JP2019197168A - 光学積層体および表示装置 - Google Patents
光学積層体および表示装置 Download PDFInfo
- Publication number
- JP2019197168A JP2019197168A JP2018091622A JP2018091622A JP2019197168A JP 2019197168 A JP2019197168 A JP 2019197168A JP 2018091622 A JP2018091622 A JP 2018091622A JP 2018091622 A JP2018091622 A JP 2018091622A JP 2019197168 A JP2019197168 A JP 2019197168A
- Authority
- JP
- Japan
- Prior art keywords
- group
- layer
- liquid crystal
- film
- protective layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
[2] 前記第2保護層は、以下の式(1)で定義される修正靱性が2300MPa・%以上である、[1]に記載の光学積層体。
修正靱性=最大応力×最大ひずみ (1)
〔ただし、最大応力および最大ひずみはそれぞれ、応力−ひずみ曲線における破壊点での応力およびひずみを示す〕
[3] 前記第1保護層の厚みは10μm〜200μmである、[1]または[2]に記載の光学積層体。
[4] 前記第2保護層の厚みは5μm〜100μmである、[1]〜[3]のいずれかに記載の光学積層体。
[5] 前記第1接着層および/または前記第2接着層の厚みは1μm以上である、[1]〜[4]のいずれかに記載の光学積層体。
[6] [1]〜[5]のいずれかに記載の光学積層体を含む表示装置。
図1に本発明の一態様に係る光学積層体の概略断面図を示す。光学積層体10は、第1保護層11、偏光層12、第1接着層13、第1位相差層14、第2接着層15、第2位相差層16および第2保護層17がこの順に積層された構成を有し、第2保護層16の厚み(B)に対する第1保護層11の厚み(A)の比率(A/B)が3.3以下であることにより、薄膜化されているにもかかわらず折曲げ可能である。折曲げ可能であるとは、折曲げ曲率2.5Rの折曲げ試験において良好な結果が得られることをいう。本発明の好ましい実施態様に係る光学積層体では、折曲げ曲率1Rの折曲げ試験において良好な結果が得られる。折曲げ曲率2.5Rおよび1Rの折曲げ試験は、後述の実施例において説明する方法に従って行われる。
第1保護層11は、表示装置を折曲げ可能とする観点から、例えば樹脂フィルムから構成されてよく、好ましくは透明樹脂フィルムから構成されてよい。樹脂フィルムは、長尺のロール状樹脂フィルムであってよく、枚葉状樹脂フィルムであってよい。連続的に製造できる点で長尺のロール状樹脂フィルムが好ましい。樹脂フィルムを構成する樹脂としては、例えば、ポリエチレン、ポリプロピレン、ノルボルネン系ポリマー等のポリオレフィン;環状オレフィン系樹脂;ポリビニルアルコール;ポリエチレンテレフタレート;ポリメタクリル酸エステル;ポリアクリル酸エステル;トリアセチルセルロース、ジアセチルセルロースおよびセルロースアセテートプロピオネート等のセルロースエステル;ポリエチレンナフタレート;ポリカーボネート;ポリスルホン;ポリエーテルスルホン;ポリエーテルケトン;ポリフェニレンスルフィド;ポリフェニレンオキシド;ポリイミド;ポリアミド;ポリアミドイミド等のプラスチックが挙げられる。中でも環状オレフィン系樹脂、セルロースエステル基材、ポリイミド、ポリアミドおよびポリアミドイミドが好ましい。第1保護層11は、剥離されずに表示装置に組み込まれる層であることができる。
第1保護層11は、配向膜を有していてよい。配向膜は、第1保護層11上に形成される偏光層12を構成する重合性液晶を所望の方向に液晶配向させる、配向規制力を有するものである。
偏光層12は、1以上の重合性液晶化合物〔以下、重合性液晶(a)ともいう〕および二色性色素を含む層であれば特に限定されない。偏光層12が光学積層体10平面方向での偏光特性を有する場合、二色性色素と重合性液晶(a)が、光学積層体10平面に対して水平配向した状態で重合性液晶(a)を硬化すればよく、偏光層20が光学積層体10の厚み方向での偏光特性を有する場合、二色性色素と重合性液晶(a)とが、光学積層体10平面に対して垂直配向した状態で重合性液晶(a)を硬化すればよい。偏光層12は、コーティング層であることが好ましく、例えば後述する組成物(A)の硬化物であってよい。
重合性液晶(a)は、重合性基を有し、かつ液晶性を有する化合物である。重合性基は、重合反応に関与する基を意味し、光重合性基であることが好ましい。ここで、光重合性基とは、後述する光重合開始剤から発生した活性ラジカルや酸等によって重合反応に関与し得る基のことをいう。重合性基としては、ビニル基、ビニルオキシ基、1−クロロビニル基、イソプロペニル基、4−ビニルフェニル基、アクリロイルオキシ基、メタクリロイルオキシ基、オキシラニル基、オキセタニル基等が挙げられる。中でも、アクリロイルオキシ基、メタクリロイルオキシ基、ビニルオキシ基、オキシラニル基およびオキセタニル基が好ましく、アクリロイルオキシ基がより好ましい。液晶性はサーモトロピック液晶でもリオトロピック液晶でもよいが、後述する二色性色素と混合する場合には、サーモトロピック液晶が好ましい。
[式(I)中、
X1、X2およびX3は、それぞれ独立に、2価の芳香族基または2価の脂環式炭化水素基を表し、ここで、該2価の芳香族基または2価の脂環式炭化水素基に含まれる水素原子は、ハロゲン原子、炭素数1〜4のアルキル基、炭素数1〜4のフルオロアルキル基、炭素数1〜4のアルコキシ基、シアノ基またはニトロ基に置換されていてもよく、該2価の芳香族基または2価の脂環式炭化水素基を構成する炭素原子が、酸素原子または硫黄原子または窒素原子に置換されていてもよい。ただし、X1、X2およびX3のうち少なくとも1つは、置換基を有していてもよい1,4−フェニレン基または置換基を有していてもよいシクロヘキサン−1,4−ジイル基である。
Y1、Y2、W1およびW2は、互いに独立に、単結合または二価の連結基である。
V1およびV2は、互いに独立に、置換基を有していてもよい炭素数1〜20のアルカンジイル基を表し、該アルカンジイル基を構成する−CH2−は、−O−、−S−または−NH−に置き換わっていてもよい。
U1およびU2は、互いに独立に、重合性基または水素原子を表し、少なくとも1つは重合性基である。]
二色性色素とは、分子の長軸方向における吸光度と、短軸方向における吸光度とが異なる性質を有する色素をいう。二色性色素としては、可視光を吸収する特性を有する特性を有する事が好ましく、380〜680nmの範囲に吸収極大波長(λMAX)を有するものがより好ましい。このような二色性色素としては、例えば、アクリジン色素、オキサジン色素、シアニン色素、ナフタレン色素、アゾ色素およびアントラキノン色素などが挙げられるが、中でもアゾ色素が好ましい。アゾ色素としては、モノアゾ色素、ビスアゾ色素、トリスアゾ色素、テトラキスアゾ色素およびスチルベンアゾ色素などが挙げられ、好ましくはビスアゾ色素およびトリスアゾ色素である。二色性色素は単独でも、組み合わせてもよいが、可視光全域で吸収を得るためには、3種類以上の二色性色素を組み合わせるのが好ましく、3種類以上のアゾ色素を組み合わせるのがより好ましい。
T1−A1(−N=N−A2)p−N=N−A3−T2(II)
[式(II)中、
A1およびA2およびA3は、互いに独立に、置換基を有していてもよい1,4−フェニレン基、ナフタレン−1,4−ジイル基または置換基を有していてもよい2価の複素環基を表し、T1およびT2は電子吸引基あるいは電子放出基であり、アゾ結合面内に対して実質的に180°の位置に有する。pは0〜4の整数を表す。pが2以上である場合、各々のA2は互いに同一でも異なっていてもよい。可視域に吸収を示す範囲で−N=N−結合が−C=C−、−COO−、−NHCO−。−N=CH−結合に置き換わっていてもよい。]
B1〜B20は、互いに独立に、水素原子、炭素数1〜6のアルキル基、炭素数1〜6のアルコキシ基、シアノ基、ニトロ基、置換または無置換のアミノ基(置換アミノ基および無置換アミノ基の定義は前記のとおり)、塩素原子またはトリフルオロメチル基を表す。高い偏光性能が得られる観点から、B2、B6、B9、B14、B18、B19は水素原子またはメチル基が好ましく、水素原子がより好ましい。
n1〜n4は、それぞれ独立に0〜3の整数を表す。
n1が2以上である場合、複数のB2はそれぞれ同一であってもよいし、異なっていてもよく、
n2が2以上である場合、複数のB6はそれぞれ同一であってもよいし、異なっていてもよく、
n3が2以上である場合、複数のB9はそれぞれ同一であってもよいし、異なっていてもよく、
n4が2以上である場合、複数のB14はそれぞれ同一であってもよいし、異なっていてもよい。
R1〜R8は、互いに独立に、水素原子、−Rx、−NH2、−NHRx、−NRx 2、−SRxまたはハロゲン原子を表す。
Rxは、炭素数1〜4のアルキル基または炭素数6〜12のアリール基を表す。]
R9〜R15は、互いに独立に、水素原子、−Rx、−NH2、−NHRx、−NRx 2、−SRxまたはハロゲン原子を表す。
Rxは、炭素数1〜4のアルキル基または炭素数6〜12のアリール基を表す。]
R16〜R23は、互いに独立に、水素原子、−Rx、−NH2、−NHRx、−NRx 2、−SRxまたはハロゲン原子を表す。
Rxは、炭素数1〜4のアルキル基または炭素数6〜12のアリール基を表す。]
D1およびD2は、互いに独立に、式(2−10a)〜式(2−10d)のいずれかで表される基を表す。
n5は1〜3の整数を表す。]
D3およびD4は、互いに独立に、式(2−11a)〜式(2−11h)のいずれかで表される基を表す。
n6は1〜3の整数を表す。]
光学積層体10は、偏光層12と第1位相差層14との間に第1接着層13を有する。第1接着層13は、粘着剤、接着剤またはこれらの組み合わせから形成することができる。第1接着層13は、通常1層であるが、2層以上であってもよい。第1接着層13は、偏光層12または第1位相差層14に接して形成されることができる。
第1位相差層14は、1以上の重合性液晶(以下、重合性液晶(b)ともいう)を重合することにより形成することができる。第1位相差層14は、コーティング層であることが好ましく、例えば後述する組成物(B)の硬化物であってよい。第1位相差層14は、ポジティブAプレートであることができ、λ/4板またはλ/2板であることができる。第1位相差層14は、ポジティブCプレートであることができる。
[式(III)中、
X1は、酸素原子、硫黄原子またはNR1−を表わす。R1は、水素原子または炭素数1〜4のアルキル基を表わす。
Y1は、置換基を有していてもよい炭素数6〜12の1価の芳香族炭化水素基または置換基を有していてもよい炭素数3〜12の1価の芳香族複素環式基を表わす。
Q3およびQ4は、それぞれ独立に、水素原子、置換基を有していてもよい炭素数1〜20の1価の脂肪族炭化水素基、炭素数3〜20の1価の脂環式炭化水素基、置換基を有していてもよい炭素数6〜20の1価の芳香族炭化水素基、ハロゲン原子、シアノ基、ニトロ基、−NR2R3または−SR2を表わすか、または、Q3とQ4とが互いに結合して、これらが結合する炭素原子とともに芳香環または芳香族複素環を形成する。R2およびR3は、それぞれ独立に、水素原子または炭素数1〜6のアルキル基を表わす。
D1およびD2は、それぞれ独立に、単結合、−C(=O)−O−、−C(=S)−O−、−CR4R5−、−CR4R5−CR6R7−、−O−CR4R5−、−CR4R5−O−CR6R7−、−CO−O−CR4R5−、−O−CO−CR4R5−、−CR4R5−O−CO−CR6R7−、−CR4R5−CO−O−CR6R7−またはNR4−CR5R6−またはCO−NR4−を表わす。
R4、R5、R6およびR7は、それぞれ独立に、水素原子、フッ素原子または炭素数1〜4のアルキル基を表わす。
G1およびG2は、それぞれ独立に、炭素数5〜8の2価の脂環式炭化水素基を表わし、該脂環式炭化水素基を構成するメチレン基は、酸素原子、硫黄原子またはNH−に置き換っていてもよく、該脂環式炭化水素基を構成するメチン基は、第三級窒素原子に置き換っていてもよい。
L1およびL2は、それぞれ独立に、1価の有機基を表わし、L1およびL2のうちの少なくとも一つは、重合性基を有する。]
P1−F1−(B1−A1)k−E1− (III−1)
P2−F2−(B2−A2)l−E2− (III−2)
[式(III−1)および式(III−2)中、
B1、B2、E1およびE2は、それぞれ独立に、−CR4R5−、−CH2−CH2−、−O−、−S−、−CO−O−、−O−CO−O−、−CS−O−、−O−CS−O−、−CO−NR1−、−O−CH2−、−S−CH2−または単結合を表わす。
A1およびA2は、それぞれ独立に、炭素数5〜8の2価の脂環式炭化水素基または炭素数6〜18の2価の芳香族炭化水素基を表わし、該脂環式炭化水素基を構成するメチレン基は、酸素原子、硫黄原子またはNH−に置き換っていてもよく、該脂環式炭化水素基を構成するメチン基は、第三級窒素原子に置き換っていてもよい。
kおよびlは、それぞれ独立に、0〜3の整数を表わす。
F1およびF2は、炭素数1〜12の2価の脂肪族炭化水素基を表わす。
P1は、重合性基を表わす。
P2は、水素原子または重合性基を表わす。
R4およびR5は、それぞれ独立に、水素原子、フッ素原子または炭素数1〜4のアルキル基を表わす。]
光学積層体10は、第1位相差層14と第2位相差層16との間に第2接着層15を有する。第2接着層15は、粘着剤、接着剤またはこれらの組み合わせから形成することができる。第2接着層15は、通常1層であるが、2層以上であってもよい。第2接着層15は、第1位相差層14または第2位相差層16に接して形成されることができる。
第2位相差層16は、1以上の重合性液晶(以下、重合性液晶(c)ともいう)を重合することにより形成することができる。第2位相差層16は、コーティング層であることが好ましく、例えば後述する組成物(C)の硬化物であってよい。第2位相差層16は、ポジティブAプレートであることができ、λ/4板であることができる。第2位相差層16は、ポジティブCプレートであることができる。
第2保護層17は、光学積層体10の折曲げ性の観点から、例えば樹脂フィルムから構成されてよく、好ましくは透明樹脂フィルムから構成されてよい。樹脂フィルムは、長尺のロール状樹脂フィルムであってよく、枚葉状樹脂フィルムであってよい。連続的に製造できる点で長尺のロール状樹脂フィルムが好ましい。樹脂フィルムを構成する樹脂としては、第1保護層11の説明において例示した樹脂、樹脂フィルム、市販の樹脂フィルムを用いることができる。第2保護層17は、剥離されずに表示装置に組み込まれる層であることができる。
修正靱性=最大応力×最大ひずみ (1)
〔ただし、最大応力および最大ひずみはそれぞれ、応力−ひずみ曲線における破壊点での応力およびひずみを示す〕
光学積層体10の製造方法の第1実施形態は、以下の工程を含む。
1)第1保護層11および偏光層12を有する積層体A31と、剥離フィルムA18、第1接着層13および剥離フィルムB19を有する第1粘着シート34とを準備する工程(図2a)。
2)第1粘着シート34の剥離フィルムA18を剥離して、第1粘着シート34の第1接着層13と積層体A31の偏光層12とを貼合する工程。第1位相差層14および第1基材(剥離フィルムC)20を有する積層体C33を準備する工程(図2b)。
3)積層体A31の剥離フィルムB19を剥離して、積層体A31の第1接着層13と積層体C33の第1位相差層14とを貼合する工程。剥離フィルムD21、第2接着層15および剥離フィルムE22を有する第2粘着シート35を準備する工程(図2c)。
4)第1基材(剥離フィルムC)20を剥離し、第2粘着シート35の剥離フィルムD21を剥離し、第1位相差層14と、第2粘着シート35の第2接着層15とを貼合する工程。第2保護層17および第2位相差層16を有する積層体B32を準備する工程(図2d)。
5)剥離フィルムE22を剥離し、第2接着層15と積層体B32の第2位相差層16とを貼合する工程(図2e)。
各工程は連続的に行うことができる。
1)剥離フィルムD21、第2接着層15および剥離フィルムE22を有する第2粘着シート35と、第2保護層17および第2位相差層16を有する積層体B32とを準備する工程(図3a)。
2)第1位相差層14および第1基材(剥離フィルムC)20を有する積層体C33を準備する工程。剥離フィルムD21を剥離し、第2接着層15と積層体B32の第2位相差層16とを貼合する工程(図3b)。
3)剥離フィルムA18、第1接着層13および剥離フィルムB19を有する第1粘着シート34を準備する工程。剥離フィルムE22を剥離し、第1位相差層14と第2接着層15とを貼合し、積層体C33の第1基材(剥離フィルムC)20を剥離する工程(図3c)。
4)第1保護層11および偏光層12を有する積層体A31を準備する工程。第1粘着シート34の剥離フィルムA18を剥離し、第1接着層13と第1位相差層14と貼合する工程(図3d)。
5)剥離フィルムB19を剥離して、第1接着層13と積層体A31の偏光層12とを貼合する工程(図3e)。
積層体A31の偏光層12は、第1保護層11上に、または第1保護層11が配向膜を有する場合には配向膜上に、1以上の重合性液晶(a)と二色性色素とを含有する組成物(A)を塗布し、重合性液晶(a)を重合することで製造することができる。組成物(A)は、溶剤、重合開始剤をさらに含み、増感剤、重合禁止剤、レベリング剤、反応性添加剤等をさらに含み得る。
組成物(A)中の重合開始剤は、1種類でも良いし、光の光源に合わせて2種類以上の複数の重合開始剤を混合しても良い。
nは1〜10までの整数を表わし、R1’は、炭素数2〜20の2価の脂肪族または脂環式炭化水素基、或いは炭素数5〜20の2価の芳香族炭化水素基を表わす。各繰返し単位にある2つのR2’は、一方が−NH−であり、他方が>N−C(=O)−R3’で示される基である。R3’は、水酸基または炭素−炭素不飽和結合を有する基を表す。
式(Y)中のR3’のうち、少なくとも1つのR3’は炭素−炭素不飽和結合を有する基である。]
重合性液晶(a)を重合させる方法としては、光重合が好ましい。光重合は、第1保護層上または配向膜上に重合性液晶(a)を組成物(A)が塗布された積層体に活性エネルギー線を照射することにより実施される。照射する活性エネルギー線としては、乾燥被膜に含まれる重合性液晶(A)の種類(特に、重合性液晶(A)が有する光重合性官能基の種類)、光重合開始剤を含む場合には光重合開始剤の種類、およびそれらの量に応じて適宜選択される。具体的には、可視光、紫外光、赤外光、X線、α線、β線、およびγ線からなる群より選択される一種以上の光が挙げられる。中でも、重合反応の進行を制御し易い点、および光重合装置として当分野で広範に用いられているものが使用できるという点で、紫外光が好ましく、紫外光によって光重合可能なように、重合性液晶(a)の種類を選択することが好ましい。
積層体B32の第2位相差層16は、第2保護層17上に、または第2保護層17が配向膜を有する場合には配向膜上に、1以上の重合性液晶(c)を含有する第2位相差層形成用組成物(C)(以下、組成物(C)ともいう)を塗布し、重合性液晶(c)を重合することで製造することができる。組成物(C)は、溶剤、重合開始剤をさらに含み、光増感剤、重合禁止剤、レベリング剤等をさらに含み得る。
積層体C33の第1位相差層14は、第1基材上に、または第1基材が配向膜を有する場合には配向膜上に、1以上の重合性液晶(b)を含有する第1位相差層形成用組成物(B)(以下、組成物(B)ともいう)を塗布し、重合性液晶(b)を重合することで製造することができる。組成物(B)は、溶剤、重合開始剤をさらに含み、光増感剤、重合禁止剤、レベリング剤等をさらに含み得る。
1)第1位相差層14および第1基材(剥離フィルムC)20を有する積層体C33を準備して、積層体33Cの第1位相差層14側の面に接着剤を塗布して第2接着層15を形成する工程。第2保護層17および第2位相差層16を有する積層体B32を準備する工程(図4a)。
2)第2接着層15と積層体B32の第2位相差層16とを貼合する工程(図4b)。
3)剥離フィルムA18、第1接着層13および剥離フィルムB19を有する第1粘着シート34を準備し、第1基材(剥離フィルムC)20を剥離する工程(図4c)。
4)第1保護層11および偏光層12を有する積層体A31を準備する工程。第1粘着シート34の剥離フィルムA18を剥離して、第1接着層13と第1位相差層14と貼合する工程(図4d)。
5)剥離フィルムB19を剥離して、第1接着層13と積層体A31の第1位相差層14と貼合する工程(図4d)。
1)第1保護層11および偏光層12を有する積層体A31を準備する工程。第1位相差層14および第1基材(剥離フィルムC)20を有する積層体C33を準備し、積層体33Cの第1位相差層14側の面に接着剤を塗布して第1接着層13を形成する工程(図5a)。
2)第1接着層13と積層体A31の偏光層12とを貼合する工程(図5b)。
3)剥離フィルムD21、第2接着層15および剥離フィルムE22を有する第2粘着シート35を準備する工程(図5c)。
4)第1基材(剥離フィルムC)20を剥離し、剥離フィルムD21を剥離し、第1位相差層14と第2接着層15とを貼合する工程。第2保護層17および第2位相差層16を有する積層体B32を準備する工程(図5d)。
5)剥離フィルムE22を剥離し、第2接着層15と第2位相差層16とを貼合する工程(図5e)。
1)第1位相差層14および第1基材(剥離フィルムC)20を有する積層体C33を準備し、第2保護層17および第2位相差層16を有する積層体B32を準備し、接着剤からなる第2接着層15を準備する工程(図6a)。
2)積層体C33と積層体B32とを第2接着層15を介して貼合する工程(図6b)。
3)第1基材(剥離フィルムC)20を剥離する工程(図6c)。
4)第1保護層11および偏光層12を有する積層体A31を準備し、積層体A31の偏光層12側の面に接着剤を塗布して第1接着層13を形成する工程(図6d)。
5)第1接着層13と第1位相差層14とを貼合する工程(図6e)。
本発明の一実施形態に係る表示装置は、光学積層体10が、粘着剤層を介して画像表示素子に貼合されたものである。光学積層体10は、第1保護層11が第2保護層17に対して視認側に配置されるように、画像表示素子に貼合されることができる。粘着剤層は、光学積層体10の用途に応じて、光学積層体10のいずれかの表面に設けることができる。粘着剤としては、特に限定されず、後述する粘着剤を用いることができる。粘着剤は、第2保護層上に形成されることができる。
記ない限り、質量%および質量部である。
光学積層体を形成する各層の厚みは、接触式膜厚測定装置(株式会社ニコン製MS−5C)によって測定した。
各実施例および比較例において得られた光学積層体について、以下のように屈曲性試験を行った。図7は、本評価試験の方法を模式的に示す図である。2つのステージ501、502を備えた屈曲装置(Science Town社製、STS−VRT−500)を準備し、ステージ501、502の上に光学積層体100を載せた(図7a)。2つのステージ501、502の間の距離(ギャップ)Cは、5mm(2.5R)または2mm(1.0R)に設定した。このステージ501、502は、2つのステージの間(ギャップ)Cを中心に揺動可能であり、初期は2つのステージ501、502は同一平面を構成する。2つのステージ501,502を位置P1及び位置P2を回転軸の中心として上方に90度回転させて2つのステージ501、502を閉じ(図7b)、再びステージ501、502を開く動作を1回の屈曲と定義する。この動作を繰り返し、光学積層体100へ最初にクラックが生じるまでの屈曲回数を数えた。評価の基準は以下の通りである。
◎(極めて良い):20万回以上、〇(良い):10万回以上20万回未満、△(使用可能):5万回以上10万回未満、×(やや劣る):1万回以上5万回未満、××(劣る):1万回未満
サンプルとして各実施例および比較例における光学積層体の第2保護層を用いて、JIS K7161に準拠してUTM(Universal Testing Machine(株式会社島津製作所製オートグラフAG−X)を用いて応力−ひずみ曲線を作成した。最大応力および最大ひずみはそれぞれ、応力−ひずみ曲線において破壊点から求めた。以下の式(1)に従って修正靱性を求めた。
修正靱性=最大応力×最大ひずみ (1)
重合性液晶化合物は、式(1−6)で表される重合性液晶化合物[以下、化合物(1−6)ともいう]と式(1−7)で表される重合性液晶化合物[以下、化合物(1−7)ともいう]とを用いた。
偏光子層形成用組成物[以下、組成物(A−1)ともいう]は、化合物(1−6)75重量部、化合物(1−7)25重量部、二色性染料としての上記式(2−1a)、(2−1b)、(2−3a)で示されるアゾ色素各2.5重量部、重合開始剤としての2−ジメチルアミノ−2−ベンジル−1−(4−モルホリノフェニル)ブタン−1−オン(Irgacure369、BASFジャパン社製)6重量部、およびレベリング剤としてのポリアクリレート化合物(BYK−361N、BYK−Chemie社製)1.2重量部を、溶剤のトルエン400重量部に混合し、得られた混合物を80℃で1時間攪拌することにより調製した。
下記に示す各成分を混合し、得られた混合物を80℃で1時間攪拌することにより、組成物(B−1)を得た。
下記式で示される化合物b−1:80重量部
レベリング剤(BYK−361N、ポリアクリレート化合物、BYK−Chemie社製):0.1重量部
溶剤(シクロペンタノン):400重量部
下記に示す各成分を混合し、得られた混合物を80℃で1時間攪拌することにより、組成物(C−1)を得た。
下記式で示される化合物c−1(LC242、BASFジャパン社製):100重量部
レベリング剤(BYK−361N、ポリアクリレート化合物、BYK−Chemie社製):0.5重量部
添加剤(LR9000、BASFジャパン社製):5.7重量部
溶剤(プロピレングリコール1−モノメチルエーテル2−アセテート):412重量部
以下の構造単位からなる光反応性基を有するポリマー1を準備した。
ポリマー1を濃度5重量%で、シクロペンタノンに溶解した溶液を配向膜形成用組成物[以下、組成物(D−1)ともいう]して用いた。
第1保護層の形成
第1保護層としてセルロース系フィルム(TACフィルム、コニカミノルタ株式会社製、厚み25μm、TAC1)を用いた。該フィルム上に、上述の通り得られた組成物(D−1)をバーコート法により塗布し、80℃の乾燥オーブン中で1分間加熱乾燥した。得られた乾燥被膜に偏光UV照射処理を施して第1配向膜(AL1)を形成した。偏光UV処理は、UV照射装置(SPOT CURE SP−7;ウシオ電機株式会社製)から照射される光を、ワイヤーグリッド(UIS−27132##、ウシオ電機株式会社製)を透過させて、波長365nmで測定した積算光量が100mJ/cm2である条件で行った。第1配向膜(AL1)の厚みは100nmであった。
形成した第1配向膜(AL1)上に、組成物(A−1)をバーコート法により塗布し、120℃の乾燥オーブンにて1分間加熱乾燥した後、室温まで冷却した。上記UV照射装置を用いて、積算光量1200mJ/cm2(365nm基準)で紫外線を、乾燥被膜に照射することにより、偏光層(pol)を形成した。得られた偏光層(pol)の厚みをレーザー顕微鏡(オリンパス株式会社社製 OLS3000)により測定したところ、1.8μmであった。このようにして偏光層(pol)/第1配向膜(AL1)/第1保護層(TAC1)からなる積層体Aを得た。
第2保護層の形成
第2保護層としてTAC1を用いた。該フィルム上に、コロナ処理を1回施した。コロナ処理の条件は、出力0.3kW、処理速度3m/分とした。該フィルム上に、組成物(D−1)をバーコート法により塗布し、90℃の乾燥オーブン中で1分間加熱乾燥して、第2配向膜(AL2)を得た。
第2保護層の第2配向膜上(AL2)に、組成物(C−1)をバーコート法により塗布し、90℃の乾燥オーブンで1分間加熱乾燥した。得られた乾燥被膜に、窒素雰囲気下で、上記UV照射装置を用いて、積算光量1000mJ/cm2(365nm基準)の紫外線を照射することにより、位相差層を形成した。得られた位相差層の厚さをレーザー顕微鏡(オリンパス株式会社社製 OLS3000)により測定したところ、2.0μmであった。第2位相差層は、厚み方向に位相差を示すポジティブCプレート(posiC)であった。このようにして第2位相差層(posiC)/第2配向膜(AL2)/第2保護層(TAC2)からなる積層体Bを得た。
第1位相差層の形成
第1基材として厚み100μmのポリエチレンテレフタレートフィルム(PET)を準備し、該フィルム上に組成物(D−1)をバーコート法により塗布し、80℃の乾燥オーブン中で1分間加熱乾燥した。得られた乾燥被膜に偏光UV照射処理を施して第3配向膜(AL3)を形成した。偏光UV処理は、上記UV照射装置を用いて、波長365nmで測定した積算光量が100mJ/cm2である条件で行った。また、偏光UVの偏光方向は偏光層の吸収軸に対して45°となるように行った。
第1接着層及び第2接着層を形成するための粘着シート(第1および第2接着層形成用粘着シート)を下記の通り作製した。
下記成分を、窒素雰囲気下で55℃で混合して反応させることによりアクリル樹脂を得た。
アクリル酸ブチル:70部
アクリル酸メチル:20部
アクリル酸:1.0部
開始剤(アゾビスイソブチルニトリル):0.2部
溶剤(酢酸エチル):80部
得られたアクリル樹脂に、コロネートL(東ソー株式会社)0.5部、シランカップリング剤X−12−981(信越シリコン株式会社)0.5部を混合して、最後に全体固形分濃度が10%になるように酢酸エチルを添加して、粘着剤形成用組成物を得た。得られた粘着剤形成用組成物を離型処理されたポリエチレンテレフタレートフィルム(SpB、厚み38μm)の離型処理面に、アプリケーターを利用して乾燥後の厚みが5μmになるように塗布した。塗布膜を100℃で1分間乾燥して、粘着剤(PSA1またはPSA2)を備えるフィルムを得た。その後、露出されている粘着剤面上に離型処理された別のポリエチレンテレフタレートフィルム(SpA、厚み38μm)を貼合した。その後、23℃、50%RHの条件で、7日間養生させた。このようにして、剥離フィルムA(SpA)/粘着剤(PSA1またはPSA2)/剥離フィルムB(SpB)からなる粘着シートを作製した。
積層体A(pol/AL1/TAC1)と第1接着層形成用粘着シート(SpA/PSA1/SpB)を準備した。
第1接着層形成用粘着シートから剥離フィルムAを剥離した(PSA1/SpB)。積層体Aの偏光層側の面と第1接着層形成用粘着シートの剥離した面とを貼合して積層体A1(SpB/PSA1/pol/AL1/TAC1)を得た。
積層体A1から剥離フィルムBを剥離し(PSA1/pol/AL1/TAC1)、第1接着層面と積層体Cの第1位相差層側の面とを貼合し、積層体A2(PET/AL3/QWP/PSA1/pol/AL1/TAC1)を得た。
積層体A2からPETを剥離し(AL3/QWP/PSA1/pol/AL1/TAC1)、第2接着層形成用粘着シートから剥離フィルムAを剥離し(PSA2/SpB)、第2接着層面と積層体A2の第3配向膜側の面とを貼合し、積層体A3(Spb/PSA2/AL3/QWP/PSA1/pol/AL1/TAC1)を得た。
積層体A3から剥離フィルムBを剥離し、積層体A3の第2接着剤層面と積層体Bの第2位相差層側の面と貼合し、光学積層体(TAC1/AL2/posiC/PSA2/AL3/QWP/PSA1/pol/AL1/TAC1)を得た。
得られた光学積層体について各層の厚み、第2保護層の修正靱性および折曲げ試験結果を表1に示す。
第1保護層の厚みを表1に示す厚み(TAC3)に変更したこと、および第2保護層の種類および厚みを表1に示す種類および厚み(PET)に変更したこと以外は、実施例1と同様にして光学積層体を得た。結果を表1に示す。表1において、PETは、ポリエチレンテレフタレートフィルムを意味する。
第1保護層の種類および厚みを表1に示す種類および厚み(HC−PI)に変更したこと以外は、実施例1と同様にして光学積層体を得た。結果を表1に示す。表1において、HC−PIは、表面にハードコート層を有するポリイミドフィルムを意味する。
第1保護層の種類および厚みを表1に示す種類および厚み(HC−PI)に変更した積層体A(pol/AL1/HC−PI)と第1接着層形成用粘着シート(SpA/PSA1/SpB)を準備した。
第1接着層形成用粘着シートから剥離フィルムAを剥離した(PSA1/SpB)。積層体Aの偏光層側の面と第1接着層形成用粘着シートの剥離した面とを貼合して積層体A1(SpB/PSA1/pol/AL1/HC−PI)を得た。
積層体A1から剥離フィルムBを剥離し(PSA1/pol/AL1/HC−PI)、第1接着層面と積層体Cの第1位相差層側の面とを貼合し、積層体A2(PET/AL3/QWP/PSA1/pol/AL1/HC−PI)を得た。
積層体A2からPETを剥離し(AL3/QWP/PSA1/pol/AL1/HC−PI)た。
次いで紫外線硬化型接着剤としてエポキシ化合物を含む組成物(株式会社ADEKA製、粘度:44mPa・s)を、積層体Bの位相差層側の面上にバーコート法により塗布し、接着剤層(AD)を形成した。
積層体A2の第3配向膜側の面と積層体Bの紫外線硬化型接着剤を塗布した面とを貼合した。
次いで積算光量(波長280〜320nmの波長領域における光照射強度の積算量)が約250mJ/cm2(測定機:FusionUV社製造UV Power PuckIIによる測定値)である紫外線(UVB)を積層体B面側から照射して光学積層体(TAC2/AL2/posiC/AD/AL3/QWP/PSA1/pol/AL1/HC−PI)を製造した。
第2保護層の種類および厚みを表1に示す種類および厚み(COP2)に変更したこと以外は、実施例1と同様にして光学積層体を得た。結果を表1に示す。表1において、COPは、環状オレフィン系樹脂フィルムを意味する。
第1保護層の厚みを表1に示す厚み(TAC4)に変更したこと以外は、実施例1と同様にして光学積層体を得た。結果を表1に示す。
積層体Bを製造する際、第2保護層表面にコロナ処理を施さなかったこと以外は、実施例1と同様にして光学積層体を得た後、光学積層体から第2保護層を剥離した。結果を表1に示す。
積層体Aを製造する際に、第1保護層の厚みを50μmに変更した(TAC5)。積層体Aの偏光層上に組成物(D−1)をバーコート法により塗布し、80℃の乾燥オーブン中で1分間加熱乾燥した。得られた乾燥被膜に偏光UV照射処理を施して第3配向膜を形成した。偏光UV処理は、UV照射装置(SPOT CURE SP−7;ウシオ電機株式会社製)を用いて、波長365nmで測定した積算光量が100mJ/cm2である条件で行った。また、偏光UVの偏光方向は偏光層の吸収軸に対して45°となるように行った。
こうして得られた第3配向膜上に、組成物(B−1)をバーコート法により塗布し、120℃の乾燥オーブンで1分間加熱乾燥した後、室温まで冷却した。得られた乾燥被膜に、上記UV照射装置を用いて、積算光量1000mJ/cm2(365nm基準)の紫外線を照射することにより、第1位相差層を形成した。第1位相差層は、λ/4板であった。
第1保護層をTACフィルムから環状オレフィン系樹脂フィルム(ARTON、JSR株式会社、COP1)に変更し、各層の厚みを表1に示す厚みに変更したこと以外は、比較例2と同様にして、光学積層体を得た。結果を表1に示す。
第1保護層の厚みを表1に示す厚みに変更したこと(TAC4)、および第2保護層の種類および厚みを表1に示す種類および厚み(COP2)に変更したこと以外は、実施例1と同様にして光学積層体を得た。結果を表1に示す。
Claims (6)
- 第1保護層、偏光層、第1接着層、第1位相差層、第2接着層、第2位相差層および第2保護層がこの順に積層され、前記第2保護層の厚み(B)に対する前記第1保護層の厚み(A)の比率(A/B)が3.3以下である、光学積層体。
- 前記第2保護層は、以下の式(1)で定義される修正靱性が2300MPa・%以上である、請求項1に記載の光学積層体。
修正靱性=最大応力×最大ひずみ (1)
〔ただし、最大応力および最大ひずみはそれぞれ、応力−ひずみ曲線における破壊点での応力およびひずみを示す〕 - 前記第1保護層の厚みは10μm〜200μmである、請求項1または2に記載の光学積層体。
- 前記第2保護層の厚みは5μm〜100μmである、請求項1〜3のいずれか1項に記載の光学積層体。
- 前記第1接着層および/または前記第2接着層の厚みは1μm以上である、請求項1〜4のいずれか1項に記載の光学積層体。
- 請求項1〜5のいずれか1項に記載の光学積層体を含む表示装置。