission of extension of time

Free format text: JAPANESE INTERMEDIATE CODE: A602

Effective date: 20130318

A521 Request for written amendment filed

Free format text: JAPANESE INTERMEDIATE CODE: A523

Effective date: 20130607

A131 Notification of reasons for refusal

Free format text: JAPANESE INTERMEDIATE CODE: A131

Effective date: 20140131

A521 Request for written amendment filed

Free format text: JAPANESE INTERMEDIATE CODE: A523

Effective date: 20140424

TRDD Decision of grant or rejection written
A01 Written decision to grant a patent or to grant a registration (utility model)

Free format text: JAPANESE INTERMEDIATE CODE: A01

Effective date: 20140620

A61 First payment of annual fees (during grant procedure)

Free format text: JAPANESE INTERMEDIATE CODE: A61

Effective date: 20140716

R150 Certificate of patent or registration of utility model

Ref document number: 5586008

Country of ref document: JP

Free format text: JAPANESE INTERMEDIATE CODE: R150

R250 Receipt of annual fees

Free format text: JAPANESE INTERMEDIATE CODE: R250

R250 Receipt of annual fees

Free format text: JAPANESE INTERMEDIATE CODE: R250

R250 Receipt of annual fees

Free format text: JAPANESE INTERMEDIATE CODE: R250

LAPS Cancellation because of no payment of annual fees