JP5568493B2 - 防振ゴム組成物 - Google Patents
防振ゴム組成物 Download PDFInfo
- Publication number
- JP5568493B2 JP5568493B2 JP2011032402A JP2011032402A JP5568493B2 JP 5568493 B2 JP5568493 B2 JP 5568493B2 JP 2011032402 A JP2011032402 A JP 2011032402A JP 2011032402 A JP2011032402 A JP 2011032402A JP 5568493 B2 JP5568493 B2 JP 5568493B2
- Authority
- JP
- Japan
- Prior art keywords
- component
- rubber composition
- vibration
- parts
- zinc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(A)ジエン系ゴム。
(B)カーボンブラック。
(C)モノメタクリル酸亜鉛を必須成分とする(メタ)アクリル酸モノマー。
(D)下記の(d1)および(d2)の少なくとも一つの吸着フィラー。
(d1)その組成に、ケイ素,アルミニウム,ナトリウム,カルシウムの四元素を全て含むゼオライト。
(d2)ハイドロタルサイト。
天然ゴム
酸化亜鉛2種、堺化学工業社製
ルーナックS30、花王社製
オゾノン6C、精工化学社製
サンノック、大内新興化学社製
ナフテン系オイル(出光興産社製、ダイアナプロセスNM−280)
FEF級カーボンブラック(東海カーボン社製、シーストSO)
合成ゼオライト(ミズカシーブス5AP、水澤化学工業社製)
ハイドロタルサイト(DHT4A、協和化学工業社製)
酸化マグネシウム(協和マグ#150、協和化学工業社製)
合成ゼオライト(ミズカライザーDS、水澤化学工業社製)
合成ゼオライト(ミズカシーブス EX122、水澤化学工業社製)
合成ゼオライト(シルトンCPT−30、水澤化学工業社製)
合成ゼオライト(ミズカライフP−1、水澤化学工業社製)
合成ゼオライト(ミズカライフF−2G、水澤化学工業社製)
合成ゼオライト(STABINEX CSH、水澤化学工業社製)
N−シクロヘキシル−2−ベンゾチアゾリルスルフェンアミド(CBS)(ノクセラーCZ、大内新興化学社製)
テトラメチルチウラムジスルフィド(TMTD)(サンセラーTT、三新化学工業社製)
硫黄、軽井沢精錬所社製
モノメタクリル酸亜鉛(PRO11542、サートマー社製)
2−tert−ブチル−6−(3−tert−ブチル−2−ヒドロキシ−5−メチルベンジル)−4−メチルフェニルアクリレート(スミカライザーGM、住友化学社製)
ノニルフェノールEO変性アクリレート(アロニックスM111、東亞合成化学社製)
NR100部と、酸化亜鉛5部と、ステアリン酸1部と、老化防止剤2部と、ワックス2部と、鉱物油5部と、カーボンブラック30部と、吸着フィラー(i)2部と、(メタ)アクリル酸モノマー (i)3部とを配合し、これらを、バンバリーミキサーによって、140℃で5分間混練した。つぎに、これに、加硫剤1部と、加硫促進剤(i)2部と、加硫促進剤(ii)1部とを配合し、オープンロールを用いて、60℃で5分間混練することにより、防振ゴム組成物を調製した。
後記の表2〜表4に示すように、各成分の配合量等を変更する以外は、実施例1に準じて、防振ゴム組成物を調製した。
各防振ゴム組成物を、160℃×20分の条件でプレス成形(加硫)し、テストピースを作製した。そして、JIS K6251に準じて、その常態物性(TS,EB,Hs)を測定した。
TS:破断点強度(MPa)
EB:破断点伸び(%)
Hs:硬度(JIS A)
上記作製のテストピースを、100℃の高温雰囲気下にて70時間放置した(熱老化試験)後、上記と同様にして、破断点伸び(EB)を測定した。そして、初期物性に対する、熱老化試験後の破断点伸びの低下率(ΔEB)を算出し、耐熱性評価において、その値が10%以下であるものを「○」と表記し、満たさないものを「×」と表記した。
各防振ゴム組成物の未加硫ゴムシート(厚み12.5mm)を、直径28mmの円筒状に打抜き、サンプルを作製し、そのサンプルを、150℃のオーブン内で20分間加熱(プレスをかけないで加硫)した。そして、上記サンプルの外観や、上記サンプルを切断した際の断面の発泡状態を目視評価した。すなわち、上記サンプルに発泡痕が顕著に確認されたものを×、若干の発泡痕は確認されたが、実使用に支障のない程度であったものを△、発泡痕が確認されなかったものを○と評価した。
上記作製のテストピースの動ばね定数(Kd100)および静ばね定数(Ks)を、それぞれJIS K 6394に準じて測定した。その値をもとに、動倍率(Kd100/Ks)を算出した。
Claims (4)
- 下記の(A)成分とともに、下記の(B)、(C)および(D)成分を含有する防振ゴム組成物であって、上記(D)成分の配合量が、上記(A)成分100重量部に対して2〜15重量部であることを特徴とする防振ゴム組成物。
(A)ジエン系ゴム。
(B)カーボンブラック。
(C)モノメタクリル酸亜鉛を必須成分とする(メタ)アクリル酸モノマー。
(D)下記の(d1)および(d2)の少なくとも一つの吸着フィラー。
(d1)その組成に、ケイ素,アルミニウム,ナトリウム,カルシウムの四元素を全て含むゼオライト。
(d2)ハイドロタルサイト。 - 上記(C)成分の配合量が、上記(A)成分100重量部に対して0.5〜10重量部である請求項1記載の防振ゴム組成物。
- 上記(C)成分の(メタ)アクリル酸モノマー全体の50重量%以上がモノメタクリル酸亜鉛であり、50重量%以下が、2−tert−ブチル−6−(3−tert−ブチル−2−ヒドロキシ−5−メチルベンジル)−4−メチルフェニルアクリレート,ステアリルメタクリレート,トリデシルメタクリレート,ポリプロピレングリコールモノメタクリレート,フェノールEO変性アクリレート,ノニルフェノールEO変性アクリレート,N−アクリロイルオキシエチルヘキサヒドロフタルイミド,イソボニルメタクリレート,テトラヒドロフルフリルアクリレート,2−フェノキシエチルメタクリレート,エトキシ化(2)ヒドロキシエチルメタクリレート,イソデシルメタクリレート,モノアクリル酸亜鉛,ジメタクリル酸亜鉛およびジアクリル酸亜鉛からなる群から選ばれた少なくとも一つである、請求項1または2記載の防振ゴム組成物。
- 請求項1〜3のいずれか一項に記載の防振ゴム組成物の加硫体。