JP4804341B2 - 固体状再生標準ビスコース繊維 - Google Patents
固体状再生標準ビスコース繊維 Download PDFInfo
- Publication number
- JP4804341B2 JP4804341B2 JP2006503941A JP2006503941A JP4804341B2 JP 4804341 B2 JP4804341 B2 JP 4804341B2 JP 2006503941 A JP2006503941 A JP 2006503941A JP 2006503941 A JP2006503941 A JP 2006503941A JP 4804341 B2 JP4804341 B2 JP 4804341B2
- Authority
- JP
- Japan
- Prior art keywords
- fiber
- viscose
- cross
- regenerated
- spinning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
1.セルロース系繊維にモノマーをグラフトさせることによる化学的改質
2.セルロース系繊維マトリックス中に,カルボキチメチルセルロース,キトサン,カルバミン酸セルロース,アルギン酸塩,ガラナ(guaran)のような吸湿性ポリマーを混合することによる化学的改質
3.例えばUS−A4,129,679に開示されているように,繊維を空洞繊維や中空扁平繊維とするような物理的改質
4.例えばEP−A10301874に開示されているように,少なくとも3つのリム(limb)を備える縦横比(アスペクト比)2:1〜10:1の複数リムを有する(multilimbed)押出し口を備える紡糸口金を用いて製造される,複数リムを有する繊維(いわゆる”トリローバル”繊維)。
破断荷重Bc[cN]が
より小さく,濡れた状態で繊維を5%延伸させるのに必要な力Bm[cN]が
より小さいことを意味する。
・Wt計算スキームを用いてDIN53814により測定した保水値が,70〜110%,好ましくは80〜90%である。
・標準ビスコース繊維の紡糸原液を,紡糸開口を有する紡糸口金を通過させ再生漕に押し出すことにより,フィラメントを製造する
・上記の紡糸開口は,複数のリムを有する開口部,好ましくは3つのリムを備えた開口部を有する
・上記開口部のリムは,縦横比(アスペクト比)が3:1以下である。
・上記のビスコース紡糸原液は,熟成指数(ripening index)が10〜20°Hottenroth,好ましくは,12〜16°Hottenrothである。
・上記ビスコース紡糸原液は,0.1〜7重量%,好ましくは2〜6重量%のセルロースに関係するセルロース調整剤(modifier)を含む
・上記再生漕は,70〜100g/l,好ましくは75〜85g/lの硫酸と,240〜380g/l,好ましくは270〜300g/lの硫酸ナトリウムと,5〜30g/l,好ましくは7〜12g/lの硫酸亜鉛を含む。
・上記再生漕は,25〜55℃,好ましくは30〜35℃の温度である。
・上記のフィラメントを,既知の方法で延伸し,加工する。
(繊維断面の顕微鏡写真の撮影)
平行にされたステープル繊維の束は,ステンレス鋼板製で直径が1〜2mmの開口に挿入される。押し出された繊維は,鋼板表面に平行に設けられたカミソリ刃により,切断される。上記の試験片は顕微鏡下に設置され,繊維の断面の顕微鏡写真が1070倍の倍率で撮影される。
この測定は,グラフィックソフトウェアと,以下のような注文仕様のプログラムを用いてパーソナルコンピュータで行うことが可能である。
Synginaテストは,タンポン中の繊維の吸湿性を評価する。以下に掲載されたテストは,EDANAテスト方法ERT 350.0−02を簡略化したものである。
1 測定セルを示す
2 供給容器を示す
3 排水路(overflow line)を示す
4 排水口(run out)を示す
6,7,11,13 それぞれゴム製のリングを示す
8 タンポンもしくはタンポン形状のプラグを示す
9 チューブを示す
10 充填チューブを示す
12 排水口を示す
14 測定器具(mensur.)を示す
A,B バルブを示す
Syngina流体として,蒸留水もしくは脱イオン水が使用される。
8〜11%の湿度を有する2.75gのステープル繊維を秤量し,カーディング装置USTER MDTA3型に,ロータリング3とともに供給する。コンバインローラの速度は,1390rpmである。それぞれ75秒間稼働させる。約90cmの長さの得られたカードスライバー(card sliver)は,30cmの長さの帯を形成するために,三重にされる。このカードスライバーは,2つのローラの間で圧力が加えられるか,あるいは,カレンダーロール上で小型化される。カードスライバーの小型化中に,非常に高い圧力を加えると,剛体やカードボード形状といった,避けなくてはならない形状が形成されてしまう。
テスト用の薄膜としては,張力が17MPaと30MPaの間にある,真っ直ぐで無潤滑のコンドームが用いられる。上記のコンドームは,開封され,解かれた状態になっている。上記のコンドームは,開放端から20mmと160mmのところに印が付けられる。
タンポン,または上記「試料の調整」の項で調整されたプレスされたプラグは,なるべく正確に0.01g秤量される。この重量は記録される。
それぞれの試料タンポン/プラグの吸湿性は,以下のようにして計算される。
A=B−C
ここで,
A=グラム単位でのタンポン/プラグの吸湿性
B=飽和状態(湿潤状態)におけるグラム単位でのタンポン/プラグの重量
C=乾燥状態におけるグラム単位でのタンポン/プラグの重量
上記繊維の保水性は,DIN53814に記載されたテスト方法により,Wt計算方法を用いて測定される。
上記繊維の水分保持量は,ビスコース芯糸の吸湿性のためのテスト方法,すなわち,European Pharmacopoeia4 01/2002:0034に記載された吸湿剤(absorbent)により測定する。
セルロースを8.70%,アルカリを5.20%,硫黄を2.3%含み,14.2°Hottenrothの熟成指数と,58ball fall seconds(bfs,Zellcheming−Merkblatt III/5/Eにより測定される)の粘度とを有するビスコースが,76.5g/lの硫酸と,272g/lの硫酸ナトリウムと,10.4g/lの硫酸亜鉛を含み,温度が32℃の再生漕に,トリローバル紡糸口金を用いて紡糸された。上記紡糸口金は,72×33μm(縦横比:2.18)の3つのリムを有するトリローバル開口部を625個有する。紡糸前に,ポリエチレングリコール1500の5重量%水溶液が,上記ビスコースに添加された。
ポリエチレングリコールをビスコースに添加しなかったことを除いては,実施例1と同じ条件で,ビスコース繊維を紡糸した。
セルロースを8.65%,アルカリを5.16%,硫黄を2.3%含み,14°Hottenrothの熟成指数と,63bfsの粘度とを有するビスコースが,131g/lの硫酸と,367g/lの硫酸ナトリウムと,11g/lの硫酸亜鉛を含む49℃の温度の再生漕に,実施例1に示したトリローバル紡糸口金を用いて紡糸された。紡糸前に,ポリエチレングリコール1500の2.5重量%水溶液が,上記ビスコースに添加された。
セルロースを8.65%,アルカリを5.14%,硫黄を2.3%含み,13.6°Hottenrothの熟成指数と,65bfsの粘度とを有するビスコースが,85g/lの硫酸と,276g/lの硫酸ナトリウムと,11g/lの硫酸亜鉛を含む31℃の温度の再生漕に,実施例1に示したトリローバル紡糸口金を用いて紡糸された。紡糸前に,ポリエチレングリコール1500の5重量%水溶液が,上記ビスコースに添加された。
セルロースを8.67%,アルカリを5.15%,硫黄を2.3%含み,15°Hottenrothの熟成指数と,62bfsの粘度とを有するビスコースが,85g/lの硫酸と,277g/lの硫酸ナトリウムと,11g/lの硫酸亜鉛とを含む53℃の温度の再生漕にトリローバル紡糸口金を用いて紡糸された。上記紡糸口金は,正三角形のコアに45×33μm(縦横比:1.36)のリムを3つ有する開口が625個設けられている。外接円の半径は,80μmである。紡糸前に,ポリエチレングリコール1500の5重量%水溶液が,上記ビスコースに添加された。
セルロースを8.23%,アルカリを7.15%,硫黄を2.20%含み,14.5°Hottenrothの熟成指数と,52bfsの粘度とを有するビスコースが,98g/lの硫酸と,351g/lの硫酸ナトリウムと,28.2g/lの硫酸亜鉛を含む49℃の再生漕に,三角形の紡糸口金を用いて紡糸された。この紡糸口金は,s=129μmの正三角形形状の開口を625個有していた。
セルロースを8.80%,アルカリを5.20%含み,13.5°Hottenrothの熟成指数と,70bfsの粘度とを有するビスコースが,76g/lの硫酸と,266g/lの硫酸ナトリウムと,10.4g/lの硫酸亜鉛を含む30℃の温度の再生漕に,トリローバル紡糸口金を用いて紡糸された。この紡糸口金は,89×25μm(縦横比:3.56)のリムを3つ有するトリローバル開口を,625個有していた。紡糸前に,ポリエチレングリコール1500の5重量%水溶液が,上記ビスコースに添加された。
Claims (9)
- 固体状再生標準ビスコース繊維の断面積が,略三角形形状を有しており,かつ,前記断面積に内接する最大の正三角形の面積の2.50倍以下であり,
0.5dtexから6.0dtexの番手を有しており,
Syngina吸湿性は,6.0g/g繊維以上であることを特徴とする,吸湿製品用の固体状再生標準ビスコース繊維。 - ステープル繊維の形状であることを特徴とする,請求項1に記載の繊維。
- 2.5dtexから4dtexの番手を有することを特徴とする,請求項1または2に記載の繊維。
- DIN53814に記載の方法で測定した保水性が70%から110%であることを特徴とする,請求項1〜3のいずれか1項に記載の繊維。
- 請求項1〜4のいずれか1項に記載の吸湿製品用の固体状再生標準ビスコース繊維を製造する方法であって,
標準ビスコース紡糸原液を,紡糸開口を含む紡糸口金を通して再生漕に紡糸し,フィラメントを形成させ,
前記紡糸開口は,複数のリムを有する開口部を有し,
前記開口部の前記リムは,縦横比が3:1以下であり,
前記ビスコース紡糸原液は,10〜20°Hottenrothの熟成指数を有し,
前記ビスコース紡糸原液は,セルロースに対して0.1〜7重量%のセルロース調整剤を含み,
前記再生漕は,70から100g/lの硫酸と,240から380g/lの硫酸ナトリウムと,5から30g/lの硫酸亜鉛とを含み,
前記再生漕は,25から55℃の温度であり,
前記フィラメントは,既知の方法で延伸および更なる処理が施されることを特徴とする,吸湿製品用の固体状再生標準ビスコース繊維の製造方法。 - 前記ビスコース調整剤は,分子量が600〜3000のポリエチレングリコールであることを特徴とする,請求項5に記載の方法。
- 前記フィラメントは,脂肪酸エステルにより処理されることを特徴とする,請求項5または6に記載の方法。
- 前記脂肪酸エステルは,ポリオキシエチレンソルビタン脂肪酸エステルであることを特徴とする,請求項7に記載の方法。
- ステープル形状に形成された請求項1〜4のいずれか1項に記載の繊維を含む,吸湿製品。