JP5411253B2 - 改良された表面特性を有するプラスチック表面 - Google Patents
改良された表面特性を有するプラスチック表面 Download PDFInfo
- Publication number
- JP5411253B2 JP5411253B2 JP2011507539A JP2011507539A JP5411253B2 JP 5411253 B2 JP5411253 B2 JP 5411253B2 JP 2011507539 A JP2011507539 A JP 2011507539A JP 2011507539 A JP2011507539 A JP 2011507539A JP 5411253 B2 JP5411253 B2 JP 5411253B2
- Authority
- JP
- Japan
- Prior art keywords
- viscosity
- polymer
- solubility parameter
- carrier polymer
- copolymers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
第1のFedorの溶解度パラメータと第1の粘度とを有する第1の溶融加工可能な熱可塑性ポリマーを含む主要部分のベースポリマー;および
キャリヤーポリマーと表面改質添加剤との組合せ
を含み、キャリヤーポリマーは、第1の溶解度パラメータより少なくとも約2.5(J/cm^3)^1/2低い第2の溶解度パラメータと第2の粘度とを有する第2の溶融加工可能な熱可塑性ポリマーを含み、キャリヤーポリマーは表面改質添加剤に付着しており、第1の粘度は、第2の粘度の少なくとも約25倍、より典型的には第2の粘度の少なくとも約30から約50倍、さらにより典型的には第2の粘度の少なくとも約100倍である組成物を提供する。「付着された(adhered)」とは、キャリヤーポリマーと表面改質添加剤が互いに緊密に混合または分散されていること、あるいは表面改質添加剤がキャリヤーポリマーで被覆されていることを意味する。
キャリヤーポリマーと表面改質添加剤との組合せを生成するステップであって、キャリヤーポリマーは、第1の溶解度パラメータより少なくとも約2.5(J/cm^3)^1/2低い第2の溶解度パラメータと第2の粘度とを有する第2の溶融加工可能な熱可塑性ポリマーを含み、キャリヤーポリマーは表面改質添加剤に付着しているステップと、
第1のFedorの溶解度パラメータと第1の粘度とを有する第1の溶融加工可能な熱可塑性ポリマーを含む主要部分のベースポリマー、および前ステップで生成されたキャリヤーポリマーと表面改質添加剤との組合せを加工して、改良された表面特性を有する部品を形成するステップであって、第1の粘度は、第2の粘度の少なくとも約25倍、より典型的には第2の粘度の少なくとも約30から約50倍、さらにより典型的には第2の粘度の少なくとも約100倍であるステップと、
を含む方法を含む。
第1のFedorの溶解度パラメータと第1の粘度とを有する第1の溶融加工可能な熱可塑性ポリマーを含むベースポリマー。
必要、所望、または慣例に応じて改良された表面特性を有する本開示の部品を調製するのに使用される溶融加工可能な熱可塑性組成物には、広範囲の種々の添加剤が存在してもよい。このような添加剤としては、フルオロポリマー、フルオロエラストマーなどのポリマー加工助剤、触媒、開始剤、酸化防止剤(例えば、ブチル化ヒドロキシトルエンなどのヒンダードフェノール)、熱安定化剤、発泡剤、紫外線安定化剤(例えば、ヒンダードアミン系光安定化剤または「HALS」)、着色顔料を含めて有機顔料、可塑剤、ブロッキング防止剤(例えば、クレー、タルク、炭酸カルシウム、シリカ、シリコーン油など)、レベリング剤、難燃剤、へこみ防止剤、帯電防止剤、スリップ剤などが挙げられる。
キャリヤーポリマーは、ベースポリマーと完全に相溶性があるというわけではない第2の溶融加工可能な熱可塑性ポリマーである。「完全に相溶性があるというわけではない」とは、Fedorの溶解度パラメータの差が少なくとも約2.5(J/cm3)1/2より大きいことを意味する。
表面改質添加剤は、固体でも、液体でもよい。表面改質剤は、シリケート;金属酸化物;炭酸カルシウム;硫酸バリウム;鉄、チタン、銅などの金属元素粉末;およびヒュームドシリカなどのシリカ、ならびにそれらの混合物からなる群から選択される固体でもよい。酸化物の代表例としては、チタン、マグネシウム、カルシウム、バリウム、ストロンチウム、亜鉛、スズ、ニッケル、ケイ素、および鉄の酸化物、ならびにヒュームドシリカが挙げられる。他の金属酸化物としては、セレン、タングステン、ルテニウム、スズ、タンタル、銀、イリジウム、モリブデン、ニオブ、インジウム、カドミウム、ハフニウム、ジルコニウム、マンガン、銅(I)、バナジウム、クロム(VI)、イットリウム、ゲルマニウムの酸化物、およびアルミノシリケートやTixZr1-xO2(式中、xは0から1の間である)などの混合酸化物が挙げられる。
Si(R1)(R2)(R3)(R4)(I)
が挙げられ、式中、少なくとも1つのRは、1〜20個の炭素原子、典型的には4〜20個の炭素原子、最も典型的には6〜20個の炭素原子を有する、アルキル、シクロアルキル、アリール、またはアラルキルなど非加水分解性有機基であり、少なくとも1つのRは、アルコキシ、ハロゲン、アセトキシ、またはヒドロキシなどの加水分解性基である。他の2つのRは独立に、上記のように加水分解性または非加水分解性である。Rの少なくとも2つ、特に3つが加水分解性であることが典型的である。非加水分解性のRは、完全フッ素置換されていても、部分フッ素置換されていてもよい。上記のように記述されるシランは、非加水分解性のR基に関連して「オルガノシラン」と本明細書では呼ばれる。オルガノシランは、直鎖状でも分枝状でもよく、置換でも非置換でもよく、また飽和でも不飽和でもよい。典型的には、非加水分解性R基は非反応性である。アルキル、シクロアルキル、アリール、およびアラルキルは、これらの基のいずれも、完全フッ素置換または部分フッ素置換されている可能性を含めて、典型的な非加水分解性Rであり、アルキルが最も典型的である。加水分解性のRが同一であるとき、オルガノシランは、
R5 xSiR6 4-x(II)
で表わすことができ、式中、R5は非加水分解性であり、R6は上記に定義したように加水分解性であり、x=1〜3である。典型的には、R6としては、メトキシ、エトキシ、クロロ、およびヒドロキシが挙げられる。容易な取扱いには、エトキシが特に典型的である。いくつかの典型的なオルガノシランとしては、オクチルトリエトキシシラン、ノニルトリエトキシシラン、デシルトリエトキシシラン、ドデシルトリエトキシシラン、トリデシルトリエトキシシラン、テトラデシルトリエトキシシラン、ペンタデシルトリエトキシシラン、ヘキサデシルトリエトキシシラン、ヘプタデシルトリエトキシシラン、およびオクタデシルトリエトキシシランが挙げられる。オルガノシランの混合物を使用することができる。
ベースポリマー、キャリヤーポリマーと表面改質添加剤との組合せを任意の添加剤と共に、フィルム、容器、ビン、チューブ、シート/プレート/プロファイル、工業用またはコンシューマ用部品などの好適な任意の成形品に形成することができる。特に好適な物品は、窓枠、外装用サイディングを限定せずに含めて、外装用建築建物部品、コンシューマ製品(例えば、パーソナルケア製品または住宅用洗浄製品)または工業用製品(例えば、工業用洗浄製品)を含めて、製品の容器など、塵埃および煤に曝露される可能性があるものである。キャリヤーポリマーと表面改質添加剤との組合せは、マスターバッチプロセスで作製することができる。マスターバッチは、顔料および/または添加剤の濃縮混合物であり、熱プロセス中、キャリヤーポリマーにカプセル化され、次いで冷却され、顆粒形状に裁断される。マスターバッチプロセスは、このような顔料および/または添加剤のポリマーへの組込みまたは分散であり、二軸押出機または他のポリマー加工装置を使用して実施することができる。最良の分散が得られるような軸設計の選択およびマスターバッチの調製方式に関する他の詳細は、「Plastics Additives and Compounding」、2007年3月/4月号、36頁、「Masterbatch production on co−rotating twin screw extruders」で見ることができる。あるいは、キャリヤーポリマーと表面改質添加剤との組合せは、物理的ブレンドでも、被覆ポリマーでもよく、ここで、コーティングは固体でも、液体でもよい。
キャリヤーポリマーと表面改質添加剤との組合せを生成するステップであって、キャリヤーポリマーは、第1の溶解度パラメータより少なくとも約2.5(J/cm^3)^1/2低い第2の溶解度パラメータと第2の粘度とを有する第2の溶融加工可能な熱可塑性ポリマーを含み、キャリヤーポリマーは表面改質添加剤に付着しているステップと、
第1のFedorの溶解度パラメータと第1の粘度とを有する第1の溶融加工可能な熱可塑性ポリマーを含む主要部分のベースポリマー、および前ステップで生成されたキャリヤーポリマーと表面改質添加剤との組合せを加工して、改良された表面特性を有する部品を形成するステップであって、第1の粘度は、第2の粘度の少なくとも約25倍、より典型的には第2の粘度の少なくとも約30から約50倍、さらにより典型的には第2の粘度の少なくとも約100倍であるステップと、
を含む。加工は、押出成形または射出成形を含んでもよい。
洗浄性:
押出成形した試料を、ダートピックアップ防止性(DPR)について試験した。部品の押出成形した試料を1.5インチ×2インチのサイズに切断し、4インチ×6インチの金属パネルに載せた。次いで、試料を載せたパネルを、木煉瓦中の45度の角度のスロット切断部に挿入した。ダストを入れるのに役立つように、パネルを3ガロンのバケツの底に置いた。ダスト組成物は下記で構成された。
19.35% 12g シリカゲル
19.35% 12g 酸化アルミニウム
9.68% 6g 酸化鉄−(ブラック)
1.61% 1g ランプブラック粉末
50.00% 31g 現地の乾燥土壌(乳鉢と乳棒で微粉砕)
シンチレーションバイアルキャップの先端部に直径1/2インチの孔をあけることによって、アプリケーターを構築した。45メッシュスクリーンを2枚切断し、バイアルキャップの内側に挿入した。ドラフトフード中、粉砕したダスト混合物でバイアルを約1/3充填した。塩またはコショウ入れを振盪するように、バイアルを試料上で振盪することによって、ダストを試料に加えた。
UV光、高温、および模擬雨を組み込んだASTM G155−1試験手順を使用する24時間曝露を行うため、試料をWeather−Ometer(Atlas Ci 5000、Xenon Weather−Ometer, Chicago, Illinois)に置いた。
DPR=10×(1−(L* si−L* ss)/(L* ci−L* cs))
式中、
L* ssは、本開示の汚染した処理試料のL*示度である。
L* siは、汚染する前の処理試料のL*示度である。
L* csは、汚染した無処理試料(対照)のL*示度である。
L* ciは、汚染する前の無処理試料(対照)のL*示度である。
PVCは、ポリ塩化ビニルである−押出成形用グレード、Polyone Corporation, Cleveland, OH。
Elvaloy(登録商標)741は、DuPont Company, Wilmington, DEからのエチレン酢酸ビニル一酸化炭素ターポリマーである。
Elvax(登録商標)3180は、DuPont Company, Wilmington, DEからのエチレン酢酸ビニルコポリマーである。
Elvaloy(登録商標)15024 ACは、DuPont Company, Wilmington, DEからのエチレンメチルアクリレートコポリマーである。
TFE/VF/PFBEは、DuPont Company, Wilmington, DEの実験室で作製されたテトラフルオロエチレン(57重量%)フッ化ビニル(35重量%)パーフルオロブチルエチレン(8重量%)ターポリマーの試料である。
Zonyl(登録商標)FS−610は、DuPont Company, Wilmington, DEからのフルオロホスフェート添加剤である。
Teflon(登録商標)マイクロパウダーMP−1100、MP−1200、およびMP−1300は、DuPont Company, Wilmington, DEによって販売されている。
R−350およびR−105は、DuPont Company, Wilmington, DEからのTiO2顔料である。
酸化亜鉛は、Umicore Marketing Services, Raleigh, NCによって輸入された無機粉末である。
ABSは、Dow Chemical Corporation, Midland, MIからのアクリルブタジエンスチレン− Magnum(登録商標)700である。
ASAは、BASF Croporation, Florham Park, NJからのアクリルスチレンアクリル−Luran(登録商標)S757である。
Aeroxide(登録商標)LE1は、Degussa Evonik Corporation, Parsippany, NJからのナノ二酸化ケイ素である。
ポリプロピレン7825は、Total Corporation, Deer Park, TXからのものである。
PDMSは、Dow Corning, Midland, MIからのポリジメチルシロキサン200である。
添加剤とキャリヤーポリマーとの組合せ、およびその調製方法を、下記の表1に示す。
円錐型スクリューを2本備えた小実験室スケールの同方向回転Haake Rheomex TW−100二軸押出機(Haake Buchler Instruments Inc , Saddle brook, NJ)を、CW Brabender,(Hackensack, NJ)で作製された駆動装置に取り付けて、表2に概説する条件下で使用して、表2で特定されるベースポリマーならびに試料1〜2および4〜8および10を押出成形した。10.5オンスのNissei FN 4000射出成形機を用いて、成形温度225℃および表2に概説する条件下で、表2で特定されるベースポリマーならびに試料3、9、および11〜14を部品(直径4インチ×厚さ0.125インチのディスク)に射出成形した。
ベースポリマーであるポリ塩化ビニル、および試料15〜18を、上記の実施例に記載されるように押出成形する。
なお、本発明は、特許請求の範囲を含め、以下の発明を包含する。
1.溶融加工可能な熱可塑性組成物であって、
第1のFedorの溶解度パラメータと第1の粘度とを有する第1の溶融加工可能な熱可塑性ポリマーを含む主要部分のベースポリマー;および
キャリヤーポリマーと表面改質添加剤との組合せ
を含み、キャリヤーポリマーは、第1の溶解度パラメータより少なくとも約2.5(J/cm^3)^1/2低い第2の溶解度パラメータと第2の粘度とを有する第2の溶融加工可能な熱可塑性ポリマーを含み、キャリヤーポリマーは表面改質添加剤に付着しており、第1の粘度は、第2の粘度の少なくとも約25倍である組成物。
2.第1の粘度が、第2の粘度の少なくとも約30から約50倍である、1に記載の組成物。
3.第1の粘度が、第2の粘度の少なくとも約100倍である、1に記載の組成物。
4.キャリヤーポリマーと表面改質添加剤との組合せが、マスターバッチプロセスで作製される、1に記載の組成物。
5.キャリヤーポリマーと表面改質添加剤との組合せが、被覆ポリマーである、1に記載の組成物。
6.被覆ポリマーが、ポリマーおよび液体コーティングを含む、1に記載の組成物。
7.被覆ポリマーが、ポリマーおよび固体コーティングを含む、1に記載の組成物。
8.キャリヤーポリマーと表面改質添加剤との組合せが、物理的ブレンドである、1に記載の組成物。
9.表面改質添加剤が、ナノサイズまたは顔料サイズの無機粒子で処理された、直径約15マイクロメートルまでのサイズの粒子である、1に記載の組成物。
10.ベースポリマーが、0.01から200g/10分のメルトインデックス値を有する、1に記載の組成物。
11.ベースポリマーが、オレフィン;エチレンと4から10個の炭素原子を含む高級オレフィンとのコポリマー;エチレンと酢酸ビニルとのコポリマー;ビニル;ポリビニルエステル;ポリスチレン;ポリスチレンを含むアクリルホモポリマー、コポリマー、およびターポリマー、アクリロニトリルブタジエンスチレンターポリマー(ABS);アクリル/スチレン/アクリルポリマー;ポリアミド;フェノール;エラストマー添加剤を含有するポリオレフィン;アルキド;アミノ樹脂;エポキシ樹脂;ポリアミド;ポリウレタン;フェノキシ樹脂;ポリスルホン;ポリカーボネート;ポリスルホン;ポリエステル;塩素化ポリエステル;ポリエーテル;アセタール樹脂;ポリイミド;ポリオキシエチレン、およびそれらの混合物からなる群から選択される、1に記載の組成物。
12.ベースポリマーが、ポリメチルメタクリレート(PMMA)、ポリオレフィン、ポリ塩化ビニル、ポリアミド、アクリロニトリルブタジエンスチレンターポリマー(ABS)、アクリル/スチレン/アクリルポリマー、ポリイミド、ポリエステル、エラストマー添加剤を含有するポリオレフィン、およびそれらの混合物からなる群から選択される、11に記載の組成物。
13.ベースポリマーがポリ塩化ビニルである、11に記載の組成物。
14.ベースポリマーが、溶融加工可能な熱可塑性組成物の全重量を基準にして約80から約99.95重量%の量で存在する、1に記載の組成物。
15.キャリヤーポリマーが、第2の溶融加工可能な熱可塑性ポリマーを含む、1に記載の組成物。
16.第2の溶融加工可能な熱可塑性ポリマーが、第1の溶解度パラメータより少なくとも約3(J/cm3)1/2低い第2の溶解度パラメータを有する、15に記載の組成物。
17.キャリヤーポリマーが、エチレン−酢酸ビニルコポリマー;アクリレートコポリマー;ポリエチレン;ポリプロピレンおよびそのコポリマー;ならびにテトラフルオロエチレンのホモポリマーおよびコポリマーからなる群から選択される、1に記載の組成物。
18.キャリヤーポリマーが、組合せの全重量を基準にして約0.05から約20重量%の量で存在する、1に記載の組成物。
19.表面改質添加剤が固体である、1に記載の組成物。
20.表面改質添加剤が液体である、1に記載の組成物。
21.固体が、シリケート;金属酸化物;炭酸カルシウム;硫酸バリウム;金属元素粉末;シリカ、およびそれらの混合物からなる群から選択される、19に記載の組成物。
22.金属酸化物が、チタン、マグネシウム、カルシウム、バリウム、ストロンチウム、亜鉛、スズ、ニッケル、ケイ素、および鉄の酸化物、セレン、タングステン、ルテニウム、スズ、タンタル、銀、イリジウム、モリブデン、ニオブ、インジウム、カドミウム、ハフニウム、ジルコニウム、マンガン、銅(I)、バナジウム、クロム(VI)、イットリウム、およびゲルマニウムの酸化物、ヒュームドシリカ、ならびにアルミノシリケートおよびTixZr1-xO2(式中、xは0から1の間である)を含む混合酸化物からなる群から選択される、21に記載の組成物。
23.表面改質添加剤が、顔料サイズまたはナノサイズの粒子である、1に記載の組成物。
24.表面改質添加剤が、ナノサイズ粒子で処理された顔料粒子である、1に記載の組成物。
25.表面改質添加剤が、オルガノシラン;オルガノシロキサン;フルオロシラン;オルガノホスホネート;オルガノリン酸;オルガノスルホン酸化合物;炭化水素系カルボン酸ならびに関連する誘導体およびポリマー;炭化水素系アミド;低分子量炭化水素ワックス;低分子量ポリオレフィンおよびそのコポリマー;炭化水素系ポリオールおよびその誘導体;アルカノールアミンおよびその誘導体;およびよく利用される有機分散剤;ならびにそれらの混合物からなる群から選択される有機表面処理剤で処理される、1に記載の組成物。
26.表面改質添加剤が、炭酸塩、硫酸塩、チタン酸塩、ヒ化物、硫化物、セレン化物、リン化物、およびそれらの2つ以上の組合せからなる群から選択される、1に記載の組成物。
27.表面改質添加剤が、無機顔料、有機有色顔料、およびそれらの混合物からなる群から選択される、1に記載の組成物。
28.表面改質添加剤が殺生物剤である、1に記載の組成物。
29.表面改質添加剤が、フルオロケミカル、レシチン、およびそれらの混合物からなる群から選択される、1に記載の組成物。
30.フルオロケミカルが、パーフルオロアルキルエステル、フッ素化ウレタン、フッ素化アクリルまたはメタクリルコポリマー、フッ素化アニオン性界面活性剤、フッ素化スルホンアミド、およびフッ素化ジオールからなる群から選択される、1に記載の組成物。
31.表面改質添加剤が、カーボンブラックまたはカリウムアイオノマーである、1に記載の組成物。
32.表面改質添加剤が、組合せの全重量を基準にして約0.05から約20重量%の量で存在してもよい、1に記載の組成物。
33.第1の表面と第2の表面とを有する部品であって、部品は、第1のFedorの溶解度パラメータと第1の粘度とを有する第1の溶融加工可能な熱可塑性ポリマーを含む主要部分のベースポリマーを含み、第1の表面および第2の表面は、キャリヤーポリマーと表面改質添加剤との組合せを含み、キャリヤーポリマーは、第1の溶解度パラメータより少なくとも約2.5(J/cm^3)^1/2低い第2の溶解度パラメータと第2の粘度とを有する第2の溶融加工可能な熱可塑性ポリマーを含み、キャリヤーポリマーは表面改質添加剤に付着しており、第1の粘度は、第2の粘度の少なくとも約25倍である部品。
34.部品が基板である、33に記載の部品。
35.第1の粘度が、第2の粘度の少なくとも約30から約50倍である、33に記載の部品。
36.第2の溶融加工可能な熱可塑性ポリマーが、第1の溶解度パラメータより少なくとも約3(J/cm3)1/2低い第2の溶解度パラメータを有する、33に記載の部品。
37.改良された表面特性を有する部品を作製する方法であって、
キャリヤーポリマーと表面改質添加剤との組合せを生成するステップであって、キャリヤーポリマーは、第1の溶解度パラメータより少なくとも約2.5(J/cm^3)^1/2低い第2の溶解度パラメータと第2の粘度とを有する第2の溶融加工可能な熱可塑性ポリマーを含み、キャリヤーポリマーは表面改質添加剤に付着しているステップと、
第1のFedorの溶解度パラメータと第1の粘度とを有する第1の溶融加工可能な熱可塑性ポリマーを含む主要部分のベースポリマー、および前ステップで生成されたキャリヤーポリマーと表面改質添加剤との組合せを加工して、改良された表面特性を有する部品を形成するステップであって、第1の粘度は、第2の粘度の少なくとも約25倍、より典型的には第2の粘度の少なくとも約30から約50倍、さらにより典型的には第2の粘度の少なくとも約100倍であるステップと、
を含む方法。
38.加工が押出成形を含む、37に記載の部品を作製する方法。
39.加工が射出成形を含む、37に記載の部品を作製する方法。
Claims (3)
- 溶融加工可能な熱可塑性組成物であって、
第1のFedorの溶解度パラメータと第1の粘度とを有する第1の溶融加工可能な熱可塑性ポリマーを含む主要部分のベースポリマー;および
キャリヤーポリマーと固体状表面改質添加剤との組合せ
を含み、キャリヤーポリマーは、第1の溶解度パラメータより少なくとも2.5(J/cm^3)^1/2低い第2の溶解度パラメータと第2の粘度とを有する第2の溶融加工可能な熱可塑性ポリマーを含み、キャリヤーポリマーは固体状表面改質添加剤に付着しており、第1の粘度は、第2の粘度の少なくとも25倍であり、前記粘度は、円錐平板粘度計を用いて、190℃、6,283ラジアン/秒および500秒で測定し、ベースポリマーはポリ塩化ビニル(PVC)であり、
前記キャリヤーポリマーが、エチレン−酢酸ビニルコポリマー;アクリレートコポリマー;ポリエチレン;ポリプロピレンおよびそのコポリマー;ならびにテトラフルオロエチレンのホモポリマーおよびコポリマーからなる群から選択される組成物。 - 第1の表面と第2の表面とを有する部品であって、部品は、第1のFedorの溶解度パラメータと第1の粘度とを有する第1の溶融加工可能な熱可塑性ポリマーを含む主要部分のベースポリマーを含み、第1の表面および第2の表面は、キャリヤーポリマーと固体状表面改質添加剤との組合せを含み、キャリヤーポリマーは、第1の溶解度パラメータより少なくとも2.5(J/cm^3)^1/2低い第2の溶解度パラメータと第2の粘度とを有する第2の溶融加工可能な熱可塑性ポリマーを含み、キャリヤーポリマーは固体状表面改質添加剤に付着しており、第1の粘度は、第2の粘度の少なくとも25倍であり、前記粘度は、円錐平板粘度計を用いて、190℃、6,283ラジアン/秒および500秒で測定し、ベースポリマーはポリ塩化ビニル(PVC)であり、前記キャリヤーポリマーが、エチレン−酢酸ビニルコポリマー;アクリレートコポリマー;ポリエチレン;ポリプロピレンおよびそのコポリマー;ならびにテトラフルオロエチレンのホモポリマーおよびコポリマーからなる群から選択される部品。
- 改良された表面特性を有する部品を作製する方法であって、
キャリヤーポリマーと固体状表面改質添加剤との組合せを生成するステップであって、キャリヤーポリマーは、第1の溶解度パラメータより少なくとも2.5(J/cm^3)^1/2低い第2の溶解度パラメータと第2の粘度とを有する第2の溶融加工可能な熱可塑性ポリマーを含み、キャリヤーポリマーは固体状表面改質添加剤に付着しているステップと、
第1のFedorの溶解度パラメータと第1の粘度とを有する第1の溶融加工可能な熱可塑性ポリマーを含む主要部分のベースポリマー、および前ステップで生成されたキャリヤーポリマーと固体状表面改質添加剤との組合せを加工して、改良された表面特性を有する部品を形成するステップであって、第1の粘度は、第2の粘度の少なくとも25倍であるステップと、を含み、前記粘度は、円錐平板粘度計を用いて、190℃、6,283ラジアン/秒および500秒で測定し、ベースポリマーはポリ塩化ビニル(PVC)であり、前記キャリヤーポリマーが、エチレン−酢酸ビニルコポリマー;アクリレートコポリマー;ポリエチレン;ポリプロピレンおよびそのコポリマー;ならびにテトラフルオロエチレンのホモポリマーおよびコポリマーからなる群から選択される方法。