JP4626951B2 - ポリアリーレンサルファイド樹脂組成物 - Google Patents
ポリアリーレンサルファイド樹脂組成物 Download PDFInfo
- Publication number
- JP4626951B2 JP4626951B2 JP2004231990A JP2004231990A JP4626951B2 JP 4626951 B2 JP4626951 B2 JP 4626951B2 JP 2004231990 A JP2004231990 A JP 2004231990A JP 2004231990 A JP2004231990 A JP 2004231990A JP 4626951 B2 JP4626951 B2 JP 4626951B2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- resin composition
- acid
- polyarylene sulfide
- sulfide resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
(A) 窒素元素の含有量が樹脂1kg当たり0.55gを超え、pHが4.5〜6.8であるポリアリーレンサルファイド樹脂100重量部に対して、
(B) アルコキシシラン化合物0.1〜3重量部
(C) 無機充填剤0〜400重量部
を配合してなるポリアリーレンサルファイド樹脂組成物である。
(A) PAS樹脂
以下のポリマーの調製例により、(A-1) 〜(A-3) のPAS樹脂を得た。
(A-1)
20LのオートクレーブにNMP(N−メチル−2−ピロリドン)5700gを仕込み、窒素ガスで置換後、約1時間かけて、攪拌機の回転数250rpmで撹拌しながら、100℃まで昇温した。100℃に到達後、濃度74.7重量%のNaOH水溶液1170g、硫黄源水溶液1990g(NaSH=21.8モル及びNa2S=0.50モルを含む)、及びNMP1000gを加え、約2時間かけて、徐々に200℃まで昇温し、水945g、NMP1590g、及び0.31モルの硫化水素を系外に排出した。
(A-2)
(A-1) と同様の重合を行い、粒状ポリマーを濾別後、アセトン洗いを3回、水洗を5回行い、洗浄した粒状ポリマーを得た。粒状ポリマーは、105℃で13時間乾燥した。このようにして得られた粒状ポリマーは、溶融粘度(310℃、ズリ速度1200sec-1)が210Pa・s、窒素元素の含有量が樹脂1kg当たり0.87g、pHが10.8であった。
(A-3)
20LのオートクレーブにNMP(N−メチル−2−ピロリドン)5700gを仕込み、窒素ガスで置換後、約1時間かけて、攪拌機の回転数250rpmで撹拌しながら、100℃まで昇温した。100℃に到達後、硫黄源水溶液1990g(NaSH=21.9モル及びNa2S=0.4モルを含む)、及びNMP1000gを加え、約2時間かけて、徐々に200℃まで昇温し、水729g、NMP1370g、及び0.70モルの硫化水素を系外に排出した。
(B) アルコキシシラン
(B-1)
γ−アミノプロピルトリエトキシシラン
(B-2)
γ−グリシドキシプロピルトリメトキシシラン
(C) 無機充填剤
(C-1)
ガラス繊維 13μmφチョップドストランド(日本電気ガラス製、ECS03T−717)
また、実施例および比較例での評価方法は以下の通りである。
[窒素量の分析法]
微量窒素硫黄分析計(ANTEK社製、ANTEK7000)を用いてPAS樹脂中の窒素含有量を測定した(窒素量の検量線はトリフェニルアミンのエチルベンゼン溶液を用いて作成した)。
[PAS樹脂のpHの測定法]
室温(15〜25℃)にて、サンプル5gとアセトン15ml、及び精製水30mlをフラスコに入れ、振とう機を用いて30分間振とうした後、分液ロートで濾過した。その上澄みのpHをpHメーターで測定した。
[引張強度の評価]
ISO3167に準じた試験片(幅10mm、厚み4mm)を成形し、ISO527−1,2に準じて測定した。
[バリ発生の評価]
一部に20μmの金型間隙を有するバリ測定部が外周に設けられている円盤状キャビティーの金型を用いて、シリンダー温度320℃、金型温度150℃で、キャビティーが完全に充填するのに必要な最小圧力で射出成形し、その部分に発生するバリ長さを写像投影機にて拡大して測定した。
実施例1〜5、比較例1〜4
(A) 成分100重量部に対して、表1に示す比率で(B) 成分を加え、ヘンシェルミキサーで5分間予備混合した。更に、(C) 成分を表1に示す比率で加え2分間混合し、これをシリンダー温度320℃の二軸押出機に投入し、ポリフェニレンサルファイド樹脂組成物のペレットを作った。得られたペレットについて、上述の方法にて引張強度、バリ長さの評価を行った。結果を表1に示す。
Claims (4)
- (A) 窒素元素の含有量が樹脂1kg当たり0.55gを超え、pHが4.5〜6.8であるポリアリーレンサルファイド樹脂100重量部に対して、
(B) アルコキシシラン化合物0.1〜3重量部
(C) 無機充填剤0〜400重量部
を配合してなるポリアリーレンサルファイド樹脂組成物。 - (B) 成分が、エポキシアルコキシシラン及び/又はアミノアルコキシシランである請求項1記載のポリアリーレンサルファイド樹脂組成物。
- (B) 成分が、γ−アミノプロピルトリエトキシシランである請求項1又は2記載のポリアリーレンサルファイド樹脂組成物。
- 請求項1〜3の何れか1項記載のポリアリーレンサルファイド樹脂組成物からなる成形品。